An aquamelt is a naturally hydrated polymeric material that is able to solidify at environmental temperatures through a controlled stress input (be it mechanical or chemical).

Contents

They are unique in being able to “lock in” work applied to them through an alteration in hydrogen bonding, which enables them to be processed with approximately 1000 times less energy than standard polymers. [1] This has been recently shown for an archetypal biopolymer, silk, [2] however the mechanism for solidification is thought to be inherent to many other biological materials. [3] [4]

Discovery and mechanism

Aquamelts were defined as a new class of polymeric material as a result of a comparison between the spinning feedstock of the Chinese silkworm ( Bombyx mori ) and molten high-density polyethylene (HDPE) [2] using shear induced polarised light imaging (SIPLI). [5]

The current understanding of shear induced fibrillation requires polymer chains to undergo the following series of steps i) long-chain molecules are stretched, ii) and form persistent point nuclei, which iii) align under flow into rows and then iv) grow to create a crystalline fibrils. [2] For these fibrils to remain, the temperature of the sample must be lowered to below the polymers melt point. This process is analogous to the fibrilogenesis of natural silk-polymers in which proteins align (refold), nucleate (denature), and crystallize (aggregate). However, for silks, fibrils persist without the need for a drop in temperature. [6] [7]

From a macromolecular perspective the two processes are thought to be similar due to a native protein's unique interaction with its closely bound water. [3] [4] Much like an individual polymer chain in a melt, a native protein and its closely bound water molecules may be considered not as a solution but as a single processable entity, a nanocomposite termed an "aquamelt".

The differences between a typical polymer and an aquamelt are highlighted by an aquamelt's ability to solidify in response to stress at environmental temperatures. This occurs when the stress applied is sufficient to separate the closely bound water from the protein, splitting the nanocomposite. This results in conformational changes to the protein and an increased probability to form hydrogen bonding between protein chains and subsequent solidification. [4] Multiscale structures, i.e., fibrils or foams are the result of a combination of directional stress fields and the self-assembly properties of the aquamelt. [7] [8]

Potential uses

Aquamelts offer several advantages over current solutions to synthetic polymer production. Firstly they are naturally sourced, with no reliance on oil for production and are recyclable and biodegradable. Secondly they can be processed at room temperatures and pressures resulting in only water as a by-product from the solidification process. Thirdly work calculations performed on silk and high-density polyethylene feedstocks revealed a tenfold difference in the amount of shear energy required in order to initiate solidification. [9] When processing temperature is taken into account the difference in energy requirements to undergo solidification is a thousandfold less for aquamelts than synthetic polymers. [1]

Related Research Articles

<span class="mw-page-title-main">Biopolymer</span> Polymer produced by a living organism

Biopolymers are natural polymers produced by the cells of living organisms. Like other polymers, biopolymers consist of monomeric units that are covalently bonded in chains to form larger molecules. There are three main classes of biopolymers, classified according to the monomers used and the structure of the biopolymer formed: polynucleotides, polypeptides, and polysaccharides. The Polynucleotides, RNA and DNA, are long polymers of nucleotides. Polypeptides include proteins and shorter polymers of amino acids; some major examples include collagen, actin, and fibrin. Polysaccharides are linear or branched chains of sugar carbohydrates; examples include starch, cellulose, and alginate. Other examples of biopolymers include natural rubbers, suberin and lignin, cutin and cutan, melanin, and polyhydroxyalkanoates (PHAs).

<span class="mw-page-title-main">Cellulose</span> Polymer of glucose and structural component of cell wall of plants and green algae

Cellulose is an organic compound with the formula (C
6H
10O
5)
n, a polysaccharide consisting of a linear chain of several hundred to many thousands of β(1→4) linked D-glucose units. Cellulose is an important structural component of the primary cell wall of green plants, many forms of algae and the oomycetes. Some species of bacteria secrete it to form biofilms. Cellulose is the most abundant organic polymer on Earth. The cellulose content of cotton fiber is 90%, that of wood is 40–50%, and that of dried hemp is approximately 57%.

