Laser beam welding

Last updated
A robot performs remote fibre laser welding.

Laser beam welding (LBW) is a welding technique used to join pieces of metal or thermoplastics through the use of a laser. The beam provides a concentrated heat source, allowing for narrow, deep welds and high welding rates. The process is frequently used in high volume and precision requiring applications using automation, as in the automotive and aeronautics industries. It is based on keyhole or penetration mode welding.

Contents

Operation

Like electron-beam welding (EBW), laser beam welding has high power density (on the order of 1 MW/cm2) resulting in small heat-affected zones and high heating and cooling rates. The spot size of the laser can vary between 0.2 mm and 13 mm, though only smaller sizes are used for welding. The depth of penetration is proportional to the amount of power supplied, but is also dependent on the location of the focal point: penetration is maximized when the focal point is slightly below the surface of the workpiece

A continuous or pulsed laser beam may be used depending upon the application. Millisecond-long pulses are used to weld thin materials such as razor blades while continuous laser systems are employed for deep welds.

LBW is a versatile process, capable of welding carbon steels, HSLA steels, stainless steel, aluminum, and titanium. Due to high cooling rates, cracking is a concern when welding high-carbon steels. The weld quality is high, similar to that of electron beam welding. The speed of welding is proportional to the amount of power supplied but also depends on the type and thickness of the workpieces. The high power capability of gas lasers make them especially suitable for high volume applications. LBW is particularly dominant in the automotive industry. [1] [2]

Some of the advantages of LBW in comparison to EBW are:

A derivative of LBW, laser-hybrid welding, combines the laser of LBW with an arc welding method such as gas metal arc welding (GMAW). This combination allows for greater positioning flexibility, since GMAW supplies molten metal to fill the joint, and due to the use of a laser, increases the welding speed over what is normally possible with GMAW. Weld quality tends to be higher as well, since the potential for undercutting is reduced. [5]

Equipment

Automation and CAM

Although laser beam welding can be accomplished by hand, most systems are automated and use a system of computer aided manufacturing based on computer aided designs. [6] [7] [8] Laser welding can also be coupled with milling to form a finished part. [9]

In 2016 the RepRap project, which historically worked on fused filament fabrication, expanded to development of open source laser welding systems. [10] Such systems have been fully characterized and can be used in a wide scale of applications while reducing conventional manufacturing costs.

Lasers

Solid state

Solid-state lasers operate at wavelengths on the order of 1  micrometer, much shorter than gas lasers used for welding, and as a result require that operators wear special eyewear or use special screens to prevent retina damage. Nd:YAG lasers can operate in both pulsed and continuous mode, but the other types are limited to pulsed mode. The original and still popular solid-state design is a single crystal shaped as a rod approximately 20 mm in diameter and 200 mm long, and the ends are ground flat. This rod is surrounded by a flash tube containing xenon or krypton. When flashed, a pulse of light lasting about two milliseconds is emitted by the laser. Disk shaped crystals are growing in popularity in the industry, and flashlamps are giving way to diodes due to their high efficiency. Typical power output for ruby lasers is 1020 W, while the Nd:YAG laser outputs between 0.046,000 W. To deliver the laser beam to the weld area, fiber optics are usually employed.

Gas

Gas lasers use high-voltage, low-current power sources to supply the energy needed to excite the gas mixture used as a lasing medium. These lasers can operate in both continuous and pulsed mode, and the wavelength of the CO2 gas laser beam is 10.6 μm, deep infrared, i.e. 'heat'. Fiber optic cable absorbs and is destroyed by this wavelength, so a rigid lens and mirror delivery system is used. Power outputs for gas lasers can be much higher than solid-state lasers, reaching 25  kW. [11]

Fiber

In fiber lasers, the main medium is the optical fiber itself. They are capable of power up to 50 kW and are increasingly being used for robotic industrial welding.

Laser beam delivery

Modern laser beam welding machines can be grouped into two types. In the traditional type, the laser output is moved to follow the seam. This is usually achieved with a robot. In many modern applications, remote laser beam welding is used. In this method, the laser beam is moved along the seam with the help of a laser scanner, so that the robotic arm does not need to follow the seam any more. The advantages of remote laser welding are the higher speed and the higher precision of the welding process.

