Exchange spring magnet

Last updated
Figure 1: The ideal magnetic hysteresis loop of an exchange spring magnet (dashed), as well as the hysteresis loops of its isolated hard (Blue) and soft (Red) components. H is the applied external magnetic field, M is the total magnetic flux density of the material. Schematic hysteresis loop of exchange spring magnet.png
Figure 1: The ideal magnetic hysteresis loop of an exchange spring magnet (dashed), as well as the hysteresis loops of its isolated hard (Blue) and soft (Red) components. H is the applied external magnetic field, M is the total magnetic flux density of the material.

An exchange spring magnet is a magnetic material with high coercivity and high saturation properties derived from the exchange interaction between a hard magnetic material and a soft magnetic material, respectively.

Contents

Coehoorn et al. were the first able to observe an actual exchange spring magnet. [1] Exchange spring magnets are cheaper than many magnets containing rare earth/transition metals (RE-TM Magnets), as the hard phase of the magnet (which commonly comprises RE-TM material) can be less than 15% of the overall magnet by volume. [2]

Principle

First proposed by Kneller and Hawig in 1991, the exchange spring magnet utilizes the epitaxy between hard and soft magnetic materials: the hard material helps retain the soft material's anisotropy, which increases its coercivity. [2]

The magnetic hysteresis loop of an exchange spring magnet theoretically takes on a shape resembling that of a summation of its hard and soft magnetic components (as seen in Figure 1), meaning its energy product is higher than those of its components. A magnet's maximum energy product (BH)max, which is roughly proportional to its coercivity (HC) and magnetization saturation (Msat), is used as a metric of its ability to do magnetic work as (BH)max is twice the magnet's available magnetostatic energy. [3] The exchange spring magnet offers a geometry able to improve upon the previously reported maximum energy products of materials such as Rare Earth/Transition Metal complexes; while both materials have sufficiently large HC values and operate at relatively high Curie Temperatures, the exchange spring magnet can achieve much higher Msat values than the Rare Earth/Transition Metal (RE-TM) complexes. [4]

An important component of exchange spring magnets is anisotropy: while exchange spring magnets that are isotropic in bulk still exhibit a greater energy product than many RE-TM magnets, the energy product of their anisotropic form is theorized to be significantly higher. [3]

Magnetic energy

Exchange energy

The magnetic moment of a bulk material is the sum of all of its atomic moments. The atomic moments' interactions with each other and with the externally applied field determine the behavior of the magnet. Each atomic magnetic moment tries to orient itself so that the total magnetic energy reaches a minimum. There are generally four types of energy competing with each other to reach equilibrium: each is derived from the exchange coupling effect, magnetic anisotropy, the magnetiostatic energy of the magnet, and the magnet's interaction with external field.

Figure 2: Four types of magnetic energy. Magnetic moments of small groups of atoms are represented by arrows. Exchange spring magnet energy type.png
Figure 2: Four types of magnetic energy. Magnetic moments of small groups of atoms are represented by arrows.

Exchange coupling is a quantum mechanical effect that keeps the adjacent moments aligned with one another. Exchange energy of adjacent moments increases as the angle between the two moments increases.

where is the exchange constant and is the position vector of neighbor with respect to site . Typical values of are on the order of J/m.

Anisotropy energy

Magnetic anisotropy energy arises from the crystalline structure of the material. For a simple case, the effect can be modeled by a uniaxial energy distribution. Along an axial direction, called the easy axis, the magnetic moments tend to align. The energy increases if the orientation of a magnetic moment deviates from the easy axis.

Magnetostatic energy

The magnetostatic energy is the energy stored in the field generated by a material's magnetic moments. The magnet's field reaches its maximum intensity if all the magnetic moments orient in one direction; this is what occurs in a hard magnet. In order to prevent building up the magnetic field, sometimes magnetic moments tend to form loops. That way, the energy stored in the magnetic field can be constrained; this is what occurs in a soft magnet. What determines whether a magnet is hard or soft is the dominant term of its magnetic energy. For hard magnets, the anisotropy constant is relatively large, making the magnetic moments align with easy axis. The opposite case applies to soft magnets, in which the magnetostatic energy is dominant.