<span class="mw-page-title-main">Polymer</span> Substance composed of macromolecules with repeating structural units

A polymer (;) is a substance or material consisting of very large molecules called macromolecules, composed of many repeating subunits. Due to their broad spectrum of properties, both synthetic and natural polymers play essential and ubiquitous roles in everyday life. Polymers range from familiar synthetic plastics such as polystyrene to natural biopolymers such as DNA and proteins that are fundamental to biological structure and function. Polymers, both natural and synthetic, are created via polymerization of many small molecules, known as monomers. Their consequently large molecular mass, relative to small molecule compounds, produces unique physical properties including toughness, high elasticity, viscoelasticity, and a tendency to form amorphous and semicrystalline structures rather than crystals.

<span class="mw-page-title-main">Spider silk</span> Protein fiber made by spiders

Spider silk is a protein fibre or silk spun by spiders. Spiders use silk to make webs or other structures that function as adhesive traps to catch prey, to entangle and restrain prey before biting, to transmit tactile information, or as nests or cocoons to protect their offspring. They can use the silk to suspend themselves from height, to float through the air, or to glide away from predators. Most spiders vary the thickness and adhesiveness of their silk according to its use.

<span class="mw-page-title-main">Fiber</span> Natural or synthetic substance made of long, thin filaments

Fiber or fibre is a natural or artificial substance that is significantly longer than it is wide. Fibers are often used in the manufacture of other materials. The strongest engineering materials often incorporate fibers, for example carbon fiber and ultra-high-molecular-weight polyethylene.

<span class="mw-page-title-main">Polymer degradation</span> Alteration in the polymer properties under the influence of environmental factors

Polymer degradation is the reduction in the physical properties of a polymer, such as strength, caused by changes in its chemical composition. Polymers and particularly plastics are subject to degradation at all stages of their product life cycle, including during their initial processing, use, disposal into the environment and recycling. The rate of this degradation varies significantly; biodegradation can take decades, whereas some industrial processes can completely decompose a polymer in hours.

Polymer chemistry is a sub-discipline of chemistry that focuses on the structures of chemicals, chemical synthesis, and chemical and physical properties of polymers and macromolecules. The principles and methods used within polymer chemistry are also applicable through a wide range of other chemistry sub-disciplines like organic chemistry, analytical chemistry, and physical chemistry. Many materials have polymeric structures, from fully inorganic metals and ceramics to DNA and other biological molecules. However, polymer chemistry is typically related to synthetic and organic compositions. Synthetic polymers are ubiquitous in commercial materials and products in everyday use, such as plastics, and rubbers, and are major components of composite materials. Polymer chemistry can also be included in the broader fields of polymer science or even nanotechnology, both of which can be described as encompassing polymer physics and polymer engineering.

<span class="mw-page-title-main">Polyacetylene</span> Organic polymer made of the repeating unit [C2H2]

Polyacetylene usually refers to an organic polymer with the repeating unit [C2H2]n. The name refers to its conceptual construction from polymerization of acetylene to give a chain with repeating olefin groups. This compound is conceptually important, as the discovery of polyacetylene and its high conductivity upon doping helped to launch the field of organic conductive polymers. The high electrical conductivity discovered by Hideki Shirakawa, Alan Heeger, and Alan MacDiarmid for this polymer led to intense interest in the use of organic compounds in microelectronics. This discovery was recognized by the Nobel Prize in Chemistry in 2000. Early work in the field of polyacetylene research was aimed at using doped polymers as easily processable and lightweight "plastic metals". Despite the promise of this polymer in the field of conductive polymers, many of its properties such as instability to air and difficulty with processing have led to avoidance in commercial applications.

<span class="mw-page-title-main">Hydrogel</span> Soft water-rich polymer gel

A hydrogel is a biphasic material, a mixture of porous, permeable solids and at least 10% by weight or volume of interstitial fluid composed completely or mainly by water. In hydrogels the porous permeable solid is a water insoluble three dimensional network of natural or synthetic polymers and a fluid, having absorbed a large amount of water or biological fluids. These properties underpin several applications, especially in the biomedical area. Many hydrogels are synthetic, but some are derived from nature. The term 'hydrogel' was coined in 1894.

