Polyphosphazene

Last updated
General structure of polyphosphazenes. Gray spheres represent any organic or inorganic group. PolyphosphazeneGeneralStructure.png
General structure of polyphosphazenes. Gray spheres represent any organic or inorganic group.

Polyphosphazenes include a wide range of hybrid inorganic-organic polymers with a number of different skeletal architectures with the backbone P-N-P-N-P-N-. [1] In nearly all of these materials two organic side groups are attached to each phosphorus center. Linear polymers have the formula (N=PR1R2)n, where R1 and R2 are organic (see graphic). Other architectures are cyclolinear and cyclomatrix polymers in which small phosphazene rings are connected together by organic chain units. Other architectures are available, such as block copolymer, star, dendritic, or comb-type structures. More than 700 different polyphosphazenes are known, with different side groups (R) and different molecular architectures. Many of these polymers were first synthesized and studied in the research group of Harry R. Allcock. [1] [2] [3] [4] [5]

Contents

Synthesis

The method of synthesis depends on the type of polyphosphazene. The most widely used method for linear polymers is based on a two-step process. [1] [2] [3] [4] In the first step, hexachlorocyclotriphosphazene(NPCl2)3 is heated in a sealed system at 250 °C to convert it to a long chain linear polymer with typically 15,000 or more repeating units. In the second step the chlorine atoms linked to phosphorus in the polymer are replaced by organic groups through reactions with alkoxides, aryloxides, amines or organometallic reagents. Because many different reagents can participate in this macromolecular substitution reaction, and because two or more reagents may be used, a large number of different polymers can be produced.. Variations to this process are possible using poly(dichlorophosphazene) made by condensation reactions. [6]

PolyphosphazeneSynthesis.png

Another synthetic process uses Cl3PNSiMe3 as a precursor: [7]

n Cl3PNSiMe3 --> [Cl2PN]n + ClSiMe3

Because the process is a living cationic polymerization, block copolymers or comb, star, or dendritic architectures are possible. [8] [9] Other synthetic methods include the condensation reactions of organic-substituted phosphoranimines. [10] [11] [12] [13]

Cyclomatrix type polymers made by linking small molecule phosphazene rings together employ difunctional organic reagents to replace the chlorine atoms in (NPCl2)3, or the introduction of allyl or vinyl substituents, which are then polymerized by free-radical methods. [14] Such polymers may be useful as coatings or thermosetting resins, often prized for their thermal stability.

Properties and uses

The linear high polymers have the geometry shown in the picture. More than 700 different macromolecules that correspond to e group]]s or combinations of different side groups. In these polymers the properties are defined by the high flexibility of the backbone. Other potentially attractive properties include radiation resistance, high refractive index, ultraviolet and visible transparency, and its fire resistance. The side groups exert an equal or even greater influence on the properties since they impart properties such as hydrophobicity, hydrophilicity, color, useful biological properties such as bioerodibility, or ion transport properties to the polymers. Representative examples of these polymers are shown below. PolyphosphazeneExamples.png

Thermoplastics

The first stable thermoplastic poly(organophosphazenes), isolated in the mid 1960s by Allcock, Kugel, and Valan, were macromolecules with trifluoroethoxy, phenoxy, methoxy, ethoxy, or various amino side groups. [2] [3] [4] Of these early species, poly[bis(trifluoroethoxyphosphazene], [NP(OCH2CF3)2]n, has proved to be the subject of intense research due to its crystallinity, high hydrophobicity, biological compatibility, fire resistance, general radiation stability, and ease of fabrication into films, microfibers and nanofibers. It has also been a substrate for various surface reactions to immobilize biological agents. The polymers with phenoxy or amino side groups have also been studied in detail.

Phosphazene elastomers

The first large-scale commercial uses for linear polyphosphazenes were in the field of high technology elastomers, with a typical example containing a combination of trifluoroethoxy and longer chain fluoroalkoxy groups. [15] [16] [17] [18] The mixture of two different side groups eliminates the crystallinity found in single-substituent polymers and allows the inherent flexibility and elasticity to become manifest. Glass transition temperatures as low as -60 °C are attainable, and properties such as oil-resistance and hydrophobicity are responsible for their utility in land vehicles and aerospace components. They have also been used in biostable biomedical devices. [19]

Other side groups, such as non-fluorinated alkoxy or oligo-alkyl ether units, yield hydrophilic or hydrophobic elastomers with glass transitions over a broad range from -100 °C to 100 °C. [20] Polymers with two different aryloxy side groups have also been developed as elastomers for fire-resistance as well as thermal and sound insulation applications.

