Shore durometer

Last updated
Two inline skate wheels with different durometer - 85A and 83A Bont High Roller G4 110mm 85A and 83A.jpg
Two inline skate wheels with different durometer – 85A and 83A
Digital Shore hardness tester Hardness tester shore (Shore durometer).jpg
Digital Shore hardness tester

The Shore durometer is a device for measuring the hardness of a material, typically of polymers. [1]

Contents

Higher numbers on the scale indicate a greater resistance to indentation and thus harder materials. Lower numbers indicate less resistance and softer materials.

The term is also used to describe a material's rating on the scale, as in an object having a "'Shore durometer' of 90."

The scale was defined by Albert Ferdinand Shore, who developed a suitable device to measure hardness in the 1920s. It was neither the first hardness tester nor the first to be called a durometer (ISV duro- and -meter ; attested since the 19th century), but today that name usually refers to Shore hardness; other devices use other measures, which return corresponding results, such as for Rockwell hardness.

Durometer scales

There are several scales of durometer, used for materials with different properties. The two most common scales, using slightly different measurement systems, are the ASTM D2240 type A and type D scales.

The A scale is for softer ones, while the D scale is for harder ones. The image of Bareiss digital durometer is shown in the photo.

However, the ASTM D2240-00 testing standard calls for a total of 12 scales, depending on the intended use: types A, B, C, D, DO, E, M, O, OO, OOO, OOO-S, and R. Each scale results in a value between 0 and 100, with higher values indicating a harder material. [2]

Method of measurement

Diagram of a durometer indenter or presser foot used for Shores A and D Durometer.svg
Diagram of a durometer indenter or presser foot used for Shores A and D

Durometer, like many other hardness tests, measures the depth of an indentation in the material created by a given force on a standardized presser foot. This depth is dependent on the hardness of the material, its viscoelastic properties, the shape of the presser foot, and the duration of the test. ASTM D2240 durometers allows for a measurement of the initial hardness, or the indentation hardness after a given period of time. The basic test requires applying the force in a consistent manner, without shock, and measuring the hardness (depth of the indentation). If a timed hardness is desired, force is applied for the required time and then read. The material under test should be a minimum of 6 mm (0.25 inches) thick. [3] Theoretical background of the test is considered in Stoßprobleme in Physik, Technik und Medizin by Grundlagen und Anwendungen [4]

Test setup for type A & D [3]
DurometerIndenting foot Kilogram-force (kgf) Newton (N)
Type AHardened steel rod 1.1 mm – 1.4 mm diameter, with a truncated 35° cone, 0.79 mm diameter0.8228.064
Type DHardened steel rod 1.1 mm – 1.4 mm diameter, with a 30° conical point, 0.1 mm radius tip4.55044.64

The ASTM D2240 standard recognizes twelve different durometer scales using combinations of specific spring forces and indentor configurations. These scales are properly referred to as durometer types; i.e., a durometer type is specifically designed to determine a specific scale, and the scale does not exist separately from the durometer. The table below provides details for each of these types, with the exception of Type R. [5]

Durometer typeConfiguration Diameter ExtensionSpring force [6]
A35° truncated cone (frustum)1.40 mm (0.055 in)2.54 mm (0.100 in)8.05 N (821 gf)
B30° cone1.40 mm (0.055 in)2.54 mm (0.100 in)8.05 N (821 gf)
C35° truncated cone (frustum)1.40 mm (0.055 in)2.54 mm (0.100 in)44.45 N (4,533 gf)
D30° cone1.40 mm (0.055 in)2.54 mm (0.100 in)44.45 N (4,533 gf)
E2.5 mm (0.098 in) spherical radius4.50 mm (0.177 in)2.54 mm (0.100 in)8.05 N (821 gf)
M30° cone0.79 mm (0.031 in)1.25 mm (0.049 in)0.765 N (78.0 gf)
01.20 mm (0.047 in) spherical radius2.40 mm (0.094 in)2.54 mm (0.100 in)8.05 N (821 gf)
001.20 mm (0.047 in) spherical radius2.40 mm (0.094 in)2.54 mm (0.100 in)1.111 N (113.3 gf)
D01.20 mm (0.047 in) spherical radius2.40 mm (0.094 in)2.54 mm (0.100 in)44.45 N (4,533 gf)
0006.35 mm (0.250 in) spherical radius10.7–11.6 mm (0.42–0.46 in)2.54 mm (0.100 in)1.111 N (113.3 gf)
000-S10.7 mm (0.42 in) radius disk11.9 mm (0.47 in)5.0 mm (0.20 in)1.932 N (197.0 gf)

