Atomic-terrace low-angle shadowing

Last updated January 03, 2023

Atomic Terrace Low Angle Shadowing (ATLAS) is a surface science technique which enables the growth of planar nanowire or nanodot arrays using molecular beam epitaxy on a vicinal surface. ATLAS utilises the inherent step-and-terrace structure of the surface as a template for such nanostructures.^[1]^[2] The technique involves the low angle incidence of flux material on vicinal substrates. Vicinal substrates are composed of atomic terraces separated by atomic steps. The ATLAS technique allows for the fabrication of well defined planar arrays of plasmonic nanostructures, of dimensions unachievable by lithography.

The technique is a "bottom-up" approach and allows great control over the separation of nanostructures within the array, as well as their individual widths. The separation is controlled by the size of the atomic terraces of the substrate, which is determined by its miscut from the principal index; and the width of the nanostructures is controlled by the oblique angle of the deposition.

ATLAS has been shown to be a very versatile technique, with the growth of metallic, semi-conducting and magnetic nanowires and nanodots demonstrated using a variety of source materials and substrates.^[3]

Basic Principles

Figure 1. Deposition at a shallow angle on a vicinal surface (a) deposition of nanostructures on the outer step edges; beam at an angle b along the "downhill" direction, (b) substrate is rotated by 180deg and the beam is directed in the "uphill" direction. ATLAS-Technique-Schematic1.png — Figure 1. Deposition at a shallow angle on a vicinal surface (a) deposition of nanostructures on the outer step edges; beam at an angle β along the "downhill" direction, (b) substrate is rotated by 180° and the beam is directed in the "uphill" direction.

Figure 1(a) shows a schematic of the deposition in the "downhill" direction, that is, from an outer step edge to a lower terrace. The deposition angle β between the beam and surface is small (1°-3°) so that some areas of the terraces are exposed to the beam, and others are geometrically shadowed.

The deposition angle β determines the width of the nanostructures, according to the following relation:

w\approx a\left({\frac {1}{\alpha }}-{\frac {1}{\alpha +\beta }}\right)

where w is the nanostructure width, a is the height of one step, α is the miscut angle and β is the deposition angle between the incident beam and the surface (α and β are assumed to be small and are measured in radians).

Figure 1(b) shows a similar situation, but this time with the substrate rotated by 180° so that the incident beam is now in the "uphill" direction, and nearly parallel to the surface. In this case, the step faces provide the bonding sites and the deposited material grows along the steps, similar to the step-flow growth mechanism.

In order to grow nanowires with a width of fifteen nanometers or less, the deposition temperature for both orientations should be chosen such that the mean free path of the adatoms on the surface is limited to a few nanometers.

Experimental Development

The ATLAS system was developed within the Applied Physics Group at the School of Physics, Trinity College, Dublin. The experimental procedure is relatively straightforward, when compared to lithography or other approaches, meaning that only standard equipment is needed.

The set-up consists of an ultrahigh vacuum chamber (base pressure in the low 10⁻¹⁰ Torr range), with the sample mounted at a large working distance (40-100 cm) from the evaporation source. This large distance provides the high collimation required for the ATLAS technique. The sample itself is mounted on a rotation stage and can be tilted through 200° with a precision of ±0.5°.

The substrate can be heated during deposition by either passing direct current through the sample for semiconductors or by driving current through a separate heating foil underneath the substrate for insulating oxides.

Versatility

The capabilities of the system were first tested by growing arrays of 10-30 nm wide metallic nanowires on two types of vicinal substrates, step-bunched Si(111) and α-Al₂O₃(0001). Deposition of Au and Ag onto these substrates yields arrays of wires with a width and height of 15 nm and 2 nm, and separated by approximately 30 nm.

Since its introduction in 2008, ATLAS has been demonstrated as a simple technique to produce nanowires of a variety of materials down to a width of 15 nm and thickness of 2 nm, on several stepped substrates.

Limitations

Although ATLAS is a versatile technique, some limitations do exist. The initial growth of the nanowires is nucleated on certain preferential adsorption sites. This can form epitaxial seeds, which grow independently of each other, until they meet, which forms an overall polycrystalline wire. This polycrystallinity can affect the stability of the wire when exposed to air, and can increase the resistance due to its defective nature. It is an ongoing topic of research to increase the quality of nanowires by lattice matching, or increasing initial mobility through heating of the substrate.

Despite these limitations, ATLAS's results of a 15 nm width is approximately a five-fold reduction in size compared to other shallow-angle techniques.^[4]

Related Research Articles

<span class="mw-page-title-main">Microelectromechanical systems</span> Very small devices that incorporate moving components

Microelectromechanical systems (MEMS), also written as micro-electro-mechanical systems and the related micromechatronics and microsystems constitute the technology of microscopic devices, particularly those with moving parts. They merge at the nanoscale into nanoelectromechanical systems (NEMS) and nanotechnology. MEMS are also referred to as micromachines in Japan and microsystem technology (MST) in Europe.

