Flowers of sulfur

Last updated
Production of flowers of sulfur occurs mainly through sublimation of natural sulfur Sulfur-sample.jpg
Production of flowers of sulfur occurs mainly through sublimation of natural sulfur

Flowers of sulfur (British spelling flowers of sulphur) is a very fine, bright yellow sulfur powder that is produced by sublimation and deposition. It can contain up to 30% of the amorphous allotrope of sulfur, which is the noncrystalline structure of sulfur. [1] It is known as flores sulphuris by apothecaries and in older scientific works. Natural sulfur was also known as brimstone, hence the alternative name flowers of brimstone. [2]

Contents

Flowers of sulfur has unique properties. Production occurs mainly through sublimation of natural sulfur. According to The Sulphur Institute, flowers of sulphur is widely used due to its powdered structure in rubber vulcanization, agricultural dusts, pharmaceutical products, stock feeds. [1] It can also be used in Flowers of Sulfur (FoS) Tests.

Properties

Although similar to chemically pure sulfur, flowers of sulfur has slightly different properties. For instance, sulfur is completely soluble in sulfur dioxide. Flowers of sulfur, however, is insoluble in sulfur dioxide. A study shows that flowers of sulfur is only partially soluble in nitric acid and bromide. Residue still revealed traces of sulfur after the extraction. When lit on fire, flowers of sulfur combust and leave a residue that oxidizes immediately. Flowers of sulfur is completely soluble when heated in anhydrous liquid bromine. [3]

Production

Flowers of sulfur were traditionally produced by subliming naturally occurring sulfur, known as sulphur vivum. Impurities and moisture could cause acid residue in the product, so it was often washed, the result being known as "washed flowers of sulfur" (in Latin, flores sulphuris loti). Distillation of sulfur vapor can also yield flowers of sulfur, by slowly quenching to room temperature. [4]

Flowers of sulfur is commercially available and can be bought through chemical supply companies [5] as well as major e-commerce websites.

Uses

Historically, flowers of sulfur were extensively used medically to cure ailments, particularly skin diseases. [6] Sublimed sulfur was applied topically for skin diseases, but was also taken orally or injected for treatment of other diseases. Flowers of sulfur is seen to inhibit bacterial growth in tubercle bacilli, [7] and S. aureus, and C. hominis. [8] More recent sources also show that flowers of sulfur acts a fungicide, insecticide, and fumigant, as well as an agent in the treatment of numerous skin diseases. [5]

In the early 20th century, flowers of sulfur was also widely used for agricultural purposes. It was specifically used in cultivating hop plants to combat and prevent fungal diseases caused by molds that can kill crops. [9] Flowers of sulfur was also used to treat rosebushes similarly. [6] These cases show that flowers of sulfur was one of the earliest fungicides and insecticides used agriculturally. A study done in 1912 shows that a small amount of sulfur affects vegetation growth significantly. With 0.023 g flowers of sulfur per kg of soil, vegetation growth increased by 10 to 40%. [10]

Flowers of Sulfur (FoS) Tests have also been used to test porosity of metallic finishes over silver, copper, and copper alloy substrates. The original FoS test method was standardized by ASTM through ASTM-B809 which was established in 1990. The current version of the standard is ASTM B809-95(2018). This test method is especially good at precipitating silver based failures such as those observed with network chip resistors. [11] The Center for Advanced Life Cycle Engineering (CALCE) and the International Electronics Manufacturing Initiative (iNEMI) have both developed tests based on varying degrees to the ASTM standard.

Elemental sulfur vapour rises from the Pu`u `O`o Crater in Hawaii. The cooled sulfur vapour product is the yellow, powdery substance around the crater. Sulfur Fumarole (23998018863).jpg
Elemental sulfur vapour rises from the Puʻu ʻŌʻō Crater in Hawaii. The cooled sulfur vapour product is the yellow, powdery substance around the crater.

Flowers of Sulfur can be used as a humid sulfur vapor test for creep corrosion. [12] Creep corrosion is the corrosion of copper or silver caused by sulfur pollution and causes failure in electronic products. Sulfur pollution includes elemental sulfur, sulfur dioxide, and hydrogen sulfide, which can oxidize metals. [13] These compounds can be produced artificially or naturally. Paper mills, craters, and volcanoes are examples of sulfur sources. FoS provides a source of elemental sulfur that can be used to test conformal coatings and have caused creep corrosion on printed circuit boards (PCBs). [13] These tests use PCBs with copper or silver components and are dried by baking. The PCBs are then exposed to constant humidity, temperature, and impurities like sulfur and dust. Airflow and temperature are the only variables in this test that need to be controlled. [14] After a few days, the amount of corrosion and colour is noted. Various analytical methods can be used to examine the product’s surface morphology, surface composition, depth profiling, and metal foil thickness. These methods include X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), energy-dispersive x-ray spectroscopy (EDX), and atomic force microscopy (AFM). [12] A test has found that FoS causes significant creep corrosion due to its hydrophobicity. [13]

