Salt glaze pottery

Last updated
German Bartmann jug, c. 1600 The Art of German Stoneware Philadelphia 2012 010.JPG
German Bartmann jug, c. 1600
Salt glazed containers Salt glazed utilitarian containers.JPG
Salt glazed containers

Salt-glaze or salt glaze pottery is pottery, usually stoneware, with a glaze of glossy, translucent and slightly orange-peel-like texture which was formed by throwing common salt into the kiln during the higher temperature part of the firing process. Sodium from the salt reacts with silica in the clay body to form a glassy coating of sodium silicate. The glaze may be colourless or may be coloured various shades of brown (from iron oxide), blue (from cobalt oxide), or purple (from manganese oxide). [1] [2] [3]

Contents

Except for its use by a few studio potters, the process is obsolete. Before its demise, in the face of environmental clean air restrictions, it was last used in the production of salt-glazed sewer-pipes. [4] [5] [6] The only commercial pottery in the UK currently licensed to produce salt glaze pottery is Errington Reay at Bardon Mill in Northumberland which was founded in 1878. [7] [8] [9]

History

Salt glaze jug, 19th century Salt glaze jug.JPG
Salt glaze jug, 19th century

The earliest known production of salt glazed stoneware was in the Rhineland of Germany around 1400; [10] it was effectively the only significant innovation in pottery of the European Middle Ages. Initially, the process was used on earthenware. By the 15th century, small pottery towns of the Westerwald, including Höhr-Grenzhausen, Siegburg, Köln, and Raeren in Flanders, were producing a salt-glazed stoneware, [11] with the Bartmann jug a typical product. In the 17th century, salt glaze gained popularity in England as well as in Colonial America. [10] Westerwald Pottery was characterized by stamped medallions and the use of a cobalt oxide based colorant for decoration. Production of salt glaze pottery in Westerwald ceased because of environmental considerations in 1983.

In the UK during the 17th century and 18th century, high quality salt-glazed stoneware was produced in Derbyshire, Nottinghamshire, London and Staffordshire. [12] Salt glazed pottery was also popular in North America from the early 17th century until the early 19th century, [13] indeed it was the dominant domestic pottery there during the 19th century. [14] Whilst its manufacture in America increased from the earliest dated production, the 1720s in Yorktown, significant amounts were imported from Britain until around the mid-19th century. [15]

During the 20th century, the technique was promoted for studio pottery use by Bernard Leach. In the 1950s, it was introduced into Japanese craft pottery through Leach's association with Shōji Hamada. Don Reitz introduced salt glazing into the curriculum at Alfred University in New York in 1959, and it subsequently spread to other American universities with ceramic art programs.[ citation needed ]

Due to concerns of significant amount of air pollution resulting from the process [16] environmental clean air restrictions led to the demise of widespread use of salt glazing. [1] It was last used on any large scale for the production of salt-glazed sewer-pipes, and other than limited use by some studio potters the process is obsolete, [1] although there are reports of it still being used for sewer-pipes in India. [17] [18]

English salt glaze stoneware

Experiments in stoneware production began in England during the second part of the 17th century. The earliest evidence has been dated 1650–1700 at the site of a kiln at Woolwich Ferry, London. The similarity of the ware to German products of a similar era has led it to be attributed to immigrant potters.

A significant English manufacturer of salt glaze pottery was John Dwight at the Fulham Pottery, which he founded in 1672. [19] [20] In a related patent application, which was granted in 1671, he also claimed to have "discovered the mystery of transparent earthenware commonly knowne by the name of porcelaine or China and Persian ware." [21]

Salt glazed jug by Doulton. England, 1875 Jug with Brown Glaze LACMA M.2001.97.3.jpg
Salt glazed jug by Doulton. England, 1875

By the 1800s Lambeth in London had become a centre for the production of salt glaze stoneware, and most especially after the establishment of Doulton and Watts Pottery, which later became Royal Doulton. The company was founded in 1815 when John Doulton formed a partnership with the owner, Martha Jones and foreman, John Watts, of an existing pottery in Lambeth. Initially the factory specialised in utilitarian salt glazed stoneware, similar to that produced by the Fulham factories. [22] During the 1830s and 1840s, considerable amounts of salt-glazed sewer-pipes were produced by Doultons following Sir Edwin Chadwick's advocacy of improved sanitary conditions. Doultons were also one of the earliest manufacturers of electrical insulators, initially using salt glaze stoneware and for the electrical telegraph systems. [23] Also, from about 1830, they started production of salt glaze stoneware vessels, which were valued for their acid resistance, for the emerging chemical industries. [23] From the 1850s Doulton & Co.'s decorative stoneware, that was produced in association with the nearby Lambeth School of Art, enjoyed significant success at various international exhibitions, including at The Great Exhibition in 1851, Philadelphia Exhibition in 1876, and also at Chicago in 1893. Their salt glaze decorative products became known as 'Doulton Ware'. By 1890 their decorative stoneware were so successful that 350 designers and artists were employed at the Lambeth factory, including the famous George Tinworth. [24] [23] Doulton’s Lambeth factory closed in 1956, due largely to new clean air regulations that prohibited the production of salt glaze in the urban environment. [25] Production, but not of salt glazing, was transferred to their factory in Burslem which had been established in 1877. [23]

