Architectural terracotta

Last updated
The Bell Edison Telephone Building in Birmingham is a late 19th-century red brick and architectural terracotta building Bell Edison Telephone Building.jpg
The Bell Edison Telephone Building in Birmingham is a late 19th-century red brick and architectural terracotta building

Architectural terracotta refers to a fired mixture of clay and water that can be used in a non-structural, semi-structural, or structural capacity on the exterior or interior of a building. [1] Terracotta pottery, as earthenware is called when not used for vessels, is an ancient building material that translates from Latin as "baked earth". Some architectural terracotta is actually stronger than stoneware. It can be unglazed, painted, slip glazed, or glazed. A piece of terracotta is composed of a hollow clay web enclosing a void space or cell. The cell can be installed in compression with mortar or hung with metal anchors; such cells are often partially backfilled with mortar.

Contents

By the late 19th century the version with a ceramic glaze, namely glazed architectural terracotta, became more popular. Terracotta can be used together with brick, for ornamental areas; if the source of the clay is the same they can be made to harmonize, or if different to contrast. It is also often a cladding over a different structural material.

Chemistry

Terracotta is made of a clay or silt matrix, a fluxing agent, and grog or bits of previously fired clay. Clays are the remnants of weathered rocks that are smaller than 2 microns. They are composed of silica and alumina. Kaolinite, halloysite, montmorillonite, illite and mica are all good types of clays for ceramic production. When mixed with water they create hydrous aluminum silica that is plastic and moldable. During the firing process the clays lose their water and become a hardened ceramic body.

Fluxes add oxygen when they burn to create more uniform melting of the silica particles throughout the body of the ceramic. This increases the strength of the material. Common fluxing materials are calcium carbonate, alkaline feldspars, manganese, and iron oxides. Grog is used to prevent shrinking and provide structure for the fine clay matrix. [2]

History

Terracotta was made by the ancient Greeks, Babylonians, ancient Egyptians, Romans, Chinese, and the Indus River Valley and Native American cultures. It was used for roof tiles, medallions, statues, capitals and other small architectural details. [3]

Ancient Eastern terracotta

Brick temple in Bhitargaon, Kanpur Brick temple Bhitargaon Kanpur.jpg
Brick temple in Bhitargaon, Kanpur

Indian terracotta manufacturers hand pressed, poured, and double-molded the clay mix. Plaster casts have been found in several ancient sites in Afghanistan, Bangladesh, [4] India and Pakistan. [5] Similarities in motifs and manufacturing processes have caused scholars to note cross cultural pollination between the Hellenic and Indus River Valley sculptural terracotta traditions. [6] Famous early examples include the Bhitargaon temple and the Jain temple in the Mahbubnagar district.

Chinese, Korean, and Japanese terracotta making traditions were focused on non-architectural uses such as statuary or cookware but various forms of terracotta tiles were popular roofing materials. [7]

Western terracotta

Antiquity–1700s

Greeks used terracotta for capitals, friezes, and other elements of their temples like at Olympia or Selenius. [8] Domestically they used it for statuary and roof tiles. The Etruscans used terracotta for roof tiles, encased beams, and enclosed brick walls with it. The Roman terracotta innovation was the underfloor or hypocaust heating system that they used for their bath houses. [9] Medieval European architecture did not expand terracotta use beyond the ancients. The manufacture of tile roofs diminished with low cost thatch roofing widely available. [10] Southern German, Italian and Spanish city states kept the tradition alive.

The Natural History Museum in London has an ornate terracotta facade typical of high Victorian architecture - the carvings represent the contents of the museum Natural History Museum London Jan 2006.jpg
The Natural History Museum in London has an ornate terracotta facade typical of high Victorian architecture – the carvings represent the contents of the museum

1700s–1880s

England

Englishmen Richard Holt and Thomas Ripley patented an artificial stone recipe in 1722. The business was fairly successful at making small architectural ornaments. Their company was taken over by George[ dubious ] and Eleanor Coade in 1769. [10] [ better source needed ] [See Coade stone, See Eleanor Coade ] George died a year later, leaving the company to his wife and daughter, both named Eleanor Coade. The Coade ladies[ dubious ] popularized the grey mix of terracotta as an alternative to stone with the help of architects like Horace Walpole and Sir John Soane. Georgian architectural style was in vogue and demand for repetitive, classically inspired décor was very fashionable. The Victoria and Albert Museum (1867–1880) and the Natural History Museum of London (1879–1880) buildings ushered in an era of mass-produced architectural terracotta.

