Metal assisted chemical etching

Last updated
Cross sectional view of a silicon wafer after metal assisted chemical etching (MACE). The dissolution rate of silicon is locally enhanced due to silver nanoparticles initially deposited at the surface. Eventually the silver nanoparticles "sink" into the wafer leaving behind columnar pores. Mace wiki.png
Cross sectional view of a silicon wafer after metal assisted chemical etching (MACE). The dissolution rate of silicon is locally enhanced due to silver nanoparticles initially deposited at the surface. Eventually the silver nanoparticles "sink" into the wafer leaving behind columnar pores.

Metal Assisted Chemical Etching (also known as MACE) is the process of wet chemical etching of semiconductors (mainly silicon) with the use of a metal catalyst, usually deposited on the surface of a semiconductor in the form of a thin film or nanoparticles. The semiconductor, covered with the metal is then immersed in an etching solution containing and oxidizing agent and hydrofluoric acid. The metal on the surface catalyzes the reduction of the oxidizing agent and therefore in turn also the dissolution of silicon. In the majority of the conducted research this phenomenon of increased dissolution rate is also spatially confined, such that it is increased in close proximity to a metal particle at the surface. Eventually this leads to the formation of straight pores that are etched into the semiconductor (see figure to the right). This means that a pre-defined pattern of the metal on the surface can be directly transferred to a semiconductor substrate. [1]

Contents

History of development

MACE is a relatively new technology in semiconductor engineering and therefore it has yet to be a process that is used in industry. The first attempts of MACE consisted of a silicon wafer that was partially covered with aluminum and then immersed in an etching solution. [2] This material combination led to an increased etching rate compared to bare silicon. Often this very first attempt is also called galvanic etching instead of metal assisted chemical etching.[ citation needed ]

Further research showed that a thin film of a noble metal deposited on a silicon wafer's surface can also locally increase the etching rate. In particular, it was observed that noble metal particles sink down into the material when the sample is immersed in an etching solution containing an oxidizing agent and hydrofluoric acid (see image in the introduction). [3] This method is now commonly called the metal assisted chemical etching of silicon. Other semiconductors were also successfully etched with MACE, such as silicon carbide [4] or gallium nitride. [5] However, the main portion of research is dedicated to MACE of silicon.

It has been shown that both noble metals such as gold, [6] platinum, [7] palladium, [8] and silver, [9] and base metals such as iron, [10] nickel, [11] [12] copper, [13] and aluminium [14] can act as a catalyst in the process.

Theory

Depiction of the mechanism of MACE: The reduction of an oxidizing agent (in this case H2O2) is catalyzed at the surface of a noble metal nanoparticle (in this case gold). Because of this, holes (h ) are injected into the valence band of the silicon substrate. These holes weaken chemical bonds at the silicon/etching solution interface and thus dissolution of the substrate with HF takes place. Mace mechanism.png
Depiction of the mechanism of MACE: The reduction of an oxidizing agent (in this case H2O2) is catalyzed at the surface of a noble metal nanoparticle (in this case gold). Because of this, holes (h ) are injected into the valence band of the silicon substrate. These holes weaken chemical bonds at the silicon/etching solution interface and thus dissolution of the substrate with HF takes place.

Some elements of MACE are commonly accepted in the scientific community, while others are still under debate. [1] There is agreement that the reduction of the oxidizing agent is catalyzed by the noble metal particle (see figure to the left). This means that the metal particle has a surplus of positive charge which is eventually transferred to the silicon substrate. Each of the positive charges in the substrate can be identified as a hole (h+) in the valence band of the substrate, or in more chemical terms it may be interpreted as a weakened Si-Si bond due to the removal of an electron. The weakened bonds can be attacked by a nucleophilic species such as HF or H2O, which in turn leads to the dissolution of the silicon substrate in close proximity to the noble metal particle. [ citation needed ]

From a thermodynamic point of view, the MACE process is possible because the redox potential of the redox couple corresponding to the used oxidizing agents (hydrogen peroxide or potassium permanganate) are below the valence band edge at the electrochemical energy scale. Equivalently, one could say that the electrochemical potential of the electron in the etching solution (due to the presence of oxidizing agent) is lower than the electrochemical potential of the electron in the substrate, hence electrons are removed from the silicon. In the end, this accumulation of positive charge leads to the dissolution of the substrate by hydrofluoric acid. [1]

