Rotary kiln

Last updated
Rotary kiln (large rust-colored horizontal tube at center right) at a Wyoming cement plant Lime plant, Wyoming.jpg
Rotary kiln (large rust-colored horizontal tube at center right) at a Wyoming cement plant
General layout of a direct fired countercurrent rotary kiln used in cement manufacture CemKilnKiln.jpg
General layout of a direct fired countercurrent rotary kiln used in cement manufacture
Rotary kiln body, with drive gear and 2 tyres (riding rings) Rotary Kiln.jpg
Rotary kiln body, with drive gear and 2 tyres (riding rings)

A rotary kiln is a pyroprocessing device used to raise materials to a high temperature (calcination) in a continuous process. Materials produced using rotary kilns include:

Contents

They are also used for roasting a wide variety of sulfide ores prior to metal extraction.

Principle of operation

The kiln is a cylindrical vessel, inclined slightly from the horizontal, which is rotated slowly about its longitudinal axis. The process feedstock is fed into the upper end of the cylinder. As the kiln rotates, material gradually moves down toward the lower end, and may undergo a certain amount of stirring and mixing. Hot gases pass along the kiln, sometimes in the same direction as the process material (co-current), but usually in the opposite direction (counter-current). The hot gases may be generated in an external furnace, or may be generated by a flame inside the kiln. Such a flame is projected from a burner-pipe (or "firing pipe") which acts like a large bunsen burner. The fuel for this may be gas, oil, pulverized petroleum coke or pulverized coal.

Construction

The basic components of a rotary kiln are the shell, the refractory lining, support tyres (riding rings) and rollers, drive gear and internal heat exchangers.

History

The rotary kiln was invented in 1873 by Frederick Ransome. [1] He filed several patents in 1885-1887, but his experiments with the idea were not a commercial success. Nevertheless, his designs provided the basis for successful kilns in the US from 1891, subsequently emulated worldwide.

Kiln shell

This is made from rolled mild steel plate, usually between 15 and 30 mm (½" to 1⅜"), welded to form a cylinder which may be up to 230 m (754.5') in length and up to 6 m (19' 8") in diameter.

Upper limits on diameter are set by the tendency of the shell to deform under its own weight to an oval cross section, with consequent flexure during rotation. Length is not necessarily limited, but it becomes difficult to cope with changes in length on heating and cooling (typically around 0.1 to 0.5% of the length) if the kiln is very long.

Refractory lining

The purpose of the refractory lining is to insulate the steel shell from the high temperatures inside the kiln, and to protect it from the corrosive properties of the process material. It may consist of refractory bricks or cast refractory concrete, or may be absent in zones of the kiln that are below approximately 250 °C (482 °F). The refractory selected depends upon the temperature inside the kiln and the chemical nature of the material being processed. In some processes, such as cement, the refractory life is prolonged by maintaining a coating of the processed material on the refractory surface. The thickness of the lining is generally in the range 80 to 300 mm (3.1" to 11 ⅜"). A typical refractory will be capable of maintaining a temperature drop of 1000 °C (1,832 °F) or more between its hot and cold faces. The shell temperature needs to be maintained below around 350 °C (662 °F) to protect the steel from damage, and continuous infrared scanners are used to give early warning of "hot-spots" indicative of refractory failure.

Tyres and rollers

Kiln tyre closeup showing typical chair arrangement LDRotaryKilnTyre.jpg
Kiln tyre closeup showing typical chair arrangement

Tyres, sometimes called riding rings, usually consist of a single annular steel casting, machined to a smooth cylindrical surface, which attach loosely to the kiln shell through a variety of "chair" arrangements. These require some ingenuity of design, since the tyre must fit the shell snugly, but also allow thermal movement. The tyre rides on pairs of steel rollers, also machined to a smooth cylindrical surface, and set about half a kiln-diameter apart. The rollers must support the kiln, and allow rotation that is as nearly frictionless as possible. A well-engineered kiln, when the power is cut off, will swing pendulum-like many times before coming to rest. The mass of a typical 6 x 60 m (19' 8" x 196' ⅜") kiln, including refractories and feed, is around 1100 tonnes (2.42Mlb), and would be carried on three tyres and sets of rollers, spaced along the length of the kiln. The longest kilns may have 8 sets of rollers, while very short and small kilns may have none. Kilns usually rotate at 0.5 to 2 rpm. The Kilns of modern cement plants are running at 4 to 5 rpm. The bearings of the rollers must be capable of withstanding the large static and live loads involved and must be carefully protected from the heat of the kiln and the ingress of dust. Since the kiln is at an angle, it also needs support to prevent it from walking off the support rollers. Usually upper and lower "retaining (or thrust) rollers" bearing against the side of tyres prevent the kiln from walking off the support rollers.

