Carbon nanotube springs are springs made of carbon nanotubes (CNTs). They are an alternate form of high-density, lightweight, reversible energy storage based on the elastic deformations of CNTs. Many previous studies on the mechanical properties of CNTs have revealed that they possess high stiffness, strength and flexibility. The Young's modulus of CNTs is 1 TPa and they have the ability to sustain reversible tensile strains of 6% [1] and the mechanical springs based on these structures are likely to surpass the current energy storage capabilities of existing steel springs and provide a viable alternative to electrochemical batteries. The obtainable energy density is predicted to be highest under tensile loading, with an energy density in the springs themselves about 2500 times greater than the energy density that can be reached in steel springs, and 10 times greater than the energy density of lithium-ion batteries.
The process of elastic energy storage in a CNT involves deforming it under an applied load. On removal of the applied load the energy released from the CNT can be used to perform mechanical work. A CNT has the ability to deform reversibly and a spring made from it can undergo repeated charge-discharge cycles without fatigue.
A CNT spring can store elastic strain energy with a density several orders of magnitude higher than conventional springs made of steel. Strain energy density in a material is proportional to the product of its Young's modulus and the square of the applied strain.
When multi-walled nanotubes (MWCNTs) are loaded, the majority of the applied load is borne by the outer shell. Owing to this limited load transfer between the different layers of MWCNTs, single walled nanotubes (SWCNTs) are more useful structural materials for springs.
Springs for energy storage can be made of SWCNTs or MWCNTs arranged in dense bundles of long, aligned tubes called "forests" of CNTs [2] that are grown by chemical vapor deposition (CVD). The "forests" can grow to heights of up to 6 millimeters. [3] A deformed CNT requires a support structure to carry the load of the spring prior to discharge. A mechanical spring must be coupled to external mechanisms to build a power source that is functionally useful. On its own a spring stores potential energy when an external force is applied to it, but releases the energy in a single rapid burst once the force is removed. An effective power source needs to store energy over a period of time, release the energy only when needed and discharge the energy at a desired power level. A CNT based portable power source should have a basic architecture made of four main components, namely a CNT spring, a supporting structure for the spring, a generator-motor combination, and a coupling mechanism between the spring and the generator.
For CNTs arranged in groups/bundles called "forests" as described earlier, efficient packing and good alignment in necessary between the tubes to achieve a high energy density. Good load transfer and effective attachment techniques are required so that the shells can be loaded to near their elastic limit.
Choosing the appropriate deformation mode consisting of any amongst axial tension, axial compression, torsion or bending or a combination of any of them. A criterion for choosing a deformation mode is not only the highest energy density, but also the proper integration of the deformed spring with the rest of the power dissipation mechanism.
A support structure is required to hold the CNT spring in the fully loaded configuration prior to its release. The design of the support structure will depend on the scale of the spring, the deformation mode the CNT is being subjected to and the architecture of the rest of the system. The material selected for the structure should have high strength, because the added mass and volume of the support contribute to reducing the energy density of the entire system.
Analysis is performed on CNTs subject to tensile loads. A hollow cylindrical structure of CNT of length L, diameter d and mean radius r is considered. The tube has thickness n.h, where n is the number of layers in the CNT and h=0.34 nm is the thickness of one shell. The Young's modulus of the material of the CNT is E. In case of SWCNTs, n=1 and n>1 in case of MWCNTs. The cylinder has inner and outer radii of
and
.
The shell's cross-sectional area is
and the total enclosed area is
.
The strain energy that can be stored in the bar under axial compression to a strain of is
) =
The strain energy density is simply the ratio of the strain energy and the enclosed volume. Therefore, in order for the strain energy density to be high the value of should be large. So, a spring in axial tension should consist of either SWCNTs with small diameters or uniformly loaded MWCNTs with densely packed shells to maximize .
The CNTs are arranged in groupings, generally bundles. The strain energy density must be reduced by a fill factor k to account for the spacing between the individual CNTs.
Consider the cross-section of a bundle of closely packed SWCNTs of radius r, arranged into a two-dimensional triangular lattice with a lattice constant of 2r+h. Ideal packing is assumed with a spacing of h=0.34 nm which is taken equal to the graphitic spacing. When the CNTs are arranged in a bundle the best packing fraction is produced when they are packed in a hexagonal closed packed structure.
Consider a cross section of one bundle. A hexagonal shape will be observed. The hexagonal shape with an area of is taken to be the repeating geometrical unit in the bundle. Calculations can be performed to show that fill factor k = 91%. In reality, there may not be ideal packing within a bundle, as the actual fraction k may be lower than the value calculated.