In integrated circuit manufacturing, photolithography or optical lithography is a general term used for techniques that use light to produce minutely patterned thin films of suitable materials over a substrate, such as a silicon wafer, to protect selected areas of it during subsequent etching, deposition, or implantation operations. Typically, ultraviolet light is used to transfer a geometric design from an optical mask to a light-sensitive chemical (photoresist) coated on the substrate. The photoresist either breaks down or hardens where it is exposed to light. The patterned film is then created by removing the softer parts of the coating with appropriate solvents.

A nanowire is a nanostructure in the form of a wire with the diameter of the order of a nanometre. More generally, nanowires can be defined as structures that have a thickness or diameter constrained to tens of nanometers or less and an unconstrained length. At these scales, quantum mechanical effects are important—which coined the term "quantum wires".

<span class="mw-page-title-main">Molecular-beam epitaxy</span> Crystal growth process

Molecular-beam epitaxy (MBE) is an epitaxy method for thin-film deposition of single crystals. MBE is widely used in the manufacture of semiconductor devices, including transistors, and it is considered one of the fundamental tools for the development of nanotechnologies. MBE is used to fabricate diodes and MOSFETs at microwave frequencies, and to manufacture the lasers used to read optical discs.

Pulsed laser deposition (PLD) is a physical vapor deposition (PVD) technique where a high-power pulsed laser beam is focused inside a vacuum chamber to strike a target of the material that is to be deposited. This material is vaporized from the target which deposits it as a thin film on a substrate. This process can occur in ultra high vacuum or in the presence of a background gas, such as oxygen which is commonly used when depositing oxides to fully oxygenate the deposited films.

Electron-beam lithography is the practice of scanning a focused beam of electrons to draw custom shapes on a surface covered with an electron-sensitive film called a resist (exposing). The electron beam changes the solubility of the resist, enabling selective removal of either the exposed or non-exposed regions of the resist by immersing it in a solvent (developing). The purpose, as with photolithography, is to create very small structures in the resist that can subsequently be transferred to the substrate material, often by etching.

Self-assembled monolayers (SAM) of organic molecules are molecular assemblies formed spontaneously on surfaces by adsorption and are organized into more or less large ordered domains. In some cases molecules that form the monolayer do not interact strongly with the substrate. This is the case for instance of the two-dimensional supramolecular networks of e.g. perylenetetracarboxylic dianhydride (PTCDA) on gold or of e.g. porphyrins on highly oriented pyrolitic graphite (HOPG). In other cases the molecules possess a head group that has a strong affinity to the substrate and anchors the molecule to it. Such a SAM consisting of a head group, tail and functional end group is depicted in Figure 1. Common head groups include thiols, silanes, phosphonates, etc.

Nanolithography (NL) is a growing field of techniques within nanotechnology dealing with the engineering of nanometer-scale structures on various materials.

Dip pen nanolithography (DPN) is a scanning probe lithography technique where an atomic force microscope (AFM) tip is used to create patterns directly on a range of substances with a variety of inks. A common example of this technique is exemplified by the use of alkane thiolates to imprint onto a gold surface. This technique allows surface patterning on scales of under 100 nanometers. DPN is the nanotechnology analog of the dip pen, where the tip of an atomic force microscope cantilever acts as a "pen," which is coated with a chemical compound or mixture acting as an "ink," and put in contact with a substrate, the "paper."

Nanoimprint lithography (NIL) is a method of fabricating nanometer scale patterns. It is a simple nanolithography process with low cost, high throughput and high resolution. It creates patterns by mechanical deformation of imprint resist and subsequent processes. The imprint resist is typically a monomer or polymer formulation that is cured by heat or UV light during the imprinting. Adhesion between the resist and the template is controlled to allow proper release.

<span class="mw-page-title-main">Nanorod</span>

In nanotechnology, nanorods are one morphology of nanoscale objects. Each of their dimensions range from 1–100 nm. They may be synthesized from metals or semiconducting materials. Standard aspect ratios are 3-5. Nanorods are produced by direct chemical synthesis. A combination of ligands act as shape control agents and bond to different facets of the nanorod with different strengths. This allows different faces of the nanorod to grow at different rates, producing an elongated object.

Interference lithography is a technique for patterning regular arrays of fine features, without the use of complex optical systems or photomasks.

Electron-beam-induced deposition (EBID) is a process of decomposing gaseous molecules by an electron beam leading to deposition of non-volatile fragments onto a nearby substrate. The electron beam is usually provided by a scanning electron microscope, which results in high spatial accuracy and the possibility to produce free-standing, three-dimensional structures.

