Modacrylic

Last updated

A modacrylic is a synthetic copolymer. Modacrylics are soft, strong, resilient and dimensionally stable. They can be easily dyed, show good press and shape retention, and are quick to dry. They have outstanding resistance to chemicals and solvents, are not attacked by moths or mildew, and are nonallergenic. Among their uses are in apparel linings, furlike outerwear, paint-roller covers, scatter rugs, carpets, and work clothing and as hair in wigs. [1]

Contents

Commercial production of modacrylic fiber began in 1949 by Union Carbide Corporation in the United States. Modacrylic and acrylic fibers are similar in composition and at one time were in the same category. In 1960 the Federal Trade Commission decided to separate the two fibers and establish a category for each. [2]

The Federal Trade Commission defines modacrylic fibers as manufactured fibers in which the fiber-forming substance is any long-chain synthetic polymer composed of less than 85%, but at least 35% weight acrylonitrile units except when the polymer qualifies as rubber. [3]

Production

Modacrylic fibers are modified acrylic fibers made from acrylonitriles, but larger amounts of other polymers are added to make the copolymers.

The modacrylic fibers are produced by polymerizing the components, dissolving the copolymer in acetone, pumping the solution into the column of warm air (dry-spun), and stretching while hot. [3]

Modacrylics are creamy or white and are produced in tow and staple form. If looked at in cross section views they have an irregular shape. Modacrylic fibers are also produced in many different lengths, crimp levels, deniers and they can have various shrinkage potentials.

Current modacrylic fiber producers include Kaneka Corporation in Japan. [4]

Properties

A modacrylic has properties that are similar to an acrylic. However, modacrylics are flame retardant and do not combust. The fibers are difficult to ignite and will self-extinguish. In addition to a modacrylic's flame retardant properties it has a relatively high durability that is comparable to wool. Modacrylic fibers have a moderate resistance to abrasion and a very low tenacity.

One of the most interesting properties of Modacrylic fabrics is the arc flash protection, where it has very good values.

Modacrylics are poor conductors of heat. The fabrics are soft, warm and resilient but are prone to pilling and matting. Modacrylics display high performance when it comes to appearance retention. The fibers are quite resilient and will not wrinkle. They also have great dimensional stability and high elastic recovery, which gives them the ability to hold their shape. [3]

Care

Modacrylics are sensitive to loss of appearance due to improper care; therefore, it is important to know how to care for modacrylics. Modacrylics are resistant to acids, weak alkalis, and organic solvents. These fibers are also resistant to moths, mildew and sunlight. Modacrylic fabrics can be machine washed using warm water and tumble dried on a low setting. Modacrylic pieces can also be dry-cleaned, however, they should not be steamed and should only be tumbled on cold. Some fabrics may also be cleaned using the furrier method (a special non immersion cleaning process). The fibers are heat sensitive and will shrink at 121 °C (250 °F) and will stiffen at temperatures over 149 °C (300 °F). [3]

Uses

Modacrylics are used by producers of technically advanced fabrics for comfortable and protective blends often used in personal protective equipment, primarily when environmental resistance or flame retardancy is necessary or required. Modacrylics can combine flame retardancy with a relatively low density, keeping protective gear from being uncomfortably heavy (i.e. shirts and trousers worn by electrical linemen). The combination of flame retardancy and low density is also useful in furnishings, draperies, and outdoor fabrics.

Modacrylics are also commonly used in fake fur fabrics, toupées, wigs and fleece-type fabric. By mixing the various forms of fibers one can easily create a realistic synthetic fur. The fabrics can then be sheared or embossed to resemble fur even more closely. The heat-sensitivity of modacrylic also allows wigs and hairpieces to be curled and heat styled without damage. [3]

Modacrylics are also used in fleece, knit-pile fabric backings, and nonwoven fabrics. Other uses of modacrylics include paint rollers, industrial fabrics, stuffed toys and filters. [5]

Related Research Articles

Thermoplastic Plastic that becomes soft when heated and hard when cooled

A thermoplastic, or thermosoft plastic, is any plastic polymer material that becomes pliable or moldable at a certain elevated temperature and solidifies upon cooling.

