Copper sheathing is a method for protecting the hull of a wooden vessel from attack by shipworm, barnacles and other marine growth through the use of copper plates affixed to the surface of the hull, below the waterline. It was pioneered and developed by the Royal Navy during the 18th century. In antiquity, ancient Greeks used lead plates to protect the underwater hull.
Deterioration of the hull of a wooden ship was a significant problem during the Age of Sail. Ships' hulls were under continuous attack by shipworm, barnacles and other marine growth, all of which had some adverse effect on the ship, be it structurally, in the case of the worm, or affecting speed and handling in the case of the weeds. The most common methods of dealing with these problems were through the use of wood, and sometimes lead, sheathing. Expendable wood sheathing effectively provided a non-structural skin to the hull for the worm to attack, and could be easily replaced in dry dock at regular intervals. However, weed grew rapidly and slowed ships. Lead sheathing, while more effective than wood in mitigating these problems, reacted badly with the iron bolts of the ships. [1]
Even older than the sheathing methods were the various graving and paying techniques. There were three main substances used: white stuff, [2] which was a mixture of whale oil, rosin and brimstone; black stuff, [2] a mixture of tar and pitch; and brown stuff, [2] which was simply brimstone added to black stuff. It was common practice to coat the hull with the selected substance, then cover that with a thin outer layer of wooden planking. [3]
The use of copper sheathing was first suggested by Charles Perry in 1708, though it was rejected by the Navy Board on grounds of high cost and perceived maintenance difficulties. The first experiments with copper sheathing were made in the late 1750s: the bottoms and sides of several ships' keels and false keels were sheathed with copper plates. [4]
In 1761, the experiment was expanded, and the 32-gun frigate HMS Alarm was ordered to have her entire bottom coppered, in response to the terrible condition in which she had returned from service in the West Indies. HMS Alarm was chosen because, in 1761, a letter had been sent regarding the ship's condition, saying that the worms from the waters had taken a significant toll on the ship’s wooden hull. [5] Before the copper plates were applied, the hull was covered with "soft stuff", which was simply hair, yarn and brown paper. The copper performed very well, both in protecting the hull from worm invasion and in preventing weed growth for, when in contact with water, the copper produced a poisonous film, composed mainly of copper oxychloride, that deterred these marine organisms. Furthermore, as this film was slightly soluble, it gradually washed away, leaving no way in which marine life could attach itself to the ship. However, it was soon discovered by the Admiralty that the copper bolts used to hold the plates to the hull had reacted with the iron bolts used in the construction of the ship, rendering many bolts nearly useless. In 1766, because of the poor condition of the iron bolts, Alarm's copper was removed. [6]
After this experiment, and deterred by the unanticipated and not understood galvanic reaction between the copper and iron, lead sheathing was tried again, though it was found to be unsuitable to the task, as the plates tended to fall from the hull alarmingly quickly. By 1764, a second vessel, HMS Dolphin, had been sheathed in copper, specifically to prepare her for a voyage of discovery in tropical waters. [7] Dolphin's hull was inspected in 1768 after the ship had twice circumnavigated the world; there was significant corrosion of the hull's iron components, which had to be replaced. [5] In 1769 another attempt was made at coppering a ship's hull, this time on a new ship that had been constructed using bolts made from a copper alloy. The results were far more favourable this time, but still the problems with the bolting remained. The onset and intensification from 1773 of the war with America took the focus off the bolting issue necessary to allow a full-scale coppering programme. [8]
By the 1780s the technology had spread to India. The ruler of Mysore, Tipu Sultan, ordered that all his navy vessels receive copper sheathing after observing the benefits in French and East India Company ships. [9]
