A building in Canterbury, England, which displays its long history in different building styles and glazing of every century from the 16th to the 20th included.
Architectural glass is glass that is used as a building material. It is most typically used as transparent glazing material in the building envelope, including windows in the external walls. Glass is also used for internal partitions and as an architectural feature. When used in buildings, glass is often of a safety type, which include reinforced, toughened and laminated glasses.
1330: "Crown glass" for art work and vessels first produced in Rouen, France.[2] "Broad Sheet" also produced. Both were also supplied for export.
1500s: A method of making mirrors out of plate glass was developed by Venetian glassmakers on the island of Murano, who covered the back of the glass with a mercury-tin amalgam, obtaining near-perfect and undistorted reflection.
1620s: "Blown plate" first produced in London.[1] Used for mirrors and coach plates.[3]
1678: "Crown glass" first produced in London.[4] This process dominated until the 19th century.
1843: An early form of "float glass" invented by Henry Bessemer, pouring glass onto liquid tin. Expensive and not a commercial success.
1874: Tempered glass is developed by Francois Barthelemy Alfred Royer de la Bastie (1830–1901) of Paris, France, by quenching almost molten glass in a heated bath of oil or grease.
Glass casting is the process in which glass objects are cast by directing molten glass into a mould where it solidifies. The technique has been used since the Egyptian period. Modern cast glass is formed by a variety of processes such as kiln casting, or casting into sand, graphite or metal moulds. Cast glass windows, albeit with poor optical qualities, began to appear in the most important buildings in Rome and the most luxurious villas of Herculaneum and Pompeii.[10]
Crown glass
The concentric arcs that distort some of these panes indicate they are crown glass, possibly of the 16th century.
One of the earliest methods of glass window manufacture was the crown glass method. Hot blown glass was cut open opposite the pipe, then rapidly spun on a table before it could cool. Centrifugal force shaped the hot globe of glass into a round, flat sheet. The sheet would then be broken off the pipe and trimmed to form a rectangular window to fit into a frame.
At the center of a piece of crown glass, a thick remnant of the original blown bottle neck would remain, hence the name "bullseye". Optical distortions produced by the bullseye could be reduced by grinding the glass. The development of diaper latticed windows was in part because three regular diamond-shaped panes could be conveniently cut from a piece of Crown glass, with minimum waste and with minimum distortion.
This method for manufacturing flat glass panels was very expensive and could not be used to make large panes. It was replaced in the 19th century by the cylinder, sheet, and rolled plate processes, but it is still used in traditional construction and restoration.
In this manufacturing process, glass is blown into a cylindrical iron mould. The ends are cut off and a cut is made down the side of the cylinder. The cut cylinder is then placed in an oven where the cylinder unrolls into a flat glass sheets.
Drawn Sheet glass (Fourcault process)
The uneven surface of old glass is visible in the reflection on this window pane.
Drawn Sheet glass was made by dipping a leader into a vat of molten glass then pulling that leader straight up while a film of glass hardened just out of the vat – this is known as the Fourcault process. This film or ribbon was pulled up continuously held by tractors on both edges while it cooled. After 12 metres or so it was cut off the vertical ribbon and tipped down to be further cut. This glass is clear but has thickness variations due to small temperature changes just out of the vat as it was hardening. These variations cause lines of slight distortions. This glass may still be seen in older houses. Float glass replaced this process.
Irving Wightman Colburn development a similar method independently. He began experimenting with the method in 1899, and started production in 1906. He went bankrupt, but was bought by Michael Joseph Owens. Because the method was imperfect, they kept refining it till 1916 when they felt it was perfect, and opened a glass factory based on the technology the year after.[11]
In 1838, James Hartley was granted a patent for Hartley's Patent Rolled Plate, manufactured by a new cast glass process. The glass is taken from the furnace in large iron ladles, which are carried upon slings running on overhead rails; from the ladle the glass is thrown upon the cast-iron bed of a rolling-table; and is rolled into sheet by an iron roller, the process being similar to that employed in making plate-glass, but on a smaller scale. The sheet thus rolled is roughly trimmed while hot and soft, so as to remove those portions of glass which have been spoiled by immediate contact with the ladle, and the sheet, still soft, is pushed into the open mouth of an annealing tunnel or temperature-controlled oven called a lehr, down which it is carried by a system of rollers.