MACE consists of multiple individual reactions. At the metal particle, the oxidizing agent is reduced. In the case of hydrogen peroxide this can be written down as follows:

The created holes (h+) are then consumed during the dissolution of silicon. There are several possible reactions via which the dissolution can take place, but here just one example is given:

There are still some unclear aspects of the MACE process. The model proposed above requires contact of the metal particle with the silicon substrate which is somehow conflicting with the etching solution being underneath the particle. This can be explained with a dissolution and redeposition of metal during MACE. In particular it is proposed, that some metal ions from the particle are dissolved and eventually are re-deposited at the silicon surface with a redox reaction. In this case the metal particle (or even larger noble metal thin films) could partially maintain contact to the substrate while also etching could partially take place underneath the metal. [15]

It is also observed that in the vicinity of straight pores as shown in the introduction also a micro-porous region between the pores is formed. Generally this is attributed to holes that diffuse away from the particle and hence contribute to etching at more distant locations. [16] This behavior is dependent on the doping type of substrate as well as on the type of noble metal particle. Therefore, it is proposed that the formation of such a porous region beneath the straight pores depends on the type of barrier that is formed at the metal/silicon interface. In the case of an upward band bending the electric field in the depletion layer would point towards the metal. Therefore, holes cannot diffuse further into the substrate and thus no formation of a micro-porous region is observed. In the case of downward band-bending holes could escape into the bulk of the silicon substrate and eventually lead to etching there. [17]

Experimental procedure of MACE

Silver nanoparticles at the surface of a silicon wafer after immersion into a solution containing silver nitrate and hydrofluoric acid. Mace particles.png
Silver nanoparticles at the surface of a silicon wafer after immersion into a solution containing silver nitrate and hydrofluoric acid.

As already stated above MACE requires metal particles or a thin metal thin film on top of a silicon substrate. This can be achieved with several methods such as sputter deposition or thermal evaporation. [18] A method to obtain particles from a continuous thin film is thermal dewetting. [19] These deposition methods can be combined with lithography [20] such that only desired regions are covered with metal. Since MACE is an anisotropic etching method (etching takes place not in all spatial directions) a pre-defined metal pattern can be directly transferred into the silicon substrate. Another method of depositing metal particles or thin films is electroless plating of noble metals on the surface of silicon. Since the redox potentials of the redox couples of noble metals are below the valence band edge of silicon, noble metal ions can (like described in the theory section) inject holes (or extract electrons) from the substrate while they are reduced. In the end metallic particles or films are obtained at the surface. [21] Finally, after the deposition of the metal on the surface of silicon, the sample is immersed in an etching solution containing hydrofluoric acid and oxidizing agent. Etching will take place as long as the oxidizing agent and the acid are consumed or until the sample is removed from the etching solution.

Applications of MACE

Schematic depiction of a silicon substrate that is covered with a protective layer (red). 1: Wet chemical etching leads to isotropic etching 2: Etching methods that operate in the gas-phase allow anisotropic etching but are expensive. Etch anisotropy.png
Schematic depiction of a silicon substrate that is covered with a protective layer (red). 1: Wet chemical etching leads to isotropic etching 2: Etching methods that operate in the gas-phase allow anisotropic etching but are expensive.

The reason why MACE is heavily researched is that it allows completely anisotropic etching of silicon substrates which is not possible with other wet chemical etching methods (see figure to the right). Usually the silicon substrate is covered with a protective layer such as photoresist before it is immersed in an etching solution. The etching solution usually has no preferred direction of attacking the substrate, therefore isotropic etching takes place. In semiconductor engineering, however it is often required that the sidewalls of the etched trenches are steep. This is usually realized with methods that operate in the gas-phase such as reactive ion etching. These methods require expensive equipment compared to simple wet etching. MACE, in principle allows the fabrication of steep trenches but is still cheap compared to gas-phase etching methods.

