Magnesium hydroxychloride

Last updated

Magnesium hydroxychloride [1] is the traditional term for several chemical compounds of magnesium, chlorine, oxygen, and hydrogen whose general formula xMgO·yMgCl2·zH2O, for various values of x, y, and z; or, equivalently, Mgx+y(OH)2xCl2y(H2O)z−x. The simple chemical formula that is often used is Mg(OH)Cl, which appears in high school subject, for example.Other names for this class are magnesium chloride hydroxide, [2] magnesium oxychloride, and basic magnesium chloride. [3] Some of these compounds are major components of Sorel cement.

Contents

Compounds

Phase diagram for the ternary system MgO - MgCl2 - H2O at ~ 23 degC. The stable oxychloride phases are P5 (Phase 5, 5:1:8) and P3 (phase 3, 3:1:8). The dark blue region is clear solution. The triple equilibrium points of the saturated solution are S1 (Sol: Mg(OH)2:P5), S2 (Sol:P5:P3), and S3 (Sol:P3: MgCl2*6H2O). The light blue region is the approximate range of compositions of homogeneous metastable gels. MgO-MgCl2-H2O phase diagram 23 C PNG.png
Phase diagram for the ternary system MgO – MgCl2 – H2O at ~ 23 °C. The stable oxychloride phases are P5 (Phase 5, 5:1:8) and P3 (phase 3, 3:1:8). The dark blue region is clear solution. The triple equilibrium points of the saturated solution are S1 (Sol:Mg(OH)2:P5), S2 (Sol:P5:P3), and S3 (Sol:P3:MgCl2·6H2O). The light blue region is the approximate range of compositions of homogeneous metastable gels.

The ternary diagram of the system MgO – MgCl2 – H2O has the following well-defined and stable phases: [4] [5] [6]

Phase 3 and phase 5 may exist at ambient temperature, whereas the phase 2 and phase 9 are stable only at temperatures above 100 °C. [5] All these compounds are colorless crystalline solids.

At ambient temperature, there are also gel-like homogeneous phases that form initially when the reagents are mixed, and eventually crystallize as phase 5, phase 3, or mixtures with Mg(OH)2 or MgCl2·6H2O. [4]

There are also other lower hydrates that can be obtained by heating the "natural" phases: [7]

In addition, a heptahydrate of phase 5, 5Mg(OH)2·MgCl2·7H2O, can be obtained by washing the natural octahydrate with ethanol. [7]

All four stable phases have anhydrous versions, such as 3Mg(OH)2·MgCl2 (anhydrous phase 3) and 5Mg(OH)2·MgCl2 (anhydrous phase 5), with the crystal structure of Mg(OH)2. They can be obtained by heating them to about 230 °C (phases 3 and 5) about 320 °C (phase 2), and about 260 °C (phase 9). [7]

History

These compounds are the primary components of matured magnesia cement, invented in 1867 by the French chemist Stanislas Sorel. [8]

In the late 19th century, several attempts were made to determine the composition of set Sorel's cement, but the results were not conclusive. [9] [10] [11] [12] Phase 3 was properly isolated and described by Robinson and Waggaman in 1909, [9] and phase 5 was identified by Lukens in 1932. [13]

Properties

Solubility

The oxychlorides are only very slightly soluble in water. [14]

In the system MgO – MgCl2 – H2O at about 23 °C, the completely liquid region has vertices at the following triple equilibrium points (as mass fractions, not molar fractions): [4]

S1 = 0.008 MgO + 0.170 MgCl2 + 0.822 H2O (Sol:Mg(OH)2:P5)
S2 = 0.010 MgO + 0.222 MgCl2 + 0.768 H2O (Sol:P5:P3)
S3 = 0.012 MgO + 0.345 MgCl2 + 0.643 H2O (Sol:P3:MgCl2·6H2O)

The other vertices are pure water, magnesium chloride hexahydrate, and the saturated Mg(OH)2 solution (0.0044 MgO + 0.9956 H2O by mass). [4]

Decomposition and degradation

The anhydrous forms decompose when heated above 450-500 °C by decomposition of the hydroxide and chloride anions, releasing water and hydrogen chloride and leaving a magnesium oxide residue, by the reactions: [7]

2 OH− → O2− + H2O
H2O + 2 Cl− → O2− + 2 HCl

Extended exposure of magnesium oxychlorides to water leaches out the soluble MgCl2, leaving hydrated brucite Mg(OH)2. [15]

