Rehydroxylation dating

Last updated April 20, 2024

Rehydroxylation [RHX] dating is a developing method for dating fired-clay ceramics.^[1] This new concept relies on a key property of ceramic materials, in which they expand and gain mass over time. After a ceramic specimen is removed from the kiln at the time of production, it immediately begins to recombine chemically with moisture from the environment. This reaction reincorporates hydroxyl (OH) groups into the ceramic material, and is described as rehydroxylation (RHX).^[2] The phenomenon has been well-documented over the past one hundred years (albeit more focused on limited timescales), and has now been proposed as a means to date fired-clay ceramics. The RHX process produces an increase in specimen weight and this weight increase provides an accurate measure of the extent of rehydroxylation. The dating clock is provided by the experimental finding that the RHX reaction follows a precise kinetic law: the weight gain increases as the fourth root of the time which has elapsed since firing.^[3] This power law and the RHX method which follows from it were discovered by scientists from the University of Manchester and the University of Edinburgh.^[4]

The concept of RHX dating was first stated in 2003 by Wilson and collaborators^[3] who noted that the "results … suggest a new method for archaeological dating of ceramics". The RHX method was then described in detail in 2009^[1] for brick and tile materials, and in relation to pottery in 2011.^[5] The archaeological pottery first used to test the developing RHX method consisted of three categories of which the dates had already been calculated by other archaeological means. The first was an Anglo-Saxon loom-weight from 560 to 660 AD, a Samian-ware sherd from 45 to 75 AD and three Werra earthenware sherds from 1605 AD.^[5] The types of samples used were deemed important for the experiment since they represented "three specific perceived issues associated with applying the RHX method to excavate archaeological pottery."^[5] These issues included potsherds found in waterlogged sites, low-firing temperature ceramics, vitrified ceramics and those containing a slip or a glaze.

RHX dating is not yet routinely or commercially available. It is the subject of a number of research and validation studies in several countries.

Power-law kinetics

The concept of clay ceramic expansion, post-firing, has been the object of discussion for a long time, first noted by Schurecht in 1928^[6] to explain crazing in ceramic glazes, and confirmed in 1954 by McBurney that this and the expansion of ceramic bodies is due to the intake of moisture from the environment.^[7] Moisture expansion has since been an important property of clay ceramics to consider when using the material, such as clay bricks in constructions. In 2003, it was proposed that moisture expansion could extend over much longer periods of time, contrasting with the previous research over more limited time scales.^[3] This was evaluated on bricks ranging from the Roman period to modern ones. It was ascertained that moisture expansion follows a power law: mass gain and expansion depend on time^1/4 across archaeological timescales. For example, if the weight of a fired-clay ceramic increases as a result of RHX by 0.1% in 1 year from firing, then the weight increase is 0.2% in 16 years, 0.3% in 81 years and 0.4% in 256 years (and so on). The reason behind this quartic root dependence is uncertain, however further research is being conducted to explain why, including NMR and IR spectroscopy.^[8] Despite the uncertainty, enough previous research and other more recent data have indicated that the law is valid.^[9]^[10] with moisture expansion and weight gain being proportional to each other for a specified material at any specified firing temperature.

The basis of RHX dating depends on this power law.

Dating methodology

First a small sample of the material is obtained. To do so, the ceramic artefact is wet cut using a water-cooled saw to avoid producing heat and consequently causing some dehydroxylation.^[5] After this, any loose debris must be removed and this can be done by thoroughly cleaning it under running water. The sample is then heated to 105 °C until constant weight to remove all capillary water and loosely adsorbed water. Next, the sample is conditioned in a controlled environment to the estimated effective lifetime temperature (ELT) and relative humidity to obtain the RHX constant ( $\alpha$ ).^[5] The ELT is generally close to (but not exactly the same as) the long-term annual mean surface air temperature. Finally, to completely remove all the water gained in the previous stage, the sample is heated to 500 °C for 4 hours until constant weight, which indicates that all the water has been lost and, therefore, has hypothetically returned to its original historical mass after removal from the kiln.^[1]^[5]

After the preparation of the sample is complete, it is transferred to a microbalance chamber and exposed to water vapour at a controlled temperature (identical to the first ELT) and relative humidity to determine the kinetics of the mass gain through recombination with water. Once this process has been carried out for the desired length of time (on average one to two days), the mass data are recorded.^[1]^[5]

Once the RHX rate is determined, it is possible to calculated exactly how long ago it was removed from the kiln,^[4] and therefore assign a date to the material.

