Concrete is a composite material composed of aggregate bonded together with a fluid cement that cures over time. Concrete is the second-most-used substance in the world after water, [1] and is the most widely used building material. [2] Its usage worldwide, ton for ton, is twice that of steel, wood, plastics, and aluminium combined.[ citation needed ]


When aggregate is mixed with dry Portland cement and water, the mixture forms a fluid slurry that is easily poured and molded into shape. The cement reacts with the water through a process called concrete hydration [3] that hardens it over several hours to form a hard matrix that binds the materials together into a durable stone-like material that has many uses. [4] This time allows concrete to not only be cast in forms, but also to have a variety of tooled processes performed. The hydration process is exothermic, which means ambient temperature plays a significant role in how long it takes concrete to set. Often, additives (such as pozzolans or superplasticizers) are included in the mixture to improve the physical properties of the wet mix, delay or accelerate the curing time, or otherwise change the finished material. Most concrete is poured with reinforcing materials (such as steel rebar) embedded to provide tensile strength, yielding reinforced concrete.

In the past, lime based cement binders, such as lime putty, were often used but sometimes with other hydraulic cements, (water resistant) such as a calcium aluminate cement or with Portland cement to form Portland cement concrete (named for its visual resemblance to Portland stone). [5] [6] Many other non-cementitious types of concrete exist with other methods of binding aggregate together, including asphalt concrete with a bitumen binder, which is frequently used for road surfaces, and polymer concretes that use polymers as a binder. Concrete is distinct from mortar. Whereas concrete is itself a building material, mortar is a bonding agent that typically holds bricks, tiles and other masonry units together. [7] Grout is another material associated with concrete and cement. It does not contain coarse aggregates and is usually either pourable or thixotropic, and is used to fill gaps between masonry components or coarse aggregate which has already been put in place. Some methods of concrete manufacture and repair involve pumping grout into the gaps to make up a solid mass in situ.


The word concrete comes from the Latin word "concretus" (meaning compact or condensed), [8] the perfect passive participle of "concrescere", from "con-" (together) and "crescere" (to grow).


Ancient times

Mayan concrete at the ruins of Uxmal (850-925 A.D.) is referenced in Incidents of Travel in the Yucatán by John L. Stephens. "The roof is flat and had been covered with cement". "The floors were cement, in some places hard, but, by long exposure, broken, and now crumbling under the feet." "But throughout the wall was solid, and consisting of large stones imbedded in mortar, almost as hard as rock."

Small-scale production of concrete-like materials was pioneered by the Nabatean traders who occupied and controlled a series of oases and developed a small empire in the regions of southern Syria and northern Jordan from the 4th century BC. They discovered the advantages of hydraulic lime, with some self-cementing properties, by 700 BC. They built kilns to supply mortar for the construction of rubble masonry houses, concrete floors, and underground waterproof cisterns. They kept the cisterns secret as these enabled the Nabataeans to thrive in the desert. [9] Some of these structures survive to this day. [9]

Classical era

Exterior of the Roman Pantheon, finished 128 AD, the largest unreinforced concrete dome in the world. Pantheon dome.jpg
Exterior of the Roman Pantheon, finished 128 AD, the largest unreinforced concrete dome in the world.
Interior of the Pantheon dome, seen from beneath. The concrete for the coffered dome was laid on moulds, mounted on temporary scaffolding. Pantheon cupola.jpg
Interior of the Pantheon dome, seen from beneath. The concrete for the coffered dome was laid on moulds, mounted on temporary scaffolding.
Opus caementicium exposed in a characteristic Roman arch. In contrast to modern concrete structures, the concrete used in Roman buildings was usually covered with brick or stone. Museo Foro Caesaragusta - Cloaca del foro 03.JPG
Opus caementicium exposed in a characteristic Roman arch. In contrast to modern concrete structures, the concrete used in Roman buildings was usually covered with brick or stone.

In the Ancient Egyptian and later Roman eras, builders discovered that adding volcanic ash to the mix allowed it to set underwater.

Concrete floors were found in the royal palace of Tiryns, Greece, which dates roughly to 1400-1200 BC. [11] [12] Lime mortars were used in Greece, such as in Crete and Cyprus, in 800 BC. The Assyrian Jerwan Aqueduct (688 BC) made use of waterproof concrete. [13] Concrete was used for construction in many ancient structures. [14]

The Romans used concrete extensively from 300 BC to 476 AD. [15] During the Roman Empire, Roman concrete (or opus caementicium ) was made from quicklime, pozzolana and an aggregate of pumice. Its widespread use in many Roman structures, a key event in the history of architecture termed the Roman architectural revolution, freed Roman construction from the restrictions of stone and brick materials. It enabled revolutionary new designs in terms of both structural complexity and dimension. [16] The Colosseum in Rome was built largely of concrete, and the Pantheon has the world's largest unreinforced concrete dome. [17]

Concrete, as the Romans knew it, was a new and revolutionary material. Laid in the shape of arches, vaults and domes, it quickly hardened into a rigid mass, free from many of the internal thrusts and strains that troubled the builders of similar structures in stone or brick. [18]

Modern tests show that opus caementicium had as much compressive strength as modern Portland-cement concrete (ca. 200 kg/cm2 [20 MPa; 2,800 psi]). [19] However, due to the absence of reinforcement, its tensile strength was far lower than modern reinforced concrete, and its mode of application also differed: [20]

Modern structural concrete differs from Roman concrete in two important details. First, its mix consistency is fluid and homogeneous, allowing it to be poured into forms rather than requiring hand-layering together with the placement of aggregate, which, in Roman practice, often consisted of rubble. Second, integral reinforcing steel gives modern concrete assemblies great strength in tension, whereas Roman concrete could depend only upon the strength of the concrete bonding to resist tension. [21]

The long-term durability of Roman concrete structures has been found to be due to its use of pyroclastic (volcanic) rock and ash, whereby the crystallization of strätlingite (a specific and complex calcium aluminosilicate hydrate) [22] and the coalescence of this and similar calcium–aluminium-silicate–hydrate cementing binders helped give the concrete a greater degree of fracture resistance even in seismically active environments. [23] Roman concrete is significantly more resistant to erosion by seawater than modern concrete; it used pyroclastic materials which react with seawater to form Al-tobermorite crystals over time. [24] [25]

The widespread use of concrete in many Roman structures ensured that many survive to the present day. The Baths of Caracalla in Rome are just one example. Many Roman aqueducts and bridges, such as the magnificent Pont du Gard in southern France, have masonry cladding on a concrete core, as does the dome of the Pantheon.

Middle Ages

After the Roman Empire, the use of burned lime and pozzolana was greatly reduced. Low kiln temperatures in the burning of lime, lack of pozzolana, and poor mixing all contributed to a decline in the quality of concrete and mortar. From the 11th century, the increased use of stone in church and castle construction led to an increased demand for mortar. Quality began to improve in the 12th century through better grinding and sieving. Medieval lime mortars and concretes were non-hydraulic and were used for binding masonry, "hearting" (binding rubble masonry cores) and foundations. Bartholomaeus Anglicus in his De proprietatibus rerum (1240) describes the making of mortar. In an English translation from 1397, it reads "lyme ... is a stone brent; by medlynge thereof with sonde and water sement is made". From the 14th century, the quality of mortar was again excellent, but only from the 17th century was pozzolana commonly added. [26]

The Canal du Midi was built using concrete in 1670. [27]

Industrial era

Smeaton's Tower Smeaton's Lighthouse00.jpg
Smeaton's Tower

Perhaps the greatest step forward in the modern use of concrete was Smeaton's Tower, built by British engineer John Smeaton in Devon, England, between 1756 and 1759. This third Eddystone Lighthouse pioneered the use of hydraulic lime in concrete, using pebbles and powdered brick as aggregate. [28]

A method for producing Portland cement was developed in England and patented by Joseph Aspdin in 1824. [29] Aspdin chose the name for its similarity to Portland stone, which was quarried on the Isle of Portland in Dorset, England. His son William continued developments into the 1840s, earning him recognition for the development of "modern" Portland cement. [30]

Reinforced concrete was invented in 1849 by Joseph Monier. [31] and the first reinforced concrete house was built by François Coignet [32] in 1853. The first concrete reinforced bridge was designed and built by Joseph Monier in 1875. [33]


Concrete is an artificial composite material, comprising a matrix of cementitious binder (typically Portland cement paste or asphalt) and a dispersed phase or "filler" of aggregate (typically a rocky material, loose stones, and sand). The binder "glues" the filler together to form a synthetic conglomerate. [34] Many types of concrete are available, determined by the formulations of binders and the types of aggregate used to suit the application of the engineered material. These variables determine strength and density, as well as chemical and thermal resistance of the finished product.

Cross section of a concrete railway sleeper below a rail DB Museum rail and concrete sleeper cross section 2.jpg
Cross section of a concrete railway sleeper below a rail

Aggregates consist of large chunks of material in a concrete mix, generally a coarse gravel or crushed rocks such as limestone, or granite, along with finer materials such as sand.

Cement paste, most commonly made of Portland cement, is the most prevalent kind of concrete binder. For cementitious binders, water is mixed with the dry cement powder and aggregate, which produces a semi-liquid slurry (paste) that can be shaped, typically by pouring it into a form. The concrete solidifies and hardens through a chemical process called hydration. The water reacts with the cement, which bonds the other components together, creating a robust, stone-like material. Other cementitious materials, such as fly ash and slag cement, are sometimes added—either pre-blended with the cement or directly as a concrete component—and become a part of the binder for the aggregate. [35] Fly ash and slag can enhance some properties of concrete such as fresh properties and durability. [35] Alternatively, other materials can also be used as a concrete binder: the most prevalent substitute is asphalt, which is used as the binder in asphalt concrete.

Admixtures are added to modify the cure rate or properties of the material. Mineral admixtures use recycled materials as concrete ingredients. Conspicuous materials include fly ash, a by-product of coal-fired power plants; ground granulated blast furnace slag, a by-product of steelmaking; and silica fume, a by-product of industrial electric arc furnaces.

Structures employing Portland cement concrete usually include steel reinforcement because this type of concrete can be formulated with high compressive strength, but always has lower tensile strength. Therefore, it is usually reinforced with materials that are strong in tension, typically steel rebar.

The mix design depends on the type of structure being built, how the concrete is mixed and delivered, and how it is placed to form the structure.


Several tons of bagged cement, about two minutes of output from a 10,000 ton per day cement kiln Stockage de ciments.JPG
Several tons of bagged cement, about two minutes of output from a 10,000 ton per day cement kiln

Portland cement is the most common type of cement in general usage. It is a basic ingredient of concrete, mortar, and many plasters. [36] British masonry worker Joseph Aspdin patented Portland cement in 1824. It was named because of the similarity of its color to Portland limestone, quarried from the English Isle of Portland and used extensively in London architecture. It consists of a mixture of calcium silicates (alite, belite), aluminates and ferrites—compounds which combine calcium, silicon, aluminium and iron in forms which will react with water. Portland cement and similar materials are made by heating limestone (a source of calcium) with clay or shale (a source of silicon, aluminium and iron) and grinding this product (called clinker ) with a source of sulfate (most commonly gypsum).