Polymer electrolytes

Linear polyphosphazenes with oligo-ethyleneoxy side chains are gums that are good solvents for salts such as lithium triflate. These solutions function as electrolytes for lithium ion transport, and they were incorporated into fire-resistant rechargeable lithium-ion polymer battery. [21] [22] [23] The same polymers are also of interest as the electrolyte in dye-sensitized solar cells. [24] Other polyphosphazenes with sulfonated aryloxy side groups are proton conductors of interest for use in the membranes of proton exchange membrane fuel cells. [25]

Hydrogels

Water-soluble poly(organophosphazenes) with oligo-ethyleneoxy side chains can be cross-linked by gamma-radiation. The cross-linked polymers absorb water to form hydrogels, which are responsive to temperature changes, expanding to a limit defined by the cross-link density below a critical solution temperature, but contracting above that temperature. This is the basis of controlled permeability membranes. Other polymers with both oligo-ethyleneoxy and carboxyphenoxy side groups expand in the presence of monovalent cations but contract in the presence of di- or tri-valent cations, which form ionic cross-links. [26] [27] [28] [29] [30] Phosphazene hydrogels have been utilized for controlled drug release and other medical applications. [27]

Bioerodible polyphosphazenes

The ease with which properties can be controlled and fine-tuned by the linkage of different side groups to polyphosphazene chains has prompted major efforts to address biomedical materials challenges using these polymers. [31] Different polymers have been studied as macromolecular drug carriers, as membranes for the controlled delivery of drugs, as biostable elastomers, and especially as tailored bioerodible materials for the regeneration of living bone. [32] [33] [34] [35] An advantage for this last application is that poly(dichlorophosphazene) reacts with amino acid ethyl esters (such as ethyl glycinate or the corresponding ethyl esters of numerous other amino acids) through the amino terminus to form polyphosphazenes with amino acid ester side groups. These polymers hydrolyze slowly to a near-neutral, pH-buffered solution of the amino acid, ethanol, phosphate, and ammonium ion. The speed of hydrolysis depends on the amino acid ester, with half-lives that vary from weeks to months depending on the structure of the amino acid ester. Nanofibers and porous constructs of these polymers assist osteoblast replication and accelerate the repair of bone in animal model studies.

Commercial aspects

No applications are commercialized for polyphosphazenes. The cyclic trimer hexachlorophosphazene ((NPCl2)3) is commercially available. It is the starting point for most commercial developments. High performance elastomers known as PN-F or Eypel-F have been manufactured for seals, O-rings, and dental devices. An aryloxy-substituted polymer has also been developed as a fire resistant expanded foam for thermal and sound insulation. The patent literature contains many references to cyclomatrix polymers derived from cyclic trimeric phosphazenes incorporated into cross-linked resins for fire resistant circuit boards and related applications.

Related Research Articles

<span class="mw-page-title-main">Aspartic acid</span> Amino acid

Aspartic acid (symbol Asp or D; the ionic form is known as aspartate), is an α-amino acid that is used in the biosynthesis of proteins. Like all other amino acids, it contains an amino group and a carboxylic acid. Its α-amino group is in the protonated –NH+
3 form under physiological conditions, while its α-carboxylic acid group is deprotonated −COO− under physiological conditions. Aspartic acid has an acidic side chain (CH2COOH) which reacts with other amino acids, enzymes and proteins in the body. Under physiological conditions (pH 7.4) in proteins the side chain usually occurs as the negatively charged aspartate form, −COO−. It is a non-essential amino acid in humans, meaning the body can synthesize it as needed. It is encoded by the codons GAU and GAC.

In polymer chemistry, ring-opening polymerization (ROP) is a form of chain-growth polymerization, in which the terminus of a polymer chain attacks cyclic monomers to form a longer polymer. The reactive center can be radical, anionic or cationic. Some cyclic monomers such as norbornene or cyclooctadiene can be polymerized to high molecular weight polymers by using metal catalysts. ROP is a versatile method for the synthesis of biopolymers.

