Alkaline anion-exchange membrane fuel cell

Last updated

An alkaline anion-exchange membrane fuel cell (AAEMFC), also known as anion-exchange membrane fuel cells (AEMFCs), alkaline membrane fuel cells (AMFCs), hydroxide-exchange membrane fuel cells (HEMFCs), or solid alkaline fuel cells (SAFCs) is a type of alkaline fuel cell that uses an anion-exchange membrane to separate the anode and cathode compartments.

Contents

Alkaline fuel cells (AFCs) are based on the transport of alkaline anions, usually hydroxide OH−
, between the electrodes. Original AFCs used aqueous potassium hydroxide (KOH) as an electrolyte. The AAEMFCs use instead a polymer membrane that transports hydroxide anions.

Alkaline Anion-Exchange Membrane Fuel Cell AAEMFC.png
Alkaline Anion-Exchange Membrane Fuel Cell

Mechanism

In an AAEMFC, the fuel, hydrogen or methanol, is supplied at the anode and oxygen through air, and water are supplied at cathode. Fuel is oxidized at anode and oxygen is reduced at cathode. At cathode, oxygen reduction produces hydroxides ions (OH−) that migrate through the electrolyte towards the anode. At anode, hydroxide ions react with the fuel to produce water and electrons. Electrons go through the circuit producing current. [1]

Electrochemical reactions when hydrogen is the fuel:

At Anode: H2 + 2OH− → 2H2O + 2e−

At cathode: O2 + 2H2O + 4e− → 4OH−

Electrochemical reactions when methanol is the fuel:

At anode: CH3OH + 6OH− → CO2 + 5H2O + 6e-

At cathode: 3/2O2 + 3H2O + 6e− → 6OH−

Mechanical properties

Measuring mechanical properties

The mechanical properties of anion-exchange membranes are relevant for use in electrochemical energy technologies such as polymer electrolyte membranes in fuel cells. Mechanical properties of polymers include the elastic modulus, tensile strength, and ductility. Traditional tensile stress-strain test used to measure these properties are very sensitive to the experimental procedure because the mechanical properties of polymers are heavily dependent on the nature of the environment such as the presence of water, organic solvents, oxygen, and temperature. [2] [3] Increasing the temperature generally results in a decrease of elastic modulus, a reduction of tensile strength, and an increase of ductility, assuming there is no modification of the microstructure. Near the glass transition temperature, very significant changes in mechanical properties is observed. Dynamic Mechanical Analysis (DMA) is a widely used complimentary, characterization technique for measuring the mechanical properties of polymers including the storage modulus and loss modulus as functions of temperature.

Methods of Increasing Mechanical Properties

One method of increasing the mechanical properties of polymers used for anion-exchange membranes (AEM) is substituting conventional ternary amine and anion exchange groups with grafted quaternary groups. [4] These ionomers results in large storage and Young's moduli, a high tensile strength, and high ductility. Exchanging the counterion from hydroxide to hydrogen carbonate, carbonate, and chloride ions further enhances the strength and elastic modulus of the membranes. Narducci and colleagues concluded that the water uptake, related to the type of anion, plays a very important role for the mechanical properties. [4] Zhang and colleagues prepared a series of robust and crosslinked poly(2,6-dimethyl-1,4-phenylene oxide)s (PPO) AEMs with chemically stable imidazolium cations through quaternization of C1, C3, C4-substituted imidazole and crosslinking them via "thiol-ene" chemistry. [5] These crosslinked AEMs showed excellent film forming properties and exhibited a higher tensile strength owing to the increased entanglement interactions in the polymer chains which in turn increased the water up take. This strong relation between water uptake and mechanical properties mirrors the findings of Narducci and colleagues. [5] The findings of Zhang et al. suggest that the crosslinking of anion conductive materials with stable sterically-protected organic cations is an effective strategy to produce robust AEMs for use in alkaline fuel cells.

