Glass disease

Last updated
Roman glass vase with a weathered surface showing discoloration, cracking and flaking Roman glass round bottom vase 01.11.010.tif
Roman glass vase with a weathered surface showing discoloration, cracking and flaking
Bottle with glass disease Glassdisease.jpg
Bottle with glass disease

Glass disease, also referred to as sick glass or glass illness, is a degradation process of glass that can result in weeping, crizzling, spalling, cracking and fragmentation. [1] [2] Glass disease is caused by an inherent instability in the chemical composition of the original glass formula. [3] Properties of a particular glass will vary with the type and proportions of silica, alkali and alkaline earth in its composition. [4] Once damage has occurred it is irreversible, but decay processes can be slowed by climate control to regulate surrounding temperature, humidity, and air flow.

Contents

Chemical composition and decay

Glass disease is caused by an inherent fault in the chemical composition of the original glass formula. [3] Glass contains three types of components: network formers establish basic structure, network stabilizers make glass strong and water resistant, and flux lowers the melting point at which the glass can be formed. [5] Common formulations of glass may include silica (SiO2) as a former, alkali oxides such as soda (Na2O) or potash (K2O) for flux, and alkaline earth oxides such as lime (CaO) for stabilizing. [4] [5]

Structurally, glass is composed of a network of SiO4-tetrahedrons. In addition to the network former silicon which establishes its principal structure, glass contains network modifying agents such as the alkali ions Na+ and K+ and the alkali earth ions Ca2+ and Mg2+. Glass does not have a defined stoichiometry, rather the network is flexible. It can incorporate other ions, depending upon factors such as the main composition and firing conditions of the glass. [6] This causes almost all glass to be chemically unstable to some extent. [7]

Electron charge differences of ions within the structure form the basis of its bonding. Both viscosity and transition temperature are related to the availability of oxygen bonds in the glass's composition. Modifying agents tend to lower the melting point of the silica. Higher contents of SiO2 increase acidity of the glass. Higher contents of CaO, Na2O, and K2O increase basicity. [6] The chemical stability of glass decreases when only Na2O and K2O are added as flux, because bonding becomes weaker. The chemical stability of glass can be increased by adding CaO, MgO, ZnO, and Al2O3. To be stable, glass composition must balance temperature lowering agents with stabilizing agents. [6]

Exposure of a glass surface to moisture, either in solution or from humidity in the atmosphere, causes chemical reactions to occur on and below the surface of the glass. The exchange of alkali metal ions (from within the glass) and hydrogen ions (from outside) can cause chemical and structural changes to the glass. When alkali metal cations in the near-surface layer are replaced by smaller hydrogen ions, structural differences between the affected surface layer and the unaffected lower layers of glass cause increasing tensile stress, which in turn can cause cracking. [7] [8]

The likelihood of degradation due to glass disease depends on the amount and proportion of alkaline compounds mixed with silica, and on surrounding conditions. [3] Inadequate calcium oxide causes the alkalis in the glass to remain water-soluble at a low level of humidity. Exposure to higher levels of relative humidity during storage or display causes alkali to hydrate and leach out of the glass. Repeated changes in humidity can be particularly damaging. Any glass object can deteriorate if it is exposed to unsuitable environmental conditions. [9] Crystal, historic glass, or treasured family items should never be exposed to the high temperatures and water pressure of a dishwasher. [10] [11]

Energy dispersive x-ray analysis (EDXA), [1] [8] scanning electron microscopy (SEM) and secondary ion mass spectrometry (SIMS) can be used to study exchange reactions in different types of glass. By quantifying and studying chemical structure and reactions at the near-surface layer, the mechanisms of glass disease can be better understood. [7] Measurement of the pH of glass surfaces is particularly important if glass objects have a matte surface, or have been exposed to kaolin or other substances. In the case of extremely small objects such as glass beads, pH measurement may be necessary to determine whether alkaline salts are present and changes in the glass are occurring. [9] [12]