Synthetic fibers or synthetic fibres are fibers made by humans through chemical synthesis, as opposed to natural fibers that are directly derived from living organisms, such as plants or fur from animals. They are the result of extensive research by scientists to replicate naturally occurring animal and plant fibers. In general, synthetic fibers are created by extruding fiber-forming materials through spinnerets, forming a fiber. These are called synthetic or artificial fibers. The word polymer comes from a Greek prefix "poly" which means "many" and suffix "mer" which means "single units"..

Polyacrylonitrile Chemical compound

Polyacrylonitrile (PAN), also known as polyvinyl cyanide and Creslan 61, is a synthetic, semicrystalline organic polymer resin, with the linear formula (C3H3N)n. Though it is thermoplastic, it does not melt under normal conditions. It degrades before melting. It melts above 300 °C if the heating rates are 50 degrees per minute or above. Almost all PAN resins are copolymers made from mixtures of monomers with acrylonitrile as the main monomer. It is a versatile polymer used to produce large variety of products including ultra filtration membranes, hollow fibers for reverse osmosis, fibers for textiles, and oxidized PAN fibers. PAN fibers are the chemical precursor of very high-quality carbon fiber. PAN is first thermally oxidized in air at 230 °C to form an oxidized PAN fiber and then carbonized above 1000 °C in inert atmosphere to make carbon fibers found in a variety of both high-tech and common daily applications such as civil and military aircraft primary and secondary structures, missiles, solid propellant rocket motors, pressure vessels, fishing rods, tennis rackets and bicycle frames. It is a component repeat unit in several important copolymers, such as styrene-acrylonitrile (SAN) and acrylonitrile butadiene styrene (ABS) plastic.

Acrylic fiber Synthetic fiber made from polymer

Acrylic fibers are synthetic fibers made from a polymer (polyacrylonitrile) with an average molecular weight of ~100,000, about 1900 monomer units. For a fiber to be called "acrylic" in the US, the polymer must contain at least 85% acrylonitrile monomer. Typical comonomers are vinyl acetate or methyl acrylate. DuPont created the first acrylic fibers in 1941 and trademarked them under the name Orlon. It was first developed in the mid-1940s but was not produced in large quantities until the 1950s. Strong and warm acrylic fiber is often used for sweaters and tracksuits and as linings for boots and gloves, as well as in furnishing fabrics and carpets. It is manufactured as a filament, then cut into short staple lengths similar to wool hairs, and spun into yarn.

Dynel

Dynel is a trade name for a type of synthetic fiber used in fibre reinforced plastic composite materials, especially for marine applications. As it is easily dyed, it was also used to fabricate wigs. The fashion designer Pierre Cardin used Dynel fabric to make a collection of heat-moulded dresses in 1968. A copolymer of acrylonitrile and vinyl chloride, Dynel shares many properties with both polyacrylonitrile and PVC. It is an acrylic resin.

Polybenzimidazole fiber is a synthetic fiber with a very high decomposition temperature. It does not exhibit a melting point, it has exceptional thermal and chemical stability, and it does not readily ignite. It was first discovered by American polymer chemist Carl Shipp Marvel in the pursuit of new materials with superior stability, retention of stiffness, toughness at elevated temperature. Due to its high stability, polybenzimidazole is used to fabricate high-performance protective apparel such as firefighter's gear, astronaut space suits, high temperature protective gloves, welders’ apparel and aircraft wall fabrics. Polybenzimidazole has been applied as a membrane in fuel cells.

Thinsulate

Thinsulate is a brand of synthetic fiber thermal insulation used in clothing. The word is a portmanteau of the words thin and insulate, trademarked by 3M. The material is made by the 3M Corporation and was first sold in 1979. It was originally marketed as an inexpensive alternative to down; at the time, 3M claimed it was twice as warm as an equivalent amount of any natural material.

Nitrile rubber, also known as nitrile butadiene rubber, NBR, Buna-N, and acrylonitrile butadiene rubber, is a synthetic rubber derived from acrylonitrile (ACN) and butadiene. Trade names include Perbunan, Nipol, Krynac and Europrene. This rubber is unusual in being resistant to oil, fuel, and other chemicals.

Acrylate polymer Group of polymers prepared from acrylate monomers

An acrylate polymer is any of a group of polymers prepared from acrylate monomers. These plastics are noted for their transparency, resistance to breakage, and elasticity.