Trinity Church in New York City, from Robert N. Dennis collection of stereoscopic views 7 Trinity Church, from Robert N. Dennis collection of stereoscopic views 7.jpg
Trinity Church in New York City, from Robert N. Dennis collection of stereoscopic views 7
United States

Most early terracotta was shipped from Europe or made by small local ceramicists. The first manufacturer of architectural terracotta was opened by Henry Tolman Jr. in Worcester, MA around 1849. In the 1850s, New York architects like Richard Upjohn and James Renwick began to use it as an economical replacement for stone. [11]

The Railway Exchange Building in Chicago is faced entirely with light cream enamel terracotta (drawing by Hugh Ferriss, 1920) Architect and engineer (1920) (14760399636).jpg
The Railway Exchange Building in Chicago is faced entirely with light cream enamel terracotta (drawing by Hugh Ferriss, 1920)

1880s–1930s

Reactions to the Chicago fire in 1871 spurred interest in terracotta as a fireproof building material. In the age of skyscraper construction, the cast iron frame needed to be protected. Terracotta was a lightweight, moldable, fire and pollution-resistant material that could be mass-produced. Architects such as Burnham and Root, H.H. Richardson, Louis Sullivan, and McKim, Mead & White became interested in using terracotta as a building material rather than just as imitation stone. [12]

Issues with installation, water penetration, and corroding interior metal caused the industry to organize the National Terracotta Society. They published two widely used standards, in 1914 and 1924, that detailed construction methods, anchoring systems, waterproofing, and maintenance standards. [13]

1930s–present

Economic interest in terracotta plummeted in the 1930s but the industry did not die out. Terracotta could not compete with newer mass-produced materials such as plate glass, new metal alloys, and cement block construction. Changing fashions towards more minimalist, modern styles such as the Bauhaus School and International Style did not help the waning industry.

Post-World War II the industry had to face the decline of buildings built during the heyday of the material, 1910–1940. Structural problems resulting from incomplete waterproofing, improper installation, poor maintenance, and interior corroding mild steel made the material unpopular in newer constructions.

To combat this accusation against quality, several other industry publications were produced between 1945 and the 1960s. They did not succeed in reviving the artistic architectural terracotta but they were able to turn their attention to public buildings. Advances in machine extruded terracotta made it competitive with other hollow clay tile alternatives at the time. In tiles form, terracotta had a renewal as a hallmark of mid-century public buildings.

It lost steam in the 1960s with the introduction of more synthetic materials on the mass market. The industry was sustained by the need for replacement blocks for old buildings, hollow clay tile, and now rainscreen. [14]

Manufacturing process

Terracotta can be made by pouring or pressing the mix into a plaster or sandstone mold, clay can be hand carved, or mix can be extruded into a mold using specialized machines. Clay shrinks as it dries from water loss therefore all molds are made slightly larger than the required dimensions. After the desired green-ware, or air dried, shape is created it is fired in a kiln for several days where it shrinks even further. The hot clay is slowly cooled then hand finished. The ceramics are shipped to the project site where they are installed by local contractors. The hollow pieces are partially backfilled with mortar then placed into the wall, suspended from metal anchors, or hung on metal shelf angles. [15]

Design

Academically trained artists were often the designers of the terracotta forms. Their drawings would be interpreted by the manufacturer who would plan out the joint locations and anchoring system. [16] Once finalized, the drawings were turned into a plaster reality by sculptors who would create the mold for the craftsmen. [17]

