Float glass

Last updated
Use of float glass at Crystal Palace railway station, London CrystalPalaceStation.jpg
Use of float glass at Crystal Palace railway station, London

Float glass is a sheet of glass made by floating molten glass on a bed of molten metal of a low melting point, typically tin, [1] although lead was used for the process in the past. [2] This method gives the sheet uniform thickness and a very flat surface. [3] The float glass process is also known as the Pilkington process, named after the British glass manufacturer Pilkington, [4] which pioneered the technique in the 1950s at their production site in St Helens, Merseyside. [5]

Contents

Modern windows are usually made from float glass, [6] though Corning Incorporated uses the overflow downdraw method. [7]

Most float glass is soda–lime glass, [8] although relatively minor quantities of specialty borosilicate [9] and flat panel display glass are also produced using the float glass process.

History

Old window containing a single sheet of float glass in the upper left section, Jena, Germany. The remaining sections are possibly not float glass as indicated by the distorted reflections of a tree. Windowfloatnofloat.jpg
Old window containing a single sheet of float glass in the upper left section, Jena, Germany. The remaining sections are possibly not float glass as indicated by the distorted reflections of a tree.

Until the 16th century, window glass or other flat glass was generally cut from large discs (or rondels) of crown glass. Larger sheets of glass were made by blowing large cylinders which were cut open and flattened, then cut into panes. Most window glass in the early 19th century was made using the cylinder method. The 'cylinders' were 6 to 8 feet (180 to 240 cm) long and 10 to 14 inches (25 to 36 cm) in diameter, limiting the width that panes of glass could be cut, and resulting in windows divided by transoms into rectangular panels.

The first advances in automating glass manufacturing were patented in 1848 by Henry Bessemer. [10] His system produced a continuous ribbon of flat glass by forming the ribbon between rollers. This was an expensive process, as the surfaces of the glass needed polishing. If the glass could be set on a perfectly smooth, flat body, like the surface of an open pan of calm liquid, this would reduce costs considerably. Attempts were made to form flat glass on a bath of molten tin—one of the few liquids denser than glass that would be calm at the high temperatures needed to make glass—most notably in the US. Several patents were granted, [11] [12] but this process was unworkable at the time.

Before the development of float glass, larger sheets of plate glass were made by casting a large puddle of glass on an iron surface, and then polishing both sides, a costly process. From the early 1920s, a continuous ribbon of plate glass was passed through a lengthy series of inline grinders and polishers, reducing glass losses and cost. [13]

Glass of lower quality, drawn glass, was made by drawing upwards from a pool of molten glass a thin sheet, held at the edges by rollers. As it cooled the rising sheet stiffened and could then be cut. The two surfaces were of lower quality i.e. not as smooth or uniform as those of float glass. This process continued in use for many years after the development of float glass.

Between 1953 and 1957, at the Cowley Hill Works St Helens, Lancashire, Sir Alastair Pilkington and Kenneth Bickerstaff of the UK's Pilkington Brothers developed the first successful commercial application for forming a continuous ribbon of glass using a molten tin bath on which the molten glass flows unhindered under the influence of gravity. [14] The success of this process lay in the careful balance of the volume of glass fed onto the bath, where it was flattened by its own weight. [15] Full scale profitable sales of float glass were first achieved in 1960, and in the 1960s the process was licensed throughout the world, replacing previous production methods. [16]

Manufacture

Float glass line Floatglasanlage.jpg
Float glass line

Float glass uses common glass-making raw materials, typically consisting of sand, soda ash (sodium carbonate), dolomite, limestone, and salt cake (sodium sulfate) etc. Other materials may be used as colourants, refining agents or to adjust the physical and chemical properties of the glass. The raw materials are mixed in a batch process, then fed together with a controlled proportion of cullet (waste glass) into a furnace, where it is heated to approximately 1,500 °C. Common float glass furnaces are 9 m wide and 45 m long and have capacities of more than 1,200 tons of glass. Once molten, the temperature of the glass is stabilised to approximately 1,200 °C to ensure a homogeneous density.

