Gold parting

Last updated

Gold parting is the separating of gold from silver (and other metallic impurities). Gold and silver are often extracted from the same ores and are chemically similar and therefore difficult to separate. The alloy of gold and silver is called electrum. [1]

Contents

Contemporary technology

Two technologies are dominant. They both start with relatively pure gold.

Other

Alternative methods exist for parting gold. Silver can be dissolved selectively by boiling the mixture with 30% nitric acid, a process sometimes called inquartation. Affination is a largely obsolete process of removing silver from gold using concentrated sulfuric acid. [4]

The Acidless Separation (ALS) has been investigated to pre-refine doré and jewelry alloys even when there is high silver content, which is normally a problem for existing chemical pre-refinement processes. The metals are separated by distillation. [5]

Cupellation removes gold and silver from mixtures containing lead and other metals, but silver cannot be separated from gold by this process alone.

History

Gold parting as a process was invented specifically to remove silver. The advent of coinage required methods to remove impurities from the gold. Over the centuries special means of separation have been invented.

The main ancient process of gold parting was by salt cementation, of which there is archaeological evidence from the 6th century BC in Sardis, Lydia. In the post-medieval period parting using antimony, sulfates and mineral acids was also used.

Early history

The very earliest attempts at refining gold can be shown by the surface enhancement of gold rings. Gold quality was increased at the surface by 80–95% gold compared to 64–75% gold at the interior found in Nahal Qanah Cave dated to the 4th millennium BC. Further evidence is from three gold chisels from the 3rd Millennium BC royal cemetery at Ur that had a surface of high gold (83%), low silver (9%) and copper (8%) compared with an interior of 45% gold, 10% silver and 45% copper. The surface was compacted and heavily burnished and indicates early use of depletion gilding.

Ancient and medieval world

Early 6th century BC Lydian gold coinage BMC 06.jpg
Early 6th century BC Lydian gold coinage

Separation of gold from silver was not practised in antiquity prior to the Lydian Period (12th century BC to 546 BC). [6] Material from Sardis (in modern Turkey) is evidence of the earliest use of gold and silver parting in the 6th century. [7] Literary sources and the lack of physical evidence suggest that gold-silver parting was not practised before the mid first millennium BC. Gold parting came with the invention of coinage and there is no evidence for the use of a true refining processes before the introduction of coinage. As refining gold (as opposed to surface enhancement) results in a noticeable loss in material, there would have been little reason to do this before the advent of coinage and the need to have a standard grade of material.

The first possible literary reference to the salt cementation parting process is in the Arthashastra, a 4th-century BC treatise from India, that mentions heating of gold with Indus earth. Indus earth is taken to mean soils high in salt, nitre and ammonium salts and therefore ideal for the cementation parting process. A better known and more detailed early description is given by Diodorus Siculus in the 1st century BC quoting an earlier lost book, On the Erythraean Sea from the 2nd century BC by Agatharchides of Cnidus. [8] An experiment recreating the process as described by Diodorus Siculus by heating a mixture of the gold and salt in a sealed pot for 5 days was done by Notton and was found to be successful.

Pliny in his Naturalis Historia mentions the purification of gold a number of times and makes reference to the salt cementation process of gold parting. He says that the gold is "roasted with a double weight of salt and three times the weight of misy (ferric sulfates) and again with two portions of salt and one of the stone which is called schiston." Here he is describing the heating of gold with salt and iron sulfates which act to dissolve the copper and silver in the gold. [9] Parting vessels used for refining gold with the cementation process have been found in London, Lincoln, York and Winchester. The London vessels, dating from the Flavian period (c. 70–85 AD), were sealed using luting clay; XRF analysis detected gold and silver, with highest concentration around the sealed region showing possible escape of silver as the volatile silver chloride. [10]