Several other stoneware potteries also operated in Lambeth between the mid-18th & 19th centuries, including James Stiff and Sons and Stephen Green's Imperial pottery. The former having started his pottery career at Doulton in 1830, before opening his own factory in 1843. [26]

New world

Salt glazed pipe vent. New Zealand, 1910 - 1936 Pipe (AM 1985.358.47-5).jpg
Salt glazed pipe vent. New Zealand, 1910 - 1936

One of the first potteries in the US was on Bean Hill in Norwich, Connecticut. They manufactured yellow-brown, salt glazed earthenware. According to a rather dubious local legend, their salt glaze technique was discovered in about 1680 by a servant. There was an earthenware vessel on the fire with brine in it to cure salt pork. While the servant was away the brine boiled over, the pot became red hot, and the sides were found to be glazed. A local potter utilized the discovery and salt-glaze became established. [27]

The earliest known production of salt glaze pottery in Australia has been dated to 1850–1883. [28]

Process

Pouring salt into a wood-fired kiln, using a carved-out piece of bamboo filled with salt soaked in water.
Modern salt-glazed porcelain piece Salt glazed porcelain fired 1320 deg centigrade lpg gas fired iron and manganese slip.jpg
Modern salt-glazed porcelain piece

The salt glaze is formed on the unglazed body by reaction of common salt with the clay body constituents, particularly silica, toward the end of firing. The body should ideally be richer in silica than normal stoneware, and iron impurities can help produce good salt glazes. A reduction atmosphere can be employed as the reduced iron silicates are very powerful fluxes.

The salting mixture of sodium chloride and water is introduced into the kiln when the appropriate temperature is reached, typically around 900 °C, or salt can be placed inside the kiln prior to firing. [29] As the kiln reaches higher temperatures, typically 1100–1200 °C, the sodium chloride vaporizes and reacts with steam to form hydrogen chloride and soda. These vapors react with the silica in the body and other body constituents. A glaze of fairly high alumina content (0.6 molecular parts) and a relatively low silica content (2.6 molecular parts), and in which the main base is soda, is formed. Salt glazes have been improved by the addition of borax, and sometimes sodium nitrate, to the salting mixture. Colouring oxides can be incorporated in the salting mixture to give decorative effects, such as a kind of aventurine glaze. [30]

Salt fumes in a firing atmosphere react in the following way:

2NaCl + 2H2O → 2NaOH + 2HCl
2NaOH → Na2O + H2O

In soda firings the reaction is a little more direct, not requiring the presence of water vapor:

Na2CO3 → Na2O + CO2

Both the hydrogen chloride and the carbon dioxide are gases; they do not react with the sodium oxide that binds with the silica and other components of the clay body. Hydrogen chloride leaving the kiln will form a hydrochloric acid vapour on contact with moisture in the air or kiln exhaust gases. Any remaining sodium oxide will form salt by reacting with hydrochloric acid vapour as the gases exit the kiln. The sodium oxide (Na2O) reacts with the alumina and silica in the clay body to form a sodium alumino-silicate glaze. [1] The general reaction is shown below, with the values for x and y varying dependent on the amounts of sodium oxide, alumina and silica composing the glaze:

Na2O + SiO2 + Al2O3·(SiO2)2 → (Na2O)x·Al2O3·(SiO2)y

Salt can also be used as a decorative element on selected individual pots. Biscuit ware can be soaked in a brine solution to create salted patterns. Rope and other textiles can also be soaked in brine and wrapped around biscuit ware. Salt can also be added, in solution, to coloured clay slips and can be sprinkled onto biscuit ware in protective, ceramic containers called saggars. A related technique, soda firing, substitutes soda ash and/or sodium bicarbonate for common salt. Whilst the application method is a little different, the alternatives need to be sprayed into the kiln, results are similar to salt glazing but for subtle differences in texture and colour.