Stages of deterioration

The processes involved in glass disease can reduce the transparency of the glass or even threaten the integrity of the structure. Glass disease causes a complex disintegration of the glass which can be identified through a variety of symptoms, including weeping, crizzling, spalling, cracking and fragmentation. [3]

Example

The following description of glass beads from an object in the collection of the British Museum, effectively illustrates the range of symptoms that can occur with glass disease:

"Two factors indicated that the deterioration was the result of the phenomenon commonly referred to as ‘glass disease’; first, damage was limited to beads of one particular colour (pale yellow) and second, visible signs of all the various stages of glass disease were present on these beads. This included the presence of small white crystals on the surface of most pale yellow beads and a fine network of uniform cracks or ‘crizzling’ crossing the surface of 55 of the 69 beads. This crizzling appeared to be more prevalent around the bead holes. A total of 32 beads had areas of spalling, or advanced crizzling, where cracks had extended further into the glass structure... Many had areas that had already spalled and the fragments lost. Vertical cracks extending through the glass were present on 37 beads and four beads had become detached due to complete fragmentation." [1]

Stage One

The initial stage of glass disease occurs when moisture causes alkali to be leached out of the glass. This becomes apparent when hygroscopic alkali deposits on the glass give it a cloudy or hazy appearance. [7] [13] This may occur within as little as five to 10 years of the glass's manufacturing. The glass may feel slippery or slimy [10] and tiny droplets, or weeping, may be seen in high humidity (above 55%). [14] The hydrated alkali can form fine crystals on the surface of the glass in low relative humidity (below 40%). [4]

At this stage, it may be possible to gently wash the glass and remove the surface alkali. [14] This will help to stabilize the glass by reducing the surface pH, and by removing dust, soiling, and hygroscopic components that attract further moisture. [9]

Stage Two

If alkali builds up due to ion exchange, and remains on the surface of the glass, the decay process will accelerate. The presence of sodium or potassium ions in the alkali build up will increase the pH on the surface of the glass, causing it to become basic. This will dissolve silica from the glass as well as releasing more alkali ions. [10] [7]

The haziness seen on the glass may not disappear entirely when washed and dried. When examined closely at an angle with a low light, fine cracks like tiny silvery lines or shimmering rays, may be visible. [13] A microscope can confirm the presence of cracks. The cracks are caused by the loss of alkali, which leaves microscopic gaps in the structure of the glass. [14]

Stage Three

As higher amounts of alkali leach from the glass cracks are likely to become deeper. Crizzling is a distinctive network of fine cracks in the glass which is visible to the naked eye. [3] [15] In some cases, the crazing can gain a more uniform appearance. [13] However, crizzling may not be uniform due to the creation of micro-climates on the glass. [14]

Stage Four

Distinct cracks may appear on the surface of the glass, and surface material may flake or chip, a process referred to as spalling. [14] [13]

Stage Five

In the most severe stage of deterioration, the structural integrity of the glass has been lost and the glass may separate into pieces. [14]

Prevalence

A survey of glass objects at the Victoria and Albert Museum in London, in 1992, found that more than 1 in 10 objects in the collection were affected by crizzling, ranging from 16th century Venetian to 20th century Scandinavian glass. [3] [16] Venetian glass is particularly susceptible because artisans minimized the use of lime, to make the glass as clear as possible. The works of modern glassmakers who experiment with their glass formulas, such as Ettore Sottsass, can also be at high risk for damage. [10]

Museums such as the National Museum of the American Indian may find glass disease an issue of great importance because many of the Native American cultural materials in their collections incorporate glass beads. [9] [17] Small ornamental glass beads were often made cheaply, using recipes with a high flux to silica ratio. This makes them more susceptible to glass disease. Blues, reds, and black are often affected by glass disease. The combination of glass beads with other materials (cordage, fabric, leather, metal, bone, surface colorants, ceremonial substances, and kaolin) complicates deterioration and conservation of ethnographic objects. [12]