Note: Type R is a designation, rather than a true "type". The R designation specifies a presser foot diameter (hence the R, for radius; obviously D could not be used) of 18 ± 0.5 mm (0.71 ± 0.02 in) in diameter, while the spring forces and indenter configurations remain unchanged. The R designation is applicable to any D2240 Type, with the exception of Type M; the R designation is expressed as Type xR, where x is the D2240 type, e.g., aR, dR, etc.; the R designation also mandates the employment of an operating stand. [5]

Some conditions and procedures that have to be met, according to DIN ISO 7619-1 standard are:

The final value of the hardness depends on the depth of the indenter after it has been applied for 15 seconds on the material. If the indenter penetrates 2.54 mm (0.100 inch) or more into the material, the durometer is 0 for that scale. If it does not penetrate at all, then the durometer is 100 for that scale. It is for this reason that multiple scales exist. But if the hardness is <10 °Sh or >90 °Sh the results are not to be trusted. The measurement must be redone with adjacent scale type.

Durometer is a dimensionless quantity, and there is no simple relationship between a material's durometer in one scale, and its durometer in any other scale, or by any other hardness test. [1]

Shore Durometers of Common Materials
MaterialDurometerScale
Bicycle gel seat15–3000
Chewing gum 2000
Sorbothane 30–7000
Rubber band 25A
Door seal55A
Automotive tire tread 70A
Soft wheels of roller skates and skateboard 78A
Hydraulic O-ring 70–90A
Pneumatic O-ring65–75A
Hard wheels of roller skates and skateboard98A
Ebonite rubber 100A
Solid truck tires50D
Hard hat (typically HDPE)75D
Cast urethane plastic80D

ASTM D2240 hardness and elastic modulus


Using linear elastic indentation hardness, a relation between the ASTM D2240 hardness and the Young's modulus for elastomers has been derived by Gent [7] .Gent's relation has the form

where is the Young's modulus in MPa and is the ASTM D2240 type A hardness.

This relation gives a value of at but departs from experimental data for . Mix and Giacomin derive comparable equations for all 12 scales that are standardized by ASTM D2240. [8]

Another relation that fits the experimental data slightly better is [9]

where is the error function, and is in units of Pa.

A first-order estimate of the relation between ASTM D2240 type D hardness (for a conical indenter with a 15° half-cone angle) and the elastic modulus of the material being tested is [10]

where is the ASTM D2240 type D hardness, and is in MPa.

Another Neo-Hookean linear relation between the ASTM D2240 hardness value and material elastic modulus has the form [10]

where is the ASTM D2240 type A hardness, is the ASTM D2240 type D hardness, and is the Young's modulus in MPa.

Patents

See also

Related Research Articles

<span class="mw-page-title-main">Structural geology</span> Science of the description and interpretation of deformation in the Earths crust

Structural geology is the study of the three-dimensional distribution of rock units with respect to their deformational histories. The primary goal of structural geology is to use measurements of present-day rock geometries to uncover information about the history of deformation (strain) in the rocks, and ultimately, to understand the stress field that resulted in the observed strain and geometries. This understanding of the dynamics of the stress field can be linked to important events in the geologic past; a common goal is to understand the structural evolution of a particular area with respect to regionally widespread patterns of rock deformation due to plate tectonics.

<span class="mw-page-title-main">Rockwell scale</span> Hardness scale

The Rockwell scale is a hardness scale based on indentation hardness of a material. The Rockwell test measures the depth of penetration of an indenter under a large load compared to the penetration made by a preload. There are different scales, denoted by a single letter, that use different loads or indenters. The result is a dimensionless number noted as HRA, HRB, HRC, etc., where the last letter is the respective Rockwell scale. Larger numbers correspond to harder materials.

<span class="mw-page-title-main">Brinell scale</span> Brinell scale of hardness

The Brinell scale characterizes the indentation hardness of materials through the scale of penetration of an indenter, loaded on a material test-piece. It is one of several definitions of hardness in materials science.

<span class="mw-page-title-main">Stiffness</span> Resistance to deformation in response to force

Stiffness is the extent to which an object resists deformation in response to an applied force.

<span class="mw-page-title-main">Toughness</span> Material ability to absorb energy and plastically deform without fracturing

In materials science and metallurgy, toughness is the ability of a material to absorb energy and plastically deform without fracturing. Toughness is the strength with which the material opposes rupture. One definition of material toughness is the amount of energy per unit volume that a material can absorb before rupturing. This measure of toughness is different from that used for fracture toughness, which describes the capacity of materials to resist fracture. Toughness requires a balance of strength and ductility.