Another magnetostatic energy arises interaction with an external field. Magnetic moments naturally try to align with the applied field.

Since the magnetostatic energy dominates in the soft magnet, the magnetic moments tend to successfully orient along the external field.

Exchange spring magnet

In the exchange spring magnet, the hard phase has high coercivity and the soft phase has high saturation. The hard phase and the soft phase interact through their interface by exchange coupling.

Figure 3: Magnetic moments at the interface of a hard magnetic material and a soft magnetic material. Assumes a one-dimensional: blue arrows stand for the magnetic moments in the hard phase, and red arrows stand for those in soft phase. The length of the arrow shows its magnetization and its width shows its coercivity. The easy axis is assumed to be in the vertical direction. Exchange spring magnet arrow 1.png
Figure 3: Magnetic moments at the interface of a hard magnetic material and a soft magnetic material. Assumes a one-dimensional: blue arrows stand for the magnetic moments in the hard phase, and red arrows stand for those in soft phase. The length of the arrow shows its magnetization and its width shows its coercivity. The easy axis is assumed to be in the vertical direction.

From left to right in Figure 3, an external field is first applied in an upward direction in order to saturate the magnet. Then, the external field is reversed and starts to demagnetize the magnet. Since the coercivity of the hard phase is relatively high, the moments remain unchanged so as to minimize the anisotropy and exchange energy. The magnetic moments in the soft phase start rotating to align with the applied field. [5] Because of the exchange coupling at the soft/hard interface, the magnetic moments at the soft phase boundary have to align with the adjacent moment in hard phase. At the regions close to the interface, because of exchange coupling, the chain of magnetic moments acts like a spring. If the external field is increased, more moments in soft phase rotate downward, and the width of the transition region becomes smaller as the exchange energy density increases. The magnetic moments in the hard phase do not rotate until the external field is high enough that the exchange energy density in the transition region is comparable to the anisotropy energy density in the hard phase. At this point, the rotation of magnetic moments in the soft phase starts to affect the hard phase. As the external field surpasses the hard material's coercivity, the hard magnet gets fully demagnetized.

In the previous process, when the magnetic moments in the hard magnet start to rotate, the intensity of external field is already much higher than the coercivity of the soft phase, but there is still a transition region in soft phase. If the thickness of the soft phase is less than twice as thick as the transition region, the soft phase should have a large effective coercivity, smaller than but comparable to the coercivity of the hard phase.

Figure 4: Magnetic moments around thin soft phase Exchange spring magnet arrow 2.png
Figure 4: Magnetic moments around thin soft phase

In a thin soft phase, it is hard for the external field to rotate the magnetic moments, similar to a hard magnet with high saturation magnetization. After applying a high external field to partially demagnetize the magnetic moments in the hard phase and after subsequently removing the external field, the rotated moments in the soft phase can be rotated back by exchange coupling with the hard phase (Figure 5). This phenomenon is shown in the hysteresis loop of an exchange spring magnet (Figure 6).

Figure 5: Magnetic moments of an exchange spring magnet upon introducing and removing a relatively large external magnetic field. Exchange spring magnet arrow 3.png
Figure 5: Magnetic moments of an exchange spring magnet upon introducing and removing a relatively large external magnetic field.
Figure 6: Demagnetization curves of an exchange spring magnet. Exchange spring magnet demag curve.png
Figure 6: Demagnetization curves of an exchange spring magnet.

Comparing the exchange spring magnet's hysteresis loop with that of a conventional hard magnet demonstrates that the exchange spring magnet is more likely to recover from the opposing external field. When the external field is removed, the remanent magnetization can recover to a value close to its original. The name "exchange spring magnet" is derived from the reversibility of magnetization. [2]

The dimension of the soft phase inside the exchange spring magnet should be kept small enough so as to retain reversible magnetization. Additionally, the volume fraction of the soft phase needs to be as large as possible in order to achieve a high magnetization saturation. One viable material geometry is to fabricate a magnet by embedding hard particles inside a soft matrix. That way, the soft matrix material occupies the largest volume fraction while being close to the hard particles. The size and spacing of the hard particles is on the scale of nanometers. If the hard magnets are spheres on an fcc space lattice in the soft magnetic phase, the volume fraction of the hard phase can be 9%. Since the total magnetization saturation is summed up by volume fraction, it is close to the value of a pure soft phase.

