Off-stoichiometry thiol-ene polymer

Last updated
Example of the curing process of the OSTE+ polymers. The respective properties of the polymer after 1st and 2nd cure. OSTEmer steps.png
Example of the curing process of the OSTE+ polymers. The respective properties of the polymer after 1st and 2nd cure.

An off-stoichiometry thiol-ene polymer is a polymer platform comprising off-stoichiometry thiol-enes (OSTE) and off-stoichiometry thiol-ene-epoxies (OSTE+).

Contents

The OSTE polymers comprise off-stoichiometry blends of thiols and allyls. After complete polymerization, typically by UV micromolding, the polymer articles contain a well-defined number of unreacted thiol or allyls groups both on the surface and in the bulk. These surface anchors can be used for subsequent direct surface modification or bonding. [1]

In later versions epoxy monomers were added to form ternary thiol-ene-epoxy monomer systems (OSTE+), where the epoxy in a second step reacts with the excess of thiols creating a final polymer article that is completely inert. [2] Some of the critical features of OSTE+ polymers include uncomplicated and rapid fabrication of complex structures in a standard chemistry labs, hydrophilic native surface properties and covalent bonding via latent epoxy chemistry. [3]

Development

The OSTE polymer resins were originally developed by Tommy Haraldsson and Fredrik Carlborg at the group of Micro and Nanosystems [4] at the Royal Institute of Technology (KTH) to bridge the gap between research prototyping and commercial production of microfluidics devices. [1] The resins were later adapted and improved for commercial applications by the Swedish start-up Mercene Labs AB under the name OSTEMER.

Reaction mechanism

The OSTE resins are cured via a rapid thiol-ene "Click" reaction between thiols and allyls. The thiols and allyls react in a perfectly alternating fashion and has a very high conversion rate (up to 99%), [5] the initial off-stoichiometry of the monomers will exactly define the number off unreacted groups left after the polymerization. With the right choice of monomers very high off-stoichiometry ratios can be attained while maintaining good mechanical properties. [1]

The off-stoichiometry thiol-ene-epoxies, or OSTE+ polymers, are created in a two-step curing process where a first rapid thiol-ene reaction defines the geometric shape of the polymer while leaving an excess of thiols and all the epoxy unreacted. In a second step all the remaining thiol groups and the epoxy groups are reacted to form an inert polymer. [6]

Properties

OSTE polymers

The main advantages put forward of the UV-cured OSTE polymers in microsystems have been their i) dry bonding capacity by reacting a polymer with thiol excess to a second polymer with allyl excess at room-temperature using only UV-light, ii) their well-defined and tunable number of surface anchors (thiols or allyls) present on the surface that can be used for direct surface modification [7] and iii) their wide tuning range of mechanical properties from rubbery to thermoplastic-like depending only on the choice of off-stoichiometry. [8] [1] The glass transition temperature typically varies from below room-temperature for high off-stoichiometric ratios to 75 °C for a stoichiometric blend of tetrathiol and triallyl. [9] They are typically transparent in the visible range. A disadvantage put forward with the OSTE-polymers is the leaching out of unreacted monomers at very high off-stoichiometric ratios which may affect cells and proteins in lab-on-chips, [1] although cell viability has been observed for cell cultures on low off-stoichiometric OSTE. [10]

OSTE+ polymers

The dual-cure thiol-ene-epoxies, or OSTE+ polymers, differ from the OSTE-polymers in that they have two separated curing steps. After the first UV-initiated step, the polymer is rubbery and can easily be deformed [11] and it has surface anchors available for surface modification. [12] During the second step, when all the thiols and epoxies are reacted the polymer stiffens and can bond to a wide number of substrates, including itself, via the epoxy chemistry. The advantages put forward for the OSTE+ are i) their unique ability for integration and bonding via the latent epoxy chemistry and the low built-in stresses in the thiol-enes polymers [13] ii) their complete inertness after final cure iii) their good barrier properties [14] and the possibility to scale up manufacturing using industrial reaction injection molding. [15] Both stiff and rubbery versions of the OSTE+ polymers have been demonstrated, showing their potential in microsystems for valving and pumping similar to PDMS components, but with the benefit of withstanding higher pressures. [11] The commercial version of the OSTE+ polymer, OSTEMER 322, has been shown to be compatible with many cell lines. [16]

