Mu-metal

Last updated • 5 min readFrom Wikipedia, The Free Encyclopedia
Assortment of mu-metal shapes used in electronics, 1951 Mu-metal assortment 1951.jpg
Assortment of mu-metal shapes used in electronics, 1951
Five-layer mu-metal box. Each layer is about 5 mm thick. It reduces the effect of the Earth's magnetic field inside by a factor of 1500. Mumetal box by Zureks.jpg
Five-layer mu-metal box. Each layer is about 5 mm thick. It reduces the effect of the Earth's magnetic field inside by a factor of 1500.

Mu-metal is a nickeliron soft ferromagnetic alloy with very high permeability, which is used for shielding sensitive electronic equipment against static or low-frequency magnetic fields.

Contents

Properties

Mu-metal has several compositions. One such composition is approximately

77% nickel,
16% iron,
5% copper, and
2% chromium or molybdenum. [1] [2]

More recently, mu-metal is considered to be ASTM A753 Alloy 4 and is composed of approximately

80% nickel,
5% molybdenum,
small amounts of various other elements such as silicon, and
12~15% iron for the remainder. [3]

The name came from the Greek letter mu (μ) which represents permeability in physics and engineering formulas. A number of different proprietary formulations of the alloy are sold under trade names such as MuMETAL, Mumetall, and Mumetal2.

Mu-metal typically has relative permeability values of 80,000–100,000 compared to several thousand for ordinary steel. It is a "soft" ferromagnetic material; it has low magnetic anisotropy and magnetostriction, [1] giving it a low coercivity so that it saturates at low magnetic fields. This gives it low hysteresis losses when used in AC magnetic circuits. Other high-permeability nickel–iron alloys such as permalloy have similar magnetic properties; mu-metal's advantage is that it is more ductile, malleable and workable, allowing it to be easily formed into the thin sheets needed for magnetic shields. [1]

Mu-metal objects require heat treatment after they are in final form—annealing in a magnetic field in hydrogen atmosphere, which increases the magnetic permeability about 40 times. [4] The annealing alters the material's crystal structure, aligning the grains and removing some impurities, especially carbon, which obstruct the free motion of the magnetic domain boundaries. Bending or mechanical shock after annealing may disrupt the material's grain alignment, leading to a drop in the permeability of the affected areas, which can be restored by repeating the hydrogen annealing step.[ citation needed ]

Application

Mu-metal shields for cathode-ray tubes (CRTs) used in oscilloscopes, from a 1945 electronics magazine Mu metal CRT shields.jpg
Mu-metal shields for cathode-ray tubes (CRTs) used in oscilloscopes, from a 1945 electronics magazine

Mu-metal is a soft magnetic alloy with exceptionally high magnetic permeability. The high permeability of mu-metal provides a low reluctance path for magnetic flux, leading to its use in magnetic shields against static or slowly varying magnetic fields. Magnetic shielding made with high-permeability alloys like mu-metal works not by blocking magnetic fields but by providing a path for the magnetic field lines around the shielded area. Thus, the best shape for shields is a closed container surrounding the shielded space.

The effectiveness of mu-metal shielding decreases with the alloy's permeability, which drops off at both low field strengths and, due to saturation, at high field strengths. Thus, mu-metal shields are often made of several enclosures one inside the other, each of which successively reduces the field inside it. Because mu-metal saturates at relatively low fields, sometimes the outer layer in such multilayer shields is made of ordinary steel. Its higher saturation value allows it to handle stronger magnetic fields, reducing them to a lower level that can be shielded effectively by the inner mu-metal layers.[ citation needed ]

RF magnetic fields above about 100 kHz can be shielded by Faraday shields: ordinary conductive metal sheets or screens which are used to shield against electric fields. [5] Superconducting materials can also expel magnetic fields by the Meissner effect, but require cryogenic temperatures.

The alloy has a low coercivity, near zero magnetostriction, and significant anisotropic magnetoresistance. The low magnetostriction is critical for industrial applications, where variable stresses in thin films would otherwise cause a ruinously large variation in magnetic properties.

