Pozzolanic activity

Last updated

The pozzolanic activity is a measure for the degree of reaction over time or the reaction rate between a pozzolan and Ca2+ or calcium hydroxide (Ca(OH)2) in the presence of water. The rate of the pozzolanic reaction is dependent on the intrinsic characteristics of the pozzolan such as the specific surface area, the chemical composition and the active phase content.

Contents

Physical surface adsorption is not considered as being part of the pozzolanic activity, because no irreversible molecular bonds are formed in the process. [1]

Reaction

The pozzolanic reaction is the chemical reaction that occurs in portland cement upon the addition of pozzolans. It is the main reaction involved in the Roman concrete invented in Ancient Rome and used to build, for example, the Pantheon. The pozzolanic reaction converts a silica-rich precursor with no cementing properties, to a calcium silicate, with good cementing properties.

In chemical terms, the pozzolanic reaction occurs between calcium hydroxide, also known as portlandite (Ca(OH)2), and silicic acid (written as H4SiO4, or Si(OH)4, in the geochemical notation):

Ca(OH)2 + H4SiO4 → CaH2SiO4·2 H2O

or summarized in abbreviated cement chemist notation:

CH + SH → C-S-H

The pozzolanic reaction can also be written in an ancient industrial silicate notations as:

Ca(OH)
2
+ H
2
SiO
3
CaSiO
3
·2 H
2
O

or even directly:

Ca(OH)
2
+ SiO
2
CaSiO
3
·H
2
O

Both notations still coexist in the literature, depending on the research field considered. However, the more recent geochemical notation in which the Si atom is tetracoordinated by four hydroxyl groups (Si(OH)
4
, also commonly noted H
4
SiO
4
) is more correct than the ancient industrial silicate notation for which silicic acid (H
2
SiO
3
) was represented in the same way as carbonic acid (H
2
CO
3
) whose geometrical configuration is trigonal planar. When only considering mass balance, they are equivalent and both are used.

The product CaH2SiO4·2 H2O is a calcium silicate hydrate, also abbreviated as C-S-H in cement chemist notation, the hyphenation denotes the variable stoichiometry. The atomic (or molar) ratio Ca/Si, CaO/SiO2, or C/S, and the number of water molecules can vary and the above-mentioned stoichiometry may differ.

Many pozzolans may also contain aluminate, or Al(OH)4, that will react with calcium hydroxide and water to form calcium aluminate hydrates such as C4AH13, C3AH6 or hydrogarnet, or in combination with silica C2ASH8 or strätlingite (cement chemist notation). In the presence of anionic groups such as sulfate, carbonate or chloride, AFm phases and AFt or ettringite phases can form.

Pozzolanic reaction is a long term reaction, which involves dissolved silicic acid, water and CaO or Ca(OH)2 or other pozzolans to form a strong cementation matrix. This process is often irreversible. Sufficient amount of free calcium ion and a high pH of 12 and above is needed to initiate and maintain the pozzolanic reaction. [2] This is because at a pH of around 12, the solubility of silicon and aluminium ions is high enough to support the pozzolanic reaction.

Activity determining parameters

Particle properties

Prolonged grinding[ clarification needed ] results in an increased pozzolanic activity by creating a larger specific surface area available for reaction. Moreover, grinding also creates crystallographic defects at and below the particle surface. The dissolution rate of the strained or partially disconnected silicate moieties is strongly enhanced. Even materials which are commonly not regarded to behave as a pozzolan, such as quartz, can become reactive once ground below a certain critical particle diameter. [3]

Composition

The overall chemical composition of a pozzolan is considered as one of the parameters governing long-term performance (e.g. compressive strength) of the blended cement binder, ASTM C618 prescribes that a pozzolan should contain SiO2 + Al2O3 + Fe2O3 ≥ 70 wt.%. In case of a (quasi) one phase material such as blast-furnace slags the overall chemical composition can be considered as meaningful parameter, for multi-phase materials only a correlation between the pozzolanic activity and the chemistry of the active phases can be sought. [4]