<span class="mw-page-title-main">Crazing</span> Fine cracks on the surface of a material

Crazing is the phenomenon that produces a network of fine cracks on the surface of a material, for example in a glaze layer. Crazing frequently precedes fracture in some glassy thermoplastic polymers. As it only takes place under tensile stress, the plane of the crazing corresponds to the stress direction. The effect is visibly distinguishable from other types of fine cracking because the crazing region has different refractive indices from surrounding material. Crazing occurs in regions of high hydrostatic tension, or in regions of very localized yielding, which leads to the formation of interpenetrating microvoids and small fibrils. If an applied tensile load is sufficient, these bridges elongate and break, causing the microvoids to grow and coalesce; as microvoids coalesce, cracks begin to form.

<span class="mw-page-title-main">Fibril</span> Thin Fibre

Fibrils are structural biological materials found in nearly all living organisms. Not to be confused with fibers or filaments, fibrils tend to have diameters ranging from 10–100 nanometers. Fibrils are not usually found alone but rather are parts of greater hierarchical structures commonly found in biological systems. Due to the prevalence of fibrils in biological systems, their study is of great importance in the fields of microbiology, biomechanics, and materials science.

<span class="mw-page-title-main">Bioplastic</span> Plastics derived from renewable biomass sources

Bioplastics are plastic materials produced from renewable biomass sources, such as vegetable fats and oils, corn starch, straw, woodchips, sawdust, recycled food waste, etc. Some bioplastics are obtained by processing directly from natural biopolymers including polysaccharides and proteins, while others are chemically synthesised from sugar derivatives and lipids from either plants or animals, or biologically generated by fermentation of sugars or lipids. In contrast, common plastics, such as fossil-fuel plastics are derived from petroleum or natural gas.

A polyolefin is a type of polymer with the general formula (CH2CHR)n where R is an alkyl group. They are usually derived from a small set of simple olefins (alkenes). Dominant in a commercial sense are polyethylene and polypropylene. More specialized polyolefins include polyisobutylene and polymethylpentene. They are all colorless or white oils or solids. Many copolymers are known, such as polybutene, which derives from a mixture of different butene isomers. The name of each polyolefin indicates the olefin from which it is prepared; for example, polyethylene is derived from ethylene, and polymethylpentene is derived from 4-methyl-1-pentene. Polyolefins are not olefins themselves because the double bond of each olefin monomer is opened in order to form the polymer. Monomers having more than one double bond such as butadiene and isoprene yield polymers that contain double bonds (polybutadiene and polyisoprene) and are usually not considered polyolefins. Polyolefins are the foundations of many chemical industries.

<span class="mw-page-title-main">Natural fiber</span> Fibers obtained from natural sources such as plants, animals or minerals without synthesis

Natural fibers or natural fibres are fibers that are produced by geological processes, or from the bodies of plants or animals. They can be used as a component of composite materials, where the orientation of fibers impacts the properties. Natural fibers can also be matted into sheets to make paper or felt.

<span class="mw-page-title-main">Nanofiber</span>

Nanofibers are fibers with diameters in the nanometer range. Nanofibers can be generated from different polymers and hence have different physical properties and application potentials. Examples of natural polymers include collagen, cellulose, silk fibroin, keratin, gelatin and polysaccharides such as chitosan and alginate. Examples of synthetic polymers include poly(lactic acid) (PLA), polycaprolactone (PCL), polyurethane (PU), poly(lactic-co-glycolic acid) (PLGA), poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV), and poly(ethylene-co-vinylacetate) (PEVA). Polymer chains are connected via covalent bonds. The diameters of nanofibers depend on the type of polymer used and the method of production. All polymer nanofibers are unique for their large surface area-to-volume ratio, high porosity, appreciable mechanical strength, and flexibility in functionalization compared to their microfiber counterparts.

Polymer nanocomposites (PNC) consist of a polymer or copolymer having nanoparticles or nanofillers dispersed in the polymer matrix. These may be of different shape, but at least one dimension must be in the range of 1–50 nm. These PNC's belong to the category of multi-phase systems that consume nearly 95% of plastics production. These systems require controlled mixing/compounding, stabilization of the achieved dispersion, orientation of the dispersed phase, and the compounding strategies for all MPS, including PNC, are similar. Alternatively, polymer can be infiltrated into 1D, 2D, 3D preform creating high content polymer nanocomposites.