Conservation

In the earliest stage of glass disease, it may be possible to wash the glass to remove the surface alkali. The Corning Museum of Glass recommends washing with tap water (tepid, not hot [18] ) and a mild (non-ionic [18] ) conservation detergent. This should be followed by rinsing with de-ionized or distilled water, and careful drying to remove moisture. Careful washing can remove surface deposits, restore the appearance of clearness to the glass, and help to slow further deterioration. [19] [18] Ethanol has also been suggested for cleaning, particularly for glass beads, depending on the surrounding materials that may be affected. [9]

Once more serious damage has occurred, it cannot be reversed. Climate control of humidity and temperature is a possible intervention. Because crizzling results from the reaction of components of the glass with water vapour, controlling humidity and temperature can slow its occurrence. [3] At the Corning Museum of Glass, items in the collection are kept at stable levels of relative humidity, between 40 and 55 percent. [10] Fans may be used within a case to encourage the movement of air and minimize adsorption of moisture on the glass surface. Deterioration is more likely to occur in areas with restricted air-flow which allow moisture to remain on the glass. [14] Chemical methods for retarding corrosion rates and stabilizing surfaces are being investigated. [4]

When a composite object contains a variety of materials, one of which is sick glass, the considerations involved in conserving and displaying the object become more complicated. For example, the British Museum chose to conserve and display a Siberian shamanic apron made of leather, glass and other materials. They weighed the likelihood that it would decay more quickly if shown against the desirability of making a unique object visible and the inevitability of its eventual degradation. "Its conservation and display ensures that access to this beautiful and unique object is maximized before the pale yellow beads, which are intrinsic to the object, are inevitably lost beyond repair." [1]

Related Research Articles

<span class="mw-page-title-main">Corrosion</span> Gradual destruction of materials by chemical reaction with its environment

Corrosion is a natural process that converts a refined metal into a more chemically stable oxide. It is the gradual deterioration of materials by chemical or electrochemical reaction with their environment. Corrosion engineering is the field dedicated to controlling and preventing corrosion.

<span class="mw-page-title-main">Silica gel</span> Chemical compound

Silica gel is an amorphous and porous form of silicon dioxide (silica), consisting of an irregular tridimensional framework of alternating silicon and oxygen atoms with nanometer-scale voids and pores. The voids may contain water or some other liquids, or may be filled by gas or vacuum. In the last case, the material is properly called silica xerogel.

Sodium silicate is a generic name for chemical compounds with the formula Na
2xSi
yO
2y+x or (Na
2O)
x·(SiO
2)
y, such as sodium metasilicate Na
2SiO
3, sodium orthosilicate Na
4SiO
4, and sodium pyrosilicate Na
6Si
2O
7. The anions are often polymeric. These compounds are generally colorless transparent solids or white powders, and soluble in water in various amounts.

<span class="mw-page-title-main">Molecular sieve</span> Filter material with homogeneously sized pores in the nanometer range

A molecular sieve is a material with pores of uniform size. These pore diameters are similar in size to small molecules, and thus large molecules cannot enter or be adsorbed, while smaller molecules can. As a mixture of molecules migrates through the stationary bed of porous, semi-solid substance referred to as a sieve, the components of the highest molecular weight leave the bed first, followed by successively smaller molecules. Some molecular sieves are used in size-exclusion chromatography, a separation technique that sorts molecules based on their size. Another important use is as a desiccant. Most of molecular sieves are aluminosilicate zeolites with Si/Al molar ratio less than 2, but there are also examples of activated charcoal and silica gel.

