Extrusion welding

Last updated January 19, 2024

Extrusion welding is one of the processes used to weld thermoplastics and composites, developed in the 1960s as an evolution of hot gas welding. It can be a manual or automated process.^[1]^[2]

The process uses a welding head that has a nozzle for hot air and an extruder that pushes filler material out. The process entails heating the joining (faying) surfaces and adding molten or plasticized filler material (extrudate) by extruding it through a die (shoe). The process applies extrudate with pressure to ensure good bonding, and then allows the part to cool.

Welding steps

The steps of this welding process are similar to other plastic welding processes and involve:^[1]^[3]

Surface preparation of base material - machining the required groove as per joint design and cleaning the faying surfaces by scraping. This removes dirt and oxides from the joining surfaces, which would potentially contaminate the finished weld.
Fit-up of weld joint - tack welding the base material components (using hot gas welding) or using a clamping system
Welding - adding the extrudate while applying pressure
Finishing of the final weld appearance - Removing flash with a scraper in order to avoid stress notches. This step may or may not be necessary.
Cooling - Allowing the part to cool down so it is ready for use

Preheat is required at the initial start of the weld. This is typically achieved by using the hot air nozzle on the welding gun and fanning the starting area. Once welding has commenced, proper travel speed and gun angle will ensure that the upcoming faying surface has been sufficiently preheated.

The filler material is a polymer that comes in the form of spooled strands or in pellets.

Joint configuration

Most weld joints are designed to be a single pass, but plates over 30 mm thickness will require multiple passes. Because most passes are designed to be done in a single pass, extrusion welding typically takes less overall time to perform as compared to other plastic welding processes, particularly its predecessor, hot gas welding.^[1]

Joint design include:

Butt joints
- Single-V
- Double-V
T-Joints
Overlap joints

Butt joints will be single-V or double-V groove with 45-90° and 0–2 mm root gap. If welding a double-V groove, welding will need to be performed in a minimum of two passes.

T-joints will normally have a single bevel of 45-60° and 0–2 mm root gap.^[1]

Both TYK connections for piping and fillet welds are achievable as well.

Applications

Extrusion welding is an attractive process for applications that take advantage of its ability to weld thick sections quickly. For some applications, especially where there are large geometry parts where more traditional plastic welding methods (such as hot plate welding) is not possible, extrusion welding is the only feasible and cost effect option. In particular, tanks for liquid waste, corrosive materials, water supply are common applications. As long as a sealing bond is achieved, extrusion welding can be used for waterproofing applications as well.^[2]^[4]^[5]

Materials

Extrusion welding has seen the most success in welding different types of polyolefins.^[2]^[4]

Common materials welded with this process are:

Polyethylene (PE), in particular high-density polyethylene
Polypropylene (PP)
Polyvinyl chloride (PVC)
Polyvinylidene fluoride (PVDF)

Equipment

While there are various forms of extrusion welding equipment, there are three main components that every extrusion welding setup contains:^[1]^[2]^[6]

Extruder

The extruder is the part of the setup that actually feeds extrudate through the system. The setup of the extruder depends on if the extrudate is in pellet or in spooled strand form. When spooled strands are used, the spool is fed through a tube into the welding head and then exits through the shoe. When pellets are used for extrudate, the pellets are fed into a hopper, then a heated spiral extruder forces them through the welding head and out through the shoe as molten filler material. Pellets can only be used when welding is being performed in the flat or horizontal position.

Radiant heat source

For most applications, the radiant heat source will be hot air. The air is heated and blown through a nozzle that is part of the weld head setup. Different nozzle geometries are available, and the welder may select a certain nozzle depending on the joint configuration. Although there is a general purpose nozzle, certain nozzles ensure more thorough or more focused heating of a given joint type. Although hot air is usually used as the means for preheat, halogen lamps are sometimes used as the means for preheating the faying surface.^[1]

Welding shoe

The welding shoe is the die at the end of the feed through which the filler material is being extruded. Typically, the shoe is made out of polytetrafluoroethylene (PTFE) because of PTFE's non-stick properties. Welding shoes come in various shapes and sizes depending on the joint design that is being welded. The welding shoe will also have guide nipples that prevent the molten extrudate from flowing in an undesired direction.