Thermal modeling of pulsed-laser welding

Pulsed-laser welding has advantages over continuous wave (CW) laser welding. Some of these advantages are lower porosity and less spatter. [12] Pulsed-laser welding also has some disadvantages such as causing hot cracking in aluminum alloys. [2] Thermal analysis of the pulsed-laser welding process can assist in prediction of welding parameters such as depth of fusion, cooling rates, and residual stresses. Due to the complexity of the pulsed laser process, it is necessary to employ a procedure that involves a development cycle. The cycle involves constructing a mathematical model, calculating a thermal cycle using numerical modeling techniques like either finite elemental modeling (FEM) or finite difference method (FDM) or analytical models with simplifying assumptions, and validating the model by experimental measurements.

A methodology combining some of the published models involves: [13] [14] [15]

  1. Determining the power absorption efficiency.
  2. Calculating the recoil pressure based on temperatures and a Clausius-Clapeyron equation.
  3. Calculate the fluid flow velocities using the volume of fluid method (VOF).
  4. Calculating the temperature distribution.
  5. Increment time and repeat steps 1–4.
  6. Validating of results

Step 1

Not all radiant energy is absorbed and turned into heat for welding. Some of the radiant energy is absorbed in the plasma created by vaporizing and then subsequently ionizing the gas. In addition, the absorptivity is affected by the wavelength of the beam, the surface composition of the material being welded, the angle of incidence, and the temperature of the material. [12]

Rosenthal point source assumption leaves an infinitely high temperature discontinuity which is addressed by assuming a Gaussian distribution instead. Radiant energy is also not uniformly distributed within the beam. Some devices produce Gaussian energy distributions, whereas others can be bimodal. [12] A Gaussian energy distribution can be applied by multiplying the power density by a function like this: [14] , where r is the radial distance from the center of the beam, =beam radius or spot size.

Using a temperature distribution instead of a point source assumption allows for easier calculation of temperature-dependent material properties such as absorptivity. On the irradiated surface, when a keyhole is formed, Fresnel reflection (the almost complete absorption of the beam energy due to multiple reflection within the keyhole cavity) occurs and can be modeled by , where ε is a function of dielectric constant, electric conductivity, and laser frequency. θ is the angle of incidence. [13] Understanding the absorption efficiency is key to calculating thermal effects.

Step 2

Lasers can weld in one of two modes: conduction and keyhole. Which mode is in operation depends on whether the power density is sufficiently high enough to cause evaporation. [12] Conduction mode occurs below the vaporization point while keyhole mode occurs above the vaporization point. The keyhole is analogous to an air pocket. The air pocket is in a state of flux. Forces such as the recoil pressure of the evaporated metal open the keyhole [13] while gravity (aka hydrostatic forces) and metal surface tension tend to collapse it. [15] At even higher power densities, the vapor can be ionized to form a plasma.

The recoil pressure is determined by using the Clausius-Clapeyron equation. [14] , where P is the equilibrium vapor pressure, T is the liquid surface temperature, HLV is the latent heat of vaporization, TLV is the equilibrium temperature at the liquid-vapor interface. Using the assumption that the vapor flow is limited to sonic velocities, [8] one gets that , where Po is atmospheric pressure and Pr is recoil pressure.

Step 3

This pertains to keyhole profiles. Fluid flow velocities are determined by [13]

where is the velocity vector, P=pressure, ρ= mass density, =viscosity, β=thermal expansion coefficient, g=gravity, and F is the volume fraction of fluid in a simulation grid cell.

Step 4

In order to determine the boundary temperature at the laser impingement surface, you would apply an equation like this. , [15] where kn=the thermal conductivity normal to the surface impinged on by the laser, h=convective heat transfer coefficient for air, σ is the Stefan–Boltzmann constant for radiation, and ε is the emissivity of the material being welded on, q is laser beam heat flux.

Unlike CW (Continuous Wave) laser welding which involves one moving thermal cycle, pulsed laser involves repetitively impinging on the same spot, thus creating multiple overlapping thermal cycles. [15] A method of addressing this is to add a step function that multiplies the heat flux by one when the beam is on but multiplies the heat flux by zero when the beam is off. [14] One way [15] to achieve this is by using a Kronecker delta which modifies q as follows: , where δ= the Kronecker delta, qe=experimentally determined heat flux. The problem with this method, is it does not allow you to see the effect of pulse duration. One way [14] of solving this is to a use a modifier that is time-dependent function such as:

where v= pulse frequency, n=0,1, 2,...,v-1), τ= pulse duration.