Drive gear

The kiln is usually turned by means of a single Girth Gear surrounding a cooler part of the kiln tube, but sometimes it is turned by driven rollers. The gear is connected through a gear train to a variable-speed electric motor. This must have high starting torque to start the kiln with a large eccentric load. A 6 x 60 m kiln requires around 800 kW to turn at 3 rpm. The speed of material flow through the kiln is proportional to rotation speed; a variable-speed drive is needed to control this. When driving through rollers, hydraulic drives may be used. These have the advantage of developing extremely high torque. In many processes, it is dangerous to allow a hot kiln to stand still if the drive power fails. Temperature differences between the top and bottom of the kiln may cause the kiln to warp, and refractory is damaged. Hence, normal practice is to provide an auxiliary drive for use during power cuts. This may be a small electric motor with an independent power supply, or a diesel engine. This turns the kiln very slowly, but enough to prevent damage.

Internal heat exchangers

Heat exchange in a rotary kiln may be by conduction, convection and radiation, in descending order of efficiency. In low-temperature processes, and in the cooler parts of long kilns lacking preheaters, the kiln is often furnished with internal heat exchangers to encourage heat exchange between the gas and the feed. These may consist of scoops or "lifters" that cascade the feed through the gas stream, or may be metallic inserts that heat up in the upper part of the kiln, and impart the heat to the feed as they dip below the feed surface as the kiln rotates. The latter are favoured where lifters would cause excessive dust pick-up. The most common heat exchanger consists of chains hanging in curtains across the gas stream.

Other equipment

The kiln connects with a material exit hood at the lower end and ducts for waste gases. This requires gas-tight seals at either end of the kiln. The exhaust gas may go to waste, or may enter a preheater, which further exchanges heat with the entering feed. The gases must be drawn through the kiln, and the preheater if fitted, by a fan situated at the exhaust end. In preheater installations which may have a high pressure-drop, considerable fan power may be needed, and the fan drive is often the largest drive in the kiln system. Exhaust gases contain dust, and there may be undesirable constituents, such as sulfur dioxide or hydrogen chloride. Equipment is installed to scrub these from the gas stream before passing to the atmosphere.

Differences according to the process

Kilns used for DRI production

Direct reduction processes based on a rotary kiln [2]
Procedes de reduction directe par tambours rotatifs.svg
Extraction Point12345
Consistency of kiln dischargesolidsemiliquidsol. (clinker)
liq. (pig iron)
Preferred iron content of ore (% Fe)30-6030-6055-6325-4550-67
Size of ore feed (mm)< 20< 20< 105-25 [3] < 5< 0.2
Influence of basicity of charge (CaO/Al
2
O
3
)
no influence0.32.8-3.0
Maximal temperature of charge (°C)600-900900-11001200-13001400-1500
Oxygen removal (% O
2
extracted from Fe
2
O
3
)
12 %20-70>90100
Examples of processesLurgiHighveld
Udy
LARCO
Elkem
RNSL/RN
Krupp
Krupp-Renn Process Basset

See also

Citations

  1. The Michigan Technic. UM Libraries. 1900. pp. 3–.
  2. Grzella, Jörg; Sturm, Peter; Krüger, Joachim; Reuter, Markus A.; Kögler, Carina; Probst, Thomas (2005). "Metallurgical Furnaces" (PDF). John Wiley & Sons. p. 7.
  3. For ilmenite and ferrous sands : size between 0.05 and 0.5 mm.

General and cited sources and further reading

Related Research Articles

<span class="mw-page-title-main">Kiln</span> Furnace for clay products

A kiln is a thermally insulated chamber, a type of oven, that produces temperatures sufficient to complete some process, such as hardening, drying, or chemical changes. Kilns have been used for millennia to turn objects made from clay into pottery, tiles and bricks. Various industries use rotary kilns for pyroprocessing and to transform many other materials.