On exposure to the atmosphere, the oxychlorides will slowly react with carbon dioxide CO2 from the air to form magnesium chlorocarbonates. Anhydrous and partially hydrated forms also absorb water, turning into phase 5 and then phase 3 on the way to the chlorocarbonate. The exceptions are the dihydrate and hexahydrate of phase 9, that remain unchanged for many months. [7]

Structure

The crystal structure of phase 3 is triclinic with space group and z = 2. [16] The solid consists polymeric aquohydroxo cations, in the form of double chains of magnesium atoms surrounded and bridged by the oxygen atoms in hydroxy groups and complexed water molecules. These linear cations are interleaved and neutralized by chloride anions and some unbound water molecules, yielding the general formula [(Mg2(OH)3(H2O)3)n]n+(Cl−)n(H2O)n. [17] [16] [7]

The structure of phase 5 is believed to be similar, with generic formula [(Mg3(OH)5(H2O)x)n]n+(Cl−)n(H2O)n(4−x). [17]

The anhydrous forms of phase 3 and phase 5 have the same structure as Mg(OH)2: namely, layers of magnesium cations, each sandwiched between two layers of hydroxy or chloride anions. [7]

Phase 5 crystals form as long needles consisting of rolled-up sheets. [18]

The Raman spectrum of phase 3 has peaks at 3639 and 3657 cm−1, whereas phase 5 has peaks at 3608 and 3691 cm−1, and brucite has a peak at 3650 cm−1. These peaks are attributed to stretching vibrations of the OH groups. Phase 3 has also a peak at 451 cm−1, attributed to the stretching of Mg–O bonds. [6] [16]

Preparation

From MgO or Mg(OH)2 and MgCl2

Phases 3 and 5 can be prepared by mixing powdered magnesium oxide MgO with a solution of magnesium chloride MgCl2 in water H2O, in molar ratios 3:1:11 and 5:1:13, respectively, at room temperature. This is the common method of preparing Sorel magnesia cement. [16] Magnesium hydroxide Mg(OH)2 can also be used instead of the oxide, with adjusted amount of water.

For best results, the magnesium oxide should have small particle size and large surface area. It can be prepared by calcination of magnesium hydroxycarbonate Mg5(OH)2(CO3)4·4H2O at about 600 °C. Higher temperatures increase particle size leading to slower reaction rate. [19]

It is believed that, during the reaction, the magnesium oxide is continuously hydrated and dissolved, helped by the slightly acidic character of the magnesium chloride solution. [17] The acidity is attributed to hydrolysis of the magnesium hexahydrate cations:

[Mg(H2O)6]2+ ↔ [Mg(OH)(H2O)5]+ + H+

The protons (which are actually hydrated, e.g. as [H3O]+) make the solution acidic; the pH varies from 6.5 to 4.7 as the concentration of MgCl2 increases from 30% to 70% (weight basis). [17] The protons then react with and dissolve the nearly insoluble oxide or hydroxide, by such reactions as [17]

MgO + 2 H+ + 5 H2O → [Mg(H2O)6]2+
Mg(OH)2 + H+ + 4 H2O → [Mg(OH)(H2O)5]+

The ions [Mg(H2O)6]2+ and [Mg(OH)(H2O)5]+ in solution then combine into complex cations with multiple magnesium atoms, bridged by hydroxide anions and water molecules (magnesium aquohydroxo complexes), with general formula [Mgx(OH)y(H2O)z](2x−y)+. [17] This process involves additional hydrolysis, turning some H2O ligands into OH− and freeing more H+, which keeps dissolving more oxide. With enough magnesium chloride, the dissolution of the oxide is relatively fast, and a clear solution of magnesium aquohydroxo cations can be obtained by filtration. [13] [12]

Over a period of several hours, those cations keep combining into larger complexes, becoming less soluble as they grow. After a few hours (at room temperature), those cations and the chloride anions precipitate as (or turn the solution into) a hydrogel, which then gradually crystallizes into a mixture of phase 3, phase 5, solid magnesium oxide and/or chloride, and/or some residual solution. [17] Depending on the proportion of the reagents, phase 5 may form at first, but then will react with excess chloride to form phase 3. [16]

The magnesium oxide can also react with water to form the hydroxide, which, being poorly soluble, would coat the oxide grains and stop further hydration. The acidity provided by hydrolysis of the cations in solution dissolves this coating, and thus allows the process to run continuously until one of the reagents is exhausted. [17]

From MgO or Mg(OH)2 and HCl

The compounds can also be prepared from magnesium oxide or hydroxide and hydrochloric acid. The MgO – H2O – MgCl2 phase diagram is contained in the MgO – H2O – HCl diagram. [4]

From MgCl2 and NaOH

The difficulties of preparing the magnesium oxide and ensuring its full reaction can be avoided by using NaOH instead of MgO or Mg(OH)2, so that all reagents are solutions. However, sodium chloride NaCl may also precipitate for certain concentrations of the reagents.