Gold parting had been well used throughout the ancient times but only in the Medieval period were clear and detailed descriptions of the processes written. All the archaeological finds of Roman and early medieval parting point to a solid state process using common salt as the active ingredient. [11] The only large group of medieval parting vessels so far discovered were found at Coppergate and Piccadilly sites in York. [12] The pinkish-purple discolouration of the vessels showed them to have been used with the salt cementation process which removes iron from the clay as ferric chloride. Other vessel fragments are known from Carlisle and Winchester. [13] Theophilus was a 12th-century German monk and in his book De Diversus Artibus [14] gives the clearest description of the salt cementation process.

break into tiny pieces a tile or piece of burnt and reddened furnace-clay and when it is powdered, divide it into two equal parts by weight and add to it a third part of salt of the same weight. It should then be lightly sprinkled with urine and mixed so that it does not stick together but is just moistened.

—  Theophilus, [15]

This mixture is then added to an earthenware pot and layered with thin sheets of gold foil. The pot is then sealed and heated in a furnace.

Then put the fire and wood below and see that a plentiful fire is not lacking for the space of a day and a night. In the morning, however, take out the gold and melt it again, hammer it, and put it into the furnace as before. After another day and night take it out again, mix a little red copper with it, melt as before, and put it back into the furnace. And when you have taken it out a third time, wash it and carefully dry it. Weigh it, when dried, and see how much has been lost, then fold it up and keep it.

—  Theophilus, [16]

It was during the medieval period that distillation was discovered and the first description of nitric acid production was given by Pseudo-Geber in the Summa perfectionis, 1330. Nitric acid is able to dissolve silver. The addition of sal ammoniac to nitric acid creates aqua regia and this acid is able to dissolve gold. Both acids are used in the acid method of parting but the acids were expensive so were not used until the post medieval period. [17]

Post medieval to modern period

Distillation using an alembic Distillation by Retort.png
Distillation using an alembic
Title page of the 1556 edition of Agricola's De Re Metallica De re metallica title page 1556.jpg
Title page of the 1556 edition of Agricola's De Re Metallica

Comprehensive accounts of the salt cementation processes is given by Biringuccio in his The Method of cementing gold and of Bringing it to its Ultimate Fineness.; in the Probierbuchlein – Little Books on Assaying; by Georgius Agricola in book 10 of De Re Metallica ; and by Ercker in his Treatise on ores and assaying. This was a period where new techniques began to be explored. Granulation of the gold instead of gold foil increased surface area and therefore the efficiency of the reaction. Salt cementation continued to be the main method of parting until the 16th century but in later Middle Ages processes using sulfur, antimony and mineral acids began to be used. There are archaeological finds at sites in London of distillation vessels for making acids in Britain from the 15th century which include fragments of ceramic cucurbits (vessels for heating reacting chemicals) which were used with alembics for distillation. [18] By the 18th century cementation was rarely used and had been replaced by acid treatment. Into modern times the acid parting method continued to be used but other methods were discovered. In 1860s Australia the Miller process was developed, this removed silver by bubbling chlorine gas through the molten gold mixture. Soon after, in the 1870s, electrolytic refining of gold was developed, the Wohlwill process, to deal with the problem of removing platinum from the gold. This technique is the most commonly used today. [19]

Historic processes

Salt cementation

This process was used from Lydian to post-medieval times. It is a solid state process relying on common salt as the active ingredient but it is possible to use a mixture of saltpetre (KNO3) and green vitriol (FeSO4). The basic process involved the mixing of argentiferous gold foil (in later periods granules were used), common salt and brick dust or burnt clay in a closed and sealed container. Theophilus mentions the addition of urine to the mix. With heating, the silver reacts with the salt to form silver chloride which is removed leaving a purified gold behind. Conditions needed for this process are below 1000 °C as the gold should not melt. Silver can be recovered by smelting the debris. [20] Heating can take 24 hours. Hoover and Hoover [21] explains the process thus: under heating salt (sodium chloride, NaCl) decomposes in the presence of silica and alumina (from the brick dust or clay) to produce hydrochloric acid and also some chlorine. This reacts with the silver to produce silver chloride (AgCl). The urine is acidic and aids decomposition. Silver chloride is volatile and would be removed from the metal. And the container is sealed to stop the escape of the silver which can be recovered later. Notton in experiments found that with one heating the gold content could be taken from 37.5% to 93% [22]

