Kroll process

Last updated

The Kroll process is a pyrometallurgical industrial process used to produce metallic titanium from titanium tetrachloride. As of 2001 William Justin Kroll's process replaced the Hunter process for almost all commercial production. [1]

Contents

Process

In the Kroll process, titanium tetrachloride is reduced by liquid magnesium to give titanium metal:

The reduction is conducted at 800–850 °C in a stainless steel retort. [2] [3] Complications result from partial reduction of the TiCl4, giving to the lower chlorides TiCl2 and TiCl3. The MgCl2 can be further refined back to magnesium.

Appurtenant processes

The resulting porous metallic titanium sponge is purified by leaching or vacuum distillation. The sponge is crushed, and pressed before it is melted in a consumable carbon electrode vacuum arc furnace, "backfilled with pure gettered argon of a pressure high enough to avoid a glow discharge". [4] The melted ingot is allowed to solidify under vacuum. It is often remelted to remove inclusions and ensure uniformity. These melting steps add to the cost of the product. Titanium is about six times as expensive as stainless steel: Potter noted in 2023 that "Titanium is just fundamentally difficult and expensive to deal with. Turning titanium ingots into bars and sheets is a challenge due to titanium’s reactivity: it readily absorbs impurities, requiring “frequent surface removal and trimming to eliminate surface defects” which are “costly and involve significant yield loss.”" The appurtenant processes that turn Kroll's sponge into useful metal have "changed little since the 1950s." [5]

History and subsequent developments

Many methods had been applied to the production of titanium metal, beginning with a report in 1887 by Nilsen and Pettersen using sodium, which was optimized into the commercial Hunter process. In this process (which ceased to be commercial in the 1990s) TiCl4 is reduced to the metal by sodium. [3]

In the 1920s Anton Eduard van Arkel working for Philips NV had described the thermal decomposition of titanium tetraiodide to give highly pure titanium.

Titanium tetrachloride was found to reduce with hydrogen at high temperatures to give hydrides that can be thermally processed to the pure metal.

With these three ideas as background, Kroll in Luxembourg developed both new reductants and new apparatus for the reduction of titanium tetrachloride. Its high reactivity toward trace amounts of water and other metal oxides presented challenges. Significant success came with the use of calcium as a reductant, but the resulting mixture still contained significant oxide impurities. [6] Major success using magnesium at 1000 °C using a molybdenum clad reactor, was reported by Kroll to the Electrochemical Society in Ottawa. [7] Kroll's titanium was highly ductile reflecting its high purity.

The Kroll process displaced the Hunter process and continues to be the dominant technology for the production of titanium metal, as well as driving the majority of the world's production of magnesium metal.[ citation needed ]

After moving to the United States, Kroll further developed the method for the production of zirconium at the Albany Research Center. [4]

See also

Related Research Articles

<span class="mw-page-title-main">Titanium</span> Chemical element with atomic number 22 (Ti)

Titanium is a chemical element; it has symbol Ti and atomic number 22. Found in nature only as an oxide, it can be reduced to produce a lustrous transition metal with a silver color, low density, and high strength, resistant to corrosion in sea water, aqua regia, and chlorine.

<span class="mw-page-title-main">Zirconium</span> Chemical element with atomic number 40 (Zr)

Zirconium is a chemical element; it has symbol Zr and atomic number 40. First identified in 1789, isolated in impure form in 1824, and manufactured at scale by 1925, pure zirconium is a lustrous transition metal with a greyish-white color that closely resembles hafnium and, to a lesser extent, titanium. It is solid at room temperature, ductile, malleable and corrosion-resistant. The name zirconium is derived from the name of the mineral zircon, the most important source of zirconium. The word is related to Persian zargun. Besides zircon, zirconium occurs in over 140 other minerals, including baddeleyite and eudialyte; most zirconium is produced as a byproduct of minerals mined for titanium and tin.

A Ziegler–Natta catalyst, named after Karl Ziegler and Giulio Natta, is a catalyst used in the synthesis of polymers of 1-alkenes (alpha-olefins). Two broad classes of Ziegler–Natta catalysts are employed, distinguished by their solubility:

<span class="mw-page-title-main">Ilmenite</span> Titanium-iron oxide mineral

Ilmenite is a titanium-iron oxide mineral with the idealized formula FeTiO
3. It is a weakly magnetic black or steel-gray solid. Ilmenite is the most important ore of titanium and the main source of titanium dioxide, which is used in paints, printing inks, fabrics, plastics, paper, sunscreen, food and cosmetics.

<span class="mw-page-title-main">Titanium tetrachloride</span> Inorganic chemical compound

Titanium tetrachloride is the inorganic compound with the formula TiCl4. It is an important intermediate in the production of titanium metal and the pigment titanium dioxide. TiCl4 is a volatile liquid. Upon contact with humid air, it forms thick clouds of titanium dioxide and hydrochloric acid, a reaction that was formerly exploited for use in smoke machines. It is sometimes referred to as "tickle" or "tickle 4", as a phonetic representation of the symbols of its molecular formula.

The Hunter process was the first industrial process to produce pure metallic titanium. It was invented in 1910 by Matthew A. Hunter, a chemist born in New Zealand who worked in the United States. The process involves reducing titanium tetrachloride (TiCl4) with sodium (Na) in a batch reactor with an inert atmosphere at a temperature of 1,000 °C. Diluted hydrochloric acid is then used to leach the salt from the product.

