6063 aluminium alloy

Last updated
A6063
Physical properties
Density (ρ)2.69 g/cm3 [1] [2]
Mechanical properties
Young's modulus (E)68.3 GPa (9,910 ksi)
Tensile strength (σt)145–186 MPa (21.0–27.0 ksi)
Elongation (ε)at break 18–33%
Poisson's ratio (ν)0.3
Thermal properties
Melting temperature (Tm)615 °C (1,139 °F)
Thermal conductivity (k)201–218 W/[m·K]
Linear thermal expansion coefficient (α)2.34·10−5/K
Specific heat capacity (c)900 J/kg·K
Electrical properties
Volume resistivity (ρ)30–35 n Ohm·m

AA 6063 is an aluminium alloy, with magnesium and silicon as the alloying elements. The standard controlling its composition is maintained by The Aluminum Association. It has generally good mechanical properties and is heat treatable and weldable. It is similar to the British aluminium alloy HE9.

Contents

6063 is the most common alloy used for aluminium extrusion. It allows complex shapes to be formed with very smooth surfaces fit for anodizing and so is popular for visible architectural applications such as window frames, door frames, roofs, and sign frames. [3] Applications requiring higher strength typically use 6061 or 6082 instead.

Chemical composition

The alloy composition of 6063 is: [2]

Aluminum alloy 6063
Constituent
element		Minimum
(% by weight)		Maximum
(% by weight)
Aluminium (Al)97.5%99.35%
Magnesium (Mg)0.45%0.90%
Silicon (Si)0.20%0.60%
Iron (Fe)00.35%
Chromium (Cr)00.10%
Copper (Cu)00.10%
Manganese (Mn)00.10%
Titanium (Ti)00.10%
Zinc (Zn)00.10%
(others)00.15% total
(0.05% each)

Mechanical properties

The mechanical properties of 6063 depend greatly on the temper, or heat treatment, of the material. [2]

6063-O

Un-heat-treated 6063 has maximum tensile strength no more than 130 MPa (19,000 psi), and no specified maximum yield strength. The material has elongation (stretch before ultimate failure) of 18%.

6063-T1

T1 temper 6063 has an ultimate tensile strength of at least 120 MPa (17,000 psi) in thicknesses up to 12.7 mm (0.5 in), and 110 MPa (16,000 psi) from 13 to 25 mm (0.5 to 1 in) thick, and yield strength of at least 62 MPa (9,000 psi) in thickness up to 13 millimetres (0.5 in) and 55 MPa (8,000 psi) from 13 mm (0.5 in) thick. It has elongation of 12%.

6063-T4

6063-T5

T5 temper 6063 has an ultimate tensile strength of at least 140 MPa (20,000 psi) in thicknesses up to 13 millimetres (0.5 in), and 130 MPa (19,000 psi) from 13 mm (0.5 in) thick, and yield strength of at least 97 MPa (14,000 psi) up to 13 millimetres (0.5 in) and 90 MPa (13,000 psi) from13 to 25 mm (0.5 to 1 in). It has elongation of 8%.

6063-T6

T6 temper 6063 has an ultimate tensile strength of at least 190 MPa (28,000 psi) and yield strength of at least 160 MPa (23,000 psi). In thicknesses of 3.15 millimetres (0.124 in) or less, it has elongation of 8% or more; in thicker sections, it has elongation of 10%.

Other tempers

6063 is also produced in tempers T52, T53, T54, T55, and T832, with various improved desired properties.

Uses

6063 is used for architectural fabrication, window and door frames, pipe and tubing, and aluminium furniture. [2]

Welding

6063 is highly weldable, using tungsten inert gas welding. Typically, after welding, the properties near the weld are those of 6063-0, a loss of strength of up to 30%. The material can be re-heat-treated to restore a higher temper for the whole piece.

Related Research Articles

<span class="mw-page-title-main">Aluminium alloy</span> Alloy in which aluminium is the predominant metal

An aluminium alloy (UK/IUPAC) or aluminum alloy is an alloy in which aluminium (Al) is the predominant metal. The typical alloying elements are copper, magnesium, manganese, silicon, tin, nickel and zinc. There are two principal classifications, namely casting alloys and wrought alloys, both of which are further subdivided into the categories heat-treatable and non-heat-treatable. About 85% of aluminium is used for wrought products, for example rolled plate, foils and extrusions. Cast aluminium alloys yield cost-effective products due to the low melting point, although they generally have lower tensile strengths than wrought alloys. The most important cast aluminium alloy system is Al–Si, where the high levels of silicon (4–13%) contribute to give good casting characteristics. Aluminium alloys are widely used in engineering structures and components where light weight or corrosion resistance is required.

Eglin steel (ES-1) is a high-strength, high-performance, low-alloy, low-cost steel, developed for a new generation of bunker buster type bombs, e.g. the Massive Ordnance Penetrator and the improved version of the GBU-28 bomb known as EGBU-28. It was developed in collaboration between the US Air Force and the Ellwood National Forge Company.

A514 is a particular type of high strength steel, which is quenched and tempered alloy steel, with a yield strength of 100,000 psi. The ArcelorMittal trademarked name is T-1. A514 is primarily used as a structural steel for building construction. A517 is a closely related alloy that is used for the production of high-strength pressure vessels.

A36 steel is a common structural steel alloy utilized in the United States. The A36 standard was established by the ASTM International. The standard was published in 1960 and has been updated several times since. Prior to 1960, the dominant standards for structural steel in North America were A7 and A9. Note that SAE/AISI A7 and A9 tool steels are not the same as the obsolete ASTM A7 and A9 structural steels.

