Precision glass moulding is a replicative process that allows the production of high precision optical components from glass without grinding and polishing. The process is also known as ultra-precision glass pressing. It is used to manufacture precision glass lenses for consumer products such as digital cameras, and high-end products like medical systems. The main advantage over mechanical lens production is that complex lens geometries such as aspheres can be produced cost-efficiently.
The precision glass moulding process consists of six steps: [1] [2]
The process is executed on a specialized moulding machine, which precisely controls the temperature, travel, and force during the process. The tools used must withstand high temperatures and pressures, and need to be resistant to chemical interaction with the glass. The mold materials also have to be suitable for machining into the precise surface profiles.
In order to ensure the desired quality the parts are measured between each process step. Additionally, the parts are handled and transported carefully between the processing and metrology steps.
Precision glass moulding can be used to produce a large variety of optical form elements such as spheres, aspheres, free-form elements and array-structures.
Concerning the curvature of the lens elements, the following statements can be drawn: Acceptable lens shapes are most bi-convex, plano-convex and mild meniscus shapes. Not unacceptable but hard to mould are bi-concave lenses, steep meniscus lenses, and lenses with severe features (e.g. a bump on a convex surface). In general, plano-curved lenses are easier to mould than lenses with both sides curved since matching of flat faces is easier. Moulding concave forms with small centre thickness is difficult due to sticking of the moulded part to the mould occurring as a result of the different thermal expansion coefficients. Furthermore, it is recommended to avoid undercuts and sharp edges. For the lens design it should be considered that the lens has to be mountable in measurement systems.
The shape of the preform or "blank" needs to be chosen according to the geometry of the finished optical element. Possible preforms are spherical (ball), near spherical (gob), plano-plano, plano-convex, plano-concave, biconvex and biconcave blanks. Ball and gob-blanks do not have to be premachined whereas other preforms require grinding and polishing. [3]
The following section describes basic traits of preform choice:
“Used specifically for lenses with positive power: biconvex, plano-convex, and meniscus where the convex side is stronger than the concave side, this only works for a relatively small volume of material.” [4]
“As a lens changes to negative in power biconcave, plano-concave, and meniscus where the concave side is stronger, an alternative preform shape, plano-plano, is required for the molding process. […] Relative to a formed preform an increase in cost is observed for the manufacturing of this type of preform.” [4]
“When the geometry of a lens extends beyond the volume range of a formed ball preform, a ground and polished ball preform is required. Used for lenses with positive power: biconvex, plano-convex, and meniscus: where the convex side is stronger, this geometry allows for molding of lenses with larger total volume. […] Relative to a formed preform and a plano-plano preform, an increase in cost is observed for the manufacturing of this type of preform.” [4]
“The Lenslet preform is primarily for lenses with positive power, biconvex, planoconvex, and meniscus: where the convex side is the strongest surface. The use of this type of preform allows for molding of the largest volume of glass at any given time in the molding machines. The Lenslet is traditionally ground and polished to a near net shape of the final lens, and then pressed. [...] The cost associated with the manufacturing of the lenslet preform is the highest of all preform types.” [4]
Precision gobs can be used as preforms for the production of aspherical lenses in a precision molding process. They are manufactured from a continuous glass melting process. The resulting precision gobs exhibit a very smooth firepolished surface with an excellent surface roughness and high volume accuracy.