Rubber toughening is a process in which rubber nanoparticles are interspersed within a polymer matrix to increase the mechanical robustness, or toughness, of the material. By "toughening" a polymer it is meant that the ability of the polymeric substance to absorb energy and plastically deform without fracture is increased. Considering the significant advantages in mechanical properties that rubber toughening offers, most major thermoplastics are available in rubber-toughened versions; for many engineering applications, material toughness is a deciding factor in final material selection.

<span class="mw-page-title-main">Nanocellulose</span> Material composed of nanosized cellulose fibrils

Nanocellulose is a term referring to nano-structured cellulose. This may be either cellulose nanocrystal, cellulose nanofibers (CNF) also called nanofibrillated cellulose (NFC), or bacterial nanocellulose, which refers to nano-structured cellulose produced by bacteria.

Bio-inks are materials used to produce engineered/artificial live tissue using 3D printing. These inks are mostly composed of the cells that are being used, but are often used in tandem with additional materials that envelope the cells. The combination of cells and usually biopolymer gels are defined as a bio-ink. They must meet certain characteristics, including such as rheological, mechanical, biofunctional and biocompatibility properties, among others. Using bio-inks provides a high reproducibility and precise control over the fabricated constructs in an automated manner. These inks are considered as one of the most advanced tools for tissue engineering and regenerative medicine (TERM).

Covalent adaptable networks (CANs) are a type of polymer material that closely resemble thermosetting polymers (thermosets). However, they are distinguished from thermosets by the incorporation of dynamic covalent chemistry into the polymer network. When a stimulus (for example heat, light, pH, ...) is applied to the material, these dynamic bonds become active and can be broken or exchanged with other pending functional groups, allowing the polymer network to change its topology. This introduces reshaping, (re)processing and recycling into thermoset-like materials.

References

  1. 1 2 "How Silkworms Beat Polymer Scientists - The Aquamelt Secret". Science Debate. 25 November 2011. Retrieved 10 April 2012.
  2. 1 2 3 Holland, C; Vollrath, F; Ryan, A; Mykhaylyk, O (2012). "Silk and Synthetic Polymers: Reconciling 100 Degrees of Separation". Advanced Materials. 24 (1): 105–109. doi:10.1002/adma.201103664. PMID   22109705.
  3. 1 2 Porter, D; Vollrath, F (2008). "The role of kinetics of water and amide bonding in protein stability". Soft Matter. 4 (1): 328–336. Bibcode:2008SMat....4..328P. doi:10.1039/B713972A.
  4. 1 2 3 Porter, D; Vollrath, F (2012). "Water mobility, denaturation and the glass transition in proteins". Biochimica et Biophysica Acta (BBA) - Proteins and Proteomics. 1824 (6): 785–791. doi:10.1016/j.bbapap.2012.03.007. PMID   22465032.
  5. ↑ Mykhaylyk, O (2010). "Time-resolved polarized light imaging of sheared materials: application to polymer crystallization". Soft Matter. 6 (18): 4430–4440. Bibcode:2010SMat....6.4430M. doi:10.1039/C0SM00332H.
  6. ↑ Boulet-Audet, M; Vollrath, F; Holland, C (2011). "Rheo-attenuated total reflectance infrared spectroscopy: a new tool to study biopolymers". Physical Chemistry Chemical Physics. 13 (9): 3979–3984. Bibcode:2011PCCP...13.3979B. doi:10.1039/C0CP02599B. PMID   21240437.
  7. 1 2 Holland, C; Urbach, J; Blair, D (2012). "Direct Visualization of Shear Dependent Silk Fibrillogenesis" (PDF). Soft Matter. 8 (9): 2590–2594. Bibcode:2012SMat....8.2590H. doi:10.1039/C2SM06886A. S2CID   97800780. Archived from the original (PDF) on 2019-12-20.
  8. ↑ Guan, J; Porter, D; K, Tian; Zhengzhong, S; Chen, X (2010). "Morphology and mechanical properties of soy protein scaffolds made by directional freezing". Journal of Applied Polymer Science. 118 (3): 328–336. doi:10.1002/app.32579.
  9. ↑ Chelsea Whyte (23 November 2011). "Face-to-face with the super-efficient silkworm". New Scientist. Archived from the original on 27 December 2011. Retrieved 10 April 2012.
This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.