<span class="mw-page-title-main">Lime kiln</span> Kiln used for the calcination of limestone

A lime kiln is a kiln used for the calcination of limestone (calcium carbonate) to produce the form of lime called quicklime (calcium oxide). The chemical equation for this reaction is

<span class="mw-page-title-main">Ball mill</span> Machine used to grind or blend materials

A ball mill is a type of grinder filled with grinding balls, used to grind or blend materials for use in mineral dressing processes, paints, pyrotechnics, ceramics, and selective laser sintering. It works on the principle of impact and attrition: size reduction is done by impact as the balls drop from near the top of the shell.

<span class="mw-page-title-main">Extrusion</span> Process of pushing material through a die to create long symmetrical-shaped objects

Extrusion is a process used to create objects of a fixed cross-sectional profile by pushing material through a die of the desired cross-section. Its two main advantages over other manufacturing processes are its ability to create very complex cross-sections; and to work materials that are brittle, because the material encounters only compressive and shear stresses. It also creates excellent surface finish and gives considerable freedom of form in the design process.

<span class="mw-page-title-main">Refractory</span> Materials resistant to decomposition under high temperatures

In materials science, a refractory is a material that is resistant to decomposition by heat or chemical attack that retains its strength and rigidity at high temperatures. They are inorganic, non-metallic compounds that may be porous or non-porous, and their crystallinity varies widely: they may be crystalline, polycrystalline, amorphous, or composite. They are typically composed of oxides, carbides or nitrides of the following elements: silicon, aluminium, magnesium, calcium, boron, chromium and zirconium. Many refractories are ceramics, but some such as graphite are not, and some ceramics such as clay pottery are not considered refractory. Refractories are distinguished from the refractory metals, which are elemental metals and their alloys that have high melting temperatures.

<span class="mw-page-title-main">Electric arc furnace</span> Type of furnace

An electric arc furnace (EAF) is a furnace that heats material by means of an electric arc.

<span class="mw-page-title-main">Thermal power station</span> Power plant that generates electricity from heat energy

A thermal power station is a type of power station in which heat energy is converted to electrical energy. In a steam-generating cycle heat is used to boil water in a large pressure vessel to produce high-pressure steam, which drives a steam turbine connected to an electrical generator. The low-pressure exhaust from the turbine enters a steam condenser where it is cooled to produce hot condensate which is recycled to the heating process to generate more high pressure steam. This is known as a Rankine cycle.

<span class="mw-page-title-main">Air preheater</span> Device designed to heat air before another process

An air preheater is any device designed to heat air before another process, with the primary objective of increasing the thermal efficiency of the process. They may be used alone or to replace a recuperative heat system or to replace a steam coil.

<span class="mw-page-title-main">Continuous casting</span> Process for solidifying molten metal

Continuous casting, also called strand casting, is the process whereby molten metal is solidified into a "semifinished" billet, bloom, or slab for subsequent rolling in the finishing mills. Prior to the introduction of continuous casting in the 1950s, steel was poured into stationary molds to form ingots. Since then, "continuous casting" has evolved to achieve improved yield, quality, productivity and cost efficiency. It allows lower-cost production of metal sections with better quality, due to the inherently lower costs of continuous, standardised production of a product, as well as providing increased control over the process through automation. This process is used most frequently to cast steel. Aluminium and copper are also continuously cast.

<span class="mw-page-title-main">Rotary dryer</span>

A rotary dryer is a type of industrial dryer used to reduce or minimize the moisture content of the material it is handling by bringing it into contact with a heated gas. The dryer is made up of a rotating cylinder, a drive mechanism, and a support structure. The cylinder is inclined slightly with the discharge end is lower than the material feed end so that material moves through the dryer under the influence of gravity. Material to be dried enters the dryer and, as the dryer rotates, the material is lifted up by a series of fins lining the inner wall of the dryer. When the material gets high enough, it falls back down to the bottom of the dryer, passing through the hot gas stream as it falls.

<span class="mw-page-title-main">Ladle (metallurgy)</span> Vessel used to transport and pour out molten metals

In metallurgy, a ladle is a bucket-shaped container or vessel used to transport and pour out molten metals. Ladles are often used in foundries and range in size from small hand-carried vessels that resemble a kitchen ladle and hold 20 kilograms (44 lb) to large steelmill ladles that hold up to 300 tonnes. Many non-ferrous foundries also use ceramic crucibles for transporting and pouring molten metal and will also refer to these as ladles.