Nanometrology is a subfield of metrology, concerned with the science of measurement at the nanoscale level. Nanometrology has a crucial role in order to produce nanomaterials and devices with a high degree of accuracy and reliability in nanomanufacturing.

The proximity effect in electron beam lithography (EBL) is the phenomenon that the exposure dose distribution, and hence the developed pattern, is wider than the scanned pattern due to the interactions of the primary beam electrons with the resist and substrate. These cause the resist outside the scanned pattern to receive a non-zero dose.

Selective area epitaxy is the local growth of epitaxial layer through a patterned amorphous dielectric mask (typically SiO₂ or Si₃N₄) deposited on a semiconductor substrate. Semiconductor growth conditions are selected to ensure epitaxial growth on the exposed substrate, but not on the dielectric mask. SAE can be executed in various epitaxial growth methods such as molecular beam epitaxy (MBE), metalorganic vapour phase epitaxy (MOVPE) and chemical beam epitaxy (CBE). By SAE, semiconductor nanostructures such as quantum dots and nanowires can be grown to their designed places.

The vapor–liquid–solid method (VLS) is a mechanism for the growth of one-dimensional structures, such as nanowires, from chemical vapor deposition. The growth of a crystal through direct adsorption of a gas phase on to a solid surface is generally very slow. The VLS mechanism circumvents this by introducing a catalytic liquid alloy phase which can rapidly adsorb a vapor to supersaturation levels, and from which crystal growth can subsequently occur from nucleated seeds at the liquid–solid interface. The physical characteristics of nanowires grown in this manner depend, in a controllable way, upon the size and physical properties of the liquid alloy.

Plasmonic nanolithography is a nanolithographic process that utilizes surface plasmon excitations such as surface plasmon polaritons (SPPs) to fabricate nanoscale structures. SPPs, which are surface waves that propagate in between planar dielectric-metal layers in the optical regime, can bypass the diffraction limit on the optical resolution that acts as a bottleneck for conventional photolithography.

Stencil lithography is a novel method of fabricating nanometer scale patterns using nanostencils, stencils with nanometer size apertures. It is a resist-less, simple, parallel nanolithography process, and it does not involve any heat or chemical treatment of the substrates .

Local oxidation nanolithography (LON) is a tip-based nanofabrication method. It is based on the spatial confinement on an oxidation reaction under the sharp tip of an atomic force microscope.

References

↑ F. Cuccureddu, V. Usov, S. Murphy, C. O. Coileain, I. V. Shvets, Planar nanowire arrays formed by atomic-terrace low-angle shadowing, Rev. Sci. Instrum. 79, 053907 (2008), Archived 2014-04-09 at archive.today
↑ Cuccureddu, F.; Usov, V.; Murphy, S.; Coileain, C.O.; Shvets, I. (20 May 2008). "Planar nanowire arrays formed by atomic-terrace low-angle shadowing". Review of Scientific Instruments. 79 (5): 053907–053907–4. Bibcode:2008RScI...79e3907C. doi:10.1063/1.2929835. hdl: 2262/40319 . ISSN 0034-6748. PMID 18513079.
↑ Floriano Cuccureddu, Shane Murphy, Igor V. Shvets, Mauro Porcu, H. W. Zandbergen, Plasmon Resonance in Silver Nanoparticles Arrays Grown by Atomic Terrace Low-Angle Shadowing, Nano Lett., 2008, 8 (10), pp 3248–3256,
↑ J. Oster, M. Kallmayer, L. Wiehl, H. J. Elmers, H. Adrian, F. Porrati, M. Huth, J. Appl. Phys. 97, 014303 (2005),

This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.

[rsi-1] F. Cuccureddu, V. Usov, S. Murphy, C. O. Coileain, I. V. Shvets, Planar nanowire arrays formed by atomic-terrace low-angle shadowing, Rev. Sci. Instrum. 79, 053907 (2008), Archived 2014-04-09 at archive.today

[2] Cuccureddu, F.; Usov, V.; Murphy, S.; Coileain, C.O.; Shvets, I. (20 May 2008). "Planar nanowire arrays formed by atomic-terrace low-angle shadowing". Review of Scientific Instruments. 79 (5): 053907–053907–4. Bibcode:2008RScI...79e3907C. doi:10.1063/1.2929835. hdl: 2262/40319 . ISSN 0034-6748. PMID 18513079.

[nanolett-3] Floriano Cuccureddu, Shane Murphy, Igor V. Shvets, Mauro Porcu, H. W. Zandbergen, Plasmon Resonance in Silver Nanoparticles Arrays Grown by Atomic Terrace Low-Angle Shadowing, Nano Lett., 2008, 8 (10), pp 3248–3256,

[old-4] J. Oster, M. Kallmayer, L. Wiehl, H. J. Elmers, H. Adrian, F. Porrati, M. Huth, J. Appl. Phys. 97, 014303 (2005),

[1]

[2]

[3]

[4]