Overglaze decoration

Last updated
Mina'i ware bowl with couple in a garden, around 1200. These Persian wares are very slightly earlier than the first Chinese use of overglaze enamels. Diameter 18.8 cm. Bowl, Mina'i ("enameled") ware MET DP372046 (cropped).jpg
Mina'i ware bowl with couple in a garden, around 1200. These Persian wares are very slightly earlier than the first Chinese use of overglaze enamels. Diameter 18.8 cm.
Nabeshima ware plate with floral design, Arita, Japan, late 17th century, Edo period. Floral Plate Nabeshima.JPG
Nabeshima ware plate with floral design, Arita, Japan, late 17th century, Edo period.

Overglaze decoration, overglaze enamelling, or on-glaze decoration, is a method of decorating pottery, most often porcelain, where the coloured decoration is applied on top of the already fired and glazed surface, and then fixed in a second firing at a relatively low temperature, often in a muffle kiln. It is often described as producing "enamelled" decoration. The colours fuse on to the glaze, so the decoration becomes durable. This decorative firing is usually done at a lower temperature which allows for a more varied and vivid palette of colours, using pigments which will not colour correctly at the high temperature necessary to fire the porcelain body. Historically, a relatively narrow range of colours could be achieved with underglaze decoration, where the coloured pattern is applied before glazing, notably the cobalt blue of blue and white porcelain.

Contents

Many historical styles, for example mina'i ware, Imari ware, Chinese doucai, and wucai, combine the two types of decoration. [1] In such cases the first firing for the body, underglaze decoration and glaze is followed by the second firing after the overglaze enamels have been applied.

The technique essentially uses powdered glass mixed with coloured pigments, and is the application of vitreous enamel to pottery; enamelled glass is very similar but on glass. Both these latter two are essentially painting techniques, and have been since they began. In contrast, on metal painting in enamel arrived very late, long after techniques such as cloisonné, where thin wires are applied to form raised barriers, which contain areas of (subsequently applied) enamel, and champlevé, where the metal surface is sunk to form areas where the enamel is poured.

In Chinese porcelain, enamels were and are sometimes applied to unglazed pieces; this is called "enamel on the biscuit" and similar terms.

History

Chelsea porcelain factory, The Music Lesson, gold anchor, c. 1765, with bocage background. 15 3/8 x 12 1/4 x 8 3/4 inches, 22 lb. (39.1 x 31.1 x 22.2 cm, 10 kg). different version, different angle. The Music Lesson MET DP-14272-001 (cropped).jpg
Chelsea porcelain factory, The Music Lesson, gold anchor, c. 1765, with bocage background. 15 3/8 × 12 1/4 × 8 3/4 inches, 22 lb. (39.1 × 31.1 × 22.2 cm, 10 kg). different version, different angle.

Enamel was used in jewellery, applied to metal, from very early on - there are examples in the Tomb of Tutankhamun of c. 1325 BC. Enamel was also used to decorate glass by the time of the Roman Empire. Applied to pottery, it is first seen in Persian mina'i ware from the late 12th century, using a group of seven main colours. Presumably the potters learnt the technique from glassmakers. [2]

Slightly later it appeared in Chinese ceramics in Cizhou stoneware from as early as the 13th century, with use on porcelain following within a century, though it did not become predominant until later, and the full possibilities were not realized until the 17th and 18th centuries in the famille jaune, noire, rose, verte group of palettes. [3] Some techniques use thin metal leaf, including mina'i ware as well as the more usual pigments, which are typically applied in a liquid or paste form, painted by brush, or using stencils or transfer printing. The Japanese kakiemon style, and other Japanese styles, used the technique from at least the second half of the 17th century. The technique was also developing in Europe, firstly in what the French called petit feu faience, and in the 18th century in porcelain, and there appears to have been some influence in both directions between Asia and Europe. From about 1770 to the mid 20th century it was the dominant decorative technique in expensive pottery, mostly porcelain, made in Europe, East Asia, [4] and (to a lesser extent) North America.

In 18th-century England, where the technique was developed, the earliest forms of transfer printing on pottery, for example by Sadler & Green in Liverpool, were overglaze, although by the end of the century it was normal to print as underglaze.

Today overglaze decoration is much less commonly used, other than in traditionalist wares, as the range of colours available in underglaze has greatly expanded. Overglazes called "lusters" are still used for achieving special effects, such as iridescence of mother-of-pearl overglazes or metallic look of overglazes made with metal (eg. gold) particles. [5] [6]

Muffle kilns

The kiln used for the second firing is usually called a muffle kiln in Europe; like other types of muffle furnaces the design isolates the objects from the flames producing the heat (with electricity this is not so important). For historical overglaze enamels the kiln was generally far smaller than that for the main firing, and produced firing temperatures in the approximate range of 750 to 950 °C, depending on the colours used. Typically, wares were fired for between five and twelve hours and then cooled over twelve hours. [7]