Porous silicon

Metal assisted chemical etching allows for the production of porous silicon with photoluminescence. [3]

Black silicon

Black silicon is silicon with a modified surface and is a type of porous silicon. There are several works[ clarification needed ] on obtaining black silicon using MACE technology. The main application of black silicon is solar energy. [11] [12]

Black Gallium Arsenide

Black Gallium Arsenide with light trapping properties have been also produced by MACE. [22]

Related Research Articles

<span class="mw-page-title-main">MEMS</span> Very small devices that incorporate moving components

MEMS is the technology of microscopic devices incorporating both electronic and moving parts. MEMS are made up of components between 1 and 100 micrometres in size, and MEMS devices generally range in size from 20 micrometres to a millimetre, although components arranged in arrays can be more than 1000 mm2. They usually consist of a central unit that processes data and several components that interact with the surroundings.

A nanowire is a nanostructure in the form of a wire with the diameter of the order of a nanometre. More generally, nanowires can be defined as structures that have a thickness or diameter constrained to tens of nanometers or less and an unconstrained length. At these scales, quantum mechanical effects are important—which coined the term "quantum wires".

<span class="mw-page-title-main">Redox</span> Chemical reaction in which oxidation states of atoms are changed

Redox is a type of chemical reaction in which the oxidation states of a substrate change. Oxidation is the loss of electrons or an increase in the oxidation state, while reduction is the gain of electrons or a decrease in the oxidation state.

A "photoelectrochemical cell" is one of two distinct classes of device. The first produces electrical energy similarly to a dye-sensitized photovoltaic cell, which meets the standard definition of a photovoltaic cell. The second is a photoelectrolytic cell, that is, a device which uses light incident on a photosensitizer, semiconductor, or aqueous metal immersed in an electrolytic solution to directly cause a chemical reaction, for example to produce hydrogen via the electrolysis of water.

<span class="mw-page-title-main">Dye-sensitized solar cell</span> Type of thin-film solar cell

A dye-sensitized solar cell is a low-cost solar cell belonging to the group of thin film solar cells. It is based on a semiconductor formed between a photo-sensitized anode and an electrolyte, a photoelectrochemical system. The modern version of a dye solar cell, also known as the Grätzel cell, was originally co-invented in 1988 by Brian O'Regan and Michael Grätzel at UC Berkeley and this work was later developed by the aforementioned scientists at the École Polytechnique Fédérale de Lausanne (EPFL) until the publication of the first high efficiency DSSC in 1991. Michael Grätzel has been awarded the 2010 Millennium Technology Prize for this invention.

Porous silicon is a form of the chemical element silicon that has introduced nanopores in its microstructure, rendering a large surface to volume ratio in the order of 500 m2/cm3.

<span class="mw-page-title-main">Piranha solution</span> Oxidizing acid mixture containing sulfuric acid and hydrogen peroxide

Piranha solution, also known as piranha etch, is a mixture of sulfuric acid and hydrogen peroxide. The resulting mixture is used to clean organic residues off substrates, for example silicon wafers. Because the mixture is a strong oxidizing agent, it will decompose most organic matter, and it will also hydroxylate most surfaces, making them highly hydrophilic (water-compatible). This means the solution can also easily dissolve fabric and skin, potentially causing severe damage and chemical burns in case of inadvertent contact. It is named after the piranha fish due to its tendency to rapidly dissolve and ’consume’ organic materials through vigorous chemical reactions.

<span class="mw-page-title-main">Microfabrication</span> Fabrication at micrometre scales and smaller

Microfabrication is the process of fabricating miniature structures of micrometre scales and smaller. Historically, the earliest microfabrication processes were used for integrated circuit fabrication, also known as "semiconductor manufacturing" or "semiconductor device fabrication". In the last two decades microelectromechanical systems (MEMS), microsystems, micromachines and their subfields, microfluidics/lab-on-a-chip, optical MEMS, RF MEMS, PowerMEMS, BioMEMS and their extension into nanoscale have re-used, adapted or extended microfabrication methods. Flat-panel displays and solar cells are also using similar techniques.

