Anti-reflective coating

Last updated

Uncoated glasses lens (top) versus lens with antireflective coating. Note the tinted reflection from the coated lens. Anti-reflective coating comparison.jpg
Uncoated glasses lens (top) versus lens with antireflective coating. Note the tinted reflection from the coated lens.

An antireflective or anti-reflection (AR) coating is a type of optical coating applied to the surface of lenses and other optical elements to reduce reflection. In typical imaging systems, this improves the efficiency since less light is lost due to reflection. In complex systems such as telescopes and microscopes the reduction in reflections also improves the contrast of the image by elimination of stray light. This is especially important in planetary astronomy. In other applications, the primary benefit is the elimination of the reflection itself, such as a coating on eyeglass lenses that makes the eyes of the wearer more visible to others, or a coating to reduce the glint from a covert viewer's binoculars or telescopic sight.

Contents

Many coatings consist of transparent thin film structures with alternating layers of contrasting refractive index. Layer thicknesses are chosen to produce destructive interference in the beams reflected from the interfaces, and constructive interference in the corresponding transmitted beams. This makes the structure's performance change with wavelength and incident angle, so that color effects often appear at oblique angles. A wavelength range must be specified when designing or ordering such coatings, but good performance can often be achieved for a relatively wide range of frequencies: usually a choice of IR, visible, or UV is offered.

Applications

Anti-reflective coatings are often used in camera lenses, giving lens elements distinctive colours. Voigtlander lenses 75mm, 50mm, and 15mm.jpg
Anti-reflective coatings are often used in camera lenses, giving lens elements distinctive colours.

Anti-reflective coatings are used in a wide variety of applications where light passes through an optical surface, and low loss or low reflection is desired. Examples include anti-glare coatings on corrective lenses and camera lens elements, and antireflective coatings on solar cells. [1]

Corrective lenses

Opticians may recommend "anti-reflection lenses" because the decreased reflection enhances the cosmetic appearance of the lenses. Such lenses are often said to reduce glare, but the reduction is very slight. [2] Eliminating reflections allows slightly more light to pass through, producing a slight increase in contrast and visual acuity.

Antireflective ophthalmic lenses should not be confused with polarized lenses, which decrease (by absorption) the visible glare of sun reflected off surfaces such as sand, water, and roads. The term "antireflective" relates to the reflection from the surface of the lens itself, not the origin of the light that reaches the lens.

Many anti-reflection lenses include an additional coating that repels water and grease, making them easier to keep clean. Anti-reflection coatings are particularly suited to high-index lenses, as these reflect more light without the coating than a lower-index lens (a consequence of the Fresnel equations). It is also generally easier and cheaper to coat high index lenses.

Photolithography

Antireflective coatings (ARC) are often used in microelectronic photolithography to help reduce image distortions associated with reflections off the surface of the substrate. Different types of antireflective coatings are applied either before (Bottom ARC, or BARC) or after the photoresist, and help reduce standing waves, thin-film interference, and specular reflections. [3] [4]

Types

Index-matching

The simplest form of anti-reflective coating was discovered by Lord Rayleigh in 1886. The optical glass available at the time tended to develop a tarnish on its surface with age, due to chemical reactions with the environment. Rayleigh tested some old, slightly tarnished pieces of glass, and found to his surprise that they transmitted more light than new, clean pieces. The tarnish replaces the air-glass interface with two interfaces: an air-tarnish interface and a tarnish-glass interface. Because the tarnish has a refractive index between those of glass and air, each of these interfaces exhibits less reflection than the air-glass interface did. In fact, the total of the two reflections is less than that of the "naked" air-glass interface, as can be calculated from the Fresnel equations.

One approach is to use graded-index (GRIN) anti-reflective coatings, that is, ones with nearly continuously varying index of refraction. [5] With these, it is possible to curtail reflection for a broad band of frequencies and incidence angles.

Single-layer interference

The simplest interference anti-reflective coating consists of a single thin layer of transparent material with refractive index equal to the square root of the substrate's refractive index. In air, such a coating theoretically gives zero reflectance for light with wavelength (in the coating) equal to four times the coating's thickness. Reflectance is also decreased for wavelengths in a broad band around the center. A layer of thickness equal to a quarter of some design wavelength is called a "quarter-wave layer".

