Polyacetylene

Last updated
Polyacetylene
Trans-Polyacetylene.svg
Skeletal formula of trans-polyacetylene
Cis-Polyacetylene.svg
Skeletal formula of cis-polyacetylene
Cis-and-trans-polyacetylene-chains-symmetric-8-based-on-xtals-3D-bs-17.png
Ball-and-stick models of the transoidal (top) and cisoidal (bottom) conformations of the trans isomer [1]
Names
IUPAC name
Polyethyne
Other names
Polyacetylene, PAc
Identifiers
ChemSpider
  • none
Properties
[C2H2]n
insoluble
Related compounds
Related compounds
 Ethyne (monomer)
Hazards
GHS labelling:
GHS-pictogram-flamme.svg
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa).
X mark.svgN  verify  (what is  Yes check.svgYX mark.svgN ?)

Polyacetylene (IUPAC name: polyethyne) usually refers to an organic polymer with the repeating unit [C2H2]n. The name refers to its conceptual construction from polymerization of acetylene to give a chain with repeating olefin groups. This compound is conceptually important, as the discovery of polyacetylene and its high conductivity upon doping helped to launch the field of organic conductive polymers. The high electrical conductivity discovered by Hideki Shirakawa, Alan Heeger, and Alan MacDiarmid for this polymer led to intense interest in the use of organic compounds in microelectronics (organic semiconductors). This discovery was recognized by the Nobel Prize in Chemistry in 2000. [2] [3] Early work in the field of polyacetylene research was aimed at using doped polymers as easily processable and lightweight "plastic metals". [4] Despite the promise of this polymer in the field of conductive polymers, many of its properties such as instability to air and difficulty with processing have led to avoidance in commercial applications.

Contents

Compounds called polyacetylenes also occur in nature, although in this context the term refers to polyynes, compounds containing multiple acetylene groups ("poly" meaning many), rather than to chains of olefin groups ("poly" meaning polymerization of). [5]

Structure

A segment of trans-polyacetylene
Trans-(CH)n.svg
Structural diagram
Polyacetylene-3D-balls.png
Ball-and-stick model

Polyacetylene consists of a long chain of carbon atoms with alternating single and double bonds between them, each with one hydrogen atom. The double bonds can have either cis or trans geometry. The controlled synthesis of each isomer of the polymer, cis-polyacetylene or trans-polyacetylene, can be achieved by changing the temperature at which the reaction is conducted. The cis form of the polymer is thermodynamically less stable than the trans isomer. Despite the conjugated nature of the polyacetylene backbone, not all of the carbon–carbon bonds in the material are equal: a distinct single/double alternation exists. [6] Each hydrogen atom can be replaced by a functional group. Substituted polyacetylenes tend to be more rigid than saturated polymers. [4] Furthermore, placing different functional groups as substituents on the polymer backbone leads to a twisted conformation of the polymer chain to interrupt the conjugation.

History

One of the earliest reported acetylene polymers was named Cuprene. Its highly cross-linked nature led to no further studies in the field for quite some time. [7] Linear polyacetylene was first prepared by Giulio Natta in 1958. [8] The resulting polyacetylene was linear, of high molecular weight, displayed high crystallinity, and had a regular structure. X-ray diffraction studies demonstrated that the resulting polyacetylene was trans-polyacetylene. [8] After this first reported synthesis, few chemists were interested in polyacetylene because the product of Natta's preparation was an insoluble, air sensitive, and infusible black powder.

