Bethanization

Last updated

Bethanization is a process patented by the Bethlehem Steel Company to protect steel from corrosion by plating it with zinc, [1] a process similar to electrogalvanization. In advertising materials, Bethlehem Steel claimed the process was more effective than hot dip galvanization, the most common means of using zinc to protect steel. [1]

Contents

The process is similar to that of Electrolytic sulfuric acid zinc plating, with few differences from bethanization. The electrolytic sulfuric acid zinc plating process uses zinc anodes, while bethanization uses inert mild steel anodes instead. The electrolytes used are manufactured by using zinc oxide dross, and dissolving it in sulfuric acid. [2]

In 1936, Bethlehem Steel spent $30 million (1936 dollars) to build a factory in Johnstown, Pennsylvania capable of creating large amounts of Bethanized wire. [3]

Material Properties

Uniformity - The zinc coating surrounding the wire is tightly bonded to the steel and uniformly distributed; weak spots on the wire will not be found.

Ductility - Bethanizing steel with 99.9 percent zinc, bonds them together tightly without any room for layers of zinc iron alloy. Zinc iron alloy is a brittle substance that induces cracking, leaving steel at critical points exposed. The zinc coating is more ductile and less brittle.

Resistance to corrosion and fatigue - Bethanized wire is claimed to have protection against corrosion and corrosion fatigue equal to that of hot-galvanized steel wire.

Strength - Wire that has been bethanized has breaking strengths claimed to be around 90 percent of bright wire strength. [4]

Use in fencing

Bethanization was applied to outdoor mesh-wire fence by the Bethlehem Steel company in the 1930s. By coating wire with purer zinc, the wire is no longer contaminated with iron unlike previous processes such as galvanization, which the company claims gives wire more durability while still retaining ductility, and also be resistant to sulfur gases that are present in Earth's atmosphere. [5] Other fencing applications that have been bethanized by the Bethlehem Steel Company include:

Related Research Articles

<span class="mw-page-title-main">Galvanization</span> Process of coating steel or iron with zinc to prevent rusting

Galvanization or galvanizing is the process of applying a protective zinc coating to steel or iron, to prevent rusting. The most common method is hot-dip galvanizing, in which the parts are coated by submerging them in a bath of hot, molten zinc.

<span class="mw-page-title-main">Metallurgy</span> Field of science that studies the physical and chemical behavior of metals

Metallurgy is a domain of materials science and engineering that studies the physical and chemical behavior of metallic elements, their inter-metallic compounds, and their mixtures, which are known as alloys.

<span class="mw-page-title-main">Rust</span> Type of iron oxide

Rust is an iron oxide, a usually reddish-brown oxide formed by the reaction of iron and oxygen in the catalytic presence of water or air moisture. Rust consists of hydrous iron(III) oxides (Fe2O3·nH2O) and iron(III) oxide-hydroxide (FeO(OH), Fe(OH)3), and is typically associated with the corrosion of refined iron.

<span class="mw-page-title-main">Electroplating</span> Creation of protective or decorative metallic coating on other metal with electric current

Electroplating, also known as electrochemical deposition or electrodeposition, is a process for producing a metal coating on a solid substrate through the reduction of cations of that metal by means of a direct electric current. The part to be coated acts as the cathode of an electrolytic cell; the electrolyte is a solution of a salt of the metal to be coated; and the anode is usually either a block of that metal, or of some inert conductive material. The current is provided by an external power supply.

<span class="mw-page-title-main">Corrosion</span> Gradual destruction of materials by chemical reaction with its environment

Corrosion is a natural process that converts a refined metal into a more chemically stable oxide. It is the gradual deterioration of materials by chemical or electrochemical reaction with their environment. Corrosion engineering is the field dedicated to controlling and preventing corrosion.

<span class="mw-page-title-main">Hot-dip galvanization</span> Process of coating iron or steel with molten zinc

Hot-dip galvanization is a form of galvanization. It is the process of coating iron and steel with zinc, which alloys with the surface of the base metal when immersing the metal in a bath of molten zinc at a temperature of around 450 °C (842 °F). When exposed to the atmosphere, the pure zinc (Zn) reacts with oxygen (O2) to form zinc oxide (ZnO), which further reacts with carbon dioxide (CO2) to form zinc carbonate (ZnCO3), a usually dull grey, fairly strong material that protects the steel underneath from further corrosion in many circumstances. Galvanized steel is widely used in applications where corrosion resistance is needed without the cost of stainless steel, and is considered superior in terms of cost and life-cycle. It can be identified by the crystallization patterning on the surface (often called a "spangle").

<span class="mw-page-title-main">Cathodic protection</span> Corrosion prevention technique

Cathodic protection is a technique used to control the corrosion of a metal surface by making it the cathode of an electrochemical cell. A simple method of protection connects the metal to be protected to a more easily corroded "sacrificial metal" to act as the anode. The sacrificial metal then corrodes instead of the protected metal. For structures such as long pipelines, where passive galvanic cathodic protection is not adequate, an external DC electrical power source is used to provide sufficient current.

<span class="mw-page-title-main">Chrome plating</span> Technique of electroplating

Chrome plating is a technique of electroplating a thin layer of chromium onto a metal object. A chrome plated part is called chrome, or is said to have been chromed. The chromium layer can be decorative, provide corrosion resistance, facilitate cleaning, and increase surface hardness. Sometimes, a less expensive substitute for chrome such as nickel may be used for aesthetic purposes.