The molten glass is fed into a "tin bath", a bath of molten tin (about 3–4 m wide, 50 m long, 6 cm deep), from a delivery canal and is poured into the tin bath by a ceramic lip known as the spout lip. [17] The amount of glass allowed to pour onto the molten tin is controlled by a gate called a tweel.

Molten tin is suitable for the float glass process because it has a higher density than glass, so the molten glass floats on it. Its boiling point is higher than the melting point of glass, and its vapour pressure at process temperature is low. However, tin oxidises in a natural atmosphere to form tin dioxide (SnO2). Known in the production process as dross, the tin dioxide adheres to the glass. To prevent oxidation, the tin bath is provided with a positive pressure protective atmosphere of nitrogen and hydrogen.

The glass flows onto the tin surface forming a floating ribbon of even thickness with perfectly smooth surfaces on both sides. As the glass flows along the tin bath, the temperature is gradually reduced from 1,100 °C until at approximately 600 °C the sheet can be lifted from the tin onto rollers. The glass ribbon is pulled off the bath by rollers at a controlled speed. Variation in the flow speed and roller speed enables glass sheets of varying thickness to be formed. Top rollers positioned above the molten tin may be used to control both the thickness and the width of the glass ribbon.

Once off the bath, the glass sheet passes through a lehr kiln for approximately 100 m, where it is cooled gradually so that it anneals without strain and does not crack from the temperature change. On exiting the "cold end" of the kiln, the glass is cut by machines.

Uses

A float glass light fitting. Ordinary float glass is green in thicker sheets due to Fe2+ impurities. Green color of float glass.jpg
A float glass light fitting. Ordinary float glass is green in thicker sheets due to Fe2+ impurities.

Today, float glass is the most widely produced form of glass, [18] with a multitude of commercial applications. [19] Due to both its high quality with no additional polishing required [20] and its structural flexibility during production, it can easily be shaped and bent into a variety of forms while in a heated, syrupy state. [21] This makes it ideal for a variety of applications such as

Most forms of specialized glass such as toughened glass, [26] frosted glass, [27] laminated safety glass [28] and soundproof glass [29] consist of standard float glass that has been further processed.

Market

As of 2009, the world float glass market, not including China and Russia, is dominated by four companies: Asahi Glass, NSG/Pilkington, Saint-Gobain, and Guardian Industries. Other companies include Sise Cam AS, Vitro, formerly PPG, Central Glass, Hankuk (HanGlas), Carlex Glass, and Cardinal Glass Industries. [30]