Next, you would apply this boundary condition and solve for Fourier's 2nd Law to obtain the internal temperature distribution. Assuming no internal heat generation, the solution is , where k=thermal conductivity, ρ=density, Cp=specific heat capacity, =fluid velocity vector.

Step 5

Incrementing is done by discretizing the governing equations presented in the previous steps and applying the next time and length steps.

Step 6

Results can be validated by specific experimental observations or trends from generic experiments. These experiments have involved metallographic verification of the depth of fusion. [9]

Consequences of simplifying assumptions

The physics of pulsed laser can be very complex and therefore, some simplifying assumptions need to be made to either speed up calculation or compensate for a lack of materials properties. The temperature-dependence of material properties such as specific heat are ignored to minimize computing time.

The liquid temperature can be overestimated if the amount of heat loss due to mass loss from vapor leaving the liquid-metal interface is not accounted for. [14]

See also

Related Research Articles

<span class="mw-page-title-main">Bremsstrahlung</span> Electromagnetic radiation due to deceleration of charged particles

In particle physics, bremsstrahlung is electromagnetic radiation produced by the deceleration of a charged particle when deflected by another charged particle, typically an electron by an atomic nucleus. The moving particle loses kinetic energy, which is converted into radiation, thus satisfying the law of conservation of energy. The term is also used to refer to the process of producing the radiation. Bremsstrahlung has a continuous spectrum, which becomes more intense and whose peak intensity shifts toward higher frequencies as the change of the energy of the decelerated particles increases.

<span class="mw-page-title-main">Kinetic theory of gases</span> Understanding of gas properties in terms of molecular motion

The kinetic theory of gases is a simple classical model of the thermodynamic behavior of gases. It treats a gas as composed of numerous particles, too small to see with a microscope, which are constantly in random motion. Their collisions with each other and with the walls of their container are used to explain physical properties of the gas—for example, the relationship between its temperature, pressure, and volume. The particles are now known to be the atoms or molecules of the gas.

<span class="mw-page-title-main">Composite material</span> Material made from a combination of two or more unlike substances

A composite material is a material which is produced from two or more constituent materials. These constituent materials have notably dissimilar chemical or physical properties and are merged to create a material with properties unlike the individual elements. Within the finished structure, the individual elements remain separate and distinct, distinguishing composites from mixtures and solid solutions. Composite materials with more than one distinct layer are called composite laminates.

<span class="mw-page-title-main">Airy disk</span> Diffraction pattern in optics

In optics, the Airy disk and Airy pattern are descriptions of the best-focused spot of light that a perfect lens with a circular aperture can make, limited by the diffraction of light. The Airy disk is of importance in physics, optics, and astronomy.

<span class="mw-page-title-main">Laser cutting</span> Technology that uses a laser to cut materials

Laser cutting is a technology that uses a laser to vaporize materials, resulting in a cut edge. While typically used for industrial manufacturing applications, it is now used by schools, small businesses, architecture, and hobbyists. Laser cutting works by directing the output of a high-power laser most commonly through optics. The laser optics and CNC are used to direct the laser beam to the material. A commercial laser for cutting materials uses a motion control system to follow a CNC or G-code of the pattern to be cut onto the material. The focused laser beam is directed at the material, which then either melts, burns, vaporizes away, or is blown away by a jet of gas, leaving an edge with a high-quality surface finish.

The classical XY model is a lattice model of statistical mechanics. In general, the XY model can be seen as a specialization of Stanley's n-vector model for n = 2.

<span class="mw-page-title-main">Dendrite (metal)</span>

A dendrite in metallurgy is a characteristic tree-like structure of crystals growing as molten metal solidifies, the shape produced by faster growth along energetically favourable crystallographic directions. This dendritic growth has large consequences in regard to material properties.

Time-domain thermoreflectance is a method by which the thermal properties of a material can be measured, most importantly thermal conductivity. This method can be applied most notably to thin film materials, which have properties that vary greatly when compared to the same materials in bulk. The idea behind this technique is that once a material is heated up, the change in the reflectance of the surface can be utilized to derive the thermal properties. The reflectivity is measured with respect to time, and the data received can be matched to a model with coefficients that correspond to thermal properties.