<span class="mw-page-title-main">Conservation science (cultural property)</span> Interdisciplinary study

With respect to cultural property, conservation science is the interdisciplinary study of the conservation of art, architecture, technical art history and other cultural works through the use of scientific inquiry. General areas of research include the technology and structure of artistic and historic works. In other words, the materials and techniques from which cultural, artistic and historic objects are made. There are three broad categories of conservation science with respect to cultural heritage: understanding the materials and techniques used by artists, study of the causes of deterioration, and improving techniques and materials for examination and treatment. Conservation science includes aspects of materials science, chemistry, physics, biology, and engineering, as well as art history and anthropology. Institutions such as the Getty Conservation Institute specialize in publishing and disseminating information relating to both tools used for and outcomes of conservation science research, as well as recent discoveries in the field.

<span class="mw-page-title-main">Conservation and restoration of parchment</span> Preservation of heritage collections

The conservation and restoration of parchment constitutes the care and treatment of parchment materials which have cultural and historical significance. Typically undertaken by professional book and document conservators, this process can include preventive measures which protect against future deterioration as well as specific treatments to alleviate changes already caused by agents of deterioration.

<span class="mw-page-title-main">Concrete degradation</span> Damage to concrete affecting its mechanical strength and its durability

Concrete degradation may have many different causes. Concrete is mostly damaged by the corrosion of reinforcement bars due to the carbonatation of hardened cement paste or chloride attack under wet conditions. Chemical damage is caused by the formation of expansive products produced by chemical reactions, by aggressive chemical species present in groundwater and seawater, or by microorganisms Other damaging processes can also involve calcium leaching by water infiltration, physical phenomena initiating cracks formation and propagation, fire or radiant heat, aggregate expansion, sea water effects, leaching, and erosion by fast-flowing water.

Conservation and restoration of movable cultural property is a term used to denote the conservation of movable cultural property items in libraries, archives, museums and private collections. Conservation encompasses all the actions taken toward the long-term preservation of cultural heritage. Activities include examination, documentation, treatment, and preventive care, which is supported by research and education. Object conservation is specifically the actions taken to preserve and restore cultural objects. The objects span a wide range of materials from a variety of cultures, time periods, and functions. Object conservation can be applied to both art objects and artifacts. Conservation practice aims to prevent damage from occurring, a process known as 'preventive conservation'. The purpose of preventive conservation is to maintain, and where possible enhance, the condition of an object, as well as managing deterioration risks, such as handling and environmental conditions. Historically, object conservation was focused on the category of fine arts but now many different types of objects are conserved. Each type of object material, typically denoted by organic or inorganic then the specific medium, requires a specialized professional conservator and often requires collaborative work between museum staff, scientists, and conservators.

<span class="mw-page-title-main">Conservation and restoration of ceramic objects</span> Preservation of heritage collections

Conservation and restoration of ceramic objects is a process dedicated to the preservation and protection of objects of historical and personal value made from ceramic. Typically, this activity of conservation-restoration is undertaken by a conservator-restorer, especially when dealing with an object of cultural heritage. Ceramics are created from a production of coatings of inorganic, nonmetallic materials using heating and cooling to create a glaze. These coatings are often permanent and sustainable for utilitarian and decorative purposes. The cleaning, handling, storage, and in general treatment of ceramics is consistent with that of glass because they are made of similar oxygen-rich components, such as silicates. In conservation ceramics are broken down into three groups: unfired clay, earthenware or terracotta, and stoneware and porcelain.

<span class="mw-page-title-main">Conservation and restoration of glass objects</span>

Conservation and restoration of glass objects is one aspect of conservation and restoration of cultural heritage. The nature and varying composition of the material, and the variety of types of object made from it, demand certain specialized techniques. The conservator needs to be aware of "agents of deterioration" presenting particular risk to glass objects, and how to prevent or counteract their effects. Relevant education and training is available in certain countries through museums, conservation institutes and universities.

The conservation and restoration of outdoor bronze artworks is an activity dedicated to the preservation, protection, and maintenance of bronze objects and artworks that are on view outside. When applied to cultural heritage this activity is generally undertaken by a conservator-restorer.