See also

References and footnotes

  1. ↑ Richet, Pascal (2021-02-05). Encyclopedia of Glass Science, Technology, History, and Culture. John Wiley & Sons. pp. 73–74. ISBN   978-1-118-79939-0.
  2. ↑ Binggeli, Corky (7 October 2013). Materials for interior environments. Wiley. p. 86. ISBN   978-1-118-30635-2. OCLC   819741821. 819741821.
  3. ↑ Groover, Mikell P. (2021). Fundamentals of Modern Manufacturing: Materials, Processes, and Systems. John Wiley & Sons. p. 207. ISBN   978-1-119-70642-7.
  4. ↑ Baker, Ian (2018-06-21). Fifty Materials That Make the World. Springer. p. 66. ISBN   978-3-319-78766-4.
  5. ↑ "The Story of Pilkington UK". www.pilkington.com. Retrieved 2023-04-09.
  6. ↑ Shackelford, James F. (2005). Introduction to Materials Science for Engineers. Pearson Education. Prentice Hall. p. 237. ISBN   978-0-13-142486-9.
  7. ↑ "LCD Glass - Display Glass". Schott AG . Archived from the original on 2008-02-01. Retrieved 2008-01-30.
  8. ↑ Khatib, Jamal (2016-08-12). Sustainability of Construction Materials. Woodhead Publishing. p. 80. ISBN   978-0-08-100391-6.
  9. ↑ Wurm, Jan (2007). Glass Structures: Design and Construction of Self-supporting Skins. Springer Science & Business Media. p. 37. ISBN   978-3-7643-7608-6.
  10. ↑ Bessemer, Henry ; British patent no. 12,101 (issued: Sept. 22, 1848).
  11. ↑ William E. Heal, "Manufacture of window and plate glass," Archived 2017-08-17 at the Wayback Machine U.S. patent no. 710,357 (filed: January 25, 1902; issued: September 30, 1902)
  12. ↑ Halbert K. Hitchcock, "Apparatus for manufacturing glass sheets or plates," Archived 2017-08-17 at the Wayback Machine U.S. patent no. 789,911 (filed: July 30, 1902; issued: May 16, 1905).
  13. ↑ "The Double Steal - the Right and Wrong Way to Steal Trade Secrets". socxfbi.org. Retrieved 2023-04-29.
  14. ↑ Pilkington, L. A. B. (1969). "Review Lecture. The Float Glass Process". Proceedings of the Royal Society of London. Series A, Mathematical and Physical Sciences. 314 (1516). The Royal Society: 1–25. Bibcode:1969RSPSA.314....1P. doi:10.1098/rspa.1969.0212. JSTOR   2416528. S2CID   109981215.
  15. ↑ US patent 2911759 – Manufacture of flat glass
  16. ↑ Nascimento, Marcio Luis Ferreira (September 2014). "Brief history of the flat glass patent – Sixty years of the float process" (PDF). World Patent Information. 38: 50–56. doi:10.1016/j.wpi.2014.04.006.
  17. ↑ B. H. W. S. de Jong, "Glass"; in Ullmann's Encyclopedia of Industrial Chemistry; 5th edition, vol. A12, VCH Publishers, Weinheim, Germany, 1989, ISBN   3-527-20112-2, pp. 365–432.
  18. ↑ Schittich, Christian; Staib, Gerald (2012-12-10). Glass Construction Manual. Walter de Gruyter. p. 61. ISBN   978-3-0346-1554-9.
  19. ↑ Sharma, S. K. (2016). Civil Engineering Construction Materials. Khanna Publishing House. p. 362. ISBN   978-93-82609-84-1.
  20. ↑ Lesko, Jim (2007-12-14). Industrial Design: Materials and Manufacturing Guide. John Wiley & Sons. p. 222. ISBN   978-0-470-05538-0.
  21. ↑ Hegger, Manfred; Auch-Schwelk, Volker (2013-02-12). Construction Materials Manual. Walter de Gruyter. p. 86. ISBN   978-3-0346-1455-9.
  22. ↑ Richet, Pascal (2021-02-05). Encyclopedia of Glass Science, Technology, History, and Culture. John Wiley & Sons. p. 1092. ISBN   978-1-118-79939-0.
  23. ↑ Spence, William P.; Kultermann, Eva (2016-01-19). Construction Materials, Methods and Techniques. Cengage Learning. p. 516. ISBN   978-1-305-53710-1.
  24. ↑ Punmia, Dr B. C.; Jain, Ashok Kumar (2003). Basic Civil Engineering. Firewall Media. p. 111. ISBN   978-81-7008-403-7.
  25. ↑ Dedek, Peter B. (2014-03-27). Historic Preservation for Designers. A&C Black. p. 244. ISBN   978-1-60901-509-1.
  26. ↑ Khatib, Jamal (2016-08-12). Sustainability of Construction Materials. Woodhead Publishing. p. 97. ISBN   978-0-08-100391-6.
  27. ↑ Schunck, Eberhard; Oster, Hans Jochen (2013-01-21). Roof Construction Manual: Pitched Roofs. Walter de Gruyter. p. 160. ISBN   978-3-0346-1563-1.
  28. ↑ Spicer, Mark (2016-11-30). Illustrated Manual of Sniper Skills. Pen and Sword. p. 127. ISBN   978-1-4738-8452-6.
  29. ↑ Yglesias, Caren (2014-02-07). The Innovative Use of Materials in Architecture and Landscape Architecture: History, Theory and Performance. McFarland. p. 76. ISBN   978-0-7864-7080-8.
  30. ↑ ""Flat glass market to be 39 million tons by 2010"". Archived from the original on 2012-07-28. Retrieved 2010-08-11.