Sum frequency generation spectroscopy (SFG) is a nonlinear laser spectroscopy technique used to analyze surfaces and interfaces. It can be expressed as a sum of a series of Lorentz oscillators. In a typical SFG setup, two laser beams mix at an interface and generate an output beam with a frequency equal to the sum of the two input frequencies, traveling in a direction allegedly given by the sum of the incident beams' wavevectors. The technique was developed in 1987 by Yuen-Ron Shen and his students as an extension of second harmonic generation spectroscopy and rapidly applied to deduce the composition, orientation distributions, and structural information of molecules at gas–solid, gas–liquid and liquid–solid interfaces. Soon after its invention, Philippe Guyot-Sionnest extended the technique to obtain the first measurements of electronic and vibrational dynamics at surfaces. SFG has advantages in its ability to be monolayer surface sensitive, ability to be performed in situ, and its capability to provide ultrafast time resolution. SFG gives information complementary to infrared and Raman spectroscopy.

In numerical analysis, von Neumann stability analysis is a procedure used to check the stability of finite difference schemes as applied to linear partial differential equations. The analysis is based on the Fourier decomposition of numerical error and was developed at Los Alamos National Laboratory after having been briefly described in a 1947 article by British researchers John Crank and Phyllis Nicolson. This method is an example of explicit time integration where the function that defines governing equation is evaluated at the current time. Later, the method was given a more rigorous treatment in an article co-authored by John von Neumann.

<span class="mw-page-title-main">Multiple-prism dispersion theory</span> Theory in optics

The first description of multiple-prism arrays, and multiple-prism dispersion, was given by Newton in his book Opticks. Prism pair expanders were introduced by Brewster in 1813. A modern mathematical description of the single-prism dispersion was given by Born and Wolf in 1959. The generalized multiple-prism dispersion theory was introduced by Duarte and Piper in 1982.

The Fréedericksz transition is a phase transition in liquid crystals produced when a sufficiently strong electric or magnetic field is applied to a liquid crystal in an undistorted state. Below a certain field threshold the director remains undistorted. As the field value is gradually increased from this threshold, the director begins to twist until it is aligned with the field. In this fashion the Fréedericksz transition can occur in three different configurations known as the twist, bend, and splay geometries. The phase transition was first observed by Fréedericksz and Repiewa in 1927. In this first experiment of theirs, one of the walls of the cell was concave so as to produce a variation in thickness along the cell. The phase transition is named in honor of the Russian physicist Vsevolod Frederiks.

<span class="mw-page-title-main">Multiple-prism grating laser oscillator</span>

Multiple-prism grating laser oscillators, or MPG laser oscillators, use multiple-prism beam expansion to illuminate a diffraction grating mounted either in Littrow configuration or grazing-incidence configuration. Originally, these narrow-linewidth tunable dispersive oscillators were introduced as multiple-prism Littrow (MPL) grating oscillators, or hybrid multiple-prism near-grazing-incidence (HMPGI) grating cavities, in organic dye lasers. However, these designs were quickly adopted for other types of lasers such as gas lasers, diode lasers, and more recently fiber lasers.

The near-horizon metric (NHM) refers to the near-horizon limit of the global metric of a black hole. NHMs play an important role in studying the geometry and topology of black holes, but are only well defined for extremal black holes. NHMs are expressed in Gaussian null coordinates, and one important property is that the dependence on the coordinate is fixed in the near-horizon limit.

Satellite surface salinity refers to measurements of surface salinity made by remote sensing satellites. The radiative properties of the ocean surface are exploited in order to estimate the salinity of the water's surface layer.

In physics and engineering, the radiative heat transfer from one surface to another is the equal to the difference of incoming and outgoing radiation from the first surface. In general, the heat transfer between surfaces is governed by temperature, surface emissivity properties and the geometry of the surfaces. The relation for heat transfer can be written as an integral equation with boundary conditions based upon surface conditions. Kernel functions can be useful in approximating and solving this integral equation.

In combustion, Frank-Kamenetskii theory explains the thermal explosion of a homogeneous mixture of reactants, kept inside a closed vessel with constant temperature walls. It is named after a Russian scientist David A. Frank-Kamenetskii, who along with Nikolay Semenov developed the theory in the 1930s.