<span class="mw-page-title-main">Anodizing</span> Metal treatment process

Anodizing is an electrolytic passivation process used to increase the thickness of the natural oxide layer on the surface of metal parts.

<span class="mw-page-title-main">Hydrogen embrittlement</span> Reduction in ductility of a metal exposed to hydrogen

Hydrogen embrittlement (HE), also known as hydrogen-assisted cracking or hydrogen-induced cracking (HIC), is a reduction in the ductility of a metal due to absorbed hydrogen. Hydrogen atoms are small and can permeate solid metals. Once absorbed, hydrogen lowers the stress required for cracks in the metal to initiate and propagate, resulting in embrittlement. Hydrogen embrittlement occurs most notably in steels, as well as in iron, nickel, titanium, cobalt, and their alloys. Copper, aluminium, and stainless steels are less susceptible to hydrogen embrittlement.

Plating is a finishing process in which a metal is deposited on a surface. Plating has been done for hundreds of years; it is also critical for modern technology. Plating is used to decorate objects, for corrosion inhibition, to improve solderability, to harden, to improve wearability, to reduce friction, to improve paint adhesion, to alter conductivity, to improve IR reflectivity, for radiation shielding, and for other purposes. Jewelry typically uses plating to give a silver or gold finish.

<span class="mw-page-title-main">Copper electroplating</span> Process of electroplating copper

Copper electroplating is the process of electroplating a layer of copper onto the surface of a metal object. Copper is used both as a standalone coating and as an undercoat onto which other metals are subsequently plated. The copper layer can be decorative, provide corrosion resistance, increase electrical and thermal conductivity, or improve the adhesion of additional deposits to the substrate.

<span class="mw-page-title-main">Electroless nickel-phosphorus plating</span> Chemical-induced nickel coating of a surface

Electroless nickel-phosphorus plating, also referred to as E-nickel, is a chemical process that deposits an even layer of nickel-phosphorus alloy on the surface of a solid substrate, like metal or plastic. The process involves dipping the substrate in a water solution containing nickel salt and a phosphorus-containing reducing agent, usually a hypophosphite salt. It is the most common version of electroless nickel plating and is often referred by that name. A similar process uses a borohydride reducing agent, yielding a nickel-boron coating instead.

The salt spray test is a standardized and popular corrosion test method, used to check corrosion resistance of materials and surface coatings. Usually, the materials to be tested are metallic and finished with a surface coating which is intended to provide a degree of corrosion protection to the underlying metal.

Electrogalvanizing is a process in which a layer of zinc is bonded to steel in order to protect against corrosion. The process involves electroplating, running a current of electricity through a saline/zinc solution with a zinc anode and steel conductor. Such Zinc electroplating or Zinc alloy electroplating maintains a dominant position among other electroplating process options, based upon electroplated tonnage per annum. According to the International Zinc Association, more than 5 million tons are used yearly for both hot dip galvanizing and electroplating. The plating of zinc was developed at the beginning of the 20th century. At that time, the electrolyte was cyanide based. A significant innovation occurred in the 1960s, with the introduction of the first acid chloride based electrolyte. The 1980s saw a return to alkaline electrolytes, only this time, without the use of cyanide. The most commonly used electrogalvanized cold rolled steel is SECC, acronym of "Steel, Electrogalvanized, Cold-rolled, Commercial quality". Compared to hot dip galvanizing, electroplated zinc offers these significant advantages:

Galvannealed or galvanneal is the result from the processes of galvanizing followed by annealing of sheet steel.

<span class="mw-page-title-main">Architectural metals</span>

Metals used for architectural purposes include lead, for water pipes, roofing, and windows; tin, formed into tinplate; zinc, copper and aluminium, in a range of applications including roofing and decoration; and iron, which has structural and other uses in the form of cast iron or wrought iron, or made into steel. Metal alloys used in building include bronze ; brass ; monel metal and nickel silver, mainly consisting of nickel and copper; and stainless steel, with important components of nickel and chromium.

Nickel electroplating is a technique of electroplating a thin layer of nickel onto a metal object. The nickel layer can be decorative, provide corrosion resistance, wear resistance, or used to build up worn or undersized parts for salvage purposes.

<span class="mw-page-title-main">Galvanic corrosion</span> Electrochemical process

Galvanic corrosion is an electrochemical process in which one metal corrodes preferentially when it is in electrical contact with another, in the presence of an electrolyte. A similar galvanic reaction is exploited in primary cells to generate a useful electrical voltage to power portable devices. This phenomenon is named after Italian physician Luigi Galvani (1737–1798).

Electrolytic iron is a form of high purity iron, obtained by electrolysis. It has a high purity greater than 99.95% with trace elements accounting for only a millionth of a decimal.

References

  1. 1 2 "Pick a fence for the yard", Kiplinger's Personal Finance. July 1973, p. 18.
  2. ↑ Ross, Robert (1988). Handbook of Metal Treatments and Testing. New York: Chapman and Hall. pp. 28–29.
  3. ↑ Special to the New York Times. "Open plant to make new Bethanized wire", The New York Times. April 17, 1936. Page 2.
  4. ↑ Bethlehem Wire Rope for bridges, towers, aerial tramways, and structures. Bethlehem Steel Company. p. 8.
  5. ↑ Bethanized Fence. Bethlehem PA: Bethlehem Steel Company. 1936. pp.  3-26.
This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.