<span class="mw-page-title-main">Polythiophene</span>

Polythiophenes (PTs) are polymerized thiophenes, a sulfur heterocycle. The parent PT is an insoluble colored solid with the formula (C4H2S)n. The rings are linked through the 2- and 5-positions. Poly(alkylthiophene)s have alkyl substituents at the 3- or 4-position(s). They are also colored solids, but tend to be soluble in organic solvents.

<span class="mw-page-title-main">Electroactive polymer</span>

An electroactive polymer (EAP) is a polymer that exhibits a change in size or shape when stimulated by an electric field. The most common applications of this type of material are in actuators and sensors. A typical characteristic property of an EAP is that they will undergo a large amount of deformation while sustaining large forces.

<span class="mw-page-title-main">Hexachlorophosphazene</span> Chemical compound

Hexachlorophosphazene is an inorganic compound with the formula (NPCl2)3. The molecule has a cyclic, unsaturated backbone consisting of alternating phosphorus and nitrogen centers, and can be viewed as a trimer of the hypothetical compound N≡PCl2. Its classification as a phosphazene highlights its relationship to benzene. There is large academic interest in the compound relating to the phosphorus-nitrogen bonding and phosphorus reactivity.

Acyclic diene metathesis or 'ADMET' is a special type of olefin metathesis used to polymerize terminal dienes to polyenes:

An inorganic polymer is a polymer with a skeletal structure that does not include carbon atoms in the backbone. Polymers containing inorganic and organic components are sometimes called hybrid polymers, and most so-called inorganic polymers are hybrid polymers. One of the best known examples is polydimethylsiloxane, otherwise known commonly as silicone rubber. Inorganic polymers offer some properties not found in organic materials including low-temperature flexibility, electrical conductivity, and nonflammability. The term inorganic polymer refers generally to one-dimensional polymers, rather than to heavily crosslinked materials such as silicate minerals. Inorganic polymers with tunable or responsive properties are sometimes called smart inorganic polymers. A special class of inorganic polymers are geopolymers, which may be anthropogenic or naturally occurring.

<span class="mw-page-title-main">Janus particles</span> Type of nanoparticle or microparticle

Janus particles are special types of nanoparticles or microparticles whose surfaces have two or more distinct physical properties. This unique surface of Janus particles allows two different types of chemistry to occur on the same particle. The simplest case of a Janus particle is achieved by dividing the particle into two distinct parts, each of them either made of a different material, or bearing different functional groups. For example, a Janus particle may have one-half of its surface composed of hydrophilic groups and the other half hydrophobic groups, the particles might have two surfaces of different color, fluorescence, or magnetic properties. This gives these particles unique properties related to their asymmetric structure and/or functionalization.

Poly(N-isopropylacrylamide) (variously abbreviated PNIPA, PNIPAM, PNIPAAm, NIPA, PNIPAA or PNIPAm) is a temperature-responsive polymer that was first synthesized in the 1950s. It can be synthesized from N-isopropylacrylamide which is commercially available. It is synthesized via free-radical polymerization and is readily functionalized making it useful in a variety of applications.

<span class="mw-page-title-main">Temperature-responsive polymer</span> Polymer showing drastic changes in physical properties with temperature

Temperature-responsive polymers or thermoresponsive polymers are polymers that exhibit drastic and discontinuous changes in their physical properties with temperature. The term is commonly used when the property concerned is solubility in a given solvent, but it may also be used when other properties are affected. Thermoresponsive polymers belong to the class of stimuli-responsive materials, in contrast to temperature-sensitive materials, which change their properties continuously with environmental conditions. In a stricter sense, thermoresponsive polymers display a miscibility gap in their temperature-composition diagram. Depending on whether the miscibility gap is found at high or low temperatures, either an upper critical solution temperature (UCST) or a lower critical solution temperature (LCST) exists.

<span class="mw-page-title-main">Oxazoline</span> Chemical compound

Oxazoline is a five-membered heterocyclic organic compound with the formula C3H5NO. It is the parent of a family of compounds called oxazolines, which contain non-hydrogenic substituents on carbon and/or nitrogen. Oxazolines are the unsaturated analogues of oxazolidines, and they are isomeric with isoxazolines, where the N and O are directly bonded. Two isomers of oxazoline are known, depending on the location of the double bond.

