Melt flow index

Last updated
MFI Measuring device Melt flow index.jpg
MFI Measuring device

The Melt Flow Index (MFI) is a measure of the ease of flow of the melt of a thermoplastic polymer. It is defined as the mass of polymer, in grams, flowing in ten minutes through a capillary of a specific diameter and length by a pressure applied via prescribed alternative gravimetric weights for alternative prescribed temperatures. [1] [2] Polymer processors usually correlate the value of MFI with the polymer grade that they have to choose for different processes, and most often this value is not accompanied by the units, because it is taken for granted to be g/10min. Similarly, the test conditions of MFI measurement are normally expressed in kilograms rather than any other units. The method is described in the similar standards ASTM D1238 [3] and ISO 1133. [4]

Contents

Melt flow rate is an indirect measure of molecular weight, with high melt flow rate corresponding to low molecular weight. At the same time, melt flow rate is a measure of the ability of the material's melt to flow under pressure. Melt flow rate is inversely proportional to viscosity of the melt at the conditions of the test, though it should be borne in mind that the viscosity for any such material depends on the applied force. Ratios between two melt flow rate values for one material at different gravimetric weights are often used as a measure for the broadness of the molecular weight distribution.

Melt flow rate is very commonly used for polyolefins, polyethylene being measured at 190 °C and polypropylene at 230 °C. The plastics engineer should choose a material with a melt index high enough that the molten polymer can be easily formed into the article intended, but low enough that the mechanical strength of the final article will be sufficient for its use.

Measurement

Overview of the measurement of melt flow index (MFI) MFI.gif
Overview of the measurement of melt flow index (MFI)

ISO standard 1133-1 governs the procedure for measurement of the melt flow rate. [5] The procedure for determining MFI is as follows:

  1. A small amount of the polymer sample (around 4 to 5 grams) is taken in the specially designed MFI apparatus. A die with an opening of typically around 2 mm diameter is inserted into the apparatus.
  2. The material is packed properly inside the barrel to avoid formation of air pockets.
  3. A piston is introduced which acts as the medium that causes extrusion of the molten polymer.
  4. The sample is preheated for a specified amount of time: 5 min at 190 °C for polyethylene and 6 min at 230 °C for polypropylene.
  5. After the preheating a specified weight is introduced onto the piston. Examples of standard weights are 2.16 kg, 5 kg, etc.
  6. The weight exerts a force on the molten polymer and it immediately starts flowing through the die.
  7. A sample of the melt is taken after the desired period of time and is weighed accurately.
  8. MFI is expressed in grams of polymer per 10 minutes of duration of the test.

Synonyms of Melt Flow Index are Melt Flow Rate and Melt Index. More commonly used are their abbreviations: MFI, MFR and MI.

Confusingly, MFR may also indicate "melt flow ratio", the ratio between two melt flow rates at different gravimetric weights. More accurately, this should be reported as FRR (flow rate ratio), or simply flow ratio. FRR is commonly used as an indication of the way in which rheological behavior is influenced by the molecular mass distribution of the material.

formerly: (MFI = Melt Flow Index) → currently: (MFR = Melt mass-Flow Rate)

formerly: (MVI = Melt Volume Index) → currently: (MVR = Melt Volume-flow Rate)

formerly: (MFR = Melt Flow Ratio) → currently: (FRR = Flow Rate Ratio)

The flow parameter that is readily accessible to most processors is the MFI. MFI is often used to determine how a polymer will process. However, MFI takes no account of the shear, shear rate or shear history and as such is not a good measure of the processing window of a polymer. It is a single-point viscosity measurement at a relatively low shear rate and temperature. Earlier, it was often said that MFI give a ‘dot’ when actually what is needed is a ‘plot’ for the polymer processors. However, this is not true now because of a unique approach developed for estimating the rheogram merely from the knowledge of the MFI. [6]

The MFI device is not an extruder in the conventional polymer processing sense in that there is no screw to compress, heat and shear the polymer. MFI additionally does not take account of long chain branching [7] nor the differences between shear and elongational rheology. [8] Therefore, two polymers with the same MFI will not behave the same under any given processing conditions. [9]

The relationship between MFI and temperature can be used to obtain the activation energies for polymers. [10] The activation energies developed from MFI values has the advantage of simplicity and easy availability. The concept of obtaining activation energy from MFI can be extended to copolymers as well wherein there exists an anomalous temperature dependence of melt viscosity leading to the existence of two distinct values of activation energies for each copolymer. [11]

For a detailed numerical simulation of the melt flow index, see [12] or. [13]

Melt Flow Index Formula

formerly MFI (currently MFR) = Weight (gram) of Melted samples in 10 minutes

Melt Flow Index Tester

Related Research Articles

<span class="mw-page-title-main">Polymer</span> Substance composed of macromolecules with repeating structural units

A polymer (;) is a substance or material consisting of very large molecules called macromolecules, composed of many repeating subunits. Due to their broad spectrum of properties, both synthetic and natural polymers play essential and ubiquitous roles in everyday life. Polymers range from familiar synthetic plastics such as polystyrene to natural biopolymers such as DNA and proteins that are fundamental to biological structure and function. Polymers, both natural and synthetic, are created via polymerization of many small molecules, known as monomers. Their consequently large molecular mass, relative to small molecule compounds, produces unique physical properties including toughness, high elasticity, viscoelasticity, and a tendency to form amorphous and semicrystalline structures rather than crystals.