Examples

Mu-metal is used to shield equipment from magnetic fields. For example:

Similar materials

Other materials with similar magnetic properties include Co-Netic, supermalloy, supermumetal, nilomag, sanbold, molybdenum permalloy, Sendust, M-1040, Hipernom, HyMu-80 and Amumetal. Electrical steel is used similarly in some transformers as a cheaper, less permeable option.

Ceramic ferrites are used for similar purposes, and have even higher permeability at high frequencies, but are brittle and nearly non-conductive, so can only replace mu-metals where conductivity and pliability aren't required.

History

Mu-metal submarine cable construction Mu-metal cable.svg
Mu-metal submarine cable construction

Mu-metal was developed by British scientists Willoughby S. Smith and Henry J. Garnett [7] [8] [9] and patented in 1923 for inductive loading of submarine telegraph cables by The Telegraph Construction and Maintenance Co. Ltd. (now Telcon Metals Ltd.), a British firm that built the Atlantic undersea telegraph cables. [10] The conductive seawater surrounding an undersea cable added a significant capacitance to the cable, causing distortion of the signal, which limited the bandwidth and slowed signaling speed to 10–12 words per minute. The bandwidth could be increased by adding inductance to compensate. This was first done by wrapping the conductors with a helical wrapping of metal tape or wire of high magnetic permeability, which confined the magnetic field.

Telcon invented mu-metal to compete with permalloy, the first high-permeability alloy used for cable compensation, whose patent rights were held by competitor Western Electric. Mu-metal was developed by adding copper to permalloy to improve ductility. 80 kilometres (50 mi) of fine mu-metal wire were needed for each 1.6 km of cable, creating a great demand for the alloy. The first year of production Telcon was making 30 tons per week. In the 1930s this use for mu-metal declined, but by World War II many other uses were found in the electronics industry (particularly shielding for transformers and cathode-ray tubes), as well as the fuzes inside magnetic mines. Telcon Metals Ltd. abandoned the trademark "MUMETAL" in 1985. [11] The last listed owner of the mark "MUMETAL" is Magnetic Shield Corporation, Illinois. [12]

Related Research Articles

<span class="mw-page-title-main">Loading coil</span> Inductor in a transmission line

A loading coil or load coil is an inductor that is inserted into an electronic circuit to increase its inductance. The term originated in the 19th century for inductors used to prevent signal distortion in long-distance telegraph transmission cables. The term is also used for inductors in radio antennas, or between the antenna and its feedline, to make an electrically short antenna resonant at its operating frequency.

Magnetostriction is a property of magnetic materials that causes them to change their shape or dimensions during the process of magnetization. The variation of materials' magnetization due to the applied magnetic field changes the magnetostrictive strain until reaching its saturation value, λ. The effect was first identified in 1842 by James Joule when observing a sample of iron.

<span class="mw-page-title-main">Induction heating</span> Process of heating an electrically conducting object by electromagnetic induction

Induction heating is the process of heating electrically conductive materials, namely metals or semi-conductors, by electromagnetic induction, through heat transfer passing through an inductor that creates an electromagnetic field within the coil to heat up and possibly melt steel, copper, brass, graphite, gold, silver, aluminum, or carbide.

<span class="mw-page-title-main">Permeability (electromagnetism)</span> Ability of magnetization

In electromagnetism, permeability is the measure of magnetization produced in a material in response to an applied magnetic field. Permeability is typically represented by the (italicized) Greek letter μ. It is the ratio of the magnetic induction to the magnetizing field as a function of the field in a material. The term was coined by William Thomson, 1st Baron Kelvin in 1872, and used alongside permittivity by Oliver Heaviside in 1885. The reciprocal of permeability is magnetic reluctivity.

