Ilsemannite is an uncommon amorphous complex heterovalent molybdenum oxide, that was first published in 1871, and has been a valid species since pre-IMA. It is a grandfathered mineral, meaning the name ilsemannite is still believed to refer to a valid species. However, it is likely that specimens formed under different conditions, in different localities do not have the same composition, and may even be a mixture of compounds.[1] Furthermore, it is hard to analyze the specimens due to them being a mixture, hence why adequate analyses are lacking of said mineral. Ilsemannite is believed to be identical to synthetic molybdic oxide.[2]
Ilsemannite is soluble in water, which at first produces a greenish blue color, which later changes to a deep molybdenum-blue.[3] This is probably why Native Americans believed that ilsemannite colored the waters blue in the Idaho Springs area, however, this has been debunked.[1] Ilsemannite is now believed to consist of molybdenum (66.34%) and oxygen (33.19%), having a negligible amount of hydrogen (0.46%) in it. It has an earthy, dull, clay-like texture, and it is amorphous, meaning ilsemannite does not grow crystals. It does not show any radioactive properties.[4]
In an occurrence near Ouray, Utah, researchers found ilsemannite specimens disseminated through a rock. Analyses showed that about 10% of the sample was water-soluble, and that the water-soluble portion contains iron sulfate. Back then, in 1917, researches concluded that specimens from other localities all showed that iron sulfate was present in each of them, which is why the formula of said mineral was believed to be MoO3·SO3·5H2O. A specimen from Saxony mixed with iron sulfate showed only small amounts of iron, and gave a strong sulfate reaction. Another specimen from Carinthia had the same reaction, however this specimen had only a trace of ferric iron, with no ferrous iron in it. The specimen from Cripple Creek, Colorado showed the exact same reaction.[5]
During a study, it was found out that jordisite alters to ilsemannite more readily than it does to molybdenite, probably due to its amorphous state. This, among the scarcity of jordisite in mineral deposits, could explain why ilsemannite can be discovered in molybdenum districts. When first found, the mineral is usually black-blue or black in color, and it turns to blue-green and fades when exposed to sunlight. When put in a furnace alongside cinnabar, the calcined product's color changed to a purplish pink color. Chemical analyses of the material were not obtained due to the fact that the very thin coating surrounding ilsemannite couldn't be separated from the specimens. Underneath this coating there was a black, submetallic, sectile mineral first believed to be metacinnabar, but it was later proved to be a molybdenum compound. It was obvious that ilsemannite was an alteration product of this compound.[3] The specimen from Colorado was described to have this coating as well, only that this time it was green. It is believed that the specimen was actually either a yellow iron sulfate, or a yellow molybdite, which was colored green due to the ilsemannite solution.[5]
Occurrences and localities
Ilsemannite forms by the oxidation of molybdenum-bearing minerals, making it a secondary mineral. It is associated with gypsum, wulfenite, melanterite, halotrichite, molybdite, molybdenite, jordisite, and other oxidized uranium minerals;[2] however, it had been found in association with cinnabar as well in 1939. In the aforementioned encounter, ilsemannite was found as veinlets and as irregular lenses or pods in association of the cinnabar specimens. These specimens were described to often stain the nearby calcites a light blue color. It has a type locality of Carinthia, and although it is an uncommon mineral, it has been described in more than a dozen of other localities since then. Despite this fact, there is still an uncertainty lingering around the chemical composition and the origin of the mineral.[3]
Related Research Articles
Barium is a chemical element with the symbol Ba and atomic number 56. It is the fifth element in group 2 and is a soft, silvery alkaline earth metal. Because of its high chemical reactivity, barium is never found in nature as a free element.
Chromium is a chemical element with the symbol Cr and atomic number 24. It is the first element in group 6. It is a steely-grey, lustrous, hard, and brittle transition metal.
Molybdenum is a chemical element with the symbol Mo and atomic number 42 which is located in period 5 and group 6. The name is from Neo-Latin molybdaenum, which is based on Ancient Greek Μόλυβδος molybdos, meaning lead, since its ores were confused with lead ores. Molybdenum minerals have been known throughout history, but the element was discovered in 1778 by Carl Wilhelm Scheele. The metal was first isolated in 1781 by Peter Jacob Hjelm.
An oxide is a chemical compound that contains at least one oxygen atom and one other element in its chemical formula. "Oxide" itself is the dianion of oxygen, an O2– (molecular) ion. with oxygen in the oxidation state of −2. Most of the Earth's crust consists of oxides. Even materials considered pure elements often develop an oxide coating. For example, aluminium foil develops a thin skin of Al2O3 (called a passivation layer) that protects the foil from further corrosion.
Tourmaline is a crystalline silicate mineral group in which boron is compounded with elements such as aluminium, iron, magnesium, sodium, lithium, or potassium. Tourmaline is a gemstone and can be found in a wide variety of colors.
Group 6, numbered by IUPAC style, is a group of elements in the periodic table. Its members are chromium (Cr), molybdenum (Mo), tungsten (W), and seaborgium (Sg). These are all transition metals and chromium, molybdenum and tungsten are refractory metals.
Iron(II) sulfate (British English: iron(II) sulphate) or ferrous sulfate denotes a range of salts with the formula Fe SO4·xH2O. These compounds exist most commonly as the heptahydrate (x = 7) but several values for x are known. The hydrated form is used medically to treat iron deficiency, and also for industrial applications. Known since ancient times as copperas and as green vitriol (vitriol is an archaic name for sulfate), the blue-green heptahydrate (hydrate with 7 molecules of water) is the most common form of this material. All the iron(II) sulfates dissolve in water to give the same aquo complex [Fe(H2O)6]2+, which has octahedral molecular geometry and is paramagnetic. The name copperas dates from times when the copper(II) sulfate was known as blue copperas, and perhaps in analogy, iron(II) and zinc sulfate were known respectively as green and white copperas.
