Hydroforming

Last updated
A plate being shaped through hydroforming Idroformatura animata.gif
A plate being shaped through hydroforming

Hydroforming is a means of shaping ductile metals such as aluminium, brass, low alloy steel, and stainless steel into lightweight, structurally stiff and strong pieces. One of the largest applications of cost-effective hydroforming is the automotive industry, which makes use of the complex shapes made possible by hydroforming to produce stronger, lighter, and more rigid unibody structures for vehicles. This technique is particularly popular with the high-end sports car industry and is also frequently employed in the shaping of aluminium tubes for bicycle frames.

Contents

Hydroforming is a specialized type of die forming that uses a high pressure hydraulic fluid to press room temperature working material into a die. To hydroform aluminium into a vehicle's frame rail, a hollow tube of aluminium is placed inside a negative mold that has the shape of the desired result. High pressure hydraulic pumps then inject fluid at very high pressure inside the aluminium tube which causes it to expand until it matches the mold. The hydroformed aluminium is then removed from the mold. Hydroforming allows complex shapes with concavities to be formed, which would be difficult or impossible with standard solid die stamping. Hydroformed parts can often be made with a higher stiffness-to-weight ratio and at a lower per unit cost than traditional stamped or stamped and welded parts. Virtually all metals capable of cold forming can be hydroformed, including aluminium, brass, carbon and stainless steel, copper, and high strength alloys.[ clarify ] [1]

Electrohydraulic forming uses electrodes to vaporize the fluid explosively in an arc to deform the working material.

Main process variants

Sheet hydroforming

This process is based on the 1950s patent for hydramolding by Fred Leuthesser, Jr. and John Fox of the Schaible Company of Cincinnati, Ohio in the United States. [2] It was originally used in producing kitchen spouts. This was done because in addition to the strengthening of the metal, hydromolding also produced less "grainy" parts, allowing for easier metal finishing. [3] In sheet hydroforming there are bladder forming (where there is a bladder that contains the liquid; no liquid contacts the sheet) and hydroforming where the fluid contacts the sheet (no bladder). Bladder forming is sometimes called flexforming. [4] Flexforming is mostly used for low volume productions, as in the aerospace field. [5] Forming with the fluid in direct contact with the part can be done either with a male solid punch (this version is sometimes called hydro-mechanical deep drawing [6] ) or with a female solid die. In hydro-mechanical deep drawing, a work piece is placed on a draw ring (blank holder) over a male punch then a hydraulic chamber surrounds the work piece and a relatively low initial pressure seats the work piece against the punch. The punch then is raised into the hydraulic chamber and pressure is increased to as high as 100 MPa (15000 psi) which forms the part around the punch. Then the pressure is released and punch retracted, hydraulic chamber lifted, and the process is complete.

Among these techniques hydraulic bulge testing allows for an increased work hardening of sheet material by distinctive stretching operations and provides better shape accuracy for complex parts. Hence, by selecting proper material and the forming parameters for hydraulic sheet bulging study one can determine Forming Limit Curves (FLCs).

Significance

Alternative names, other variants and similar processes

  • Hydromec (Hydromechanical deep drawing)
  • Aquadraw
  • Bulge forming
  • Explosive forming
    • For large parts, explosive hydroforming can generate the forming pressure by simply exploding a charge above the part (complete with evacuated mold) which is immersed in a pool of water. The tooling can be much cheaper than what would be required for any press-type process. The hydroforming-into-a-mold process also works using only a shock wave in air as the pressuring medium. Particularly when the explosives are close to the workpiece, inertia effects make the result more complicated than forming by hydrostatic pressure alone.
  • Rubber pad forming