<span class="mw-page-title-main">Permalloy</span> Nickel–iron alloy with high magnetic permeability

Permalloy is a nickel–iron magnetic alloy, with about 80% nickel and 20% iron content. Invented in 1914 by physicist Gustav Elmen at Bell Telephone Laboratories, it is notable for its very high magnetic permeability, which makes it useful as a magnetic core material in electrical and electronic equipment, and also in magnetic shielding to block magnetic fields. Commercial permalloy alloys typically have relative permeability of around 100,000, compared to several thousand for ordinary steel.

<span class="mw-page-title-main">Magnetic core</span> Object used to guide and confine magnetic fields

A magnetic core is a piece of magnetic material with a high magnetic permeability used to confine and guide magnetic fields in electrical, electromechanical and magnetic devices such as electromagnets, transformers, electric motors, generators, inductors, loudspeakers, magnetic recording heads, and magnetic assemblies. It is made of ferromagnetic metal such as iron, or ferrimagnetic compounds such as ferrites. The high permeability, relative to the surrounding air, causes the magnetic field lines to be concentrated in the core material. The magnetic field is often created by a current-carrying coil of wire around the core.

<span class="mw-page-title-main">Electromagnetic shielding</span> Using conductive or magnetic materials to reduce electromagnetic field intensity

In electrical engineering, electromagnetic shielding is the practice of reducing or redirecting the electromagnetic field (EMF) in a space with barriers made of conductive or magnetic materials. It is typically applied to enclosures, for isolating electrical devices from their surroundings, and to cables to isolate wires from the environment through which the cable runs. Electromagnetic shielding that blocks radio frequency (RF) electromagnetic radiation is also known as RF shielding.

<span class="mw-page-title-main">Saturation (magnetic)</span> Feature of some magnetic materials

Seen in some magnetic materials, saturation is the state reached when an increase in applied external magnetic field H cannot increase the magnetization of the material further, so the total magnetic flux density B more or less levels off. Saturation is a characteristic of ferromagnetic and ferrimagnetic materials, such as iron, nickel, cobalt and their alloys. Different ferromagnetic materials have different saturation levels.

<span class="mw-page-title-main">Ferrite (magnet)</span> Ferrimagnetic ceramic material composed of iron(III) oxide and a divalent metallic element

A ferrite is one of a family of iron oxide-containing magnetic ceramic materials. They are ferrimagnetic, meaning they are attracted by magnetic fields and can be magnetized to become permanent magnets. Unlike many ferromagnetic materials, most ferrites are not electrically conductive, making them useful in applications like magnetic cores for transformers to suppress eddy currents.

Eddy-current testing is one of many electromagnetic testing methods used in nondestructive testing (NDT) making use of electromagnetic induction to detect and characterize surface and sub-surface flaws in conductive materials.

Marine grade stainless alloys typically contain molybdenum to resist the corrosive effects of NaCl or salt in seawater. Concentrations of salt in seawater can vary, and splash zones can cause concentrations to increase dramatically from the spray and evaporation.

Sendust is a magnetic metal powder that was invented by Hakaru Masumoto at Tohoku Imperial University in Sendai, Japan circa 1936 as an alternative to permalloy in inductor applications for telephone networks. Sendust composition is typically 85% iron, 9% silicon and 6% aluminium. The powder is sintered into cores to manufacture inductors. Sendust cores have high magnetic permeability, low loss, low coercivity good temperature stability and saturation flux density up to 1 T.

Supermalloy is an alloy composed of nickel (75%), iron (20%), and molybdenum (5%). It is a high permeability ferromagnetic alloy used in magnetic cores and magnetic shielding in electrical components, such as pulse transformers and ultra-sensitive magnetic amplifiers. It has a resistivity of 0.6 Ω·mm2/m, an extremely high relative magnetic permeability, and a low coercivity. Supermalloy is used in manufacturing components for radio engineering, telephony, and telemechanics instruments.

<span class="mw-page-title-main">Wolfson Centre for Magnetics</span> Cardiff University, UK research centre

Wolfson Centre for Magnetics (WCM) is a research and knowledge centre operating within School of Engineering at Cardiff University.

