Glass formation

Last updated

A glass is an amorphous solid completely lacking long range periodic atomic structure that exhibits a region of glass transformation. This broad definition means that any material be it organic, inorganic, metallic, etc. in nature may form a glass if it exhibits glass transformation behavior. However prior to 1900 very few non-silicate glasses were known and the theories developed were consequently heavily influenced by existing observations of silicate melts (compounds containing silicon and oxygen). These theories are grouped under the heading of structural theories of glass formation. In later years many non-silicate glasses were discovered and it is recognized today that almost any material is capable of forming a glass given the right experimental conditions and focus has changed from which materials will form a glass to under what conditions will a particular material form a glass. More recent theories focus on the kinetics behind the formation of glass and these kinetic theories of glass formation have largely replaced earlier structural theories.

Contents

Structural theories of glass formation

Among the first structural theories of glass formation was that which was developed by Goldschmidt who stated that glasses of the general formula RnOm will form glasses when the ratio of the ionic radii of the cation to the oxygen is in the range of 0.2 to 0.4. When this condition is true the cation tends to be bonded to 4 oxygen atoms and have a tetrahedral coordination. As such Goldschmidt concluded from this that only cations with tetrahedral coordination would form glasses on cooling. The conclusion was empirical and no attempt was made to explain this observation by Goldschmidt.

The ideas of Goldschmidt were extended by Zachariasen who attempted to explain why certain coordination numbers would favor glass formation. He noted that silicates which formed glasses rather than recrystallizing after melting and cooling formed network structures consisting of tetrahedra joined at all four corners in a non-periodic non-symmetric manner (unlike crystals which are periodic and symmetrical. These networks extend in all three dimensions in a manner such that the average behavior of the glass is identical - the properties of the glass are isotropic. Using this as his basis Zachariasen concluded that the ability to form a glass was dependent on the ability to form these networks. He then went on to explain the necessary conditions for forming such a network, which he defined as follows:

  1. An oxygen atom cannot be connected to more than two cations otherwise the variation in bond angles required to form a non periodic network cannot be achieved.
  2. The number of oxygen atoms must be small either 3 or 4, which was and empirically determined condition based on the fact that the only glasses known at the time were formed from either triangular or tetrahedrally coordinated cations.
  3. At least 3 corners of a polyhedron must be shared in order to yield a 3 dimensional structure and the polyhedra may only be joined at the corners (they do not share edges or faces).

He also stated that the melt must be cooled under appropriate conditions in order for glass formation to occur, anticipating later kinetic theories of glass formation. Other statements of Zachariasen were used as the basis for a class of glass formation models known as random network theory. However, in his original work Zachariasen did not use the term random network preferring instead to use "vitreous network" as the structure is not truly random and is constrained by minimum distances between atoms. As a consequence not all inter-nuclear distances are equally probably and observed x ray patterns for glasses are a consequence of a vitreous network.

Other structural theories of glass formation focused on the nature of the bonds between cations and anions. For example, Smekal suggested that only bonds which are intermediate in nature lying between purely ionic and purely covalent in a melt would allow for the formation of glass. He suggested this on the basis that ionic bonds lack the directionality required to form a network and that covalent bonds would enforce strict bond angles preventing the variation required for the formation of a non periodic network. Stanworth attempted to better quantify this mixed bond concept and divided oxides into three groups on the basis of electronegativity of the cation. The groups were as follows:

  1. network formers: cations which form bonds to oxygen with near 50% ionic character produce good glasses
  2. intermediates: form slightly more ionic bonds with oxygen though the cannot form glasses themselves they can partially replace cations of the network former class.
  3. modifiers: cations with very low electronegativities which form highly ionic bonds with oxygen, these never act as network formers and can only modify structures created by network formers.

Bond strength was also suggested as an important factor in the formation of glasses. Sun argued that strong bonds were important for the formation of glasses as they prevent the reorganization of the material into a crystal structure during cooling, therefore facilitating glass formation. The bond strength he referred to could be given by the energy required to dissociate an oxide structure in the gaseous phase divided by the number of bonds. Although this model yielded results that were compatible with previous observations, it yielded no new insights into the formation of glass. Rawson argued that Sun ignored the importance of temperature in his model suggesting that higher melting points yields more energy for bond disruption whilst low temperatures afford less energy. He argued that a material with a low melting temperature and high bond strength would be a better glass former than a one with a similar bond strength but a much higher melting point. Although the application of this model to single cation oxides does little to improve the results of the application of the Sun model, it does predict the excellent glass forming property of boric oxide and extension to binary and ternary systems yields the prediction that the ease of glass formation should be improved for compositions near eutectics. This observation has often been made and is dubbed the "liquidus temperature effect". An example of this is the glass formation of the CaO-Al2O3 binary in a region near a eutectic.

