Iron armour

Last updated
Cross section of HMS Warrior's bulkhead armour HMS Warrior (1860) bulkhead armour.jpg
Cross section of HMS Warrior's bulkhead armour

Iron armour was a type of naval armour used on warships and, to a limited degree, fortifications. The use of iron gave rise to the term ironclad as a reference to a ship 'clad' in iron. The earliest material available in sufficient quantities for armouring ships was iron, wrought or cast. While cast iron has never been used for naval armour, it did find a use in land fortifications, presumable due to the lower cost of the material. One well known example of cast-iron armour for land use is the Gruson turret, first tested by the Prussian government in 1868. Armoured ships may have been built as early as 1203, [1] in the far east. In the West, they first become common when France launched the first ocean-going ironclad La Gloire in 1859. The British Navy responded with HMS Warrior in 1860, triggering a naval arms race with bigger, more heavily armed and armoured ironclads.

Early experiments showed that wrought iron was superior to cast iron, and wrought iron was subsequently adopted for naval use. British efforts at perfecting iron armour were headed by a government Special Committee on Iron, formed in 1861 by War Secretary Lord Herbert for the continued research into naval armour. Among its members was Sir William Fairbairn, a noted civil and structural engineer who had also built over 80 iron vessels before retiring from shipbuilding. Other members included metallurgist John Percy, civil engineer William Pole and representatives of the Royal Engineers, Royal Artillery and Royal Navy. This committee worked four years, between 1861 and 1865, during which time it formulated the best performing armor with the metallurgy as then known, suggested ways for improving its production and quality and helped develop more effective shot against ironclad vessels. [2]

For instance, two processes were used in constructing iron armor. In the first, hammering, large lumps of iron of scrap or puddled iron were heated to welding temperature and placed under heavy steel hammers. Repeated blows welded these lumps into one solid plate and shaped it to the required form and dimensions. Hammered iron plate was the armor used in the earliest ironclad vessels, including HMS Warrior. The second method, rolling, involved stacking iron lumps atop one another, heating them to welding temperature and passing them between two iron rollers to become one plate of the required size. Rolled iron was difficult to produce initially, as it required machinery of immense size and great power. However, when the Special Committee tested both types of plate in 1863, it found that rolled iron was superior to hammered due to greater uniformity in quality. The committee and iron manufacturers worked together on how to more easily produce rolled plate, which became standard use in warships beginning in 1865. [3]

The committee addressed the use of wooden backing with iron armor. Early European iron armour consisted of between four and five inches (roughly 10 to 13 cm) of wrought iron backed by between 18 and 36 inches (roughly one-half to one metre) of solid wood. After considerable testing, the committee found that wood prevented spalling, cushioned the shock of a hit from damaging the structure of the ship and distributed the force over a larger area, which prevented penetration. The drawback of using wood and iron was extreme weight. Experiments with reducing or eliminating wooden backing to save weight proved unsuccessful. The committee also tested steel as potential armor as its members felt that the harder the armor, the better it might deflect or resist shot. However, the steel being produced at that time proved too brittle to be effective. Iron, being softer, bent, dented and distorted but held together and remained an effective means of protection. [4]

Experiments were also carried out with laminated armour, but these did not lead to any improvements and single plates were preferred. Many ships made during the US Civil War used laminated armour but this was necessitated by lack of facilities for manufacturing single plates of proper thickness.

Due to the ever increasing thickness of the armour, and the associated weight, proposals were made from an early date to faceharden the iron or weld steel plates to the front face of iron armour. Efforts to carry out these proposals failed for many reasons, primarily because the metallurgy at the time was not up to the task.

By the mid-to-late 1870s, iron armour started to give way to steel armour, which promised to reduce the thickness, and therefore the weight, of the armour.

Related Research Articles

<span class="mw-page-title-main">Armour</span> Covering used to protect from physical injury or damage

Armour or armor is a covering used to protect an object, individual, or vehicle from physical injury or damage, especially direct contact weapons or projectiles during combat, or from a potentially dangerous environment or activity. Personal armour is used to protect soldiers and war animals. Vehicle armour is used on warships, armoured fighting vehicles, and some mostly ground attack combat aircraft.