Vertical pugmill used by the Moravian Pottery and Tile Works in Pennsylvania to refine the clay used for tile production 12-INCH VERTICAL PUG MILL, MANUFACTURED BY THE CROSSLEY MANUFACTURING CO. OF TRENTON, NJ. IT WAS PURCHASED IN 1902, AND USED AT THE FIRST MORAVIAN POTTERY AND TILE WORKS BEFORE HAER PA,9-DOYLT.V,8-28.tif
Vertical pugmill used by the Moravian Pottery and Tile Works in Pennsylvania to refine the clay used for tile production

Clay preparation

Clay selection was very important to manufacture of terracotta. Homogenous, finer grain sizes were preferred. [18] The color of the clay body was determined by the types of deposits that were locally available to the manufacture. Sand was added to temper the process. Crushed ceramic scraps called grog were also added to stiffen the product and help reduce shrinkage.

Weathering the clay allowed pyrites to chemically change to hydrated ferric oxide and reduced alkali content. This aging minimizes the potential chemical changes during the rest of the manufacturing process. [19] The weathered raw clay was dried, ground, and screened. Later, it would have been pugged in a mill that would mix the clay with water using rotating blades and force the blend through a sieve.

Hand pressing terracotta

An artist makes a negative plaster mold based on a clay positive prototype. 1–1¼" of the clay/water mixture is pressed into the mold. Wire mesh or other stiffeners are added to create the web, or clay body that surrounds the hollow cell. The product is air dried to allow the plaster to suck the moisture out of the green clay product. It is fired then slowly cooled. [15]

Extrusion

Mechanized extrusion was used for the mass-production of terracotta blocks, popular in the 1920s. Prepared clay was fed into a machine that would then push the mix through a mold. The technique required the blocks to be made with simple shapes, so this process was often used for flooring, roofing, cladding, and later hollow clay tiles. [20]

A downdraft kiln designed for the Pomona Terra Cotta Manufacturing Company in Guilford County, North Carolina Pomona Terra Cotta Manufacturing Company, West Market Street, Greensboro, Guilford County, NC HAER NC,41-GREBO,4- (sheet 3 of 3).tif
A downdraft kiln designed for the Pomona Terra Cotta Manufacturing Company in Guilford County, North Carolina

Glazing

The last step before firing the greenware was glazing. True glazes are made from various salts but prior to the 1890s most blocks were slip glazed or coated with a watered-down version of the clay mix. Liquefying the clay increased the amount of small silica particles that would be deposited on the surface of the block. These would melt during firing and harden. By 1900 almost all colors could be achieved with the addition of salt glazes. Black or brown were made by adding manganese oxide. [17]

Philadelphia Art Museum's terracotta pediment using polychrome glazing Art Museum pediment.jpg
Philadelphia Art Museum's terracotta pediment using polychrome glazing

Firing

The kiln firing process could take days, up to two weeks. The clay is heated slowly to around 500°C to sweat off the loose or macroscopic water between the molecules. Then the temperature is increased to close to 900°C to release the chemically bonded water in gaseous form and the clay particles will begin to melt together or sinter. If the kiln reaches 1000°C then the clay particles will vitrtify and become glass like. After the maximum temperature was reached then the clay was slowly cooled over a few days. During firing a fireskin is created. A fireskin is the glass-like "bread crust" that covers the biscuit or interior body.

Various kilns were used as technology developed and capital was available for investment. Muffle kilns were the most common kiln. They were used as early as 1870. The kilns burned gas, coal, or oil that heated an interior chamber from an exterior chamber. The walls "muffled" the heat so the greenware was not directly exposed to the flames. [17]

Down-draught kilns were also widely used. The interior chamber radiated heat around the terracotta by pulling in hot air from behind an exterior cavity wall. Like the muffle wall, the cavity wall protected the greenware from burning. [16]

Installation

The earliest terracotta elements were laid directly into the masonry but as structural metal became more popular terracotta was suspended by metal anchors. The development of cast and later wrought iron as a structural material was closely linked to the rise of terracotta. Cast iron was first used as columns in the 1820s by William Strickland. Over the course of the 19th century metal became more incorporated into construction but it was not widely used structurally until the late 1890s.