Sulfur and antimony processes

Separation of gold and silver by sulfur, De Re Metallica 1556 De Re Metallica 1556 p 363 AQ22 (2).TIF
Separation of gold and silver by sulfur, De Re Metallica 1556

This is similar to the salt cementation process but creates sulfides instead of chlorides. Finely divided impure gold and elemental sulfur are reacted together under moderate heat in a sealed crucible. The impurities form metal sulfides and the gold is left unreacted. The gaseous sulfide condenses on the crucible fabric. The antimony process is the same but uses stibnite (Sb2S3) instead of sulfur because stibnite is stable at a higher temperature than sulfur. This is much quicker than the salt process and gave a purer gold, but it could dissolve some of the gold as well. This process is first described in the Probierbuchlein. [23]

Acid parting

Pure gold precipitate produced by the aqua regia refining process Golddust.jpg
Pure gold precipitate produced by the aqua regia refining process

The distillation was used in the 12th century Europe after its introduction from the East [24] and after that period more powerful acids could be created. Nitric acid (aqua fortis, called by Agricola aqua valens) could be made by the distillation of saltpetre (KNO3) with water and alum (KAl(SO4)2) or vitriol (FeSO4). [18] [19]

2KNO3 + H2O + FeSO4 → FeO + K2SO4 + 2HNO3

Nitric acid, after distillation to increase the acid strength, is capable of dissolving the silver but it will not (by itself) dissolve the gold. However, nitric acid is not able to (fully) extract silver and other impurities from an alloy with a high content of gold. Therefore, one part of scrap gold was typically alloyed with three parts of copper (quartering) before parting with nitric acid. Another method uses Sterling silver instead of copper. One part pure gold is alloyed with three parts Sterling silver (inquarting). The resulting six karat (6K) gold can then be parted with dilute nitric acid (one part 68–70% nitric acid to one part distilled water). With the karat gold this low (6K), and over medium high heat, the dilute nitric acid will dissolve the Sterling silver (and other base metals in the karat gold) starting on the outside surface of the 6K gold alloy, working its way into the gold alloy, forming a honeycomb structure as it works its way into the metals. Since nitric acid will not dissolve gold, nearly pure gold (very close to 99.5% pure) will be left behind after the reaction is complete. After removing the solid gold other elements like silver and copper may be extracted from the liquid. To get the gold to a very high level of purity (999 fine gold) it is sometimes processed further with aqua regia to effectively remove all the impurities.

Aqua regia was also used for parting. It was made by adding sal ammoniac to nitric acid which produced a mixture of hydrochloric acid and nitric acid. This acid dissolved the gold to a soluble chloride and the silver was attacked and precipitated as an insoluble chloride. Silver was removed by filtering and gold was then recovered by evaporating the liquid and heating the residue. Nitric acid was suitable for separating small quantities of gold from silver and aqua regia used to separate small quantities of silver from gold. Aqua regia acid process is used by refiners of scrap gold used in jewelry manufacturing. This process is also well suited to recycling consumers' used or broken jewelry directly back onto the global market 24kt inventory. [17]