To determine the date of the material, the rate of the mass gain needs to be calculated using the following equation:

$y=\alpha (T)t^{1/4}$ ^[1]^[8]

where $\alpha$ is the mass gain rate constant, $T$ is temperature (the ELT) and $t$ is time. The older the sample, the greater the mass gained from combining chemically with water, since the initial mass of the sample is equal to the sum of that of the original fired material and the water combined with it over its lifetime.^[1] From there, using other data obtained, the age is calculated using:

$t_{\alpha }=[{\frac {m_{\alpha }}{\alpha m_{4}}}]^{4}$ ^[8]

where $t_{\alpha }$ is the time elapsed since the last historical firing (age of material), $m_{\alpha }$ is the mass of hydroxyl groups, $m_{4}$ is the hypothetical mass at complete dehydroxylation and $\alpha$ represents the rate constant. To ensure the date is accurate, either multiple samples from the same artefact can be taken and analysed, or the sample can be dated again using an alternative means and the results compared.

Technical issues

When developing the method, it was important to understand whether variations in humidity affect the RHX mass gain rate of the ceramic material. Little research had not yet examined this in-depth. Therefore, a study was carried out on samples from the XIX^th and XX^th centuries,^[11] in which they dehydrated the samples to remove any physically and chemically bonded water and placed them in conditions which were varied between dry and humid extremes. The conclusion was that variations in humidity do not affect the kinetics of RHX since it only affects the physically bonded water content, rather than the chemically bonded hydroxyl ions.^[11] This is because the RHX reaction occurs extremely slowly, and only minute amounts of water are required to feed it, with sufficient water being available in virtually all terrestrial environments. Neither systematic nor transient changes in humidity have an effect on long-term rehydroxylation kinetics. However, they do affect instantaneous gravimetric measurements or introduce systematic error, for example through capillary condensation.^[11]

Changes in temperature can strongly affect the rate of RHX and this may impact the calculated age of the ceramic. To illustrate this, the hypothetical example of a 1000-year-old sample is used.^[12] During the first 500 years, the ambient temperature remains at 10 °C; for the following 500 years, the temperature increases to 15 °C. Therefore, after the first 500 years, the rate of RHX increases. The mass of the material also begins to increase at a faster rate than previously.^[12] Thus, when calculating dates, scientists must be able to estimate the temperature history of the sample. The method of calculation is based on temperature data for the location, with adjustments for burial depth and long-term temperature variation from historical records,^[12] such as seasonal and climatic changes. This information is used to estimate an effective lifetime temperature or ELT which is then used in the dating calculation.^[5] Recognition of the effects of changes in temperature is vital since reheating the material to a high enough temperature causes the ceramic to lose some or all of the water gained since the original firing, thus affecting the age calculated.^[13] For example, a medieval brick examined by Wilson and her colleagues^[1] produced a date of 66 years, instead of the expected earlier date. Closer analysis revealed that the exterior of the brick contained vitrified elements, indicating that it had been exposed to extreme heat since the original time of firing. This was due to the brick having been dehydroxylated by the intense heat of incendiary bombing and fires during World War II.^[14] To avoid this type of error or confirm the calculated date, archaeological methods can be used alongside RHX dating, such as stratigraphic dating, radiocarbon dating or other archaeological methods.

The main application of the RHX technique is to date archaeological ceramics. Yet most archaeological material contains components which causes either addition mass gain or additional mass loss during the RHX measurement process.^[15] These components can be an intrinsic part of the object, for example materials added as temper, or compounds which have become incorporated into the object during use, such as organic residues, or other elements which have entered into the object during burial or conservation. Removing the contaminants without affecting the RHX technique is currently being researched. The method deemed the most effective out of the others tested consisted of an acid-base treatment, using hydrochloric acid (HCl) to clean the samples, followed by a solution of hydrogen peroxide (H₂O₂) to oxidise them.^[16] Since RHX dating has yet to become a key part of dating ceramic artefacts due to its very recent development, the residues on the outside/inside of the ceramic can be dated using other methods, including radiocarbon, Thermoluminescence (TL), Optically Stimulated Luminescence (OSL) and Electron Paramagnetic Resonance (EPR).^[8]