With this route, stable phase 5 precipitates in a rather narrow range of conditions, namely when the concentration [Cl] of chloride anions in solution is 2.02 ± 0.03 mol/L, the concentration [Mg] of magnesium (as Mg2+ and other cations) is 1.78 ± 0.07 mol/L, and the pH is 7.65 ± 0.05. Stable phase 3 precipitates in a broader range of cases, namely when [Cl] is 6.48 ± 2.17 mol/L, [Mg] is 3.14 ± 1.12 mol/L, and the pH is 6.26 ± 0.14 [14] [19]

Other

A short note from 1872 reported the formation a solid with approximate formula 5MgO·MgCl2·13H2O, as a mass of fine needles, from a solution of magnesium ammonium chloride Mg[NH4]Cl3 with excess ammonia left standing for several months. [10]

G. André claimed in 1882 the preparation of anhydrous oxychlorides by fusing anhydrous magnesium chloride with powdered magnesium oxide. [12]

Related Research Articles

<span class="mw-page-title-main">Magnesium sulfate</span> Chemical compound with formula MgSO4

Magnesium sulfate or magnesium sulphate is a chemical compound, a salt with the formula MgSO4, consisting of magnesium cations Mg2+ (20.19% by mass) and sulfate anions SO2−4. It is a white crystalline solid, soluble in water but not in ethanol.

<span class="mw-page-title-main">Magnesium carbonate</span> Chemical compound

Magnesium carbonate, MgCO3, is an inorganic salt that is a colourless or white solid. Several hydrated and basic forms of magnesium carbonate also exist as minerals.

Iron(III) chloride describes the inorganic compounds with the formula FeCl3(H2O)x. Also called ferric chloride, these compounds are some of the most important and commonplace compounds of iron. They are available both in anhydrous and in hydrated forms which are both hygroscopic. They feature iron in its +3 oxidation state. The anhydrous derivative is a Lewis acid, while all forms are mild oxidizing agents. It is used as a water cleaner and as an etchant for metals.

Cement chemist notation (CCN) was developed to simplify the formulas cement chemists use on a daily basis. It is a shorthand way of writing the chemical formula of oxides of calcium, silicon, and various metals.

<span class="mw-page-title-main">Magnesium chloride</span> Inorganic salt: MgCl2 and its hydrates

Magnesium chloride is an inorganic compound with the formula MgCl2. It forms hydrates MgCl2·nH2O, where n can range from 1 to 12. These salts are colorless or white solids that are highly soluble in water. These compounds and their solutions, both of which occur in nature, have a variety of practical uses. Anhydrous magnesium chloride is the principal precursor to magnesium metal, which is produced on a large scale. Hydrated magnesium chloride is the form most readily available.

<span class="mw-page-title-main">Zinc chloride</span> Chemical compound

Zinc chloride is the name of inorganic chemical compounds with the formula ZnCl2·nH2O, with x ranging from 0 to 4.5, forming hydrates. Zinc chloride, anhydrous and its hydrates are colorless or white crystalline solids, and are highly soluble in water. Five hydrates of zinc chloride are known, as well as four forms of anhydrous zinc chloride. This salt is hygroscopic and even deliquescent. Zinc chloride finds wide application in textile processing, metallurgical fluxes, and chemical synthesis. No mineral with this chemical composition is known aside from the very rare mineral simonkolleite, Zn5(OH)8Cl2·H2O.

<span class="mw-page-title-main">Aluminium chloride</span> Chemical compound

Aluminium chloride, also known as aluminium trichloride, is an inorganic compound with the formula AlCl3. It forms a hexahydrate with the formula [Al(H2O)6]Cl3, containing six water molecules of hydration. Both the anhydrous form and the hexahydrate are colourless crystals, but samples are often contaminated with iron(III) chloride, giving them a yellow colour.

<span class="mw-page-title-main">Chromium(III) chloride</span> Chemical compound

Chromium(III) chloride (also called chromic chloride) is an inorganic chemical compound with the chemical formula CrCl3. It forms several hydrates with the formula CrCl3·nH2O, among which are hydrates where n can be 5 (chromium(III) chloride pentahydrate CrCl3·5H2O) or 6 (chromium(III) chloride hexahydrate CrCl3·6H2O). The anhydrous compound with the formula CrCl3 are violet crystals, while the most common form of the chromium(III) chloride are the dark green crystals of hexahydrate, CrCl3·6H2O. Chromium chlorides find use as catalysts and as precursors to dyes for wool.

