Impregnation resin

Last updated

Impregnation resins are slightly viscous, organic liquids that are used in the forest products industry for wood modification. They typically contain formaldehyde and are composed of dimers and trimers of the main molecule. These can become polymer solutions upon curing inside of a wood substrate, imparting stabilizing properties. Impregnation of these resins involves a vacuum chamber procedure that completely disperses the resin into the wood. Once inside of the wood, the resin can diffuse into the cell wall and enhance the physical strength of the wood even further. [1]

Contents

Applications

Impregnation resins were designed to be used in the forest products industry to modify wood and enhance its natural properties. Wood impregnation resins typically are designed to end up inside wood cell walls, where they generally increase strength, hardness, dimensional stability, and resistance to decay. [2] In recent years, interest in wood, or lumber, has increased because less energy is needed to convert trees into wood than what is required by other building materials. [3] Although wood does have advantages over other building materials, it also has major disadvantages. Wood swells in high humidity and shrinks when the air is dry. [4] It can also decay if allowed to stay moist for extended periods, and has variable properties from board to board. Resin impregnation can improve all these properties. The impregnation of resins into wood substrate involves a vacuum treatment process that disperses a monomer solution throughout the finer structures inside of the wood. Polymerization of the resin is accomplished by curing with heat, setting the impregnation resin into a solid substance state. Impregnating the wood with resin followed by curing bulks the cell wall of the wood and imparts enhanced properties. [1] Demand for impregnating resins is proliferating across the globe due to increased efficiency in the overall electric insulation process of automotive and electronic parts.

While there are no new commercial developments with impregnation resins for wood modification, there are constant innovations being discovered in industry and research institutes. [5]

Types of impregnation resins

Phenol-formaldehyde resins

Main products of phenol reacting with formaldehyde in a PF resin: mono-, di-, and trimethylol phenol (left to right) Mono, di, trimethylol phenol.svg
Main products of phenol reacting with formaldehyde in a PF resin: mono-, di-, and trimethylol phenol (left to right)

Phenol-formaldehyde resins (PF) were the first commercially relevant impregnation resins, made by reacting phenol and formaldehyde, creating a polymer network inside of the wood upon curing. [7] Phenol can react with formaldehyde at the ortho and para positions, generating mono, di, and trimethylolphenol as the reaction products. [6] Besides being the first synthetic polymers to be commercialized, [7] studies show that PF resins have superior performance over other resins in terms of imparting strength, stability, and decay resistance to the wood substrate. [1] The dimensional stability displayed by the wood samples impregnated with PF resins is mostly a function of the mass of resin inside the wood cell wall. [8] [9] [10] PF impregnated wood is sometimes called impreg. Before curing, PF resins act as cell wall plasticizer, allowing wood to be compressed more easily. After cure, the PF prevents wood from springing back. This has been used to make high density, very hard wood products, known as “compreg” or “staybwood”. [11] The increase in both strength and stability of the wood is due to the cross-linking of the resin components and the resin's ability to bulk the cell wall. PF is black, obscuring any natural color of the wood.

Urea-formaldehyde resins

The basic reaction of urea and formaldehyde to create a urea-formaldehyde resin, followed by the condensation Urea formaldehyde.jpg
The basic reaction of urea and formaldehyde to create a urea-formaldehyde resin, followed by the condensation

Urea-formaldehyde resins (UF) are a class of impregnation resins for wood modification made by reacting urea with formaldehyde. This resin can be polymerized after impregnation into the wood substrate by oven-curing. UF resins are beginning to be used less in the wood modification industry due to the fact that they are less durable than other impregnation resins and do not stand up well to harsh weather conditions. [13] When exposed to water, UF resins can hydrolyze to release formaldehyde out of the wood substrate. [14] For this reason, they are mostly used as impregnation resins when the wood substrate will be used for indoor purposes. [13] Wood is modified for outdoor use to improve stability against weather conditions, therefore PF resins are more suitable for this purpose. [1]