Research and application of the method

The RHX technique was the product of a three-year study by a collaboration of University of Manchester and University of Edinburgh researchers, led by Moira Wilson. Though it has only been established on bricks and tiles of up to 2,000 years of age, research is continuing to determine whether RHX can be accurately used on any fired-clay material, for example earthenware of up to 10,000 years of age.^[4] This is because the mass gain only approximates a 1-2% increase of the original mass of the material over the course of a few millennia. The potential capacity for further adsorption of water could extend to 10,000 years, since the kinetic power law on which the method relies remains true for large time scales.^[1] Since the method remains under refinement, it is not yet a standard means of dating archaeological ceramics.

The original work of Wilson and co-workers was undertaken on construction materials, bricks and tiles. Transferring the method to ceramics has brought additional challenges but initial results have demonstrated that ceramics have the same “internal clock” as bricks.^[17] Several other studies have attempted to replicate the RHX technique,^[13]^[18]^[19]^[20]^[21] but using archaeological ceramics. These studies have encountered issues with components within the ceramics, including the mineralogy or the temper added to the clay, causing either addition mass gain or additional mass loss during the RHX measurement process. The quality of data generated by the Manchester and Edinburgh groups has been due to analysing fired-clay materials which do not contain these components. Efforts to successfully replicate the original work and overcome the challenges presented by archaeological ceramics are underway in several academic institutions worldwide.

One example of this research is a study from 2011 that was conducted on sherds of XIX^th century Davenport ceramics excavated in Utah, United States of America to assess the validity of the original method, specifically the rate equation. The study confirmed that RHX dating is applicable to archaeological ceramics, with Bowen and his colleagues stating "the development of a refined expression for rehydration/RHX behaviour would allow a dramatic enhancement of the anthropological research questions currently being posed".^[22] In spite of the success, they stressed that knowledge of the mineralogy of the sample is vital.^[22] They noted that some minerals, such as illite, undergo dehydration and dehydroxylation reversibly; others, such as kaolinite, undergo this at varying temperatures since they vitrify. Therefore, in order to dehydrate the sample effectively, a suitable temperature needs to be chosen to avoid compromising the integrity of the sample components. It was also concluded that more research needed to be carried out to further examine the effects of mineralogy on RHX dating.^[22]

A more recent analysis from 2017 on potsherds from southern Apulia, Italy proved the potential for the RHX method to become a reliable "alternative or ancillary"^[21] means of dating ceramics. The samples used were fragments of Byzantine pottery which had been dated previously by association with other artefacts using radiocarbon analysis. Meanwhile, it was noted that since RHX dating has not been tested sufficiently, it cannot yet replace more conventional ways of dating pottery, such as radiocarbon which has extensive proof of its accuracy. The ages calculated for the Byzantine sherds through RHX dating were concurrent with the known ones. The study also emphasised the possible value of this method in refining chronological pottery seriation in cases where the pottery style remains similar over extended periods of time in a specific region, such as the Byzantine vessels examined.^[21]

Overall, the RHX dating technique shows great potential within the field of Archaeology and research continues to allow for its use in more general studies.

Related Research Articles

A ceramic is any of the various hard, brittle, heat-resistant, and corrosion-resistant materials made by shaping and then firing an inorganic, nonmetallic material, such as clay, at a high temperature. Common examples are earthenware, porcelain, and brick.

A kiln is a thermally insulated chamber, a type of oven, that produces temperatures sufficient to complete some process, such as hardening, drying, or chemical changes. Kilns have been used for millennia to turn objects made from clay into pottery, tiles and bricks. Various industries use rotary kilns for pyroprocessing and to transform many other materials.

Pottery is the process and the products of forming vessels and other objects with clay and other raw materials, which are fired at high temperatures to give them a hard and durable form. The place where such wares are made by a potter is also called a pottery. The definition of pottery, used by the ASTM International, is "all fired ceramic wares that contain clay when formed, except technical, structural, and refractory products". End applications include tableware, decorative ware, sanitary ware, and in technology and industry such as electrical insulators and laboratory ware. In art history and archaeology, especially of ancient and prehistoric periods, pottery often means vessels only, and sculpted figurines of the same material are called terracottas.