Olefin fiber is a synthetic fiber made from a polyolefin, such as polypropylene or polyethylene. It is used in wallpaper, carpeting, ropes, and vehicle interiors.

Fire-retardant fabric Flame retardant fabric

Fire-retardant fabrics are textiles that are more resistant to fire than others through chemical treatment of flame-retardant or manufactured fireproof fibers.

A technical textile is a textile product manufactured for non-aesthetic purposes, where function is the primary criterion. Technical textiles include textiles for automotive applications, medical textiles, geotextiles, agrotextiles, and protective clothing.

Superabsorbent polymer Polymers that can absorb and retain extremely large amounts of a liquid relative to their own mass

A superabsorbent polymer (SAP) is a water-absorbing polymer that can absorb and retain extremely large amounts of a liquid relative to its own mass.

A fabric structure is a structure made of fabric, with or without a structural frame. The technology provides end users a variety of aesthetic free-form building designs. Custom-made structures are engineered and fabricated to meet worldwide structural, flame retardant, weather-resistant, and natural force requirements. Fabric structures are considered a sub-category of tensile structure.

Finishing (textiles) Manufacturing process

In textile manufacturing, finishing refers to the processes that convert the woven or knitted cloth into a usable material and more specifically to any process performed after dyeing the yarn or fabric to improve the look, performance, or "hand" (feel) of the finish textile or clothing. The precise meaning depends on context.

Fire-safe polymers are polymers that are resistant to degradation at high temperatures. There is need for fire-resistant polymers in the construction of small, enclosed spaces such as skyscrapers, boats, and airplane cabins. In these tight spaces, ability to escape in the event of a fire is compromised, increasing fire risk. In fact, some studies report that about 20% of victims of airplane crashes are killed not by the crash itself but by ensuing fires. Fire-safe polymers also find application as adhesives in aerospace materials, insulation for electronics, and in military materials such as canvas tenting.

Wet process engineering is one of the major streams in textile engineering which refers to the engineering of textile chemical processes and associated applied science. The other three streams in textile engineering are yarn engineering, fabric engineering, and apparel engineering. The processes of this stream are involved or carried out in an aqueous stage. Hence, it is called a wet process which usually covers pre-treatment, dyeing, printing, and finishing.

Acrylonitrile styrene acrylate Chemical compound

Acrylonitrile styrene acrylate (ASA), also called acrylic styrene acrylonitrile, is an amorphous thermoplastic developed as an alternative to acrylonitrile butadiene styrene (ABS), but with improved weather resistance, and is widely used in the automotive industry. It is an acrylate rubber-modified styrene acrylonitrile copolymer. It is used for general prototyping in 3D printing, where its UV resistance and mechanical properties make it an excellent material for use in fused deposition modelling printers.

Kaneka Corporation

Kaneka Corporation is a Japanese international chemical manufacturing company based in Osaka. The company was founded in 1949 and produces chemical products such as functional resin, foam resin, and synthetic fibers.

Fabric treatment

Fabric treatments are processes that make fabric softer, or water resistant, or enhance dye penetration after they are woven. Fabric treatments get applied when the textile itself cannot add other properties. Treatments include, scrim, foam lamination, fabric protector or stain repellent, anti microbial and flame retardant.

References

  1. ↑ Modacrylic. Columbia Encyclopedia. 20 June 2006. http://www.bartleby.com/65/mo/modacryl.html Archived 2007-02-12 at the Wayback Machine
  2. ↑ "Textile Reference Manual: What's the Story Behind These Fibers Called Modacrylics". Archived from the original on 2006-03-13. Retrieved 2007-06-25.
  3. 1 2 3 4 5 Kadolph, S.J & Langford, A.L. (2002). Textiles 9th Edition. New Jersey: Pearson Education, Inc. (pp. 118).
  4. ↑ "Synthetic Fibers | KANEKA CORPORATION". Archived from the original on 2008-05-01. Retrieved 2008-03-27.
  5. ↑ "Modacrylic Fiber - Modacrylic Staple Fiber, Modacrylic Tow Fiber". Archived from the original on 2010-03-28. Retrieved 2007-08-14.
This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.