Related Research Articles

<span class="mw-page-title-main">Nitric acid</span> Highly corrosive mineral acid

Nitric acid is the inorganic compound with the formula HNO3. It is a highly corrosive mineral acid. The compound is colorless, but samples tend to acquire a yellow cast over time due to decomposition into oxides of nitrogen. Most commercially available nitric acid has a concentration of 68% in water. When the solution contains more than 86% HNO3, it is referred to as fuming nitric acid. Depending on the amount of nitrogen dioxide present, fuming nitric acid is further characterized as red fuming nitric acid at concentrations above 86%, or white fuming nitric acid at concentrations above 95%.

<span class="mw-page-title-main">Sulfur</span> Chemical element, symbol S and atomic number 16

Sulfur (also spelled sulphur in British English) is a chemical element; it has symbol S and atomic number 16. It is abundant, multivalent and nonmetallic. Under normal conditions, sulfur atoms form cyclic octatomic molecules with the chemical formula S8. Elemental sulfur is a bright yellow, crystalline solid at room temperature.

<span class="mw-page-title-main">Hydrogen sulfide</span> Poisonous, corrosive and flammable gas

Hydrogen sulfide is a chemical compound with the formula H2S. It is a colorless chalcogen-hydride gas, and is poisonous, corrosive, and flammable, with trace amounts in ambient atmosphere having a characteristic foul odor of rotten eggs. Swedish chemist Carl Wilhelm Scheele is credited with having discovered the chemical composition of purified hydrogen sulfide in 1777.

<span class="mw-page-title-main">Corrosion</span> Gradual destruction of materials by chemical reaction with its environment

Corrosion is a natural process that converts a refined metal into a more chemically stable oxide. It is the gradual deterioration of materials by chemical or electrochemical reaction with their environment. Corrosion engineering is the field dedicated to controlling and preventing corrosion.

A period 5 element is one of the chemical elements in the fifth row of the periodic table of the chemical elements. The periodic table is laid out in rows to illustrate recurring (periodic) trends in the chemical behaviour of the elements as their atomic number increases: a new row is begun when chemical behaviour begins to repeat, meaning that elements with similar behaviour fall into the same vertical columns. The fifth period contains 18 elements, beginning with rubidium and ending with xenon. As a rule, period 5 elements fill their 5s shells first, then their 4d, and 5p shells, in that order; however, there are exceptions, such as rhodium.

In physical chemistry and engineering, passivation is coating a material so that it becomes "passive", that is, less readily affected or corroded by the environment. Passivation involves creation of an outer layer of shield material that is applied as a microcoating, created by chemical reaction with the base material, or allowed to build by spontaneous oxidation in the air. As a technique, passivation is the use of a light coat of a protective material, such as metal oxide, to create a shield against corrosion. Passivation of silicon is used during fabrication of microelectronic devices. Undesired passivation of electrodes, called "fouling", increases the circuit resistance so it interferes with some electrochemical applications such as electrocoagulation for wastewater treatment, amperometric chemical sensing, and electrochemical synthesis.

Sulfide (British English also sulphide) is an inorganic anion of sulfur with the chemical formula S2− or a compound containing one or more S2− ions. Solutions of sulfide salts are corrosive. Sulfide also refers to large families of inorganic and organic compounds, e.g. lead sulfide and dimethyl sulfide. Hydrogen sulfide (H2S) and bisulfide (SH−) are the conjugate acids of sulfide.

<span class="mw-page-title-main">Tarnish</span> Corrosion on outer layer of some metals

Tarnish is a thin layer of corrosion that forms over copper, brass, aluminum, magnesium, neodymium and other similar metals as their outermost layer undergoes a chemical reaction. Tarnish does not always result from the sole effects of oxygen in the air. For example, silver needs hydrogen sulfide to tarnish, although it may tarnish with oxygen over time. It often appears as a dull, gray or black film or coating over metal. Tarnish is a surface phenomenon that is self-limiting, unlike rust. Only the top few layers of the metal react. The layer of tarnish seals and protects the underlying layers from reacting.

<span class="mw-page-title-main">Anodizing</span> Metal treatment process

Anodizing is an electrolytic passivation process used to increase the thickness of the natural oxide layer on the surface of metal parts.

<span class="mw-page-title-main">Hydrogen embrittlement</span> Reduction in ductility of a metal exposed to hydrogen

Hydrogen embrittlement (HE), also known as hydrogen-assisted cracking or hydrogen-induced cracking (HIC), is a reduction in the ductility of a metal due to absorbed hydrogen. Hydrogen atoms are small and can permeate solid metals. Once absorbed, hydrogen lowers the stress required for cracks in the metal to initiate and propagate, resulting in embrittlement. Hydrogen embrittlement occurs most notably in steels, as well as in iron, nickel, titanium, cobalt, and their alloys. Copper, aluminium, and stainless steels are less susceptible to hydrogen embrittlement.