The expression of strain energy shows that it is advantageous to apply a high tensile strain to the springs to maximize energy storage since strain energy is proportional to square of the strain.
Analysis is performed on CNTs subject to compressive loads. The CNT is assumed to be a hollow cylindrical beam of length L, Young's modulus E, and thickness n.h, where n is the number of layers and h=0.34 nm is the thickness of one shell (taken equal to the separation between graphene sheets in graphite). The continuous tube has a mean radius r and diameter d. The cylinder has inner and outer radii of
and
.
The shell's cross-sectional area is
and the total enclosed area is
.
The strain energy that can be stored in the bar under axial compression to a strain of is
) =
The strain energy density is just the strain energy divided by the enclosed volume. High energy densities are achieved with a high ratio. Therefore, in order for CNT springs to achieve a high energy density either SWCNTs with small diameters or MWCNTs with densely packed shells should be used.
The purpose of using a support structure is to be able to store energy before it is released for use. The support structure should be strong enough to support the applied load (used to compress the CNTs) without reaching failure itself. Another point of consideration is that the energy density of the combined spring and supporting structure is always lower than the energy density of the spring alone.
A CNT spring made of bundles of densely packed 1 nm diameter SWCNTs stretched to a 10% strain is predicted to have an energy density of 3.4×106 kJ/m3. The energy density of CNT springs loaded in tension is higher than the energy density of CNT springs loaded in compression. [4] Whereas the current maximum energy density of a carbon-steel watch spring is reported to be between 1080 kJ/m3 [5] and 3000 kJ/m3. [6] Calculations show that when a support structure made of single crystal silicon carbide is used the energy density of CNT springs reduces to 1×106 kJ/m3. Even after considering a support structure and other energy extraction hardware associated with a CNT spring energy harvesting device, its energy density is much greater than mechanical springs and is in approximately the same range as that of lithium-ion batteries. The energy density is much lower than the energy density of any hydrocarbon used in combustion processes.
A large number of CNTs are needed to store a significant amount of energy that can be used for macroscopic processes. In order to achieve such a large amount of energy storage the CNT springs must maintain high stiffness and elasticity. It is in practice quite difficult to have such high stiffness and elastic strains in yarns or fibers made up of assemblies of CNTs as they seldom maintain mechanical properties of an individual SWCNT. This behavior occurs due to atomic defects and imperfect organisation.
Elastic loading is the preferred loading mechanism for reversible energy storage, experiments have been performed that indicate that loading within the fibers deviates from purely elastic behavior.
Only a portion of the CNTs contribute to the load bearing at a given strain. The unequal amount of slack within each CNT due to the presence of atomic defects and tangling causes different CNTs to fracture at different strains.
When MWCNTs are loaded in tension it is difficult to grasp their inner shells. Tensile tests of MWCNTs attached to atomic force microscope (AFM) tips at both ends show that fracture occurs at the outer shell in a way such that majority loading occurs at the outer shell and little load transfer occurs to the inner shells. This causes the stiffness and strength of MWCNTs to be lower than they would be if the shells were loaded equally.
A carbon nanotube (CNT) is a tube made of carbon with a diameter in the nanometer range (nanoscale). They are one of the allotropes of carbon.
A composite material is a material which is produced from two or more constituent materials. These constituent materials have notably dissimilar chemical or physical properties and are merged to create a material with properties unlike the individual elements. Within the finished structure, the individual elements remain separate and distinct, distinguishing composites from mixtures and solid solutions.
Young's modulus is a mechanical property of solid materials that measures the tensile or compressive stiffness when the force is applied lengthwise. It is the modulus of elasticity for tension or axial compression. Young's modulus is defined as the ratio of the stress applied to the object and the resulting axial strain in the linear elastic region of the material.
Dynamic mechanical analysis is a technique used to study and characterize materials. It is most useful for studying the viscoelastic behavior of polymers. A sinusoidal stress is applied and the strain in the material is measured, allowing one to determine the complex modulus. The temperature of the sample or the frequency of the stress are often varied, leading to variations in the complex modulus; this approach can be used to locate the glass transition temperature of the material, as well as to identify transitions corresponding to other molecular motions.
In materials science and continuum mechanics, viscoelasticity is the property of materials that exhibit both viscous and elastic characteristics when undergoing deformation. Viscous materials, like water, resist shear flow and strain linearly with time when a stress is applied. Elastic materials strain when stretched and immediately return to their original state once the stress is removed.