The dimensions of the optical elements that can be moulded depend on the size of the moulding machine. The precision glass moulding process is not limited to small optics. For the right element geometry, it can enable economical production of aspheric lenses up to 60 mm in diameter and more than 20 mm thick. [5]
General design recommendations:
Size:
Radius:
Optical Surfaces:
Volume:
Although the form, dimensional and positional tolerances that can be achieved in precision glass moulding are subject to a natural border, the values being achieved in practice strongly depend on the degree of control and experience in mould making and moulding. The table below gives an overview of achievable manufacturing tolerances in precision glass moulding at different companies. [8]
| Parameter | Rochester Precision Optics [9] | Braunecker [10] | Lightpath Technologies [11] !! Ingeneric [12] !! | ||
|---|---|---|---|---|---|
| Diameter | +0/-0.010 mm | +/-0.005 mm | 0,005 mm | +/- 0.005 mm | |
| Center thickness | +/-0,012 mm | +/- 0.010 mm | 0,010 mm | +/- 0.01 mm | |
| Alignment | 2,5 min (axis) | < 1.5min (angular) | 5 μm | - | 5 μm |
| Scratch-Dig | 20-10 | 20-10/10-5 | - | 20-10 | |
| Abbe-Number | +/-0.5% | +/-1% | 1% | - | |
| Surface Roughness | - | <3 nm | <3 nm | 5 nm | 4 nm |
| Index of Refraction | +/-0.0003 | +/-0.001 | 0,001 | - | |
| Wedge | 0.01mm | +/-1 arcmin | 1 arcmin | 3' | |
| RMS WFE | Diffraction Limited |
For aspherical lenses, the design should be able to tolerate 0.010 mm of lateral shear between surfaces plus 5 micrometres Total Internal Reflection of wedge (across the part without considering the lateral shear) to be considered robust. [7]
Specifications for aspheres: [6]
Due to the fast cooling after moulding, the part retains a small amount of residual stress. Consequently, the glass exhibits a small change in the refractive index which has to be considered in the optical design. A higher cooling rate corresponds to a larger decrease of the refractive index. A lower cooling rate could circumvent the index drop, but would be less cost-efficient [4]
Many glasses can be used with PGM. However, there are some limitations: [4]
So-called "low-Tg-glasses" with a maximum transition temperature of less than 550 °C have been developed in order to enable new manufacturing routes for the moulds. Mould materials such as steel can be used for moulding low-Tg-glasses whereas high-Tg–glasses require a high-temperature mould material, such as tungsten carbide.
The mould material must have sufficient strength, hardness and accuracy at high temperature and pressure. Good oxidation resistance, low thermal expansion and high thermal conductivity are also required. The material of the mould has to be suitable to withstand the process temperatures without undergoing deforming processes. Therefore, the mould material choice depends critically on the transition temperature of the glass material. For low-Tg-glasses, steel moulds with a nickel alloy coating can be used. Since they cannot withstand the high temperatures required for regular optical glasses, heat-resistant materials such as carbide alloys have to be used instead in this case. In addition, mould materials include aluminium alloys, glasslike or vitreous carbon, silicon carbide, silicon nitride and a mixture of silicon carbide and carbon. [18]
A commonly used material in mould making is tungsten carbide. The mould inserts are produced by means of powder metallurgy, i.e. a sintering process followed by post-machining processes and sophisticated grinding operations. Most commonly a metallic binder (usually cobalt) is added in liquid phase sintering. In this process, the metallic binder improves the toughness of the mould as well as the sintering quality in the liquid phase to fully dense material. [19] Moulds made of hard materials have a typical lifetime of thousands of parts (size dependent) and are cost-effective for volumes of 200-1000+ (depending upon the size of the part).
This article describes how mould inserts are manufactured for precision glass moulding.
In order to ensure high quality standards metrology steps are implemented between each process step.
In order to save the quality and enable an early warning in case of any problems between every single step there has to be a step of measurement and referencing. Besides that the time for transport and handling has to be taken into account in the planning of the process.