Tube hydroforming

In tube hydroforming there are two major practices: high pressure and low pressure. With the high pressure process the tube is fully enclosed in a die prior to pressurization of the tube. In low pressure the tube is slightly pressurized to a fixed volume during the closing of the die (this used to be called the Variform process). Historically, the process was patented in the '50s, [7] but it was industrially spread in the 1970s for the production of large T-shaped joints for the oil and gas industry. Today it is mostly used in the automotive sector, where many industrial applications can be found. [8] [9] With the rise of the electric bicycle it is now a method of choice for e-bicycle manufacturers. Especially down tubes and top tubes are favorably made with hydroforming in order to fit the battery for the electric bicycle. Newest applications in the bicycle industry are now hydroformed handlebars to improve aero dynamics and ergonomics. In tube hydroforming pressure is applied to the inside of a tube that is held by dies with the desired cross sections and forms. When the dies are closed, the tube ends are sealed by axial punches and the tube is filled with hydraulic fluid. The internal pressure can go up to a few thousand bars and it causes the tube to calibrate against the dies. The fluid is injected into the tube through one of the two axial punches. Axial punches are movable and their action is required to provide axial compression and to feed material towards the center of the bulging tube. Transverse counterpunches may also be incorporated in the forming die in order to form protrusions with small diameter/length ratio. Transverse counter punches may also be used to punch holes in the work piece at the end of the forming process.

Designing the process has in the past been a challenging task, since initial analytical modeling is possible only for limited cases. [10] Advances in FEA and FEM in recent years has enabled hydroform processes to be more widely engineered for varieties of parts and materials. Often FEM simulations must be performed in order to find a feasible process solution and to define the correct loading curves: pressure vs. time and axial feed vs. time. [11] In the case of more complex tube hydroformed parts the tube must be pre-bent prior to loading into the hydroforming die. Bending is done sequentially along the length of the tube, with the tube being bent around bending discs (or dies) as the tube length is fed in. Bending can be done with or without mandrels. This additional complexity of process further increases the reliance on FEM for designing and evaluating manufacturing processes. The feasibility of a hydroforming process must take into consideration the initial tube material properties and its potential for variation, along with the bending process, hydraulic pressure throughout the forming process, in inclusion of axial feed or not, in order to predict metal formability.

Process sequence in tube hydroforming of a t-shape with counterpunch Tube hydroforming process sequence.gif
Process sequence in tube hydroforming of a t-shape with counterpunch

Typical tools

Tools and punches can be interchanged for different part requirements. One advantage of hydroforming is the savings on tools. For sheet metal only a draw ring and punch (metalworking) or male die is required. Depending on the part being formed, the punch can be made from epoxy, rather than metal. The bladder of the hydroform itself acts as the female die eliminating the need to fabricate it. This allows for changes in material thickness to be made with usually no necessary changes to the tool. However, dies must be highly polished and in tube hydroforming a two-piece die is required to allow opening and closing.

Geometry produced

Another advantage of hydroforming is that complex shapes can be made in one step. In sheet hydroforming with the bladder acting as the male die almost limitless geometries can be produced. However, the process is limited by the very high closing force required in order to seal the dies, especially for large panels and thick hard materials. Small concave corner radii are difficult to be completely calibrated, i.e. filled, because too large a pressure would be required. in fact, the die closing force can be very high, both in tube and sheet hydroforming and may easily overcome the maximum tonnage of the forming press. In order to keep the die closing force under prescribed limits, the maximum internal fluid pressure must be limited. This reduces the calibration abilities of the process, i.e. it reduces the possibility of forming parts with small concave radii. Limits of the sheet hydroforming process are due to risks of excessive thinning, fracture, wrinkling and are strictly related to the material formability and to a proper selection of process parameters (e.g. hydraulic pressure vs. time curve). Tube hydroforming can produce many geometric options as well, reducing the need for tube welding operations. Similar limitations and risks can be listed as in sheet hydroforming; however, the maximum closing force is seldom a limiting factor in tube hydroforming. [12]

Tolerances and surface finish

Hydroforming is capable of producing parts within tight tolerances including aircraft tolerances where a common tolerance for sheet metal parts is within 0.76 mm (1/30th of an inch). Metal hydroforming also allows for a smoother finish as draw marks produced by the traditional method of pressing a male and female die together are eliminated.

While springback has long been a topic of discussion for sheet metal forming operations it has been far less of a topic of research for tube hydroforming. This may in part be a result of the relatively low levels of springback naturally occurring when deforming the tubes into their closed section geometries. Tube Hydroformed sections by the nature of their closed sections are very rigid and do not display high degrees of elastic deformation under load. For this reason it is likely that negative residual stress induced during tube hydroforming might be insufficient to deform the part elastically after the completion of forming. However, as more and more tubular parts are being manufactured using high strength steel and advanced high strength steel [13] parts, springback must be accounted for in the design and manufacture of closed section tube hydroformed parts.