6061 aluminium alloy is a precipitation-hardened aluminium alloy, containing magnesium and silicon as its major alloying elements. Originally called "Alloy 61S", it was developed in 1935. It has good mechanical properties, exhibits good weldability, and is very commonly extruded. It is one of the most common alloys of aluminium for general-purpose use.

7075 aluminium alloy (AA7075) is an aluminium alloy with zinc as the primary alloying element. It has excellent mechanical properties and exhibits good ductility, high strength, toughness, and good resistance to fatigue. It is more susceptible to embrittlement than many other aluminium alloys because of microsegregation, but has significantly better corrosion resistance than the alloys from the 2000 series. It is one of the most commonly used aluminium alloys for highly stressed structural applications and has been extensively used in aircraft structural parts.

2024 aluminium alloy is an aluminium alloy, with copper as the primary alloying element. It is used in applications requiring high strength-to-weight ratio, as well as good fatigue resistance. It is weldable only through friction welding, and has average machinability. Due to poor corrosion resistance, it is often clad with aluminium or Al-1Zn for protection, although this may reduce the fatigue strength. In older systems of terminology, 2XXX series alloys were known as duralumin, and this alloy was named 24ST.

5086 aluminium alloy is an aluminium–magnesium alloy, primarily alloyed with magnesium. It is not strengthened by heat treatment, instead becoming stronger due to strain hardening, or cold mechanical working of the material.

5083 aluminium alloy is an aluminium–magnesium alloy with magnesium and traces of manganese and chromium. It is highly resistant to attack by seawater and industrial chemicals.

7005 is an aluminium wrought alloy used in bicycle frames. Due to its relative ease of welding, it does not require expensive heat treating. It is, however, harder to form, making manufacture more challenging. It has an Ultimate Tensile Strength of 350 MPa, a Fatigue Strength of 150 MPa and a density of 2.78 g/cm3. It does not need to be precipitation hardened, but can be cooled in air.

5059 aluminium alloy is an aluminium–magnesium alloy, primarily alloyed with magnesium. It is not strengthened by heat treatment, instead becoming stronger due to strain hardening, or cold mechanical working of the material.

2014 aluminium alloy (aluminum) is an aluminium-based alloy often used in the aerospace industry.

7068 aluminium alloy is one of the strongest commercially available aluminium alloys, with a tensile strength comparable to that of some steels. This material, also known as an aircraft alloy, is heat treatable.

6005 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family. It is closely related, but not identical, to 6005A aluminium alloy. The main difference between the two alloys is that 6005 has a higher minimum composition percentage of aluminium than 6005A. The most common forming method is extrusion. It can also be forged or rolled, but as a wrought alloy it is not used in casting. It is commonly heat treated to produce tempers with a higher strength at the expense of ductility.

6005A aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family. It is closely related, but not identical, to 6005 aluminium alloy. Between those two alloys, 6005A is more heavily alloyed, but the difference does not make a marked impact on material properties. It can be formed by extrusion, forging or rolling, but as a wrought alloy it is not used in casting. It cannot be work hardened, but is commonly heat treated to produce tempers with a higher strength at the expense of ductility.

6060 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family. It is much more closely related to the alloy 6063 than to 6061. The main difference between 6060 and 6063 is that 6063 has a slightly higher magnesium content. It can be formed by extrusion, forging or rolling, but as a wrought alloy it is not used in casting. It cannot be work hardened, but is commonly heat treated to produce tempers with a higher strength but lower ductility.

6105 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family. It is one of the least common of the alloys in this series. While most wrought aluminium alloys are covered by multiple standards, 6105 is only dealt with in ASTM B221: Standard Specification for Aluminum and Aluminum-Alloy Extruded Bars, Rods, Wire, Profiles, and Tubes. It is formed by extrusion, and supplied in heat treated form. It can alternately referred to by the UNS designation A96105.

The 6463 aluminium alloy is an aluminium alloy in the wrought aluminium-magnesium-silicon family. It is related to 6063 aluminium alloy, but unlike 6063 it is generally not formed using any processes other than extrusion. It is commonly heat treated to produce tempers with a higher strength but lower ductility. Like 6063, it is often used in architectural applications.

<span class="mw-page-title-main">HY-80</span> Alloy steel

HY-80 is a high-tensile, high yield strength, low alloy steel. It was developed for use in naval applications, specifically the development of pressure hulls for the US nuclear submarine program and is still currently used in many naval applications. It is valued for its strength to weight ratio.

USAF-96 is a high-strength, high-performance, low-alloy, low-cost steel, developed for new generation of bunker buster type bombs, e.g. the Massive Ordnance Penetrator and the improved version of the GBU-28 bomb known as EGBU-28. It was developed by the US Air Force at the Eglin Air Force Munitions Directorate. It uses only materials domestic to the USA. In particular it requires no tungsten.

References

  1. ↑ ASM Handbook Committee (1990). Properties and Selection: Nonferrous alloys and special-purpose materials. ASM Handbook. Vol. 2. p. 103. doi:10.31399/asm.hb.v02.9781627081627. ISBN   978-1-62708-162-7.
  2. 1 2 3 4 "Alloy 6063" (PDF). catalog datasheet. Alcoa Aluminum. Archived from the original (PDF) on 2003-10-06. Retrieved 1 November 2006.
  3. ↑ "Aluminium 6063/6063A". Aluminium Alloys – Properties, Fabrication and Applications. 21 April 2005. Retrieved 2016-07-25.

Further reading

Aluminum alloy table

This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.