A series of disastrous fires (Chicago, 1871; Boston, 1872; and San Francisco, 1906) earned terracotta a reputation for being a fireproof, lightweight cladding material that could protect metal from melting. Holes were bored in the hollow blocks in choice locations to allow for metal 'J' or 'Z' hooks to connect the blocks to the load bearing steel frame and/or masonry walls. The metal could be hung vertically or anchored horizontally. Pins, clamps, clips, plates, and a variety of other devices were used to help secure the blocks. The joints would then be mortared and the block would be partially backfilled. [16]

Cracking caused by corroding metal anchors at the First Congregational Church of Long Beach, California Detail on E Collonade.jpg
Cracking caused by corroding metal anchors at the First Congregational Church of Long Beach, California

Degradation

The most common reasons for terracotta to fail are: poor manufacturing, improper installation, weathering, freeze/thaw cycling, and salt formation from atmospheric pollution. The porosity of terracotta greatly impacts its performance. The ability or inability for water and pollutants to enter into the material is directly correlated to its structural capacity. Terracotta is very strong in compression but weak in tension and shear strength. Any anomalous material expanding (ice, salts, incompatible fill material, or corroding metal anchors which cause rust jacking) inside the clay body will cause it to crack and eventually spall. [21]

Inherent faults can severely impact the performance of the material. Improper molding can cause air pockets to form that increase the rate of deterioration. If the block is not fired or cooled properly then the fireskin will not be uniformly adhered to the substrate and can flake off. Likewise, if a glaze is not fired properly it will crack, flake, and fall off. Discolorations can result from mineral impurities such as pyrites or barium carbonates.

A fair amount of damage comes from clumsy transportation, storage, or installation of the material. If the mortar used around and inside the blocks is too strong then the stress will be translated to the terracotta block which will fail over time. Corroding interior metal anchors expand at a faster rate than the surrounding ceramic body causing it to fail from the inside out. Improper loading of the hollow terracotta blocks can create stress cracks.

Imperfect repair work often exacerbates the underlying problems, speeding up the decay of surrounding elements as well. Making penetrations in terracotta units to attach objects to the outside walls also allows moisture to enter the system, and often crack the terracotta as well. Installing sealant rather than mortar, or applying impervious coating, will trap moisture within the terracotta. [21]

The environment also plays a large role in the survival of terracotta. Different types of air pollution can cause different types of surface problems. When it rains, water and salts get sucked into the voids in and around the terracotta through capillary action. If it freezes then ice forms, putting internal stress on the material, causing it to crack from inside. A similar problem happens with atmospheric pollutants that are carried into the gaps by rains water. The pollution creates a mildly acidic solution that eats at the clay body or a salt crust forms, causing similar issues as ice. [22]

With the majority of terracotta buildings being over one-hundred years old, failing terracotta has become a problem in many cities such as New York. Regular inspections and maintenance and repair programs are required by law, but nonetheless well-publicized incidents such as the death of Erica Tishman after a piece of terracotta fell from a 105-year old building. [23]

See also

Manufacturers

Related Research Articles

<span class="mw-page-title-main">Brick</span> Block or a single unit of a ceramic material used in masonry construction

A brick is a type of construction material used to build walls, pavements and other elements in masonry construction. Properly, the term brick denotes a unit primarily composed of clay, but is now also used informally to denote units made of other materials or other chemically cured construction blocks. Bricks can be joined using mortar, adhesives or by interlocking. Bricks are usually produced at brickworks in numerous classes, types, materials, and sizes which vary with region, and are produced in bulk quantities.

<span class="mw-page-title-main">Masonry</span> Building of structures from individual units of stone, bricks, or blocks

Masonry is the craft of building a structure with brick, stone, or similar material, including mortar plastering which are often laid in, bound and pasted together by mortar. The term masonry can also refer to the building units themselves.

