7075 aluminium alloy

Last updated
A7075 T6
Physical properties
Density (ρ)2.81 g/cm3 (0.102 lb/cu in)
Mechanical properties
Young's modulus (E)71.7 GPa (10,400 ksi)
Tensile strength (σt)572 MPa (83.0 ksi)
Elongation (ε)at break 11%
Poisson's ratio (ν)0.33
Hardness—Rockwell 87 HRB
Thermal properties
Melting temperature (Tm)477 °C (891 °F)
Thermal conductivity (k) [1] 130–150 W/m*K
Linear thermal expansion coefficient (α)2.36*10−5 K−1
Specific heat capacity (c)714.8 J/kg*K
Electrical properties
Volume resistivity (ρ)51.5 nOhm*m

7075 aluminium alloy (AA7075) is an aluminium alloy with zinc as the primary alloying element. It has excellent mechanical properties and exhibits good ductility, high strength, toughness, and good resistance to fatigue. It is more susceptible to embrittlement than many other aluminium alloys because of microsegregation, but has significantly better corrosion resistance than the alloys from the 2000 series. It is one of the most commonly used aluminium alloys for highly stressed structural applications and has been extensively used in aircraft structural parts. [2]

Contents

7075 aluminium alloy's composition roughly includes 5.6–6.1% zinc, 2.1–2.5% magnesium, 1.2–1.6% copper, and less than a half percent of silicon, iron, manganese, titanium, chromium, and other metals. It is produced in many tempers, some of which are 7075-0, 7075-T6, 7075-T651.

The first 7075 was developed in secret by a Japanese company, Sumitomo Metal, in 1935, [3] but reverse engineered by Alcoa in 1943, after examining a captured Japanese aircraft. [4] 7075 was standardized for aerospace use in 1945. [5] 7075 was eventually used for airframe production in the Imperial Japanese Navy.

Basic properties

Aluminium 7075A has a density of 2.810 g/cm3. [6]

Mechanical properties

The mechanical properties of 7075 depend greatly on the tempering of the material. [7]

7075-O

Un-heat-treated 7075 (7075-0 temper) has a maximum tensile strength of no more than 280 MPa (40,000 psi), and maximum yield strength of no more than 140 MPa (21,000 psi). The material has an elongation (stretch before ultimate failure) of 9–10%. As is the case for all 7075 aluminum alloys, 7075-0 is highly corrosion-resistant combined with generally acceptable strength profile.

7075-T6

T6 temper 7075 has an ultimate tensile strength of 510–540 MPa (74,000–78,000 psi) and yield strength of at least 430–480 MPa (63,000–69,000 psi). It has a failure elongation of 5–11%. [8]

The T6 temper is usually achieved by homogenizing the cast 7075 at 450 °C for several hours, quenching, and then ageing at 120 °C for 24 hours. This yields the peak strength of the 7075 alloys. The strength is derived mainly from finely dispersed eta and eta' precipitates both within grains and along grain boundaries. [9]

7075-T651

T651 temper 7075 has an ultimate tensile strength of 570 MPa (83,000 psi) and yield strength of 500 MPa (73,000 psi). It has a failure elongation of 3–9%. These properties can change depending on the form of material used. The thicker plates may exhibit lower strengths and elongation than the numbers listed above.

7075-T7

T7 temper has an ultimate tensile strength of 505 MPa (73,200 psi) and a yield strength of 435 MPa (63,100 psi). It has a failure elongation of 13%. [10] T7 temper is achieved by overaging (meaning aging past the peak hardness) the material. This is often accomplished by aging at 100–120 °C for several hours and then at 160–180 °C for 24 hours or more. The T7 temper produces a microstructure of mostly eta precipitates. In contrast to the T6 temper, these eta particles are much larger and prefer growth along the grain boundaries. This reduces the susceptibility to stress corrosion cracking. T7 temper is equivalent to T73 temper. [9]

7075-RRA

The retrogression and reage (RRA) temper is a multistage heat treatment temper. Starting with a sheet in the T6 temper, it involves overaging past peak hardness (T6 temper) to near the T7 temper. A subsequent reaging at 120 °C for 24 hours returns the hardness and strength to or very nearly to T6 temper levels. [9]

RRA treatments can be accomplished with many different procedures. The general guidelines are retrogressing between 180 and 240 °C for 15 min 10 s. [11]