Related Research Articles

<span class="mw-page-title-main">Glass</span> Transparent non-crystalline solid material

Glass is an amorphous (non-crystalline) solid. Because it is often transparent and chemically inert, glass has found widespread practical, technological, and decorative use in window panes, tableware, and optics. Some common objects made of glass like "a glass" of water, "glasses", and "magnifying glass", are named after the material.

<span class="mw-page-title-main">Solder</span> Alloy used to join metal pieces

Solder is a fusible metal alloy used to create a permanent bond between metal workpieces. Solder is melted in order to wet the parts of the joint, where it adheres to and connects the pieces after cooling. Metals or alloys suitable for use as solder should have a lower melting point than the pieces to be joined. The solder should also be resistant to oxidative and corrosive effects that would degrade the joint over time. Solder used in making electrical connections also needs to have favorable electrical characteristics.

Fiberglass or fibreglass is a common type of fiber-reinforced plastic using glass fiber. The fibers may be randomly arranged, flattened into a sheet called a chopped strand mat, or woven into glass cloth. The plastic matrix may be a thermoset polymer matrix—most often based on thermosetting polymers such as epoxy, polyester resin, or vinyl ester resin—or a thermoplastic.

<span class="mw-page-title-main">Extrusion</span> Process of pushing material through a die to create long symmetrical-shaped objects

Extrusion is a process used to create objects of a fixed cross-sectional profile by pushing material through a die of the desired cross-section. Its two main advantages over other manufacturing processes are its ability to create very complex cross-sections; and to work materials that are brittle, because the material encounters only compressive and shear stresses. It also creates excellent surface finish and gives considerable freedom of form in the design process.

<span class="mw-page-title-main">Alastair Pilkington</span> British inventor

Sir Lionel Alexander Bethune Pilkington, known as Sir Alastair Pilkington, was a British engineer and businessman who invented and perfected the float glass process for commercial manufacturing of plate glass.

<span class="mw-page-title-main">Pilkington</span> British glass manufacturer

Pilkington is a glass-manufacturing company which is based in Lathom, Lancashire, England. It includes several legal entities in the UK, and is a subsidiary of Japanese company Nippon Sheet Glass (NSG). It was formerly an independent company listed on the London Stock Exchange and a constituent of the FTSE 100 Index.

<span class="mw-page-title-main">Calender</span> Manufacturing device

A calender is a series of hard pressure rollers used to finish or smooth a sheet of material such as paper, textiles, rubber, or plastics. Calender rolls are also used to form some types of plastic films and to apply coatings. Some calender rolls are heated or cooled as needed. Calenders are sometimes misspelled calendars.

<span class="mw-page-title-main">Sheet metal</span> Metal formed into thin, flat pieces

Sheet metal is metal formed into thin, flat pieces, usually by an industrial process.

<span class="mw-page-title-main">Rolling (metalworking)</span> Metal forming process

In metalworking, rolling is a metal forming process in which metal stock is passed through one or more pairs of rolls to reduce the thickness, to make the thickness uniform, and/or to impart a desired mechanical property. The concept is similar to the rolling of dough. Rolling is classified according to the temperature of the metal rolled. If the temperature of the metal is above its recrystallization temperature, then the process is known as hot rolling. If the temperature of the metal is below its recrystallization temperature, the process is known as cold rolling. In terms of usage, hot rolling processes more tonnage than any other manufacturing process, and cold rolling processes the most tonnage out of all cold working processes. Roll stands holding pairs of rolls are grouped together into rolling mills that can quickly process metal, typically steel, into products such as structural steel, bar stock, and rails. Most steel mills have rolling mill divisions that convert the semi-finished casting products into finished products.