In modern cement kilns, many advanced features are used to lower the fuel consumption per ton of clinker produced. Cement kilns are extremely large, complex, and inherently dusty industrial installations, and have emissions which must be controlled. Of the various ingredients used to produce a given quantity of concrete, the cement is the most energetically expensive. Even complex and efficient kilns require 3.3 to 3.6 gigajoules of energy to produce a ton of clinker and then grind it into cement. Many kilns can be fueled with difficult-to-dispose-of wastes, the most common being used tires. The extremely high temperatures and long periods of time at those temperatures allows cement kilns to efficiently and completely burn even difficult-to-use fuels. [37]


Combining water with a cementitious material forms a cement paste by the process of hydration. The cement paste glues the aggregate together, fills voids within it, and makes it flow more freely. [38]

As stated by Abrams' law, a lower water-to-cement ratio yields a stronger, more durable concrete, whereas more water gives a freer-flowing concrete with a higher slump. [39] Impure water used to make concrete can cause problems when setting or in causing premature failure of the structure. [40]

Portland cement consists of five major compounds of calcium silicates and aluminates ranging from 5 to 50% in weight, which all undergo hydration to contribute to final material's strength. Thus, the hydration of cement involves many reactions, often occurring at the same time. As the reactions proceed, the products of the cement hydration process gradually bond together the individual sand and gravel particles and other components of the concrete to form a solid mass. [41]

Hydration of tricalcium silicate

Cement chemist notation: C3S + H → C-S-H + CH + heat
Standard notation: Ca3SiO5 + H2O → (CaO)·(SiO2)·(H2O)(gel) + Ca(OH)2
Balanced: 2Ca3SiO5 + 7H2O → 3(CaO)·2(SiO2)·4(H2O)(gel) + 3Ca(OH)2 (approximately; the exact ratios of the CaO, SiO2 and H2O in C-S-H can vary) [41]

Due to the nature of the chemical bonds created in these reactions and the final characteristics of the particles formed, the process of cement hydration is considered irreversible, which makes methods of cement recycling prohibitive. [42]


Crushed stone aggregate Gravel 03375C.JPG
Crushed stone aggregate

Fine and coarse aggregates make up the bulk of a concrete mixture. Sand, natural gravel, and crushed stone are used mainly for this purpose. Recycled aggregates (from construction, demolition, and excavation waste) are increasingly used as partial replacements for natural aggregates, while a number of manufactured aggregates, including air-cooled blast furnace slag and bottom ash are also permitted.

The size distribution of the aggregate determines how much binder is required. Aggregate with a very even size distribution has the biggest gaps whereas adding aggregate with smaller particles tends to fill these gaps. The binder must fill the gaps between the aggregate as well as paste the surfaces of the aggregate together, and is typically the most expensive component. Thus, variation in sizes of the aggregate reduces the cost of concrete. [43] The aggregate is nearly always stronger than the binder, so its use does not negatively affect the strength of the concrete.

Redistribution of aggregates after compaction often creates non-homogeneity due to the influence of vibration. This can lead to strength gradients. [44]

Decorative stones such as quartzite, small river stones or crushed glass are sometimes added to the surface of concrete for a decorative "exposed aggregate" finish, popular among landscape designers.


Admixtures are materials in the form of powder or fluids that are added to the concrete to give it certain characteristics not obtainable with plain concrete mixes. Admixtures are defined as additions "made as the concrete mix is being prepared". [45] The most common admixtures are retarders and accelerators. In normal use, admixture dosages are less than 5% by mass of cement and are added to the concrete at the time of batching/mixing. [46] (See § Production below.) The common types of admixtures [47] are as follows:

Mineral admixtures and blended cements

Components of cement:
comparison of chemical and physical characteristics [lower-alpha 1] [49] [50] [51]
Siliceous [lower-alpha 2]
fly ash
Calcareous [lower-alpha 3]
fly ash
Proportion by mass (%)
CaO6352140< 1
Specific surface (m2/kg) [lower-alpha 4] 37042042040015,000
– 30,000
Specific gravity3.152.382.652.942.22
General purposePrimary binderCement replacementCement replacementCement replacementProperty enhancer
  1. Values shown are approximate: those of a specific material may vary.
  2. ASTM C618 Class F
  3. ASTM C618 Class C
  4. Specific surface measurements for silica fume by nitrogen adsorption (BET) method, others by air permeability method (Blaine).

Inorganic materials that have pozzolanic or latent hydraulic properties, these very fine-grained materials are added to the concrete mix to improve the properties of concrete (mineral admixtures), [46] or as a replacement for Portland cement (blended cements). [52] Products which incorporate limestone, fly ash, blast furnace slag, and other useful materials with pozzolanic properties into the mix, are being tested and used. These developments are ever growing in relevance to minimize the impacts caused by cement use, notorious for being one of the largest producers (at about 5 to 10%) of global greenhouse gas emissions. [53] The use of alternative materials also is capable of lowering costs, improving concrete properties, and recycling wastes, the latest being relevant for circular economy aspects of the construction industry, whose demand is ever growing with greater impacts on raw material extraction, waste generation and landfill practices.


Concrete plant showing a concrete mixer being filled from ingredient silos Concrete plant in Mansfield, Ohio.jpg
Concrete plant showing a concrete mixer being filled from ingredient silos
Concrete mixing plant in Birmingham, Alabama in 1936 Concrete mixing plant, Birmingham, Alabama, view 2.jpg
Concrete mixing plant in Birmingham, Alabama in 1936

Concrete production is the process of mixing together the various ingredients—water, aggregate, cement, and any additives—to produce concrete. Concrete production is time-sensitive. Once the ingredients are mixed, workers must put the concrete in place before it hardens. In modern usage, most concrete production takes place in a large type of industrial facility called a concrete plant, or often a batch plant. The usual method of placement is casting in formwork, which holds the mix in shape until it has set enough to hold its shape unaided.

In general usage, concrete plants come in two main types, ready mix plants and central mix plants. A ready-mix plant mixes all the ingredients except water, while a central mix plant mixes all the ingredients including water. A central-mix plant offers more accurate control of the concrete quality through better measurements of the amount of water added, but must be placed closer to the work site where the concrete will be used, since hydration begins at the plant.

A concrete plant consists of large storage hoppers for various reactive ingredients like cement, storage for bulk ingredients like aggregate and water, mechanisms for the addition of various additives and amendments, machinery to accurately weigh, move, and mix some or all of those ingredients, and facilities to dispense the mixed concrete, often to a concrete mixer truck.

Modern concrete is usually prepared as a viscous fluid, so that it may be poured into forms, which are containers erected in the field to give the concrete its desired shape. Concrete formwork can be prepared in several ways, such as slip forming and steel plate construction. Alternatively, concrete can be mixed into dryer, non-fluid forms and used in factory settings to manufacture precast concrete products.

A wide variety of equipment is used for processing concrete, from hand tools to heavy industrial machinery. Whichever equipment builders use, however, the objective is to produce the desired building material; ingredients must be properly mixed, placed, shaped, and retained within time constraints. Any interruption in pouring the concrete can cause the initially placed material to begin to set before the next batch is added on top. This creates a horizontal plane of weakness called a cold joint between the two batches. [59] Once the mix is where it should be, the curing process must be controlled to ensure that the concrete attains the desired attributes. During concrete preparation, various technical details may affect the quality and nature of the product.

Design mix

Design mix ratios are decided by an engineer after analyzing the properties of the specific ingredients being used. Instead of using a 'nominal mix' of 1 part cement, 2 parts sand, and 4 parts aggregate (the second example from above), a civil engineer will custom-design a concrete mix to exactly meet the requirements of the site and conditions, setting material ratios and often designing an admixture package to fine-tune the properties or increase the performance envelope of the mix. Design-mix concrete can have very broad specifications that cannot be met with more basic nominal mixes, but the involvement of the engineer often increases the cost of the concrete mix.

Concrete Mixes are primarily divided into nominal mix, standard mix and design mix.

Nominal mix ratios are given in volume of . Nominal mixes are a simple, fast way of getting a basic idea of the properties of the finished concrete without having to perform testing in advance.

Various governing bodies (such as British Standards) define nominal mix ratios into a number of grades, usually ranging from lower compressive strength to higher compressive strength. The grades usually indicate the 28-day cube strength. [60]


Thorough mixing is essential to produce uniform, high-quality concrete.

Separate paste mixing has shown that the mixing of cement and water into a paste before combining these materials with aggregates can increase the compressive strength of the resulting concrete. [61] The paste is generally mixed in a high-speed, shear-type mixer at a w/c (water to cement ratio) of 0.30 to 0.45 by mass. The cement paste premix may include admixtures such as accelerators or retarders, superplasticizers, pigments, or silica fume. The premixed paste is then blended with aggregates and any remaining batch water and final mixing is completed in conventional concrete mixing equipment. [62]

Sample analysis – Workability

Concrete floor of a parking garage being placed Cannon Renewal Project - October 2016 (30662609012).jpg
Concrete floor of a parking garage being placed
Pouring and smoothing out concrete at Palisades Park in Washington, DC Concreteathruz.jpg
Pouring and smoothing out concrete at Palisades Park in Washington, DC

Workability is the ability of a fresh (plastic) concrete mix to fill the form/mold properly with the desired work (pouring, pumping, spreading, tamping, vibration) and without reducing the concrete's quality. Workability depends on water content, aggregate (shape and size distribution), cementitious content and age (level of hydration) and can be modified by adding chemical admixtures, like superplasticizer. Raising the water content or adding chemical admixtures increases concrete workability. Excessive water leads to increased bleeding or segregation of aggregates (when the cement and aggregates start to separate), with the resulting concrete having reduced quality. Changes in gradation can also affect workability of the concrete, although a wide range of gradation can be used for various applications. [63] [64] An undesirable gradation can mean using a large aggregate that is too large for the size of the formwork, or which has too few smaller aggregate grades to serve to fill the gaps between the larger grades, or using too little or too much sand for the same reason, or using too little water, or too much cement, or even using jagged crushed stone instead of smoother round aggregate such as pebbles. Any combination of these factors and others may result in a mix which is too harsh, i.e., which does not flow or spread out smoothly, is difficult to get into the formwork, and which is difficult to surface finish. [65]

Workability can be measured by the concrete slump test, a simple measure of the plasticity of a fresh batch of concrete following the ASTM C 143 or EN 12350-2 test standards. Slump is normally measured by filling an "Abrams cone" with a sample from a fresh batch of concrete. The cone is placed with the wide end down onto a level, non-absorptive surface. It is then filled in three layers of equal volume, with each layer being tamped with a steel rod to consolidate the layer. When the cone is carefully lifted off, the enclosed material slumps a certain amount, owing to gravity. A relatively dry sample slumps very little, having a slump value of one or two inches (25 or 50 mm) out of one foot (300 mm). A relatively wet concrete sample may slump as much as eight inches. Workability can also be measured by the flow table test.

Slump can be increased by addition of chemical admixtures such as plasticizer or superplasticizer without changing the water-cement ratio. [66] Some other admixtures, especially air-entraining admixture, can increase the slump of a mix.

High-flow concrete, like self-consolidating concrete, is tested by other flow-measuring methods. One of these methods includes placing the cone on the narrow end and observing how the mix flows through the cone while it is gradually lifted.

After mixing, concrete is a fluid and can be pumped to the location where needed.


A concrete slab being kept hydrated during water curing by submersion (ponding) Curing-concrete.jpg
A concrete slab being kept hydrated during water curing by submersion (ponding)

Maintaining optimal conditions for cement hydration

Concrete must be kept moist during curing in order to achieve optimal strength and durability. [67] During curing hydration occurs, allowing calcium-silicate hydrate (C-S-H) to form. Over 90% of a mix's final strength is typically reached within four weeks, with the remaining 10% achieved over years or even decades. [68] The conversion of calcium hydroxide in the concrete into calcium carbonate from absorption of CO2 over several decades further strengthens the concrete and makes it more resistant to damage. This carbonation reaction, however, lowers the pH of the cement pore solution and can corrode the reinforcement bars.

Hydration and hardening of concrete during the first three days is critical. Abnormally fast drying and shrinkage due to factors such as evaporation from wind during placement may lead to increased tensile stresses at a time when it has not yet gained sufficient strength, resulting in greater shrinkage cracking. The early strength of the concrete can be increased if it is kept damp during the curing process. Minimizing stress prior to curing minimizes cracking. High-early-strength concrete is designed to hydrate faster, often by increased use of cement that increases shrinkage and cracking. The strength of concrete changes (increases) for up to three years. It depends on cross-section dimension of elements and conditions of structure exploitation. [69] Addition of short-cut polymer fibers can improve (reduce) shrinkage-induced stresses during curing and increase early and ultimate compression strength. [70]

Properly curing concrete leads to increased strength and lower permeability and avoids cracking where the surface dries out prematurely. Care must also be taken to avoid freezing or overheating due to the exothermic setting of cement. Improper curing can cause scaling, reduced strength, poor abrasion resistance and cracking.