A crucible is a ceramic or metal container in which metals or other substances may be melted or subjected to very high temperatures. Although crucibles have historically tended to be made out of clay, they can be made from any material that withstands temperatures high enough to melt or otherwise alter its contents.

Vitrification is the full or partial transformation of a substance into a glass, that is to say, a non-crystalline amorphous solid. Glasses differ from liquids structurally and glasses possess a higher degree of connectivity with the same Hausdorff dimensionality of bonds as crystals: dim_H = 3. In the production of ceramics, vitrification is responsible for their impermeability to water.

Earthenware is glazed or unglazed nonvitreous pottery that has normally been fired below 1,200 °C (2,190 °F). Basic earthenware, often called terracotta, absorbs liquids such as water. However, earthenware can be made impervious to liquids by coating it with a ceramic glaze, and such a process is used for the great majority of modern domestic earthenware. The main other important types of pottery are porcelain, bone china, and stoneware, all fired at high enough temperatures to vitrify. End applications include tableware and decorative ware such as figurines.

<span class="mw-page-title-main">Potter's wheel</span> Machine used in the shaping of round ceramic ware

In pottery, a potter's wheel is a machine used in the shaping of clay into round ceramic ware. The wheel may also be used during the process of trimming excess clay from leather-hard dried ware that is stiff but malleable, and for applying incised decoration or rings of colour. Use of the potter's wheel became widespread throughout the Old World but was unknown in the Pre-Columbian New World, where pottery was handmade by methods that included coiling and beating.

Dental porcelain is a dental material used by dental technicians to create biocompatible lifelike dental restorations, such as crowns, bridges, and veneers. Evidence suggests they are an effective material as they are biocompatible, aesthetic, insoluble and have a hardness of 7 on the Mohs scale. For certain dental prostheses, such as three-unit molars porcelain fused to metal or in complete porcelain group, zirconia-based restorations are recommended.

Thermal shock is a phenomenon characterized by a rapid change in temperature that results in a transient mechanical load on an object. The load is caused by the differential expansion of different parts of the object due to the temperature change. This differential expansion can be understood in terms of strain, rather than stress. When the strain exceeds the tensile strength of the material, it can cause cracks to form and eventually lead to structural failure.

Ceramics of Indigenous peoples of the Americas is an art form with at least a 7500-year history in the Americas. Pottery is fired ceramics with clay as a component. Ceramics are used for utilitarian cooking vessels, serving and storage vessels, pipes, funerary urns, censers, musical instruments, ceremonial items, masks, toys, sculptures, and a myriad of other art forms.

Grog, also known as firesand and chamotte, is a raw material usually made from crushed and ground potsherds, reintroduced into crude clay to temper it before making ceramic ware. It has a high percentage of silica and alumina.

Ceramic glaze, or simply glaze, is a glassy coating on ceramics. It is used for decoration, to ensure the item is impermeable to liquids and to minimise the adherence of pollutants.

This is a list of pottery and ceramic terms.

Fritware, also known as stone-paste, is a type of pottery in which frit is added to clay to reduce its fusion temperature. The mixture may include quartz or other siliceous material. An organic compound such as gum or glue may be added for binding. The resulting mixture can be fired at a lower temperature than clay alone. A glaze is then applied on the surface.

Ceramic petrography is a laboratory-based scientific archaeological technique that examines the mineralogical and microstructural composition of ceramics and other inorganic materials under the polarised light microscope in order to interpret aspects of the provenance and technology of artefacts.

Conservation and restoration of ceramic objects is a process dedicated to the preservation and protection of objects of historical and personal value made from ceramic. Typically, this activity of conservation-restoration is undertaken by a conservator-restorer, especially when dealing with an object of cultural heritage. Ceramics are created from a production of coatings of inorganic, nonmetallic materials using heating and cooling to create a glaze. These coatings are often permanent and sustainable for utilitarian and decorative purposes. The cleaning, handling, storage, and in general treatment of ceramics is consistent with that of glass because they are made of similar oxygen-rich components, such as silicates. In conservation ceramics are broken down into three groups: unfired clay, earthenware or terracotta, and stoneware and porcelain.

Ceramic art is art made from ceramic materials, including clay. It may take varied forms, including artistic pottery, including tableware, tiles, figurines and other sculpture. As one of the plastic arts, ceramic art is a visual art. While some ceramics are considered fine art, such as pottery or sculpture, most are considered to be decorative, industrial or applied art objects. Ceramic art can be created by one person or by a group, in a pottery or a ceramic factory with a group designing and manufacturing the artware.