Comparison with traditional alkaline fuel cell

The alkaline fuel cell used by NASA in 1960s for Apollo and Space Shuttle program generated electricity at nearly 70% efficiency using aqueous solution of KOH as an electrolyte. In that situation, CO2 coming in through oxidant air stream and generated as by product from oxidation of methanol, if methanol is the fuel, reacts with electrolyte KOH forming CO32−/HCO3−. Unfortunately as a consequence, K2CO3 or KHCO3 precipitate on the electrodes. However, this effect has found to be mitigated by the removal of cationic counterions from the electrode, and carbonate formation has been found to be entirely reversible by several industrial and academic groups, most notably Varcoe. Low-cost CO2 systems have been developed using air as the oxidant source. [6] In alkaline anion-exchange membrane fuel cell, aqueous KOH is replaced with a solid polymer electrolyte membrane, that can conduct hydroxide ions. This could overcome the problems of electrolyte leakage and carbonate precipitation, though still taking advantage of benefits of operating a fuel cell in an alkaline environment. In AAEMFCs, CO2 reacts with water forming H2CO3, which further dissociate to HCO3− and CO32−. The equilibrium concentration of CO32−/HCO3− is less than 0.07% and there is no precipitation on the electrodes in the absence of cations (K+, Na+). [7] [8] The absence of cations is, however, difficult to achieve, as most membranes are conditioned to functional hydroxide or bicarbonate forms out of their initial, chemically stable halogen form, and may significantly impact fuel cell performance by both competitively adsorbing to active sites and exerting Helmholtz-layer effects. [9]

In comparison, against alkaline fuel cell, alkali anion-exchange membrane fuel cells also protect the electrode from solid carbonate precipitation, which can cause fuel (oxygen/hydrogen) transport problem during start-up. [10]

The large majority of membranes/ionomer that have been developed are fully hydrocarbon, allowing for much easier catalyst recycling and lower fuel crossover. Methanol has an advantage of easier storage and transportation and has higher volumetric energy density compared to hydrogen. Also, methanol crossover from anode to cathode is reduced in AAEMFCs compared to PEMFCs, due to the opposite direction of ion transport in the membrane, from cathode to anode. In addition, use of higher alcohols such as ethanol and propanol is possible in AAEMFCs, since anode potential in AAEMFCs is sufficient to oxidize C-C bonds present in alcohols. [11] [8]

Challenges

The biggest challenge in developing AAEMFCs is the anion-exchange membrane (AEM). A typical AEM is composed of a polymer backbone with tethered cationic ion-exchange groups to facilitate the movement of free OH− ions. This is the inverse of Nafion used for PEMFCs, where an anion is covalently attached to the polymer and protons hop from one site to another. The challenge is to fabricate AEM with high OH− ion conductivity and mechanical stability without chemical deterioration at elevated pH and temperatures. The main mechanisms of degradation are Hofmann elimination when β-hydrogens are present and direct nucleophilic attack by OH− ion at the cationic site. One approach towards improving the chemical stability towards Hofmann elimination is to remove all β-hydrogens at the cationic site. All these degradation reactions limit the polymer backbone chemistries and the cations that can be incorporated for developing AEM.

Another challenge is achieving OH− ion conductivity comparable to H+ conductivity observed in PEMFCs. Since the diffusion coefficient of OH− ions is half that of H+ (in bulk water), a higher concentration of OH− ions is needed to achieve similar results, which in turn needs higher ion-exchange capacity of the polymer. [12] However, high ion-exchange capacity leads to excessive swelling of polymer on hydration and concomitant loss of mechanical properties.

Management of water in AEMFCs has also been shown to be a challenge. Recent research has shown [13] that careful balancing of the humidity of the feed gases significantly improves fuel cell performance.

See also

Related Research Articles

<span class="mw-page-title-main">Fuel cell</span> Device that converts the chemical energy from a fuel into electricity

A fuel cell is an electrochemical cell that converts the chemical energy of a fuel and an oxidizing agent into electricity through a pair of redox reactions. Fuel cells are different from most batteries in requiring a continuous source of fuel and oxygen to sustain the chemical reaction, whereas in a battery the chemical energy usually comes from substances that are already present in the battery. Fuel cells can produce electricity continuously for as long as fuel and oxygen are supplied.

<span class="mw-page-title-main">Electrolysis</span> Technique in chemistry and manufacturing

In chemistry and manufacturing, electrolysis is a technique that uses direct electric current (DC) to drive an otherwise non-spontaneous chemical reaction. Electrolysis is commercially important as a stage in the separation of elements from naturally occurring sources such as ores using an electrolytic cell. The voltage that is needed for electrolysis to occur is called the decomposition potential. The word "lysis" means to separate or break, so in terms, electrolysis would mean "breakdown via electricity."

An electrolyte is a medium containing ions that are electrically conductive through the movement of those ions, but not conducting electrons. This includes most soluble salts, acids, and bases dissolved in a polar solvent, such as water. Upon dissolving, the substance separates into cations and anions, which disperse uniformly throughout the solvent. Solid-state electrolytes also exist. In medicine and sometimes in chemistry, the term electrolyte refers to the substance that is dissolved.

The chloralkali process is an industrial process for the electrolysis of sodium chloride (NaCl) solutions. It is the technology used to produce chlorine and sodium hydroxide, which are commodity chemicals required by industry. Thirty five million tons of chlorine were prepared by this process in 1987. The chlorine and sodium hydroxide produced in this process are widely used in the chemical industry.