Melamine-formaldehyde resins

Melamine reacting with formaldehyde to form hexamethylolmelamine Melaminmethyloles.png
Melamine reacting with formaldehyde to form hexamethylolmelamine

Melamine formaldehyde resins (MF) are a class of impregnation resins for wood modification that are made by reacting melamine with formaldehyde in a condensation of these two monomers. Melamine formaldehyde resins are unique because they have heat and fire-resistant properties that would add extra improvement to wood substrates besides the normal impregnation resin benefits. They are also clear, allowing the finished product to have any color or pattern. This has led to their widespread use, for example in countertops under the trade name formica. The fire-resistant properties are derived from the nitrogen contained in melamine, which releases as a gas when it is exposed to high heat and can extinguish a flame. [15] Melamine is also a heat sink, and this is beneficial because it can absorb a large amount of energy in the form of heat. It further helps the fire-resistant properties because once exposed to flame, melamine forms a layer of char on the wood substrate and this protects the more combustible groups of the wood and the polymer. [16] Although MF resins have this extra benefit, it is difficult to use them for impregnation resins because of the high free formaldehyde content. [1] In industry, there are strict regulations in place to keep the amount of free formaldehyde in any given product below a certain detectable limit. These regulations help keep people and animals coming in contact with these products safe because formaldehyde is an irritant and can be harmful at higher levels. [17] Adding urea to MF resins has been shown to lower the amount of free formaldehyde below the legal limit and is often used for this purpose. [1] Another complication with MF resins is the low solubility of melamine in water. [16] Because of this and the free formaldehyde content, MF resins are not used as commonly in the field of wood modification.

Resin specifications

Impregnation resins are required to have the following properties in order to be successful in wood modification: [1]

Ability to flow deeply into the wood

Cut-away drawing of a wood cell wall Cut-away drawing of a wood cell wall.gif
Cut-away drawing of a wood cell wall

The ideal condition for modification by impregnation is to have the resin flow deeply into the wood structure and access all the cells. [18] Most wood cells are shaped like hollow straws, millimeters long and tens of microns wide, with a hollow center. [19] Resin flows through the lumen and pit network, ideally gaining access to all the cells, and then ideally the resin enters the cell walls by diffusion. To flow deeply into the wood, low viscosity resin without particles is necessary because of the long and tortuous path with many narrow points. Even with an ideal resin, pits can be aspirated from drying, keeping all resin out of a cell. [20]

Small size of resin molecules

There is very little free volume even in water saturated wood cell walls, so large molecules, such as most resins of even at only 1000 molecular weight (~ 5 monomers), cannot enter. [21] The smaller the impregnating molecule, the more mass of resin can be loaded into the cell wall. Having low molecular weight also keeps viscosity low, which improves flow through the lumen and pit structure. [22]

Contain soluble/polar components

Impregnation resins need to be soluble in polar solvents because they are often diluted with water during the procedure. This is also a key factor because polar solvents help swell the cell wall of the wood and make it easier for the resin to diffuse into the interior of the wall. The resin molecules themselves should also be polar enough to have an affinity to the cell wall and the components of it. [1] The main components of wood's cell wall are cellulose, hemicellulose, and lignin, all of which have polar components that can have an affinity for a polar impregnation resin.

Impregnation process

The most widely used method to saturate wood with impregnation resins is by a vacuum treatment process. [23] This process uses a sealable vessel to contain the wooden samples while they are in treatment. After the samples have been oven-dried and placed into the vessel, a vacuum is pulled up to a certain psi depending on the procedure. Then the resin of choice is introduced into the vessel by a backfilling process and remains in a vacuum pulled state for the amount of time dictated by the procedure. Once the samples have been under vacuum for a sufficient amount of time for the resin to enter the wood the vacuum is released, and the samples remain in the resin solution to allow diffusion to happen. [24] Diffusion is not controlled by the vacuum stage of the process, it is purely controlled by time. [1] If the resin meets all of the required specifications, it will diffuse into the cell wall and the impregnation process will be complete. [1]

See also

Related Research Articles

<span class="mw-page-title-main">Bakelite</span> First synthetic plastic

Bakelite, formally poly­oxy­benzyl­methylene­glycol­anhydride, is a thermosetting phenol formaldehyde resin, formed from a condensation reaction of phenol with formaldehyde. The first plastic made from synthetic components, it was developed by Leo Baekeland in Yonkers, New York, in 1907, and patented on December 7, 1909.