Curing techniques avoiding water loss by evaporation

During the curing period, concrete is ideally maintained at controlled temperature and humidity. To ensure full hydration during curing, concrete slabs are often sprayed with "curing compounds" that create a water-retaining film over the concrete. Typical films are made of wax or related hydrophobic compounds. After the concrete is sufficiently cured, the film is allowed to abrade from the concrete through normal use. [71]

Traditional conditions for curing involve spraying or ponding the concrete surface with water. The adjacent picture shows one of many ways to achieve this, ponding—submerging setting concrete in water and wrapping in plastic to prevent dehydration. Additional common curing methods include wet burlap and plastic sheeting covering the fresh concrete.

For higher-strength applications, accelerated curing techniques may be applied to the concrete. A common technique involves heating the poured concrete with steam, which serves to both keep it damp and raise the temperature so that the hydration process proceeds more quickly and more thoroughly.

Alternative types


Asphalt concrete (commonly called asphalt, [72] blacktop, or pavement in North America, and tarmac, bitumen macadam, or rolled asphalt in the United Kingdom and the Republic of Ireland) is a composite material commonly used to surface roads, parking lots, airports, as well as the core of embankment dams. [73] Asphalt mixtures have been used in pavement construction since the beginning of the twentieth century. [74] It consists of mineral aggregate bound together with asphalt, laid in layers, and compacted. The process was refined and enhanced by Belgian inventor and U.S. immigrant Edward De Smedt. [75]

The terms asphalt (or asphaltic) concrete, bituminous asphalt concrete, and bituminous mixture are typically used only in engineering and construction documents, which define concrete as any composite material composed of mineral aggregate adhered with a binder. The abbreviation, AC, is sometimes used for asphalt concrete but can also denote asphalt content or asphalt cement, referring to the liquid asphalt portion of the composite material.

Graphene enhanced concrete

Graphene enhanced concretes are standard designs of concrete mixes, except that during the cement-mixing or production process, a small amount of chemically engineered graphene (typically < 0.5% by weight) is added. [76] [77] These enhanced graphene concretes are designed around the concrete application.


Bacteria such as Bacillus pasteurii , Bacillus pseudofirmus , Bacillus cohnii, Sporosarcina pasteuri, and Arthrobacter crystallopoietes increase the compression strength of concrete through their biomass. However some forms of bacteria can also be concrete-destroying. [78] Bacillus sp. CT-5. can reduce corrosion of reinforcement in reinforced concrete by up to four times. Sporosarcina pasteurii reduces water and chloride permeability. B. pasteurii increases resistance to acid. [79] Bacillus pasteurii and B. sphaericuscan induce calcium carbonate precipitation in the surface of cracks, adding compression strength. [80]


Decorative plate made of Nano concrete with High-Energy Mixing (HEM) Decorative cameo plate.jpg
Decorative plate made of Nano concrete with High-Energy Mixing (HEM)

Nanoconcrete (also spelled "nano concrete"' or "nano-concrete") is a class of materials that contains Portland cement particles that are no greater than 100 μm [81] and particles of silica no greater than 500 μm, which fill voids that would otherwise occur in normal concrete, thereby substantially increasing the material's strength. [82] It is widely used in foot and highway bridges where high flexural and compressive strength are indicated. [80]


Pervious concrete is a mix of specially graded coarse aggregate, cement, water, and little-to-no fine aggregates. This concrete is also known as "no-fines" or porous concrete. Mixing the ingredients in a carefully controlled process creates a paste that coats and bonds the aggregate particles. The hardened concrete contains interconnected air voids totaling approximately 15 to 25 percent. Water runs through the voids in the pavement to the soil underneath. Air entrainment admixtures are often used in freeze-thaw climates to minimize the possibility of frost damage. Pervious concrete also permits rainwater to filter through roads and parking lots, to recharge aquifers, instead of contributing to runoff and flooding. [83]


Polymer concretes are mixtures of aggregate and any of various polymers and may be reinforced. The cement is costlier than lime-based cements, but polymer concretes nevertheless have advantages; they have significant tensile strength even without reinforcement, and they are largely impervious to water. Polymer concretes are frequently used for the repair and construction of other applications, such as drains.


Volcanic concrete substitutes volcanic rock for the limestone that is burned to form clinker. It consumes a similar amount of energy, but does not directly emit carbon as a byproduct. [84] Volcanic rock/ash are used as supplementary cementitious materials in concrete to improve the resistance to sulfate, chloride and alkali silica reaction due to pore refinement. [85] Also, they are generally cost effective in comparison to other aggregates, [86] good for semi and light weight concretes, [86] and good for thermal and acoustic insulation. [86]

Pyroclastic materials, such as pumice, scoria, and ashes are formed from cooling magma during explosive volcanic eruptions. They are used as supplementary cementitious materials (SCM) or as aggregates for cements and concretes. [87] They have been extensively used since ancient times to produce materials for building applications. For example, pumice and other volcanic glasses were added as a natural pozzolanic material for mortars and plasters during the construction of the Villa San Marco in the Roman period (89 BC – 79 AD), which remain one of the best-preserved otium villae of the Bay of Naples in Italy. [88]

Waste light

Waste light is form of polymer modified concrete. The specific polymer admixture allows the replacement of all the traditional aggregates (gravel, sand, stone) by any mixture of solid waste materials in the grain size of 3–10 mm to form a low-compressive-strength (3–20 N/mm2) product [89] for road and building construction. One cubic meter of waste light concrete contains 1.1–1.3 m3 of shredded waste and no other aggregates.

Sulfur concrete

Sulfur concrete is a special concrete that uses sulfur as a binder and does not require cement or water.


Concrete has relatively high compressive strength, but much lower tensile strength. [90] Therefore, it is usually reinforced with materials that are strong in tension (often steel). The elasticity of concrete is relatively constant at low stress levels but starts decreasing at higher stress levels as matrix cracking develops. Concrete has a very low coefficient of thermal expansion and shrinks as it matures. All concrete structures crack to some extent, due to shrinkage and tension. Concrete that is subjected to long-duration forces is prone to creep.

Tests can be performed to ensure that the properties of concrete correspond to specifications for the application.

Compression testing of a concrete cylinder Concrete Compression Testing.jpg
Compression testing of a concrete cylinder

The ingredients affect the strengths of the material. Concrete strength values are usually specified as the lower-bound compressive strength of either a cylindrical or cubic specimen as determined by standard test procedures.

The strengths of concrete is dictated by its function. Very low-strength—14 MPa (2,000 psi) or less—concrete may be used when the concrete must be lightweight. [91] Lightweight concrete is often achieved by adding air, foams, or lightweight aggregates, with the side effect that the strength is reduced. For most routine uses, 20 to 32 MPa (2,900 to 4,600 psi) concrete is often used. 40 MPa (5,800 psi) concrete is readily commercially available as a more durable, although more expensive, option. Higher-strength concrete is often used for larger civil projects. [92] Strengths above 40 MPa (5,800 psi) are often used for specific building elements. For example, the lower floor columns of high-rise concrete buildings may use concrete of 80 MPa (11,600 psi) or more, to keep the size of the columns small. Bridges may use long beams of high-strength concrete to lower the number of spans required. [93] [94] Occasionally, other structural needs may require high-strength concrete. If a structure must be very rigid, concrete of very high strength may be specified, even much stronger than is required to bear the service loads. Strengths as high as 130 MPa (18,900 psi) have been used commercially for these reasons. [93]

Energy efficiency

The cement produced for making concrete accounts for about 8% of worldwide CO2 emissions per year (compared to, e.g., global aviation at 1.9%). [95] [96] The two largest sources of CO2 are produced by the cement manufacturing process, arising from (1) the decarbonation reaction of limestone in the cement kiln (T ≈ 950 °C), and (2) from the combustion of fossil fuel to reach the sintering temperature (T ≈ 1450 °C) of cement clinker in the kiln. The energy required for extracting, crushing, and mixing the raw materials (construction aggregates used in the concrete production, and also limestone and clay feeding the cement kiln) is lower. Energy requirement for transportation of ready-mix concrete is also lower because it is produced nearby the construction site from local resources, typically manufactured within 100 kilometers of the job site. [97] The overall embodied energy of concrete at roughly 1 to 1.5 megajoules per kilogram is therefore lower than for many structural and construction materials. [98]

Once in place, concrete offers a great energy efficiency over the lifetime of a building. [99] Concrete walls leak air far less than those made of wood frames. [100] Air leakage accounts for a large percentage of energy loss from a home. The thermal mass properties of concrete increase the efficiency of both residential and commercial buildings. By storing and releasing the energy needed for heating or cooling, concrete's thermal mass delivers year-round benefits by reducing temperature swings inside and minimizing heating and cooling costs. [101] While insulation reduces energy loss through the building envelope, thermal mass uses walls to store and release energy. Modern concrete wall systems use both external insulation and thermal mass to create an energy-efficient building. Insulating concrete forms (ICFs) are hollow blocks or panels made of either insulating foam or rastra that are stacked to form the shape of the walls of a building and then filled with reinforced concrete to create the structure.

Fire safety

Boston City Hall (1968) is a Brutalist design constructed largely of precast and poured in place concrete. Boston City Hall - Boston, MA - DSC04704 (cropped).JPG
Boston City Hall (1968) is a Brutalist design constructed largely of precast and poured in place concrete.

Concrete buildings are more resistant to fire than those constructed using steel frames, since concrete has lower heat conductivity than steel and can thus last longer under the same fire conditions. Concrete is sometimes used as a fire protection for steel frames, for the same effect as above. Concrete as a fire shield, for example Fondu fyre, can also be used in extreme environments like a missile launch pad.

Options for non-combustible construction include floors, ceilings and roofs made of cast-in-place and hollow-core precast concrete. For walls, concrete masonry technology and Insulating Concrete Forms (ICFs) are additional options. ICFs are hollow blocks or panels made of fireproof insulating foam that are stacked to form the shape of the walls of a building and then filled with reinforced concrete to create the structure.

Concrete also provides good resistance against externally applied forces such as high winds, hurricanes, and tornadoes owing to its lateral stiffness, which results in minimal horizontal movement. However, this stiffness can work against certain types of concrete structures, particularly where a relatively higher flexing structure is required to resist more extreme forces.

Earthquake safety

As discussed above, concrete is very strong in compression, but weak in tension. Larger earthquakes can generate very large shear loads on structures. These shear loads subject the structure to both tensile and compressional loads. Concrete structures without reinforcement, like other unreinforced masonry structures, can fail during severe earthquake shaking. Unreinforced masonry structures constitute one of the largest earthquake risks globally. [102] These risks can be reduced through seismic retrofitting of at-risk buildings, (e.g. school buildings in Istanbul, Turkey). [103]

Construction with concrete

The City Court Building in Buffalo, New York Buffalo City Court Building, 1971-74, Pfohl, Roberts and Biggie (8448022295).jpg
The City Court Building in Buffalo, New York

Concrete is one of the most durable building materials. It provides superior fire resistance compared with wooden construction and gains strength over time. Structures made of concrete can have a long service life. [104] Concrete is used more than any other artificial material in the world. [105] As of 2006, about 7.5 billion cubic meters of concrete are made each year, more than one cubic meter for every person on Earth. [106]

Reinforced concrete

Christ the Redeemer statue in Rio de Janeiro, Brazil. It is made of reinforced concrete clad in a mosaic of thousands of triangular soapstone tiles. O Cristo Redentor.JPG
Christ the Redeemer statue in Rio de Janeiro, Brazil. It is made of reinforced concrete clad in a mosaic of thousands of triangular soapstone tiles.