Fabrication

OSTE polymers

The OSTE resins can be cast and cured in a structured silicone molds [1] or coated permanent photoresist. [17] OSTE polymers have also shown excellent photostructuring capability [18] using photomasks, enabling for example powerful and flexible capillary pumps. [19]

OSTE+ polymers

The OSTE+ resins are first UV-cured in the same way as the OSTE-polymers but are later thermally cured to stiffen and bond to a substrate.

Applications

Lab-on-a-chip

OSTE+ allows for soft lithography microstructuring, strong biocompatible dry bonding to almost any substrate during Lab-on-a-chip (LoC) manufacturing, while simultaneously mimicking the mechanical properties found in thermoplastic polymers, hence allowing for true prototyping of commercial LoC. [20] The commonly used materials for microfluidics suffer from unwieldy steps and often ineffective bonding processes, especially when packaging biofunctionalized surfaces, which makes LoC assembly difficult and costly [21] [22] OSTE+ polymer which effectively bonds to nine dissimilar types of substrates, requires no surface treatment prior to the bonding at room temperature, features high Tg, and achieves good bonding strength to at least 100 °C. [20] Moreover, it has been demonstrated that excellent results can be obtained using photolithography on OSTE polymer, opening wider potential applications. [23]

Bio packaging

Biosensors are used for a range of biological measurements. [24] [25]

OSTE packaging for biosensing has been demonstrated for QCM, [26] and photonic ring resonator sensors. [27]

Wafer bonding

Adhesive wafer bonding has become an established technology in microelectromechanical systems (MEMS) integration and packaging applications. [28] OSTE is suitable for heterogeneous silicon wafer level integration depending on its application in low temperature processes due to its ability to cure even in room temperatures. [29]

Microarray imprinting and surface energy patterning

Imprinting of arrays with hydrophilic-in-hydrophobic microwells is made possible using an innovative surface energy replication approach by means of a hydrophobic thiol-ene polymer formulation. In this polymer, hydrophobic-moiety-containing monomers self-assemble at the hydrophobic surface of the imprinting stamp, which results in a hydrophobic replica surface after polymerization. After removing the stamp, microwells with hydrophobic walls and a hydrophilic bottom are obtained. Such fast and inexpensive procedure can be utilised in digital microwell array technology toward diagnostic applications. [30] [31]

OSTE e-beam resist

OSTE resin can also be used as e-beam resist, resulting in nanostructures that allow direct protein functionalization. [32]

Related Research Articles

<span class="mw-page-title-main">Microfluidics</span> Interdisciplinary science

Microfluidics refers to a system that manipulates a small amount of fluids using small channels with sizes ten to hundreds micrometres. It is a multidisciplinary field that involves molecular analysis, molecular biology, and microelectronics. It has practical applications in the design of systems that process low volumes of fluids to achieve multiplexing, automation, and high-throughput screening. Microfluidics emerged in the beginning of the 1980s and is used in the development of inkjet printheads, DNA chips, lab-on-a-chip technology, micro-propulsion, and micro-thermal technologies.

<span class="mw-page-title-main">Photoresist</span> Light-sensitive material used in making electronics

A photoresist is a light-sensitive material used in several processes, such as photolithography and photoengraving, to form a patterned coating on a surface. This process is crucial in the electronics industry.