The most common type of optical glass is crown glass, which has an index of refraction of about 1.52. An optimal single-layer coating would have to be made of a material with an index of about 1.23. There are no solid materials with such a low refractive index. The closest materials with good physical properties for a coating are magnesium fluoride, MgF2 (with an index of 1.38), and fluoropolymers, which can have indices as low as 1.30, but are more difficult to apply. [6] MgF2 on a crown glass surface gives a reflectance of about 1%, compared to 4% for bare glass. MgF2 coatings perform much better on higher-index glasses, especially those with index of refraction close to 1.9. MgF2 coatings are commonly used because they are cheap and durable. When the coatings are designed for a wavelength in the middle of the visible band, they give reasonably good anti-reflection over the entire band.

Researchers have produced films of mesoporous silica nanoparticles with refractive indices as low as 1.12, which function as antireflection coatings. [7]

Multi-layer interference

By using alternating layers of a low-index material like silica and a higher-index material, it is possible to obtain reflectivities as low as 0.1% at a single wavelength. Coatings that give very low reflectivity over a broad band of frequencies can also be made, although these are complex and relatively expensive. Optical coatings can also be made with special characteristics, such as near-zero reflectance at multiple wavelengths, or optimal performance at angles of incidence other than 0°.

Absorbing

An additional category of anti-reflection coatings is the so-called "absorbing ARC". These coatings are useful in situations where high transmission through a surface is unimportant or undesirable, but low reflectivity is required. They can produce very low reflectance with few layers, and can often be produced more cheaply, or at greater scale, than standard non-absorbing AR coatings. (See, for example, US Patent 5,091,244.) Absorbing ARCs often make use of unusual optical properties exhibited in compound thin films produced by sputter deposition. For example, titanium nitride and niobium nitride are used in absorbing ARCs. These can be useful in applications requiring contrast enhancement or as a replacement for tinted glass (for example, in a CRT display).

Moth eye

Moths' eyes have an unusual property: their surfaces are covered with a natural nanostructured film, which eliminates reflections. This allows the moth to see well in the dark, without reflections to give its location away to predators. [8] The structure consists of a hexagonal pattern of bumps, each roughly 200 nm high and spaced on 300 nm centers. [9] This kind of antireflective coating works because the bumps are smaller than the wavelength of visible light, so the light sees the surface as having a continuous refractive index gradient between the air and the medium, which decreases reflection by effectively removing the air-lens interface. Practical anti-reflective films have been made by humans using this effect; [10] this is a form of biomimicry. Canon uses the moth-eye technique in their SubWavelength structure Coating, which significantly reduces lens flare. [11]

Such structures are also used in photonic devices, for example, moth-eye structures grown from tungsten oxide and iron oxide can be used as photoelectrodes for splitting water to produce hydrogen. [12] The structure consists of tungsten oxide spheroids of several 100 micrometer size coated with a few nanometers thin iron-oxide layer. [13] [14]

Circular polarizer

Reflections are blocked by a circular polarizer Circular polarizer as anti-reflective coating.png
Reflections are blocked by a circular polarizer

A circular polarizer laminated to a surface can be used to eliminate reflections. [15] [16] The polarizer transmits light with one chirality ("handedness") of circular polarization. Light reflected from the surface after the polarizer is transformed into the opposite "handedness". This light cannot pass back through the circular polarizer because its chirality has changed (e.g. from right circular polarized to left circularly polarized). A disadvantage of this method is that if the input light is unpolarized, the transmission through the assembly will be less than 50%.

Theory

An anti-reflection coated window, shown at a 45deg and a 0deg angle of incidence Antireflection coating split pic.jpg
An anti-reflection coated window, shown at a 45° and a 0° angle of incidence

There are two separate causes of optical effects due to coatings, often called thick-film and thin-film effects. Thick-film effects arise because of the difference in the index of refraction between the layers above and below the coating (or film); in the simplest case, these three layers are the air, the coating, and the glass. Thick-film coatings do not depend on how thick the coating is, so long as the coating is much thicker than a wavelength of light. Thin-film effects arise when the thickness of the coating is approximately the same as a quarter or a half a wavelength of light. In this case, the reflections of a steady source of light can be made to add destructively and hence reduce reflections by a separate mechanism. In addition to depending very much on the thickness of the film and the wavelength of light, thin-film coatings depend on the angle at which the light strikes the coated surface.