With the American war in full swing, the Royal Navy set about coppering the bottoms of the entire fleet in 1778. This would not have happened but for war. This also came about because in 1778 a Mr. Fisher, a Liverpool shipbuilder (who did a brisk trade with West Africa) sent a letter to the Navy Board. [11] In it he recommended "copper sheathing" as a solution to the problems of ship worm in warm tropical waters, and the effect on speed of tendrils of seaweed latching onto hulls. The letter itself does not survive and is obliquely referred to in other official correspondence held by the National Maritime Museum; it may have contained or been coincidental with a critical new technical breakthrough of protecting the iron bolting by applying thick paper between the copper plates and the hull. This had recently been trialled successfully (probably) on HMS Jupiter. This breakthrough was to be what would win over the Admiralty. [8]
Fisher's letter was seen by the new Navy Board Controller Charles Middleton, who had the major problem at the time with supplying over 100 ships for the American Revolutionary War (1775–1783), which was compounded that same year (1778) by French opportunism in declaring war on Britain to support the American rebels. This effectively turned what was a local civil war into a global conflict. Spain followed in 1779 and the Netherlands in 1780, and so Britain had to face its three greatest rivals. Middleton took the view that Britain was "outnumbered at every station", and the Navy was required to "extricate us from present danger". He understood that coppering allowed the navy to stay at sea for much longer without the need for cleaning and repairs to the underwater hull, making it a very attractive, if expensive, proposition. He had to expand the Navy but there was no time to add to the fleet, and limited resources available. It could take five years and 2000 trees to build a warship. However he could refurbish the existing fleet, he grasped Fisher's solution and on 21 January 1779 wrote to the Admiralty. He also petitioned King George III directly on this "matter of the gravest importance" for the necessary funding. He took with him a model of HMS Bellona showing a coppered bottom to illustrate the method. The King backed him for what was an expensive process for an untested technology.
Each ship on average required 15 tonnes of copper applied on average as 300 plates. All the copper was supplied by British mines (the only country in the world at that time that could do so), the largest mine being Parys Mountain in Anglesey, north Wales. The Parys mine had recently begun large-scale production and had glutted the British market with cheap copper; however, the 14 tons of metal required to copper a 74-gun third-rate ship of the line still cost £1,500, [12] compared to £262 for wood. The benefits of increased speed and time at sea were deemed to justify the costs involved. Middleton, in May 1779, placed orders at the Portsmouth Docks for coppering all ships up to and including 32 guns when next they entered dry dock. In July, this order was expanded to include ships of 44 guns and fewer, in total 51 ships within a year. It was then decided that the entire fleet should be coppered, due to the difficulties in maintaining a mixed fleet of coppered and non-coppered ships. By 1781, 82 ships of the line had been coppered, along with fourteen 50-gun ships, 115 frigates, and 182 unrated vessels.
All this was too late to avert the loss of the American colonies, however; meanwhile the French were threatening the lucrative sugar trade in the Caribbean, reckoned at the time as being of more importance to British interests than the 13 colonies. The sugar trade was paying for the costs of the American Revolutionary War and the Anglo-French War (1778–1783). The Royal Navy's newly coppered ships, as yet untested, were used successfully by Rodney in defeating the French at the Battle of the Saintes off Dominica in 1782.
By the time the war ended in 1783, problems with the hull bolting were once more becoming apparent. [13] Finally, a suitable alloy for the hull bolts was found, that of copper and zinc. At great cost the Admiralty decided in 1786 to go ahead with the re-bolting of every ship in the navy, thus finally eliminating the bolt corrosion problem. This process lasted several years, after which no significant changes to the coppering system were required and metal plating remained a standard method of protecting a ship's underwater hull until the advent of modern anti-fouling paint. [4] In the 19th century, pure copper was partially superseded by Muntz metal, an alloy of 60% copper, 40% zinc and a trace of iron. Muntz metal had the advantage of being somewhat cheaper than copper.