<span class="mw-page-title-main">Microarray</span> Small-scale two-dimensional array of samples on a solid support

A microarray is a multiplex lab-on-a-chip. Its purpose is to simultaneously detect the expression of thousands of biological interactions. It is a two-dimensional array on a solid substrate—usually a glass slide or silicon thin-film cell—that assays (tests) large amounts of biological material using high-throughput screening miniaturized, multiplexed and parallel processing and detection methods. The concept and methodology of microarrays was first introduced and illustrated in antibody microarrays by Tse Wen Chang in 1983 in a scientific publication and a series of patents. The "gene chip" industry started to grow significantly after the 1995 Science Magazine article by the Ron Davis and Pat Brown labs at Stanford University. With the establishment of companies, such as Affymetrix, Agilent, Applied Microarrays, Arrayjet, Illumina, and others, the technology of DNA microarrays has become the most sophisticated and the most widely used, while the use of protein, peptide and carbohydrate microarrays is expanding.

<span class="mw-page-title-main">Epoxy</span> Type of material

Epoxy is the family of basic components or cured end products of epoxy resins. Epoxy resins, also known as polyepoxides, are a class of reactive prepolymers and polymers which contain epoxide groups. The epoxide functional group is also collectively called epoxy. The IUPAC name for an epoxide group is an oxirane.

A lab-on-a-chip (LOC) is a device that integrates one or several laboratory functions on a single integrated circuit of only millimeters to a few square centimeters to achieve automation and high-throughput screening. LOCs can handle extremely small fluid volumes down to less than pico-liters. Lab-on-a-chip devices are a subset of microelectromechanical systems (MEMS) devices and sometimes called "micro total analysis systems" (μTAS). LOCs may use microfluidics, the physics, manipulation and study of minute amounts of fluids. However, strictly regarded "lab-on-a-chip" indicates generally the scaling of single or multiple lab processes down to chip-format, whereas "μTAS" is dedicated to the integration of the total sequence of lab processes to perform chemical analysis.

<span class="mw-page-title-main">Polydimethylsiloxane</span> Chemical compound

Polydimethylsiloxane (PDMS), also known as dimethylpolysiloxane or dimethicone, is a silicone polymer with a wide variety of uses, from cosmetics to industrial lubrication and passive daytime radiative cooling.

Nanolithography (NL) is a growing field of techniques within nanotechnology dealing with the engineering of nanometer-scale structures on various materials.

<span class="mw-page-title-main">Nanoimprint lithography</span> Method of fabricating nanometer scale patterns using a special stamp

Nanoimprint lithography (NIL) is a method of fabricating nanometer-scale patterns. It is a simple nanolithography process with low cost, high throughput and high resolution. It creates patterns by mechanical deformation of imprint resist and subsequent processes. The imprint resist is typically a monomer or polymer formulation that is cured by heat or UV light during the imprinting. Adhesion between the resist and the template is controlled to allow proper release.

<span class="mw-page-title-main">SU-8 photoresist</span> Epoxy-based polymer

SU-8 is a commonly used epoxy-based negative photoresist. Negative refers to a photoresist whereby the parts exposed to UV become cross-linked, while the remainder of the film remains soluble and can be washed away during development.

<span class="mw-page-title-main">Photopolymer</span>

A photopolymer or light-activated resin is a polymer that changes its properties when exposed to light, often in the ultraviolet or visible region of the electromagnetic spectrum. These changes are often manifested structurally, for example hardening of the material occurs as a result of cross-linking when exposed to light. An example is shown below depicting a mixture of monomers, oligomers, and photoinitiators that conform into a hardened polymeric material through a process called curing.

<span class="mw-page-title-main">Micropatterning</span>

Micropatterning is the art of miniaturisation of patterns. Especially used for electronics, it has recently become a standard in biomaterials engineering and for fundamental research on cellular biology by mean of soft lithography. It generally uses photolithography methods but many techniques have been developed.

<span class="mw-page-title-main">Epichlorohydrin</span> Chemical compound

Epichlorohydrin is an organochlorine compound and an epoxide. Despite its name, it is not a halohydrin. It is a colorless liquid with a pungent, garlic-like odor, moderately soluble in water, but miscible with most polar organic solvents. It is a chiral molecule generally existing as a racemic mixture of right-handed and left-handed enantiomers. Epichlorohydrin is a highly reactive electrophilic compound and is used in the production of glycerol, plastics, epoxy glues and resins, epoxy diluents and elastomers.