Many pozzolans consist of a heterogeneous mixture of phases of different pozzolanic activity. Obviously, the content in reactive phases is an important property determining the overall reactivity. In general, the pozzolanic activity of phases thermodynamically stable at ambient conditions is low when compared to on an equal specific surface basis to less thermodynamically stable phase assemblages. Volcanic ash deposits containing large amounts of volcanic glass or zeolites are more reactive than quartz sands or detrital clay minerals. In this respect, the thermodynamic driving force behind the pozzolanic reaction serves as a rough indicator of the potential reactivity of a (alumino-)silicate material. Similarly, materials showing structural disorder such as glasses show higher pozzolanic activities than crystalline ordered compounds. [5]

Reaction conditions

The rate of the pozzolanic reaction can also be controlled by external factors such as the mix proportions, the amount of water or space available for the formation and growth of hydration products and the temperature of reaction. Therefore, typical blended cement mix design properties such as the replacement ratio of pozzolan for Portland cement, the water to binder ratio and the curing conditions strongly affect the reactivity of the added pozzolan.

Pozzolanic activity tests

Mechanical tests

Mechanical evaluation of the pozzolanic activity is based upon a comparison of the compressive strength of mortar bars containing pozzolans as a partial replacement for Portland cement to reference mortar bars containing only Portland cement as binder. The mortar bars are prepared, cast, cured and tested following a detailed set of prescriptions. Compressive strength testing is carried out at fixed moments, typically 3, 7, and 28 days after mortar preparation. A material is considered pozzolanically active when it contributes to the compressive strength, taking into account the effect of dilution. Most national and international technical standards or norms include variations of this methodology.

Chemical tests

A pozzolanic material is by definition capable of binding calcium hydroxide in the presence of water. Therefore, the chemical measurement of this pozzolanic activity represents a way of evaluating pozzolanic materials. This can be done by directly measuring the amount of calcium hydroxide a pozzolan consumes over time. At high water to binder ratio (suspended solutions), this can be measured by titrimety or by spectroscopic techniques. At lower water to binder ratios (pastes), thermal analysis or X-ray powder diffraction techniques are commonly used to determine remaining calcium hydroxide contents. Other direct methods have been developed that aim to directly measure the degree of reaction of the pozzolan itself. Here, selective dissolutions, X-ray powder diffraction or scanning electron microscopy image analysis methods have been used.

Indirect methods comprise on the one hand methods that investigate which material properties are responsible for the pozzolan's reactivity with portlandite. Material properties of interest are the (re)active silica and alumina content, the specific surface area and/or the reactive mineral and amorphous phases of the pozzolanic material. Other methods indirectly determine the extent of the pozzolanic activity by measuring an indicative physical property of the reacting system. Measurements of the electrical conductivity, chemical shrinkage of the pastes or the heat evolution by heat flow calorimetry reside in the latter category.

See also

Related Research Articles

<span class="mw-page-title-main">Cement</span> Hydraulic binder used in the composition of mortar and concrete

A cement is a binder, a chemical substance used for construction that sets, hardens, and adheres to other materials to bind them together. Cement is seldom used on its own, but rather to bind sand and gravel (aggregate) together. Cement mixed with fine aggregate produces mortar for masonry, or with sand and gravel, produces concrete. Concrete is the most widely used material in existence and is behind only water as the planet's most-consumed resource.

<span class="mw-page-title-main">Soda lime</span> Chemical mixture for absorbing carbon dioxide

Soda lime, a mixture of sodium hydroxide (NaOH) and calcium oxide (CaO), is used in granular form within recirculating breathing environments like general anesthesia and its breathing circuit, submarines, rebreathers, and hyperbaric chambers and underwater habitats. Its purpose is to eliminate carbon dioxide from breathing gases, preventing carbon dioxide retention and, eventually, carbon dioxide poisoning. The creation of soda lime involves treating slaked lime with a concentrated sodium hydroxide solution.

Cement chemist notation (CCN) was developed to simplify the formulas cement chemists use on a daily basis. It is a shorthand way of writing the chemical formula of oxides of calcium, silicon, and various metals.