Equivalent materials

Table of equivalent materials [12]
USISOEuropean UnionGermanyJapanAustraliaChina
StandardAISI (UNS)StandardDesignationStandardNumerical (Chemical symbols)StandardDesignation (Material number)StandardGradeStandardDesignationStandardGrade
ASTM B209,

ASTM B210, ASTM B211, ASTM B221, AMS-QQ-A-225/9, AMS-QQ-A-200/11, AMS-QQ-A-250/12, AMS-WW-T-700/7

7075

(A97075)

ISO 209AW-7075EN 573-3EN AW-7075

(EN AW-AlZn5,5MgCu)

DIN 1725-1AlZnMgCu1,5 (3.4365)JIS H4000;

JIS H4040

7075AS 2848.1,

AS/NZS 1734, AS/NZS 1865, AS/NZS 1866

7075GB/T 3190;

GB/T 3880.2

7075

Uses

The world's first mass-production usage of the 7075 aluminum alloy was for the Mitsubishi A6M Zero fighter. The aircraft was known for its excellent maneuverability which was facilitated by the higher strength of 7075 compared to previous aluminum alloys.

7000 series alloys such as 7075 are often used in transport applications due to their high specific strength, including marine, automotive and aviation. [7] [13] These same properties lead to its use in rock climbing equipment, bicycle components, inline-skating-frames and hang glider airframes are commonly made from 7075 aluminium alloy. Hobby-grade RC models commonly use 7075 and 6061 for chassis plates. 7075 is used in the manufacturing of M16 rifles for the U.S. military as well as AR-15 style rifles for the civilian market. In particular high-quality M16 rifle lower and upper receivers, as well as extension tubes, are typically made from 7075-T6 alloy. Desert Tactical Arms, SIG Sauer, and French armament company PGM use it for their precision rifles. It is also commonly used in shafts for lacrosse sticks, such as the STX sabre, and camping knife and fork sets. It is a common material used in competition yo-yos as well.

Another application for the 7075-series alloy has been in connecting rods used in drag racing engines.  Aluminum rods do not have the fatigue life of forged steel rods, but have less mass than their steel counterparts, resulting in lower mechanical stress during periods in which an engine is operated under full-throttle, high-RPM conditions.

It has also been the standard material for crankcase guards on off-road motorcycles.

Due to its high strength, low density, thermal properties, and its ability to be highly polished, 7075 is widely used in mold tool manufacturing. This alloy has been further refined into other 7000 series alloys for this application, namely 7050 and 7020.

Aerospace applications

7075 was used in the Space Shuttle SRB nozzles, and the external tank SRB beam in the Inter-tank section. The forward- and aft skirt as well as the Interstage of the S-II, the second stage of the Saturn V was made from 7075. [14]

Applications

  1. Aircraft fittings
  2. Gears and shafts
  3. Missile parts
  4. Regulating valve parts
  5. Worm gears
  6. Aerospace/defense applications
  7. Automotive
  8. Bicycle Chainrings
  9. Bicycle Gearboxes
  10. Archery equipment


Trade names

7075 has been sold under various trade names including Zicral, Ergal, and Fortal Constructal. Some 7000 series alloys sold under brand names for making molds include Alumec 79, Alumec 89, Contal, Certal, Alumould, and Hokotol.

See also

  1. Northwest Airlines Flight 421
  2. https://www.thomasnet.com/articles/metals-metal-products/all-about-7075-aluminum-properties-strength-and-uses/
  3. WHAT ARE THE DIFFERENCES BETWEEN 6061 AND 7075 ALUMINUM?
  4. 7075 Aluminum: Get to Know its Properties and Uses
  5. Properties of 7075 aluminum alloy Archived 2018-10-16 at the Wayback Machine
  6. Properties of 7075 aluminum alloy
  7. 7075 aluminum

Related Research Articles

Beryllium copper (BeCu), also known as copper beryllium (CuBe), beryllium bronze, and spring copper, is a copper alloy with 0.5–3% beryllium. Copper beryllium alloys are often used because of their high strength and good conductivity of both heat and electricity. It is used for its ductility, weldability in metalworking, and machining properties. It has many specialized applications in tools for hazardous environments, musical instruments, precision measurement devices, bullets, and some uses in the field of aerospace. Beryllium copper and other beryllium alloys are harmful carcinogens that present a toxic inhalation hazard during manufacturing.