<span class="mw-page-title-main">Terracotta</span> Clay-based earthenware used for sculpture

Terracotta, also known as terra cotta or terra-cotta, is a term used in some contexts for earthenware. It is a clay-based non-vitreous ceramic, fired at relatively low temperatures.

<span class="mw-page-title-main">Earthenware</span> Nonvitreous pottery

Earthenware is glazed or unglazed nonvitreous pottery that has normally been fired below 1,200 °C (2,190 °F). Basic earthenware, often called terracotta, absorbs liquids such as water. However, earthenware can be made impervious to liquids by coating it with a ceramic glaze, and such a process is used for the great majority of modern domestic earthenware. The main other important types of pottery are porcelain, bone china, and stoneware, all fired at high enough temperatures to vitrify. End applications include tableware and decorative ware such as figurines.

<span class="mw-page-title-main">Tile</span> Manufactured pieces for covering surfaces

Tiles are usually thin, square or rectangular coverings manufactured from hard-wearing material such as ceramic, stone, metal, baked clay, or even glass. They are generally fixed in place in an array to cover roofs, floors, walls, edges, or other objects such as tabletops. Alternatively, tile can sometimes refer to similar units made from lightweight materials such as perlite, wood, and mineral wool, typically used for wall and ceiling applications. In another sense, a tile is a construction tile or similar object, such as rectangular counters used in playing games. The word is derived from the French word tuile, which is, in turn, from the Latin word tegula, meaning a roof tile composed of fired clay.

<span class="mw-page-title-main">Building material</span> Material which is used for construction purposes

Building material is material used for construction. Many naturally occurring substances, such as clay, rocks, sand, wood, and even twigs and leaves, have been used to construct buildings. Apart from naturally occurring materials, many man-made products are in use, some more and some less synthetic. The manufacturing of building materials is an established industry in many countries and the use of these materials is typically segmented into specific specialty trades, such as carpentry, insulation, plumbing, and roofing work. They provide the make-up of habitats and structures including homes.

<span class="mw-page-title-main">Glazed architectural terra-cotta</span> Coated fired clay used to decorate buildings

Glazed architectural terra cotta is a ceramic masonry building material used as a decorative skin. It featured widely in the 'terracotta revival' from the 1880s until the 1930s. It was used in the UK, United States, Canada and Australia and is still one of the most common building materials found in U.S. urban environments. It is the glazed version of architectural terracotta; the material in both its glazed and unglazed versions is sturdy and relatively inexpensive, and can be molded into richly ornamented detail. Glazed terra-cotta played a significant role in architectural styles such as the Chicago School and Beaux-Arts architecture.

<span class="mw-page-title-main">Modelling clay</span> Any of a group of malleable substances used in building and sculpting

Modelling clay or modelling compound is any of a group of malleable substances used in building and sculpting. The material compositions and production processes vary considerably.

<span class="mw-page-title-main">Teco pottery</span>

The American Terracotta Tile and Ceramic Company was founded in 1881; originally as Spring Valley Tile Works; in Terra Cotta, Illinois, between Crystal Lake, Illinois and McHenry, Illinois near Chicago by William Day Gates. It became the country's first manufactury of architectural terracotta in 1889. The production consisted of drain tile, brick, chimney tops, finials, urns, and other economically fireproof building materials. Gates used the facilities to experiment with clays and glazes in an effort to design a line of art pottery which led to the introduction of Teco Pottery. American Terra Cotta's records are housed at the University of Minnesota and include original architectural drawings.

<span class="mw-page-title-main">Ceramic glaze</span> Fused coating on ceramic objects

Ceramic glaze, or simply glaze, is a glassy coating on ceramics. It is used for decoration, to ensure the item is impermeable to liquids and to minimise the adherence of pollutants.

<span class="mw-page-title-main">Architectural sculpture in the United States</span>

Architectural sculpture is a general categorization used to describe items used for the decoration of buildings and structures. In the United States, the term encompasses both sculpture that is attached to a building and free-standing pieces that are a part of an architects design.