The polished plate glass process starts with sheet or rolled plate glass. This glass is dimensionally inaccurate and often created visual distortions. These rough panes were ground flat and then polished clear. This was a fairly expensive process.
Before the float process, mirrors were plate glass as sheet glass had visual distortions that were akin to those seen in amusement park or funfair mirrors.
In 1918 the Belgian engineer Emil Bicheroux improved the plate glass manufacturing by pouring molten glass between two rollers, which resulted in more even thickness and fewer undulations, and reduced the need for grinding and polishing. This process was further improved in the US.[12]
Rolled plate (figured) glass
Figure rolled glass
The elaborate patterns found on figured (or 'Cathedral') rolled-plate glass are produced in a similar fashion to the rolled plate glass process except that the plate is cast between two rollers, one of which carries a pattern. On occasion, both rollers can carry a pattern. The pattern is impressed upon the sheet by a printing roller which is brought down upon the glass as it leaves the main rolls while still soft. This glass shows a pattern in high relief. The glass is then annealed in a lehr.
The glass used for this purpose is typically whiter in colour than the clear glasses used for other applications.
Only some of the figured glasses may be toughened, dependent on the depth of the embossed pattern. Single rolled figured glass, where the pattern is only imprinted into one surface, may be laminated to produce a safety glass. The much less common 'double rolled figured glass', where the pattern is embossed into both surfaces, can not be made into a safety glass but will already be thicker than average figured plate to accommodate both patterned faces. The finished thickness being dependent on the imprinted design.
Ninety percent of the world's flat glass is produced by the float glass process[citation needed] invented in the 1950s by Sir Alastair Pilkington of Pilkington Glass, in which molten glass is poured onto one end of a molten tin bath. The glass floats on the tin, and levels out as it spreads along the bath, giving a smooth face to both sides. The glass cools and slowly solidifies as it travels over the molten tin and leaves the tin bath in a continuous ribbon. The glass is then annealed by cooling in an oven called a lehr. The finished product has near-perfect parallel surfaces.
The side of the glass that has been in contact with the tin has a very small amount of the tin embedded in its surface. This quality makes that side of the glass easier to be coated in order to turn it into a mirror, however that side is also softer and easier to scratch.
Glass is produced in standard metric thicknesses of 2, 3, 4, 5, 6, 8, 10, 12, 15, 19 and 25mm, with 10mm being the most popular sizing in the architectural industry. Molten glass floating on tin in a nitrogen/hydrogen atmosphere will spread out to a thickness of about 6mm and stop due to surface tension. Thinner glass is made by stretching the glass while it floats on the tin and cools. Similarly, thicker glass is pushed back and not permitted to expand as it cools on the tin.
Toughened glass
Toughened (or tempered) glass is made from standard Float Glass to create an impact resistant, safety glass. Broken float glass yields sharp, hazardous shards. The toughening process introduces tensions between internal and external surfaces to increase its strength and ensure in the case of breakages the glass shatters into small, harmless pieces of glass. The cut glass panels are put into a toughening furnace. Here the glass panels are heated to upward of 600 degrees C and then the surfaces are cooled rapidly with cold air. This produces tensile stresses on the surface of the glass with the warmer internal glass particles. As the top thickness of the glass cools it contracts and forces the corresponding glass elements to contract to introduce stresses into the glass panel and increasing strength.[13]
Prism glass is architectural glass which bends light. It was frequently used around the turn of the 20th century to provide natural light to underground spaces and areas far from windows.[14] Prism glass can be found on sidewalks, where it is known as vault lighting,[15] in windows, partitions, and canopies, where it is known as prism tiles, and as deck prisms, which were used to light spaces below deck on sailing ships. It could be highly ornamented; Frank Lloyd Wright created over forty different designs for prism tiles.[16] Modern architectural prism lighting is generally done with a plastic film applied to ordinary window glass. [17]
Glass block, also known as glass brick, is an architectural element made from glass used in areas where privacy or visual obscuration is desired while admitting light, such as underground parking garages, washrooms, and municipal swimming baths. Glass block was originally developed in the early 1900s to provide natural light in industrial factories.