The next major development of polyacetylene polymerization was made by Hideki Shirakawa’s group who were able to prepare silvery films of polyacetylene. They discovered that the polymerization of polyacetylene could be achieved at the surface of a concentrated solution of the catalyst system of Et3Al and Ti(OBu)4 in an inert solvent such as toluene. [6] In parallel with Shirakawa's studies, Alan Heeger and Alan MacDiarmid were studying the metallic properties of polythiazyl [(SN)x], a related but inorganic polymer. [9] Polythiazyl caught Heeger's interest as a chain-like metallic material, and he collaborated with Alan MacDiarmid who had previous experience with this material. By the early 1970s, this polymer was known to be superconductive at low temperatures. [9] Shirakawa, Heeger, and MacDiarmid collaborated on further development of polyacetylene. [8]

Upon doping polyacetylene with I2, the conductivity increased seven orders of magnitude. [6] Similar results were achieved using Cl2 and Br2. These materials exhibited the largest room temperature conductivity observed for a covalent organic polymer, and this seminal report was key in furthering the development of organic conductive polymers. [10] Further studies led to improved control of the cis/trans isomer ratio and demonstrated that cis-polyacetylene doping led to higher conductivity than doping of trans-polyacetylene. [6] Doping cis-polyacetylene with AsF5 further increased the conductivities, bringing them close to that of copper. Furthermore, it was found that heat treatment of the catalyst used for polymerization led to films with higher conductivities. [11]

To account for such an increase in conductivity in polyacetylene, J. R. Schrieffer and Heeger considered the existence of topologically protected solitonic defects, their model is now known as the Su–Schrieffer–Heeger model, which has served as model in other contexts to understand topological insulators. [12]

Synthesis

From acetylene

Ziegler-Natta scheme Ziegler natta scheme for polyacetylene.png
Ziegler–Natta scheme

A variety of methods have been developed to synthesize polyacetylene, from pure acetylene and other monomers. One of the most common methods uses a Ziegler–Natta catalyst, such as Ti(OiPr)4/Al(C2H5)3, with gaseous acetylene. This method allows control over the structure and properties of the final polymer by varying temperature and catalyst loading. [13] Mechanistic studies suggest that this polymerization involves metal insertion into the triple bond of the monomer. [14]

Insertion mechanism for polyacetylene Insertion mechanism for polyacetylene.png
Insertion mechanism for polyacetylene

By varying the apparatus and catalyst loading, Shirakawa and coworkers were able to synthesize polyacetylene as thin films, rather than insoluble black powders. They obtained these films by coating the walls of a reaction flask under inert conditions with a solution of the Ziegler–Natta catalyst and adding gaseous acetylene resulting in immediate formation of a film. [15] Enkelmann and coworkers further improved polyacetylene synthesis by changing the catalyst to a Co(NO3)2/NaBH4 system, which was stable to both oxygen and water. [7]

Polyacetylene can also be produced by radiation polymerization of acetylene. Glow-discharge radiation, gamma radiation, and ultraviolet irradiation have been used. These methods avoid the use of catalysts and solvent, but require low temperatures to produce regular polymers. Gas-phase polymerization typically produces irregular cuprene, whereas liquid-phase polymerization, conducted at −78 °C produces linear cis-polyacetylene, and solid-phase polymerization, conducted at still lower temperature, produces trans-polyacetylene. [8]

Ring-opening metathesis polymerization

Polyacetylene can be synthesized by ring-opening metathesis polymerisation (ROMP) from cyclooctatetraene, a material easier to handle than the acetylene monomer. [16] This synthetic route also provides a facile method for adding solubilizing groups to the polymer while maintaining the conjugation. [4] Robert Grubbs and coworkers synthesized a variety of polyacetylene derivatives with linear and branched alkyl chains. Polymers with linear groups such as n-octyl had high conductivity but low solubility, while highly branched tert-butyl groups increased solubility but decreased conjugation due to polymer twisting to avoid steric crowding. They obtained soluble and conductive polymers with sec-butyl and neopentyl groups, because the methylene (CH2) unit directly connected to the polymer reduces steric crowding and prevents twisting. [4]

Grubbs route to polyacetylene Modified Grubbs.png
Grubbs route to polyacetylene

From precursor polymers

Dehydrohalogenation route to polyacetylene PVC base polyacetylene.png
Dehydrohalogenation route to polyacetylene

Polyacetylene can also be synthesized from precursor polymers. This method enables processing of the polymer before conversion to insoluble polyacetylene. Short, irregular segments of polyacetylene can be obtained by dehydrohalogenation of poly(vinyl chloride). [17]