<span class="mw-page-title-main">Moving heat source model for thin plates</span>

In heat transfer, moving heat sources is an engineering problems, particularly in welding. In the early 20th century, welding engineers began studying moving heat sources in thin plates, both empirically and theoretically. Depending on welding parameters, plate geometry and material properties, the solution takes three different forms: semi-infinite, intermediate, or thin plate. The temperature distribution and cooling rates can be determined from theoretical solutions to the problem, allowing engineers to better understand the consequences of heat sources on weldability and end item performance.

In combustion, Clarke's equation is a third-order nonlinear partial differential equation, first derived by John Frederick Clarke in 1978. The equation describes the thermal explosion process, including both effects of constant-volume and constant-pressure processes, as well as the effects of adiabatic and isothermal sound speeds. The equation reads as

In plasma physics and magnetic confinement fusion, neoclassical transport or neoclassical diffusion is a theoretical description of collisional transport in toroidal plasmas, usually found in tokamaks or stellerators. It is a modification of classical diffusion adding in effects of non-uniform magnetic fields due to the toroidal geometry, which give rise to new diffusion effects.

References

  1. Cary and Helzer, p 210
  2. 1 2 Cieslak, M. (1988). "On the weldability, composition, and hardness of pulsed and continuous Nd: YAG laser welds in aluminum alloys 6061, 5456, and 5086". Metallurgical Transactions B. 9 (2): 319–329. doi:10.1007/BF02654217. S2CID   135498572.
  3. "Ensuring the Quality of Laser Welds". Element. Retrieved 2022-05-31.
  4. "Laser Beam Welding - an overview | ScienceDirect Topics". www.sciencedirect.com. Retrieved 2022-05-31.
  5. Weman, p 98
  6. Reinhart, G., Munzert, U. and Vogl, W., 2008. A programming system for robot-based remote-laser-welding with conventional optics. CIRP Annals-Manufacturing Technology, 57(1), pp.37-40.
  7. Kim, P., Rhee, S. and Lee, C.H., 1999. Automatic teaching of welding robot for free-formed seam using laser vision sensor. Optics and Lasers in Engineering, 31(3), pp.173-182.
  8. 1 2 Cline, H. E.; Anthony, T. R. (1977-09-01). "Heat treating and melting material with a scanning laser or electron beam". Journal of Applied Physics. 48 (9): 3895–3900. doi:10.1063/1.324261. ISSN   0021-8979.
  9. 1 2 Sabbaghzadeh, Jamshid; Azizi, Maryam; Torkamany, M. Javad (2008). "Numerical and experimental investigation of seam welding with a pulsed laser". Optics & Laser Technology. 40 (2): 289–296. doi:10.1016/j.optlastec.2007.05.005.
  10. John J. Laureto, Serguei V. Dessiatoun, Michael M. Ohadi and Joshua M. Pearce. Open Source Laser Polymer Welding System: Design and Characterization of Linear Low-Density Polyethylene Multilayer Welds. Machines 2016, 4(3), 14; doi: 10.3390/machines4030014
  11. Cary and Helzer, p 209
  12. 1 2 3 4 Steen, William M.; Mazumder, Jyotirmoy (2010). Laser Material Processing. doi:10.1007/978-1-84996-062-5. ISBN   978-1-84996-061-8.
  13. 1 2 3 4 Lee, Jae Y.; Ko, Sung H.; Farson, Dave F.; Yoo, Choong D. (2002). "Mechanism of keyhole formation and stability in stationary laser welding". Journal of Physics D: Applied Physics. 35 (13): 1570. doi:10.1088/0022-3727/35/13/320. ISSN   0022-3727. S2CID   250782960.
  14. 1 2 3 4 5 6 Chen, Guibo; Gu, Xiuying; Bi, Juan (2016). "Numerical analysis of thermal effect in aluminum alloy by repetition frequency pulsed laser". Optik. 127 (20): 10115–10121. doi:10.1016/j.ijleo.2016.08.010.
  15. 1 2 3 4 5 Frewin (January 1999). "Finite Element Model of Pulsed Laser Welding". Welding Journal. 78: 15–2.

Bibliography