<span class="mw-page-title-main">Pozzolana</span> Natural siliceous or siliceous-aluminous material

Pozzolana or pozzuolana, also known as pozzolanic ash, is a natural siliceous or siliceous-aluminous material which reacts with calcium hydroxide in the presence of water at room temperature. In this reaction insoluble calcium silicate hydrate and calcium aluminate hydrate compounds are formed possessing cementitious properties. The designation pozzolana is derived from one of the primary deposits of volcanic ash used by the Romans in Italy, at Pozzuoli. The modern definition of pozzolana encompasses any volcanic material, predominantly composed of fine volcanic glass, that is used as a pozzolan. Note the difference with the term pozzolan, which exerts no bearing on the specific origin of the material, as opposed to pozzolana, which can only be used for pozzolans of volcanic origin, primarily composed of volcanic glass.

<span class="mw-page-title-main">Lime (material)</span> Calcium oxides and/or hydroxides

Lime is an inorganic material composed primarily of calcium oxides and hydroxides. It is also the name for calcium oxide which occurs as a product of coal-seam fires and in altered limestone xenoliths in volcanic ejecta. The International Mineralogical Association recognizes lime as a mineral with the chemical formula of CaO. The word lime originates with its earliest use as building mortar and has the sense of sticking or adhering.

Metakaolin is the anhydrous calcined form of the clay mineral kaolinite. Rocks that are rich in kaolinite are known as china clay or kaolin, traditionally used in the manufacture of porcelain. The particle size of metakaolin is smaller than cement particles, but not as fine as silica fume.

In inorganic chemistry, mineral hydration is a reaction which adds water to the crystal structure of a mineral, usually creating a new mineral, commonly called a hydrate.

<span class="mw-page-title-main">Ground granulated blast-furnace slag</span> Granular slag by-product of iron and steel-making used as supplementary cementitious material

Ground granulated blast-furnace slag is obtained by quenching molten iron slag from a blast furnace in water or steam, to produce a glassy, granular product that is then dried and ground into a fine powder. Ground granulated blast furnace slag is a latent hydraulic binder forming calcium silicate hydrates (C-S-H) after contact with water. It is a strength-enhancing compound improving the durability of concrete. It is a component of metallurgic cement. Its main advantage is its slow release of hydration heat, allowing limitation of the temperature increase in massive concrete components and structures during cement setting and concrete curing, or to cast concrete during hot summer.

<span class="mw-page-title-main">Pozzolan</span> Siliceous volcanic ashes commonly used as supplementary cementitious material

Pozzolans are a broad class of siliceous and aluminous materials which, in themselves, possess little or no cementitious value but which will, in finely divided form and in the presence of water, react chemically with calcium hydroxide (Ca(OH)2) at ordinary temperature to form compounds possessing cementitious properties. The quantification of the capacity of a pozzolan to react with calcium hydroxide and water is given by measuring its pozzolanic activity. Pozzolana are naturally occurring pozzolans of volcanic origin.

Alite is an impure form of tricalcium silicate, Ca3SiO5, sometimes formulated as 3CaO·SiO2, typically with 3-4% of substituent oxides. It is the major, and characteristic, phase in Portland cement. The name was given by Törnebohm in 1897 to a crystal identified in microscopic investigation of Portland cement. Hatrurite is the name of a mineral that is substituted C3S.

Belite is an industrial mineral important in Portland cement manufacture. Its main constituent is dicalcium silicate, Ca2SiO4, sometimes formulated as 2 CaO · SiO2 (C2S in cement chemist notation).

<span class="mw-page-title-main">Cement clinker</span> Main component of Portland cement

Cement clinker is a solid material produced in the manufacture of portland cement as an intermediary product. Clinker occurs as lumps or nodules, usually 3 millimetres (0.12 in) to 25 millimetres (0.98 in) in diameter. It is produced by sintering limestone and aluminosilicate materials such as clay during the cement kiln stage.

<span class="mw-page-title-main">Calcium aluminate cements</span> Rapidly setting hydraulic cements

Calcium aluminate cements are cements consisting predominantly of hydraulic calcium aluminates. Alternative names are "aluminous cement", "high-alumina cement", and "Ciment fondu" in French. They are used in a number of small-scale, specialized applications.

<span class="mw-page-title-main">Thaumasite</span> Complex calcium silicate hydrate mineral

Thaumasite is a calcium silicate mineral, containing Si atoms in unusual octahedral configuration, with chemical formula Ca3Si(OH)6(CO3)(SO4)·12H2O, also sometimes more simply written as CaSiO3·CaCO3·CaSO4·15H2O.