Thermal conversion of precursor polymers is a more effective method for synthesizing long polyacetylene chains. In the Durham-precursor route, polymers are prepared by ring-opening metathesis polymerization, and a subsequent heat-induced reverse Diels–Alder reaction yields the final polymer, as well as a volatile side product. [7]

Durham precursor polymer route to polyacetylene Durham precursor 3.png
Durham precursor polymer route to polyacetylene

Doping

When polyacetylene films are exposed to vapors of electron-accepting compounds (p-type dopants), the electrical conductivity of the material increases by orders of magnitude over the undoped material. [18] [19] p-Type dopants include Br2, I2, Cl2, and AsF5. These dopants act by abstracting an electron from the polymer chain. The conductivity of these polymers is believed to be a result of the creation of charge-transfer complexes between the polymer and halogen. [10] Charge transfer occurs from the polymer to the acceptor compound; the polyacetylene chain acts as a cation and the acceptor as an anion. The "hole" on the polymer backbone is weakly associated with the anionic acceptor by Coulomb potential. [18] Polyacetylene doped with (p-type) dopants retain their high conductivity even after exposure to air for several days. [8]

Electron-donating (n-type) dopants can also be used to create conductive polyacetylene. [19] n-Type dopants for polyacetylene include lithium, sodium, and potassium. [8] As with p-type dopants, charge-transfer complexes are created, where the polymer backbone is anionic and the donor is cationic. The increase in conductivity upon treatment with an n-type dopant is not as significant as those achieved upon treatment with a p-type dopant. Polyacetylene chains doped with n-type dopants are extremely sensitive to air and moisture. [8]

Polyacetylene can also be doped electrochemically. [19]

The conductivity of polyacetylene depends on structure and doping. Undoped trans-polyacetylene films have a conductivity of 4.4×10−5 Ω−1cm−1, while cis-polyacetylene has a lower conductivity of 1.7×10−9 Ω−1cm−1. [19] Doping with bromine causes an increase in conductivity to 0.5 Ω−1cm−1, while a higher conductivity of 38 Ω−1cm−1 is obtained through doping with iodine. [10] Doping of either cis- or trans-polyacetylene leads to an increase in their conductivities by at least six orders of magnitude. Doped cis-polyacetylene films usually have conductivities two or three times greater than doped trans-polyacetylene even though the parent film has lower conductivity. [20]

Properties

The structure of polyacetylene films have been examined by both infrared spectroscopy [21] and Raman spectroscopy, [22] and found that the structure depends on synthetic conditions. When the synthesis is performed below −78 °C, the cis form predominates, while above 150 °C the trans form is favored. At room temperature, the polymerization yields a ratio of 60:40 cis:trans. [20] Films containing the cis form appear coppery, while the trans form is silvery. [20] Films of cis-polyacetylene are very flexible and can be readily stretched, while trans -polyacetylene is much more brittle.

The synthesis and processing of polyacetylene films affects the properties. Increasing the catalyst ratio creates thicker films with a greater draw ratio, allowing them to be stretched further. [8] Lower catalyst loadings leads to the formation of dark red gels, which can be converted to films by cutting and pressing between glass plates. [20] A foam-like material can be obtained from the gel by displacing the solvent with benzene, then freezing and subliming the benzene. [8] Polyacetylene has a bulk density of 0.4 g/cm3, while density of the foam is significantly lower, at 0.02–0.04 g/cm3. [8] The morphology consists of fibrils, with an average width of 200 Å. These fibrils form an irregular, web-like network, with some cross-linking between chains. [8] The insolubility of polyacetylene makes it difficult to characterize this material and to determine the extent of cross-linking in the material.