Related Research Articles

<span class="mw-page-title-main">Pottery</span> Craft of making objects from clay

Pottery is the process and the products of forming vessels and other objects with clay and other raw materials, which are fired at high temperatures to give them a hard and durable form. The place where such wares are made by a potter is also called a pottery. The definition of pottery, used by the ASTM International, is "all fired ceramic wares that contain clay when formed, except technical, structural, and refractory products". End applications include tableware, decorative ware, sanitaryware, and in technology and industry such as electrical insulators and laboratory ware. In art history and archaeology, especially of ancient and prehistoric periods, pottery often means vessels only, and sculpted figurines of the same material are called terracottas.

<span class="mw-page-title-main">Raku ware</span> Type of Japanese pottery traditionally used in tea ceremonies

Raku ware is a type of Japanese pottery traditionally used in Japanese tea ceremonies, most often in the form of chawan tea bowls. It is traditionally characterised by being hand-shaped rather than thrown, fairly porous vessels, which result from low firing temperatures, lead glazes and the removal of pieces from the kiln while still glowing hot. In the traditional Japanese process, the fired raku piece is removed from the hot kiln and is allowed to cool in the open air.

<span class="mw-page-title-main">Earthenware</span> Nonvitreous pottery

Earthenware is glazed or unglazed nonvitreous pottery that has normally been fired below 1,200 °C (2,190 °F). Basic earthenware, often called terracotta, absorbs liquids such as water. However, earthenware can be made impervious to liquids by coating it with a ceramic glaze, and is used for the great majority of modern domestic earthenware. The main other important types of pottery are porcelain, bone china, and stoneware, all fired at high enough temperatures to vitrify. End applications include tableware, decorative ware such as figurines.

<span class="mw-page-title-main">Stoneware</span> Term for pottery or other ceramics fired at a relatively high temperature

Stoneware is a rather broad term for pottery fired at a relatively high temperature. A modern technical definition is a vitreous or semi-vitreous ceramic made primarily from stoneware clay or non-refractory fire clay. End applications include tableware, decorative ware such as figurines.

<span class="mw-page-title-main">Japanese pottery and porcelain</span> Ceramics from Japan

Pottery and porcelain, is one of the oldest Japanese crafts and art forms, dating back to the Neolithic period. Kilns have produced earthenware, pottery, stoneware, glazed pottery, glazed stoneware, porcelain, and blue-and-white ware. Japan has an exceptionally long and successful history of ceramic production. Earthenwares were made as early as the Jōmon period, giving Japan one of the oldest ceramic traditions in the world. Japan is further distinguished by the unusual esteem that ceramics holds within its artistic tradition, owing to the enduring popularity of the tea ceremony.

<span class="mw-page-title-main">Celadon</span> Term for ceramics with two different types of glazes

Celadon is a term for pottery denoting both wares glazed in the jade green celadon color, also known as greenware or "green ware", and a type of transparent glaze, often with small cracks, that was first used on greenware, but later used on other porcelains. Celadon originated in China, though the term is purely European, and notable kilns such as the Longquan kiln in Zhejiang province are renowned for their celadon glazes. Celadon production later spread to other parts of East Asia, such as Japan and Korea as well as Southeast Asian countries such as Thailand. Eventually, European potteries produced some pieces, but it was never a major element there. Finer pieces are in porcelain, but both the color and the glaze can be produced in stoneware and earthenware. Most of the earlier Longquan celadon is on the border of stoneware and porcelain, meeting the Chinese but not the European definitions of porcelain.

<span class="mw-page-title-main">Saggar</span> Type of kiln furniture

A saggar is a type of kiln furniture. It is a ceramic boxlike container used in the firing of pottery to enclose or protect ware being fired inside a kiln. The name may be a contraction of the word safeguard.

<span class="mw-page-title-main">Oribe ware</span> Type of Japanese pottery

Oribe ware is a style of Japanese pottery that first appeared in the sixteenth century. It is a type of Japanese stoneware recognized by its freely-applied glaze as well as its dramatic visual departure from the more somber, monochrome shapes and vessels common in Raku ware of the time. The ceramics were often asymmetrical, embracing the eccentricity of randomized shapes. Deformed shapes were not at all uncommon. These shapes were achieved through the implementation of moulding as a technique, as opposed to working on a potter’s wheel. Sometimes, bowls were so deformed that they became difficult to use – whisking tea could even become a difficult task.

<span class="mw-page-title-main">Shino ware</span> Type of Japanese pottery

Shino ware is Japanese pottery, usually stoneware, originally from Mino Province, in present-day Gifu Prefecture, Japan. It emerged in the 16th century, but the use of shino glaze is now widespread, both in Japan and abroad. It is identified by thick white glazes, red scorch marks, and a texture of small holes. Some experts believe it should not be treated as distinct from Oribe ware but described as "white Oribe", with the pottery usually called just Oribe described as "green Oribe" instead.