Notes

  1. Vainker, 188–189, 192–193, 195
  2. Needham, 618, "Gulbenkian", Only the Best: Masterpieces of the Calouste Gulbenkian Museum, Lisbon, eds. Katharine Baetjer, James David Draper, 1999, Metropolitan Museum of Art, ISBN   0870999265, 9780870999260, google books, and Watson, 326
  3. Vainker, 117, 119, 181–182, 188-189
  4. Vainker, 202-207
  5. Norsker, Henrik (2013-11-21). Glazes — for the Self-Reliant Potter: A Publication of Deutsches Zentrum für Entwicklungstechnologien — GATE. A division of the Deutsche Gesellschaft für Technische Zusammenarbeit (GTZ) GmbH. Springer Science & Business Media. p. 96. ISBN   978-3-663-06865-5.
  6. Reinhardt, Emily (2023-09-05). The Beginner's Guide to Decorating Pottery: An Introduction to Glazes, Patterns, Inlay, Luster, and Dimensional Designs. Quarry Books. p. 42. ISBN   978-0-7603-8139-7.
  7. Hughes, 34-35

Related Research Articles

<span class="mw-page-title-main">Slipware</span> Pottery with a coating of slip

Slipware is pottery identified by its primary decorating process where slip is placed onto the leather-hard (semi-hardened) clay body surface before firing by dipping, painting or splashing. Slip is an aqueous suspension of a clay body, which is a mixture of clays and other minerals such as quartz, feldspar and mica. The slip placed onto a wet or leather-hard clay body surface by a variety of techniques including dipping, painting, piping or splashing. Slipware is the pottery on which slip has been applied either for glazing or decoration. Slip is liquified clay or clay slurry, with no fixed ratio of water and clay, which is used either for joining pottery pieces together by slip casting with mould, glazing or decorating the pottery by painting or dipping the pottery with slip.

<span class="mw-page-title-main">Creamware</span> Cream-coloured, refined earthenware with a lead glaze over a pale body

Creamware is a cream-coloured refined earthenware with a lead glaze over a pale body, known in France as faïence fine, in the Netherlands as Engels porselein, and in Italy as terraglia inglese. It was created about 1750 by the potters of Staffordshire, England, who refined the materials and techniques of salt-glazed earthenware towards a finer, thinner, whiter body with a brilliant glassy lead glaze, which proved so ideal for domestic ware that it supplanted white salt-glaze wares by about 1780. It was popular until the 1840s.

<span class="mw-page-title-main">Lustreware</span> Pottery with a reflective or iridescent surface

Lustreware or lusterware is a type of pottery or porcelain with a metallic glaze that gives the effect of iridescence. It is produced by metallic oxides in an overglaze finish, which is given a second firing at a lower temperature in a "muffle kiln", or a reduction kiln, excluding oxygen.

<span class="mw-page-title-main">Blue and white pottery</span> Vases

"Blue and white pottery" covers a wide range of white pottery and porcelain decorated under the glaze with a blue pigment, generally cobalt oxide. The decoration was commonly applied by hand, originally by brush painting, but nowadays by stencilling or by transfer-printing, though other methods of application have also been used. The cobalt pigment is one of the very few that can withstand the highest firing temperatures that are required, in particular for porcelain, which partly accounts for its long-lasting popularity. Historically, many other colours required overglaze decoration and then a second firing at a lower temperature to fix that.

<i>Famille jaune, noire, rose, verte</i>

Famille jaune, noire, rose, verte are terms used in the West to classify Chinese porcelain of the Qing dynasty by the dominant colour of its enamel palette. These wares were initially grouped under the French names of famille verte, and famille rose by Albert Jacquemart in 1862. The other terms famille jaune (yellow) and famille noire (black) may have been introduced later by dealers or collectors and they are generally considered subcategories of famille verte. Famille verte porcelain was produced mainly during the Kangxi era, while famille rose porcelain was popular in the 18th and 19th century. Much of the Chinese production was Jingdezhen porcelain, and a large proportion were made for export to the West, but some of the finest were made for the Imperial court.

<span class="mw-page-title-main">Famille rose</span>

Famille rose is a type of Chinese porcelain introduced in the 18th century and defined by pink overglaze enamel. It is a Western classification for Qing dynasty porcelain known in Chinese by various terms: fencai, ruancai, yangcai, and falangcai. The colour palette is thought to have been brought to China during the reign of Kangxi (1654–1722) by Western Jesuits who worked at the palace, but perfected only in the Yongzheng era when the finest pieces were made, and famille rose ware reached the peak of its technical excellence during the Qianlong period.

<span class="mw-page-title-main">Swatow ware</span>

Swatow ware or Zhangzhou ware is a loose grouping of mainly late Ming dynasty Chinese export porcelain wares initially intended for the Southeast Asian market. The traditional name in the West arose because Swatow, or present-day Shantou, was the South Chinese port in Guangdong province from which the wares were thought to have been shipped. The many kilns were probably located all over the coastal region, but mostly near Zhangzhou, Pinghe County, Fujian, where several were excavated in the mid-1990s, which has clarified matters considerably.

<span class="mw-page-title-main">Transfer printing</span>

Transfer printing is a method of decorating pottery or other materials using an engraved copper or steel plate from which a monochrome print on paper is taken which is then transferred by pressing onto the ceramic piece. Pottery decorated using this technique is known as transferware or transfer ware.