Examples

Notable examples include:

Sheet Hydro Forming

Tube Hydro Forming

See also

Related Research Articles

<span class="mw-page-title-main">Forging</span> Metalworking process

Forging is a manufacturing process involving the shaping of metal using localized compressive forces. The blows are delivered with a hammer or a die. Forging is often classified according to the temperature at which it is performed: cold forging, warm forging, or hot forging. For the latter two, the metal is heated, usually in a forge. Forged parts can range in weight from less than a kilogram to hundreds of metric tons. Forging has been done by smiths for millennia; the traditional products were kitchenware, hardware, hand tools, edged weapons, cymbals, and jewellery.

In materials science, superplasticity is a state in which solid crystalline material is deformed well beyond its usual breaking point, usually over about 400% during tensile deformation. Such a state is usually achieved at high homologous temperature. Examples of superplastic materials are some fine-grained metals and ceramics. Other non-crystalline materials (amorphous) such as silica glass and polymers also deform similarly, but are not called superplastic, because they are not crystalline; rather, their deformation is often described as Newtonian fluid. Superplastically deformed material gets thinner in a very uniform manner, rather than forming a "neck" that leads to fracture. Also, the formation of microvoids, which is another cause of early fracture, is inhibited. Superplasticity must not be confused with superelasticity.

A die is a specialized machine tool used in manufacturing industries to cut and/or form material to a desired shape or profile. Stamping dies are used with a press, as opposed to drawing dies and casting dies which are not. Like molds, dies are generally customized to the item they are used to create.

<span class="mw-page-title-main">Extrusion</span> Process of pushing material through a die to create long symmetrical-shaped objects

Extrusion is a process used to create objects of a fixed cross-sectional profile by pushing material through a die of the desired cross-section. Its two main advantages over other manufacturing processes are its ability to create very complex cross-sections; and to work materials that are brittle, because the material encounters only compressive and shear stresses. It also creates excellent surface finish and gives considerable freedom of form in the design process.

<span class="mw-page-title-main">Sheet metal</span> Metal formed into thin, flat pieces

Sheet metal is metal formed into thin, flat pieces, usually by an industrial process.

<span class="mw-page-title-main">Drawing (manufacturing)</span> Use of tensile forces to elongate a workpiece

Drawing is a manufacturing process that uses tensile forces to elongate metal, glass, or plastic. As the material is drawn (pulled), it stretches and becomes thinner, achieving a desired shape and thickness. Drawing is classified into two types: sheet metal drawing and wire, bar, and tube drawing. Sheet metal drawing is defined as a plastic deformation over a curved axis. For wire, bar, and tube drawing, the starting stock is drawn through a die to reduce its diameter and increase its length. Drawing is usually performed at room temperature, thus classified as a cold working process; however, drawing may also be performed at higher temperatures to hot work large wires, rods, or hollow tubes in order to reduce forces.

<span class="mw-page-title-main">Punching</span> Creating a hole by forcing a tool through the workpiece

Punching is a forming process that uses a punch press to force a tool, called a punch, through the workpiece to create a hole via shearing. Punching is applicable to a wide variety of materials that come in sheet form, including sheet metal, paper, vulcanized fibre and some forms of plastic sheet. The punch often passes through the work into a die. A scrap slug from the hole is deposited into the die in the process. Depending on the material being punched this slug may be recycled and reused or discarded.

<span class="mw-page-title-main">Stamping (metalworking)</span> Forming metal sheets with a stamping press

Stamping is the process of placing flat sheet metal in either blank or coil form into a stamping press where a tool and die surface forms the metal into a net shape. Stamping includes a variety of sheet-metal forming manufacturing processes, such as punching using a machine press or stamping press, blanking, embossing, bending, flanging, and coining. This could be a single stage operation where every stroke of the press produces the desired form on the sheet metal part, or could occur through a series of stages.