Annealed glass
Annealed glass is glass without internal stresses caused by heat treatment, i.e., rapid cooling, or by toughening or heat strengthening. Glass becomes annealed if it is heated above a transition point then allowed to cool slowly, without being quenched. Float glass is annealed during the process of manufacture. However, most toughened glass is made from float glass that has been specially heat-treated.
Annealed glass breaks into large, jagged shards that can cause serious injury and is considered a hazard in architectural applications. Building codes in many parts of the world restrict the use of annealed glass in areas where there is a high risk of breakage and injury, for example in bathrooms, door panels, fire exits and at low heights in schools or domestic houses. Safety glass, such as laminated or tempered must be used in these settings to reduce risk of injury.
Laminated glass is manufactured by bonding two or more layers of glass together with an interlayer, such as PVB, under heat and pressure, to create a single sheet of glass. When broken, the interlayer keeps the layers of glass bonded and prevents it from breaking apart. The interlayer can also give the glass a higher sound insulation rating.
There are several types of laminated glasses manufactured using different types of glass and interlayers which produce different results when broken.
Laminated glass that is made up of annealed glass is normally used when safety is a concern, but tempering is not an option. Windshields are typically laminated glasses. When broken, the PVB layer prevents the glass from breaking apart, creating a "spider web" cracking pattern.
Tempered laminated glass is designed to shatter into small pieces, preventing possible injury. When both pieces of glass are broken it produces a "wet blanket" effect and it will fall out of its opening.
Heat strengthened laminated glass is stronger than annealed, but not as strong as tempered. It is often used where security is a concern. It has a larger break pattern than tempered, but because it holds its shape (unlike the "wet blanket" effect of tempered laminated glass) it remains in the opening and can withstand more force for a longer period of time, making it much more difficult to get through.
Laminated glass has similar properties to ballistic glass, but the two should not be confused. Both are made using a PVB interlayer, but they have drastically different tensile strength. Ballistic glass and laminated glass are both rated to different standards and have a different shatter pattern.[18]
Heat-strengthened glass
Heat-strengthened glass, or tempered glass, is glass that has been heat treated to induce surface compression, but not to the extent of causing it to "dice" on breaking in the manner of tempered glass. On breaking, heat-strengthened glass breaks into sharp pieces that are typically somewhat smaller than those found on breaking annealed glass, and is intermediate in strength between annealed and toughened glasses.
Heat-strengthened glass can take a strong direct hit without shattering, but has a weak edge. By simply tapping the edge of heat-strengthened glass with a solid object, it is possible to shatter the entire sheet.
Chemically strengthened glass is a type of glass that has increased strength. When broken it still shatters in long pointed splinters similar to float (annealed) glass. For this reason, it is not considered a safety glass and must be laminated if a safety glass is required. Chemically strengthened glass is typically six to eight times the strength of annealed glass.
The glass is chemically strengthened by submerging the glass in a bath containing a potassium salt (typically potassium nitrate) at 450°C (842°F). This causes sodium ions in the glass surface to be replaced by potassium ions from the bath solution.
Unlike toughened glass, chemically strengthened glass may be cut after strengthening, but loses its added strength within the region of approximately 20mm of the cut. Similarly, when the surface of chemically strengthened glass is deeply scratched, this area loses its additional strength.