The use of reinforcement, in the form of iron was introduced in the 1850s by French industrialist François Coignet, and it was not until the 1880s that German civil engineer G. A. Wayss used steel as reinforcement. Concrete is a relatively brittle material that is strong under compression but less in tension. Plain, unreinforced concrete is unsuitable for many structures as it is relatively poor at withstanding stresses induced by vibrations, wind loading, and so on. Hence, to increase its overall strength, steel rods, wires, mesh or cables can be embedded in concrete before it is set. This reinforcement, often known as rebar, resists tensile forces. [108]

Reinforced concrete (RC) is a versatile composite and one of the most widely used materials in modern construction. It is made up of different constituent materials with very different properties that complement each other. In the case of reinforced concrete, the component materials are almost always concrete and steel. These two materials form a strong bond together and are able to resist a variety of applied forces, effectively acting as a single structural element. [109]

Reinforced concrete can be precast or cast-in-place (in situ) concrete, and is used in a wide range of applications such as; slab, wall, beam, column, foundation, and frame construction. Reinforcement is generally placed in areas of the concrete that are likely to be subject to tension, such as the lower portion of beams. Usually, there is a minimum of 50 mm cover, both above and below the steel reinforcement, to resist spalling and corrosion which can lead to structural instability. [108] Other types of non-steel reinforcement, such as Fibre-reinforced concretes are used for specialized applications, predominately as a means of controlling cracking. [109]

Precast concrete

Precast concrete is concrete which is cast in one place for use elsewhere and is a mobile material. The largest part of precast production is carried out in the works of specialist suppliers, although in some instances, due to economic and geographical factors, scale of product or difficulty of access, the elements are cast on or adjacent to the construction site. [110] Precasting offers considerable advantages because it is carried out in a controlled environment, protected from the elements, but the downside of this is the contribution to greenhouse gas emission from transportation to the construction site. [109]

Advantages to be achieved by employing precast concrete: [110]

Mass structures

Aerial photo of reconstruction at Taum Sauk (Missouri) pumped storage facility in late November 2009. After the original reservoir failed, the new reservoir was made of roller-compacted concrete. UserKTrimble-AP Taum Sauk Reservoir UnderConstruction Nov 22 2009 crop1.jpg
Aerial photo of reconstruction at Taum Sauk (Missouri) pumped storage facility in late November 2009. After the original reservoir failed, the new reservoir was made of roller-compacted concrete.

Due to cement's exothermic chemical reaction while setting up, large concrete structures such as dams, navigation locks, large mat foundations, and large breakwaters generate excessive heat during hydration and associated expansion. To mitigate these effects, post-cooling [111] is commonly applied during construction. An early example at Hoover Dam used a network of pipes between vertical concrete placements to circulate cooling water during the curing process to avoid damaging overheating. Similar systems are still used; depending on volume of the pour, the concrete mix used, and ambient air temperature, the cooling process may last for many months after the concrete is placed. Various methods also are used to pre-cool the concrete mix in mass concrete structures. [111]

Another approach to mass concrete structures that minimizes cement's thermal by-product is the use of roller-compacted concrete, which uses a dry mix which has a much lower cooling requirement than conventional wet placement. It is deposited in thick layers as a semi-dry material then roller compacted into a dense, strong mass.

Surface finishes

Black basalt polished concrete floor Smpolishedconcrete2.jpg
Black basalt polished concrete floor

Raw concrete surfaces tend to be porous and have a relatively uninteresting appearance. Many finishes can be applied to improve the appearance and preserve the surface against staining, water penetration, and freezing.

Examples of improved appearance include stamped concrete where the wet concrete has a pattern impressed on the surface, to give a paved, cobbled or brick-like effect, and may be accompanied with coloration. Another popular effect for flooring and table tops is polished concrete where the concrete is polished optically flat with diamond abrasives and sealed with polymers or other sealants.

Other finishes can be achieved with chiseling, or more conventional techniques such as painting or covering it with other materials.

The proper treatment of the surface of concrete, and therefore its characteristics, is an important stage in the construction and renovation of architectural structures. [112]

Prestressed structures

Stylized cacti decorate a sound/retaining wall in Scottsdale, Arizona Scott System cacti.jpg
Stylized cacti decorate a sound/retaining wall in Scottsdale, Arizona

Prestressed concrete is a form of reinforced concrete that builds in compressive stresses during construction to oppose tensile stresses experienced in use. This can greatly reduce the weight of beams or slabs, by better distributing the stresses in the structure to make optimal use of the reinforcement. For example, a horizontal beam tends to sag. Prestressed reinforcement along the bottom of the beam counteracts this. In pre-tensioned concrete, the prestressing is achieved by using steel or polymer tendons or bars that are subjected to a tensile force prior to casting, or for post-tensioned concrete, after casting.

There are two different systems being used: [109]

More than 55,000 miles (89,000 km) of highways in the United States are paved with this material. Reinforced concrete, prestressed concrete and precast concrete are the most widely used types of concrete functional extensions in modern days. For more information see Brutalist architecture.


Once mixed, concrete is typically transported to the place where it is intended to become a structural item. Various methods of transportation and placement are used depending on the distances involve, quantity needed, and other details of application. Large amounts are often transported by truck, poured free under gravity or through a tremie, or pumped through a pipe. Smaller amounts may be carried in a skip (a metal container which can be tilted or opened to release the contents, usually transported by crane or hoist), or wheelbarrow, or carried in toggle bags for manual placement underwater.

Cold weather placement

Pohjolatalo, an office building made of concrete in the city center of Kouvola in Kymenlaakso, Finland Pohjolatalo Kouvola 001.jpg
Pohjolatalo, an office building made of concrete in the city center of Kouvola in Kymenlaakso, Finland

Extreme weather conditions (extreme heat or cold; windy conditions, and humidity variations) can significantly alter the quality of concrete. Many precautions are observed in cold weather placement. [113] Low temperatures significantly slow the chemical reactions involved in hydration of cement, thus affecting the strength development. Preventing freezing is the most important precaution, as formation of ice crystals can cause damage to the crystalline structure of the hydrated cement paste. If the surface of the concrete pour is insulated from the outside temperatures, the heat of hydration will prevent freezing.

The American Concrete Institute (ACI) definition of cold weather placement, ACI 306, [114] is:

  • A period when for more than three successive days the average daily air temperature drops below 40 °F (~ 4.5 °C), and
  • Temperature stays below 50 °F (10 °C) for more than one-half of any 24-hour period.

In Canada, where temperatures tend to be much lower during the cold season, the following criteria are used by CSA A23.1:

  • When the air temperature is ≤ 5 °C, and
  • When there is a probability that the temperature may fall below 5 °C within 24 hours of placing the concrete.

The minimum strength before exposing concrete to extreme cold is 500 psi (3.4 MPa). CSA A 23.1 specified a compressive strength of 7.0 MPa to be considered safe for exposure to freezing.

Underwater placement

Assembled tremie placing concrete underwater Tremie operation.png
Assembled tremie placing concrete underwater

Concrete may be placed and cured underwater. Care must be taken in the placement method to prevent washing out the cement. Underwater placement methods include the tremie, pumping, skip placement, manual placement using toggle bags, and bagwork. [115]

Grouted aggregate is an alternative method of forming a concrete mass underwater, where the forms are filled with coarse aggregate and the voids then completely filled with pumped grout. [115]


Concrete roads are more fuel efficient to drive on, [116] more reflective and last significantly longer than other paving surfaces, yet have a much smaller market share than other paving solutions. Modern-paving methods and design practices have changed the economics of concrete paving, so that a well-designed and placed concrete pavement will be less expensive on initial costs and significantly less expensive over the life cycle. Another major benefit is that pervious concrete can be used, which eliminates the need to place storm drains near the road, and reducing the need for slightly sloped roadway to help rainwater to run off. No longer requiring discarding rainwater through use of drains also means that less electricity is needed (more pumping is otherwise needed in the water-distribution system), and no rainwater gets polluted as it no longer mixes with polluted water. Rather, it is immediately absorbed by the ground.[ citation needed ]

Environment, health and safety

The manufacture and use of concrete produce a wide range of environmental, economic and social impacts.

Concrete, cement and the environment

A major component of concrete is cement, a fine powder used mainly to bind sand and coarser aggregates together in concrete. Although a variety of cement types exist, the most common is "Portland cement", which is produced by mixing clinker with smaller quantities of other additives such as gypsum and ground limestone. The production of clinker, the main constituent of cement, is responsible for the bulk of the sector's greenhouse gas emissions, including both energy intensity and process emissions. [117]

The cement industry is one of the three primary producers of carbon dioxide, a major greenhouse gas – the other two being energy production and transportation industries. On average, every tonne of cement produced releases one tonne of CO2 into the atmosphere. Pioneer cement manufacturers have claimed to reach lower carbon intensities, with 590 kg of CO2eq per tonne of cement produced. [118] The emissions are due to combustion and calcination processes, [119] which roughly account for 40% and 60% of the greenhouse gases, respectively. Considering that cement is only a fraction of the constituents of concrete, it is estimated that a tonne of concrete is responsible for emitting about 100–200 kg of CO2. [120] [121] Every year more than 10 billion tonnes of concrete are used worldwide. [121] In the coming years, large quantities of concrete will continue to be used, and the mitigation of CO2 emissions from the sector will be even more critical.

Concrete is used to create hard surfaces that contribute to surface runoff, which can cause heavy soil erosion, water pollution, and flooding, but conversely can be used to divert, dam, and control flooding. Concrete dust released by building demolition and natural disasters can be a major source of dangerous air pollution. Concrete is a contributor to the urban heat island effect, though less so than asphalt.

Concrete and climate change mitigation

Reducing the cement clinker content might have positive effects on the environmental life-cycle assessment of concrete. Some research work on reducing the cement clinker content in concrete has already been carried out. However, there exist different research strategies. Often replacement of some clinker for large amounts of slag or fly ash was investigated based on conventional concrete technology. This could lead to a waste of scarce raw materials such as slag and fly ash. The aim of other research activities is the efficient use of cement and reactive materials like slag and fly ash in concrete based on a modified mix design approach. [122]

An environmental investigation found that the embodied carbon of a precast concrete facade can be reduced by 50% when using the presented fiber reinforced high performance concrete in place of typical reinforced concrete cladding. [123]

Studies have been conducted about commercialization of low-carbon concretes. Life cycle assessment (LCA) of low-carbon concrete was investigated according to the ground granulated blast-furnace slag (GGBS) and fly ash (FA) replacement ratios. Global warming potential (GWP) of GGBS decreased by 1.1 kg CO2 eq/m3, while FA decreased by 17.3 kg CO2 eq/m3 when the mineral admixture replacement ratio was increased by 10%. This study also compared the compressive strength properties of binary blended low-carbon concrete according to the replacement ratios, and the applicable range of mixing proportions was derived. [124]

Researchers at University of Auckland are working on utilizing biochar in concrete applications to reduce carbon emissions during concrete production and to improve strength. [125]

Concrete and climate change adaptation

High-performance building materials will be particularly important for enhancing resilience, including for flood defenses and critical-infrastructure protection. Risks to infrastructure and cities posed by extreme weather events are especially serious for those places exposed to flood and hurricane damage, but also where residents need protection from extreme summer temperatures. Traditional concrete can come under strain when exposed to humidity and higher concentrations of atmospheric CO2. While concrete is likely to remain important in applications where the environment is challenging, novel, smarter and more adaptable materials are also needed. [121] [126]

Concrete – health and safety

Recycled crushed concrete, to be reused as granular fill, is loaded into a semi-dump truck Crushed Concrete Granular Fill.jpg
Recycled crushed concrete, to be reused as granular fill, is loaded into a semi-dump truck

Grinding of concrete can produce hazardous dust. Exposure to cement dust can lead to issues such as silicosis, kidney disease, skin irritation and similar effects. The U.S. National Institute for Occupational Safety and Health in the United States recommends attaching local exhaust ventilation shrouds to electric concrete grinders to control the spread of this dust. In addition, the Occupational Safety and Health Administration (OSHA) has placed more stringent regulations on companies whose workers regularly come into contact with silica dust. An updated silica rule, which OSHA put into effect 23 September 2017 for construction companies, restricted the amount of breathable crystalline silica workers could legally come into contact with to 50 micro grams per cubic meter of air per 8-hour workday. That same rule went into effect 23 June 2018 for general industry, hydraulic fracturing and maritime. That deadline was extended to 23 June 2021 for engineering controls in the hydraulic fracturing industry. Companies which fail to meet the tightened safety regulations can face financial charges and extensive penalties. The presence of some substances in concrete, including useful and unwanted additives, can cause health concerns due to toxicity and radioactivity. Fresh concrete (before curing is complete) is highly alkaline and must be handled with proper protective equipment.