<span class="mw-page-title-main">Telluric acid</span> Chemical compound (Te(OH)6)

Telluric acid, or more accurately orthotelluric acid, is a chemical compound with the formula Te(OH)6, often written as H6TeO6. It is a white crystalline solid made up of octahedral Te(OH)6 molecules which persist in aqueous solution. In the solid state, there are two forms, rhombohedral and monoclinic, and both contain octahedral Te(OH)6 molecules, containing one hexavalent tellurium (Te) atom in the +6 oxidation state, attached to six hydroxyl (–OH) groups, thus, it can be called tellurium(VI) hydroxide. Telluric acid is a weak acid which is dibasic, forming tellurate salts with strong bases and hydrogen tellurate salts with weaker bases or upon hydrolysis of tellurates in water. It is used as tellurium-source in the synthesis of oxidation catalysts.

Sorel cement is a non-hydraulic cement first produced by the French chemist Stanislas Sorel in 1867.

<span class="mw-page-title-main">Sodium metasilicate</span> Chemical compound

Sodium metasilicate is the chemical substance with formula Na
2SiO
3, which is the main component of commercial sodium silicate solutions. It is an ionic compound consisting of sodium cations Na+
 and the polymeric metasilicate anions [–SiO2−
3–]n. It is a colorless crystalline hygroscopic and deliquescent solid, soluble in water but not in alcohols.

Basic oxides are oxides that show basic properties, in opposition to acidic oxides. A basic oxide can either react with water to form a base, or with an acid to form a salt and water in a neutralization reaction.

In inorganic chemistry, mineral hydration is a reaction which adds water to the crystal structure of a mineral, usually creating a new mineral, commonly called a hydrate.

Magnesium compounds are compounds formed by the element magnesium (Mg). These compounds are important to industry and biology, including magnesium carbonate, magnesium chloride, magnesium citrate, magnesium hydroxide, magnesium oxide, magnesium sulfate, and magnesium sulfate heptahydrate.

An AFm phase is an "alumina, ferric oxide, monosubstituted" phase, or aluminate ferrite monosubstituted, or Al2O3, Fe2O3 mono, in cement chemist notation (CCN). AFm phases are important hydration products in the hydration of Portland cements and hydraulic cements.

<span class="mw-page-title-main">Sodium metaborate</span> Chemical compound

Sodium metaborate is a chemical compound of sodium, boron, and oxygen with formula NaBO2. However, the metaborate ion is trimeric in the anhydrous solid, therefore a more correct formula is Na3B3O6 or (Na+)3[B3O6]3−. The formula can be written also as Na2O·B2O3 to highlight the relation to the main oxides of sodium and boron. The name is also applied to several hydrates whose formulas can be written NaBO2·nH2O for various values of n.

Friedel's salt is an anion exchanger mineral belonging to the family of the layered double hydroxides (LDHs). It has affinity for anions as chloride and iodide and is capable of retaining them to a certain extent in its crystallographical structure.

<span class="mw-page-title-main">Leonite</span> Hydrated double sulfate of magnesium and potassium

Leonite is a hydrated double sulfate of magnesium and potassium. It has the formula K2SO4·MgSO4·4H2O. The mineral was named after Leo Strippelmann, who was director of the salt works at Westeregeln in Germany. The mineral is part of the blodite group of hydrated double sulfate minerals.

Cobalt compounds are chemical compounds formed by cobalt with other elements.

Calcium hydroxychloride or calcium chloride hydroxide is an inorganic compound with the chemical formula Ca(OH)Cl. It consists of calcium cations (Ca2+) and chloride (Cl−) and hydroxide (−OH) anions. A white solid, it forms by the reaction of hydrogen chloride with calcium hydroxide According to X-ray crystallography, it adopts a layered structure related to brucite (magnesium hydroxide, Mg(OH)2).