Products of oxidation of polyacetylene Oxidation of Polyacetylene.jpg
Products of oxidation of polyacetylene

For applications, polyacetylenes suffer from many drawbacks. They are insoluble in solvents, making it essentially impossible to process the material. While both cis and trans-polyacetylene show high thermal stability, [20] exposure to air causes a large decrease in the flexibility and conductivity. [8] When polyacetylene is exposed to air, oxidation of the backbone by O2 occurs. Infrared spectroscopy shows formation of carbonyl groups, epoxides, and peroxides. [8] [23] Coating with polyethylene or wax can slow the oxidation temporarily, while coating with glass increases stability indefinitely. [8]

Applications

Polyacetylene has no commercial applications, although the discovery of polyacetylene as a conductive organic polymer led to many developments in materials science. Conducting polymers are of interest for solution-processing for film-forming conductive polymers. [6] Therefore, attention has shifted to other conductive polymers for application purposes including polythiophene and polyaniline. Molecular electronics could also be a potential application of conductive polyacetylene.

See also

Related Research Articles

<span class="mw-page-title-main">Organic electronics</span> Field of materials science

Organic electronics is a field of materials science concerning the design, synthesis, characterization, and application of organic molecules or polymers that show desirable electronic properties such as conductivity. Unlike conventional inorganic conductors and semiconductors, organic electronic materials are constructed from organic (carbon-based) molecules or polymers using synthetic strategies developed in the context of organic chemistry and polymer chemistry.

A Ziegler–Natta catalyst, named after Karl Ziegler and Giulio Natta, is a catalyst used in the synthesis of polymers of 1-alkenes (alpha-olefins). Two broad classes of Ziegler–Natta catalysts are employed, distinguished by their solubility:

Polymer chemistry is a sub-discipline of chemistry that focuses on the structures of chemicals, chemical synthesis, and chemical and physical properties of polymers and macromolecules. The principles and methods used within polymer chemistry are also applicable through a wide range of other chemistry sub-disciplines like organic chemistry, analytical chemistry, and physical chemistry. Many materials have polymeric structures, from fully inorganic metals and ceramics to DNA and other biological molecules. However, polymer chemistry is typically related to synthetic and organic compositions. Synthetic polymers are ubiquitous in commercial materials and products in everyday use, such as plastics, and rubbers, and are major components of composite materials. Polymer chemistry can also be included in the broader fields of polymer science or even nanotechnology, both of which can be described as encompassing polymer physics and polymer engineering.

<span class="mw-page-title-main">Hideki Shirakawa</span> Japanese chemist, engineer, and professor

Hideki Shirakawa is a Japanese chemist, engineer, and Professor Emeritus at the University of Tsukuba and Zhejiang University. He is best known for his discovery of conductive polymers. He was co-recipient of the 2000 Nobel Prize in Chemistry jointly with Alan MacDiarmid and Alan Heeger.

<span class="mw-page-title-main">Conductive polymer</span> Organic polymers that conduct electricity

Conductive polymers or, more precisely, intrinsically conducting polymers (ICPs) are organic polymers that conduct electricity. Such compounds may have metallic conductivity or can be semiconductors. The main advantage of conductive polymers is that they are easy to process, mainly by dispersion. Conductive polymers are generally not thermoplastics, i.e., they are not thermoformable. But, like insulating polymers, they are organic materials. They can offer high electrical conductivity but do not show similar mechanical properties to other commercially available polymers. The electrical properties can be fine-tuned using the methods of organic synthesis and by advanced dispersion techniques.

Poly(<i>p</i>-phenylene vinylene) Chemical compound

Poly(p-phenylene vinylene) (PPV, or polyphenylene vinylene) is a conducting polymer of the rigid-rod polymer family. PPV is the only polymer of this type that can be processed into a highly ordered crystalline thin film. PPV and its derivatives are electrically conducting upon doping. Although insoluble in water, its precursors can be manipulated in aqueous solution. The small optical band gap and its bright yellow fluorescence makes PPV a candidate in applications such as light-emitting diodes (LED) and photovoltaic devices. Moreover, PPV can be doped to form electrically conductive materials. Its physical and electronic properties can be altered by the inclusion of functional side groups.

<span class="mw-page-title-main">Polythiophene</span>

Polythiophenes (PTs) are polymerized thiophenes, a sulfur heterocycle. The parent PT is an insoluble colored solid with the formula (C4H2S)n. The rings are linked through the 2- and 5-positions. Poly(alkylthiophene)s have alkyl substituents at the 3- or 4-position(s). They are also colored solids, but tend to be soluble in organic solvents.