Rheology is the study of the flow of matter, primarily in a fluid state, but also as "soft solids" or solids under conditions in which they respond with plastic flow rather than deforming elastically in response to an applied force. Rheology is a branch of physics, and it is the science that deals with the deformation and flow of materials, both solids and liquids.

The Deborah number (De) is a dimensionless number, often used in rheology to characterize the fluidity of materials under specific flow conditions. It quantifies the observation that given enough time even a solid-like material might flow, or a fluid-like material can act solid when it is deformed rapidly enough. Materials that have low relaxation times flow easily and as such show relatively rapid stress decay.

<span class="mw-page-title-main">Thermoplastic</span> Plastic that softens with heat and hardens on cooling

A thermoplastic, or thermosoftening plastic, is any plastic polymer material that becomes pliable or moldable at a certain elevated temperature and solidifies upon cooling.

In materials science and continuum mechanics, viscoelasticity is the property of materials that exhibit both viscous and elastic characteristics when undergoing deformation. Viscous materials, like water, resist shear flow and strain linearly with time when a stress is applied. Elastic materials strain when stretched and immediately return to their original state once the stress is removed.

<span class="mw-page-title-main">Wood–plastic composite</span> Composite materials made of wood fiber and thermoplastics

Wood-plastic composites (WPCs) are composite materials made of wood fiber/wood flour and thermoplastic(s) such as polythene (PE), polypropylene (PP), polyvinyl chloride (PVC), or polylactic acid (PLA).

Amorphous poly alpha olefin is a commodity chemical used in multiple applications.

<span class="mw-page-title-main">Linear low-density polyethylene</span> Polymer

Linear low-density polyethylene (LLDPE) is a substantially linear polymer (polyethylene), with significant numbers of short branches, commonly made by copolymerization of ethylene with longer-chain olefins. Linear low-density polyethylene differs structurally from conventional low-density polyethylene (LDPE) because of the absence of long chain branching. The linearity of LLDPE results from the different manufacturing processes of LLDPE and LDPE. In general, LLDPE is produced at lower temperatures and pressures by copolymerization of ethylene and such higher alpha-olefins as butene, hexene, or octene. The copolymerization process produces an LLDPE polymer that has a narrower molecular weight distribution than conventional LDPE and in combination with the linear structure, significantly different rheological properties.

An ionomer is a polymer composed of repeat units of both electrically neutral repeating units and ionized units covalently bonded to the polymer backbone as pendant group moieties. Usually no more than 15 mole percent are ionized. The ionized units are often carboxylic acid groups.

<span class="mw-page-title-main">Rheometer</span> Scientific instrument used to measure fluid flow (rheology)

A rheometer is a laboratory device used to measure the way in which a viscous fluid flows in response to applied forces. It is used for those fluids which cannot be defined by a single value of viscosity and therefore require more parameters to be set and measured than is the case for a viscometer. It measures the rheology of the fluid.

<span class="mw-page-title-main">Hot-melt adhesive</span> Glue applied by heating

Hot-melt adhesive (HMA), also known as hot glue, is a form of thermoplastic adhesive that is commonly sold as solid cylindrical sticks of various diameters designed to be applied using a hot glue gun. The gun uses a continuous-duty heating element to melt the plastic glue, which the user pushes through the gun either with a mechanical trigger mechanism on the gun, or with direct finger pressure. The glue squeezed out of the heated nozzle is initially hot enough to burn and even blister skin. The glue is sticky when hot, and solidifies in a few seconds to one minute. Hot-melt adhesives can also be applied by dipping or spraying, and are popular with hobbyists and crafters both for affixing and as an inexpensive alternative to resin casting.

<span class="mw-page-title-main">Shear thinning</span> Non-Newtonian fluid behavior

In rheology, shear thinning is the non-Newtonian behavior of fluids whose viscosity decreases under shear strain. It is sometimes considered synonymous for pseudo-plastic behaviour, and is usually defined as excluding time-dependent effects, such as thixotropy.

<span class="mw-page-title-main">Manfred Wagner</span> German chemical engineer

Manfred Hermann Wagner is the author of Wagner model and the molecular stress function theory for polymer rheology. He is a Professor for Polymer engineering and Polymer physics at the Technical University of Berlin.

Thermoplastic elastomers (TPE), sometimes referred to as thermoplastic rubbers (TPR), are a class of copolymers or a physical mix of polymers that consist of materials with both thermoplastic and elastomeric properties.

<span class="mw-page-title-main">Pressure-sensitive adhesive</span> Type of non reactive adhesive

Pressure-sensitive adhesive is a type of nonreactive adhesive which forms a bond when pressure is applied to bond the adhesive with a surface. No solvent, water, or heat is needed to activate the adhesive. It is used in pressure-sensitive tapes, labels, glue dots, stickers, sticky note pads, automobile trim, and a wide variety of other products.