<span class="mw-page-title-main">Lateral flow test</span> Immunochromatographic testing devices

A lateral flow test (LFT), is an assay also known as a lateral flow device (LFD), lateral flow immunochromatographic assay, or rapid test. It is a simple device intended to detect the presence of a target substance in a liquid sample without the need for specialized and costly equipment. LFTs are widely used in medical diagnostics in the home, at the point of care, and in the laboratory. For instance, the home pregnancy test is an LFT that detects a specific hormone. These tests are simple and economical and generally show results in around five to thirty minutes. Many lab-based applications increase the sensitivity of simple LFTs by employing additional dedicated equipment. Because the target substance is often a biological antigen, many lateral flow tests are rapid antigen tests.

Adhesive bonding describes a wafer bonding technique with applying an intermediate layer to connect substrates of different types of materials. Those connections produced can be soluble or insoluble. The commercially available adhesive can be organic or inorganic and is deposited on one or both substrate surfaces. Adhesives, especially the well-established SU-8, and benzocyclobutene (BCB), are specialized for MEMS or electronic component production.

<span class="mw-page-title-main">Micropump</span>

Micropumps are devices that can control and manipulate small fluid volumes. Although any kind of small pump is often referred to as a micropump, a more accurate definition restricts this term to pumps with functional dimensions in the micrometer range. Such pumps are of special interest in microfluidic research, and have become available for industrial product integration in recent years. Their miniaturized overall size, potential cost and improved dosing accuracy compared to existing miniature pumps fuel the growing interest for this innovative kind of pump.

Polymeric materials have widespread application due to their versatile characteristics, cost-effectiveness, and highly tailored production. The science of polymer synthesis allows for excellent control over the properties of a bulk polymer sample. However, surface interactions of polymer substrates are an essential area of study in biotechnology, nanotechnology, and in all forms of coating applications. In these cases, the surface characteristics of the polymer and material, and the resulting forces between them largely determine its utility and reliability. In biomedical applications for example, the bodily response to foreign material, and thus biocompatibility, is governed by surface interactions. In addition, surface science is integral part of the formulation, manufacturing, and application of coatings.

Expanding monomers are monomers which increase in volume (expand) during polymerization. They can be added to monomer formulations to counteract the usual volume shrinking to manufacture products with higher quality and durability. Volume Shrinkage is in first line for the unmeltable thermosets a problem, since those are of fixed shape after polymerization completed.

In organosulfur chemistry, the thiol-ene reaction is an organic reaction between a thiol and an alkene to form a thioether. This reaction was first reported in 1905, but it gained prominence in the late 1990s and early 2000s for its feasibility and wide range of applications. This reaction is accepted as a click chemistry reaction given the reactions' high yield, stereoselectivity, high rate, and thermodynamic driving force.

A microvalve is a microscale valve, i.e. a microfluidic two-port component that regulates the flow between two fluidic ports. Microvalves are basic components in microfluidic devices, such as labs-on-a-chip, where they are used to control the fluidic transport. During the period from 1995 to 2005, many microelectromechanical systems-based microvalves were developed.

Solvent bonding is not a method of adhesive bonding, but rather a method of fusing two thermoplastic plastics. Application of a solvent to a thermoplastic material softens the polymer, and with applied pressure this results in polymer chain interdiffusion at the bonding junction. When the solvent evaporates, this leaves a fully consolidated bond-line. An advantage to solvent bonding versus other polymer joining methods is that bonding generally occurs below the glass transition temperature of the polymer.