<span class="mw-page-title-main">Architectural glass</span> Building material

Architectural glass is glass that is used as a building material. It is most typically used as transparent glazing material in the building envelope, including windows in the external walls. Glass is also used for internal partitions and as an architectural feature. When used in buildings, glass is often of a safety type, which include reinforced, toughened and laminated glasses.

<span class="mw-page-title-main">Tempered glass</span> Type of safety glass processed to increase its strength

Tempered or toughened glass is a type of safety glass processed by controlled thermal or chemical treatments to increase its strength compared with normal glass. Tempering puts the outer surfaces into compression and the interior into tension. Such stresses cause the glass, when broken, to shatter into small granular chunks instead of splintering into large jagged shards as ordinary annealed glass does. These smaller, granular chunks are less likely to cause deep penetration when forced into the surface of an object compared to larger, jagged shards because the reduction in both the mass and the maximum dimension of a glass fragment corresponds with a reduction in both the momentum and the penetration depth of the glass fragment.

<span class="mw-page-title-main">Melt spinning</span> Technique of shooting liquid metal on cooled rotating drum

Melt spinning is a metal forming technique that is typically used to form thin ribbons of metal or alloys with a particular atomic structure.

The Fourcault process is a method of manufacturing plate glass. First developed in Belgium by Émile Fourcault (1862–1919) during the early 1900s, the process was used globally. Fourcault is an example of a "vertical draw" process, in that the glass is drawn against gravity in an upward direction. Gravity forces influence parts of the process.

In the manufacture of float glass, a lehr oven is a long kiln with an end-to-end temperature gradient, which is used for annealing newly made glass objects that are transported through the temperature gradient either on rollers or on a conveyor belt. The annealing renders glass into a stronger material with fewer internal stresses, and with a lower probability of breaking.

Glass production involves two main methods – the float glass process that produces sheet glass, and glassblowing that produces bottles and other containers. It has been done in a variety of ways during the history of glass.

The overflow downdraw method or fusion method is a technique for producing flat glass. The key advantage of this technique as compared to the float glass process is that the pristine surfaces are not touched by molten tin. The technique is used for the production of very thin flat panel display glass by the companies Asahi Glass Co., Corning, Nippon Electric Glass, Samsung Corning Precision Materials, and various other companies operating in the field of display glass and other types of thin glass.

Tape casting is a casting process used in the manufacture of thin ceramic tapes and sheets from ceramic slurry. The ceramic slurry is cast in a thin layer onto a flat surface and then dried and sintered. It's a part of powder metallurgy.

<span class="mw-page-title-main">History of glass</span>

The history of glass-making dates back to at least 3,600 years ago in Mesopotamia. However, most writers claim that they may have been producing copies of glass objects from Egypt. Other archaeological evidence suggests that the first true glass was made in coastal north Syria, Mesopotamia or Egypt. The earliest known glass objects, of the mid 2,000 BCE, were beads, perhaps initially created as the accidental by-products of metal-working (slags) or during the production of faience, a pre-glass vitreous material made by a process similar to glazing. Glass products remained a luxury until the disasters that overtook the late Bronze Age civilizations seemingly brought glass-making to a halt.

<span class="mw-page-title-main">Glazing (window)</span> Part of a wall or window, made of glass

Glazing, which derives from the Middle English for 'glass', is a part of a wall or window, made of glass. Glazing also describes the work done by a professional "glazier". Glazing is also less commonly used to describe the insertion of ophthalmic lenses into an eyeglass frame.

A die in polymer processing is a metal restrictor or channel capable of providing a constant cross sectional profile to a stream of liquid polymer. This allows for continuous processing of shapes such as sheets, films, pipes, rods, and other more complex profiles. This is a continuous process, allowing for constant production, as opposed to a sequential (non-constant) process such as injection molding.

This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.