Welding parameters

There are several main welding parameters, and each of them have a different bearing on the welding process. Some are dependent on the welder, whereas others can be set on the machine before welding commences. Getting a good balance of each parameter is the key to achieving strong and aesthetic welds. Automation or skill by an experienced welder, coupled with properly set parameters will result in consistent and reproducible welds.^[2]

Welding speed

Welding speed or travel speed, is the rate at which the weld is traversing down the weld joint. For an automated system, the welding speed can be set before the machine starts to go. With a manual setup, the travel speed will depend on the welder. If the travel speed is too fast, there won't be enough filler material deposited, resulting in a small weld bead. Traveling too quickly may also not provide enough time to get sufficient heat to the faying surfaces. This will result in poor adhesion of the extrudate to the faying surface. This poor adhesion leads to poor strength of the welded part. Conversely, if the travel speed is too low, then too much filler material will be deposited, resulting in an unaesthetic weld and potentially flash formation which will then need to be removed.^[6]

Position of the welding head

Position of the welding gun is essential to ensure that the extrudate is being deposited in the right area. When a manual system is being used, the welder will need to ensure that the welding head is aimed correctly. If there is misalignment between the gun and the joint, the material will not be deposited to the correct area. To help guide the welder, the weld shoe will be specifically shaped for a given joint geometry so that the position is maintained throughout welding.^[6]

Temperature of the extrudate

The temperature of the extrudate will be set on the extruder before welding begins. The temperature must be high enough such that the extrudate will be sufficiently fluid to flow, but not so high that the polymer filler material will begin to chemically breakdown. The ideal temperature for the extrudate will be dependent on what polymer being used.^[1]

Airflow rate and air temperature

Studies by have found that airflow rate and temperature are the two biggest factors in the development of creep strength of the welded parts. This is because airflow rate and air temperature are the two biggest factors in development of a melt layer prior to welding. The melt layer is the layer of molten polymer on top of the faying surface. When the melt layer reaches an ideal thickness for welding, the creep strength of the welds increase dramatically. Like with the temperature of the extrudate however, the ideal temperature and airflow rate for base material will depend on what polymer is being welded. Additionally, airflow may be altered depending on the shape of the nozzle.^[3]^[5]

Extrusion rate

Extrusion rate is how much extrudate is actually being transferred into the joint at any given time. Along with extrudate temperature and airflow rate/temperature, extrusion rate must be balanced in order to achieve ideal weld properties. If not enough material is added, then there won't be complete fusion of the joint. Conversely, if too much filler is added, then there is potential to create flash or sharp point at the toes of the weld cap. These would act as stress risers and dramatically decrease the strength of the weld both in dynamic and fatigue loading.^[5]

Advantages and disadvantages

Advantages

The main advantage of extrusion welding is that it can achieve very high deposition rates of filler material into a joint, thus cutting down on cycle time. As compared to hot gas welding, which is a polymer welding process that could have many of the same applications, the time to completion for a weld is as much as 5-6x faster.^[1]

With proper parameters, the fusion areas of the weld will actually not be the weakest part of a given fabricated polymeric part.^[5]

Because many of the main welding parameters are preset on the machine, getting consistent high quality welds is possible.

Disadvantages

If using manual extrusion welding, the welder must have a certain amount of skill in order to produce sound welds. This is especially true when welding in vertical or overhead positions. Furthermore, a manual machine could be as heavy as 12 kg, which would prove to be cumbersome.^[1]^[2]

Related Research Articles

Welding is a fabrication process that joins materials, usually metals or thermoplastics, by using high heat to melt the parts together and allowing them to cool, causing fusion. Welding is distinct from lower temperature techniques such as brazing and soldering, which do not melt the base metal.

In metallurgy, a flux is a chemical cleaning agent, flowing agent, or purifying agent. Fluxes may have more than one function at a time. They are used in both extractive metallurgy and metal joining.

Plastic welding is welding for semi-finished plastic materials, and is described in ISO 472 as a process of uniting softened surfaces of materials, generally with the aid of heat. Welding of thermoplastics is accomplished in three sequential stages, namely surface preparation, application of heat and pressure, and cooling. Numerous welding methods have been developed for the joining of semi-finished plastic materials. Based on the mechanism of heat generation at the welding interface, welding methods for thermoplastics can be classified as external and internal heating methods, as shown in Fig 1.

Extrusion is a process used to create objects of a fixed cross-sectional profile by pushing material through a die of the desired cross-section. Its two main advantages over other manufacturing processes are its ability to create very complex cross-sections; and to work materials that are brittle, because the material encounters only compressive and shear stresses. It also creates excellent surface finish and gives considerable freedom of form in the design process.

Wood-plastic composites (WPCs) are composite materials made of wood fiber/wood flour and thermoplastic(s) such as polythene (PE), polypropylene (PP), polyvinyl chloride (PVC), or polylactic acid (PLA).