<span class="mw-page-title-main">Underglaze</span>

Underglaze is a method of decorating pottery in which painted decoration is applied to the surface before it is covered with a transparent ceramic glaze and fired in a kiln. Because the glaze subsequently covers it, such decoration is completely durable, and it also allows the production of pottery with a surface that has a uniform sheen. Underglaze decoration uses pigments derived from oxides which fuse with the glaze when the piece is fired in a kiln. It is also a cheaper method, as only a single firing is needed, whereas overglaze decoration requires a second firing at a lower temperature.

<span class="mw-page-title-main">Ding ware</span>

Ding ware, Ting ware or Dingyao are Chinese ceramics, mostly porcelain, that were produced in the prefecture of Dingzhou in Hebei in northern China. The main kilns were at Jiancicun or Jianci in Quyang County. They were produced between the Tang and Yuan dynasties of imperial China, though their finest period was in the 11th century, under the Northern Song. The kilns "were in almost constant operation from the early eighth until the mid-fourteenth century."

<span class="mw-page-title-main">Chinese ceramics</span> Pottery and porcelain from China

Chinese ceramics are one of the most significant forms of Chinese art and ceramics globally. They range from construction materials such as bricks and tiles, to hand-built pottery vessels fired in bonfires or kilns, to the sophisticated Chinese porcelain wares made for the imperial court and for export.

<span class="mw-page-title-main">Ceramic glaze</span> Fused coating on ceramic objects

Ceramic glaze, or simply glaze, is a glassy coating on ceramics. It is used for decoration, to ensure the item is impermeable to liquids and to minimise the adherence of pollutants.

<span class="mw-page-title-main">In-glaze decoration</span>

In-glaze or inglaze is a method of decorating pottery, where the materials used allow painted decoration to be applied on the surface of the glaze before the glost firing so that it fuses into the glaze in the course of firing.

This is a list of pottery and ceramic terms.

<i>Sancai</i>

Sancai is a versatile type of decoration on Chinese pottery using glazes or slip, predominantly in the three colours of brown, green, and a creamy off-white. It is particularly associated with the Tang dynasty (618–907) and its tomb figures, appearing around 700. Therefore, it is commonly referred to as Chinese: 唐三彩 Tang Sancai in Chinese. Tang sancai wares were sometimes referred in China and the West as egg-and-spinach by dealers, for their use of green, yellow, and white, especially when combined with a streaked effect.

<span class="mw-page-title-main">Jingdezhen porcelain</span> Chinese pottery produced as early as the sixth century CE in or near Jingdezhen in Jiangxi, China

Jingdezhen porcelain is Chinese porcelain produced in or near Jingdezhen in Jiangxi province in southern China. Jingdezhen may have produced pottery as early as the sixth century CE, though it is named after the reign name of Emperor Zhenzong, in whose reign it became a major kiln site, around 1004. By the 14th century it had become the largest centre of production of Chinese porcelain, which it has remained, increasing its dominance in subsequent centuries. From the Ming period onwards, official kilns in Jingdezhen were controlled by the emperor, making imperial porcelain in large quantity for the court and the emperor to give as gifts.

<span class="mw-page-title-main">Cizhou ware</span>

Cizhou ware or Tz'u-chou ware is a wide range of Chinese ceramics from between the late Tang dynasty and the early Ming dynasty, but especially associated with the Northern Song to Yuan period in the 11–14th century. It has been increasingly realized that a very large number of sites in northern China produced these wares, and their decoration is very variable, but most characteristically uses black and white, in a variety of techniques. For this reason Cizhou-type is often preferred as a general term. All are stoneware in Western terms, and "high-fired" or porcelain in Chinese terms. They were less high-status than other types such as celadons and Jun ware, and are regarded as "popular", though many are finely and carefully decorated.

<span class="mw-page-title-main">China painting</span> Art of painting on ceramics

China painting, or porcelain painting, is the decoration of glazed porcelain objects such as plates, bowls, vases or statues. The body of the object may be hard-paste porcelain, developed in China in the 7th or 8th century, or soft-paste porcelain, developed in 18th-century Europe. The broader term ceramic painting includes painted decoration on lead-glazed earthenware such as creamware or tin-glazed pottery such as maiolica or faience.

<i>Doucai</i> Technique in painting Chinese porcelain

Doucai is a technique in painting Chinese porcelain, where parts of the design, and some outlines of the rest, are painted in underglaze blue, and the piece is then glazed and fired. The rest of the design is then added in overglaze enamels of different colours and the piece fired again at a lower temperature of about 850°C to 900°C.

<i>Minai</i> ware Type of Persian pottery

Mina'i ware is a type of Persian pottery, or Islamic pottery developed in Kashan in the decades leading up to the Mongol invasion of Persia and Mesopotamia in 1219, after which production ceased. It has been described as "probably the most luxurious of all types of ceramic ware produced in the eastern Islamic lands during the medieval period". The ceramic body of white-ish fritware or stonepaste is fully decorated with detailed paintings using several colours, usually including figures.

References