<span class="mw-page-title-main">Shigaraki ware</span>

Shigaraki ware (信楽焼) is a type of stoneware pottery made in Shigaraki area, Japan. The kiln is one of the Six Ancient Kilns in Japan. Although figures representing the tanuki are a popular product included as Shigaraki ware, the kiln and local pottery tradition has a long history.

<span class="mw-page-title-main">Royal Doulton</span> British ceramics manufacturing company

Royal Doulton is an English ceramic and home accessories manufacturer that was founded in 1815. Operating originally in Vauxhall, London, and later moving to Lambeth, in 1882 it opened a factory in Burslem, Stoke-on-Trent, in the centre of English pottery. From the start, the backbone of the business was a wide range of utilitarian wares, mostly stonewares, including storage jars, tankards and the like, and later extending to drain pipes, lavatories, water filters, electrical porcelain and other technical ceramics. From 1853 to 1901, its wares were marked Doulton & Co., then from 1901, when a royal warrant was given, Royal Doulton.

<span class="mw-page-title-main">Chinese ceramics</span> Pottery and porcelain from China

Chinese ceramics show a continuous development since pre-dynastic times and are one of the most significant forms of Chinese art and ceramics globally. The first pottery was made during the Palaeolithic era. Chinese ceramics range from construction materials such as bricks and tiles, to hand-built pottery vessels fired in bonfires or kilns, to the sophisticated Chinese porcelain wares made for the imperial court and for export. Porcelain was a Chinese invention and is so identified with China that it is still called "china" in everyday English usage.

<span class="mw-page-title-main">Tin-glazing</span>

Tin-glazing is the process of giving tin-glazed pottery items a ceramic glaze that is white, glossy and opaque, which is normally applied to red or buff earthenware. Tin-glaze is plain lead glaze with a small amount of tin oxide added. The opacity and whiteness of tin glaze encourage its frequent decoration. Historically this has mostly been done before the single firing, when the colours blend into the glaze, but since the 17th century also using overglaze enamels, with a light second firing, allowing a wider range of colours. Majolica, maiolica, delftware and faience are among the terms used for common types of tin-glazed pottery.

<span class="mw-page-title-main">Ash glaze</span> Ceramic glazes made from wood-ash

Ash glazes are ceramic glazes made from the ash of various kinds of wood or straw. They have historically been important in East Asia, especially Chinese pottery, Korean pottery, and Japanese pottery. Many traditionalist East Asian potteries still use ash glazing, and it has seen a large revival in studio pottery in the West and East. Some potters like to achieve random effects by setting up the kiln so that ash created during firing falls onto the pots; this is called "natural" or "naturally occurring" ash glaze. Otherwise the ash is mixed with water, and often clay, and applied as a paste.

<span class="mw-page-title-main">Ceramic glaze</span> Fused coating on ceramic objects

Ceramic glaze, or simply glaze, is a glassy coating on ceramics. It is used for decoration, to ensure the item is impermeable to liquids and to minimise the adherence of pollutants.

This is a list of pottery and ceramic terms.

<span class="mw-page-title-main">Fritware</span>

Fritware, also known as stone-paste, is a type of pottery in which frit is added to clay to reduce its fusion temperature. The mixture may include quartz or other siliceous material. An organic compound such as gum or glue may be added for binding. The resulting mixture can be fired at a lower temperature than clay alone. A glaze is then applied on the surface.

<span class="mw-page-title-main">Fulham Pottery</span> Stoneware maker in London, 1672-1956

The Fulham Pottery was founded in Fulham, London, by John Dwight in 1672, at the junction of New King's Road and Burlington Road, Fulham, not far from Putney Bridge. Dwight is the earliest clearly documented maker of stoneware in England, although immigrant Dutch or German potters were probably active several decades before. By 1690 there was a rival stoneware operation in Fulham, run by the Dutch Elers brothers, who after a few years went off to become important early figures in transforming the Staffordshire pottery industry.

<span class="mw-page-title-main">Ceramic art</span> Decorative objects made from clay and other raw materials by the process of pottery

Ceramic art is art made from ceramic materials, including clay. It may take forms including artistic pottery, including tableware, tiles, figurines and other sculpture. As one of the plastic arts, ceramic art is one of the visual arts. While some ceramics are considered fine art, such as pottery or sculpture, most are considered to be decorative, industrial or applied art objects. Ceramics may also be considered artefacts in archaeology. Ceramic art can be made by one person or by a group of people. In a pottery or ceramic factory, a group of people design, manufacture and decorate the art ware. Products from a pottery are sometimes referred to as "art pottery". In a one-person pottery studio, ceramists or potters produce studio pottery.