See also

Citations

  1. ↑ Renner, Hermann; Schlamp, Günther; Hollmann, Dieter; Lüschow, Hans Martin; Tews, Peter; Rothaut, Josef; Dermann, Klaus; Knödler, Alfons; Hecht, Christian; Schlott, Martin; Drieselmann, Ralf; Peter, Catrin; Schiele, Rainer (2000). "Gold, Gold Alloys, and Gold Compounds". Ullmann's Encyclopedia of Industrial Chemistry. doi:10.1002/14356007.a12_499. ISBN   3527306730.
  2. 1 2 Yannopoulos, J. C. (1991). The extractive metallurgy of gold. New York: Van Nostrand Reinhold. pp. 242–243. ISBN   978-0-442-31797-3.
  3. 1 2 Rapson, William S. (1992). "Mining, Extraction and Refining of Gold". Interdisciplinary Science Reviews. 17 (3): 203–212 [210]. Bibcode:1992ISRv...17..203R. doi:10.1179/030801892789816145.
  4. ↑ Etris, S. F. (2010). "Silver and Silver Alloys". Kirk-Othmer Encyclopedia of Chemical Technology. pp. 1–43. doi:10.1002/0471238961.1909122205201809.a01.pub3. ISBN   978-0471238966.
  5. ↑ Boscato, M. (2016). "Presentation of a new acid-free refinement process for gold and silver". Jewel Technology Forum.
  6. ↑ Craddock, P. T. 2000a Historical Survey of Gold Refining: 1 Surface Treatments and Refining Worldwide, and in Europe Prior to AD 1500. In A. Ramage and P. T Craddock (eds) King Croesus' Gold; Excavations at Sardis and the History of Gold Refining. London: British Museum Press pp27
  7. ↑ Rehren, T. 2003. Crucibles as Reaction Vessels in Ancient Metallurgy. In Craddock, P. T and Lang, J. (eds.) Mining and Metal Production through the Ages. London: British Museum Press pp207
  8. ↑ Notton, J. H. F. (1974). "Ancient Egyptian gold refining". Gold Bulletin. 7 (2): 50–56 [52]. doi: 10.1007/BF03215038 .
  9. ↑ Craddock, P. T. 2000a Historical Survey of Gold Refining: 1 Surface Treatments and Refining Worldwide, and in Europe Prior to AD 1500. In A. Ramage and P. T Craddock (eds) King Croesus' Gold; Excavations at Sardis and the History of Gold Refining. London: British Museum Press. Pp38
  10. ↑ Bayley, J. 1990. Archaeological Evidence for Parting. In E. Pernicka and G. A. Wagner (eds) Archaeometry '90. Basel ; Boston : Birkhäuser Verlag
  11. ↑ Bayley, J. 2008. Medieval precious metal refining: archaeology and contemporary texts compared. In Martinon-Torres, M. and Rehren, T. (eds) Archaeology, history and science: integrating approaches to ancient materials. Walnut Creek: Left Coast Press. Pp142-3
  12. ↑ Bayley, J. 1992. Non-Ferrous Metalworking at 16–22 Coppergate. The Archaeology of York 17/7. London:CBA
  13. ↑ Bayley, J. 2008. Medieval precious metal refining: archaeology and contemporary texts compared. In Martinon-Torres, M. and Rehren, T. (eds) Archaeology, history and science: integrating approaches to ancient materials. Walnut Creek: Left Coast Press pp143
  14. ↑ Hawthorne, J. G .; Smith, C. S. (1979). On divers arts: the foremost medieval treatise on painting, glassmaking, and metalwork. New York: Dover Publications. ISBN   978-0-486-23784-8.
  15. ↑ Dodwell, C. R. (1971). "Gold metallurgy in the twelfth century". Gold Bulletin. 4 (3): 51–55. doi: 10.1007/BF03215143 .
  16. ↑ Craddock, P. T. 2000a Historical Survey of Gold Refining: 1 Surface Treatments and Refining Worldwide, and in Europe Prior to AD 1500. In A. Ramage and P. T Craddock (eds) King Croesus' Gold; Excavations at Sardis and the History of Gold Refining. London: British Museum Press. Pp38–39
  17. 1 2 Taylor, F. S. 1956. Pre-scientific Industrial Chemistry. In C. Singer, E.J. Holmyard, A.R. Hall and T. I. Williams (eds) A history of technology: Vol.2, The Mediterranean civilizations and the Middle Ages; c700 B.C. to c,A.D. 1500. Oxford : Clarendon Press pp356-7
  18. 1 2 Bayley, J. 2008. Medieval precious metal refining: archaeology and contemporary texts compared. In Martinon-Torres, M. and Rehren, T. (eds) Archaeology, history and science: integrating approaches to ancient materials. Walnut Creek: Left Coast Press pp145
  19. 1 2 Craddock, P. T. 2000b Historical Survey of Gold Refining: 2 Post-medieval Europe. In A. Ramage and P. T Craddock (eds) King Croesus' Gold; Excavations at Sardis and the History of Gold Refining. London: British Museum Press pp69
  20. ↑ Rehren, T. 2003. Crucibles as Reaction Vessels in Ancient Metallurgy. In Craddock, P. T and Lang, J. (eds.) Mining and Metal Production through the Ages. London: British Museum Press 207
  21. ↑ Hoover, H.C. and Hoover, L. H. 1950. Georgius Agricola: De re metallica New York : Dover pp456
  22. ↑ Notton, J. H. F. (1974). "Ancient Egyptian gold refining". Gold Bulletin. 7 (2): 50–56 [55]. doi: 10.1007/BF03215038 .
  23. ↑ Craddock, P. T. 2000b Historical Survey of Gold Refining: 2 Post-medieval Europe. In A. Ramage and P. T Craddock (eds) King Croesus' Gold; Excavations at Sardis and the History of Gold Refining. London: British Museum Press. pp68
  24. ↑ Taylor, F. S. 1956. Pre-scientific Industrial Chemistry. In C. Singer, E.J. Holmyard, A.R. Hall and T. I. Williams (eds) A history of technology: Vol.2, The Mediterranean civilizations and the Middle Ages; c700 B.C. to c,A.D. 1500. Oxford : Clarendon Press