Lubomyr Taras Romankiw was a Ukrainian-Canadian-American computer scientist, researcher and inventor. Although a Canadian citizen, he spent his entire career at IBM's Thomas J. Watson Research Center in Yorktown Heights, New York. He was an IBM fellow, the highest Technical ranking at IBM.

In electronics, a ferrite core is a type of magnetic core made of ferrite on which the windings of electric transformers and other wound components such as inductors are formed. It is used for its properties of high magnetic permeability coupled with low electrical conductivity. Moreover, because of its comparatively low losses at high frequencies, ferrite is extensively used for the cores of RF transformers and inductors in applications such as switched-mode power supplies and ferrite loopstick antennas for AM radio receivers.

The word electricity refers generally to the movement of electrons, or other charge carriers, through a conductor in the presence of a potential difference or an electric field. The speed of this flow has multiple meanings. In everyday electrical and electronic devices, the signals travel as electromagnetic waves typically at 50%–99% of the speed of light in vacuum. The electrons themselves move much more slowly. See drift velocity and electron mobility.

<span class="mw-page-title-main">Materials for use in vacuum</span>

Materials for use in vacuum are materials that show very low rates of outgassing in vacuum and, where applicable, are tolerant to bake-out temperatures. The requirements grow increasingly stringent with the desired degree of vacuum to be achieved in the vacuum chamber. The materials can produce gas by several mechanisms. Molecules of gases and water can be adsorbed on the material surface. Materials may sublimate in vacuum. Or the gases can be released from porous materials or from cracks and crevices. Traces of lubricants, residues from machining, can be present on the surfaces. A specific risk is outgassing of solvents absorbed in plastics after cleaning.

A molypermalloy powder (MPP) core is a toroidal magnetic core comprised from the powder of multiple alloys. It is distributed with air gaps to help condense its magnetic field to minimize core losses. Its composition is made from approximately 79% nickel, 17% iron, and 4% molybdenum.

References

  1. 1 2 3 Jiles, David (1998). Introduction to Magnetism and Magnetic Materials. CRC Press. p. 354. ISBN   978-0-412-79860-3.
  2. Weast, Robert (1983). Handbook of Chemistry and Physics (64th ed.). CRC Press. p. E-108. ISBN   978-0-8493-0463-7.
  3. "MuMetal Home". mu-metal.com. Josh Wickler. Retrieved 2015-07-06.
  4. "Mu Metal specifications". Shielding Specifications. Nick Murby. 2009-03-25. Retrieved 2013-01-21.
  5. "Magnetic Fields and Shields". FAQ. Magnetic Shield Corp. Archived from the original on 2008-12-18. Retrieved 2008-12-14.
  6. Daniels, Ryan J.; McIntyre, Timothy; Kisner, Roger; Killough, Stephen; Lenarduzzi, Roberto (April 2015). "Design and implementation of a Hall Effect sensor array applied to recycling hard drive magnets". SoutheastCon 2015. pp. 1–6. doi:10.1109/SECON.2015.7132879. ISBN   978-1-4673-7300-5. S2CID   7196422.
  7. GB279549A,"New and improved magnetic alloys and their application in the manufacture of telegraphic and telephonic cables",issued 1927-10-27
  8. US Patent 1582353 Willoughby Statham Smith, Henry Joseph Garnett, Magnetic Alloy, filed January 10, 1924, granted April 27, 1926
  9. US Patent 1552769 Willoughby Statham Smith, Henry Joseph Garnett, Magnetic Alloy, filed January 10, 1924, granted September 8, 1925
  10. Green, Allen (2004). "150 Years Of Industry & Enterprise At Enderby's Wharf". History of the Atlantic Cable and Undersea Communications. FTL Design. Retrieved 2008-12-14.
  11. "Trademark Status & Document Retrieval". tsdr.uspto.gov. Retrieved 2017-07-28.
  12. "Trademark Status & Document Retrieval". tsdr.uspto.gov. Retrieved 2017-07-28.