<span class="mw-page-title-main">Bending (metalworking)</span> Metalworking to produce a V-, U- or channel shape

Bending is a manufacturing process that produces a V-shape, U-shape, or channel shape along a straight axis in ductile materials, most commonly sheet metal. Commonly used equipment include box and pan brakes, brake presses, and other specialized machine presses. Typical products that are made like this are boxes such as electrical enclosures and rectangular ductwork.

<span class="mw-page-title-main">Deep drawing</span> Metalworking process

Deep drawing is a sheet metal forming process in which a sheet metal blank is radially drawn into a forming die by the mechanical action of a punch. It is thus a shape transformation process with material retention. The process is considered "deep" drawing when the depth of the drawn part exceeds its diameter. This is achieved by redrawing the part through a series of dies.

Metal bellows are elastic vessels that can be compressed when pressure is applied to the outside of the vessel, or extended under vacuum. When the pressure or vacuum is released, the bellows will return to its original shape, provided the material has not been stressed past its yield strength. They are used both for their ability to deform under pressure and to provide a hermetic seal that allows movement.

<span class="mw-page-title-main">Press brake</span> Machine for bending sheet and plate material

A press brake is a machine used for bending sheet metal and metal plate, most commonly sheet metal. It forms predetermined bends by clamping the workpiece between a matching top tool and bottom die.

Explosive forming is a metalworking technique in which an explosive charge is used instead of a punch or press. It can be used on materials for which a press setup would be prohibitively large or require an unreasonably high pressure, and is generally much cheaper than building a large enough and sufficiently high-pressure press; on the other hand, it is unavoidably an individual job production process, producing one product at a time and with a long setup time. There are various approaches; one is to place metal plate over a die, with the intervening space evacuated by a vacuum pump, place the whole assembly underwater, and detonate a charge at an appropriate distance from the plate. For complicated shapes, a segmented die can be used to produce in a single operation a shape that would require many manufacturing steps, or to be manufactured in parts and welded together with an accompanying loss of strength at the welds. There is often some degree of work hardening from the explosive-forming process, particularly in mild steel.

<span class="mw-page-title-main">Photochemical machining</span> Process that uses chemicals to machine sheet metal

Photochemical machining (PCM), also known as photochemical milling or photo etching, is a chemical milling process used to fabricate sheet metal components using a photoresist and etchants to corrosively machine away selected areas. This process emerged in the 1960s as an offshoot of the printed circuit board industry. Photo etching can produce highly complex parts with very fine detail accurately and economically.

<span class="mw-page-title-main">Rubber pad forming</span> Metalworking process

Rubber pad forming (RPF) is a metalworking process where sheet metal is pressed between a die and a rubber block, made of polyurethane. Under pressure, the rubber and sheet metal are driven into the die and conform to its shape, forming the part. The rubber pads can have a general purpose shape, like a membrane. Alternatively, they can be machined in the shape of die or punch.

Impact extrusion is a manufacturing process similar to extrusion and drawing by which products are made with a metal slug. The slug is pressed at a high velocity with extreme force into a die or mold by a punch.

Hot metal gas forming (HMGF) is a method of die forming in which a metal tube is heated to a pliable state, near to but below its melting point, then pressurized internally by a gas in order to form the tube outward into the shape defined by an enclosing die cavity. The high temperatures allow the metal to elongate, or stretch, to much greater degrees without rupture than are possible in previously utilized cold and warm forming methods. In addition, the metal can be formed into finer details and requires less overall forming force than traditional methods.

For sheet metal forming analysis within the metal forming process, a successful technique requires a non-contact optical 3D deformation measuring system. The system analyzes, calculates and documents deformations of sheet metal parts, for example. It provides the 3D coordinates of the component's surface as well as the distribution of major and minor strain on the surface and the material thickness reduction. In the Forming Limit Diagram, the measured deformations are compared to the material characteristics. The system supports optimization processes in sheet metal forming by means of;

<span class="mw-page-title-main">Metal spinning</span> Metalworking process

Metal spinning, also known as spin forming or spinning or metal turning most commonly, is a metalworking process by which a disc or tube of metal is rotated at high speed and formed into an axially symmetric part. Spinning can be performed by hand or by a CNC lathe.