Once process and tool have been developed, precision glass moulding has a great advantage over conventional production techniques. The majority of the lens quality characteristics are tool-bound. This means that lenses, which are pressed with the same tool and process, usually have only insignificantly small deviations. For example, an important characteristic of a lens is the form of the optical surface. In the case of aspherical lenses the measurement of optical surfaces is very difficult and connected to high efforts. Additionally, when working with tactile measurement systems there is always a risk that the optical surface might be scratched. For precision moulded lenses such measurements are only necessary for a small amount of sample lenses in order to qualify the tool. The series production can then be executed without further need for measurements. In this case, only the cleanliness of the optical surface has to be monitored. Another advantage is that the lens' center thickness can be estimated from the easily measurable edge thickness or by applying a contactless measurement system. [20]
In order to enhance the mould insert's lifetime, protective coatings can be applied. “The materials that have been selected for the antistick coatings can be divided into 5 groups including: (1) single layer carbides, nitrides, oxides and borides such as TiN, BN, TiAlN, NiAlN, TiBC, TiBCN, NiCrSiB and Al2O3, (2) nitrides or carbides based gradient and multilayers, (3) nitrides based superlattice films, (4) amorphous carbon or diamond-like carbon and (5) precious metal based alloys” [21]
Experiments carried out by Ma et al. yield the following results: [21] “The higher the temperature, the smaller the wetting angle between glass gob and substrate could be observed. This indicates that severe interface chemical reaction occurred and resulted in the loss of transparency in glass appearance. The wetting experiment in nitrogen ambient improved the sticking situation. The combination of chemically stable substrates and coatings, such as Sapphire (substrate) / GaN (film) and Glass (substrate) / Al2O3 (film) can achieve the best antistick propose. The precious metal films such as PtIr (Platinum, Iridium) coated on the ceramic substrates can effectively reduce the interface reaction between the glass and substrates.”
Although PtIr is used as a standard coating material, it has the disadvantage of being expensive. Therefore, research activities aim at substituting PtIr with cheaper materials.
A ceramic is any of the various hard, brittle, heat-resistant, and corrosion-resistant materials made by shaping and then firing an inorganic, nonmetallic material, such as clay, at a high temperature. Common examples are earthenware, porcelain, and brick.
A lens is a transmissive optical device that focuses or disperses a light beam by means of refraction. A simple lens consists of a single piece of transparent material, while a compound lens consists of several simple lenses (elements), usually arranged along a common axis. Lenses are made from materials such as glass or plastic and are ground, polished, or molded to the required shape. A lens can focus light to form an image, unlike a prism, which refracts light without focusing. Devices that similarly focus or disperse waves and radiation other than visible light are also called "lenses", such as microwave lenses, electron lenses, acoustic lenses, or explosive lenses.
A corrective lens is a transmissive optical device that is worn on the eye to improve visual perception. The most common use is to treat refractive errors: myopia, hypermetropia, astigmatism, and presbyopia. Glasses or "spectacles" are worn on the face a short distance in front of the eye. Contact lenses are worn directly on the surface of the eye. Intraocular lenses are surgically implanted most commonly after cataract removal but can be used for purely refractive purposes.
Injection moulding is a manufacturing process for producing parts by injecting molten material into a mould, or mold. Injection moulding can be performed with a host of materials mainly including metals, glasses, elastomers, confections, and most commonly thermoplastic and thermosetting polymers. Material for the part is fed into a heated barrel, mixed, and injected into a mould cavity, where it cools and hardens to the configuration of the cavity. After a product is designed, usually by an industrial designer or an engineer, moulds are made by a mould-maker from metal, usually either steel or aluminium, and precision-machined to form the features of the desired part. Injection moulding is widely used for manufacturing a variety of parts, from the smallest components to entire body panels of cars. Advances in 3D printing technology, using photopolymers that do not melt during the injection moulding of some lower-temperature thermoplastics, can be used for some simple injection moulds.
Powder metallurgy (PM) is a term covering a wide range of ways in which materials or components are made from metal powders. PM processes can reduce or eliminate the need for subtractive processes in manufacturing, lowering material losses and reducing the cost of the final product.
Fibre-reinforced plastic is a composite material made of a polymer matrix reinforced with fibres. The fibres are usually glass, carbon, aramid, or basalt. Rarely, other fibres such as paper, wood, boron, or asbestos have been used. The polymer is usually an epoxy, vinyl ester, or polyester thermosetting plastic, though phenol formaldehyde resins are still in use.