<span class="mw-page-title-main">Formaldehyde</span> Organic compound (H–CHO); simplest aldehyde

Formaldehyde ( for-MAL-di-hide, fər-) (systematic name methanal) is an organic compound with the chemical formula CH2O and structure H−CHO, more precisely H2C=O. The compound is a pungent, colourless gas that polymerises spontaneously into paraformaldehyde. It is stored as aqueous solutions (formalin), which consists mainly of the hydrate CH2(OH)2. It is the simplest of the aldehydes (R−CHO). As a precursor to many other materials and chemical compounds, in 2006 the global production of formaldehyde was estimated at 12 million tons per year. It is mainly used in the production of industrial resins, e.g., for particle board and coatings. Small amounts also occur naturally.

<span class="mw-page-title-main">Engineered wood</span> Range of derivative wood products engineered for uniform and predictable structural performance

Engineered wood, also called mass timber, composite wood, human-made wood, or manufactured board, includes a range of derivative wood products which are manufactured by binding or fixing the strands, particles, fibres, or veneers or boards of wood, together with adhesives, or other methods of fixation to form composite material. The panels vary in size but can range upwards of 64 by 8 feet and in the case of cross-laminated timber (CLT) can be of any thickness from a few inches to 16 inches (410 mm) or more. These products are engineered to precise design specifications, which are tested to meet national or international standards and provide uniformity and predictability in their structural performance. Engineered wood products are used in a variety of applications, from home construction to commercial buildings to industrial products. The products can be used for joists and beams that replace steel in many building projects. The term mass timber describes a group of building materials that can replace concrete assemblies.

<span class="mw-page-title-main">Oriented strand board</span> Engineered wood particle board

Oriented strand board (OSB) is a type of engineered wood similar to particle board, formed by adding adhesives and then compressing layers of wood strands (flakes) in specific orientations. It was invented by Armin Elmendorf in California in 1963. OSB may have a rough and variegated surface with the individual strips of around 2.5 cm × 15 cm, lying unevenly across each other, and is produced in a variety of types and thicknesses.

<span class="mw-page-title-main">Medium-density fibreboard</span> Engineered wood product

Medium-density fibreboard (MDF) is an engineered wood product made by breaking down hardwood or softwood residuals into wood fibre, often in a defibrator, combining it with wax and a resin binder, and forming it into panels by applying high temperature and pressure. MDF is generally denser than plywood. It is made up of separated fibre but can be used as a building material similar in application to plywood. It is stronger and denser than particle board.

<span class="mw-page-title-main">Thermosetting polymer</span> Polymer obtained by irreversibly hardening (curing) a resin

In materials science, a thermosetting polymer, often called a thermoset, is a polymer that is obtained by irreversibly hardening ("curing") a soft solid or viscous liquid prepolymer (resin). Curing is induced by heat or suitable radiation and may be promoted by high pressure or mixing with a catalyst. Heat is not necessarily applied externally, and is often generated by the reaction of the resin with a curing agent. Curing results in chemical reactions that create extensive cross-linking between polymer chains to produce an infusible and insoluble polymer network.

<span class="mw-page-title-main">Phenol formaldehyde resin</span> Chemical compound

Phenol formaldehyde resins (PF) are synthetic polymers obtained by the reaction of phenol or substituted phenol with formaldehyde. Used as the basis for Bakelite, PFs were the first commercial synthetic resins. They have been widely used for the production of molded products including billiard balls, laboratory countertops, and as coatings and adhesives. They were at one time the primary material used for the production of circuit boards but have been largely replaced with epoxy resins and fiberglass cloth, as with fire-resistant FR-4 circuit board materials.