Circular economy

Concrete is an excellent material with which to make long-lasting and energy-efficient buildings. However, even with good design, human needs change and potential waste will be generated. [127]

End-of-life: concrete degradation and waste

The Tunkhannock Viaduct in northeastern Pennsylvania opened in 1915 and is still in regular use today Tunkhannock Viaduct, NE Pennsylvania USA.jpg
The Tunkhannock Viaduct in northeastern Pennsylvania opened in 1915 and is still in regular use today

Concrete can be damaged by many processes, such as the expansion of corrosion products of the steel reinforcement bars, freezing of trapped water, fire or radiant heat, aggregate expansion, sea water effects, bacterial corrosion, leaching, erosion by fast-flowing water, physical damage and chemical damage (from carbonatation, chlorides, sulfates and distillate water). [128] The micro fungi Aspergillus alternaria and Cladosporium were able to grow on samples of concrete used as a radioactive waste barrier in the Chernobyl reactor; leaching aluminium, iron, calcium, and silicon. [129]

Concrete may be considered waste according to the European Commission decision of 2014/955/EU for the List of Waste under the codes: 17 (construction and demolition wastes, including excavated soil from contaminated sites) 01 (concrete, bricks, tiles and ceramics), 01 (concrete), and 17.01.06* (mixtures of, separate fractions of concrete, bricks, tiles and ceramics containing hazardous substances), and 17.01.07 (mixtures of, separate fractions of concrete, bricks, tiles and ceramics other than those mentioned in 17.01.06). [130] It is estimated that in 2018 the European Union generated 371,910 thousand tons of mineral waste from construction and demolition, and close to 4% of this quantity is considered hazardous. Germany, France and the United Kingdom were the top three polluters with 86,412 thousand tons, 68,976 and 68,732 thousand tons of construction waste generation, respectively. [131]

Currently, there is not an End-of-Waste criteria for concrete materials in the EU. However, different sectors have been proposing alternatives for concrete waste and re purposing it as a secondary raw material in various applications, including concrete manufacturing itself. [132]

Reuse of concrete

Reuse of blocks in original form, or by cutting into smaller blocks, has even less environmental impact; however, only a limited market currently exists. Improved building designs that allow for slab reuse and building transformation without demolition could increase this use. Hollow core concrete slabs are easy to dismantle and the span is normally constant, making them good for reuse. [127]

Other cases of re-use are possible with pre-cast concrete pieces: through selective demolition, such pieces can be disassembled and collected for further use in other building sites. Studies show that back-building and remounting plans for building units (i.e., re-use of pre-fabricated concrete) is an alternative for a kind of construction which protects resources and saves energy. Especially long-living, durable, energy-intensive building materials, such as concrete, can be kept in the life-cycle longer through recycling. Prefabricated constructions are the prerequisites for constructions necessarily capable of being taken apart. In the case of optimal application in the building carcass, savings in costs are estimated in 26%, a lucrative complement to new building methods. However, this depends on several courses to be set. [133] The viability of this alternative has to be studied as the logistics associated with transporting heavy pieces of concrete can impact the operation financially and also increase the carbon footprint of the project. Also, ever changing regulations on new buildings worldwide may require higher quality standards for construction elements and inhibit the use of old elements which may be classified as obsolete.

Recycling of concrete

Concrete recycling is an increasingly common method for disposing of concrete structures. Concrete debris were once routinely shipped to landfills for disposal, but recycling is increasing due to improved environmental awareness, governmental laws and economic benefits.

Contrary to general belief, concrete recovery is achievable – concrete can be crushed and reused as aggregate in new projects. [127]

Recycling or recovering concrete reduces natural resource exploitation and associated transportation costs, and reduces waste landfill. However, it has little impact on reducing greenhouse gas emissions as most emissions occur when cement is made, and cement alone cannot be recycled. At present, most recovered concrete is used for road sub-base and civil engineering projects. From a sustainability viewpoint, these relatively low-grade uses currently provide the optimal outcome. [134]

The recycling process can be done in situ, with mobile plants, or in specific recycling units. The input material can be returned concrete which is fresh (wet) from ready-mix trucks, production waste at a pre-cast production facility, or waste from construction and demolition. The most significant source is demolition waste, preferably pre-sorted from selective demolition processes. [127]

By far the most common method for recycling dry and hardened concrete involves crushing. Mobile sorters and crushers are often installed on construction sites to allow on-site processing. In other situations, specific processing sites are established, which are usually able to produce higher quality aggregate. Screens are used to achieve desired particle size, and remove dirt, foreign particles and fine material from the coarse aggregate. [135] [127]

Chloride and sulfates are undesired contaminants originated from soil and weathering and can provoke corrosion problems on aluminium and steel structures. [135] The final product, Recycled Concrete Aggregate (RCA), presents interesting properties such as: angular shape, rougher surface, lower specific gravity (20%), higher water absorption, and pH greater than 11 – this elevated pH increases the risk of alkali reactions. [127]

The lower density of RCA usually Increases project efficiency and improve job cost – recycled concrete aggregates yield more volume by weight (up to 15%). [134] The physical properties of coarse aggregates made from crushed demolition concrete make it the preferred material for applications such as road base and sub-base. This is because recycled aggregates often have better compaction properties and require less cement for sub-base uses. Furthermore, it is generally cheaper to obtain than virgin material. [127]

Applications of recycled concrete aggregate

The main commercial applications of the final recycled concrete aggregate are:

  • Aggregate base course (road base), or the untreated aggregates used as foundation for roadway pavement, is the underlying layer (under pavement surfacing) which forms a structural foundation for paving. To this date this has been the most popular application for RCA due to technical-economic aspects. [136]
  • Aggregate for ready-mix concrete, by replacing from 10 to 45% of the natural aggregates in the concrete mix with a blend of cement, sand and water. Some concept buildings are showing the progress of this field. Because the RCA itself contains cement, the ratios of the mix have to be adjusted to achieve desired structural requirements such as workability, strength and water absorption. [127]
  • Soil Stabilization, with the incorporation of recycled aggregate, lime, or fly ash into marginal quality subgrade material used to enhance the load bearing capacity of that subgrade. [136]
  • Pipe bedding: serving as a stable bed or firm foundation in which to lay underground utilities. Some countries' regulations prohibit the use of RCA and other construction and demolition wastes in filtration and drainage beds due to potential contamination with chromium and pH-value impacts. [127] [136]
  • Landscape Materials: to promote green architecture. To date, recycled concrete aggregate has been used as boulder/stacked rock walls, underpass abutment structures, erosion structures, water features, retaining walls, and more. [136]

Cradle-to-cradle challenges

Circularity of Concrete: Cradle-to-Cradle design Circular Economy of concrete.jpg
Circularity of Concrete: Cradle-to-Cradle design

The applications developed for RCA so far are not exhaustive, and many more uses are to be developed as regulations, institutions and norms find ways to accommodate construction and demolition waste as secondary raw materials in a safe and economic way. However, considering the purpose of having a circularity of resources in the concrete life cycle, the only application of RCA that could be considered as recycling of concrete is the replacement of natural aggregates on concrete mixes. All the other applications would fall under the category of downcycling. It is estimated that even near complete recovery of concrete from construction and demolition waste will only supply about 20% of total aggregate needs in the developed world. [127]

The path towards circularity goes beyond concrete technology itself, depending on multilateral advances in the cement industry, research and development of alternative materials, building design and management, and demolition as well as conscious use of spaces in urban areas to reduce consumption.

World records

The world record for the largest concrete pour in a single project is the Three Gorges Dam in Hubei Province, China by the Three Gorges Corporation. The amount of concrete used in the construction of the dam is estimated at 16 million cubic meters over 17 years. The previous record was 12.3 million cubic meters held by Itaipu hydropower station in Brazil. [137] [138] [139]

The world record for concrete pumping was set on 7 August 2009 during the construction of the Parbati Hydroelectric Project, near the village of Suind, Himachal Pradesh, India, when the concrete mix was pumped through a vertical height of 715 m (2,346 ft). [140] [141]

The Polavaram dam works in Andhra Pradesh on 6 January 2019 entered the Guinness World Records by pouring 32,100 cubic metres of concrete in 24 hours. [142] The world record for the largest continuously poured concrete raft was achieved in August 2007 in Abu Dhabi by contracting firm Al Habtoor-CCC Joint Venture and the concrete supplier is Unibeton Ready Mix. [143] [144] The pour (a part of the foundation for the Abu Dhabi's Landmark Tower) was 16,000 cubic meters of concrete poured within a two-day period. [145] The previous record, 13,200 cubic meters poured in 54 hours despite a severe tropical storm requiring the site to be covered with tarpaulins to allow work to continue, was achieved in 1992 by joint Japanese and South Korean consortiums Hazama Corporation and the Samsung C&T Corporation for the construction of the Petronas Towers in Kuala Lumpur, Malaysia. [146]

The world record for largest continuously poured concrete floor was completed 8 November 1997, in Louisville, Kentucky by design-build firm EXXCEL Project Management. The monolithic placement consisted of 225,000 square feet (20,900 m2) of concrete placed in 30 hours, finished to a flatness tolerance of FF 54.60 and a levelness tolerance of FL 43.83. This surpassed the previous record by 50% in total volume and 7.5% in total area. [147] [148]

The record for the largest continuously placed underwater concrete pour was completed 18 October 2010, in New Orleans, Louisiana by contractor C. J. Mahan Construction Company, LLC of Grove City, Ohio. The placement consisted of 10,251 cubic yards of concrete placed in 58.5 hours using two concrete pumps and two dedicated concrete batch plants. Upon curing, this placement allows the 50,180-square-foot (4,662 m2) cofferdam to be dewatered approximately 26 feet (7.9 m) below sea level to allow the construction of the Inner Harbor Navigation Canal Sill & Monolith Project to be completed in the dry. [149]

See also

Further reading

Related Research Articles

<span class="mw-page-title-main">Cement</span> Hydraulic binder used in the composition of mortar and concrete

A cement is a binder, a chemical substance used for construction that sets, hardens, and adheres to other materials to bind them together. Cement is seldom used on its own, but rather to bind sand and gravel (aggregate) together. Cement mixed with fine aggregate produces mortar for masonry, or with sand and gravel, produces concrete. Concrete is the most widely used material in existence and is behind only water as the planet's most-consumed resource.

<span class="mw-page-title-main">Mortar (masonry)</span> Workable paste which hardens to bind building blocks

Mortar is a workable paste which hardens to bind building blocks such as stones, bricks, and concrete masonry units, to fill and seal the irregular gaps between them, spread the weight of them evenly, and sometimes to add decorative colors or patterns to masonry walls. In its broadest sense, mortar includes pitch, asphalt, and soft mud or clay, as those used between mud bricks, as well as cement mortar. The word "mortar" comes from Old French mortier, "builder's mortar, plaster; bowl for mixing." (13c.).

<span class="mw-page-title-main">Asphalt concrete</span> Composite material used for paving

Asphalt concrete is a composite material commonly used to surface roads, parking lots, airports, and the core of embankment dams. Asphalt mixtures have been used in pavement construction since the beginning of the twentieth century. It consists of mineral aggregate bound together with bitumen, laid in layers, and compacted. The process was refined and enhanced by Belgian-American inventor Edward De Smedt.

<span class="mw-page-title-main">Building material</span> Material which is used for construction purposes

Building material is material used for construction. Many naturally occurring substances, such as clay, rocks, sand, wood, and even twigs and leaves, have been used to construct buildings. Apart from naturally occurring materials, many man-made products are in use, some more and some less synthetic. The manufacturing of building materials is an established industry in many countries and the use of these materials is typically segmented into specific specialty trades, such as carpentry, insulation, plumbing, and roofing work. They provide the make-up of habitats and structures including homes.

<span class="mw-page-title-main">Efflorescence</span> Migration of a salt to the surface of a porous material

In chemistry, efflorescence is the migration of a salt to the surface of a porous material, where it forms a coating. The essential process involves the dissolving of an internally held salt in water, or occasionally in another solvent. The water, with the salt now held in solution, migrates to the surface, then evaporates, leaving a coating of the salt.