<span class="mw-page-title-main">Proton-exchange membrane fuel cell</span> Power generation technology

Proton-exchange membrane fuel cells (PEMFC), also known as polymer electrolyte membrane (PEM) fuel cells, are a type of fuel cell being developed mainly for transport applications, as well as for stationary fuel-cell applications and portable fuel-cell applications. Their distinguishing features include lower temperature/pressure ranges and a special proton-conducting polymer electrolyte membrane. PEMFCs generate electricity and operate on the opposite principle to PEM electrolysis, which consumes electricity. They are a leading candidate to replace the aging alkaline fuel-cell technology, which was used in the Space Shuttle.

<span class="mw-page-title-main">Alkaline fuel cell</span> Type of fuel cell

The alkaline fuel cell (AFC), also known as the Bacon fuel cell after its British inventor, Francis Thomas Bacon, is one of the most developed fuel cell technologies. Alkaline fuel cells consume hydrogen and pure oxygen, to produce potable water, heat, and electricity. They are among the most efficient fuel cells, having the potential to reach 70%.

<span class="mw-page-title-main">Zinc–air battery</span> High-electrical energy density storage device

A zinc–air battery is a metal–air electrochemical cell powered by the oxidation of zinc with oxygen from the air. During discharge, a mass of zinc particles forms a porous anode, which is saturated with an electrolyte. Oxygen from the air reacts at the cathode and forms hydroxyl ions which migrate into the zinc paste and form zincate, releasing electrons to travel to the cathode. The zincate decays into zinc oxide and water returns to the electrolyte. The water and hydroxyl from the anode are recycled at the cathode, so the water is not consumed. The reactions produce a theoretical voltage of 1.65 Volts, but is reduced to 1.35–1.4 V in available cells.

A proton-exchange membrane, or polymer-electrolyte membrane (PEM), is a semipermeable membrane generally made from ionomers and designed to conduct protons while acting as an electronic insulator and reactant barrier, e.g. to oxygen and hydrogen gas. This is their essential function when incorporated into a membrane electrode assembly (MEA) of a proton-exchange membrane fuel cell or of a proton-exchange membrane electrolyser: separation of reactants and transport of protons while blocking a direct electronic pathway through the membrane.

<span class="mw-page-title-main">Electrolysis of water</span> Electricity-induced chemical reaction

Electrolysis of water is using electricity to split water into oxygen and hydrogen gas by electrolysis. Hydrogen gas released in this way can be used as hydrogen fuel, but must be kept apart from the oxygen as the mixture would be extremely explosive. Separately pressurised into convenient 'tanks' or 'gas bottles', hydrogen can be used for oxyhydrogen welding and other applications, as the hydrogen / oxygen flame can reach approximately 2,800°C.

Direct-ethanol fuel cells or DEFCs are a category of fuel cell in which ethanol is fed directly into the cell. They have been used as a model to investigate a range of fuel cell concepts including the use of PEM.

Gas diffusion electrodes (GDE) are electrodes with a conjunction of a solid, liquid and gaseous interface, and an electrical conducting catalyst supporting an electrochemical reaction between the liquid and the gaseous phase.

Chlorine gas can be produced by extracting from natural materials, including the electrolysis of a sodium chloride solution (brine) and other ways.

The Glossary of fuel cell terms lists the definitions of many terms used within the fuel cell industry. The terms in this fuel cell glossary may be used by fuel cell industry associations, in education material and fuel cell codes and standards to name but a few.

An anion exchange membrane (AEM) is a semipermeable membrane generally made from ionomers and designed to conduct anions but reject gases such as oxygen or hydrogen.

The lithium–air battery (Li–air) is a metal–air electrochemical cell or battery chemistry that uses oxidation of lithium at the anode and reduction of oxygen at the cathode to induce a current flow.

Electrodeionization (EDI) is a water treatment technology that utilizes DC power, ion exchange membranes, and ion exchange resin to deionize water. EDI is typically employed as a polishing treatment following reverse osmosis (RO), and is used in the production of ultrapure water. It differs from other RO polishing methods, like chemically regenerated mixed beds, by operating continuously without chemical regeneration.

An ion-exchange membrane is a semi-permeable membrane that transports certain dissolved ions, while blocking other ions or neutral molecules.

A polymer electrolyte is a polymer matrix capable of ion conduction. Much like other types of electrolyte—liquid and solid-state—polymer electrolytes aid in movement of charge between the anode and cathode of a cell. The use of polymers as an electrolyte was first demonstrated using dye-sensitized solar cells. The field has expanded since and is now primarily focused on the development of polymer electrolytes with applications in batteries, fuel cells, and membranes.