References

  1. 1 2 3 4 5 6 Carlborg, Carl Fredrik; Haraldsson, Tommy; Öberg, Kim; Malkoch, Michael; van der Wijngaart, Wouter (2011). "Beyond PDMS: off-stoichiometry thiol–ene (OSTE) based soft lithography for rapid prototyping of microfluidic devices". Lab on a Chip. 11 (18): 3136–47. doi:10.1039/c1lc20388f. ISSN   1473-0197. PMID   21804987.
  2. ↑ Saharil, Farizah; Carlborg, Carl Fredrik; Haraldsson, Tommy; van der Wijngaart, Wouter (2012). "Biocompatible "click" wafer bonding for microfluidic devices". Lab on a Chip. 12 (17): 3032–5. doi:10.1039/c2lc21098c. ISSN   1473-0197. PMID   22760578.
  3. ↑ Vastesson, Proc. IEEE Transducers 2013 Barcelona, 408-411 (2013)
  4. ↑ MICROFLUIDICS & LAB-ON-CHIP
  5. ↑ Hoyle, Charles E. (2010). "Thiol-Ene Click Chemistry". Angewandte Chemie International Edition. 49 (9): 1540–1573. doi:10.1002/anie.200903924. PMID   20166107.
  6. ↑ Saharil, Journal of Micromechanics and Microengineering 23, 025021 (2013)
  7. ↑ BIOMICROFLUIDICS 6, 016505 (2012)
  8. ↑ Lafleur , Analyst 138, 845-849 (2013)
  9. ↑ Archived 2014-03-01 at the Wayback Machine OSTE+ Official datasheet
  10. ↑ Errando-Herranz, Proc. MicroTAS 2013 Freiburg, (2013)
  11. 1 2 Hansson, Proc. IEEE MEMS 2014 San Francisco, (2014)
  12. ↑ Zhou, Proc. MicroTAS 2013 Freiburg, (2013)
  13. ↑ Hoyle, Charles E. (2004). "Thiol-enes: Chemistry of the past with promise for the future". Journal of Polymer Science Part A: Polymer Chemistry. 42 (21): 5301–5338. Bibcode:2004JPoSA..42.5301H. doi:10.1002/pola.20366.
  14. ↑ Saharil, Journal of Micromechanics and Microengineering 23, 025021 (2013)
  15. ↑ Sandström, N; Shafagh, R Z; Vastesson, A; Carlborg, C F; Wijngaart, W van der; Haraldsson, T (2015). "Reaction injection molding and direct covalent bonding of OSTE+ polymer microfluidic devices". Journal of Micromechanics and Microengineering. 25 (7): 075002. Bibcode:2015JMiMi..25g5002S. doi:10.1088/0960-1317/25/7/075002. S2CID   53682690.
  16. ↑ Sticker, Drago; Rothbauer, Mario; Lechner, Sarah; Hehenberger, Marie-Therese; Ertl, Peter (2015-11-24). "Multi-layered, membrane-integrated microfluidics based on replica molding of a thiol–ene epoxy thermoset for organ-on-a-chip applications". Lab Chip. 15 (24): 4542–4554. doi:10.1039/c5lc01028d. ISSN   1473-0189. PMID   26524977.
  17. ↑ Fredrik, Carlborg, Carl; M., Cretich; Tommy, Haraldsson; L., Sola; M., Bagnati; M., Chiari; Wouter, van der Wijngaart (2011-01-01). Biosticker : patterned microfluidic stickers for rapid integration with microarrays. The 15th International Conference on Miniaturized Systems for Chemistry and Life Sciences. pp. 311–313.{{cite conference}}: CS1 maint: multiple names: authors list (link)
  18. ↑ Hillmering, Mikael; Pardon, Gaspard; Vastesson, Alexander; Supekar, Omkar; Carlborg, Carl Fredrik; Brandner, Birgit D.; Wijngaart, Wouter van der; Haraldsson, Tommy (2016-02-15). "Off-stoichiometry improves the photostructuring of thiol–enes through diffusion-induced monomer depletion". Microsystems & Nanoengineering. 2: 15043. doi:10.1038/micronano.2015.43. ISSN   2055-7434. PMC   6444721 . PMID   31057810.