Related Research Articles

<span class="mw-page-title-main">Brass</span> Alloy of copper and zinc

Brass is an alloy of copper (Cu) and zinc (Zn), in proportions which can be varied to achieve different colours and mechanical, electrical, acoustic, and chemical properties, but copper typically has the larger proportion. In use since prehistoric times, it is a substitutional alloy: atoms of the two constituents may replace each other within the same crystal structure.

<span class="mw-page-title-main">Lydia</span> Ancient Anatolian kingdom

Lydia was an Iron Age kingdom situated in the west of Asia Minor, in modern-day Turkey. The ethnic group inhabiting this kingdom are known as the Lydians, and their language as Lydian and their capital was Sardis.

<span class="mw-page-title-main">Metallurgy</span> Field of science that studies the physical and chemical behavior of metals

Metallurgy is a domain of materials science and engineering that studies the physical and chemical behavior of metallic elements, their inter-metallic compounds, and their mixtures, which are known as alloys.

<span class="mw-page-title-main">Nitric acid</span> Highly corrosive mineral acid

Nitric acid is the inorganic compound with the formula HNO3. It is a highly corrosive mineral acid. The compound is colorless, but samples tend to acquire a yellow cast over time due to decomposition into oxides of nitrogen. Most commercially available nitric acid has a concentration of 68% in water. When the solution contains more than 86% HNO3, it is referred to as fuming nitric acid. Depending on the amount of nitrogen dioxide present, fuming nitric acid is further characterized as red fuming nitric acid at concentrations above 86%, or white fuming nitric acid at concentrations above 95%.

<span class="mw-page-title-main">Silver</span> Chemical element, symbol Ag and atomic number 47

Silver is a chemical element; it has symbol Ag ) and atomic number 47. A soft, white, lustrous transition metal, it exhibits the highest electrical conductivity, thermal conductivity, and reflectivity of any metal. The metal is found in the Earth's crust in the pure, free elemental form, as an alloy with gold and other metals, and in minerals such as argentite and chlorargyrite. Most silver is produced as a byproduct of copper, gold, lead, and zinc refining.