<span class="mw-page-title-main">Polypyrrole</span>

Polypyrrole (PPy) is an organic polymer obtained by oxidative polymerization of pyrrole. It is a solid with the formula H(C4H2NH)nH. It is an intrinsically conducting polymer, used in electronics, optical, biological and medical fields.

<span class="mw-page-title-main">Polyaniline</span>

Polyaniline (PANI) is a conducting polymer and organic semiconductor of the semi-flexible rod polymer family. The compound has been of interest since the 1980s because of its electrical conductivity and mechanical properties. Polyaniline is one of the most studied conducting polymers.

Organic semiconductors are solids whose building blocks are pi-bonded molecules or polymers made up by carbon and hydrogen atoms and – at times – heteroatoms such as nitrogen, sulfur and oxygen. They exist in the form of molecular crystals or amorphous thin films. In general, they are electrical insulators, but become semiconducting when charges are either injected from appropriate electrodes, upon doping or by photoexcitation.

<span class="mw-page-title-main">Alan MacDiarmid</span> American-New Zealand chemist (1927–2007)

Alan Graham MacDiarmid, ONZ FRS was a New Zealand-born American chemist, and one of three recipients of the Nobel Prize for Chemistry in 2000.

<span class="mw-page-title-main">Alan J. Heeger</span> American physicist and academic (1936–2023)

Alan Jay Heeger is an American physicist, academic and Nobel Prize laureate in chemistry.

<span class="mw-page-title-main">Polymer science</span> Subfield of materials science concerned with polymers

Polymer science or macromolecular science is a subfield of materials science concerned with polymers, primarily synthetic polymers such as plastics and elastomers. The field of polymer science includes researchers in multiple disciplines including chemistry, physics, and engineering.

<span class="mw-page-title-main">Polyyne</span> Any organic compound with alternating C–C and C≡C bonds

A polyyne is any organic compound with alternating single and triple bonds; that is, a series of consecutive alkynes, (−C≡C−)n with n greater than 1. These compounds are also called polyacetylenes, especially in the natural products and chemical ecology literature, even though this nomenclature more properly refers to acetylene polymers composed of alternating single and double bonds (−CR=CR′−)n with n greater than 1. They are also sometimes referred to as oligoynes, or carbinoids after "carbyne" (−C≡C−)∞, the hypothetical allotrope of carbon that would be the ultimate member of the series. The synthesis of this substance has been claimed several times since the 1960s, but those reports have been disputed. Indeed, the substances identified as short chains of "carbyne" in many early organic synthesis attempts would be called polyynes today.

<span class="mw-page-title-main">Polythiazyl</span> Chemical compound

Polythiazyl, (SN)x, is an electrically conductive, gold- or bronze-colored polymer with metallic luster. It was the first conductive inorganic polymer discovered and was also found to be a superconductor at very low temperatures. It is a fibrous solid, described as "lustrous golden on the faces and dark blue-black", depending on the orientation of the sample. It is air stable and insoluble in all solvents.

A polymer-based battery uses organic materials instead of bulk metals to form a battery. Currently accepted metal-based batteries pose many challenges due to limited resources, negative environmental impact, and the approaching limit of progress. Redox active polymers are attractive options for electrodes in batteries due to their synthetic availability, high-capacity, flexibility, light weight, low cost, and low toxicity. Recent studies have explored how to increase efficiency and reduce challenges to push polymeric active materials further towards practicality in batteries. Many types of polymers are being explored, including conductive, non-conductive, and radical polymers. Batteries with a combination of electrodes are easier to test and compare to current metal-based batteries, however batteries with both a polymer cathode and anode are also a current research focus. Polymer-based batteries, including metal/polymer electrode combinations, should be distinguished from metal-polymer batteries, such as a lithium polymer battery, which most often involve a polymeric electrolyte, as opposed to polymeric active materials.