Glass coated with a low-emissivity substance can reflect radiant infrared energy, encouraging radiant heat to remain on the same side of the glass from which it originated, while letting visible light pass. This often results in more efficient windows because radiant heat originating from indoors in winter is reflected back inside, while infrared heat radiation from the sun during summer is reflected away, keeping it cooler inside.
Electrically heatable glass is a relatively new product, which helps to find solutions while designing buildings and vehicles. The idea of heating glass is based on usage of energy-efficientlow-emissive glass that is generally simple silicate glass with special metallic oxides coating. Heatable glass can be used in all kinds of standard glazing systems, made of wood, plastic, aluminum or steel.
Self-cleaning glass
A recent (2001 Pilkington Glass) innovation is so-called self-cleaning glass, aimed at building, automotive and other technical applications. A nanometre-scale coating of titanium dioxide on the outer surface of glass introduces two mechanisms which lead to the self-cleaning property. The first is a photo-catalytic effect, in which ultra-violet rays catalyse the breakdown of organic compounds on the window surface; the second is a hydrophilic effect in which water is attracted to the surface of the glass, forming a thin sheet which washes away the broken-down organic compounds.
Insulating glass, or double glazing, consists of a window or glazing element of two or more layers of glazing separated by a spacer along the edge and sealed to create a dead air space between the layers. This type of glazing has functions of thermal insulation and noise reduction. When the space is filled with an inert gas it is part of energy conservationsustainable architecture design for low energy buildings.
Evacuated glazing
A 1994 innovation for insulated glazing is evacuated glass, which as yet is produced commercially only in Japan and China.[19] The extreme thinness of evacuated glazing offers many new architectural possibilities, particularly in building conservation and historicist architecture, where evacuated glazing can replace traditional single glazing, which is much less energy-efficient.
An evacuated glazing unit is made by sealing the edges of two glass sheets, typically by using a solder glass, and evacuating the space inside with a vacuum pump. The evacuated space between the two sheets can be very shallow and yet be a good insulator, yielding insulative window glass with nominal thicknesses as low as 6mm overall. The reasons for this low thickness are deceptively complex, but the potential insulation is good essentially because there can be no convection or gaseous conduction in a vacuum.
Unfortunately, evacuated glazing does have some disadvantages; its manufacture is complicated and difficult. For example, a necessary stage in the manufacture of evacuated glazing is outgassing; that is, heating it to liberate any gases adsorbed on the inner surfaces, which could otherwise later escape and destroy the vacuum. This heating process currently means that evacuated glazing cannot be toughened or heat-strengthened. If an evacuated safety glass is required, the glass must be laminated. The high temperatures necessary for outgassing also tend to destroy the highly effective "soft" low-emissivity coatings that are often applied to one or both of the internal surfaces (i.e. the ones facing the air gap) of other forms of modern insulative glazing, in order to prevent loss of heat through infrared radiation. Slightly less effective "hard" coatings are still suitable for evacuated glazing, however.
Furthermore, because of the atmospheric pressure present on the outside of an evacuated glazing unit, its two glass sheets must somehow be held apart in order to prevent them flexing together and touching each other, which would defeat the object of evacuating the unit. The task of holding the panes apart is performed by a grid of spacers, which typically consist of small stainless steel discs that are placed around 20mm apart. The spacers are small enough that they are visible only at very close distances, typically up to 1 m. However, the fact that the spacers will conduct some heat often leads in cold weather to the formation of temporary, grid-shaped patterns on the surface of an evacuated window, consisting either of small circles of interior condensation centred around the spacers, where the glass is slightly colder than average, or, when there is dew outside, small circles on the exterior face of the glass, in which the dew is absent because the spacers make the glass near them slightly warmer.
The conduction of heat between the panes, caused by the spacers, tends to limit evacuated glazing's overall insulative effectiveness. Nevertheless, evacuated glazing is still as insulative as much thicker conventional double glazing and tends to be stronger, since the two constituent glass sheets are pressed together by the atmosphere, and hence react practically as one thick sheet to bending forces. Evacuated glazing also offers very good sound insulation in comparison with other popular types of window glazing.