  19. ↑ Hansson, Jonas; Yasuga, Hiroki; Haraldsson, Tommy; Wijngaart, Wouter van der (2016-01-05). "Synthetic microfluidic paper: high surface area and high porosity polymer micropillar arrays". Lab Chip. 16 (2): 298–304. doi:10.1039/c5lc01318f. ISSN   1473-0189. PMID   26646057.
  20. 1 2 Saharil, Farizah; Carlborg, Carl Fredrik; Haraldsson, Tommy; Van Der Wijngaart, Wouter (2012). "Biocompatible "click" wafer bonding for microfluidic devices". Lab on a Chip. 12 (17): 3032–3035. doi:10.1039/C2LC21098C. PMID   22760578.
  21. ↑ Eddings, Mark A.; Johnson, Michael A.; Gale, Bruce K. (2008). "Determining the optimal PDMS–PDMS bonding technique for microfluidic devices". Journal of Micromechanics and Microengineering. 18 (6). doi:10.1088/0960-1317/18/6/067001.
  22. ↑ Kalkandjiev, K.; Riegger, L.; Kosse, D.; Welsche, M.; Gutzweiler, L.; Zengerle, R.; Koltay, P. (2011). "Microfluidics in silicon/Polymer technology as a cost-efficient alternative to silicon/Glass" (PDF). Journal of Micromechanics and Microengineering. 21 (2): 025008. Bibcode:2011JMiMi..21b5008K. doi:10.1088/0960-1317/21/2/025008.
  23. ↑ Pardon, Gaspard; Saharil, Farizah; Karlsson, J. Mikael; Supekar, Omkar; Carlborg, Carl Fredrik; Van Der Wijngaart, Wouter; Haraldsson, Tommy (2014). "Rapid mold-free manufacturing of microfluidic devices with robust and spatially directed surface modifications". Microfluidics and Nanofluidics. 17 (4): 773–779. doi:10.1007/s10404-014-1351-9.
  24. ↑ Homola, Chemical Reviews, 108 (2), 462–493, 2008
  25. ↑ Carlborg, Proc. MicroTAS 2011 Seatle, 311-313 (2011)
  26. ↑ Sandström, Proc. IEEE Transducers 2011 Beijing, 2778-2781 (2011)
  27. ↑ Errando-Herranz, Opt. Express 21, 21293 (2013)
  28. ↑ Niklaus F, Stemme G, Lu J-Q and Gutmann R J 2006 Adhesive wafer bonding J. Appl. Phys. 99 03110
  29. ↑ [ permanent dead link ] Forsberg, Journal of Micromechanics and Microengineering 23, 085019 (2013)
  30. ↑ Decrop, Deborah; Pardon, Gaspard; Shafagh, Reza; Spacic, Dragana; van der Wijngaart, Wouter; Lammertyn, Jeroen; Haraldsson, Tommy (2017). "Single-Step Imprinting of Femtoliter Microwell Arrays Allows Digital Bioassays with Attomolar Limit of Detection". ACS Applied Materials & Interfaces. 9 (12): 10418–10426. doi:10.1021/acsami.6b15415. PMID   28266828.
  31. ↑ Shafagh, Reza; Decrop, Deborah; Ven, Karen; Vanderbeke, Arno; Hanusa, Robert; Pardon, Gaspard; Haraldsson, Tommy; Lammertyn, Jeroen; van der Wijngaart, Wouter (2019). "Reaction injection molding of hydrophilic-in-hydrophobic femtolitre-well arrays". Microsystems & Nanoengineering. 5 (25): 25. Bibcode:2019MicNa...5...25Z. doi:10.1038/s41378-019-0065-2. PMC   6545322 . PMID   31231538.
  32. ↑ Shafagh, Reza; Vastesson, Alexander; Guo, Weijin; van der Wijngaart, Wouter; Haraldsson, Tommy (2018). "E-Beam Nanostructuring and Direct Click Biofunctionalization of Thiol–Ene Resist". ACS Nano. 12 (10): 9940–9946. doi:10.1021/acsnano.8b03709. PMID   30212184. S2CID   52271550.
This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.