Reflection

Whenever a ray of light moves from one medium to another (for example, when light enters a sheet of glass after travelling through air), some portion of the light is reflected from the surface (known as the interface) between the two media. This can be observed when looking through a window, for instance, where a (weak) reflection from the front and back surfaces of the window glass can be seen. The strength of the reflection depends on the ratio of the refractive indices of the two media, as well as the angle of the surface to the beam of light. The exact value can be calculated using the Fresnel equations.

When the light meets the interface at normal incidence (perpendicularly to the surface), the intensity of light reflected is given by the reflection coefficient, or reflectance, R:

where n0 and nS are the refractive indices of the first and second media respectively. The value of R varies from 0 (no reflection) to 1 (all light reflected) and is usually quoted as a percentage. Complementary to R is the transmission coefficient, or transmittance, T. If absorption and scattering are neglected, then the value T is always 1 − R. Thus if a beam of light with intensity I is incident on the surface, a beam of intensity RI is reflected, and a beam with intensity TI is transmitted into the medium.

Reflection and transmission of an uncoated and coated surface Optical-coating-1.png
Reflection and transmission of an uncoated and coated surface

For the simplified scenario of visible light travelling from air (n0 ≈ 1.0) into common glass (nS ≈ 1.5), the value of R is 0.04, or 4%, on a single reflection. So at most 96% of the light (T = 1 − R = 0.96) actually enters the glass, and the rest is reflected from the surface. The amount of light reflected is known as the reflection loss.

In the more complicated scenario of multiple reflections, say with light travelling through a window, light is reflected both when going from air to glass and at the other side of the window when going from glass back to air. The size of the loss is the same in both cases. Light also may bounce from one surface to another multiple times, being partially reflected and partially transmitted each time it does so. In all, the combined reflection coefficient is given by 2R/(1 + R). For glass in air, this is about 7.7%.

Rayleigh's film

As observed by Lord Rayleigh, a thin film (such as tarnish) on the surface of glass can reduce the reflectivity. This effect can be explained by envisioning a thin layer of material with refractive index n1 between the air (index n0) and the glass (index nS). The light ray now reflects twice: once from the surface between air and the thin layer, and once from the layer-to-glass interface.

From the equation above and the known refractive indices, reflectivities for both interfaces can be calculated, denoted R01 and R1S respectively. The transmission at each interface is therefore T01 = 1 − R01 and T1S = 1 − R1S. The total transmittance into the glass is thus T1ST01. Calculating this value for various values of n1, it can be found that at one particular value of optimal refractive index of the layer, the transmittance of both interfaces is equal, and this corresponds to the maximal total transmittance into the glass.

This optimal value is given by the geometric mean of the two surrounding indices:

For the example of glass (nS ≈ 1.5) in air (n0 ≈ 1.0), this optimal refractive index is n1 ≈ 1.225. [17] [18]

The reflection loss of each interface is approximately 1.0% (with a combined loss of 2.0%), and an overall transmission T1ST01 of approximately 98%. Therefore, an intermediate coating between the air and glass can halve the reflection loss.

Interference coatings

The use of an intermediate layer to form an anti-reflection coating can be thought of as analogous to the technique of impedance matching of electrical signals. (A similar method is used in fibre optic research, where an index-matching oil is sometimes used to temporarily defeat total internal reflection so that light may be coupled into or out of a fiber.) Further reduced reflection could in theory be made by extending the process to several layers of material, gradually blending the refractive index of each layer between the index of the air and the index of the substrate.

Practical anti-reflection coatings, however, rely on an intermediate layer not only for its direct reduction of reflection coefficient, but also use the interference effect of a thin layer. Assume the layer's thickness is controlled precisely, such that it is exactly one quarter of the wavelength of light in the layer (λ/4 = λ0/(4n1), where λ0 is the vacuum wavelength). The layer is then called a quarter-wave coating. For this type of coating a normally incident beam I, when reflected from the second interface, will travel exactly half its own wavelength further than the beam reflected from the first surface, leading to destructive interference. This is also true for thicker coating layers (3λ/4, 5λ/4, etc.), however the anti-reflective performance is worse in this case due to the stronger dependence of the reflectance on wavelength and the angle of incidence.