<span class="mw-page-title-main">Sardis</span> Ancient city in Turkey

Sardis or Sardes was an ancient city best known as the capital of the Lydian Empire. After the fall of the Lydian Empire, it became the capital of the Persian satrapy of Lydia and later a major center of Hellenistic and Byzantine culture. Now an active archaeological site, it is located in modern day Turkey, in Manisa Province near the town of Sart.

<span class="mw-page-title-main">Aqua regia</span> Mixture of nitric acid and hydrochloric acid in a 1:3 molar ratio

Aqua regia is a mixture of nitric acid and hydrochloric acid, optimally in a molar ratio of 1:3. Aqua regia is a fuming liquid. Freshly prepared aqua regia is colorless, but it turns yellow, orange or red within seconds from the formation of nitrosyl chloride and nitrogen dioxide. It was named by alchemists because it can dissolve noble metals like gold and platinum, though not all metals.

Extractive metallurgy is a branch of metallurgical engineering wherein process and methods of extraction of metals from their natural mineral deposits are studied. The field is a materials science, covering all aspects of the types of ore, washing, concentration, separation, chemical processes and extraction of pure metal and their alloying to suit various applications, sometimes for direct use as a finished product, but more often in a form that requires further working to achieve the given properties to suit the applications.

<span class="mw-page-title-main">Noble metal</span> Metallic elements that are nearly chemically inert

A noble metal is ordinarily regarded as a metallic chemical element that is generally resistant to corrosion and is usually found in nature in its raw form. Gold, platinum, and the other platinum group metals are most often so classified. Silver, copper, and mercury are sometimes included as noble metals, but each of these usually occurs in nature combined with sulfur.

<span class="mw-page-title-main">Crucible</span> Container in which substances are heated

A crucible is a ceramic or metal container in which metals or other substances may be melted or subjected to very high temperatures. Although crucibles have historically tended to be made out of clay, they can be made from any material that withstands temperatures high enough to melt or otherwise alter its contents.

<span class="mw-page-title-main">Crucible steel</span> Type of steel

Crucible steel is steel made by melting pig iron, iron, and sometimes steel, often along with sand, glass, ashes, and other fluxes, in a crucible. In ancient times steel and iron were impossible to melt using charcoal or coal fires, which could not produce temperatures high enough. However, pig iron, having a higher carbon content and thus a lower melting point, could be melted, and by soaking wrought iron or steel in the liquid pig-iron for a long time, the carbon content of the pig iron could be reduced as it slowly diffused into the iron, turning both into steel. Crucible steel of this type was produced in South and Central Asia during the medieval era. This generally produced a very hard steel, but also a composite steel that was inhomogeneous, consisting of a very high-carbon steel and a lower-carbon steel. This often resulted in an intricate pattern when the steel was forged, filed or polished, with possibly the most well-known examples coming from the wootz steel used in Damascus swords. The steel was often much higher in carbon content and in quality in comparison with other methods of steel production of the time because of the use of fluxes. The steel was usually worked very little and at relatively low temperatures to avoid any decarburization, hot short crumbling, or excess diffusion of carbon; just enough hammering to form the shape of a sword. With a carbon content close to that of cast iron, it usually required no heat treatment after shaping other than air cooling to achieve the correct hardness, relying on composition alone. The higher-carbon steel provided a very hard edge, but the lower-carbon steel helped to increase the toughness, helping to decrease the chance of chipping, cracking, or breaking.

<span class="mw-page-title-main">Industrial processes</span> Process of producing goods

Industrial processes are procedures involving chemical, physical, electrical, or mechanical steps to aid in the manufacturing of an item or items, usually carried out on a very large scale. Industrial processes are the key components of heavy industry.

<i>Tumbaga</i> Alloy of gold and copper used in pre-Columbian Mesoamerica

Tumbaga is the name for a non-specific alloy of gold and copper given by Spanish Conquistadors to metals composed of these elements found in widespread use in pre-Columbian Mesoamerica in North America and South America.