Fabrication

The fabrication of an exchange spring magnet requires precise control of the particle-matrix structure at the nanometer-scale dimension. Several approaches have been tested, including metallurgical method, sputtering, and particle self-assembly.

Related Research Articles

<span class="mw-page-title-main">Ferromagnetism</span> Mechanism by which materials form into and are attracted to magnets

Ferromagnetism is a property of certain materials which results in a large observed magnetic permeability, and in many cases a large magnetic coercivity allowing the material to form a permanent magnet. Ferromagnetic materials are the familiar metals noticeably attracted to a magnet, a consequence of their large magnetic permeability. Magnetic permeability describes the induced magnetization of a material due to the presence of an external magnetic field, and it is this temporarily induced magnetization inside a steel plate, for instance, which accounts for its attraction to the permanent magnet. Whether or not that steel plate acquires a permanent magnetization itself, depends not only on the strength of the applied field, but on the so-called coercivity of that material, which varies greatly among ferromagnetic materials.

<span class="mw-page-title-main">Magnet</span> Material or object that produces a magnetic field

A magnet is a material or object that produces a magnetic field. This magnetic field is invisible but is responsible for the most notable property of a magnet: a force that pulls on other ferromagnetic materials, such as iron, steel, nickel, cobalt, etc. and attracts or repels other magnets.

<span class="mw-page-title-main">Antiferromagnetism</span> Regular pattern of magnetic moment ordering

In materials that exhibit antiferromagnetism, the magnetic moments of atoms or molecules, usually related to the spins of electrons, align in a regular pattern with neighboring spins pointing in opposite directions. This is, like ferromagnetism and ferrimagnetism, a manifestation of ordered magnetism. The phenomenon of antiferromagnetism was first introduced by Lev Landau in 1933.

<span class="mw-page-title-main">Ferrimagnetism</span> Type of magnetic phenomenon

A ferrimagnetic material is a material that has populations of atoms with opposing magnetic moments, as in antiferromagnetism, but these moments are unequal in magnitude so a spontaneous magnetization remains. This can for example occur when the populations consist of different atoms or ions (such as Fe2+ and Fe3+).

Remanence or remanent magnetization or residual magnetism is the magnetization left behind in a ferromagnetic material after an external magnetic field is removed. Colloquially, when a magnet is "magnetized", it has remanence. The remanence of magnetic materials provides the magnetic memory in magnetic storage devices, and is used as a source of information on the past Earth's magnetic field in paleomagnetism. The word remanence is from remanent + -ence, meaning "that which remains".

<span class="mw-page-title-main">Coercivity</span>

Coercivity, also called the magnetic coercivity, coercive field or coercive force, is a measure of the ability of a ferromagnetic material to withstand an external magnetic field without becoming demagnetized. Coercivity is usually measured in oersted or ampere/meter units and is denoted HC.

<span class="mw-page-title-main">Neodymium magnet</span> Strongest type of permanent magnet from an alloy of neodymium, iron and boron

A neodymium magnet (also known as NdFeB, NIB or Neo magnet) is the most widely used type of rare-earth magnet. It is a permanent magnet made from an alloy of neodymium, iron, and boron to form the Nd2Fe14B tetragonal crystalline structure. Developed independently in 1984 by General Motors and Sumitomo Special Metals, neodymium magnets are the strongest type of permanent magnet available commercially.

In physics, a ferromagnetic material is said to have magnetocrystalline anisotropy if it takes more energy to magnetize it in certain directions than in others. These directions are usually related to the principal axes of its crystal lattice. It is a special case of magnetic anisotropy.In other words, the excess energy required to magnetize a specimen in a particular direction over that required to magnetize it along the easy direction is called crystalline anisotropy energy.

<span class="mw-page-title-main">Alnico</span>

Alnico is a family of iron alloys which in addition to iron are composed primarily of aluminium (Al), nickel (Ni), and cobalt (Co), hence the acronym al-ni-co. They also include copper, and sometimes titanium. Alnico alloys are ferromagnetic, and are used to make permanent magnets. Before the development of rare-earth magnets in the 1970s, they were the strongest type of permanent magnet. Other trade names for alloys in this family are: Alni, Alcomax, Hycomax, Columax, and Ticonal.