Chronological dating, or simply dating, is the process of attributing to an object or event a date in the past, allowing such object or event to be located in a previously established chronology. This usually requires what is commonly known as a "dating method". Several dating methods exist, depending on different criteria and techniques, and some very well known examples of disciplines using such techniques are, for example, history, archaeology, geology, paleontology, astronomy and even forensic science, since in the latter it is sometimes necessary to investigate the moment in the past during which the death of a cadaver occurred. These methods are typically identified as absolute, which involves a specified date or date range, or relative, which refers to dating which places artifacts or events on a timeline relative to other events and/or artifacts. Other markers can help place an artifact or event in a chronology, such as nearby writings and stratigraphic markers.

The conservation and restoration of ancient Greek pottery is a sub-section of the broader topic of conservation and restoration of ceramic objects. Ancient Greek pottery is one of the most commonly found types of artifacts from the ancient Greek world. The information learned from vase paintings forms the foundation of modern knowledge of ancient Greek art and culture. Most ancient Greek pottery is terracotta, a type of earthenware ceramic, dating from the 11th century BCE through the 1st century CE. The objects are usually excavated from archaeological sites in broken pieces, or shards, and then reassembled. Some have been discovered intact in tombs. Professional conservator-restorers, often in collaboration with curators and conservation scientists, undertake the conservation-restoration of ancient Greek pottery.

<span class="mw-page-title-main">Ancient Egyptian pottery</span>

Ancient Egyptian pottery includes all objects of fired clay from ancient Egypt. First and foremost, ceramics served as household wares for the storage, preparation, transport, and consumption of food, drink, and raw materials. Such items include beer and wine mugs and water jugs, but also bread moulds, fire pits, lamps, and stands for holding round vessels, which were all commonly used in the Egyptian household. Other types of pottery served ritual purposes. Ceramics are often found as grave goods.