<span class="mw-page-title-main">Conservation and restoration of plastic objects</span>

Conservation and restoration of objects made from plastics is work dedicated to the conservation of objects of historical and personal value made from plastics. When applied to cultural heritage, this activity is generally undertaken by a conservator-restorer.

<span class="mw-page-title-main">Conservation and restoration of clocks</span> Preservation of tangible objects

The conservation and restoration of clocks refers to the care given to the physical and functional aspects of time measuring devices featuring "moving hands on a dial face" exclusive of watches. Care for clocks constitutes regulating the external environment, cleaning, winding, lubrication, pest-management, and repairing or replacing mechanical and aesthetic components to preserve or achieve the desired state as specified by the owner. Clocks are typically composed of multiple types of materials such as wood, metal, paint, plastic, etc., which have unique behaviors and environmental interactions, making treatment options complex. The materials used and the complexity of clockwork warrant having a Horological Conservator complete the work.

The conservation and restoration of lacquerware prevents and mitigates deterioration or damage to objects made with lacquer. The two main types of lacquer are Asian, made with sap from the Urushi tree, and European, made with a variety of shellac and natural resins. Lacquer can be damaged by age, light, water, temperature, or damaged substrate.

<span class="mw-page-title-main">Conservation and restoration of bone, horn, and antler objects</span> Preservation of heritage collections

Conservation-restoration of bone, horn, and antler objects involves the processes by which the deterioration of objects either containing or made from bone, horn, and antler is contained and prevented. Their use has been documented throughout history in many societal groups as these materials are durable, plentiful, versatile, and naturally occurring/replenishing.

<span class="mw-page-title-main">Conservation and restoration of paintings</span> Preservation of heritage collections

The conservation and restoration of paintings is carried out by professional painting conservators. Paintings cover a wide range of various mediums, materials, and their supports. Painting types include fine art to decorative and functional objects spanning from acrylics, frescoes, and oil paint on various surfaces, egg tempera on panels and canvas, lacquer painting, water color and more. Knowing the materials of any given painting and its support allows for the proper restoration and conservation practices. All components of a painting will react to its environment differently, and impact the artwork as a whole. These material components along with collections care will determine the longevity of a painting. The first steps to conservation and restoration is preventive conservation followed by active restoration with the artist's intent in mind.

<span class="mw-page-title-main">Conservation and restoration of wooden artifacts</span> Preservation of heritage collections

The conservation and restoration of wooden artifacts refers to the preservation of art and artifacts made of wood. Conservation and restoration in regards to cultural heritage is completed by a conservator-restorer.

<span class="mw-page-title-main">Conservation and restoration of photographic plates</span>

The conservation and restoration of photographic plates is the practice of caring for and maintaining photographic plates to preserve their materials and content. It covers the necessary measures that can be taken by conservators, curators, collection managers, and other professionals to conserve the material unique to photographic plate processes. This practice includes understanding the composition and agents of deterioration of photographic plates, as well as the preventive conservation and interventive conservation measures that can be taken to increase their longevity.

The alkaline magma series is a chemically distinct range of magma compositions that describes the evolution of an alkaline mafic magma into a more evolved, silica-rich end member.

<span class="mw-page-title-main">Agents of deterioration</span> Major causes of damage to cultural heritage

The 'ten agents of deterioration' are a conceptual framework developed by the Canadian Conservation Institute (CCI) used to categorise the major causes of change, loss or damage to cultural heritage objects. Also referred to as the 'agents of change', the framework was first developed in the late 1980s and early 1990s. The defined agents reflect and systematise the main chemical and physical deterioration pathways to which most physical material is subject. They are a major influence on the applied practice of conservation, restoration, and collection management, finding particular use in risk management for cultural heritage collections.