With its widespread adoption by the Royal Navy, some shipping owners employed the method on their merchant vessels. A single coppered vessel was recorded on the register of Lloyd's of London in 1777, a slaver sloop Hawke, 140 tons. [14] [15] This particular vessel impressed the Admiralty when it was inspected by Sandwich in 1775 at Sheerness after a 5-year voyage to India. [16] By 1786, 275 vessels (around 3% of the merchant fleet) were coppered. By 1816, this had risen to 18% of British merchant ships. [15] Copper sheets were exported to India for use on ships built there. In the late 18th and early 19th century, around 30% of Indian ships were coppered. [17]
Merchant ship owners were attracted by the savings made possible by copper sheathing, despite the initial outlay. As the coppering was expensive, only the better owners tended to invest in the method, and as a result the use of copper sheathing tended to indicate a well-found and maintained ship, which led to Lloyd's of London charging lower insurance premiums, as the vessels were better risks.[ citation needed ] From this stems the phrase "copper-bottomed" as an indication of quality.
Coppering was more commonly used on merchant ships sailing in warm waters. Ships sailing in colder, northern waters often continued to use replaceable, wooden sheathing planks. Wood-boring organisms were less of a problem for these vessels and they were often routinely careened – an operation that could cause considerable damage to expensive coppering. [15] Coppering was widely used on slave ships. [15] After the Abolition of the Slave Trade Act became British law in 1807, the slave trade became illegal so slavers valued fast ships that were more likely to evade patrolling Royal Navy vessels intent on capturing them.
In the late 18th to early 19th century, Sir Humphry Davy performed many experiments to determine how to lessen the corrosion that the seawater caused on unprotected copper sheathing. To this end he had various thicknesses of copper submerged on the shore and then measured how much the sea water had degraded each one. Sheets of different metals remained in the seawater for four months and then were examined. Two harbour ships were also used in this test, one with an additional zinc band, the other with an iron one. Davy observed, that while the zinc and iron themselves became covered in carbonate that allowed weeds, plant life and insects to attach themselves to the metal, the copper sheets that were connected to cast iron or zinc parts were free of any attached life forms or discoloration. Unprotected copper would quickly go from a reddish color to a greenish color of corrosion. [18] When the other metals were mixed with copper in ratios from 1:40 to 1:150, there was no visible sign of corrosion and minimal weight loss. [18] When the ratio was changed to 1:200 and 1:400, there was significant corrosion and weight loss. Davy therefore advocated cast iron for protecting copper, since it was the cheapest to manufacture, and in his observations malleable iron and zinc seemed to wear down faster.
The term copper-bottomed continues to be used to describe a venture, plan or investment that is safe and is certain to be successful. [19] The related copper-fastened (and verb form copperfasten ) is used similarly, though with the nuance of "secured, unambiguous", rather than "trustworthy, reliable". [20]
HMS Scorpion was an ironclad turret ship built by John Laird Sons & Company, at Birkenhead, England. She was one of two sister ships secretly ordered from the Laird shipyard in 1862 by the Confederate States of America.
The first HMS Wivern was an ironclad turret ship built at Birkenhead, England. She was one of two sister ships secretly ordered from the John Laird Sons & Company shipyard in 1862 by the Confederate States of America.
An ironclad is a steam-propelled warship protected by steel or iron armor constructed from 1859 to the early 1890s. The ironclad was developed as a result of the vulnerability of wooden warships to explosive or incendiary shells. The first ironclad battleship, Gloire, was launched by the French Navy in November 1859, narrowly preempting the British Royal Navy. However, Britain built the first completely iron-hulled warships.
Anti-fouling paint is a specialized category of coatings applied as the outer (outboard) layer to the hull of a ship or boat, to slow the growth of and facilitate detachment of subaquatic organisms that attach to the hull and can affect a vessel's performance and durability. It falls into a category of commercially available underwater hull paints, also known as bottom paints.
Biofouling or biological fouling is the accumulation of microorganisms, plants, algae, or small animals where it is not wanted on surfaces such as ship and submarine hulls, devices such as water inlets, pipework, grates, ponds, and rivers that cause degradation to the primary purpose of that item. Such accumulation is referred to as epibiosis when the host surface is another organism and the relationship is not parasitic. Since biofouling can occur almost anywhere water is present, biofouling poses risks to a wide variety of objects such as boat hulls and equipment, medical devices and membranes, as well as to entire industries, such as paper manufacturing, food processing, underwater construction, and desalination plants.