<span class="mw-page-title-main">Ready-mix concrete</span> Concrete that is manufactured in a batch plant, according to a set engineered mix design

Ready-mix concrete (RMC) is concrete that is manufactured in a batch plant, according to each specific job requirement, then delivered to the job site "ready to use".

<span class="mw-page-title-main">Concrete recycling</span> Re-use of rubble from demolished concrete structures

Concrete recycling is the use of rubble from demolished concrete structures. Recycling is cheaper and more ecological than trucking rubble to a landfill. Crushed rubble can be used for road gravel, revetments, retaining walls, landscaping gravel, or raw material for new concrete. Large pieces can be used as bricks or slabs, or incorporated with new concrete into structures, a material called urbanite.

Engineered Cementitious Composite (ECC), also called Strain Hardening Cement-based Composites (SHCC) or more popularly as bendable concrete, is an easily molded mortar-based composite reinforced with specially selected short random fibers, usually polymer fibers. Unlike regular concrete, ECC has a tensile strain capacity in the range of 3–7%, compared to 0.01% for ordinary portland cement (OPC) paste, mortar or concrete. ECC therefore acts more like a ductile metal material rather than a brittle glass material, leading to a wide variety of applications.

Metakaolin is the anhydrous calcined form of the clay mineral kaolinite. Minerals that are rich in kaolinite are known as china clay or kaolin, traditionally used in the manufacture of porcelain. The particle size of metakaolin is smaller than cement particles, but not as fine as silica fume.

<span class="mw-page-title-main">Ground granulated blast-furnace slag</span> Granular slag by-product of iron and steel-making used as supplementary cementitious material

Ground granulated blast-furnace slag is obtained by quenching molten iron slag from a blast furnace in water or steam, to produce a glassy, granular product that is then dried and ground into a fine powder. Ground granulated blast furnace slag is a latent hydraulic binder forming calcium silicate hydrates (C-S-H) after contact with water. It is a strength-enhancing compound improving the durability of concrete. It is a component of metallurgic cement. Its main advantage is its slow release of hydration heat, allowing limitation of the temperature increase in massive concrete components and structures during cement setting and concrete curing, or to cast concrete during hot summer.

<span class="mw-page-title-main">Construction aggregate</span> Coarse to fine grain rock materials used in concrete

Construction aggregate, or simply aggregate, is a broad category of coarse- to medium-grained particulate material used in construction, including sand, gravel, crushed stone, slag, recycled concrete and geosynthetic aggregates. Aggregates are the most mined materials in the world. Aggregates are a component of composite materials such as concrete and asphalt; the aggregate serves as reinforcement to add strength to the overall composite material. Due to the relatively high hydraulic conductivity value as compared to most soils, aggregates are widely used in drainage applications such as foundation and French drains, septic drain fields, retaining wall drains, and roadside edge drains. Aggregates are also used as base material under foundations, roads, and railroads. In other words, aggregates are used as a stable foundation or road/rail base with predictable, uniform properties, or as a low-cost extender that binds with more expensive cement or asphalt to form concrete. Although most kinds of aggregate require a form of binding agent, there are types of self-binding aggregate which do not require any form of binding agent.

<span class="mw-page-title-main">Pozzolan</span> Siliceous volcanic ashes commonly used as supplementary cementitious material

Pozzolans are a broad class of siliceous and aluminous materials which, in themselves, possess little or no cementitious value but which will, in finely divided form and in the presence of water, react chemically with calcium hydroxide (Ca(OH)2) at ordinary temperature to form compounds possessing cementitious properties. The quantification of the capacity of a pozzolan to react with calcium hydroxide and water is given by measuring its pozzolanic activity. Pozzolana are naturally occurring pozzolans of volcanic origin.

Self-consolidating concrete or self-compacting concrete (SCC) is a concrete mix which has a low yield stress, high deformability, good segregation resistance, and moderate viscosity.

<span class="mw-page-title-main">Types of concrete</span> Building material consisting of aggregates cemented by a binder

Concrete is produced in a variety of compositions, finishes and performance characteristics to meet a wide range of needs.

Concrete has relatively high compressive strength, but significantly lower tensile strength. The compressive strength is typically controlled with the ratio of water to cement when forming the concrete, and tensile strength is increased by additives, typically steel, to create reinforced concrete. In other words we can say concrete is made up of sand, ballast, cement and water.

<span class="mw-page-title-main">Geopolymer cement</span> Aluminosilicate-based cement with a low-carbon footprint

Geopolymer cement is a binding system that hardens at room temperature.

Sulfur concrete, sometimes named thioconcrete or sulfurcrete, is a composite construction material, composed mainly of sulfur and aggregate. Cement and water, important compounds in normal concrete, are not part of sulfur concrete. The concrete is heated above the melting point of elemental sulfur at ca. 140 °C (284 °F) in a ratio of between 12% and 25% sulfur, the rest being aggregate.

The environmental impact of concrete, its manufacture, and its applications, are complex, driven in part by direct impacts of construction and infrastructure, as well as by CO2 emissions; between 4-8% of total global CO2 emissions come from concrete. Many depend on circumstances. A major component is cement, which has its own environmental and social impacts and contributes largely to those of concrete.

<span class="mw-page-title-main">Self-healing concrete</span>

Self-healing concrete is characterized as the capability of concrete to fix its cracks on its own autogenously or autonomously. It not only seals the cracks but also partially or entirely recovers the mechanical properties of the structural elements. This kind of concrete is also known as self-repairing concrete. Because concrete has a poor tensile strength compared to other building materials, it often develops cracks in the surface. These cracks reduce the durability of the concrete because they facilitate the flow of liquids and gases that may contain harmful compounds. If microcracks expand and reach the reinforcement, not only will the concrete itself be susceptible to attack, but so will the reinforcement steel bars. Therefore, it is essential to limit the crack's width and repair it as quickly as feasible. Self-healing concrete would not only make the material more sustainable, but it would also contribute to an increase in the service life of concrete structures and make the material more durable and environmentally friendly.

<span class="mw-page-title-main">3D concrete printing</span>

3D concrete printing, or simply concrete printing, refers to digital fabrication processes for cementitious materials based on one of several different 3D printing technologies. 3D printed concrete eliminates the need for formwork, reducing material waste and allowing for greater geometric freedom in complex structures. With recent developments in mix design and 3D printing technology over the last decade, 3D concrete printing has grown exponentially since its emergence in the 1990s. Architectural and structural applications of 3D-printed concrete include the production of building blocks, building modules, street furniture, pedestrian bridges, and low-rise residential structures.