<span class="mw-page-title-main">Poly(methacrylic acid)</span> Chemical compound

Poly(methacrylic acid) (PMAA) is a polymer made from methacrylic acid, which is a carboxylic acid. It is often available as its sodium salt, poly(methacrylic acid) sodium salt. The monomer is a viscous liquid with a pungent odour. The first polymeric form of methacrylic acid was described in 1880 by Engelhorn and Fittig. The use of high purity monomers is required for proper polymerization conditions and therefore it is necessary to remove any inhibitors by extraction or via distillation. To prevent inhibition by dissolved oxygen, monomers should be carefully degassed prior to the start of the polymerization.

<span class="mw-page-title-main">Polyaspartic acid</span> Chemical compound

Polyaspartic acid (PASA) is a biodegradable, water-soluble condensation polymer based on the amino acid aspartic acid. It is a biodegradable replacement for water softeners and related applications. PASA can be chemically crosslinked with a wide variety of methods to yield PASA hydrogels. The resulting hydrogels are pH-sensitive such that under acidic conditions, they shrink, while the swelling capacity increases under alkaline conditions.

Self-healing hydrogels are a specialized type of polymer hydrogel. A hydrogel is a macromolecular polymer gel constructed of a network of crosslinked polymer chains. Hydrogels are synthesized from hydrophilic monomers by either chain or step growth, along with a functional crosslinker to promote network formation. A net-like structure along with void imperfections enhance the hydrogel's ability to absorb large amounts of water via hydrogen bonding. As a result, hydrogels, self-healing alike, develop characteristic firm yet elastic mechanical properties. Self-healing refers to the spontaneous formation of new bonds when old bonds are broken within a material. The structure of the hydrogel along with electrostatic attraction forces drive new bond formation through reconstructive covalent dangling side chain or non-covalent hydrogen bonding. These flesh-like properties have motivated the research and development of self-healing hydrogels in fields such as reconstructive tissue engineering as scaffolding, as well as use in passive and preventive applications.

<span class="mw-page-title-main">Star-shaped polymer</span>

Star-shaped polymers are the simplest class of branched polymers with a general structure consisting of several linear chains connected to a central core. The core, or the center, of the polymer can be an atom, molecule, or macromolecule; the chains, or "arms", consist of variable-length organic chains. Star-shaped polymers in which the arms are all equivalent in length and structure are considered homogeneous, and ones with variable lengths and structures are considered heterogeneous.

<span class="mw-page-title-main">Graft polymer</span> Polymer with a backbone of one composite and random branches of another composite

In polymer chemistry, graft polymers are segmented copolymers with a linear backbone of one composite and randomly distributed branches of another composite. The picture labeled "graft polymer" shows how grafted chains of species B are covalently bonded to polymer species A. Although the side chains are structurally distinct from the main chain, the individual grafted chains may be homopolymers or copolymers. Graft polymers have been synthesized for many decades and are especially used as impact resistant materials, thermoplastic elastomers, compatibilizers, or emulsifiers for the preparation of stable blends or alloys. One of the better-known examples of a graft polymer is a component used in high impact polystyrene, consisting of a polystyrene backbone with polybutadiene grafted chains.

Amino acid N-carboxyanhydrides, also called Leuchs' anhydrides, are a family of heterocyclic organic compounds derived from amino acids. They are white, moisture-reactive solids. They have been evaluated for applications the field of biomaterials.

A photolabile protecting group is a chemical modification to a molecule that can be removed with light. PPGs enable high degrees of chemoselectivity as they allow researchers to control spatial, temporal and concentration variables with light. Control of these variables is valuable as it enables multiple PPG applications, including orthogonality in systems with multiple protecting groups. As the removal of a PPG does not require chemical reagents, the photocleavage of a PPG is often referred to as "traceless reagent processes", and is often used in biological model systems and multistep organic syntheses. Since their introduction in 1962, numerous PPGs have been developed and utilized in a variety of wide-ranging applications from protein science to photoresists. Due to the large number of reported protecting groups, PPGs are often categorized by their major functional group(s); three of the most common classifications are detailed below.

β-Butyrolactone Chemical compound

β-Butyrolactone is the intramolecular carboxylic acid ester (lactone) of the optically active 3-hydroxybutanoic acid. It is produced during chemical synthesis as a racemate. β-Butyrolactone is suitable as a monomer for the production of the biodegradable polyhydroxyalkanoate poly(3-hydroxybutyrate) (PHB). Polymerisation of racemic (RS)-β-butyrolactone provides (RS)-polyhydroxybutyric acid, which, however, is inferior in essential properties to the (R)-poly-3-hydroxybutyrate originating from natural sources.