HMS Culloden was a 74-gun third-rate ship of the line of the Royal Navy, built at Deptford Dockyard, England, and launched on 18 May 1776. She was the fourth warship to be named after the Battle of Culloden, which took place in Scotland in 1746 and saw the defeat of the Jacobite rising.
Muntz metal is an alpha-beta brass alloy composed of approximately 60% copper, 40% zinc and a trace of iron. It is named after George Fredrick Muntz, a metal-roller of Birmingham, England, who commercialised the alloy following his patent of 1832.
Edmund Davy FRS was a professor of chemistry at the Royal Cork Institution from 1813 and at the Royal Dublin Society from 1826. He discovered acetylene, as it was later named by Marcellin Berthelot. He was also an original member of the Chemical Society, and a member of the Royal Irish Academy.
The two Scorpion-class ironclads, HMS Scorpion and HMS Wivern, were ironclad warships ordered by the Confederate States Navy in 1862 and seized in 1863 by the British to prevent their delivery. This would have violated the Foreign Enlistment Act, which forbade British subjects to build or arm any ships for governments at war with governments friendly to Great Britain. The Scorpion class were masted turret ships, each with two gun turrets that were designed to mount a pair of heavy muzzle-loading guns. They were purchased for service in the Royal Navy in 1864 and served briefly with the Channel Fleet before they became guard ships at Bermuda and Hong Kong. Scorpion was sold in 1903 and sank under tow to be scrapped, while Wivern was sold for scrap in 1922.
The Swiftsure class battleships of the late Victorian era were broadside ironclads designed and built specifically for service as Flagships on the Pacific station.
Composite construction is a generic term to describe any building construction involving multiple dissimilar materials. Composite construction is often used in building aircraft, watercraft, and building construction. There are several reasons to use composite materials including increased strength, aesthetics, and environmental sustainability.
HMS Alarm was a 32-gun fifth-rate Niger-class frigate of the Royal Navy, and was the first Royal Navy ship to bear this name. She was built at King's Yard in Harwich by John Barnard.
The Revere Copper Company is a copper rolling mill in the United States. It operated North America's first copper rolling mill. It was started by Paul Revere in 1801 in Canton, Massachusetts, and developed a commercially viable process for manufacturing copper sheets.
HMS Calypso was a corvette of the Royal Navy and the lead ship of its namesake class. Built for distant cruising in the heyday of the British Empire, the vessel served as a warship and training vessel until 1922, when it was sold.
HMS Cordelia was a Comus-class corvette of the Royal Navy, built at the Portsmouth Dockyard and launched on 25 October 1881.
HMS Pylades was a Satellite-class composite screw sloop of the Royal Navy, built at Sheerness Dockyard and launched on 5 November 1884. She was later reclassified as a corvette and was the last corvette built for the Royal Navy until the Second World War.
HMS Victory is a 104-gun first-rate ship of the line of the Royal Navy. She was ordered in 1758, laid down in 1759, and launched in 1765. With 246 years of service as of 2024, she is the world's oldest naval vessel still in commission.
Galvanic corrosion is an electrochemical process in which one metal corrodes preferentially when it is in electrical contact with another, in the presence of an electrolyte. A similar galvanic reaction is exploited in primary cells to generate a useful electrical voltage to power portable devices. This phenomenon is named after Italian physician Luigi Galvani (1737–1798).
HMS Canada was a Comus-class screw corvette of the Royal Navy. She was launched in 1881 and sold for scrap in 1897. Her bow badge was removed prior to being sold for scrap and is displayed in the Maritime Museum of British Columbia.
HMS Cleopatra was a Royal Navy Comus-class screw corvette built in 1878.
{{cite book}}: |work= ignored (help){{cite book}}: |work= ignored (help)Genuine; trustworthy.