Gas tungsten arc welding (GTAW), also known as tungsten inert gas (TIG) welding, is an arc welding process that uses a non-consumable tungsten electrode to produce the weld. The weld area and electrode are protected from oxidation or other atmospheric contamination by an inert shielding gas. A filler metal is normally used, though some welds, known as 'autogenous welds', or 'fusion welds' do not require it. When helium is used, this is known as heliarc welding. A constant-current welding power supply produces electrical energy, which is conducted across the arc through a column of highly ionized gas and metal vapors known as a plasma. TIG welding is most commonly used to weld thin sections of stainless steel and non-ferrous metals such as aluminum, magnesium, and copper alloys. The process grants the operator greater control over the weld than competing processes such as shielded metal arc welding and gas metal arc welding, allowing stronger, higher-quality welds. However, TIG welding is comparatively more complex and difficult to master, and furthermore, it is significantly slower than most other welding techniques. A related process, plasma arc welding, uses a slightly different welding torch to create a more focused welding arc and as a result is often automated.

Plasma arc welding (PAW) is an arc welding process similar to gas tungsten arc welding (GTAW). The electric arc is formed between an electrode and the workpiece. The key difference from GTAW is that in PAW, the electrode is positioned within the body of the torch, so the plasma arc is separated from the shielding gas envelope. The plasma is then forced through a fine-bore copper nozzle which constricts the arc and the plasma exits the orifice at high velocities and a temperature approaching 28,000 °C (50,000 °F) or higher.

Electric resistance welding (ERW) is a welding process in which metal parts in contact are permanently joined by heating them with an electric current, melting the metal at the joint. Electric resistance welding is widely used, for example, in manufacture of steel pipe and in assembly of bodies for automobiles. The electric current can be supplied to electrodes that also apply clamping pressure, or may be induced by an external magnetic field. The electric resistance welding process can be further classified by the geometry of the weld and the method of applying pressure to the joint: spot welding, seam welding, flash welding, projection welding, for example. Some factors influencing heat or welding temperatures are the proportions of the workpieces, the metal coating or the lack of coating, the electrode materials, electrode geometry, electrode pressing force, electric current and length of welding time. Small pools of molten metal are formed at the point of most electrical resistance as an electric current is passed through the metal. In general, resistance welding methods are efficient and cause little pollution, but their applications are limited to relatively thin materials.

Blow molding is a manufacturing process for forming hollow plastic parts. It is also used for forming glass bottles or other hollow shapes.

Ceramic forming techniques are ways of forming ceramics, which are used to make everything from tableware such as teapots to engineering ceramics such as computer parts. Pottery techniques include the potter's wheel, slip casting and many others.

Plastics extrusion is a high-volume manufacturing process in which raw plastic is melted and formed into a continuous profile. Extrusion produces items such as pipe/tubing, weatherstripping, fencing, deck railings, window frames, plastic films and sheeting, thermoplastic coatings, and wire insulation.

<span class="mw-page-title-main">Oxy-fuel welding and cutting</span> Metalworking technique using a fuel and oxygen

Oxy-fuel welding and oxy-fuel cutting are processes that use fuel gases and oxygen to weld or cut metals. French engineers Edmond Fouché and Charles Picard became the first to develop oxygen-acetylene welding in 1903. Pure oxygen, instead of air, is used to increase the flame temperature to allow localized melting of the workpiece material in a room environment. A common propane/air flame burns at about 2,250 K, a propane/oxygen flame burns at about 2,526 K, an oxyhydrogen flame burns at 3,073 K and an acetylene/oxygen flame burns at about 3,773 K.

Extrusion coating is the coating of a molten web of synthetic resin onto a substrate material. It is a versatile coating technique used for the economic application of various plastics, notably polyethylene, onto paperboard, corrugated fiberboard, paper, aluminium foils, cellulose, Non-wovens, or plastic films.

Hot plate welding, also called heated tool welding, is a thermal welding technique for joining thermoplastics. A heated tool is placed against or near the two surfaces to be joined in order to melt them. Then, the heat source is removed, and the surfaces are brought together under pressure. Hot plate welding has relatively long cycle times, ranging from 10 seconds to minutes, compared to vibration or ultrasonic welding. However, its simplicity and ability to produce strong joints in almost all thermoplastics make it widely used in mass production and for large structures, like large-diameter plastic pipes. Different inspection techniques are implemented in order to identify various discontinuities or cracks.

Extrusion in food processing consists of forcing soft mixed ingredients through an opening in a perforated plate or die designed to produce the required shape. The extruded food is then cut to a specific size by blades. The machine which forces the mix through the die is an extruder, and the mix is known as the extrudate. The extruder is typically a large, rotating screw tightly fitting within a stationary barrel, at the end of which is the die.