<span class="mw-page-title-main">Polysulfobetaine</span> Dipolar ion polymer

Polysulfobetaines are zwitterionic polymers that contain a positively charged quaternary ammonium and a negatively charged sulfonate group within one constitutional repeat unit. In recent years, polysulfobetaines have received increasing attention owing to their good biotolerance and ultralow-fouling behavior towards surfaces. These properties are mainly referred to a tightly bound hydration layer around each zwitterionic group, which effectively suppresses protein adsorption and thus, improves anti-fouling behavior. Therefore, polysulfobetaines have been typically employed as ultrafiltration membranes, blood-contacting devices, and drug delivery materials.

References

  1. 1 2 3 Allcock, H. R., Kugel, R. L. (1965). "Synthesis of High Polymeric Alkoxy and Aryloxyphosphonitriles". Journal of the American Chemical Society. 87 (18): 4216–4217. doi:10.1021/ja01096a056.{{cite journal}}: CS1 maint: multiple names: authors list (link)
  2. 1 2 3 Allcock, H. R., Kugel, R. L., Valan, K. J. (1966). "Phosphonitrilic Compounds. VI. High Molecular Weight Poly(alkoxy- and aryloxyphosphazenes)". Inorganic Chemistry. 5 (10): 1709–1715. doi:10.1021/ic50044a016.{{cite journal}}: CS1 maint: multiple names: authors list (link)
  3. 1 2 3 Allcock, H. R., Kugel, R. L. (1966). "Phosphonitrilic Compounds. VII. High Molecular Weight Poly(diaminophosphazenes)". Inorganic Chemistry. 5 (10): 1716–1718. doi:10.1021/ic50044a017.{{cite journal}}: CS1 maint: multiple names: authors list (link)
  4. 1 2 3 "Allcock Research Group Web Site".
  5. ↑ Allcock, Harry R. (2003). Chemistry and Applications of Polyphosphazenes. Wiley-Interscience.
  6. ↑ Gleria, M., De Jaeger, R. and Potin, P. (2004). Synthesis and Characterization of Poly(organophosphazenes). New York: Nova Science Publishers.{{cite book}}: CS1 maint: multiple names: authors list (link)
  7. ↑ Rothemund, Sandra; Teasdale, Ian (2016). "Preparation of polyphosphazenes: A tutorial review". Chemical Society Reviews. 45 (19): 5200–5215. doi: 10.1039/C6CS00340K . PMC   5048340 . PMID   27314867.
  8. ↑ Honeyman, C. H., Manners, I., Morrissey, C. T., Allcock, H. R. (1995). "Ambient Temperature Synthesis of Poly(dichlorophosphazene) with Molecular Weight Control". Journal of the American Chemical Society. 117 (26): 7035–7036. doi:10.1021/ja00131a040.{{cite journal}}: CS1 maint: multiple names: authors list (link)
  9. ↑ Allcock, H. R., Crane, C. A., Morrissey, C. T., Nelson, J. M., Reeves, S. D., Honeyman, C. H., Manners, I. (1996). ""Living" Cationic Polymerization of Phosphoranimines as an Ambient Temperature Route to Polyphosphazenes with Controlled Molecular Weights". Macromolecules. 29 (24): 7740–7747. Bibcode:1996MaMol..29.7740A. doi:10.1021/ma960876j.{{cite journal}}: CS1 maint: multiple names: authors list (link)
  10. ↑ Wisian-Neilson, P.; Neilson, R. H. (1980). "Poly(dimethylphosphazene), (Me2PN)n". Journal of the American Chemical Society. 102 (8): 2848–2849. doi:10.1021/ja00528a060.
  11. ↑ Neilson, R. H., Wisian Neilson, P. (1988). "Poly(alkyl/arylphosphazenes) and their precursors". Chemical Reviews. 88 (3): 541–562. doi:10.1021/cr00085a005.{{cite journal}}: CS1 maint: multiple names: authors list (link)