<span class="mw-page-title-main">Wrought iron</span> Iron alloy with a very low carbon content

Wrought iron is an iron alloy with a very low carbon content in contrast to that of cast iron. It is a semi-fused mass of iron with fibrous slag inclusions, which give it a wood-like "grain" that is visible when it is etched, rusted, or bent to failure. Wrought iron is tough, malleable, ductile, corrosion resistant, and easily forge welded, but is more difficult to weld electrically.

<span class="mw-page-title-main">Chobham armour</span> British-designed composite tank armour

Chobham armour is the informal name of a composite armour developed in the 1960s at the British tank research centre on Chobham Common, Surrey. The name has since become the common generic term for composite ceramic vehicle armour. Other names informally given to Chobham armour include Burlington and Dorchester. Special armour is a broader informal term referring to any armour arrangement comprising sandwich reactive plates, including Chobham armour.

<span class="mw-page-title-main">Ironclad warship</span> Steam-propelled warship protected by iron or steel armor plates

An ironclad is a steam-propelled warship protected by iron or steel armor plates, constructed from 1859 to the early 1890s. The ironclad was developed as a result of the vulnerability of wooden warships to explosive or incendiary shells. The first ironclad battleship, Gloire, was launched by the French Navy in November 1859 - narrowly pre-empting the British Royal Navy.

Rolled homogeneous armour (RHA) is a type of vehicle armour made of a single steel composition hot-rolled to improve its material characteristics, as opposed to layered or cemented armour. Its first common application was in tanks. After World War II, it began to fall out of use on main battle tanks and other armoured fighting vehicles intended to see front-line combat as new anti-tank weapon technologies were developed which were capable of relatively easily penetrating rolled homogeneous armour plating even of significant thickness.

<span class="mw-page-title-main">William Fairbairn</span> Scottish civil engineer and shipbuilder

Sir William Fairbairn, 1st Baronet of Ardwick was a Scottish civil engineer, structural engineer and shipbuilder. In 1854 he succeeded George Stephenson and Robert Stephenson to become the third president of the Institution of Mechanical Engineers.

<span class="mw-page-title-main">Bodkin point</span> Type of arrowhead

A bodkin point is a type of arrowhead. In its simplest form it is an uncomplicated squared metal spike, and was used extensively during the Middle Ages. The typical bodkin was a square-section arrowhead, generally up to 11.5 cm (4.5 in) long and 1 cm (0.39 in) thick at its widest point, tapered down behind this initial "punch" shape. Bodkin arrows complemented traditional broadhead arrows, as bodkin point arrows were designed to defeat mail armor while broadhead point arrows caused more serious wounds and tissue damage.

<span class="mw-page-title-main">Vehicle armour</span> High-strength plating used to fortify important vehicles against bullets, shells etc.

Military vehicles are commonly armoured to withstand the impact of shrapnel, bullets, shells, rockets, and missiles, protecting the personnel inside from enemy fire. Such vehicles include armoured fighting vehicles like tanks, aircraft, and ships.

<span class="mw-page-title-main">Naval artillery</span> Artillery mounted on a warship

Naval artillery is artillery mounted on a warship, originally used only for naval warfare and then subsequently used for more specialized roles in surface warfare such as naval gunfire support (NGFS) and anti-aircraft warfare (AAW) engagements. The term generally refers to tube-launched projectile-firing weapons and excludes self-propelled projectiles such as torpedoes, rockets, and missiles and those simply dropped overboard such as depth charges and naval mines.

<span class="mw-page-title-main">Harvey armor</span> Type of casehardened naval armor

Harvey armor was a type of steel naval armor developed in the early 1890s in which the front surfaces of the plates were case hardened. The method for doing this was known as the Harvey process, and was invented by the American engineer Hayward Augustus Harvey.

Compound armour was a type of armour used on warships in the 1880s, developed in response to the emergence of armor-piercing shells and the continual need for reliable protection with the increasing size in naval ordnance. Compound armour was a non-alloyed attempt to combine the benefits of two different metals—the hardness of steel with the toughness of iron—that would stand up to intense and repeated punishment in battle. By the end of the decade it had been rendered obsolete by nickel-steel armour. However, the general principle of compound iron was used for case-hardened armour, which replaced nickel-steel in the mid-1890s and is still used today.