<span class="mw-page-title-main">Ammonium sulfate</span> Chemical compound

Ammonium sulfate (American English and international scientific usage; ammonium sulphate in British English); (NH4)2SO4, is an inorganic salt with a number of commercial uses. The most common use is as a soil fertilizer. It contains 21% nitrogen and 24% sulfur.

In horticulture, lime sulfur (lime sulphur in British English, see American and British English spelling differences) is mainly a mixture of calcium polysulfides and thiosulfate (plus other reaction by-products as sulfite and sulfate) formed by reacting calcium hydroxide with elemental sulfur, used in pest control. It can be prepared by boiling in water a suspension of poorly soluble calcium hydroxide (lime) and solid sulfur together with a small amount of surfactant to facilitate the dispersion of these solids in water. After elimination of any residual solids (flocculation, decantation and filtration), it is normally used as an aqueous solution, which is reddish-yellow in colour and has a distinctive offensive odor of hydrogen sulfide (H2S, rotten eggs).

<span class="mw-page-title-main">Electroless nickel-phosphorus plating</span> Chemical-induced nickel coating of a surface

Electroless nickel-phosphorus plating, also referred to as E-nickel, is a chemical process that deposits an even layer of nickel-phosphorus alloy on the surface of a solid substrate, like metal or plastic. The process involves dipping the substrate in a water solution containing nickel salt and a phosphorus-containing reducing agent, usually a hypophosphite salt. It is the most common version of electroless nickel plating and is often referred by that name. A similar process uses a borohydride reducing agent, yielding a nickel-boron coating instead.

<span class="mw-page-title-main">Sulfur water</span> Water exposed to hydrogen sulfide gas

Sulfur water is a condition where water is exposed to hydrogen sulfide gas, giving a distinct "rotten egg" smell. This condition has different purposes in culture varying to health and implications to plumbing.

<span class="mw-page-title-main">Mixed flowing gas testing</span>

Mixed flowing gas (MFG) is a type of laboratory environmental testing for products, particularly electronics, to evaluate resistance to corrosion due to gases in the atmosphere. Mixed Flowing Gas (MFG) test is a laboratory test in which the temperature (°C), relative humidity (%RH), concentration of gaseous pollutants (in parts per billion, ppb or parts per million ppm level), and other critical variables (such as volume exchange rate and airflow rate) are carefully defined, monitored and controlled. The purpose of this test is to simulate corrosion phenomenon due to atmospheric exposure. The electronic product is exposed to gases such as chlorine, hydrogen sulfide, nitrogen dioxide, and sulfur dioxide at levels in the parts per billion range, in a controlled environmental chamber. Test samples that have been exposed to MFG testing have ranged from bare metal surfaces, to electrical connectors, and to complete assemblies. In regards to noble metal plated connector applications, MFG testing has been widely accepted as a qualification test method to evaluate the performance of these connectors.

Sulfur concrete, sometimes named thioconcrete or sulfurcrete, is a composite construction material, composed mainly of sulfur and aggregate. Cement and water, important compounds in normal concrete, are not part of sulfur concrete. The concrete is heated above the melting point of elemental sulfur at ca. 140 °C (284 °F) in a ratio of between 12% and 25% sulfur, the rest being aggregate.

<span class="mw-page-title-main">Conservation and restoration of silver objects</span> Preservation of heritage collections

The conservation and restoration of silver objects is an activity dedicated to the preservation and protection of objects of historical and personal value made from silver. When applied to cultural heritage this activity is generally undertaken by a conservator-restorer.

<span class="mw-page-title-main">Flowers of sulfur tests</span>

Flowers of sulfur (FOS) testing was developed to determine the porosity of metallic coatings susceptible to sulfur induced corrosion [see below ASTM B809-95(2018)]. Applicable substrates are silver, copper, copper alloys and any other metal or metal alloy with which sulfur will react. For porosity testing, coatings can be single or multiple layers of any metal that is not corroded and sealed by a self-limiting reaction in the reducing sulfur environment of the FOS test. The simplest recommended technique is to identify any porosity of the coating as revealed by the presence of surface spots. These surface spots form where the environmental sulfur has penetrated and reacted with the base metal, producing a metal sulfide. Chalcocite, copper (I) sulfide is dark-grey to black. Silver (I) sulfide is also grey-black.