References

1 2 3 4 5 6 7 8 Wilson, Moira A.; Carter, Margaret A.; Hall, Christopher; Hoff, William D.; Ince, Ceren; Wilson, Moira A.; Savage, Shaun D.; McKay, Bernard; Betts, Ian M. (8 August 2009). "Dating fired-clay ceramics using long-term power law rehydroxylation kinetics". Proceedings of the Royal Society A. 465 (2108): 2407–2415. Bibcode:2009RSPSA.465.2407W. doi:10.1098/rspa.2009.0117.
↑ Hamilton, Andrea; Hall, Christopher (2012). "A review of rehydroxylation in fired-clay ceramics". Journal of the American Ceramic Society. 95 (9): 2673–2678. doi:10.1111/j.1551-2916.2012.05298.x.
1 2 3 Wilson, Moira A; Hoff, William D; Hall, Christopher; McKay, Bernard; Hiley, Anna (2003). "Kinetics of moisture expansion in fired clay ceramics: a (time)^1/4 law". Physical Review Letters. 90 (12): 125503. Bibcode:2003PhRvL..90l5503W. doi:10.1103/PhysRevLett.90.125503. PMID 12688883.
1 2 3 "Fire and water reveal new archaeological dating method". ScienceDaily. May 25, 2009.
1 2 3 4 5 6 7 8 Wilson, Moira A; Hamilton, Andrea; Ince, Ceren; Carter, Margaret A; Hall, Christopher (2012). "Rehydroxylation (RHX) dating of archaeological pottery". Proceedings of the Royal Society A. 468 (2147): 3476–3493. Bibcode:2012RSPSA.468.3476W. doi: 10.1098/rspa.2012.0109 .
↑ Schurecht, H. G. (May 1928). "Methods for testing crazing of glazes caused by increases in size of ceramic bodies". Journal of the American Ceramic Society. 11 (5): 271–277. doi:10.1111/j.1151-2916.1928.tb16178.x. ISSN 0002-7820.
↑ McBurney, JW (1954). "Masonry cracking and damage caused by moisture expansion of structural clay tile". Proceedings - American Society for Testing and Materials. 54: 1219–1241.
1 2 3 4 Avramovska, Marija; Chmelik, Christian; Derkowski, Arkadiusz; Fantalkin, Alexander; Freude, Dieter; Haase, Jürgen; Hare, Vincent; Kärger, Jörg; Kuligiewicz, Artur; Moinester, Murray (24 February 2021). "Searching for the fundamentals of rehydroxylation dating of archaeological ceramics via NMR and IR microscopy". Journal of the American Ceramic Society. 104 (10): 5328–5340. doi: 10.1111/jace.17753 . ISSN 0002-7820.
↑ Kuligiewicz, Artur; Derkowski, Arkadiusz (2021). "Rehydroxylation of fired clays: Is the time to the quarter (TTTQ) model correct?". Journal of Archaeological Science. 125: 1–9. Bibcode:2021JArSc.125j5301K. doi: 10.1016/j.jas.2020.105301 . ISSN 0305-4403.
↑ Hall, Christopher; Wilson, Moira A; Hoff, William D (2011). "Kinetics of long-term moisture expansion in fired-clay brick". Journal of the American Ceramic Society. 94 (1): 3651–3654. doi:10.1111/j.1551-2916.2011.04831.x.
1 2 3 Drelich, Jaroslaw; Bowen, Patrick K.; Scarlett, Timothy J. (15 March 2013). Hall, C. (ed.). "Effect of Humidity Instability on Rehydroxylation in Fired Clay Ceramics". Journal of the American Ceramic Society. 96 (4): 1047–1050. doi:10.1111/jace.12262.
1 2 3 Hall, Christopher; Hamilton, Andrea; Wilson, Moira A (2013). "The influence of temperature on rehydroxylation (RHX) kinetics in archaeological pottery". Journal of Archaeological Science. 40 (1): 305–312. Bibcode:2013JArSc..40..305H. doi:10.1016/j.jas.2012.06.040.
1 2 Burakov, K.S.; Nachasova, I. E (2013). "Archaeomagnetic Study and Rehydroxlyation Dating of Fired-Clay Ceramics". Izvestiya, Physics of the Solid Earth. 49 (1): 105–112. Bibcode:2013IzPSE..49..105B. doi:10.1134/S1069351312120026.
↑ Dacey, James (June 8, 2009). "Archaeological dating by re-firing ancient pots". Physics World.
↑ Wilson, Moira A.; Clelland, Sarah-Jane; Carter, Maragret A; Ince, Ceren; Hall Christopher; Hamilton Andrea; Batt, Catherine M (2013). "Rehydroxylation of fired-clay ceramics: Factors affecting early-stage mass gain in dating experiments" (PDF). Archaeometry. 56 (4): 689–702. doi: 10.1111/arcm.12038 . hdl:10454/6239.
↑ Numrich, M.; Kutschera, W.; Steier, P.; Sterba, J. H.; Golser, R. (2015). "On the effect of organic carbon on rehydroxylation (RHX) dating". Journal of Archaeological Science. 57: 92–97. Bibcode:2015JArSc..57...92N. doi:10.1016/j.jas.2015.01.016. ISSN 0305-4403.
↑ Clegg, Francis; Breen, Christopher; Carter, Margaret A; Ince, Ceren; Savage, Shaun D; Wilson, Moira A (2012). "Dehydroxylation and Rehydroxylation Mechanisms in Fired Clay Ceramic: A TG-MS and DRIFTS Investigation". Journal of the American Ceramic Society. 95 (1): 416–422. doi:10.1111/j.1551-2916.2011.04926.x.
↑ Shoval, Shlomo; Paz, Yitzhak (2013). "A study of the mass-gain of ancient pottery in relation to archeological ages using thermal analysis". Applied Clay Science. 82: 113–120. Bibcode:2013ApCS...82..113S. doi:10.1016/j.clay.2013.06.027.
↑ Barrett, Gerard, T. (2013). "Rehydroxylation dating of fired clays: an improved time-offset model to account for the effect of cooling on post-reheating mass gain". Journal of Archaeological Science. 40 (10): 3596–3603. Bibcode:2013JArSc..40.3596B. doi:10.1016/j.jas.2013.04.032.{{cite journal}}: CS1 maint: multiple names: authors list (link)
↑ Le Goff, Maxime; Gallet Yves (2014). "Evaluation of the rehydroxylation dating method: Insights from a new measurement device". Quaternary Geochronology. 20: 89–98. Bibcode:2014QuGeo..20...89L. doi:10.1016/j.quageo.2013.12.001.
1 2 3 Arthur, Paul; Buccolieri, Alessandro; Imperiale, Marco Leo (2017). "Experimental rehydroxylation and the dating of early medieval and Byzantine ceramics. A southern Italian case study". European Journal of Postclassical Archaeologies. 7: 225–238. ISSN 2039-7895.
1 2 3 Bowen, Patrick K; Ranck, Helen J; Scarlett, Timothy J; Drelich, Jaroslaw W (Jaroslaw Drelich) (2011). "Rehydration/rehydroxylation kinetics of reheated XIX-Century Davenport (Utah) ceramic". Journal of the American Ceramic Society . 94 (8): 2585–2591. doi:10.1111/j.1551-2916.2011.04451.x.