<span class="mw-page-title-main">Formica (plastic)</span> Brand of composite materials

Formica Laminate is a laminated composite material invented at the Westinghouse Electric Corporation in the United States in 1912. Originally used to replace mica in electrical applications, it has since been manufactured for multiple applications. It has been produced by Formica Group manufacturing sites across the globe since. Formica Group are best known for the company's classic product: a heat-resistant, wipe-clean laminate of paper with melamine resin.

<span class="mw-page-title-main">Particle board</span> Glued wood product

Particle board, also known as particleboard or chipboard, is an engineered wood product, belonging to the wood-based panels, manufactured from wood chips and a synthetic, mostly formaldehyde based resin or other suitable binder, which is pressed under a hot press, batch- or continuous- type, and produced. Particle board is often confused with oriented strand board, a different type of fiberboard that uses machined wood flakes and offers more strength.

Urea-formaldehyde (UF), also known as urea-methanal, so named for its common synthesis pathway and overall structure, is a nontransparent thermosetting resin or polymer. It is produced from urea and formaldehyde. These resins are used in adhesives, plywood, particle board, medium-density fibreboard (MDF), and molded objects. In agriculture, urea-formaldehyde compounds are one of the most commonly used types of slow-release fertilizer.

Wood glue is an adhesive used to tightly bond pieces of wood together. Many substances have been used as glues. Traditionally animal proteins like casein from milk or collagen from animal hides and bones were boiled down to make early glues. They worked by solidifying as they dried. Later, glues were made from plant starches like flour or potato starch. When combined with water and heated, the starch gelatinizes and forms a sticky paste as it dries. Plant-based glues were common for books and paper products, though they can break down more easily over time compared to animal-based glues. Examples of modern wood glues include polyvinyl acetate (PVA) and epoxy resins. Some resins used in producing composite wood products may contain formaldehyde. As of 2021, “the wood panel industry uses almost 95% of synthetic petroleum-derived thermosetting adhesives, mainly based on urea, phenol, and melamine, among others”.

<span class="mw-page-title-main">Polybenzoxazine</span> Type of bicyclic heterocyclic monomer

Polybenzoxazines, also called benzoxazine resins, are cured polymerization products derived from benzoxazine monomers.

<span class="mw-page-title-main">Melamine resin</span> Hard, thermosetting plastic material often used in dinnerware

Melamine resin or melamine formaldehyde is a resin with melamine rings terminated with multiple hydroxyl groups derived from formaldehyde. This thermosetting plastic material is made from melamine and formaldehyde. In its butylated form, it is dissolved in n-butanol and xylene. It is then used to cross-link with alkyd, epoxy, acrylic, and polyester resins, used in surface coatings. There are many types, varying from very slow to very fast curing.

Polymer engineering is generally an engineering field that designs, analyses, and modifies polymer materials. Polymer engineering covers aspects of the petrochemical industry, polymerization, structure and characterization of polymers, properties of polymers, compounding and processing of polymers and description of major polymers, structure property relations and applications.

A thermoset polymer matrix is a synthetic polymer reinforcement where polymers act as binder or matrix to secure in place incorporated particulates, fibres or other reinforcements. They were first developed for structural applications, such as glass-reinforced plastic radar domes on aircraft and graphite-epoxy payload bay doors on the Space Shuttle.

In polymer chemistry, in situ polymerization is a preparation method that occurs "in the polymerization mixture" and is used to develop polymer nanocomposites from nanoparticles. There are numerous unstable oligomers (molecules) which must be synthesized in situ for use in various processes. The in situ polymerization process consists of an initiation step followed by a series of polymerization steps, which results in the formation of a hybrid between polymer molecules and nanoparticles. Nanoparticles are initially spread out in a liquid monomer or a precursor of relatively low molecular weight. Upon the formation of a homogeneous mixture, initiation of the polymerization reaction is carried out by addition of an adequate initiator, which is exposed to a source of heat, radiation, etc. After the polymerization mechanism is completed, a nanocomposite is produced, which consists of polymer molecules bound to nanoparticles.