<span class="mw-page-title-main">Vickers hardness test</span> Hardness test

The Vickers hardness test was developed in 1921 by Robert L. Smith and George E. Sandland at Vickers Ltd as an alternative to the Brinell method to measure the hardness of materials. The Vickers test is often easier to use than other hardness tests since the required calculations are independent of the size of the indenter, and the indenter can be used for all materials irrespective of hardness. The basic principle, as with all common measures of hardness, is to observe a material's ability to resist plastic deformation from a standard source. The Vickers test can be used for all metals and has one of the widest scales among hardness tests. The unit of hardness given by the test is known as the Vickers Pyramid Number (HV) or Diamond Pyramid Hardness (DPH). The hardness number can be converted into units of pascals, but should not be confused with pressure, which uses the same units. The hardness number is determined by the load over the surface area of the indentation and not the area normal to the force, and is therefore not pressure.

Indentation hardness tests are used in mechanical engineering to determine the hardness of a material to deformation. Several such tests exist, wherein the examined material is indented until an impression is formed; these tests can be performed on a macroscopic or microscopic scale.

<span class="mw-page-title-main">Knoop hardness test</span>

The Knoop hardness test is a microhardness test – a test for mechanical hardness used particularly for very brittle materials or thin sheets, where only a small indentation may be made for testing purposes. A pyramidal diamond point is pressed into the polished surface of the test material with a known load, for a specified dwell time, and the resulting indentation is measured using a microscope. The geometry of this indenter is an extended pyramid with the length to width ratio being 7:1 and respective face angles are 172 degrees for the long edge and 130 degrees for the short edge. The depth of the indentation can be approximated as 1/30 of the long dimension. The Knoop hardness HK or KHN is then given by the formula:

Nanotribology is the branch of tribology that studies friction, wear, adhesion and lubrication phenomena at the nanoscale, where atomic interactions and quantum effects are not negligible. The aim of this discipline is characterizing and modifying surfaces for both scientific and technological purposes.

<span class="mw-page-title-main">Yield (engineering)</span> Phenomenon of deformation due to structural stress

In materials science and engineering, the yield point is the point on a stress-strain curve that indicates the limit of elastic behavior and the beginning of plastic behavior. Below the yield point, a material will deform elastically and will return to its original shape when the applied stress is removed. Once the yield point is passed, some fraction of the deformation will be permanent and non-reversible and is known as plastic deformation.

In materials science, hardness is a measure of the resistance to localized plastic deformation, such as an indentation or a scratch (linear), induced mechanically either by pressing or abrasion. In general, different materials differ in their hardness; for example hard metals such as titanium and beryllium are harder than soft metals such as sodium and metallic tin, or wood and common plastics. Macroscopic hardness is generally characterized by strong intermolecular bonds, but the behavior of solid materials under force is complex; therefore, hardness can be measured in different ways, such as scratch hardness, indentation hardness, and rebound hardness. Hardness is dependent on ductility, elastic stiffness, plasticity, strain, strength, toughness, viscoelasticity, and viscosity. Common examples of hard matter are ceramics, concrete, certain metals, and superhard materials, which can be contrasted with soft matter.

Nanoindentation, also called instrumented indentation testing, is a variety of indentation hardness tests applied to small volumes. Indentation is perhaps the most commonly applied means of testing the mechanical properties of materials. The nanoindentation technique was developed in the mid-1970s to measure the hardness of small volumes of material.

<span class="mw-page-title-main">Ceramography</span> Preparation and study of ceramics with optical instruments

Ceramography is the art and science of preparation, examination and evaluation of ceramic microstructures. Ceramography can be thought of as the metallography of ceramics. The microstructure is the structure level of approximately 0.1 to 100 µm, between the minimum wavelength of visible light and the resolution limit of the naked eye. The microstructure includes most grains, secondary phases, grain boundaries, pores, micro-cracks and hardness microindentations. Most bulk mechanical, optical, thermal, electrical and magnetic properties are significantly affected by the microstructure. The fabrication method and process conditions are generally indicated by the microstructure. The root cause of many ceramic failures is evident in the microstructure. Ceramography is part of the broader field of materialography, which includes all the microscopic techniques of material analysis, such as metallography, petrography and plastography. Ceramography is usually reserved for high-performance ceramics for industrial applications, such as 85–99.9% alumina (Al2O3) in Fig. 1, zirconia (ZrO2), silicon carbide (SiC), silicon nitride (Si3N4), and ceramic-matrix composites. It is seldom used on whiteware ceramics such as sanitaryware, wall tiles and dishware.