Fracture mechanics is the field of mechanics concerned with the study of the propagation of cracks in materials. It uses methods of analytical solid mechanics to calculate the driving force on a crack and those of experimental solid mechanics to characterize the material's resistance to fracture.
In materials science, work hardening, also known as strain hardening, is the strengthening of a metal or polymer by plastic deformation. Work hardening may be desirable, undesirable, or inconsequential, depending on the context.
Dynamic modulus is the ratio of stress to strain under vibratory conditions. It is a property of viscoelastic materials.
In materials science and engineering, the yield point is the point on a stress-strain curve that indicates the limit of elastic behavior and the beginning of plastic behavior. Below the yield point, a material will deform elastically and will return to its original shape when the applied stress is removed. Once the yield point is passed, some fraction of the deformation will be permanent and non-reversible and is known as plastic deformation.
Elastic energy is the mechanical potential energy stored in the configuration of a material or physical system as it is subjected to elastic deformation by work performed upon it. Elastic energy occurs when objects are impermanently compressed, stretched or generally deformed in any manner. Elasticity theory primarily develops formalisms for the mechanics of solid bodies and materials. The elastic potential energy equation is used in calculations of positions of mechanical equilibrium. The energy is potential as it will be converted into other forms of energy, such as kinetic energy and sound energy, when the object is allowed to return to its original shape (reformation) by its elasticity.
The three-point bending flexural test provides values for the modulus of elasticity in bending , flexural stress , flexural strain and the flexural stress–strain response of the material. This test is performed on a universal testing machine with a three-point or four-point bend fixture. The main advantage of a three-point flexural test is the ease of the specimen preparation and testing. However, this method has also some disadvantages: the results of the testing method are sensitive to specimen and loading geometry and strain rate.
The J-integral represents a way to calculate the strain energy release rate, or work (energy) per unit fracture surface area, in a material. The theoretical concept of J-integral was developed in 1967 by G. P. Cherepanov and independently in 1968 by James R. Rice, who showed that an energetic contour path integral was independent of the path around a crack.
The T-failure criterion is a set of material failure criteria that can be used to predict both brittle and ductile failure.
In nanotechnology, a carbon nanobud is a material that combines carbon nanotubes and spheroidal fullerenes, both allotropes of carbon, forming "buds" attached to the tubes. Carbon nanobuds were discovered and synthesized in 2006.
Methods have been devised to modify the yield strength, ductility, and toughness of both crystalline and amorphous materials. These strengthening mechanisms give engineers the ability to tailor the mechanical properties of materials to suit a variety of different applications. For example, the favorable properties of steel result from interstitial incorporation of carbon into the iron lattice. Brass, a binary alloy of copper and zinc, has superior mechanical properties compared to its constituent metals due to solution strengthening. Work hardening has also been used for centuries by blacksmiths to introduce dislocations into materials, increasing their yield strengths.
The mechanical properties of carbon nanotubes reveal them as one of the strongest materials in nature. Carbon nanotubes (CNTs) are long hollow cylinders of graphene. Although graphene sheets have 2D symmetry, carbon nanotubes by geometry have different properties in axial and radial directions. It has been shown that CNTs are very strong in the axial direction. Young's modulus on the order of 270 - 950 GPa and tensile strength of 11 - 63 GPa were obtained.
Organic photovoltaic devices (OPVs) are fabricated from thin films of organic semiconductors, such as polymers and small-molecule compounds, and are typically on the order of 100 nm thick. Because polymer based OPVs can be made using a coating process such as spin coating or inkjet printing, they are an attractive option for inexpensively covering large areas as well as flexible plastic surfaces. A promising low cost alternative to conventional solar cells made of crystalline silicon, there is a large amount of research being dedicated throughout industry and academia towards developing OPVs and increasing their power conversion efficiency.
In materials science, a general rule of mixtures is a weighted mean used to predict various properties of a composite material. It provides a theoretical upper- and lower-bound on properties such as the elastic modulus, ultimate tensile strength, thermal conductivity, and electrical conductivity. In general there are two models, one for axial loading, and one for transverse loading.
Anelasticity is a property of materials that describes their behaviour when undergoing deformation. Its formal definition does not include the physical or atomistic mechanisms but still interprets the anelastic behaviour as a manifestation of internal relaxation processes. It is a behaviour differing from elastic behaviour.
Nano-I-beams are nanostructures characterized by their I-shaped cross-section, resembling the letter I in macroscopic scale. They are typically made from hybrid organic/inorganic materials and have unique properties that make them suitable for various applications in structural nano-mechanics.