<span class="mw-page-title-main">Liquid Impact Forming</span> Metalworking process

Liquid Impact Forming is a metalworking process in which the combined use of a stamping press and a liquid medium forms the desired shape on the workpiece. This technique is a synthesis of two metalworking processes; stamping (metalworking) and hydroforming. It is especially suited for the cold forming of tubular structural parts in automotive, railroad and aerospace industries.

References

  1. ↑ "The Hydroforming Process". Jones Metal Products. Retrieved 2011-06-21.
  2. ↑ "first HF patent" . Retrieved 17 July 2012.[ dead link ]
  3. ↑ U.S. patent 2,713,314
  4. ↑ Hatipoğlu, H. Ali; Polat, Naki; Köksal, Arif; Tekkaya, A.Erman (1 January 2007). "Modeling Flexforming (Fluid Cell Forming) Process with Finite Element Method". Key Engineering Materials. 344: 469–476. doi:10.4028/www.scientific.net/KEM.344.469. S2CID   137151717.
  5. ↑ Strano, M (2006). "Optimization under uncertainty of sheet-metal-forming processes by the finite element method". Proceedings of the Institution of Mechanical Engineers, Part B: Journal of Engineering Manufacture. 220 (8): 1305–1315. doi:10.1243/09544054JEM480. S2CID   108843522.
  6. ↑ Dachang, Kang; Yu, Chen; Yongchao, Xu (2005). "Hydromechanical deep drawing of superalloy cups". Journal of Materials Processing Technology. 166 (2): 243–246. doi:10.1016/j.jmatprotec.2004.08.024.
  7. ↑ "first thf patent" . Retrieved 17 July 2012.[ dead link ]
  8. ↑ Hydroforming for advanced manufacturing, Ed. by M, Koç, 2009 Woodhead Publishing Limited
  9. ↑ Hydroforming technology. (conference report): Advanced Materials & Processes (Refereed) : May 1, 1997: ASM International: v151  : n5  : p50(4)
  10. ↑ Asnafi, Nader (1999). "Analytical modelling of tube hydroforming". Thin-Walled Structures. 34 (4): 295–330. doi:10.1016/S0263-8231(99)00018-X.
  11. ↑ Strano, Matteo; Jirathearanat, Suwat; Shr, Shiuan-Guang; Altan, Taylan (2004). "Virtual process development in tube hydroforming". Journal of Materials Processing Technology. 146 (1): 130–136. doi:10.1016/S0924-0136(03)00853-7.
  12. ↑ "Hydroforming".
  13. ↑ Hertell (May 11, 2015). "Great Designs in Steel 2015" (PDF). Autosteel.org.
  14. ↑ Weinreb, Sander (8–11 July 2003). Low cost microwave ground terminals for space communication (PDF). 5th International symposium on reducing the cost of spacecraft ground systems and operations. Pasadena, CA: NASA. Archived from the original (PDF) on 20 March 2009. Retrieved 2008-11-21.
  15. 1 2 Harjinder Singh (2003). Fundamentals of Hydroforming. SME. p. 4. ISBN   978-0-87263-662-0.
  16. ↑ Tony Swan (July 2000). "2001 Pontiac Aztek - First Drive Review". Caranddriver.com. Retrieved 2008-12-05.
  17. ↑ Eric Lundin (24 July 2003). "Tier 1 supplier builds four-stage competitive strategy". The Fabricator. Retrieved 2008-12-05.
  18. ↑ "2009 Harley Davidson V-Rod Muscle". thekneeslider.com. Retrieved 2008-12-05.
  19. 1 2 "Hydroformed Frame Repairs". I-Car Advantage Online. 13 September 2004. Archived from the original on 21 October 2012. Retrieved 2008-12-05.
  20. ↑ "2006 Pontiac Solstice Sheetmetal Hydroforming Technology". The Auto Channel. Retrieved 2008-12-05.
  21. ↑ "Utility Vehicle has hydroformed steel frame". ThomasNet. 5 December 2003. Retrieved 2008-12-05.
  22. ↑ Silva, D. C.; Paschoarelli, L. C.; Medola, F. O. (2019). "Evaluation of Two Wheelchair Hand Rim Models: Contact Pressure Distribution in Straight Line and Curve Trajectories". Ergonomics. 62 (12): 1563–1571. doi:10.1080/00140139.2019.1660000. PMID   31446854. S2CID   201748187.

This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.