Formaldehyde resin may refer to:

<span class="mw-page-title-main">Decorative laminate</span> Laminated composite material primarily used as a finish for furniture and wall panels

Decorative laminates are laminated products primarily used as furniture surface materials or wall paneling. It can be manufactured as either high- or low-pressure laminate, with the two processes not much different from each other except for the pressure applied in the pressing process. Also, laminate can be produced either in batches or in a continuous process; the latter is called continuous pressure laminate (CPL).

Wood stabilization is a series of processes which use pressure and/or vacuum to impregnate wood cellular structure with certain monomers, acrylics, phenolics or other resins to improve dimensional stability and/or material properties. When exposed to moisture through humidity absorption or direct immersion, most wood species will expand and change shape. When moisture comes into contact with wood, the water molecules penetrate the cell wall and become bound to cell wall components through hydrogen bonding. With addition of water to the cell wall, wood volume increases nearly proportionally to the volume of water added. Swelling increases until the fiber saturation point has been reached. Wood stabilization limits water absorption into the wood structure, thereby limiting the dimensional changes which arise from moisture exposure.

<span class="mw-page-title-main">Furfurylated wood</span> Type of modified wood that is treated with furfuryl alcohol

Furfurylated wood is the end product of treating wood with furfuryl alcohol. This chemical process is also called furfurylation. Furfurylation is a commercially used wood modification process to enhance the physical, mechanical and biological properties of wood. In this process -which is based on principles of wood science- the cell walls of the wood swell with furfuryl alcohol, which polymerizes within the cell walls. This treatment reduces the water absorption capacity of the wood, thus minimizing its tendency to deform with changes in moisture. The hardness and rot resistance of the modified wood are also improved compared to natural, untreated wood. The furfuryl alcohol used is obtained through the hydrogenation of furfural from biological agriwaste residues, such as husks and bagasse.