Kinetic theories of glass formation

The structural theories of glass formation only consider the relative ease of glass formation. Materials which form glasses under a moderate cooling rate are called good glass formers, those that require a rapid cooling rate are called poor glass formers and those that require extreme cooling rates are referred to a non-glass formers. As it is now recognized that nearly any material is capable of forming a glass given the correct experimental conditions the focus of kinetic theories of glass formation is to identify how fast a system must be cooled to form a glass and avoid detectable crystallization, rather than whether or not a system will form a glass. [1]

Related Research Articles

<span class="mw-page-title-main">Ionic bonding</span> Chemical bonding involving attraction between ions

Ionic bonding is a type of chemical bonding that involves the electrostatic attraction between oppositely charged ions, or between two atoms with sharply different electronegativities, and is the primary interaction occurring in ionic compounds. It is one of the main types of bonding, along with covalent bonding and metallic bonding. Ions are atoms with an electrostatic charge. Atoms that gain electrons make negatively charged ions. Atoms that lose electrons make positively charged ions. This transfer of electrons is known as electrovalence in contrast to covalence. In the simplest case, the cation is a metal atom and the anion is a nonmetal atom, but these ions can be of a more complex nature, e.g. molecular ions like NH+
4 or SO2−
4. In simpler words, an ionic bond results from the transfer of electrons from a metal to a non-metal in order to obtain a full valence shell for both atoms.

<span class="mw-page-title-main">Silicon</span> Chemical element, symbol Si and atomic number 14

Silicon is a chemical element with the symbol Si and atomic number 14. It is a hard, brittle crystalline solid with a blue-grey metallic luster, and is a tetravalent metalloid and semiconductor. It is a member of group 14 in the periodic table: carbon is above it; and germanium, tin, lead, and flerovium are below it. It is relatively unreactive.

<span class="mw-page-title-main">Silicon dioxide</span> Oxide of silicon

Silicon dioxide, also known as silica, is an oxide of silicon with the chemical formula SiO2, most commonly found in nature as quartz and in various living organisms. In many parts of the world, silica is the major constituent of sand. Silica is one of the most complex and most abundant families of materials, existing as a compound of several minerals and as a synthetic product. Notable examples include fused quartz, fumed silica, silica gel, opal and aerogels. It is used in structural materials, microelectronics, and as components in the food and pharmaceutical industries.

<span class="mw-page-title-main">Ionic compound</span> Chemical compound involving ionic bonding

In chemistry, an ionic compound is a chemical compound composed of ions held together by electrostatic forces termed ionic bonding. The compound is neutral overall, but consists of positively charged ions called cations and negatively charged ions called anions. These can be simple ions such as the sodium (Na+) and chloride (Cl−) in sodium chloride, or polyatomic species such as the ammonium (NH+
4) and carbonate (CO2−
3) ions in ammonium carbonate. Individual ions within an ionic compound usually have multiple nearest neighbours, so are not considered to be part of molecules, but instead part of a continuous three-dimensional network. Ionic compounds usually form crystalline structures when solid.

An oxyanion, or oxoanion, is an ion with the generic formula A
xOz−
y. Oxyanions are formed by a large majority of the chemical elements. The formulae of simple oxyanions are determined by the octet rule. The corresponding oxyacid of an oxyanion is the compound H
zA
xO
y. The structures of condensed oxyanions can be rationalized in terms of AOn polyhedral units with sharing of corners or edges between polyhedra. The oxyanions adenosine monophosphate (AMP), adenosine diphosphate (ADP) and adenosine triphosphate (ATP) are important in biology.

The cubical atom was an early atomic model in which electrons were positioned at the eight corners of a cube in a non-polar atom or molecule. This theory was developed in 1902 by Gilbert N. Lewis and published in 1916 in the article "The Atom and the Molecule" and used to account for the phenomenon of valency. Lewis' theory was based on Abegg's rule. It was further developed in 1919 by Irving Langmuir as the cubical octet atom. The figure below shows structural representations for elements of the second row of the periodic table.

Ice I<sub>h</sub> Hexagonal crystal form of ordinary ice or frozen water

Ice Ih is the hexagonal crystal form of ordinary ice, or frozen water. Virtually all ice in the biosphere is ice Ih, with the exception only of a small amount of ice Ic that is occasionally present in the upper atmosphere. Ice Ih exhibits many peculiar properties that are relevant to the existence of life and regulation of global climate. For a description of these properties, see Ice, which deals primarily with ice Ih.

In chemistry, the valence or valency of an element is the measure of its combining capacity with other atoms when it forms chemical compounds or molecules.

<span class="mw-page-title-main">Bismuth(III) oxide</span> Chemical compound

Bismuth(III) oxide is perhaps the most industrially important compound of bismuth. It is also a common starting point for bismuth chemistry. It is found naturally as the mineral bismite (monoclinic) and sphaerobismoite, but it is usually obtained as a by-product of the smelting of copper and lead ores. Dibismuth trioxide is commonly used to produce the "Dragon's eggs" effect in fireworks, as a replacement of red lead.