If the intensities of the two beams R1 and R2 are exactly equal, they will destructively interfere and cancel each other, since they are exactly out of phase. Therefore, there is no reflection from the surface, and all the energy of the beam must be in the transmitted ray, T. In the calculation of the reflection from a stack of layers, the transfer-matrix method can be used.

Interference in a quarter-wave anti-reflection coating Optical-coating-2.png
Interference in a quarter-wave anti-reflection coating

Real coatings do not reach perfect performance, though they are capable of reducing a surface reflection coefficient to less than 0.1%. Also, the layer will have the ideal thickness for only one distinct wavelength of light. Other difficulties include finding suitable materials for use on ordinary glass, since few useful substances have the required refractive index (n ≈ 1.23) that will make both reflected rays exactly equal in intensity. Magnesium fluoride (MgF2) is often used, since this is hard-wearing and can be easily applied to substrates using physical vapor deposition, even though its index is higher than desirable (n = 1.38).

Further reduction is possible by using multiple coating layers, designed such that reflections from the surfaces undergo maximal destructive interference. One way to do this is to add a second quarter-wave thick higher-index layer between the low-index layer and the substrate. The reflection from all three interfaces produces destructive interference and anti-reflection. Other techniques use varying thicknesses of the coatings. By using two or more layers, each of a material chosen to give the best possible match of the desired refractive index and dispersion, broadband anti-reflection coatings covering the visible range (400–700 nm) with maximal reflectivities of less than 0.5% are commonly achievable.

The exact nature of the coating determines the appearance of the coated optic; common AR coatings on eyeglasses and photographic lenses often look somewhat bluish (since they reflect slightly more blue light than other visible wavelengths), though green and pink-tinged coatings are also used.

If the coated optic is used at non-normal incidence (that is, with light rays not perpendicular to the surface), the anti-reflection capabilities are degraded somewhat. This occurs because the phase accumulated in the layer relative to the phase of the light immediately reflected decreases as the angle increases from normal. This is counterintuitive, since the ray experiences a greater total phase shift in the layer than for normal incidence. This paradox is resolved by noting that the ray will exit the layer spatially offset from where it entered and will interfere with reflections from incoming rays that had to travel further (thus accumulating more phase of their own) to arrive at the interface. The net effect is that the relative phase is actually reduced, shifting the coating, such that the anti-reflection band of the coating tends to move to shorter wavelengths as the optic is tilted. Non-normal incidence angles also usually cause the reflection to be polarization-dependent.

Textured coatings

Reflection can be reduced by texturing the surface with 3D pyramids or 2D grooves (gratings). These kind of textured coating can be created using for example the Langmuir-Blodgett method. [19]

If wavelength is greater than the texture size, the texture behaves like a gradient-index film with reduced reflection. To calculate reflection in this case, effective medium approximations can be used. To minimize reflection, various profiles of pyramids have been proposed, such as cubic, quintic or integral exponential profiles.

If wavelength is smaller than the textured size, the reflection reduction can be explained with the help of the geometric optics approximation: rays should be reflected many times before they are sent back toward the source. In this case the reflection can be calculated using ray tracing.

Using texture reduces reflection for wavelengths comparable with the feature size as well. In this case no approximation is valid, and reflection can be calculated by solving Maxwell equations numerically.

Antireflective properties of textured surfaces are well discussed in literature for a wide range of size-to-wavelength ratios (including long- and short-wave limits) to find the optimal texture size. [20]

History

As mentioned above, natural index-matching "coatings" were discovered by Lord Rayleigh in 1886. Harold Dennis Taylor of Cooke company developed a chemical method for producing such coatings in 1904. [21] [22]

Interference-based coatings were invented and developed in 1935 by Alexander Smakula, who was working for the Carl Zeiss optics company. [23] [24] [25] Anti-reflection coatings were a German military secret until the early stages of World War II. [26] Katharine Burr Blodgett and Irving Langmuir developed organic anti-reflection coatings known as Langmuir–Blodgett films in the late 1930s.