<span class="mw-page-title-main">Magnetic hysteresis</span>

Magnetic hysteresis occurs when an external magnetic field is applied to a ferromagnet such as iron and the atomic dipoles align themselves with it. Even when the field is removed, part of the alignment will be retained: the material has become magnetized. Once magnetized, the magnet will stay magnetized indefinitely. To demagnetize it requires heat or a magnetic field in the opposite direction. This is the effect that provides the element of memory in a hard disk drive.

<span class="mw-page-title-main">Giant magnetoresistance</span>

Giant magnetoresistance (GMR) is a quantum mechanical magnetoresistance effect observed in multilayers composed of alternating ferromagnetic and non-magnetic conductive layers. The 2007 Nobel Prize in Physics was awarded to Albert Fert and Peter Grünberg for the discovery of GMR.

A single-molecule magnet (SMM) is a metal-organic compound that has superparamagnetic behavior below a certain blocking temperature at the molecular scale. In this temperature range, a SMM exhibits magnetic hysteresis of purely molecular origin. In contrast to conventional bulk magnets and molecule-based magnets, collective long-range magnetic ordering of magnetic moments is not necessary.

<span class="mw-page-title-main">Ferrite (magnet)</span>

A ferrite is a ceramic material made by mixing and firing large proportions of iron(III) oxide (Fe2O3, rust) blended with small proportions of one or more additional metallic elements, such as strontium, barium, manganese, nickel, and zinc. They are ferrimagnetic, meaning they can be magnetized or attracted to a magnet. Unlike other ferromagnetic materials, most ferrites are not electrically conductive, making them useful in applications like magnetic cores for transformers to suppress eddy currents. Ferrites can be divided into two families based on their resistance to being demagnetized (magnetic coercivity).

Exchange bias or exchange anisotropy occurs in bilayers of magnetic materials where the hard magnetization behavior of an antiferromagnetic thin film causes a shift in the soft magnetization curve of a ferromagnetic film. The exchange bias phenomenon is of tremendous utility in magnetic recording, where it is used to pin the state of the readback heads of hard disk drives at exactly their point of maximum sensitivity; hence the term "bias."

<span class="mw-page-title-main">Spin valve</span>

A spin valve is a device, consisting of two or more conducting magnetic materials, whose electrical resistance can change between two values depending on the relative alignment of the magnetization in the layers. The resistance change is a result of the giant magnetoresistive effect. The magnetic layers of the device align "up" or "down" depending on an external magnetic field. In the simplest case, a spin valve consists of a non-magnetic material sandwiched between two ferromagnets, one of which is fixed (pinned) by an antiferromagnet which acts to raise its magnetic coercivity and behaves as a "hard" layer, while the other is free (unpinned) and behaves as a "soft" layer. Due to the difference in coercivity, the soft layer changes polarity at lower applied magnetic field strength than the hard one. Upon application of a magnetic field of appropriate strength, the soft layer switches polarity, producing two distinct states: a parallel, low-resistance state, and an antiparallel, high-resistance state.

<span class="mw-page-title-main">Magnetic domain</span> Region of a magnetic material in which the magnetization has uniform direction

A magnetic domain is a region within a magnetic material in which the magnetization is in a uniform direction. This means that the individual magnetic moments of the atoms are aligned with one another and they point in the same direction. When cooled below a temperature called the Curie temperature, the magnetization of a piece of ferromagnetic material spontaneously divides into many small regions called magnetic domains. The magnetization within each domain points in a uniform direction, but the magnetization of different domains may point in different directions. Magnetic domain structure is responsible for the magnetic behavior of ferromagnetic materials like iron, nickel, cobalt and their alloys, and ferrimagnetic materials like ferrite. This includes the formation of permanent magnets and the attraction of ferromagnetic materials to a magnetic field. The regions separating magnetic domains are called domain walls, where the magnetization rotates coherently from the direction in one domain to that in the next domain. The study of magnetic domains is called micromagnetics.