A pulverizer or grinder is a mechanical device for the grinding of many different types of materials. For example, a pulverizer mill is used to pulverize coal for combustion in the steam-generating furnaces of coal power plants.

<span class="mw-page-title-main">Cement kiln</span> High temperature rotating oven used for producing clinker

Cement kilns are used for the pyroprocessing stage of manufacture of portland and other types of hydraulic cement, in which calcium carbonate reacts with silica-bearing minerals to form a mixture of calcium silicates. Over a billion tonnes of cement are made per year, and cement kilns are the heart of this production process: their capacity usually defines the capacity of the cement plant. As the main energy-consuming and greenhouse-gas–emitting stage of cement manufacture, improvement of kiln efficiency has been the central concern of cement manufacturing technology. Emissions from cement kilns are a major source of greenhouse gas emissions, accounting for around 2.5% of non-natural carbon emissions worldwide.

<span class="mw-page-title-main">Calcium aluminate cements</span> Rapidly setting hydraulic cements

Calcium aluminate cements are cements consisting predominantly of hydraulic calcium aluminates. Alternative names are "aluminous cement", "high-alumina cement", and "Ciment fondu" in French. They are used in a number of small-scale, specialized applications.

A regenerative heat exchanger, or more commonly a regenerator, is a type of heat exchanger where heat from the hot fluid is intermittently stored in a thermal storage medium before it is transferred to the cold fluid. To accomplish this the hot fluid is brought into contact with the heat storage medium, then the fluid is displaced with the cold fluid, which absorbs the heat.

<span class="mw-page-title-main">Rawmill</span>

A raw mill is the equipment used to grind raw materials into "rawmix" during the manufacture of cement. Rawmix is then fed to a cement kiln, which transforms it into clinker, which is then ground to make cement in the cement mill. The raw milling stage of the process effectively defines the chemistry of the finished cement, and has a large effect upon the efficiency of the whole manufacturing process.

Permanent mold casting is a metal casting process that employs reusable molds, usually made from metal. The most common process uses gravity to fill the mold, however gas pressure or a vacuum are also used. A variation on the typical gravity casting process, called slush casting, produces hollow castings. Common casting metals are aluminium, magnesium, and copper alloys. Other materials include tin, zinc, and lead alloys and iron and steel are also cast in graphite molds.

<span class="mw-page-title-main">Sectional cooler</span>

A sectional cooler is a type of liquid cooled rotary drum cooler used for continuous processes in chemical engineering. Sectional coolers consist of a rotating cylinder, a drive unit and a support structure. At each end of the drum there are stationary chutes for material feed and outlet. Depending on the size of the cooler the drum is pivoted on a shaft running through its axis, or is supported on running treads or external ring gears. The interior of the drum consists of several wedge-shaped chambers arranged around a central hollow shaft. This arrangement is completely surrounded by a jacket of water. In the wedge-shaped chambers are angled fins or shovels which move material through the cooler as the drum is rotated.

<span class="mw-page-title-main">Thermal wheel</span> Type of energy recovery heat exchanger

A thermal wheel, also known as a rotary heat exchanger, or rotary air-to-air enthalpy wheel, energy recovery wheel, or heat recovery wheel, is a type of energy recovery heat exchanger positioned within the supply and exhaust air streams of air-handling units or rooftop units or in the exhaust gases of an industrial process, in order to recover the heat energy. Other variants include enthalpy wheels and desiccant wheels. A cooling-specific thermal wheel is sometimes referred to as a Kyoto wheel.

<span class="mw-page-title-main">Industrial furnace</span> Device used for providing heat in industrial applications

An industrial furnace, also known as a direct heater or a direct fired heater, is a device used to provide heat for an industrial process, typically higher than 400 degrees Celsius. They are used to provide heat for a process or can serve as reactor which provides heats of reaction. Furnace designs vary as to its function, heating duty, type of fuel and method of introducing combustion air. Heat is generated by an industrial furnace by mixing fuel with air or oxygen, or from electrical energy. The residual heat will exit the furnace as flue gas. These are designed as per international codes and standards the most common of which are ISO 13705 / American Petroleum Institute (API) Standard 560. Types of industrial furnaces include batch ovens, metallurgical furnaces, vacuum furnaces, and solar furnaces. Industrial furnaces are used in applications such as chemical reactions, cremation, oil refining, and glasswork.