<span class="mw-page-title-main">Anion exchange membrane electrolysis</span> Splitting of water using a semipermeable membrane

Anion exchange membrane(AEM) electrolysis is the electrolysis of water that utilises a semipermeable membrane that conducts hydroxide ions (OH−) called an anion exchange membrane. Like a proton-exchange membrane (PEM), the membrane separates the products, provides electrical insulation between electrodes, and conducts ions. Unlike PEM, AEM conducts hydroxide ions. The major advantage of AEM water electrolysis is that a high-cost noble metal catalyst is not required, low-cost transition metal catalyst can be used instead. AEM electrolysis is similar to alkaline water electrolysis, which uses a non-ion-selective separator instead of an anion-exchange membrane.

References

  1. ↑ Winter, M; Brodd, R. J. (2004). "What are batteries, fuel cells, and supercapacitors?". Chemical Reviews. 104 (10): 4245–4269. doi: 10.1021/cr020730k . PMID   15669155.
  2. ↑ Knauth, Philippe; Di Vona, Maria Luisa, eds. (2012-01-27). Solid State Proton Conductors. doi:10.1002/9781119962502. ISBN   9781119962502.
  3. ↑ Majsztrik, Paul W.; Bocarsly, Andrew B.; Benziger, Jay B. (2008-11-18). "Viscoelastic Response of Nafion. Effects of Temperature and Hydration on Tensile Creep". Macromolecules. 41 (24): 9849–9862. Bibcode:2008MaMol..41.9849M. doi:10.1021/ma801811m. ISSN   0024-9297.
  4. 1 2 Narducci, Riccardo; Chailan, J.-F.; Fahs, A.; Pasquini, Luca; Vona, Maria Luisa Di; Knauth, Philippe (2016). "Mechanical properties of anion exchange membranes by combination of tensile stress–strain tests and dynamic mechanical analysis". Journal of Polymer Science Part B: Polymer Physics. 54 (12): 1180–1187. Bibcode:2016JPoSB..54.1180N. doi:10.1002/polb.24025. ISSN   1099-0488.
  5. 1 2 Zhang, Xiaojuan; Cao, Yejie; Zhang, Min; Huang, Yingda; Wang, Yiguang; Liu, Lei; Li, Nanwen (2020-02-15). "Enhancement of the mechanical properties of anion exchange membranes with bulky imidazolium by "thiol-ene" crosslinking". Journal of Membrane Science. 596: 117700. doi:10.1016/j.memsci.2019.117700. ISSN   0376-7388. S2CID   213381503.
  6. ↑ "Operating Method of Anion-Exchange Membrane-Type Fuel Cell".
  7. ↑ Adams, L. A.; Varcoe, J. R. (2008). "A carbon dioxide tolerant aqueouselectrolyte-free anion-exchange membrane alkaline fuel cell" (PDF). ChemSusChem. 1 (1–2): 79–81. doi:10.1002/cssc.200700013. PMID   18605667. Archived from the original (PDF) on 2018-07-20.
  8. 1 2 Shen, P. K.; Xu, C. (2005). Adv. Fuel Cells: 149–179.{{cite journal}}: CS1 maint: untitled periodical (link)
  9. ↑ Mills, J. N.; McCrum, I. T.; Janik, M. J. (2014). Phys. Chem. Chem. Phys. 16 (27): 13699–13707. Bibcode:2014PCCP...1613699M. doi:10.1039/c4cp00760c. PMID   24722828.{{cite journal}}: CS1 maint: untitled periodical (link)
  10. ↑ Anion Exchange Membrane and Ionomer for Alkaline Membrane Fuel Cells Archived December 7, 2008, at the Wayback Machine
  11. ↑ Varcoe, J. R.; Slade, R. C. T. (2005). "Prospects for Alkaline Anion-Exchange Membranes in Low Temperature Fuel Cells" (PDF). Fuel Cells. 5 (2): 187–200. doi:10.1002/fuce.200400045. S2CID   18476566.
  12. ↑ Agel, E; Bouet, J.; Fauvarque, J.F (2001). "Characterization and use of anionic membranes for alkaline fuel cells". Journal of Power Sources. 101 (2): 267–274. Bibcode:2001JPS...101..267A. doi:10.1016/s0378-7753(01)00759-5.
  13. ↑ Omasta, T.J.; Wang, L.; Peng, X.; Lewis, C.A.; Varcoe, J.R.; Mustain, W.E. (2017). "Importance of balancing membrane and electrode water in anion-exchange membrane fuel cells" (PDF). Journal of Power Sources. 375: 205–213. doi:10.1016/j.jpowsour.2017.05.006.
This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.