Plasma etching is a form of plasma processing used to fabricate integrated circuits. It involves a high-speed stream of glow discharge (plasma) of an appropriate gas mixture being shot at a sample. The plasma source, known as etch species, can be either charged (ions) or neutral. During the process, the plasma generates volatile etch products at room temperature from the chemical reactions between the elements of the material etched and the reactive species generated by the plasma. Eventually the atoms of the shot element embed themselves at or just below the surface of the target, thus modifying the physical properties of the target.

<span class="mw-page-title-main">Indium(III) oxide</span> Chemical compound

Indium(III) oxide (In2O3) is a chemical compound, an amphoteric oxide of indium.

The RCA clean is a standard set of wafer cleaning steps which need to be performed before high-temperature processing steps of silicon wafers in semiconductor manufacturing.

<span class="mw-page-title-main">Etching (microfabrication)</span> Technique in microfabrication used to remove material and create structures

Etching is used in microfabrication to chemically remove layers from the surface of a wafer during manufacturing. Etching is a critically important process module in fabrication, and every wafer undergoes many etching steps before it is complete.

Black silicon is a semiconductor material, a surface modification of silicon with very low reflectivity and correspondingly high absorption of visible light.

<span class="mw-page-title-main">Vapor–liquid–solid method</span> Mechanism to grow nano wires

The vapor–liquid–solid method (VLS) is a mechanism for the growth of one-dimensional structures, such as nanowires, from chemical vapor deposition. The growth of a crystal through direct adsorption of a gas phase on to a solid surface is generally very slow. The VLS mechanism circumvents this by introducing a catalytic liquid alloy phase which can rapidly adsorb a vapor to supersaturation levels, and from which crystal growth can subsequently occur from nucleated seeds at the liquid–solid interface. The physical characteristics of nanowires grown in this manner depend, in a controllable way, upon the size and physical properties of the liquid alloy.

Nanoarchitectures for lithium-ion batteries are attempts to employ nanotechnology to improve the design of lithium-ion batteries. Research in lithium-ion batteries focuses on improving energy density, power density, safety, durability and cost.

<span class="mw-page-title-main">Silicon nanotube</span>

Silicon nanotubes are nanoparticles which create a tube-like structure from silicon atoms. As with silicon nanowires, they are technologically important due to their unusual physical properties, which differ fundamentally to those of bulk silicon. The first reports on silicon nanotubes appeared around the year 2000.

<span class="mw-page-title-main">Wright etch</span>

The Wright etch is a preferential etch for revealing defects in <100>- and <111>-oriented, p- and n-type silicon wafers used for making transistors, microprocessors, memories, and other components. Revealing, identifying, and remedying such defects is essential for progress along the path predicted by Moore's law. It was developed by Margaret Wright Jenkins (1936-2018) in 1976 while working in research and development at Motorola Inc. in Phoenix, AZ. It was published in 1977. This etchant reveals clearly defined oxidation-induced stacking faults, dislocations, swirls and striations with minimum surface roughness or extraneous pitting. These defects are known causes of shorts and current leakage in finished semiconductor devices should they fall across isolated junctions. A relatively low etch rate at room temperature provides etch control. The long shelf life of this etchant allows the solution to be stored in large quantities.

Scanning electrochemical microscopy (SECM) is a technique within the broader class of scanning probe microscopy (SPM) that is used to measure the local electrochemical behavior of liquid/solid, liquid/gas and liquid/liquid interfaces. Initial characterization of the technique was credited to University of Texas electrochemist, Allen J. Bard, in 1989. Since then, the theoretical underpinnings have matured to allow widespread use of the technique in chemistry, biology and materials science. Spatially resolved electrochemical signals can be acquired by measuring the current at an ultramicroelectrode (UME) tip as a function of precise tip position over a substrate region of interest. Interpretation of the SECM signal is based on the concept of diffusion-limited current. Two-dimensional raster scan information can be compiled to generate images of surface reactivity and chemical kinetics.