This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.

[WilsonCHH09-1] 1 2 3 4 5 6 7 8 Wilson, Moira A.; Carter, Margaret A.; Hall, Christopher; Hoff, William D.; Ince, Ceren; Wilson, Moira A.; Savage, Shaun D.; McKay, Bernard; Betts, Ian M. (8 August 2009). "Dating fired-clay ceramics using long-term power law rehydroxylation kinetics". Proceedings of the Royal Society A. 465 (2108): 2407–2415. Bibcode:2009RSPSA.465.2407W. doi:10.1098/rspa.2009.0117.

[HamiltonH12-2] Hamilton, Andrea; Hall, Christopher (2012). "A review of rehydroxylation in fired-clay ceramics". Journal of the American Ceramic Society. 95 (9): 2673–2678. doi:10.1111/j.1551-2916.2012.05298.x.

[WilsonHHM03-3] 1 2 3 Wilson, Moira A; Hoff, William D; Hall, Christopher; McKay, Bernard; Hiley, Anna (2003). "Kinetics of moisture expansion in fired clay ceramics: a (time)^1/4 law". Physical Review Letters. 90 (12): 125503. Bibcode:2003PhRvL..90l5503W. doi:10.1103/PhysRevLett.90.125503. PMID 12688883.

[SD-4] 1 2 3 "Fire and water reveal new archaeological dating method". ScienceDaily. May 25, 2009.

[WilsonHIC12-5] 1 2 3 4 5 6 7 8 Wilson, Moira A; Hamilton, Andrea; Ince, Ceren; Carter, Margaret A; Hall, Christopher (2012). "Rehydroxylation (RHX) dating of archaeological pottery". Proceedings of the Royal Society A. 468 (2147): 3476–3493. Bibcode:2012RSPSA.468.3476W. doi: 10.1098/rspa.2012.0109 .

[6] Schurecht, H. G. (May 1928). "Methods for testing crazing of glazes caused by increases in size of ceramic bodies". Journal of the American Ceramic Society. 11 (5): 271–277. doi:10.1111/j.1151-2916.1928.tb16178.x. ISSN 0002-7820.

[7] McBurney, JW (1954). "Masonry cracking and damage caused by moisture expansion of structural clay tile". Proceedings - American Society for Testing and Materials. 54: 1219–1241.

[:0-8] 1 2 3 4 Avramovska, Marija; Chmelik, Christian; Derkowski, Arkadiusz; Fantalkin, Alexander; Freude, Dieter; Haase, Jürgen; Hare, Vincent; Kärger, Jörg; Kuligiewicz, Artur; Moinester, Murray (24 February 2021). "Searching for the fundamentals of rehydroxylation dating of archaeological ceramics via NMR and IR microscopy". Journal of the American Ceramic Society. 104 (10): 5328–5340. doi: 10.1111/jace.17753 . ISSN 0002-7820.

[9] Kuligiewicz, Artur; Derkowski, Arkadiusz (2021). "Rehydroxylation of fired clays: Is the time to the quarter (TTTQ) model correct?". Journal of Archaeological Science. 125: 1–9. Bibcode:2021JArSc.125j5301K. doi: 10.1016/j.jas.2020.105301 . ISSN 0305-4403.

[HallWH11-10] Hall, Christopher; Wilson, Moira A; Hoff, William D (2011). "Kinetics of long-term moisture expansion in fired-clay brick". Journal of the American Ceramic Society. 94 (1): 3651–3654. doi:10.1111/j.1551-2916.2011.04831.x.