<span class="mw-page-title-main">Koishiwara ware</span> Type of Japanese pottery

Koishiwara ware, formerly known as Nakano ware, is a type of Japanese pottery traditionally from Koishiwara, Fukuoka Prefecture in western Japan. Koishiwara ware consists of utility vessels such as bowls, plates, and tea cups. The style is often slipware.

References

  1. 1 2 3 4 Dictionary Of Ceramics. Arthur Dodd & David Murfin. 3rd edition. The Institute Of Minerals. 1994.
  2. "Salt Glaze ware". www.thepotteries.org. Retrieved 2016-07-01.
  3. ’The ABC of English salt-glaze stoneware from Dwight to Doulton.’ Blacker J.F. S.Paul & Company, London 1922.
  4. 'Dictionary of Ceramics' 3rd ed. A.Dodd, D.Murfin. The Instiutue of Materials. 1994
  5. 'If You Believe What You Read About Salt Glazing Read On ...' I.Lewis. Interceram 45, No.4, 1996
  6. 'Development Of A Low-Emission Salt-Glazing Procedure Using NaOH Instead Of NaCl' R.Knodt, A.Normann, S.Blasner, J.Denissen, J. de Jong Keram.Z. 53, No.4, 2001.
  7. "Home". North East Life. Retrieved 2016-07-01.
  8. "Errington Reay - Outstanding Handmade Pottery". www.erringtonreay.co.uk. Retrieved 2016-07-01.
  9. "What´s on North East - Venues". www.whatsonnortheast.com. Archived from the original on 2016-04-02. Retrieved 2016-07-01.
  10. 1 2 "Salt Glazed 'Bartmann' Jug, German, 1594 CE". www-01.glendale.edu. Retrieved 2016-07-01.
  11. G.C.Nelson. 'Ceramics: A Potter's Handbook.' Holt, Rinehart and Winston, Inc., New York. 1966. ISBN   0-03-086000-8
  12. "Production strategies in the Nottingham salt-glazed stoneware industry - The University of Nottingham". www.nottingham.ac.uk. Retrieved 2016-07-01.
  13. 'Salt-glazed Stoneware in Early America.' J.E.Skerry, S.Findlen Hood. University Press of New England & Colonial Williamsburg Foundation. 2009
  14. "Subscribers Only | Maine Antique Digest". www.maineantiquedigest.com. Retrieved 2016-07-01.
  15. 'A Guide To Artifacts Of Colonial America.' I.N.Hume. University of Pennsylvania Press. 2001.
  16. Stegnel, Gil. "Salt Firing, Science, and the Environment" (PDF). Ceramic Arts Daily.
  17. "SSI Circulars". www.dcmsme.gov.in. Retrieved 2016-07-01.
  18. Services, NIIR Project Consultancy. "Projects on PIPE & TUBES | NPCS". www.niir.org. Retrieved 2016-07-01.
  19. 'John Dwight's Fulham Pottery, 1672-1978: A Collection of Documentary Sources.' D.Haselgrove & J.Murray. Journal of Ceramic History 11 (1979).
  20. 'John Dwight.' M.Bimson. Transactions of the English Ceramic Circle 5, no.2 (1961)
  21. "Industries: Pottery, Fulham stoneware | British History Online". www.british-history.ac.uk. Retrieved 2016-07-01.
  22. Perry, Michael. "Doulton history 1854-2005". www.potteryhistories.com. Retrieved 2016-07-01.
  23. 1 2 3 4 "Royal Doulton Potteries". www.thepotteries.org. Retrieved 2016-07-01.
  24. Royal Doulton, McKeown J. Shire Publications Ltd. 2004.
  25. "Doulton ware | pottery" . Retrieved 2016-07-01.
  26. "Stiff Dates". www.mernick.org.uk. Retrieved 2016-07-01.
  27. Tyler, Sarah Lester (1906). Norwich Early Homes and History. Faith Trumbull Chapter of D.A.R. p. 19.
  28. Ioannou, Norris (1987). A German Potter In the Barossa Valley, South Australia, c.1850-1883 (PDF). Australian Historical Archaeology. p. 33.
  29. Troy, Jack. "Sources of Sodium as Vapor Glaze". Studio Potter.
  30. Rado, P. An Introduction to the Technology Of Pottery. 2nd edition. Pergamon Press, 1988.

Further reading