Diamond turning is turning using a cutting tool with a diamond tip. It is a process of mechanical machining of precision elements using lathes or derivative machine tools equipped with natural or synthetic diamond-tipped tool bits. The term single-point diamond turning (SPDT) is sometimes applied, although as with other lathe work, the "single-point" label is sometimes only nominal. The process of diamond turning is widely used to manufacture high-quality aspheric optical elements from crystals, metals, acrylic, and other materials. Plastic optics are frequently molded using diamond turned mold inserts. Optical elements produced by the means of diamond turning are used in optical assemblies in telescopes, video projectors, missile guidance systems, lasers, scientific research instruments, and numerous other systems and devices. Most SPDT today is done with computer numerical control (CNC) machine tools. Diamonds also serve in other machining processes, such as milling, grinding, and honing. Diamond turned surfaces have a high specular brightness and require no additional polishing or buffing, unlike other conventionally machined surfaces.
Compression molding is a method of molding in which the molding material, generally preheated, is first placed in an open, heated mold cavity. The mold is closed with a top force or plug member, pressure is applied to force the material into contact with all mold areas, while heat and pressure are maintained until the molding material has cured; this process is known as compression molding method and in case of rubber it is also known as 'Vulcanisation'. The process employs thermosetting resins in a partially cured stage, either in the form of granules, putty-like masses, or preforms.
Blow molding is a manufacturing process for forming hollow plastic parts. It is also used for forming glass bottles or other hollow shapes.
An end mill is a type of milling cutter, a cutting tool used in industrial milling applications. It is distinguished from the drill bit in its application, geometry, and manufacture. While a drill bit can only cut in the axial direction, most milling bits can cut in the radial direction. Not all mills can cut axially; those designed to cut axially are known as end mills.
An aspheric lens or asphere is a lens whose surface profiles are not portions of a sphere or cylinder. In photography, a lens assembly that includes an aspheric element is often called an aspherical lens.
An optical fiber, or optical fibre, is a flexible glass or plastic fiber that can transmit light from one end to the other. Such fibers find wide usage in fiber-optic communications, where they permit transmission over longer distances and at higher bandwidths than electrical cables. Fibers are used instead of metal wires because signals travel along them with less loss and are immune to electromagnetic interference. Fibers are also used for illumination and imaging, and are often wrapped in bundles so they may be used to carry light into, or images out of confined spaces, as in the case of a fiberscope. Specially designed fibers are also used for a variety of other applications, such as fiber optic sensors and fiber lasers.
Compact disc manufacturing is the process by which commercial compact discs (CDs) are replicated in mass quantities using a master version created from a source recording. This may be either in audio form (CD-DA) or data form (CD-ROM). This process is used in the mastering of read-only compact discs. DVDs and Blu-rays use similar methods.
Optical lens design is the process of designing a lens to meet a set of performance requirements and constraints, including cost and manufacturing limitations. Parameters include surface profile types, as well as radius of curvature, distance to the next surface, material type and optionally tilt and decenter. The process is computationally intensive, using ray tracing or other techniques to model how the lens affects light that passes through it.
Optical manufacturing and testing is the process of manufacturing and testing optical components. It spans a wide range of manufacturing procedures and optical test configurations.
A diamond tool is a cutting tool with diamond grains fixed on the functional parts of the tool via a bonding material or another method. As diamond is a superhard material, diamond tools have many advantages as compared with tools made with common abrasives such as corundum and silicon carbide.
Glass production involves two main methods – the float glass process that produces sheet glass, and glassblowing that produces bottles and other containers. It has been done in a variety of ways during the history of glass.
Cemented carbides are a class of hard materials used extensively for cutting tools, as well as in other industrial applications. It consists of fine particles of carbide cemented into a composite by a binder metal. Cemented carbides commonly use tungsten carbide (WC), titanium carbide (TiC), or tantalum carbide (TaC) as the aggregate. Mentions of "carbide" or "tungsten carbide" in industrial contexts usually refer to these cemented composites.
Conformal cooling channel is a cooling passageway which follows the shape or profile of the mould core or cavity to perform rapid uniform cooling process for injection moulding or blow moulding processes.
3D metal moulding, also referred to as metal injection moulding or (MIM), is used to manufacture components with complex geometries. The process uses a mixture of metal powders and polymer binders – also known as "feedstock" – which are then injection moulded.
{{cite web}}: CS1 maint: archived copy as title (link){{cite journal}}: Cite journal requires |journal= (help)