This is a list of pottery and ceramic terms.

Ceramic houses are buildings made of an earth mixture which is high in clay, and fired to become ceramic. The process of building and firing such houses was developed by Iranian architect Nader Khalili in the late 1970s; he named it Geltaftan. "Gel" means "clay" and "taftan" means "firing, baking, and weaving clay" in Persian language. Khalili's research into creating ceramic houses was strongly based on the idea that permanent, water-resistant, and earthquake-resistant houses could be built with the implementation of the four elements: earth and water to build the forms, and fire and air to finish them. His impassioned work led to a few small scale projects in Iran, including the Javadabad Elementary School, and the Ghaled Mofid restoration project. Aside from Khalili's own documented work, there seems to be little widespread research on ceramic houses.

Terra Cotta is a clay-based ceramic material, and objects made in it.

<span class="mw-page-title-main">Roof tiles</span> Tile designed to keep out rain

Roof tiles are overlapping tiles designed mainly to keep out precipitation such as rain or snow, and are traditionally made from locally available materials such as clay or slate. Later tiles have been made from materials such as concrete, and plastic.

<span class="mw-page-title-main">Structural clay tile</span> Class of building block

Structural clay tile describes a category of burned-clay building materials used to construct roofing, walls, and flooring for structural and non-structural purposes, especially in fireproofing applications. Also called building tile, structural terra cotta, hollow tile, saltillo tile, and clay block, the material is an extruded clay shape with substantial depth that allows it to be laid in the same manner as other clay or concrete masonry. In North America it was chiefly used during the late 19th and early 20th centuries, reaching peak popularity at the turn of the century and declining around the 1950s. Structural clay tile grew in popularity in the end of the nineteenth-century because it could be constructed faster, was lighter, and required simpler flat falsework than earlier brick vaulting construction. Each unit is generally made of clay or terra-cotta with hollow cavities, or cells, inside it. The colors of terracotta transform from gray to orange, red, yellow, and cream tones. This is due to an effect of the firing process which hardens the clay so it can be used for structural purposes. The material is commonly used in floor arches, fireproofing, partition walls, and furring. It continues to be used in Europe to build fire-resistant walls and partitions. In North America the material has largely been replaced by concrete masonry units.

Ceramic building material, often abbreviated to CBM, is an umbrella term used in archaeology to cover all building materials made from baked clay. It is particularly, but not exclusively, used in relation to Roman building materials.

<span class="mw-page-title-main">Malibu tile</span>

Malibu tile is a type of ceramic tile that takes its inspiration from the tiles that were produced at Malibu Potteries in Malibu, California, during the latter half of the 1920s. These tiles reflect a style of design that is referred to as Hispano-Moresque or Arabesque exhibiting bright contrasting glaze colors often in geometric patterns that are reminiscent of tiles produced many centuries ago in the Near and Middle East, North Africa and southern Spain. The Adamson House in Malibu, California, now the Malibu Lagoon Museum, contains the largest and most varied display of Malibu Potteries tile. The Adamson House was added to the National Register of Historic Places in 1977 and became a California Historical Landmark in 1985.

<span class="mw-page-title-main">John Marriott Blashfield</span> English property developer and mosaic floor and ornamental terracotta manufacturer

John Marriott Blashfield (1811–1882) was a property developer and mosaic floor and ornamental terracotta manufacturer. He originally worked for the cement makers Wyatt, Parker and & Co in Millwall, but moved the business to Stamford in Lincolnshire in 1858, when it was renamed The Stamford Terracotta Company.

<span class="mw-page-title-main">Ceramic art</span> Decorative objects made from clay and other raw materials by the process of pottery

Ceramic art is art made from ceramic materials, including clay. It may take varied forms, including artistic pottery, including tableware, tiles, figurines and other sculpture. As one of the plastic arts, ceramic art is a visual art. While some ceramics are considered fine art, such as pottery or sculpture, most are considered to be decorative, industrial or applied art objects. Ceramic art can be created by one person or by a group, in a pottery or a ceramic factory with a group designing and manufacturing the artware.