  1. Gagg, Colin R. (1 May 2014). "Cement and concrete as an engineering material: An historic appraisal and case study analysis". Engineering Failure Analysis. 40: 114–140. doi:10.1016/j.engfailanal.2014.02.004. ISSN   1350-6307.
  2. Crow, James Mitchell (March 2008). "The concrete conundrum" (PDF). Chemistry World: 62–66. Archived (PDF) from the original on 9 October 2022.
  3. "Scientific Principles". Retrieved 24 May 2023.
  4. Li, Zongjin (2011). Advanced concrete technology. John Wiley & Sons. ISBN   978-0470902431.
  5. Industrial Resources Council (2008). "Portland Cement Concrete". Retrieved 15 June 2018.
  6. National Highway Institute. "Portland Cement Concrete Materials" (PDF). Federal Highway Administration. Archived (PDF) from the original on 9 October 2022.
  7. Allen, Edward; Iano, Joseph (2013). Fundamentals of building construction : materials and methods (Sixth ed.). Hoboken: John Wiley & Sons. p. 314. ISBN   978-1118420867. OCLC   835621943.
  8. "concretus". Latin Lookup. Archived from the original on 12 May 2013. Retrieved 1 October 2012.
  9. 1 2 Gromicko, Nick; Shepard, Kenton (2016). "The History of Concrete". International Association of Certified Home Inspectors, Inc. Retrieved 27 December 2018.
  10. Moore, David (6 October 2014). "Roman Concrete Research". Archived from the original on 6 October 2014. Retrieved 13 August 2022.
  11. Heinrich Schliemann; Wilhelm Dörpfeld; Felix Adler (1885). Tiryns: The Prehistoric Palace of the Kings of Tiryns, the Results of the Latest Excavations. New York: Charles Scribner's Sons. pp.  190, 203–204, 215.
  12. Sparavigna, Amelia Carolina (2011). "Ancient concrete works". arXiv: 1110.5230 [physics.pop-ph].
  13. Jacobsen T and Lloyd S, (1935) "Sennacherib's Aqueduct at Jerwan," Oriental Institute Publications 24, Chicago University Press
  14. Stella L. Marusin (1 January 1996). "Ancient Concrete Structures". Concrete International. 18 (1): 56–58.
  15. "The History of Concrete". Dept. of Materials Science and Engineering, University of Illinois, Urbana-Champaign. Archived from the original on 27 November 2012. Retrieved 8 January 2013.
  16. Lancaster, Lynne (2005). Concrete Vaulted Construction in Imperial Rome. Innovations in Context. Cambridge University Press. ISBN   978-0511160684.
  17. Moore, David (1999). "The Pantheon". Archived from the original on 1 October 2011. Retrieved 26 September 2011.
  18. D.S. Robertson (1969). Greek and Roman Architecture, Cambridge, p. 233
  19. Cowan, Henry J. (1977). The master builders : a history of structural and environmental design from ancient Egypt to the nineteenth century. New York: Wiley. ISBN   0-471-02740-5. OCLC   2896326.
  20. "CIVL 1101". Archived from the original on 27 February 2017.
  21. Robert Mark, Paul Hutchinson: "On the Structure of the Roman Pantheon", Art Bulletin, Vol. 68, No. 1 (1986), p. 26, fn. 5
  22. Kwan, Stephen; Larosa, Judith; Grutzeck, Michael W. (1995). "29Si and27Al MASNMR Study of Stratlingite". Journal of the American Ceramic Society. 78 (7): 1921–1926. doi:10.1111/j.1151-2916.1995.tb08910.x.
  23. Jackson, Marie D.; Landis, Eric N.; Brune, Philip F.; Vitti, Massimo; Chen, Heng; Li, Qinfei; Kunz, Martin; Wenk, Hans-Rudolf; Monteiro, Paulo J. M.; Ingraffea, Anthony R. (30 December 2014). "Mechanical resilience and cementitious processes in Imperial Roman architectural mortar". PNAS. 111 (52): 18484–18489. Bibcode:2014PNAS..11118484J. doi: 10.1073/pnas.1417456111 . PMC   4284584 . PMID   25512521.
  24. Marie D. Jackson; Sean R. Mulcahy; Heng Chen; Yao Li; Qinfei Li; Piergiulio Cappelletti; Hans-Rudolf Wenk (3 July 2017). "Phillipsite and Al-tobermorite mineral cements produced through low-temperature water-rock reactions in Roman marine concrete". American Mineralogist. 102 (7): 1435–1450. Bibcode:2017AmMin.102.1435J. doi:10.2138/am-2017-5993CCBY. S2CID   53452767.
  25. Knapton, Sarah (3 July 2017). "Secret of how Roman concrete survived tidal battering for 2,000 years revealed". The Telegraph. Archived from the original on 4 July 2017.
  26. Peter Hewlett and Martin Liska (eds.), Lea's Chemistry of Cement and Concrete, 5th ed. (Butterworth-Heinemann, 2019), pp. 3–4.
  27. Rassia, Stamatina Th; Pardalos, Panos M. (15 August 2013). Cities for Smart Environmental and Energy Futures: Impacts on Architecture and Technology. Springer Science & Business Media. p. 58. ISBN   978-3-642-37661-0.
  28. Nick Gromicko & Kenton Shepard. "the History of Concrete". The International Association of Certified Home Inspectors (InterNACHI). Archived from the original on 15 January 2013. Retrieved 8 January 2013.
  29. Herring, Benjamin. "The Secrets of Roman Concrete" (PDF). Archived (PDF) from the original on 15 September 2012. Retrieved 1 October 2012.
  30. Courland, Robert (2011). Concrete planet : the strange and fascinating story of the world's most common man-made material. Amherst, NY: Prometheus Books. ISBN   978-1616144814. Archived from the original on 4 November 2015. Retrieved 28 August 2015.
  31. "The History of Concrete and Cement". ThoughtCo. 9 April 2012. Retrieved 13 August 2022.
  32. "Francois Coignet – French house builder" . Retrieved 23 December 2016.
  33. « Château de Chazelet » [archive], notice no PA00097319, base Mérimée, ministère français de la Culture.
  34. "Concrete: Scientific Principles". Retrieved 6 October 2021.
  35. 1 2 Askarian, Mahya; Fakhretaha Aval, Siavash; Joshaghani, Alireza (22 January 2019). "A comprehensive experimental study on the performance of pumice powder in self-compacting concrete (SCC)". Journal of Sustainable Cement-Based Materials. 7 (6): 340–356. doi:10.1080/21650373.2018.1511486. S2CID   139554392.
  36. Melander, John M.; Farny, James A.; Isberner, Albert W. Jr. (2003). "Portland Cement Plaster/Stucco Manual" (PDF). Portland Cement Association. Archived (PDF) from the original on 12 April 2021. Retrieved 13 July 2021.
  37. Evelien Cochez; Wouter Nijs; Giorgio Simbolotti & Giancarlo Tosato. "Cement Production" (PDF). IEA ETSAP – Energy Technology Systems Analysis Programme. Archived from the original (PDF) on 24 January 2013. Retrieved 9 January 2013.
  38. Gibbons, Jack. "Measuring Water in Concrete". Concrete Construction. Archived from the original on 11 May 2013. Retrieved 1 October 2012.
  39. "Chapter 9: Designing and Proportioning Normal Concrete Mixtures" (PDF). PCA manual. Portland Concrete Association. Archived (PDF) from the original on 26 May 2012. Retrieved 1 October 2012.
  40. Taha, Ramzi A.; Al-Harthy, Ali S.; Al-Jabri, Khalifa S. (2010). "Use of production and brackish water in concrete mixtures" (PDF). International Journal of Sustainable Water and Environmental System. 1 (2): 39–43. doi:10.5383/swes.01.02.001. S2CID   250602063. Archived (PDF) from the original on 9 October 2022.
  41. 1 2 "Cement hydration". Understanding Cement. Archived from the original on 17 October 2012. Retrieved 1 October 2012.
  42. "Cement Paste – an overview". | ScienceDirect Topics. Retrieved 6 October 2021.
  43. "The Effect of Aggregate Properties on Concrete". 25 December 2012. Archived from the original on 25 December 2012. Retrieved 13 August 2022.
  44. Veretennykov, Vitaliy I.; Yugov, Anatoliy M.; Dolmatov, Andriy O.; Bulavytskyi, Maksym S.; Kukharev, Dmytro I.; Bulavytskyi, Artem S. (2008). "Concrete Inhomogeneity of Vertical Cast-in-Place Elements in Skeleton-Type Buildings". AEI 2008. pp. 1–10. doi:10.1061/41002(328)17. ISBN   978-0784410028.
  45. Gerry Bye; Paul Livesey; Leslie Struble (2011). "Admixtures and Special Cements". Portland Cement: Third edition. doi:10.1680/pc.36116.185 (inactive 1 August 2023). ISBN   978-0727736116.{{cite book}}: CS1 maint: DOI inactive as of August 2023 (link)
  46. 1 2 U.S. Federal Highway Administration (14 June 1999). "Admixtures". Archived from the original on 27 January 2007. Retrieved 25 January 2007.
  47. Cement Admixture Association. "Admixture Types". Archived from the original on 3 September 2011. Retrieved 25 December 2010.
  48. Hamakareem, Madeh Izat (14 November 2013). "Effect of Air Entrainment on Concrete Strength". The Constructor. Retrieved 13 November 2020.
  49. Holland, Terence C. (2005). "Silica Fume User's Manual" (PDF). Silica Fume Association and United States Department of Transportation Federal Highway Administration Technical Report FHWA-IF-05-016. Retrieved 31 October 2014.
  50. Kosmatka, S.; Kerkhoff, B.; Panerese, W. (2002). Design and Control of Concrete Mixtures (14 ed.). Portland Cement Association, Skokie, Illinois.
  51. Gamble, William. "Cement, Mortar, and Concrete". In Baumeister; Avallone; Baumeister (eds.). Mark's Handbook for Mechanical Engineers (Eighth ed.). McGraw Hill. Section 6, page 177.
  52. Kosmatka, S.H.; Panarese, W.C. (1988). Design and Control of Concrete Mixtures. Skokie, IL: Portland Cement Association. pp. 17, 42, 70, 184. ISBN   978-0893120870.
  53. "Paving the way to greenhouse gas reductions". MIT News | Massachusetts Institute of Technology. 28 August 2011. Archived from the original on 31 October 2012. Retrieved 13 August 2022.
  54. U.S. Federal Highway Administration (14 June 1999). "Fly Ash". Archived from the original on 21 June 2007. Retrieved 24 January 2007.
  55. U.S. Federal Highway Administration. "Ground Granulated Blast-Furnace Slag". Archived from the original on 22 January 2007. Retrieved 24 January 2007.
  56. U.S. Federal Highway Administration. "Silica Fume". Archived from the original on 22 January 2007. Retrieved 24 January 2007.
  57. Mullapudi, Taraka Ravi Shankar; Gao, Di; Ayoub, Ashraf (September 2013). "Non-destructive evaluation of carbon nanofibre concrete". Magazine of Concrete Research. 65 (18): 1081–1091. doi:10.1680/macr.12.00187.
  58. Tuan, Christopher; Yehia, Sherif (1 July 2004). "Evaluation of Electrically Conductive Concrete Containing Carbon Products for Deicing". ACI Materials Journal. 101 (4): 287–293.
  59. "Cold Joints". The Concrete Society. Archived from the original on 4 March 2016. Retrieved 30 December 2015.
  60. "Grades of Concrete with Proportion (Mix Ratio)". 26 March 2018.
  61. "Concrete International". 1 November 1989. Archived from the original on 28 September 2007. Retrieved 13 August 2022.
  62. "ACI 304R-00: Guide for Measuring, Mixing, Transporting, and Placing Concrete (Reapproved 2009)".
  63. Sarviel, Ed (1993). Construction Estimating Reference Data. Craftsman Book Company. p. 74. ISBN   978-0-934041-84-3.
  64. Cook, Marllon Daniel; Ghaeezadah, Ashkan; Ley, M. Tyler (1 February 2018). "Impacts of Coarse-Aggregate Gradation on the Workability of Slip-Formed Concrete". Journal of Materials in Civil Engineering. 30 (2): 04017265. doi:10.1061/(ASCE)MT.1943-5533.0002126. ISSN   1943-5533.
  65. "Aggregate in Concrete – the Concrete Network". Archived from the original on 2 February 2017. Retrieved 15 January 2017.
  66. Ferrari, L.; Kaufmann, J.; Winnefeld, F.; Plank, J. (October 2011). "Multi-method approach to study influence of superplasticizers on cement suspensions". Cement and Concrete Research. 41 (10): 1058–1066. doi:10.1016/j.cemconres.2011.06.010.
  67. "Curing Concrete" Peter C. Taylor CRC Press 2013. ISBN   978-0415779524. eBook ISBN   978-0203866139
  68. "Concrete Testing". Archived from the original on 24 October 2008. Retrieved 10 November 2008.
  69. Resulting strength distribution in vertical elements researched and presented at the article "Concrete inhomogeneity of vertical cast-in-place elements in skeleton-type buildings". Archived 3 April 2015 at the Wayback Machine
  70. ""Admixtures for Cementitious Applications."" (PDF). Archived from the original (PDF) on 17 October 2016.
  71. "Home" (PDF). Archived (PDF) from the original on 8 December 2015. Retrieved 12 November 2015.
  72. The American Heritage Dictionary of the English Language. Boston: Houghton Mifflin Harcourt. 2011. p. 106. ISBN   978-0547041018.
  73. "Asphalt concrete cores for embankment dams". International Water Power and Dam Construction. Archived from the original on 7 July 2012. Retrieved 3 April 2011.
  74. Polaczyk, Pawel; Huang, Baoshan; Shu, Xiang; Gong, Hongren (September 2019). "Investigation into Locking Point of Asphalt Mixtures Utilizing Superpave and Marshall Compactors". Journal of Materials in Civil Engineering. 31 (9): 04019188. doi:10.1061/(ASCE)MT.1943-5533.0002839. S2CID   197635732.
  75. Reid, Carlton (2015). Roads Were Not Built for Cars: How Cyclists Were the First to Push for Good Roads & Became the Pioneers of Motoring. Island Press. p. 120. ISBN   978-1610916899.
  76. Dalal, Sejal P.; Dalal, Purvang (March 2021). "Experimental Investigation on Strength and Durability of Graphene Nanoengineered Concrete". Construction and Building Materials. 276: 122236. doi:10.1016/j.conbuildmat.2020.122236. S2CID   233663658.
  77. Dalal, Sejal P.; Desai, Kandarp; Shah, Dhairya; Prajapati, Sanjay; Dalal, Purvang; Gandhi, Vimal; Shukla, Atindra; Vithlani, Ravi (January 2022). "Strength and feasibility aspects of concrete mixes induced with low-cost surfactant functionalized graphene powder". Asian Journal of Civil Engineering. 23 (1): 39–52. doi:10.1007/s42107-021-00407-7. S2CID   257110774.