References

  1. ↑ Bodine, M. W. Jr. (1976): "Magnesium hydroxychloride: A possible pH buffer in marine evaporite brines?" Geology, volume 4, issue 2, pages 76-80. doi : 10.1130/0091-7613(1976)4<76:MHAPPB>2.0.CO;2
  2. ↑ Yongliang Xiong, Haoran Deng, Martin Nemer, and Shelly Johnsen (2010): "Experimental determination of the solubility constant for magnesium chloride hydroxide hydrate (Mg3Cl(OH)5·4H2O, phase 5) at room temperature, and its importance to nuclear waste isolation in geological repositories in salt formations". Geochimica et Cosmochimica Acta, volume 74, issue 16, pages 4605–4611. doi : 10.1016/j.gca.2010.05.029
  3. ↑ JianSong Wu, YingKai Xiao, JingYun Su, TingTing Deng, JieRong Feng, YuYing Mo, and Mei Zeng (2011): "The growth mechanism of the basic magnesium chloride whisker". Science China Technological Sciences, volume 54, issue 3, pages 682–690. doi : 10.1007/s11431-011-4300-9
  4. 1 2 3 4 5 6 Ladawan Urwongse and Charles A, Sorrell (1980): "The System MgO‐MgCl2‐H2O at 23°C". Journal of the American Ceramic Society, volume 63, issue 9-10, pages 501-504. doi : 10.1111/j.1151-2916.1980.tb10752.x
  5. 1 2 Zongjin Li and C. K. Chau (2007): "Influence of molar ratios on properties of magnesium oxychloride cement". Cement and Concrete Research, volume 37, issue 6, pages 866-870. doi : 10.1016/j.cemconres.2007.03.015
  6. 1 2 Ronan M. Dorrepaal and Aoife A. Gowen (2018): "Identification of Magnesium Oxychloride Cement Biomaterial Heterogeneity using Raman Chemical Mapping and NIR Hyperspectral Chemical Imaging". Scientific Reports, volume 8, article number 13034. doi : 10.1038/s41598-018-31379-5
  7. 1 2 3 4 5 6 7 W. F. Cole and T. Demediuk (1955): "X-Ray, thermal, and Dehydration studies on Magnesium oxychlorides". Australian Journal of Chemistry, volume 8, issue 2, pages 234-251. doi : 10.1071/CH9550234
  8. ↑ Stanislas Sorel (1867): "Sur un nouveau ciment magnesién". Comptes rendus hebdomadaires des séances de l'Académie des sciences, volume 65, pages 102–104.
  9. 1 2 W. O. Robinson and W. H. Waggaman (1909): "Basic magnesium chlorides". Journal of Physical Chemistry, volume 13, issue 9, pages 673–678. doi : 10.1021/j150108a002
  10. 1 2 J. W. C. Davis (1872): "Composition of Crystalline Deposit from a Solution of Magnesium and Ammonium Chloride". The Chemical News and Journal of Physical Science, volume 25, page 258.
  11. ↑ Otto Krause (1873): "Ueber Magnesiumoxychlorid". Annalen der Chemie und Pharmacie, volume 165, pages 38–44.
  12. 1 2 3 G. M. André (1882): "Sur les oxychlorures de magnésium". Comptes rendus hebdomadaires des séances de l'Académie des sciences, volume 94, pages 444–446.
  13. 1 2 H. S. Lukens (1932): "The composition of magnesium oxychloride". Journal of the American Chemical Society, volume 54, issue 6, pages 2372–2380. doi : 10.1021/ja01345a026
  14. 1 2 Carmen Mažuranić, Halka Bilinski, and Boris Matković (1982): "Reaction Products in the System MgCl2‐NaOH‐H2O". Journal of the American Ceramic Society, volume 65, issue 10, pages 523-526. doi : 10.1111/j.1151-2916.1982.tb10346.x
  15. ↑ Amal Brichni, Halim Hammi, Salima Aggoun, and M'nif Adel (2016): "Optimization of magnesium oxychloride cement properties by silica glass". Advances in Cement Research (Springer conference proceedings). doi : 10.1680/jadcr.16.00024
  16. 1 2 3 4 5 Isao Kanesaka and Shin Aoyama (2001): "Vibrational spectra of magnesia cement, phase 3". Journal of Raman Spectroscopy, volume 32, issue 5, pages 361-367. doi : 10.1002/jrs.706
  17. 1 2 3 4 5 6 7 8 Deng Dehua and Zhang Chuanmei (1999): "The formation mechanism of the hydrate phases in magnesium oxychloride cement". Cement and Concrete Research, volume 29, issue 9, pages 1365-1371. doi : 10.1016/S0008-8846(98)00247-6
  18. ↑ B. Tooper and L. Cartz (1966): "Structure and Formation of Magnesium Oxychloride Sorel Cements". Nature, volume 211, pages 64–66. doi : 10.1038/211064a0
  19. 1 2 Halka Bilinski, Boris Matković, Carmen Mažuranić, and Toncci Balić Žunić (1984): "The Formation of Magnesium Oxychloride Phases in the Systems MgO‐MgCl2‐H2O and NaOH‐MgCl2‐H2O". Journal of the American Ceramic Society, volume 67, issue 4, pages 266-269. doi : 10.1111/j.1151-2916.1984.tb18844.x
This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.