References

  1. 1 2 3 4 5 6 7 8 9 10 Hill, Callum A. S. (2006). Wood Modification: Chemical, Thermal and Other Processes - Hill - Wiley Online Library. doi:10.1002/0470021748. ISBN   9780470021743.
  2. ↑ Hill, C.A.S. Wood Modification: Chemical, Thermal, and Other Processes; John Wiley and Sons: New York, 2006.
  3. ↑ Bergman, R.; Puettmann, M.; Taylor, A.; Skog, K.E. The Carbon Impacts of Wood Products. Forest Products J. 2014, 64, 220-231 https://www.fpl.fs.fed.us/documnts/pdf2014/fpl_2014_bergman007.pdf Archived 2022-08-15 at the Wayback Machine
  4. ↑ Glass, S.V.; Zelinka, S.L. Moisture Relations and Physical Properties of Wood, Chapter 4. In Wood Handbook: Wood as an Engineering Material, Ross, R., Ed. USDA Forest Products Laboratory: Madison, WI, 2010 https://www.fpl.fs.fed.us/documnts/fplgtr/fplgtr190/chapter_04.pdf Archived 2022-06-04 at the Wayback Machine
  5. ↑ Hill, Callum (2011-05-01). Wood modification: An update. Vol. 6.
  6. 1 2 Goldstein, Irving; Dreher, William; Jeroski, Edward; Nielson, J. F.; Oberley, William; Weaver, J. W. (1959-10-01). "Wood Processing. Inhibiting Against Swelling Decay". Industrial & Engineering Chemistry. 51 (10): 1313–1317. doi:10.1021/ie50598a042. ISSN   0019-7866.
  7. 1 2 "Phenol-formaldehyde resin | chemical compound". Encyclopedia Britannica. Retrieved 2018-03-15.
  8. ↑ Furuno, T.; Imamura, Y.; Kajita, H. The modification of wood by treatment with low molecular weight phenol-formaldehyde resin: A properties enhancement with neutralized phenolic-resin and resin penetration into wood cell walls. Wood Sci.Technol. 2004, 37, 349-361, doi:https://doi.org/10.1007/s00226-003-0176-6.
  9. ↑ Ohmae, K.; Minato, K.; Norimoto, M. The analysis of dimensional changes due to chemical treatments and water soaking for hinoki (Chamaecyparis obtusa) wood. Holzforschung 2002, 56, 98-102, doi:https://doi.org/10.1515/HF.2002.016
  10. ↑ Stamm, A.J. Chapter 19: Dimensional Stabilization. In Wood and Cellulose Science, The Ronald Press Co: New York, 1964.
  11. ↑ Ibach, R.E. Ch 19:Specialty treatments. In Wood handbook: wood as an engineering material: chapter General technical report FPL; GTR-190. Madison, WI: US Dept. of Agriculture, Forest Service, Forest Products Laboratory, 2010 https://www.fpl.fs.fed.us/documnts/fplgtr/fpl_gtr190.pdf Archived 2021-04-24 at the Wayback Machine
  12. ↑ CROW (2015). "Urea-Formaldehyde Resins". Polymer Properties Database.
  13. 1 2 "Urea-formaldehyde resin | chemical compound". Encyclopedia Britannica. Retrieved 2018-03-16.
  14. ↑ Myers, George E. (1986-08-08). "Mechanisms of Formaldehyde Release from Bonded Wood Products". Formaldehyde Release from Wood Products. ACS Symposium Series. Vol. 316. American Chemical Society. pp. 87–106. doi:10.1021/bk-1986-0316.ch008. ISBN   978-0841209824.
  15. ↑ CROW (2015). "MF Resins". Polymer Properties Database.
  16. 1 2 "Melamine - Flame Retardants". fr.polymerinsights.com. Archived from the original on 2018-03-17. Retrieved 2018-03-16.
  17. ↑ EPA, OCSPP, US (2016-07-08). "Formaldehyde Emission Standards for Composite Wood Products | US EPA". US EPA. Retrieved 2018-03-16.
  18. ↑ Rowell, R. Chemical modification of wood. In Handbook of Wood Chemistry and Wood Composites, Rowell, R., Ed. Taylor & Francis: Boca Raton, FL, 2005; pp. 381-420.
  19. ↑ Wiedenhoeft, A. Chapter 3: Structure and function of wood. In Wood handbook: wood as an engineering material General technical report FPL GTR-190, Ross, R., Ed. US Dept. of Agriculture, Forest Service, Forest Products Laboratory: Madison, WI, 2010. https://www.fpl.fs.fed.us/documnts/fplgtr/fplgtr190/chapter_03.pdf Archived 2020-03-05 at the Wayback Machine
  20. ↑ Shmulsky, R.; Jones, P.D. Forest products and wood science: an introduction, 7th ed.; John Wiley & Sons: 2019.
  21. ↑ Hunt, C.G.; Frihart, C.R.; Dunky, M.; Rohumaa, A. Understanding Wood Bonds; Going Beyond What Meets the Eye: A Critical Review. Rev. Adhes. Adhes. 2018, 6, 369–440, doi : 10.7569/raa.2018.097312; https://www.fpl.fs.fed.us/documnts/pdf2018/fpl_2018_hunt002.pdf Archived 2022-01-20 at the Wayback Machine
  22. ↑ Wan, H.; Kim, M.G. Distribution of phenol-formaldehyde resin in impregnated southern pine and effects on stabilization. Wood Fiber Sci. 2008, 40, 181-189.
  23. ↑ Moore, Gregory R.; Kline, Donald E.; Blankenhorn, Paul R. (2007-06-27). "Impregnation of Wood With a High Viscosity Epoxy Resin". Wood and Fiber Science. 15 (3): 223–234. ISSN   0735-6161.
  24. ↑ Stamm, Alfred J.; Hansen, L. A. (1935-12-01). "Minimizing Wood Shrinkage and Swelling". Industrial & Engineering Chemistry. 27 (12): 1480–1484. doi:10.1021/ie50312a022. ISSN   0019-7866.
This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.