<span class="mw-page-title-main">Alkali–silica reaction</span> Chemical reaction damaging concrete

The alkali–silica reaction (ASR), also commonly known as concrete cancer, is a deleterious internal swelling reaction that occurs over time in concrete between the highly alkaline cement paste and the reactive amorphous silica found in many common aggregates, given sufficient moisture.

<span class="mw-page-title-main">Roman concrete</span> Building material used in ancient Rome

Roman concrete, also called opus caementicium, was used in construction in ancient Rome. Like its modern equivalent, Roman concrete was based on a hydraulic-setting cement added to an aggregate.

Calcium silicate hydrates are the main products of the hydration of Portland cement and are primarily responsible for the strength of cement-based materials. They are the main binding phase in most concrete. Only well defined and rare natural crystalline minerals can be abbreviated as CSH while extremely variable and poorly ordered phases without well defined stoichiometry, as it is commonly observed in hardened cement paste (HCP), are denoted C-S-H.

<span class="mw-page-title-main">Concrete degradation</span> Damage to concrete affecting its mechanical strength and its durability

Concrete degradation may have many different causes. Concrete is mostly damaged by the corrosion of reinforcement bars due to the carbonatation of hardened cement paste or chloride attack under wet conditions. Chemical damage is caused by the formation of expansive products produced by chemical reactions, by aggressive chemical species present in groundwater and seawater, or by microorganisms Other damaging processes can also involve calcium leaching by water infiltration, physical phenomena initiating cracks formation and propagation, fire or radiant heat, aggregate expansion, sea water effects, leaching, and erosion by fast-flowing water.

<span class="mw-page-title-main">Energetically modified cement</span> Class of cements, mechanically processed to transform reactivity

Energetically modified cements (EMCs) are a class of cements made from pozzolans, silica sand, blast furnace slag, or Portland cement. The term "energetically modified" arises by virtue of the mechanochemistry process applied to the raw material, more accurately classified as "high energy ball milling" (HEBM). At its simplest this means a milling method that invokes high kinetics by subjecting "powders to the repeated action of hitting balls" as compared to (say) the low kinetics of rotating ball mills. This causes, amongst others, a thermodynamic transformation in the material to increase its chemical reactivity. For EMCs, the HEBM process used is a unique form of specialised vibratory milling discovered in Sweden and applied only to cementitious materials, here called "EMC Activation".

Cement hydration and strength development mainly depend on two silicate phases: tricalcium silicate (C3S) (alite), and dicalcium silicate (C2S) (belite). Upon hydration, the main reaction products are calcium silicate hydrates (C-S-H) and calcium hydroxide Ca(OH)2, written as CH in the cement chemist notation. C-S-H is the phase playing the role of the glue in the cement hardened paste and responsible of its cohesion. Cement also contains two aluminate phases: C3A and C4AF, respectively the tricalcium aluminate and the tetracalcium aluminoferrite. C3A hydration products are AFm, calcium aluminoferrite monosulfate, and ettringite, a calcium aluminoferrite trisulfate (AFt). C4AF hydrates as hydrogarnet and ferrous ettringite.

References

  1. Takemoto, K.; Uchikawa H. (1980). "Hydration of pozzolanic cements". Proceedings of the 7th International Congress on the Chemistry of Cement. IV-2: 1–29.
  2. Cherian, C.; Arnepalli, D. (2015). "A critical appraisal of the role of clay mineralogy in lime stabilization". International Journal of Geosynthetics and Ground Engineering. 1 (1): 1–20. doi: 10.1007/s40891-015-0009-3 . S2CID   256465326.
  3. Benezet, J.C.; Benhassaine A. (1999). "Grinding and pozzolanic reactivity of quartz powders". Powder Technology. 105 (1–3): 167–171. doi:10.1016/S0032-5910(99)00133-3.
  4. Massazza, F. (2001). "Pozzolana and pozzolanic cements". Lea's Chemistry of Cement and Concrete. Butterworth-Heinemann: 471–636.
  5. Snellings, R.; Mertens G.; Elsen J. (2012). "Supplementary cementitious materials". Reviews in Mineralogy and Geochemistry. 74 (1): 211–278. Bibcode:2012RvMG...74..211S. doi:10.2138/rmg.2012.74.6.

Further reading