<span class="mw-page-title-main">Magnesium alloy</span> Mixture of magnesium with other metals

Magnesium alloys are mixtures of magnesium with other metals, often aluminium, zinc, manganese, silicon, copper, rare earths and zirconium. Magnesium alloys have a hexagonal lattice structure, which affects the fundamental properties of these alloys. Plastic deformation of the hexagonal lattice is more complicated than in cubic latticed metals like aluminium, copper and steel; therefore, magnesium alloys are typically used as cast alloys, but research of wrought alloys has been more extensive since 2003. Cast magnesium alloys are used for many components of modern automobiles and have been used in some high-performance vehicles; die-cast magnesium is also used for camera bodies and components in lenses.

<span class="mw-page-title-main">Aluminium alloy</span> Alloy in which aluminium is the predominant metal

An aluminium alloy (UK/IUPAC) or aluminum alloy is an alloy in which aluminium (Al) is the predominant metal. The typical alloying elements are copper, magnesium, manganese, silicon, tin, nickel and zinc. There are two principal classifications, namely casting alloys and wrought alloys, both of which are further subdivided into the categories heat-treatable and non-heat-treatable. About 85% of aluminium is used for wrought products, for example rolled plate, foils and extrusions. Cast aluminium alloys yield cost-effective products due to the low melting point, although they generally have lower tensile strengths than wrought alloys. The most important cast aluminium alloy system is Al–Si, where the high levels of silicon (4–13%) contribute to give good casting characteristics. Aluminium alloys are widely used in engineering structures and components where light weight or corrosion resistance is required.

Eglin steel (ES-1) is a high-strength, high-performance, low-alloy, low-cost steel, developed for a new generation of bunker buster type bombs, e.g. the Massive Ordnance Penetrator and the improved version of the GBU-28 bomb known as EGBU-28. It was developed in collaboration between the US Air Force and the Ellwood National Forge Company.

6061 aluminium alloy is a precipitation-hardened aluminium alloy, containing magnesium and silicon as its major alloying elements. Originally called "Alloy 61S", it was developed in 1935. It has good mechanical properties, exhibits good weldability, and is very commonly extruded. It is one of the most common alloys of aluminium for general-purpose use.

2024 aluminium alloy is an aluminium alloy, with copper as the primary alloying element. It is used in applications requiring high strength-to-weight ratio, as well as good fatigue resistance. It is weldable only through friction welding, and has average machinability. Due to poor corrosion resistance, it is often clad with aluminium or Al-1Zn for protection, although this may reduce the fatigue strength. In older systems of terminology, 2XXX series alloys were known as duralumin, and this alloy was named 24ST.

5086 aluminium alloy is an aluminium–magnesium alloy, primarily alloyed with magnesium. It is not strengthened by heat treatment, instead becoming stronger due to strain hardening, or cold mechanical working of the material.

AA 6063 is an aluminium alloy, with magnesium and silicon as the alloying elements. The standard controlling its composition is maintained by The Aluminum Association. It has generally good mechanical properties and is heat treatable and weldable. It is similar to the British aluminium alloy HE9.

<span class="mw-page-title-main">Alclad</span>

Alclad is a corrosion-resistant aluminium sheet formed from high-purity aluminium surface layers metallurgically bonded to high-strength aluminium alloy core material. It has a melting point of about 500 °C (932 °F). Alclad is a trademark of Alcoa but the term is also used generically.

5083 aluminium alloy is an aluminium–magnesium alloy with magnesium and traces of manganese and chromium. It is highly resistant to attack by seawater and industrial chemicals.

The skin of an aircraft is the outer surface which covers much of its wings and fuselage. The most commonly used materials are aluminum and aluminium alloys with other metals, including zinc, magnesium and copper.

<span class="mw-page-title-main">Friction stir processing</span>

Friction stir processing (FSP) is a method of changing the properties of a metal through intense, localized plastic deformation. This deformation is produced by forcibly inserting a non-consumable tool into the workpiece, and revolving the tool in a stirring motion as it is pushed laterally through the workpiece. The precursor of this technique, friction stir welding, is used to join multiple pieces of metal without creating the heat affected zone typical of fusion welding.