<span class="mw-page-title-main">Chemical milling</span> Manufacturing process using etching chemicals to remove material

Chemical milling or industrial etching is the subtractive manufacturing process of using baths of temperature-regulated etching chemicals to remove material to create an object with the desired shape. Other names for chemical etching include photo etching, chemical etching, photo chemical etching and photochemical machining. It is mostly used on metals, though other materials are increasingly important. It was developed from armor-decorating and printing etching processes developed during the Renaissance as alternatives to engraving on metal. The process essentially involves bathing the cutting areas in a corrosive chemical known as an etchant, which reacts with the material in the area to be cut and causes the solid material to be dissolved; inert substances known as maskants are used to protect specific areas of the material as resists.

Silicon nanowires, also referred to as SiNWs, are a type of semiconductor nanowire most often formed from a silicon precursor by etching of a solid or through catalyzed growth from a vapor or liquid phase. Such nanowires have promising applications in lithium ion batteries, thermoelectrics and sensors. Initial synthesis of SiNWs is often accompanied by thermal oxidation steps to yield structures of accurately tailored size and morphology.

References

  1. 1 2 3 Huang, Zhipeng; Geyer, Nadine; Werner, Peter; de Boor, Johannes; Gösele, Ulrich (11 January 2011). "Metal‐Assisted Chemical Etching of Silicon: A Review: In memory of Prof. Ulrich Gösele". Advanced Materials. 23 (2): 285–308. doi:10.1002/adma.201001784. PMID   20859941. S2CID   205237664.
  2. ↑ Dimova-Malinovska, D; Sendova-Vassileva, M; Tzenov, N; Kamenova, M (April 1997). "Preparation of thin porous silicon layers by stain etching". Thin Solid Films. 297 (1–2): 9–12. doi:10.1016/S0040-6090(96)09434-5.
  3. 1 2 Li, X.; Bohn, P. W. (16 October 2000). "Metal-assisted chemical etching in HF/H2O2 produces porous silicon". Applied Physics Letters. 77 (16): 2572–2574. doi: 10.1063/1.1319191 .
  4. ↑ Leitgeb, Markus; Zellner, Christopher; Schneider, Michael; Schwab, Stefan; Hutter, Herbert; Schmid, Ulrich (1 November 2017). "Metal assisted photochemical etching of 4H silicon carbide". Journal of Physics D: Applied Physics. 50 (43): 435301. doi: 10.1088/1361-6463/aa8942 .
  5. ↑ Dı́az, Diego J.; Williamson, Todd L.; Adesida, Ilesanmi; Bohn, Paul W.; Molnar, Richard J. (15 December 2003). "Morphology evolution and luminescence properties of porous GaN generated via Pt-assisted electroless etching of hydride vapor phase epitaxy GaN on sapphire". Journal of Applied Physics. 94 (12): 7526–7534. doi:10.1063/1.1628833.
  6. ↑ Mikhael, Bechelany; Elise, Berodier; Xavier, Maeder; Sebastian, Schmitt; Johann, Michler; Laetitia, Philippe (26 October 2011). "New Silicon Architectures by Gold-Assisted Chemical Etching". ACS Applied Materials & Interfaces. 3 (10): 3866–3873. doi:10.1021/am200948p. PMID   21882843.
  7. ↑ Tsujino, Kazuya; Matsumura, Michio (2005). "Helical Nanoholes Bored in Silicon by Wet Chemical Etching Using Platinum Nanoparticles as Catalyst". Electrochemical and Solid-State Letters. 8 (12): C193. doi:10.1149/1.2109347.
  8. ↑ Chen, Jun-Ming; Chen, Chia-Yuan; Wong, C.P.; Chen, Chia-Yun (January 2017). "Inherent formation of porous p-type Si nanowires using palladium-assisted chemical etching". Applied Surface Science. 392: 498–502. doi:10.1016/j.apsusc.2016.09.048.