<span class="mw-page-title-main">Finery forge</span>

A finery forge is a forge used to produce wrought iron from pig iron by decarburization in a process called "fining" which involved liquifying cast iron in a fining hearth and removing carbon from the molten cast iron through oxidation. Finery forges were used as early as the 3rd century BC in China. The finery forge process was replaced by the puddling process and the roller mill, both developed by Henry Cort in 1783–4, but not becoming widespread until after 1800.

<span class="mw-page-title-main">Casemate ironclad</span> American Civil War warship type

The casemate ironclad was a type of iron or iron-armored gunboat briefly used in the American Civil War by both the Confederate States Navy and the Union Navy. Unlike a monitor-type ironclad which carried its armament encased in a separate armored gun deck/turret, it exhibited a single casemate structure, or armored citadel, on the main deck housing the entire gun battery. As the guns were carried on the top of the ship yet still fired through fixed gunports, the casemate ironclad is seen as an intermediate stage between the traditional broadside frigate and modern warships.

French ironclad <i>Jeanne dArc</i> French Navys Alma-class ironclad

Jeanne d'Arc was a wooden-hulled armored corvette built for the French Navy in the late 1860s. She was named for Joan of Arc, a Roman Catholic saint and heroine of the Hundred Years War. Jeanne d'Arc participated in the Franco-Prussian War of 1870–1871 and remained in commission afterwards, unlike many of her sisters. The ship was condemned in 1883, but nothing further is known as to her disposition.

<i>Aetna</i>-class ironclad floating battery

The Aetna-class ironclad floating batteries were built during the Crimean War for the attack of Russian coastal fortifications.

<i>Alma</i>-class ironclad French class of Ironclad Corvettes

The Alma-class ironclads were a group of seven wooden-hulled, armored corvettes built for the French Navy in the mid to late 1860s. Three of the ships attempted to blockade Prussian ports in the Baltic Sea in 1870 during the Franco-Prussian War. Three others patrolled the North Sea and the Atlantic, while the last ship was en route to Japan when the war began and blockaded two small Prussian ships in a Japanese harbor. Afterwards they alternated periods of reserve and active commissions, many of them abroad. Three of the ships participated in the French occupation of Tunisia in 1881 while another helped to intimidate the Vietnamese Government into accepting status as a French protectorate and played a small role in the Sino-French War of 1884–85.

French ironclad <i>La Galissonnière</i> French Navys La Galissonnière-class ironclad

La Galissonnière was lead ship of a class of wooden-hulled, armored corvettes built for the French Navy during the 1870s. She was named after the victor of the Battle of Minorca in 1756, Marquis de la Galissonnière. She bombarded Sfax in 1881 as part of the French occupation of Tunisia and was present in Alexandria shortly before the British bombarded it before the beginning of the 1882 Anglo-Egyptian War. The ship participated in a number of battles during the Sino-French War of 1884–85. La Galissonnière was condemned in 1894.

Special treatment steel (STS), also known as protective deck plate, was a type of warship armor developed by Carnegie Steel around 1910.

Ducol or "D"-steel is the name of a number of high-strength low-alloy steels of varying composition, first developed from the early 1920s by the Scottish firm of David Colville & Sons, Motherwell.

Naval armor refers to the various protections schemes employed by warships, and is distinguished from other kinds of armour. Naval sailing ships have had protection from weaponry since at least ancient times, when Greek and Roman warships used simple cladding. As weapons evolved and became more destructive, naval armour became an important part of warships. Korean and European ships began to use some iron plating in the 1500s. The first ironclad warship was created in 1859, and the pace of armour advancement accelerated quickly thereafter. The emergence of battleships around the turn of the 20th century saw ships become increasingly large and well armoured. Vast quantities of heavily armoured ships were used during the World Wars, and were crucial in the outcome. The emergence of guided missiles in the last part of the 20th century has greatly reduced the utility of armor, and most modern warships are now only lightly armored.

References

  1. 中國古代船舶 Archived 2006-06-16 at the Wayback Machine
  2. Fairbairn, pp. 351-9.
  3. Fairbairn, pp. 353-4.
  4. Baxter, p. 202-3; Fairbairn, pp. 356-8; Osborne, pp. 32-3; Sandler, p. 53.