<span class="mw-page-title-main">Cupellation</span> Refining process in metallurgy

Cupellation is a refining process in metallurgy in which ores or alloyed metals are treated under very high temperatures and subjected to controlled operations to separate noble metals, like gold and silver, from base metals, like lead, copper, zinc, arsenic, antimony, or bismuth, present in the ore. The process is based on the principle that precious metals typically oxidise or react chemically at much higher temperatures than base metals. When they are heated at high temperatures, the precious metals remain apart, and the others react, forming slags or other compounds.

The Wohlwill process is an industrial-scale chemical procedure used to refine gold to the highest degree of purity (99.999%). The process was invented in 1874 by Emil Wohlwill. This electrochemical process involves using a cast gold ingot, often called a doré bar, of 95%+ gold to serve as an anode. Lower percentages of gold in the anode will interfere with the reaction, especially when the contaminating metal is silver or one of the platinum group elements. The cathodes for this reaction are small sheets of pure (24k) gold sheeting or stainless steel. Current is applied to the system, and electricity travels through the electrolyte of chloroauric acid. Gold and other metals are dissolved at the anode, and pure gold is plated onto the gold cathode. When the anode is dissolved, the cathode is removed and melted or otherwise processed in the manner required for sale or use. The resulting gold is 99.999% pure, and of higher purity than gold produced by the other common refining method, the Miller process, which produces gold of 99.5% purity.

In metallurgy, refining consists of purifying an impure metal. It is to be distinguished from other processes such as smelting and calcining in that those two involve a chemical change to the raw material, whereas in refining, the final material is usually identical chemically to the original one, only it is purer. The processes used are of many types, including pyrometallurgical and hydrometallurgical techniques.

Leaching is a process widely used in extractive metallurgy where ore is treated with chemicals to convert the valuable metals within the ore, into soluble salts while the impurity remains insoluble. These can then be washed out and processed to give the pure metal; the materials left over are commonly known as tailings. Compared to pyrometallurgy, leaching is easier to perform, requires less energy and is potentially less harmful as no gaseous pollution occurs. Drawbacks of leaching include its lower efficiency and the often significant quantities of waste effluent and tailings produced, which are usually either highly acidic or alkali as well as toxic.

<span class="mw-page-title-main">Mining and metallurgy in medieval Europe</span> Medieval European history

During the Middle Ages, between the 5th and 16th century AD, Western Europe saw a period of growth in the mining industry. The first important mines were those at Goslar in the Harz mountains, taken into commission in the 10th century. Another notable mining town is Falun in Sweden where copper has been mined since at least the 10th century and possibly even earlier.

<span class="mw-page-title-main">Roman metallurgy</span> Production and usage of metal in ancient Rome

Metals and metal working had been known to the people of modern Italy since the Bronze Age. By 53 BC, Rome had expanded to control an immense expanse of the Mediterranean. This included Italy and its islands, Spain, Macedonia, Africa, Asia Minor, Syria and Greece; by the end of the Emperor Trajan's reign, the Roman Empire had grown further to encompass parts of Britain, Egypt, all of modern Germany west of the Rhine, Dacia, Noricum, Judea, Armenia, Illyria, and Thrace. As the empire grew, so did its need for metals.

<span class="mw-page-title-main">Non-ferrous extractive metallurgy</span> Metallurgy process

Non-ferrous extractive metallurgy is one of the two branches of extractive metallurgy which pertains to the processes of reducing valuable, non-iron metals from ores or raw material. Metals like zinc, copper, lead, aluminium as well as rare and noble metals are of particular interest in this field, while the more common metal, iron, is considered a major impurity. Like ferrous extraction, non-ferrous extraction primarily focuses on the economic optimization of extraction processes in separating qualitatively and quantitatively marketable metals from its impurities (gangue).

References

This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.