The bond valencemethod or mean method is a popular method in coordination chemistry to estimate the oxidation states of atoms. It is derived from the bond valence model, which is a simple yet robust model for validating chemical structures with localized bonds or used to predict some of their properties. This model is a development of Pauling's rules.

<span class="mw-page-title-main">Glass-to-metal seal</span>

Glass-to-metal seals are a very important element of the construction of vacuum tubes, electric discharge tubes, incandescent light bulbs, glass encapsulated semiconductor diodes, reed switches, pressure tight glass windows in metal cases, Vacuum Insulating Glass and metal or ceramic packages of electronic components.

<span class="mw-page-title-main">Solid</span> State of matter

Solid is one of the four fundamental states of matter. The molecules in a solid are closely packed together and contain the least amount of kinetic energy. A solid is characterized by structural rigidity and resistance to a force applied to the surface. Unlike a liquid, a solid object does not flow to take on the shape of its container, nor does it expand to fill the entire available volume like a gas. The atoms in a solid are bound to each other, either in a regular geometric lattice, or irregularly. Solids cannot be compressed with little pressure whereas gases can be compressed with little pressure because the molecules in a gas are loosely packed.

<span class="mw-page-title-main">Chemical compound</span> Substance composed of multiple elements that are chemically bonded

A chemical compound is a chemical substance composed of many identical molecules containing atoms from more than one chemical element held together by chemical bonds. A molecule consisting of atoms of only one element is therefore not a compound. A compound can be transformed into a different substance by a chemical reaction, which may involve interactions with other substances. In this process, bonds between atoms may be broken and/or new bonds formed.

The glass–liquid transition, or glass transition, is the gradual and reversible transition in amorphous materials from a hard and relatively brittle "glassy" state into a viscous or rubbery state as the temperature is increased. An amorphous solid that exhibits a glass transition is called a glass. The reverse transition, achieved by supercooling a viscous liquid into the glass state, is called vitrification.

A network solid or covalent network solid is a chemical compound in which the atoms are bonded by covalent bonds in a continuous network extending throughout the material. In a network solid there are no individual molecules, and the entire crystal or amorphous solid may be considered a macromolecule. Formulas for network solids, like those for ionic compounds, are simple ratios of the component atoms represented by a formula unit.

Solids can be classified according to the nature of the bonding between their atomic or molecular components. The traditional classification distinguishes four kinds of bonding:

<span class="mw-page-title-main">Structure of liquids and glasses</span> Atomic-scale non-crystalline structure of liquids and glasses

The structure of liquids, glasses and other non-crystalline solids is characterized by the absence of long-range order which defines crystalline materials. Liquids and amorphous solids do, however, possess a rich and varied array of short to medium range order, which originates from chemical bonding and related interactions. Metallic glasses, for example, are typically well described by the dense random packing of hard spheres, whereas covalent systems, such as silicate glasses, have sparsely packed, strongly bound, tetrahedral network structures. These very different structures result in materials with very different physical properties and applications.

Gallium lanthanum sulfide glass is the name of a family of chalcogenide glasses, referred to as gallium lanthanum sulfide (Ga-La-S) glasses. They are mixtures of La2S3, La2O3, and Ga2S3, which form the basic glass with other glass modifiers added as needed. Gallium-lanthanum-sulfide glasses have a wide range of vitreous formation centered around a 70% Ga2S3 : 30% La2S3 mixture, and readily accept other modifier materials into their structure. This means that Ga-La-S composition can be adjusted to give a wide variety of optical and physical properties.

William Houlder Zachariasen, more often known as W. H. Zachariasen, was a Norwegian-American physicist, specializing in X-ray crystallography and famous for his work on the structure of glass.

Fluorine forms a great variety of chemical compounds, within which it always adopts an oxidation state of −1. With other atoms, fluorine forms either polar covalent bonds or ionic bonds. Most frequently, covalent bonds involving fluorine atoms are single bonds, although at least two examples of a higher order bond exist. Fluoride may act as a bridging ligand between two metals in some complex molecules. Molecules containing fluorine may also exhibit hydrogen bonding. Fluorine's chemistry includes inorganic compounds formed with hydrogen, metals, nonmetals, and even noble gases; as well as a diverse set of organic compounds. For many elements the highest known oxidation state can be achieved in a fluoride. For some elements this is achieved exclusively in a fluoride, for others exclusively in an oxide; and for still others the highest oxidation states of oxides and fluorides are always equal.

References

  1. ↑ Shelby, J. E. (2021). Introduction to glass science and technology (3rd ed.). London, UK. pp. 7–11. ISBN   978-1-83916-141-4. OCLC   1222776999.
This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.