Heat reduction glass
One type of heat reduction glass uses radiative cooling. This glass includes a 1.2 micron-thick their transparent radiative cooler (TRC) layer of silica, alumina, and titanium oxide upon glass coated with contact lenspolymer. The layer permits only visible light to cross, cutting buildings’ cooling costs by as much as one-third. The developers used machine learning and quantum computing to rapidly test models and identify the best. alternative.[20]
Seismic requirements
The most current building code enforced in most jurisdictions in the United States is the 2006 International Building Code (IBC, 2006). The 2006 IBC references for the 2005 edition of the standard Minimum Design Loads for buildings and other Structures prepared by the American Society of Civil Engineers (ASCE, 2005) for its seismic provisions. ASCE 7-05 contains specific requirements for nonstructural components including requirements for architectural glass.[21]
Reflected sunlight
If incorrectly designed, concave surfaces with extensive amounts of glass can act as solar concentrators depending on the angle of the sun, potentially injuring people and damaging property.[22]
Glass is an amorphous (non-crystalline) solid. Because it is often transparent and chemically inert, glass has found widespread practical, technological, and decorative use in window panes, tableware, and optics. Some common objects made of glass like "a glass" of water, "glasses", and "magnifying glass", are named after the material.
A window is an opening in a wall, door, roof, or vehicle that allows the exchange of light and may also allow the passage of sound and sometimes air. Modern windows are usually glazed or covered in some other transparent or translucent material, a sash set in a frame in the opening; the sash and frame are also referred to as a window. Many glazed windows may be opened, to allow ventilation, or closed to exclude inclement weather. Windows may have a latch or similar mechanism to lock the window shut or to hold it open by various amounts.
In passive solar building design, windows, walls, and floors are made to collect, store, reflect, and distribute solar energy, in the form of heat in the winter and reject solar heat in the summer. This is called passive solar design because, unlike active solar heating systems, it does not involve the use of mechanical and electrical devices.
BoPET is a polyester film made from stretched polyethylene terephthalate (PET) and is used for its high tensile strength, chemical stability, dimensional stability, transparency, reflectivity when metallized, gas and moisture barrier properties, and electrical insulation. The film is "biaxially oriented", which means that the polymer chains are oriented parallel to the plane of the film, and therefore oriented in two axes. A variety of companies manufacture boPET and other polyester films under different brand names. In the UK and US, the best-known trade names are Mylar, Melinex, Lumirror and Hostaphan. It was the first biaxially oriented polymer to be manufactured on a mass commercial scale.
Float glass is a sheet of glass made by floating molten glass on a bed of molten metal of a low melting point, typically tin, although lead was used for the process in the past. This method gives the sheet uniform thickness and a very flat surface. The float glass process is also known as the Pilkington process, named after the British glass manufacturer Pilkington, which pioneered the technique in the 1950s at their production site in St Helens, Merseyside.
A solar thermal collector collects heat by absorbing sunlight. The term "solar collector" commonly refers to a device for solar hot water heating, but may refer to large power generating installations such as solar parabolic troughs and solar towers or non-water heating devices such as solar cookers or solar air heaters.
A curtain wall is an exterior covering of a building in which the outer walls are non-structural, instead serving to protect the interior of the building from the elements. Because the curtain wall façade carries no structural load beyond its own dead load weight, it can be made of lightweight materials. The wall transfers lateral wind loads upon it to the main building structure through connections at floors or columns of the building.
Polyvinyl butyral is a resin mostly used for applications that require strong binding, optical clarity, adhesion to many surfaces, toughness and flexibility. It is prepared from polyvinyl alcohol by reaction with butyraldehyde. The major application is laminated safety glass for automobile windshields. Trade names for PVB-films include KB PVB, GUTMANN PVB, Saflex, GlasNovations, Butacite, WINLITE, S-Lec, Trosifol and EVERLAM. PVB is also available as 3D printer filament that is stronger and more heat resistant than polylactic acid (PLA).