In condensed matter physics, magnetic anisotropy describes how an object's magnetic properties can be different depending on direction. In the simplest case, there is no preferential direction for an object's magnetic moment. It will respond to an applied magnetic field in the same way, regardless of which direction the field is applied. This is known as magnetic isotropy. In contrast, magnetically anisotropic materials will be easier or harder to magnetize depending on which way the object is rotated.

Single domain, in magnetism, refers to the state of a ferromagnet in which the magnetization does not vary across the magnet. A magnetic particle that stays in a single domain state for all magnetic fields is called a single domain particle. Such particles are very small. They are also very important in a lot of applications because they have a high coercivity. They are the main source of hardness in hard magnets, the carriers of magnetic storage in tape drives, and the best recorders of the ancient Earth's magnetic field.

The Stoner–Wohlfarth model is a widely used model for the magnetization of single-domain ferromagnets. It is a simple example of magnetic hysteresis and is useful for modeling small magnetic particles in magnetic storage, biomagnetism, rock magnetism and paleomagnetism.

<span class="mw-page-title-main">Demagnetizing field</span> Internal magnetic field generated by a magnet

The demagnetizing field, also called the stray field, is the magnetic field (H-field) generated by the magnetization in a magnet. The total magnetic field in a region containing magnets is the sum of the demagnetizing fields of the magnets and the magnetic field due to any free currents or displacement currents. The term demagnetizing field reflects its tendency to act on the magnetization so as to reduce the total magnetic moment. It gives rise to shape anisotropy in ferromagnets with a single magnetic domain and to magnetic domains in larger ferromagnets.

References

  1. Coehoorn, R.; de Mooij, D.B.; De Waard, C. (1989). "Meltspun permanent magnet materials containing Fe3B as the main phase". Journal of Magnetism and Magnetic Materials. 80 (1): 101–104. Bibcode:1989JMMM...80..101C. doi:10.1016/0304-8853(89)90333-8.
  2. 1 2 3 Kneller, E. F.; Hawig, R. (July 1991). "The exchange-spring magnet: a new material principle for permanent magnets". IEEE Transactions on Magnetics. 27 (4): 3588–3560. Bibcode:1991ITM....27.3588K. doi:10.1109/20.102931.
  3. 1 2 Fullerton, E.E.; Jiang, J.S.; Bader, S.D. (1999). "Hard/Soft magnetic heterostructures: model exchange-spring magnets". Journal of Magnetism and Magnetic Materials. 200 (1–3): 392–404. Bibcode:1999JMMM..200..392F. doi:10.1016/S0304-8853(99)00376-5.
  4. Coey, J.M.D; Skomski, R. (1993). "New Magnets from Interstitial Intermetallics". Physica ScriptaT49A: 315-321.
  5. 1 2 Monteiro, Pedro M. S.; Schmool, D. S. (June 2010). "Magnetization dynamics in exchange-coupled spring systems with perpendicular anisotropy". Physical Review B. 81 (21): 214439. arXiv: 0911.4137 . Bibcode:2010PhRvB..81u4439M. doi:10.1103/PhysRevB.81.214439. S2CID   119248589.
  6. Zeng, Hao; Li, Jing; Liu, J. P.; Wang, Zhong L.; Sun, Shouheng (28 November 2002). "Exchange-coupled nanocomposite magnets by nanoparticle self-assembly". Nature. 420 (6914): 395–398. Bibcode:2002Natur.420..395Z. doi:10.1038/nature01208. PMID   12459779. S2CID   4348807.
  7. Davies, J.E.; Hellwig, O.; Fullerton, E.E.; Jiang, J.S.; Bader, S.D.; Zimányi, G.T.; Liu, K. (2005). "Anisotropy dependence of irreversible switching in Fe / Sm Co and Fe Ni / Fe Pt exchange spring magnet films". Applied Physics Letters86: 262503. doi : 10.1063/1.1954898
  8. Liu, J.P.; Luo, C.P.; Liu, Y.; Sellmyer, D.J. (1998). "High energy products in rapidly annealed nanoscale Fe/Pt multilayers". Applied Physics Letters. 72 (4): 483–485. Bibcode:1998ApPhL..72..483L. doi:10.1063/1.120793.