A die in polymer processing is a metal restrictor or channel capable of providing a constant cross sectional profile to a stream of liquid polymer. This allows for continuous processing of shapes such as sheets, films, pipes, rods, and other more complex profiles. This is a continuous process, allowing for constant production, as opposed to a sequential (non-constant) process such as injection molding.

Fused filament fabrication (FFF), also known as fused deposition modeling, or filament freeform fabrication, is a 3D printing process that uses a continuous filament of a thermoplastic material. Filament is fed from a large spool through a moving, heated printer extruder head, and is deposited on the growing work. The print head is moved under computer control to define the printed shape. Usually the head moves in two dimensions to deposit one horizontal plane, or layer, at a time; the work or the print head is then moved vertically by a small amount to begin a new layer. The speed of the extruder head may also be controlled to stop and start deposition and form an interrupted plane without stringing or dribbling between sections. "Fused filament fabrication" was coined by the members of the RepRap project to give an acronym (FFF) that would be legally unconstrained in its use.

Melt blowing is a conventional fabrication method of micro- and nanofibers where a polymer melt is extruded through small nozzles surrounded by high speed blowing gas. The randomly deposited fibers form a nonwoven sheet product applicable for filtration, sorbents, apparels and drug delivery systems. The substantial benefits of melt blowing are simplicity, high specific productivity and solvent-free operation. Choosing an appropriate combination of polymers with optimized rheological and surface properties, scientists have been able to produce melt-blown fibers with an average diameter as small as 36 nm.

Hot-gas welding is a manual plastic welding process for joining thermoplastic materials. A hot-gas torch is used to direct hot air to both the joint surface and weld rod, heating the materials to their softening temperature. Application of pressure on the heated weld rod to the joint surface bonds the materials together to form a completed weld. This technique is not easily automatized and is primarily used for repairs or individual manufacturing needs of small or complex components.

Spin welding is a form of friction welding used to join thermoplastic parts. The parts to be welded must be round, and in plane with each other. Like all other welding methods this process utilizes heat, time, and pressure to create a weld joint. Heat is generated via internal friction generated between the two parts when rotating and subjected to a load normal to the weld joint. This frictional heat causes the plastic to melt and a bond to be created.

References

1 2 3 4 5 6 7 8 9 Plastics and Composites Welding Handbook. Hanser. 2003. pp. 91–108. ISBN 1-56990-313-1.
1 2 3 4 5 6 Handbook of Plastics Joining: A Practical Guide. Norwich, NY: Troughton. 2008. pp. 73–79. ISBN 978-0-8155-1581-4.
1 2 Michel, P. (1989-10-15). "An Analysis of the Extrusion Welding Process". Polymer Engineering and Science. 29 (19): 1376–1381. doi:10.1002/pen.760291908.
1 2 Gehde, Michael (1997). "Extrusion Welding of Polypropylene". Welding in the World. 39: 279–285.
1 2 3 4 Gehde and Ehrenstein, Michael and Gottfried (1991-04-15). "Structure and Mechanical Properties of Optimized Extrusion Welds". Polymer Engineering and Science. 31 (7): 495–501. doi:10.1002/pen.760310705.
1 2 3 Plastic Extrusion Welder Australia - How To Weld Plastic Using a Plastic Extrusion Welder. YouTube . Archived from the original on 2021-12-08.

This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.

[:0-1] 1 2 3 4 5 6 7 8 9 Plastics and Composites Welding Handbook. Hanser. 2003. pp. 91–108. ISBN 1-56990-313-1.

[:1-2] 1 2 3 4 5 6 Handbook of Plastics Joining: A Practical Guide. Norwich, NY: Troughton. 2008. pp. 73–79. ISBN 978-0-8155-1581-4.

[:2-3] 1 2 Michel, P. (1989-10-15). "An Analysis of the Extrusion Welding Process". Polymer Engineering and Science. 29 (19): 1376–1381. doi:10.1002/pen.760291908.

[:3-4] 1 2 Gehde, Michael (1997). "Extrusion Welding of Polypropylene". Welding in the World. 39: 279–285.

[:4-5] 1 2 3 4 Gehde and Ehrenstein, Michael and Gottfried (1991-04-15). "Structure and Mechanical Properties of Optimized Extrusion Welds". Polymer Engineering and Science. 31 (7): 495–501. doi:10.1002/pen.760310705.

[:5-6] 1 2 3 Plastic Extrusion Welder Australia - How To Weld Plastic Using a Plastic Extrusion Welder. YouTube . Archived from the original on 2021-12-08.

[1]

[2]

[3]

[4]

[5]

[6]