Cathedral glass is the name given commercially to monochromatic sheet glass. It is thin by comparison with 'slab glass', may be coloured, and is textured on one side. The name draws from the fact that windows of stained glass were a feature of medieval European cathedrals from the 10th century onward.
Safety glass is glass with additional safety features that make it less likely to break, or less likely to pose a threat when broken. Common designs include toughened glass, laminated glass, and wire mesh glass. Toughened glass was invented in 1874 by Francois Barthelemy Alfred Royer de la Bastie. Wire mesh glass was invented in 1892 by Frank Shuman. Laminated glass was invented in 1903 by the French chemist Édouard Bénédictus (1878–1930).
Tempered or toughened glass is a type of safety glass processed by controlled thermal or chemical treatments to increase its strength compared with normal glass. Tempering puts the outer surfaces into compression and the interior into tension. Such stresses cause the glass, when broken, to shatter into small granular chunks instead of splintering into large jagged shards as ordinary annealed glass does. These smaller, granular chunks are less likely to cause deep penetration when forced into the surface of an object compared to larger, jagged shards because the reduction in both the mass and the maximum dimension of a glass fragment corresponds with a reduction in both the momentum and the penetration depth of the glass fragment.
Laminated glass is a type of safety glass consisting of two or more layers of glass with one or more thin polymer interlayers between them which prevent the glass from breaking into large sharp pieces. Breaking produces a characteristic "spider web" cracking pattern when the impact is not enough to completely pierce the glass.
Safety and security window films are polyester or PET films that are applied to glass and glazing in order to hold them together if the glass is shattered. The main difference between film and laminated glass is that these shatter safe films can be applied to the glass or glazing after manufacture or installation. I.e., these films are retrofit products. These films are used widely all over the world; they can be found on trains, buses, cars, and buildings.
The Fourcault process is a method of manufacturing plate glass. First developed in Belgium by Émile Fourcault (1862–1919) during the early 1900s, the process was used globally. Fourcault is an example of a "vertical draw" process, in that the glass is drawn against gravity in an upward direction. Gravity forces influence parts of the process.
Chemically strengthened glass is a type of glass that has increased strength as a result of a post-production chemical process. When broken, it still shatters in long pointed splinters similar to float glass. For this reason, it is not considered a safety glass and must be laminated if safety glass is required. However, chemically strengthened glass is typically six to eight times the strength of float glass. The most common trademark for this kind of glass is Gorilla glass.
Glass production involves two main methods – the float glass process that produces sheet glass, and glassblowing that produces bottles and other containers. It has been done in a variety of ways during the history of glass.
Glazing, which derives from the Middle English for 'glass', is a part of a wall or window, made of glass. Glazing also describes the work done by a professional "glazier". Glazing is also less commonly used to describe the insertion of ophthalmic lenses into an eyeglass frame.
Insulating glass (IG) consists of two or more glass window panes separated by a space to reduce heat transfer across a part of the building envelope. A window with insulating glass is commonly known as double glazing or a double-paned window, triple glazing or a triple-paned window, or quadruple glazing or a quadruple-paned window, depending upon how many panes of glass are used in its construction.
Thermal fracturing in glass occurs when a sufficient temperature differential is created within glass. As a warmed area expands or a cooled area contracts, stress forces develop, potentially leading to fracture. A temperature differential may be created in many ways, including solar heating, space heating devices, fire, or hot and cold liquids. Sloping glass surfaces are subject to greater solar radiation than vertical surfaces and so are more prone to solar thermal fracture. In framed window glass, the edges are relatively cooler than the exposed areas, so space heating devices in very close proximity may cause thermal fracture.
Copper foil is a thin sheet of copper metal that is widely used in various applications due to its excellent electrical conductivity, malleability, and corrosion resistance. It is an essential material in the electronics industry, especially for manufacturing printed circuit boards (PCBs) and other electronic components.