  12. ↑ Montague, R. A., Matyjaszewski, K. (1990). "Synthesis of Poly[bis(trifluoroethoxy)phosphazene] under Mild Conditions using a Fluoride Initiator". Journal of the American Chemical Society. 112 (18): 6721–6723. doi:10.1021/ja00174a047.{{cite journal}}: CS1 maint: multiple names: authors list (link)
  13. ↑ Matyjaszewski, K., Moore, M. M., White (1993). "Synthesis of Polyphosphazene Block Copolymers bearing Alkoxyethoxy and Trifluoroethoxy Groups". Macromolecules. 26 (25): 6741–6748. Bibcode:1993MaMol..26.6741M. doi:10.1021/ma00077a008.{{cite journal}}: CS1 maint: multiple names: authors list (link)
  14. ↑ Allen, C. W., Shaw, J. C., Brown, D. E. (1988). "Copolymerization of ((alpha-methylethenyl)phenyl)pentafluorocyclotriphosphazenes with Styrene and Methyl Methacrylate". Macromolecules. 21 (9): 2653–2657. Bibcode:1988MaMol..21.2653A. doi:10.1021/ma00187a001.{{cite journal}}: CS1 maint: multiple names: authors list (link)
  15. ↑ Rose, S. H. (1968). "Synthesis of Phosphonitrilic Fluoroelastomers". Journal of Polymer Science Part B: Polymer Letters. 6 (12): 837–839. Bibcode:1968JPoSL...6..837R. doi:10.1002/pol.1968.110061203.
  16. ↑ Singler, R. E., Schneider, N. S., Hagnauer, G. L. (1975). "Polyphosphazenes: Synthesis—properties—Applications". Polymer Engineering and Science. 15 (5): 321–338. doi:10.1002/pen.760150502.{{cite journal}}: CS1 maint: multiple names: authors list (link)
  17. ↑ US 4945139,Charles H. Kolich; W. Dirk Klobucar& Jeffrey T. Books,"Process for surface treating phosphonitrilic fluoroelastomers",published Jul 31, 1990, assigned to Ethyl Corporation
  18. ↑ Tate, D. P. (1974). "Polyphosphazene Elastomers". Journal of Polymer Science: Polymer Symposia. 48: 33–45. doi:10.1002/polc.5070480106.
  19. ↑ Gettleman, L.; Farris, C. L.; Rawls, H. R. & LeBouef, R. J. (1984). "Soft and Firm Denture Liner for a Composite Denture and Method of Fabricating".{{cite journal}}: Cite journal requires |journal= (help)
  20. ↑ Weikel, Arlin L.; Lee, David K.; Krogman, Nicholas R.; Allcock, Harry R. (2011). "Phase changes of poly(alkoxyphosphazenes), and their behavior in the presence of oligoisobutylene". Polymer Engineering & Science. 51 (9): 1693–1700. doi:10.1002/pen.21623.
  21. ↑ Blonsky, P. M.; Shriver, D. F.; Austin, P. E.; Allcock, H. R. (1984). "Polyphosphazene solid electrolytes". Journal of the American Chemical Society. 106 (22): 6854–6855. doi:10.1021/ja00334a071. Archived from the original on September 24, 2017.
  22. ↑ H. R.; O’Connor, S. J. M.; Olmeijer, D. L.; Napierala, M. E.; Cameron, C. G. (1996). "Cation Complexation and Conductivity in Crown Ether Bearing Polyphosphazenes". Macromolecules. 29 (23): 7544–7552. Bibcode:1996MaMol..29.7544A. doi:10.1021/ma960592z.
  23. ↑ Fei, S.-T.; Allcock, H. R. (2010). "Methoxyethoxyethoxyphosphazenes as Ionic Conductive Fire Retardant /additives for Lithium Battery Systems". Journal of Power Sources. 195 (7): 2082–2088. Bibcode:2010JPS...195.2082F. doi:10.1016/j.jpowsour.2009.09.043.
  24. ↑ Fei, S.-T; Lee, S.-H. A; Pursel, S. M.; Basham, J.; Hess, A.; Grimes, C. A.; Horn, M. W.; Mallouk, T. E.; Allcock, H. R. (2011). "Electrolyte Infiltration in Phosphazene-Based Dye-Sensitized Solar Cells". Journal of Power Sources. 21 (11): 2641–2651. Bibcode:2011JPS...196.5223F. doi:10.1016/j.jpowsour.2011.01.052.