  78. Falkow, Stanley; Rosenberg, Eugene; Schleifer, Karl-Heinz; Stackebrandt, Erko (13 July 2006). The Prokaryotes: Vol. 2: Ecophysiology and Biochemistry. Springer Science & Business Media. p. 1005. ISBN   978-0-387-25492-0.
  79. Metwally, Gehad A. M.; Mahdy, Mohamed; Abd El-Raheem, Ahmed El-Raheem H. (1 August 2020). "Performance of Bio Concrete by Using Bacillus Pasteurii Bacteria". Civil Engineering Journal. 6 (8): 1443–1456. doi:10.28991/cej-2020-03091559. ISSN   2476-3055. S2CID   221651057.
  80. 1 2 Raju, N. Krishna (2018). Prestressed Concrete, 6e. McGraw-Hill Education. p. 1131. ISBN   978-9387886254.
  81. Tiwari, AK; Chowdhury, Subrato (2013). "An over view of the application of nanotechnology in construction materials". Proceedings of the International Symposium on Engineering under Uncertainty: Safety Assessment and Management (ISEUSAM-2012). Cakrabartī, Subrata; Bhattacharya, Gautam. New Delhi: Springer India. p. 485. ISBN   978-8132207573. OCLC   831413888.
  82. Saravanan, M. M.; Sivaraja, M. (10 May 2016). "Study And Development Of The Properties Of Nano-Concrete". Global Journal of Engineering Science and Research Management. doi:10.5281/zenodo.51258.
  83. "Ground Water Recharging Through Pervious Concrete Pavement". ResearchGate. Retrieved 26 January 2021.
  84. Lavars, Nick (10 June 2021). "Stanford's low-carbon cement swaps limestone for volcanic rock". New Atlas. Archived from the original on 10 June 2021. Retrieved 11 June 2021.
  85. Celik, K.; Jackson, M. D.; Mancio, M.; Meral, C.; Emwas, A. -H.; Mehta, P. K.; Monteiro, P. J. M. (1 January 2014). "High-volume natural volcanic pozzolan and limestone powder as partial replacements for portland cement in self-compacting and sustainable concrete". Cement and Concrete Composites. 45: 136–147. doi:10.1016/j.cemconcomp.2013.09.003. hdl:11511/37244. ISSN   0958-9465. S2CID   138740924.
  86. 1 2 3 Lemougna, Patrick N.; Wang, Kai-tuo; Tang, Qing; Nzeukou, A. N.; Billong, N.; Melo, U. Chinje; Cui, Xue-min (1 October 2018). "Review on the use of volcanic ashes for engineering applications". Resources, Conservation and Recycling. 137: 177–190. doi:10.1016/j.resconrec.2018.05.031. ISSN   0921-3449. S2CID   117442866.
  87. Brown, R. J.; Calder, E. S. (2005), "Pyroclastics", in Selley, Richard C.; Cocks, L. Robin M.; Plimer, Ian R. (eds.), Encyclopedia of Geology, Oxford: Elsevier, pp. 386–397, doi:10.1016/b0-12-369396-9/00153-2, ISBN   978-0123693969 , retrieved 6 October 2021
  88. Izzo, Francesco; Arizzi, Anna; Cappelletti, Piergiulio; Cultrone, Giuseppe; De Bonis, Alberto; Germinario, Chiara; Graziano, Sossio Fabio; Grifa, Celestino; Guarino, Vincenza; Mercurio, Mariano; Morra, Vincenzo (1 August 2016). "The art of building in the Roman period (89 BC – 79 AD): Mortars, plasters and mosaic floors from ancient Stabiae (Naples, Italy)". Construction and Building Materials. 117: 129–143. doi:10.1016/j.conbuildmat.2016.04.101. ISSN   0950-0618.
  89. "MASUKO light concrete" . Retrieved 13 November 2020.
  90. "Relation Between Compressive and Tensile Strength of Concrete". Archived from the original on 6 January 2019. Retrieved 6 January 2019.
  91. "Structural lightweight concrete" (PDF). Concrete Construction. The Aberdeen Group. March 1981. Archived from the original (PDF) on 11 May 2013.
  92. "Ordering Concrete by PSI". American Concrete. Archived from the original on 11 May 2013. Retrieved 10 January 2013.
  93. 1 2 Henry G. Russel, PE. "Why Use High Performance Concrete?" (PDF). Technical Talk. Archived (PDF) from the original on 15 May 2013. Retrieved 10 January 2013.
  94. "Concrete in Practice: What, Why, and How?" (PDF). NRMCA-National Ready Mixed Concrete Association. Archived (PDF) from the original on 4 August 2012. Retrieved 10 January 2013.
  95. Ritchie, Hannah; Roser, Max; Rosado, Pablo (11 May 2020). "CO₂ and Greenhouse Gas Emissions". Our World in Data via
  96. "Making Concrete Change: Innovation in Low-carbon Cement and Concrete". Chatham House. 13 June 2018. Archived from the original on 19 December 2018. Retrieved 17 December 2018.
  97. Rubenstein, Madeleine (9 May 2012). "Emissions from the Cement Industry". State of the Planet. Earth Institute, Columbia University. Archived from the original on 22 December 2016. Retrieved 13 December 2016.
  98. "Concrete and Embodied Energy – Can using concrete be carbon neutral". 22 February 2013. Archived from the original on 16 January 2017. Retrieved 15 January 2017.
  99. Gajda, John (2001). "Energy Use of Single-Family Houses with Various Exterior Walls" (PDF). Archived (PDF) from the original on 9 October 2022.
  100. Green Building with Concrete. Taylor & Francis Group. 2015. ISBN   978-1498704113.[ page needed ]
  101. "Features and Usage of Foam Concrete". Archived from the original on 29 November 2012.
  102. "Unreinforced Masonry Buildings and Earthquakes: Developing Successful Risk Reduction Programs FEMA P-774". Archived from the original on 12 September 2011.
  103. Simsir, C.C.; Jain, A.; Hart, G.C.; Levy, M.P. (12–17 October 2008). Seismic Retrofit Design Of Historic Century-Old School Buildings In Istanbul, Turkey (PDF). 14th World Conference on Earthquake Engineering. Archived from the original (PDF) on 11 January 2012.
  104. Nawy, Edward G. (2008). Concrete Construction Engineering Handbook. CRC Press. ISBN   978-1420007657.
  105. Lomborg, Bjørn (2001). The Skeptical Environmentalist: Measuring the Real State of the World. Cambridge University Press. p.  138. ISBN   978-0521804479.
  106. "Minerals commodity summary – cement – 2007". US United States Geological Survey. 1 June 2007. Archived from the original on 13 December 2007. Retrieved 16 January 2008.
  107. Murray, Lorraine. "Christ the Redeemer (last updated 13 January 2014)". Encyclopædia Britannica . Retrieved 5 November 2022.
  108. 1 2 "Reinforced concrete".
  109. 1 2 3 4 Claisse, Peter A. (2016), "Composites", Civil Engineering Materials, Elsevier, pp. 431–435, doi:10.1016/b978-0-08-100275-9.00038-3, ISBN   978-0081002759 , retrieved 5 October 2021
  110. 1 2 Richardson, John (2003), Newman, John; Choo, Ban Seng (eds.), "21 – Precast concrete structural elements", Advanced Concrete Technology, Oxford: Butterworth-Heinemann, pp. 3–46, ISBN   978-0750656863 , retrieved 7 October 2021
  111. 1 2 "Mass Concret" (PDF). Archived from the original (PDF) on 27 September 2011.
  112. Sadowski, Łukasz; Mathia, Thomas (2016). "Multi-scale Metrology of Concrete Surface Morphology: Fundamentals and specificity". Construction and Building Materials. 113: 613–621. doi:10.1016/j.conbuildmat.2016.03.099.
  113. "Winter is Coming! Precautions for Cold Weather Concreting". FPrimeC Solutions. 14 November 2016. Archived from the original on 13 January 2017. Retrieved 11 January 2017.
  114. "306R-16 Guide to Cold Weather Concreting". Archived from the original on 15 September 2017.
  115. 1 2 Larn, Richard; Whistler, Rex (1993). "17 – Underwater concreting". Commercial Diving Manual (3rd ed.). Newton Abbott, UK: David and Charles. pp. 297–308. ISBN   0715301004.
  116. "Mapping of Excess Fuel Consumption". Archived from the original on 2 January 2015.
  117. Akerman, Patrick; Cazzola, Pierpaolo; Christiansen, Emma Skov; Heusden, Renée Van; Iperen, Joanna Kolomanska-van; Christensen, Johannah; Crone, Kilian; Dawe, Keith; Smedt, Guillaume De; Keynes, Alex; Laporte, Anaïs; Gonsolin, Florie; Mensink, Marko; Hebebrand, Charlotte; Hoenig, Volker; Malins, Chris; Neuenhahn, Thomas; Pyc, Ireneusz; Purvis, Andrew; Saygin, Deger; Xiao, Carol; Yang, Yufeng (1 September 2020). "Reaching Zero with Renewables".
  118. "Leading the way to carbon neutrality" (PDF). HeidelbergCement. 24 September 2020. Archived (PDF) from the original on 9 October 2022.
  119. "Cement Clinker Calcination in Cement Production Process". AGICO Cement Plant Supplier. 4 April 2019.
  120. "Carbon footprint" (PDF). Portland Cement Association. Archived (PDF) from the original on 9 October 2022.
  121. 1 2 3 Lehne, Johanna; Preston, Felix (13 June 2018). "Making Concrete Change: Innovation in Low-carbon Cement and Concrete".
  122. Proske, Tilo; Hainer, Stefan; Rezvani, Moien; Graubner, Carl-Alexander (September 2013). "Eco-friendly concretes with reduced water and cement contents – Mix design principles and laboratory tests". Cement and Concrete Research. 51: 38–46. doi:10.1016/j.cemconres.2013.04.011.
  123. O’Hegarty, Richard; Kinnane, Oliver; Newell, John; West, Roger (November 2021). "High performance, low carbon concrete for building cladding applications". Journal of Building Engineering. 43: 102566. doi:10.1016/j.jobe.2021.102566.
  124. Lee, Jaehyun; Lee, Taegyu; Jeong, Jaewook; Jeong, Jaemin (January 2021). "Sustainability and performance assessment of binary blended low-carbon concrete using supplementary cementitious materials". Journal of Cleaner Production. 280: 124373. doi:10.1016/j.jclepro.2020.124373. S2CID   224849505.
  125. Akhtar, Ali; Sarmah, Ajit K. (20 September 2018). "Strength improvement of recycled aggregate concrete through silicon rich char derived from organic waste". Journal of Cleaner Production. 196: 411–423. doi:10.1016/j.jclepro.2018.06.044. ISSN   0959-6526. S2CID   158759120.
  126. Mehta, P. Kumar (1 February 2009). "Global Concrete Industry Sustainability". Concrete International. 31 (2): 45–48.
  127. 1 2 3 4 5 6 7 8 9 10 World Business Council for Sustainable Development, "The Cement Sustainability Initiative – Recycling concrete", available online at: (last access on October 5th 2021)
  128. Luis Emilio Rendon Diaz Miron; Dessi A. Koleva (2017). Concrete Durability: Cementitious Materials and Reinforced Concrete Properties, Behavior and Corrosion Resistance. Springer. pp. 2–. ISBN   978-3319554631.
  129. Gadd, Geoffrey Michael (1 March 2010). "Metals, minerals and microbes: geomicrobiology and bioremediation". Microbiology. 156 (3): 609–643. doi:10.1099/mic.0.037143-0. PMID   20019082.
  130. The European Commission (2014). "Commission decision of 18 December 2014 amending decision 2000/532/EC on the list of waste pursuant to Directive 2008/98/EC of the European Parliament of the Council, 2014/955/EU". Official Journal of the European Union.
  131. "Generation of waste by waste category, hazardousness and NACE Rev. 2 activity". Eurostat . 29 June 2021. Archived from the original on 7 March 2021. Retrieved 5 October 2021.
  132. Tecnalia, "End of Waste criteria protocol for waste used as aggregates", Cinderela project, M26, D5.5 May 2021
  133. Asam, C., "Recycling prefabricated concrete components – a contribution to sustainable construction", Institute for Preservation and Modernization of Buildings at the Technical University of Berlin
  134. 1 2 "The Economics | Construction & Demolition Recycling Association". Retrieved 5 October 2021.
  135. 1 2 "How to Recycle | Construction & Demolition Recycling Association". Retrieved 5 October 2021.
  136. 1 2 3 4 "Save Money and Reduce Environmental Impact by Recycling Concretes". The Balance Small Business. Retrieved 5 October 2021.
  137. "Itaipu Web-site". 2 January 2012. Archived from the original on 9 February 2012. Retrieved 2 January 2012.
  138. Sources, Other News (14 July 2009). "China's Three Gorges Dam, by the Numbers". Probe International. Archived from the original on 29 March 2017. Retrieved 13 August 2022.
  139. "Concrete Pouring of Three Gorges Project Sets World Record". People's Daily. 4 January 2001. Archived from the original on 27 May 2010. Retrieved 24 August 2009.
  140. "Concrete Pumping to 715 m Vertical – A New World Record Parbati Hydroelectric Project Inclined Pressure Shaft Himachal Pradesh – A case Study". The Masterbuilder. Archived from the original on 21 July 2011. Retrieved 21 October 2010.
  141. "SCHWING Stetter Launches New Truck mounted Concrete Pump S-36". NBM&CW (New Building Materials and Construction World). October 2009. Archived from the original on 14 July 2011. Retrieved 21 October 2010.
  142. Janyala, Sreenivas (7 January 2019). "Andhra Pradesh: Polavaram project enters Guinness Book of World Record for concrete pouring". The India Express. Retrieved 7 January 2020.
  143. "Concrete Supplier for Landmark Tower". Archived from the original on 15 May 2013.
  144. "The world record Concrete Supplier for Landmark Tower Unibeton Ready Mix". Archived from the original on 24 November 2012.
  145. "Abu Dhabi – Landmark Tower has a record-breaking pour" (PDF). Al Habtoor Engineering. September–October 2007. p. 7. Archived from the original (PDF) on 8 March 2011.
  146. National Geographic Channel International / Caroline Anstey (2005), Megastructures: Petronas Twin Towers
  147. "Continuous cast: Exxcel Contract Management oversees record concrete pour". 1 March 1998. Archived from the original on 26 May 2010. Retrieved 25 August 2009.
  148. Exxcel Project Management – Design Build, General Contractors Archived 28 August 2009 at the Wayback Machine . Retrieved 19 February 2013.
  149. "Contractors Prepare to Set Gates to Close New Orleans Storm Surge Barrier". 12 May 2011. Archived from the original on 13 January 2013. Retrieved 13 August 2022.