7005 is an aluminium wrought alloy used in bicycle frames. Due to its relative ease of welding, it does not require expensive heat treating. It is, however, harder to form, making manufacture more challenging. It has an Ultimate Tensile Strength of 350 MPa, a Fatigue Strength of 150 MPa and a density of 2.78 g/cm3. It does not need to be precipitation hardened, but can be cooled in air.

5059 aluminium alloy is an aluminium–magnesium alloy, primarily alloyed with magnesium. It is not strengthened by heat treatment, instead becoming stronger due to strain hardening, or cold mechanical working of the material.

2014 aluminium alloy (aluminum) is an aluminium-based alloy often used in the aerospace industry.

7068 aluminium alloy is one of the strongest commercially available aluminium alloys, with a tensile strength comparable to that of some steels. This material, also known as an aircraft alloy, is heat treatable.

7022 aluminium alloy is an alloy in the wrought aluminium-zinc family. It is one of the more complex grades in the 7000 series, with at least 87.85% aluminium by weight.

USAF-96 is a high-strength, high-performance, low-alloy, low-cost steel, developed for new generation of bunker buster type bombs, e.g. the Massive Ordnance Penetrator and the improved version of the GBU-28 bomb known as EGBU-28. It was developed by the US Air Force at the Eglin Air Force Munitions Directorate. It uses only materials domestic to the USA. In particular it requires no tungsten.

Aluminium 7050 alloy is a heat treatable alloy. It has high toughness, high strength. It has high stress corrosion cracking resistance. It has electric conductivity of value having 40 percent of copper. 7050 aluminium is known as a commercial aerospace alloy.

Aluminium–copper alloys (AlCu) are aluminium alloys that consist largely of aluminium (Al) and traces of copper (Cu) as the main alloying elements. Important grades also contain additives of magnesium, iron, nickel and silicon, often manganese is also included to increase strength. The main area of application is aircraft construction. The alloys have medium to high strength and can be age hardened. They are both wrought alloy. Also available as cast alloy. Their susceptibility to corrosion and their poor weldability are disadvantageous.

References

  1. ↑ Juan J. Valencia, Peter N. Quested, "Thermophysical Properties"
  2. ↑ ASM Handbook Volume 2: Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, 1990 pp. 137–38
  3. ↑ Yoshio, Baba."Extra super duralumin and successive aluminium alloys for aircraft." Journal of Japan Institute of Light Metals (Sumitomo Light Metal Ind. Ltd., Japan) (in Japanese), Volume 39, Issue 5, p. 378. Retrieved: 22 November 2015.
  4. ↑ Yoshida, Hideo (2020). Shoeisha. ISBN   978-4-86693-295-8
  5. ↑ Canadian Aeronautics and Space Journal, 1989 vol 35-36 p. 129
  6. ↑ "7075 (AlZn5.5MgCu, 3.4365, 2L95, A97075) Aluminum :: MakeItFrom.com". www.makeitfrom.com. Retrieved 22 April 2018.
  7. 1 2 Alcoa 7075 data sheet Archived 2013-08-29 at the Wayback Machine (PDF), accessed October 13, 2006
  8. ↑ "ASM Material Data Sheet". asm.matweb.com. Archived from the original on 16 October 2018. Retrieved 22 April 2018.
  9. 1 2 3 Park, J. K., and A. J. Ardell. "Microstructures of the Commercial 7075 AI Alloy in the T651 and T7 Tempers". Metall. Trans. A. 14A (1983): 1957. Print.
  10. ↑ "ASM Material Data Sheet". asm.matweb.com. Retrieved 22 April 2018.
  11. ↑ Cina, Baruch M. REDUCING THE SUSCEPTIBILITY OF ALLOYS, PARTICULARLY ALUMINIUM ALLOYS, TO STRESS CORROSION CRACKING. Israel Aircraft Industries Ltd., assignee. Patent 3856584. 24 Dec. 1974. Print.
  12. ↑ "7075 Aluminum Alloy Properties, 7075-T6, T7351, T651". www.theworldmaterial.com. Archived from the original on 2021-10-16.
  13. ↑ T Hashimoto, S Jyogan (Showa Aluminium), K Nakata, Y G Kin and M Ushio (Osaka University): FSW joining of high strength Al alloy
  14. ↑ McCutcheon, Kimble D. (3 August 2022). "U.S. Manned Rocket Propulsion Evolution Part 8.20: The Saturn V S-II".

Further reading

This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.