  25. ↑ Tang, H.; Pintauro, P. N. (2001). "Polyphosphazene membranes. IV. Polymer morphology and proton conductivity in sulfonated poly[bis(3-methylphenoxy)phosphazene] films". Journal of Applied Polymer Science. 79: 49–59. doi:10.1002/1097-4628(20010103)79:1<49::aid-app60>3.0.co;2-j.
  26. ↑ H. R. Allcock; S. Kwon; G. H. Riding; R. J. Fitzpatrick; J. L. Bennett (1988). "Hydrophilic Polyphosphazenes as Hydrogels: Radiation Cr osslinking and Hydrogel Characteristics of Poly[bis(methoxyethoxyethoxy)phosphazene]". Biomaterials. 9 (6): 509–513. doi:10.1016/0142-9612(88)90046-4. PMID   3224138.
  27. 1 2 Kim, J.; Chun, C.; Kim, B.; Hong, J. M.; Cho J.–K; Lee. S. H. & Song, S.–C. (2012). "Thermosensitive/magnetic poly(organophosphazene) hydrogel as a long-term magnetic resonance contrast platform". Biomaterials. 33 (1): 218–224. doi:10.1016/j.biomaterials.2011.09.033. PMID   21975461.
  28. ↑ H. R. Allcock; S. R. Pucher; M. L. Turner; R. J. Fitzpatrick (1992). "Poly(organophosphazenes) with Poly(alkyl ether) Side Groups: A Study of Their Water Solubility and the Swelling Characteristics of Their Hydrogels". Macromolecules. 25 (21): 5573–5577. Bibcode:1992MaMol..25.5573A. doi:10.1021/ma00047a002.
  29. ↑ . R. Allcock; R. J. Fitzpatrick; K. B. Visscher (1992). "Thin-layer grafts of poly[bis((methoxyethoxy)ethoxy)phosphazene] on organic polymer surfaces". Chemistry of Materials. 4 (4): 775–780. doi:10.1021/cm00022a007.
  30. ↑ H. R. Allcock; A. M. A. Ambrosio (1996). "Synthesis and Characterization of pH-Senstitive Poly(organophosphazene) Hydrogels". Biomaterials. 17 (23): 2295–2302. doi:10.1016/0142-9612(96)00073-7. PMID   8968526.
  31. ↑ Chen, Feiyang; Teniola, Oyindamola R.; Laurencin, Cato T. (2022-04-01). "Biodegradable polyphosphazenes for regenerative engineering". Journal of Materials Research. 37 (8): 1417–1428. doi: 10.1557/s43578-022-00551-z . ISSN   2044-5326. S2CID   248257951.
  32. ↑ Allcock, H. R.; Pucher, S. R.; Scopelianos, A. G. (1994). "Poly[amino acid ester)phosphazenes] as Substrates for the Controlled Release of Small Molecules". Biomaterials. 15 (8): 563–569. doi:10.1016/0142-9612(94)90205-4. PMID   7948574.
  33. ↑ Deng, M., Kumbar, S. G., Wan, Y. Toti, U. S. Allcock, H. R., Laurencin, C. T. (2010). "Polyphosphazene Polymers for Tissue Engineering: An Analysis of Material Synthesis, Characterization, and Applications". Soft Matter. 6 (14): 3119–3132. Bibcode:2010SMat....6.3119D. doi:10.1039/b926402g.{{cite journal}}: CS1 maint: multiple names: authors list (link)
  34. ↑ Deng, M., Kumbar, S. G., Nair, L. S. Arlin L. Weikel, A. L, Allcock, H. R., Laurencin, C. T. (2011). "Biomimetic Structures: Biological Implications of Dipeptide-Substituted Polyphosphazene–Polyester Blend Nanofiber Matrices for Load-Bearing Bone Regeneration". Advanced Functional Materials. 21 (14): 2641–2651. doi:10.1002/adfm.201100275. S2CID   96953240.{{cite journal}}: CS1 maint: multiple names: authors list (link)
  35. ↑ Allcock, H. R.; Morozowich, N. (2012). "Bioerodible Polyphosphazenes and their Medical Potential". Polymer Chemistry. 3 (3): 578–590. doi:10.1039/c1py00468a.

Further information

"H. R. Allcock Research Group" . Retrieved 2020-08-22.

This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.