<span class="mw-page-title-main">Van Arkel–de Boer process</span> Process for the commercial production of pure titanium and zirconium

The van Arkel–de Boer process, also known as the iodide process or crystal-bar process, was the first industrial process for the commercial production of pure ductile titanium, zirconium and some other metals. It was developed by Anton Eduard van Arkel and Jan Hendrik de Boer in 1925 for Philips Nv. Now it is used in the production of small quantities of ultrapure titanium and zirconium. It primarily involves the formation of the metal iodides and their subsequent decomposition to yield pure metal, for example at one of the Allegheny Technologies' Albany plants.

<span class="mw-page-title-main">FFC Cambridge process</span> Metal and metalloid synthesis process by electrolysis

The FFC Cambridge process is an electrochemical method for producing Titanium (Ti) from titanium oxide by electrolysis in molten calcium salts.

<span class="mw-page-title-main">Hafnium tetrachloride</span> Chemical compound

Hafnium(IV) chloride is the inorganic compound with the formula HfCl4. This colourless solid is the precursor to most hafnium organometallic compounds. It has a variety of highly specialized applications, mainly in materials science and as a catalyst.

<span class="mw-page-title-main">Titanocene dichloride</span> Chemical compound

Titanocene dichloride is the organotitanium compound with the formula (η5-C5H5)2TiCl2, commonly abbreviated as Cp2TiCl2. This metallocene is a common reagent in organometallic and organic synthesis. It exists as a bright red solid that slowly hydrolyzes in air. It shows antitumour activity and was the first non-platinum complex to undergo clinical trials as a chemotherapy drug.

<span class="mw-page-title-main">Zirconium(IV) chloride</span> Chemical compound

Zirconium(IV) chloride, also known as zirconium tetrachloride, is an inorganic compound frequently used as a precursor to other compounds of zirconium. This white high-melting solid hydrolyzes rapidly in humid air.

Titanium(III) chloride is the inorganic compound with the formula TiCl3. At least four distinct species have this formula; additionally hydrated derivatives are known. TiCl3 is one of the most common halides of titanium and is an important catalyst for the manufacture of polyolefins.

Titanium powder metallurgy (P/M) offers the possibility of creating net shape or near net shape parts without the material loss and cost associated with having to machine intricate components from wrought billet. Powders can be produced by the blended elemental technique or by pre-alloying and then consolidated by metal injection moulding, hot isostatic pressing, direct powder rolling or laser engineered net shaping.

<span class="mw-page-title-main">Thorium(IV) chloride</span> Chemical compound

Thorium(IV) chloride describes a family of inorganic compounds with the formula ThCl4(H2O)n. Both the anhydrous and tetrahydrate (n = 4) forms are known. They are hygroscopic, water-soluble white salts.

Vacuum arc remelting (VAR) is a secondary melting process for production of metal ingots with elevated chemical and mechanical homogeneity for highly demanding applications. The VAR process has revolutionized the specialty traditional metallurgical techniques industry, and has made possible tightly-controlled materials used in biomedical, aviation and aerospace.

The chloride process is used to separate titanium from its ores. The goal of the process is to win high purity titanium dioxide from ores such as ilmenite (FeTiO3) and rutile (TiO2). The strategy exploits the volatility of TiCl4, which is readily purified and converted to the dioxide. Millions of tons of TiO2 are produced annually by this process, mainly for use as white pigments. The chloride process has largely displaced the older sulfate process, which relies on hot sulfuric acid to extract iron and other impurities from ores.

Tetrachloride may refer to:

<span class="mw-page-title-main">Titanium ethoxide</span> Chemical compound

Titanium ethoxide is a chemical compound with the formula Ti4(OCH2CH3)16. It is a commercially available colorless liquid that is soluble in organic solvents but hydrolyzes readily. Its structure is more complex than suggested by its empirical formula. Like other alkoxides of titanium(IV) and zirconium(IV), it finds used in organic synthesis and materials science.

The hydrogen assisted magnesiothermic reduction ("HAMR") process is a thermochemical process to obtain titanium metal from titanium oxides.

References

  1. ↑ Holleman, A. F.; Wiberg, E. "Inorganic Chemistry" Academic Press: San Diego, 2001. ISBN   0-12-352651-5.
  2. ↑ Habashi, F. (ed.) Handbook of Extractive Metallurgy, Wiley-VCH, Weinheim, 1997.
  3. 1 2 Heinz Sibum; Volker Günther; Oskar Roidl; Fathi Habashi; Hans Uwe Wolf (2005). "Titanium, Titanium Alloys, and Titanium Compounds". Ullmann's Encyclopedia of Industrial Chemistry . Weinheim: Wiley-VCH. doi:10.1002/14356007.a27_095. ISBN   978-3527306732.
  4. 1 2 Kroll, W.J. (1955). "How commercial titanium and zirconium were born". Journal of the Franklin Institute. 260 (3): 169–192. doi:10.1016/0016-0032(55)90727-4.
  5. ↑ Potter, Brian (7 July 2023). "The Story of Titanium".
  6. ↑ W. Kroll "Verformbares Titan und Zirkon" (Eng: Ductile Titanium and Zirconium) Zeitschrift für anorganische und allgemeine Chemie Volume 234, p. 42-50. doi : 10.1002/zaac.19372340105
  7. ↑ W. J. Kroll, "The Production of Ductile Titanium" Transactions of the Electrochemical Society volume 78 (1940) 35–47.

Further reading

This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.