<span class="mw-page-title-main">Kesternich test</span>

The Kesternich test is a common name for the corrosion test with sulfur dioxide (SO2) under general moisture condensation. This test was developed in 1951 by Wilhelm Kesternich to simulate the damaging effects of acid rain. Acid rain and acidic industrial pollutants are corrosive and can degrade coatings and plated surfaces. Kesternich testing, or sulfur dioxide testing, simulates acid rain or industrial chemical exposure to evaluate the relative corrosion resistance of the coating, substrate, or part itself. The test can be used for coatings or for base materials. The test method is defined by various standards, DIN EN ISO 6988, DIN 50018, ASTM G87, ISO 3231, ISO 22479 are the most common. The parts to be tested are placed in a test chamber with a capacity of 300L and exposed to warm, moist air in combination with a certain amount of sulfur dioxide

<span class="mw-page-title-main">Potassium thiosulfate</span> Chemical compound

Potassium thiosulfate, commonly abbreviated KTS, is an inorganic compound with the formula K2S2O3. This salt can form multiple hydrates, such as the monohydrate, dihydrate, and the pentahydrate, all of which are white or colorless solids. It is used as a fertilizer.

References

  1. 1 2 "About Sulfur". Glossary. The Sulphur Institute. Retrieved 2022-10-26.
  2. ↑ "A Popular Course on Chemistry: VIII Suflur". Magazine of Popular Science, and Journal of the Useful Arts. Vol. 4. 1837. p. 392.
  3. ↑ Bjerregaard AP (November 1919). "A Method for Bringing Elementary Sulfur into Solution for Analysis". Journal of Industrial & Engineering Chemistry. 11 (11): 1055. doi:10.1021/ie50119a019. ISSN   0095-9014.
  4. ↑ Meyer B (January 1976). Emeléus HJ, Sharpe AG (eds.). "The Structures of Elemental Sulfur". Advances in Inorganic Chemistry and Radiochemistry. 18. Academic Press: 287–317. doi:10.1016/S0065-2792(08)60032-1. ISBN   9780120236183.
  5. 1 2 "Flowers Of Sulfur | Spectrum". www.spectrumchemical.com. Retrieved 2016-11-28.
  6. 1 2 Lewis W (1799). The New Dispensatory (Sixth ed.). F. Wingrave. pp. 458–461.
  7. ↑ Lawson GB (June 1934). "The Inhibitory Action of Sulphur on the Growth of Tubercle Bacilli". American Review of Tuberculosis. 29 (6): 650–651. doi:10.1164/art.1934.29.6.650 (inactive 31 January 2024). ISSN   0096-0381.{{cite journal}}: CS1 maint: DOI inactive as of January 2024 (link)
  8. ↑ Weld JT, Gunther A (April 1947). "The Antibacterial Properties of Sulfur". The Journal of Experimental Medicine. 85 (5): 531–542. doi:10.1084/jem.85.5.531. PMC   2135706 . PMID   19871634.
  9. ↑ Amos A (1910-03-04). "The Uses of Sulphur in the Cultivation and Curing of Hops". Journal of the Institute of Brewing. 16 (2): 142–163. doi:10.1002/j.2050-0416.1910.tb04691.x. ISSN   2050-0416.
  10. ↑ Boullanger E (1912). "Action du Soufre en Fleur sur la Végétation" [The Action of Flower of Sulfur on Vegetation]. Comptes rendus de l'Académie des Sciences[Proceedings of the Academy of Sciences] (in French). 154: 369–70 – via CAplus.
  11. ↑ Osterman M, Utter R (March 2021). "Is Our Silver Corrosion Measurement Correct? Research Note". Journal of Electronic Materials. 50 (3): 939–940. Bibcode:2021JEMat..50..939O. doi:10.1007/s11664-020-08640-7. ISSN   0361-5235. S2CID   230113122.
  12. 1 2 Lee, Dem; Chen, Cheng Chih; Lee, Jeffrey ChangBing; Liou, Peggy (October 2014). "The effect of the pre-treatment of metal foil on Sulfur's Corrosive Reaction Rate in Flower of Sulfur test". 2014 9th International Microsystems, Packaging, Assembly and Circuits Technology Conference (IMPACT). Taipei, Taiwan: IEEE. pp. 96–101. doi:10.1109/IMPACT.2014.7048429. ISBN   978-1-4799-7727-7. S2CID   40267401.
  13. 1 2 3 Isaacs, Phil; Zhang, Jing; Munson, Terry (February 2020). "Understanding Creep Corrosion Field Fails". 2020 Pan Pacific Microelectronics Symposium (Pan Pacific). HI, USA: IEEE. pp. 1–6. doi:10.23919/PanPacific48324.2020.9059471. ISBN   978-1-944543-14-3. S2CID   215740547.
  14. ↑ Fu, H.; Singh, Prabjit; Campbell, L.; Zhang, Jing (2014). "Testing Printed Circuit Boards for Creep Corrosion in Flowers of Sulfur Chamber" (PDF). S2CID   11958801.

This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.