References

  1. "Standard Definitions of Terms Relating to Structural Clay Products". ASTM. Designation C43.
  2. Pollard, A.M.; Heron, Carl (2008). Archeological Chemistry. Cambridge, UK: Royal Society of Chemistry. pp. Chapter 7.
  3. Taylor, Mary; Bradshaw, H.C. (1916). "Architectural Terra-Cottas from Two Temples at Falerii Veteres". Papers of the British School at Rome. 8 (1): 1–34. doi:10.1017/s0068246200005407. S2CID   130444171.
  4. "Terracotta Art - Banglapedia".
  5. Brancaccio, Pia (2005). "Sātavāhana Terracottas: Connections with the Hellenistic Tradition". East and West. 55 (1/4): 55–69.
  6. "Graeco-Buddhist Terra Cotta Head". Bulletin of the Pennsylvania Museum. 18 (1): 5–7. 1922. doi:10.2307/3794024. JSTOR   3794024.
  7. "On the Older Forms of Terra-Cotta Roofing Tiles". The American Architect and Building News. 35 (848): 197. March 26, 1892.
  8. Geer, Walter (1891). Terr-Cotta in Architecture. New York: Gazley.
  9. Koçyiğit, Oğuz (2006). "Terracotta Spacers from the Bathhouse at Amorium". Anatolian Studies. 56: 113–125. doi:10.1017/s006615460000079x. S2CID   114377247.
  10. 1 2 Elliott, Cecil D. (1992). Terracotta. Cambridge, MA: MIT Press. pp. 52–64.
  11. Shockley, Jay; Tunick, Susan (2012). "A Capital Idea: Philadelphia and the Promotion of 1850s American Terra Cotta". APT Bulletin. 43 (2/3): 31–38.
  12. Taylor, James (1891–1892). "History of Terra Cotta in New York City". Architectural Record. 1: 136–148.
  13. Fus, Michael (1997). Architectural terra cotta: standards, specifications, and testing. Chicago, IL: School of the Art Institute of Chicago. p. PhD. Dissertation.
  14. Tunich, Susan (1998). "The Reign of Terra Cotta in the United States: Enduring in an Inhospitable Environment, 1930–1968". APT Bulletin. 29 (1): 43–48. doi:10.2307/1504547. JSTOR   1504547.
  15. 1 2 Gerns, Edward; Will, Rachel (2016). "Architectural Terra Cotta". APT Bulletin. 47 (2/3): 1–8.
  16. 1 2 3 Didden, Amanda (2003). Standardization of terracotta anchorage: an analysis of shop drawings from the Northwestern Terra Cotta Company and the O.W. Ketcham Terra Cotta Works. Philadelphia, PA: University of Pennsylvania.
  17. 1 2 3 Mack, Robert C. (1983). "The Manufacture and Use of Architectural Terra Cotta in the United States". The Technology of Historic American Buildings: 117–151.
  18. "Terracotta". Scientific American (209). 1872.{{cite journal}}: More than one of |number= and |issue= specified (help)
  19. Mack, Robert C. (1983). "The Manufacture and Use of Architectural Terra Cotta in the United States". The Technology of Historic American Buildings: 117–151.
  20. Tunick, Susan (1997). Terra-Cotta Skyline: New York's Architectural Ornament. Princeton Architectural Press. pp. Chapter 6.
  21. 1 2 Sanders, Arthur L.; Shypula, Kara L. (2015). "Caring for Glazed Architectural Terra Cotta" (PDF). Hoffmann Architects Journal. 32 (1). Hamden, CT: 3.
  22. Patterson Tiller, de Teel (1979). "The Preservation of Historic Glazed Architectural Terra-cotta". National Park Service.
  23. Otterman, Sharon; Haag, Matthew (2019-12-17). "Woman Killed by Falling Debris Near Times Square". The New York Times. Retrieved 2021-04-29.