  9. ↑ Lee, Jung-In; Park, Soojin (January 2013). "High-performance porous silicon monoxide anodes synthesized via metal-assisted chemical etching". Nano Energy. 2 (1): 146–152. doi:10.1016/j.nanoen.2012.08.009.
  10. ↑ Loni, A.; Barwick, D.; Batchelor, L.; Tunbridge, J.; Han, Y.; Li, Z. Y.; Canham, L. T. (1 May 2011). "Extremely High Surface Area Metallurgical-Grade Porous Silicon Powder Prepared by Metal-Assisted Etching". Electrochemical and Solid-State Letters. 14 (5): K25–K27. doi: 10.1149/1.3548513 .
  11. 1 2 Volovlikova, Olga V.; Gavrilov, S.A.; Lazarenko, P.I.; Kukin, A.V.; Dudin, A.A.; Tarhanov, A.K. (June 2019). "Influence of Etching Regimes on the Reflectance of Black Silicon Films Formed by Ni-Assisted Chemical Etching". Key Engineering Materials. 806: 24–29. doi:10.4028/www.scientific.net/KEM.806.24. S2CID   197607732.
  12. 1 2 Azeredo, B P; Sadhu, J; Ma, J; Jacobs, K; Kim, J; Lee, K; Eraker, J H; Li, X; Sinha, S; Fang, N; Ferreira, P; Hsu, K (7 June 2013). "Silicon nanowires with controlled sidewall profile and roughness fabricated by thin-film dewetting and metal-assisted chemical etching". Nanotechnology. 24 (22): 225305. doi:10.1088/0957-4484/24/22/225305. PMID   23644697. S2CID   6072818.
  13. ↑ Qiu, Teng; Chu, Paul K. (May 2008). "Self-selective electroless plating: An approach for fabrication of functional 1D nanomaterials". Materials Science and Engineering: R: Reports. 61 (1–6): 59–77. doi:10.1016/j.mser.2008.03.001.
  14. ↑ Uddin, Shahnawaz; Hashim, Md Roslan; Pakhuruddin, Mohd Zamir (June 2021). "Aluminium-assisted chemical etching for fabrication of black silicon". Materials Chemistry and Physics. 265: 124469. doi:10.1016/j.matchemphys.2021.124469. S2CID   233542194.
  15. ↑ Geyer, Nadine; Fuhrmann, Bodo; Huang, Zhipeng; de Boor, Johannes; Leipner, Hartmut S.; Werner, Peter (21 June 2012). "Model for the Mass Transport during Metal-Assisted Chemical Etching with Contiguous Metal Films As Catalysts". The Journal of Physical Chemistry C. 116 (24): 13446–13451. doi:10.1021/jp3034227.
  16. ↑ Li, Xiuling (April 2012). "Metal assisted chemical etching for high aspect ratio nanostructures: A review of characteristics and applications in photovoltaics". Current Opinion in Solid State and Materials Science. 16 (2): 71–81. doi:10.1016/j.cossms.2011.11.002.
  17. ↑ Lai, Ruby A.; Hymel, Thomas M.; Narasimhan, Vijay K.; Cui, Yi (13 April 2016). "Schottky Barrier Catalysis Mechanism in Metal-Assisted Chemical Etching of Silicon". ACS Applied Materials & Interfaces. 8 (14): 8875–8879. doi:10.1021/acsami.6b01020. OSTI   1579822. PMID   27018712.
  18. ↑ Kabalan, Amal. "A Comparative Study on the Effects of Passivation Methods on the Carrier Lifetime of RIE and MACE Silicon Micropillars." Applied Sciences 9.9 (2019): 1804.
  19. ↑ Backes, A., et al. "Influence of metallic catalyst and doping level on the metal assisted chemical etching of silicon." Scripta Materialia 114 (2016): 27-30.
  20. ↑ Chang, Shih‐Wei, et al. "Densely packed arrays of ultra‐high‐aspect‐ratio silicon nanowires fabricated using block‐copolymer lithography and metal‐assisted etching." Advanced functional materials 19.15 (2009): 2495-2500.
  21. ↑ Smith, Zachary R., Rosemary L. Smith, and Scott D. Collins. "Mechanism of nanowire formation in metal assisted chemical etching." Electrochimica Acta 92 (2013): 139-147.
  22. ↑ Lova, Paola; Robbiano, Valentina; Cacialli, Franco; Comoretto, Davide; Soci, Cesare (2018). "Black GaAs by Metal-Assisted Chemical Etching". ACS Applied Materials & Interfaces. 10 (39): 33434–33440. doi: 10.1021/acsami.8b10370 . PMID   30191706.
This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.