[:1-11] 1 2 3 Drelich, Jaroslaw; Bowen, Patrick K.; Scarlett, Timothy J. (15 March 2013). Hall, C. (ed.). "Effect of Humidity Instability on Rehydroxylation in Fired Clay Ceramics". Journal of the American Ceramic Society. 96 (4): 1047–1050. doi:10.1111/jace.12262.

[HallWH12-12] 1 2 3 Hall, Christopher; Hamilton, Andrea; Wilson, Moira A (2013). "The influence of temperature on rehydroxylation (RHX) kinetics in archaeological pottery". Journal of Archaeological Science. 40 (1): 305–312. Bibcode:2013JArSc..40..305H. doi:10.1016/j.jas.2012.06.040.

[BUR2013-13] 1 2 Burakov, K.S.; Nachasova, I. E (2013). "Archaeomagnetic Study and Rehydroxlyation Dating of Fired-Clay Ceramics". Izvestiya, Physics of the Solid Earth. 49 (1): 105–112. Bibcode:2013IzPSE..49..105B. doi:10.1134/S1069351312120026.

[PW-14] Dacey, James (June 8, 2009). "Archaeological dating by re-firing ancient pots". Physics World.

[WIL2013-15] Wilson, Moira A.; Clelland, Sarah-Jane; Carter, Maragret A; Ince, Ceren; Hall Christopher; Hamilton Andrea; Batt, Catherine M (2013). "Rehydroxylation of fired-clay ceramics: Factors affecting early-stage mass gain in dating experiments" (PDF). Archaeometry. 56 (4): 689–702. doi: 10.1111/arcm.12038 . hdl:10454/6239.

[16] Numrich, M.; Kutschera, W.; Steier, P.; Sterba, J. H.; Golser, R. (2015). "On the effect of organic carbon on rehydroxylation (RHX) dating". Journal of Archaeological Science. 57: 92–97. Bibcode:2015JArSc..57...92N. doi:10.1016/j.jas.2015.01.016. ISSN 0305-4403.

[CLG2012-17] Clegg, Francis; Breen, Christopher; Carter, Margaret A; Ince, Ceren; Savage, Shaun D; Wilson, Moira A (2012). "Dehydroxylation and Rehydroxylation Mechanisms in Fired Clay Ceramic: A TG-MS and DRIFTS Investigation". Journal of the American Ceramic Society. 95 (1): 416–422. doi:10.1111/j.1551-2916.2011.04926.x.

[SHV2013-18] Shoval, Shlomo; Paz, Yitzhak (2013). "A study of the mass-gain of ancient pottery in relation to archeological ages using thermal analysis". Applied Clay Science. 82: 113–120. Bibcode:2013ApCS...82..113S. doi:10.1016/j.clay.2013.06.027.

[BAR2013-19] Barrett, Gerard, T. (2013). "Rehydroxylation dating of fired clays: an improved time-offset model to account for the effect of cooling on post-reheating mass gain". Journal of Archaeological Science. 40 (10): 3596–3603. Bibcode:2013JArSc..40.3596B. doi:10.1016/j.jas.2013.04.032.{{cite journal}}: CS1 maint: multiple names: authors list (link)

[GOF2014-20] Le Goff, Maxime; Gallet Yves (2014). "Evaluation of the rehydroxylation dating method: Insights from a new measurement device". Quaternary Geochronology. 20: 89–98. Bibcode:2014QuGeo..20...89L. doi:10.1016/j.quageo.2013.12.001.

[:2-21] 1 2 3 Arthur, Paul; Buccolieri, Alessandro; Imperiale, Marco Leo (2017). "Experimental rehydroxylation and the dating of early medieval and Byzantine ceramics. A southern Italian case study". European Journal of Postclassical Archaeologies. 7: 225–238. ISSN 2039-7895.

[BowenRSD11-22] 1 2 3 Bowen, Patrick K; Ranck, Helen J; Scarlett, Timothy J; Drelich, Jaroslaw W (Jaroslaw Drelich) (2011). "Rehydration/rehydroxylation kinetics of reheated XIX-Century Davenport (Utah) ceramic". Journal of the American Ceramic Society . 94 (8): 2585–2591. doi:10.1111/j.1551-2916.2011.04451.x.

[1]

[2]

[3]

[4]

[5]

[6]

[7]

[8]

[9]

[10]

[11]

[12]

[13]

[14]

[15]

[16]

[17]

[18]

[19]

[20]

[21]

[22]