<span class="mw-page-title-main">Transparent conducting film</span> Optically transparent and electrically conductive material

Transparent conducting films (TCFs) are thin films of optically transparent and electrically conductive material. They are an important component in a number of electronic devices including liquid-crystal displays, OLEDs, touchscreens and photovoltaics. While indium tin oxide (ITO) is the most widely used, alternatives include wider-spectrum transparent conductive oxides (TCOs), conductive polymers, metal grids and random metallic networks, carbon nanotubes (CNT), graphene, nanowire meshes and ultra thin metal films.

<span class="mw-page-title-main">Polyfluorene</span> Chemical compound

Polyfluorene is a polymer with formula (C13H8)n, consisting of fluorene units linked in a linear chain — specifically, at carbon atoms 2 and 7 in the standard fluorene numbering. It can also be described as a chain of benzene rings linked in para positions with an extra methylene bridge connecting every pair of rings.

<span class="mw-page-title-main">Park Yung-woo</span> South Korean physicist (born 1952)

Park Yung-woo is a South Korean physicist, who has worked in the field of materials science.

Conducting polymer metal nanocomposites are.

References

  1. ↑ Perego, Giovanni; Lugli, Gabriele; Pedretti, Ugo; Cesari, Marco (1988). "X-ray investigation on highly oriented polyacetylene, 1. Crystal structure of cis- and trans-polyacetylene". Makromol. Chem. 189 (11): 2657–2669. doi:10.1002/macp.1988.021891113.
  2. ↑ Heeger, Alan (2001). "Nobel Lecture: Semiconducting and metallic polymers: The fourth generation of polymeric materials". Reviews of Modern Physics. 73 (3): 681–700. Bibcode:2001RvMP...73..681H. doi: 10.1103/RevModPhys.73.681 .
  3. ↑ "The Nobel Prize in Chemistry 2000".
  4. 1 2 3 4 Gorman, C. B.; Ginsburg, E. J.; Grubbs, R. H. (1993). "Soluble, Highly Conjugated Derivatives of Polyacetylene from the Ring-Opening Metathesis Polymerization of Monosubstituted Cyclooctratetraenes: Synthesis and the Relationship between Polymer Structure and Physical Properties". Journal of the American Chemical Society. 115 (4): 1397–1409. doi:10.1021/ja00057a024.
  5. ↑ Minto, Robert E. (2008). "Biosynthesis and function of polyacetylenes and allied natural products". Progress in Lipid Research. 47 (4): 233–306. doi:10.1016/j.plipres.2008.02.002. PMC   2515280 . PMID   18387369..
  6. 1 2 3 4 5 Norden, B; Krutmeijer, E. "The Nobel Prize in Chemistry, 2000: Conductive Polymers" (PDF).
  7. 1 2 3 Feast, W.J.; Tsibouklis, J.; Pouwer, K.L.; Groenendaal, L.; Meijer, E.W. (1996). "Synthesis, processing and material properties of conjugated polymers". Polymer. 37 (22): 5017. doi:10.1016/0032-3861(96)00439-9.
  8. 1 2 3 4 5 6 7 8 9 10 11 12 13 14 Saxon, A.M.; Liepins, F.; Aldissi, M. (1985). "Polyacetylene: Its Synthesis, Doping, and Structure". Prog. Polym. Sci. 11 (1–2): 57. doi:10.1016/0079-6700(85)90008-5.
  9. 1 2 Hall, N; McDiarmid, Alan; Heeger, Alan (2003). "Twenty-five years of conducting polymers" (PDF). Chem. Comm. (1): 1–4. doi:10.1039/B210718J. PMID   12610942. Archived from the original (PDF) on 2016-03-04. Retrieved 2014-03-14.