References

  1. 1 2 3 4 Swift, Rachel; Meek, Andrew S.; Rode, Nicole; Komlosy, Anouska (2012). "A radioactive shamanic apron with glass disease" (PDF). The British Museum Technical Research Bulletin. 6: 25–32. Retrieved 20 April 2018.
  2. ↑ Kunicki-Goldfinger, Jerzy J. (2008). "Unstable historic glass: symptoms, causes, mechanisms and conservation". Reviews in Conservation. 9: 47–60. Archived from the original on 10 September 2018. Retrieved 19 April 2018.
  3. 1 2 3 4 5 6 7 Connor, Steve (11 October 1992). "Museum tries to stem disease affecting glass: Chemists are being used to combat a disease that is shattering exhibits". The Independent. Retrieved 19 April 2018.
  4. 1 2 3 4 Hogg, Simon; McPhail, David; Oakley, Victoria; Rogers, Philip (1998). "Cracking Crizzling - Eight Years of Collaborative Research". Conservation Journal (29). Retrieved 19 April 2018.
  5. 1 2 Cansler, Clay (2017). "From Ancient to Art Nouveau". Distillations. 3 (2): 24–25.
  6. 1 2 3 Gradmann, Rena (2016). Analysis of historical islamic glazes and the development of a substitution. w: Julius Maximilian University of Würzburg. Retrieved 20 April 2018.
  7. 1 2 3 4 5 Oakley, Victoria; Rogers, Philip; McPhail, David; Amaku, Afi (April 1992). "Vessel Glass Deterioration in the Museum Environment: A Quantitative Study by Surface Analysis". Conservation Journal (3). Retrieved 21 April 2018.
  8. 1 2 "20 years ago - Investigating crizzling". Chemistry World. 3 October 2012. Retrieved 22 April 2018.
  9. 1 2 3 4 5 O'Hern, Robin; McHugh, Kelly (2014). "Red, Blue, and Wound all over: Evaluating Condition Change and Cleaning of Glass Disease on Beads" (PDF). Objects Specialty Group Postprints. Twenty–One: 205–228. Retrieved 22 April 2018.
  10. 1 2 3 4 5 Laidman, Jenni (May 13, 2002). "Seeking cures for glass disease". The Blade. Retrieved 20 April 2018.
  11. ↑ "Caring for Your Glass". Victoria and Albert Museum. Retrieved 22 April 2018.
  12. 1 2 Lovell, Adam (July 18, 2006). GLASS BEAD DETERIORATION OF ETHNOGRAPHIC OBJECTS: IDENTIFICATION, PREVENTION, AND TREATMENT (PDF). Pleasant Hill, CA: John F. Kennedy University. Archived from the original (PDF) on 4 March 2016. Retrieved 22 April 2018.
  13. 1 2 3 4 "Crizzling". Corning Museum of Glass. April 26, 2012. Retrieved April 26, 2012.
  14. 1 2 3 4 5 6 7 Koob, Stephen (2006). Conservation and Care of Glass Objects. New York: Archetype Publications. ISBN   1-904982-08-5.
  15. ↑ Brill, Robert H. (1975). "Crizzling – a problem in glass conservation" (PDF). Journal of Glass Studies. 20: 121–131. Retrieved 20 April 2018.
  16. ↑ Jordan, Fi; Oakley, Victoria (2005). "In pursuit of a clear answer: An Exhibition Road partnership". Conservation Journal (50). Retrieved 22 April 2018.
  17. ↑ Ohern, Robin; McHugh, Kelly (2013). "Deterioration and Conservation of Unstable Glass Beads on Native American Objects" (PDF). The Bead Forum. 63. Retrieved 22 April 2018.
  18. 1 2 3 Newton, Roy; Davison, Sandra (1996). Conservation of glass. Oxford: Butterworth-Heinemann. pp. 207–209. ISBN   0750624485.
  19. ↑ "Washing Glass". Corning Museum of Glass. December 9, 2011.

Further reading

This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.