The Barcol hardness test characterizes the indentation hardness of materials through the depth of penetration of an indentor, loaded on a material sample and compared to the penetration in a reference material. The method is most often used for composite materials such as reinforced thermosetting resins or to determine how much a resin or plastic has cured. The test complements the measurement of glass transition temperature, as an indirect measure of the degree of cure of a composite. It is inexpensive and quick, and provides information on the cure throughout a part.

<span class="mw-page-title-main">Meyer hardness test</span>

The Meyer hardness test is a hardness test based upon projected area of an impression. The hardness, , is defined as the maximum load, divided by the projected area of the indent, .

Meyer's law is an empirical relation between the size of a hardness test indentation and the load required to leave the indentation. The formula was devised by Eugene Meyer of the Materials Testing Laboratory at the Imperial School of Technology, Charlottenburg, Germany, circa 1908.

<span class="mw-page-title-main">Nanoindenter</span>

A nanoindenter is the main component for indentation hardness tests used in nanoindentation. Since the mid-1970s nanoindentation has become the primary method for measuring and testing very small volumes of mechanical properties. Nanoindentation, also called depth sensing indentation or instrumented indentation, gained popularity with the development of machines that could record small load and displacement with high accuracy and precision. The load displacement data can be used to determine modulus of elasticity, hardness, yield strength, fracture toughness, scratch hardness and wear properties.

The Leeb Rebound Hardness Test (LRHT) invented by Swiss company Proceq SA is one of the four most used methods for testing metal hardness. This portable method is mainly used for testing sufficiently large workpieces.

<span class="mw-page-title-main">Palmqvist method</span>

The Palmqvist method, or the Palmqvist toughness test, is a common method to determine the fracture toughness for cemented carbides. In this case, the material's fracture toughness is given by the critical stress intensity factor KIc.

<span class="mw-page-title-main">Indentation size effect</span> Property of materials at small scales

The indentation size effect (ISE) is the observation that hardness tends to increase as the indent size decreases at small scales. When an indent is created during material testing, the hardness of the material is not constant. At the small scale, materials will actually be harder than at the macro-scale. For the conventional indentation size effect, the smaller the indentation, the larger the difference in hardness. The effect has been seen through nanoindentation and microindentation measurements at varying depths. Dislocations increase material hardness by increasing flow stress through dislocation blocking mechanisms. Materials contain statistically stored dislocations (SSD) which are created by homogeneous strain and are dependent upon the material and processing conditions. Geometrically necessary dislocations (GND) on the other hand are formed, in addition to the dislocations statistically present, to maintain continuity within the material.

References

  1. 1 2 "Shore (Durometer) Hardness Testing of Plastics" . Retrieved 2006-07-22.
  2. "Material Hardness". CALCE and the University of Maryland. 2001. Archived from the original on 2007-07-07. Retrieved 2006-07-22.
  3. 1 2 "Rubber Hardness". National Physical Laboratory, UK. 2006. Retrieved 2006-07-22.
  4. Willert, Emanuel (2020). Stoßprobleme in Physik, Technik und Medizin: Grundlagen und Anwendungen (in German). Springer Vieweg. doi:10.1007/978-3-662-60296-6. ISBN   978-3-662-60295-9. S2CID   212954456.
  5. 1 2 "DuroMatters! Basic Durometer Testing Information" (PDF). CCSi, Inc. Archived from the original (PDF) on 24 March 2012. Retrieved 29 May 2011.
  6. "Standard Test Method for Rubber Property—Durometer Hardness1". ASTM International (D2240 − 15´1): 5. November 2017. doi:10.1520/D2240-15E01.
  7. A. N. Gent (1958), On the relation between indentation hardness and Young's modulus, Institution of Rubber Industry -- Transactions, 34, pp. 46–57. doi : 10.5254/1.3542351
  8. A. W. Mix and A. J. Giacomin (2011), Standardized Polymer Durometry, Journal of Testing and Evaluation, 39(4), pp. 1–10. doi : 10.1520/JTE103205
  9. British Standard 903 (1950, 1957), Methods of testing vulcanised rubber Part 19 (1950) and Part A7 (1957).
  10. 1 2 Qi, H. J., Joyce, K., Boyce, M. C. (2003), Durometer hardness and the stress-strain behavior of elastomeric materials, Rubber Chemistry and Technology, 76(2), pp. 419–435. doi : 10.5254/1.3547752