  10. 1 2 3 Shirakawa, H.; Louis, E.J.; MacDiarmid, A.G.; Chiang, C.K.; Heeger, A.J. (1977). "Synthesis of Electrically Conducting Organic Polymers: Halogen Derivatives of Polyacetylene, (CH)x". Journal of the Chemical Society, Chemical Communications (16): 578–580. doi:10.1039/C39770000578.
  11. ↑ Shirakawa, Hideki (1995). "Synthesis and characterization of highly conducting polyacetylene". Synthetic Metals. 69 (1–3): 3. doi:10.1016/0379-6779(94)02340-5.
  12. ↑ Meier, Eric J.; An, Fangzhao Alex; Gadway, Bryce (2016). "Observation of the topological soliton state in the Su–Schrieffer–Heeger model". Nature Communications. 7 (1): 13986. arXiv: 1607.02811 . Bibcode:2016NatCo...713986M. doi:10.1038/ncomms13986. ISSN   2041-1723. PMC   5196433 . PMID   28008924.
  13. ↑ Feast, W. J.; Tsibouklis, J.; Pouwer, K. L.; Groenendaal, L.; Meijer, E. W. (1996). "Synthesis, processing and material properties of conjugated polymers". Polymer. 37 (22): 5017–5047. doi:10.1016/0032-3861(96)00439-9.
  14. ↑ Clarke, T. C.; Yannoni, T. S.; Katz, T. J. (1983). "Mechanism of Ziegler–Natta Polymerization of Acetylene: A Nutation NMR Study". Journal of the American Chemical Society. 105 (26): 7787–7789. doi:10.1021/ja00364a076.
  15. ↑ Ito, T.; Shirakawa, H.; Ikeda, S. (1974). "Simultaneous Polymerization and Formation of Polyacetylene Film on the Surface of Concentrated Soluble Ziegler-Type Catalyst Solution". Journal of Polymer Science Part A. 12 (13): 11–20. Bibcode:1996JPoSA..34.2533I. doi:10.1002/pola.1996.854.
  16. ↑ Klavetter, Floyd L.; Grubbs, Robert H. (1988). "Polycyclooctatetraene (Polyacetylene): Synthesis and Properties". Journal of the American Chemical Society. 110 (23): 7807–7813. doi:10.1021/ja00231a036.
  17. ↑ "Conducting Polymers" (PDF). ch.ic.ac.uk.
  18. 1 2 Chiang, C.K.; Gau, S.C.; Fincher, C.R.; Park, Y.W.; MacDiarmid, A.G.; Heeger, A.J. (1978). "Polyacetylene, (CH)x: n-type and p-type doping and compensation". Appl. Phys. Lett. 33 (1): 18. Bibcode:1978ApPhL..33...18C. doi:10.1063/1.90166.
  19. 1 2 3 4 MacDiarmid, Alan Graham; Mammone, R. J.; Kaner, R. B.; Porter, Lord; Pethig, R.; Heeger, A. J.; Rosseinsky, D. R.; Gillespie, Ronald James; Day, Peter (1985-05-30). "The concept of 'doping' of conducting polymers: the role of reduction potentials". Philosophical Transactions of the Royal Society of London. Series A, Mathematical and Physical Sciences. 314 (1528): 3–15. Bibcode:1985RSPTA.314....3M. doi:10.1098/rsta.1985.0004. S2CID   91941666.
  20. 1 2 3 4 5 MacDiarmid, A; Heeger, A. (1979). "Organic Metals and Semiconductors: The Chemistry of Polyacetylene (CHx) and its Derivatives" (PDF). Synthetic Metals. 1 (101–118): 101. doi:10.1016/0379-6779(80)90002-8. Archived from the original on September 24, 2017.
  21. ↑ Shirakawa, H. S.; Ito, T. S.; Ikeda, S. (1971). "Infrared Spectroscopy of Poly(acetylene)". Polym. J. 2 (2): 231–244. doi: 10.1295/polymj.2.231 .
  22. ↑ Shirakawa, H. S.; Ito, T. S.; Ikeda, S. (1973). "Raman Scattering and Electronic Spectra of Poly(acetylene)". Polym. J. 4 (4): 460–462. doi: 10.1295/polymj.4.460 .
  23. ↑ Will, F.G.; D.W. McKee (1983). "Thermal Oxidation of Polyacetylene". Journal of Polymer Science. 21 (12): 3479–3492. Bibcode:1983JPoSA..21.3479W. doi:10.1002/pol.1983.170211210.
This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.