Iron(III) oxide or ferric oxide is the inorganic compound with the formula Fe2O3. It is one of the three main oxides of iron, the other two being iron(II) oxide (FeO), which is rare; and iron(II,III) oxide (Fe3O4), which also occurs naturally as the mineral magnetite. As the mineral known as hematite, Fe2O3 is the main source of iron for the steel industry. Fe2O3 is readily attacked by acids. Iron(III) oxide is often called rust, and to some extent this label is useful, because rust shares several properties and has a similar composition; however, in chemistry, rust is considered an ill-defined material, described as Hydrous ferric oxide.
Sulfide (British English also sulphide) is an inorganic anion of sulfur with the chemical formula S2− or a compound containing one or more S2− ions. Solutions of sulfide salts are corrosive. Sulfide also refers to chemical compounds large families of inorganic and organic compounds, e.g. lead sulfide and dimethyl sulfide. Hydrogen sulfide (H2S) and bisulfide (SH−) are the conjugate acids of sulfide.
Chalcanthite is a richly colored blue-green water-soluble sulfate mineral CuSO4 · 5H2O. It is commonly found in the late-stage oxidation zones of copper deposits. Due to its ready solubility, chalcanthite is more common in arid regions.
Wulfenite is a lead molybdate mineral with the formula PbMoO4. It can be most often found as thin tabular crystals with a bright orange-red to yellow-orange color, sometimes brown, although the color can be highly variable. In its yellow form it is sometimes called "yellow lead ore".
Barium sulfate (or sulphate) is the inorganic compound with the chemical formula BaSO4. It is a white crystalline solid that is odorless and insoluble in water. It occurs as the mineral barite, which is the main commercial source of barium and materials prepared from it. The white opaque appearance and its high density are exploited in its main applications.
Molybdenum trioxide describes a family of inorganic compounds with the formula MoO3(H2O)n where n = 0, 1, 2. These compounds are produced on the largest scale of any molybdenum compound. The anhydrous oxide is a precursor to molybdenum metal, an important alloying agent. It is also an important industrial catalyst. It is a yellow solid, although impure samples can appear blue or green.
A chalcogenide is a chemical compound consisting of at least one chalcogen anion and at least one more electropositive element. Although all group 16 elements of the periodic table are defined as chalcogens, the term chalcogenide is more commonly reserved for sulfides, selenides, tellurides, and polonides, rather than oxides. Many metal ores exist as chalcogenides. Photoconductive chalcogenide glasses are used in xerography. Some pigments and catalysts are also based on chalcogenides. The metal dichalcogenide MoS2 is a common solid lubricant.
Red beds are sedimentary rocks, typically consisting of sandstone, siltstone, and shale, that are predominantly red in color due to the presence of ferric oxides. Frequently, these red-colored sedimentary strata locally contain thin beds of conglomerate, marl, limestone, or some combination of these sedimentary rocks. The ferric oxides, which are responsible for the red color of red beds, typically occur as a coating on the grains of sediments comprising red beds. Classic examples of red beds are the Permian and Triassic strata of the western United States and the Devonian Old Red Sandstone facies of Europe.
A native metal is any metal that is found pure in its metallic form in nature. Metals that can be found as native deposits singly or in alloys include aluminium, antimony, arsenic, bismuth, cadmium, chromium, cobalt, indium, iron, manganese, molybdenum, nickel, niobium, rhenium, selenium, tantalum, tellurium, tin, titanium, tungsten, vanadium, and zinc, as well as the gold group and the platinum group. Among the alloys found in native state have been brass, bronze, pewter, German silver, osmiridium, electrum, white gold, silver-mercury amalgam, and gold-mercury amalgam.
High-temperature corrosion is a mechanism of corrosion that takes place when gas turbines, diesel engines, furnaces or other machinery come in contact with hot gas containing certain contaminants. Fuel sometimes contains vanadium compounds or sulfates which can form compounds during combustion having a low melting point. These liquid melted salts are strongly corrosive for stainless steel and other alloys normally inert against the corrosion and high temperatures. Other high-temperature corrosions include high-temperature oxidation, sulfidation and carbonization. High temperature oxidation and other corrosion types are commonly modelled using the Deal-Grove model to account for diffusion and reaction processes.
Glass coloring and color marking may be obtained in several ways.
by the addition of coloring ions,
by precipitation of nanometer-sized colloids, Ancient Roman enamelled glass, 1st century, Begram Hoard
by colored inclusions
by light scattering
by dichroic coatings, or
by colored coatings
Concrete degradation may have many different causes. Concrete is mostly damaged by the corrosion of reinforcement bars due to the carbonatation of hardened cement paste or chloride attack under wet conditions. Chemical damages are caused by the formation of expansive products produced by various chemical reactions, by aggressive chemical species present in groundwater and seawater, or by microorganisms. Other damaging processes can also involve calcium leaching by water infiltration and different physical phenomena initiating cracks formation and propagation. All these detrimental processes and damaging agents adversely affects the concrete mechanical strength and its durability.
Antimony sulfate, Sb2(SO4)3, is a hygroscopic salt formed by reacting antimony or its compounds with hot sulfuric acid. It is used in doping of semiconductors and in the production of explosives and fireworks.
This page is based on this Wikipedia article Text is available under the CC BY-SA 4.0 license; additional terms may apply. Images, videos and audio are available under their respective licenses.