Thermoplastic polyurethane (TPU) is any of a class of polyurethane plastics with many properties, including elasticity, transparency, and resistance to oil, grease, and abrasion. Technically, they are thermoplastic elastomers consisting of linear segmented block copolymers composed of hard and soft segments.

Hot plate welding, also called heated tool welding, is a thermal welding technique for joining thermoplastics. A heated tool is placed against or near the two surfaces to be joined in order to melt them. Then, the heat source is removed, and the surfaces are brought together under pressure. Hot plate welding has relatively long cycle times, ranging from 10 seconds to minutes, compared to vibration or ultrasonic welding. However, its simplicity and ability to produce strong joints in almost all thermoplastics make it widely used in mass production and for large structures, like large-diameter plastic pipes. Different inspection techniques are implemented in order to identify various discontinuities or cracks.

Rheological weldability (RW) of thermoplastics considers the materials flow characteristics in determining the weldability of the given material. The process of welding thermal plastics requires three general steps, first is surface preparation. The second step is the application of heat and pressure to create intimate contact between the components being joined and initiate inter-molecular diffusion across the joint and the third step is cooling. RW can be used to determine the effectiveness of the second step of the process for given materials.

Thermoplastics containing short fiber reinforcements were first introduced commercially in the 1960s. The most common type of fibers used in short fiber thermoplastics are glass fiber and carbon fiber . Adding short fibers to thermoplastic resins improves the composite performance for lightweight applications. In addition, short fiber thermoplastic composites are easier and cheaper to produce than continuous fiber reinforced composites. This compromise between cost and performance allows short fiber reinforced thermoplastics to be used in myriad applications.

Squeeze flow is a type of flow in which a material is pressed out or deformed between two parallel plates or objects. First explored in 1874 by Josef Stefan, squeeze flow describes the outward movement of a droplet of material, its area of contact with the plate surfaces, and the effects of internal and external factors such as temperature, viscoelasticity, and heterogeneity of the material. Several squeeze flow models exist to describe Newtonian and non-Newtonian fluids undergoing squeeze flow under various geometries and conditions. Numerous applications across scientific and engineering disciplines including rheometry, welding engineering, and materials science provide examples of squeeze flow in practical use.

References

  1. ↑ A. V. Shenoy, D. R. Saini: Melt Flow Index: More Than Just a Quality Control Parameter. Part I., Advances in Polymer Technology, Vol. 6, No. 1, pages 1–58 (1986); Part II., Advances in Polymer Technology, Vol. 6, No. 2, pages 125–145 (1986).
  2. ↑ A. V. Shenoy and D. R. Saini: Thermoplastic Melt Rheology and Processing, Marcel Dekker Inc., New York (1996).
  3. ↑ ASTM D1238-04
  4. ↑ ISO 1133:1997.
  5. ↑ "ISO 1133-1:2011 Plastics -- Determination of the melt mass-flow rate (MFR) and melt volume-flow rate (MVR) of thermoplastics -- Part 1: Standard method" . Retrieved 6 May 2014.
  6. ↑ Shenoy, A. V.; Chattopadhyay, S.; Nadkarni, V. M. (1983). "From melt flow index to rheogram". Rheologica Acta. 22: 90–101. doi:10.1007/BF01679833. S2CID   53622815.
  7. ↑ Shenoy, A. V.; Saini, D. R. (1984). "Upgrading the melt flow index to rheogram approach in the low shear rate region". Journal of Applied Polymer Science. 29 (5): 1581–1593. doi:10.1002/app.1984.070290513.
  8. ↑ Shenoy, A. V.; Saini, D. R. (1985). Angewandte Makromolekulare Chemie. 135: 77–84. doi:10.1002/apmc.1985.051350107.{{cite journal}}: Missing or empty |title= (help)
  9. ↑ P. Prentice, Rheology and its role in plastics processing: No. 12, p 25, Section 3.1.3, 1995
  10. ↑ Saini, D. R.; Shenoy, A. V. (1983). "A new method for the determination of flow activation energy of polymer melt". Journal of Macromolecular Science, Part B. 22 (3): 437–449. Bibcode:1983JMSB...22..437S. doi:10.1080/00222348308215200.
  11. ↑ Shenoy, A.V.; Saini, D.R. (1988). "Effects of temperature on the flow of copolymer melts". Materials Chemistry and Physics. 19 (1–2): 123–130. doi:10.1016/0254-0584(88)90005-3.
  12. ↑ Mertz, Alex M., “Understanding Melt Flow Index and ASTM D1238,” Master's Thesis, University of Wisconsin, Mechanical Engineering Dept., Madison, WI (July, 2012).
  13. ↑ Mertz, A.M., A.W. Mix, H.M. Baek and A.J. Giacomin, “Understanding Melt Index and ASTM D1238,” Journal of Testing and Evaluation, 41(1), 1–13 (2013).
This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.