See also

Related Research Articles

Mirror Object that reflects light

A mirror is an object that reflects an image. Light that bounces off a mirror will show an image of whatever is in front of it, when focused through the lens of the eye or a camera. Mirrors reverse the direction of the image in an equal yet opposite angle from which the light shines upon it. This allows the viewer to see themselves or objects behind them, or even objects that are at an angle from them but out of their field of view, such as around a corner. Natural mirrors have existed since prehistoric times, such as the surface of water, but people have been manufacturing mirrors out of a variety of materials for thousands of years, like stone, metals, and glass. In modern mirrors, metals like silver or aluminum are often used due to their high reflectivity, applied as a thin coating on glass because of its naturally smooth and very hard surface.

Optics Branch of physics that studies light

Optics is the branch of physics that studies the behaviour and properties of light, including its interactions with matter and the construction of instruments that use or detect it. Optics usually describes the behaviour of visible, ultraviolet, and infrared light. Because light is an electromagnetic wave, other forms of electromagnetic radiation such as X-rays, microwaves, and radio waves exhibit similar properties.

Refractive index Ratio of the speed of light in vacuum to that in the medium

In optics, the refractive index of a material is a dimensionless number that describes how fast light travels through the material. It is defined as

Brewsters angle angle of incidence for which all reflected light will be polarized

Brewster's angle is an angle of incidence at which light with a particular polarization is perfectly transmitted through a transparent dielectric surface, with no reflection. When unpolarized light is incident at this angle, the light that is reflected from the surface is therefore perfectly polarized. This special angle of incidence is named after the Scottish physicist Sir David Brewster (1781–1868).

Prism Transparent optical element with flat, polished surfaces that refract light

An optical prism is a transparent optical element with flat, polished surfaces that refract light. At least one surface must be angled—elements with two parallel surfaces are not prisms. The traditional geometrical shape of an optical prism is that of a triangular prism with a triangular base and rectangular sides, and in colloquial use "prism" usually refers to this type. Some types of optical prism are not in fact in the shape of geometric prisms. Prisms can be made from any material that is transparent to the wavelengths for which they are designed. Typical materials include glass, plastic, and fluorite.

Reflection (physics) Change in direction of a wavefront at an interface between two different media so that the wavefront returns into the medium from which it originated

Reflection is the change in direction of a wavefront at an interface between two different media so that the wavefront returns into the medium from which it originated. Common examples include the reflection of light, sound and water waves. The law of reflection says that for specular reflection the angle at which the wave is incident on the surface equals the angle at which it is reflected. Mirrors exhibit specular reflection.

Optical coating

An optical coating is one or more thin layers of material deposited on an optical component such as a lens or mirror, which alters the way in which the optic reflects and transmits light. One type of optical coating is an anti-reflective coating, which reduces unwanted reflections from surfaces, and is commonly used on spectacle and camera lenses. Another type is the high-reflector coating, which can be used to produce mirrors that reflect greater than 99.99% of the light that falls on them. More complex optical coatings exhibit high reflection over some range of wavelengths, and anti-reflection over another range, allowing the production of dichroic thin-film filters.

Optical filter

An optical filter is a device that selectively transmits light of different wavelengths, usually implemented as a glass plane or plastic device in the optical path, which are either dyed in the bulk or have interference coatings. The optical properties of filters are completely described by their frequency response, which specifies how the magnitude and phase of each frequency component of an incoming signal is modified by the filter.

Newtons rings

Newton's rings is a phenomenon in which an interference pattern is created by the reflection of light between two surfaces; a spherical surface and an adjacent touching flat surface. It is named after Isaac Newton, who investigated the effect in 1666. When viewed with monochromatic light, Newton's rings appear as a series of concentric, alternating bright and dark rings centered at the point of contact between the two surfaces. When viewed with white light, it forms a concentric ring pattern of rainbow colors, because the different wavelengths of light interfere at different thicknesses of the air layer between the surfaces.

Ellipsometry

Ellipsometry is an optical technique for investigating the dielectric properties of thin films. Ellipsometry measures the change of polarization upon reflection or transmission and compares it to a model.

Polarizer Optical filter device

A polarizer or polariser is an optical filter that lets light waves of a specific polarization pass through while blocking light waves of other polarizations. It can filter a beam of light of undefined or mixed polarization into a beam of well-defined polarization, that is polarized light. The common types of polarizers are linear polarizers and circular polarizers. Polarizers are used in many optical techniques and instruments, and polarizing filters find applications in photography and LCD technology. Polarizers can also be made for other types of electromagnetic waves besides visible light, such as radio waves, microwaves, and X-rays.

Dielectric mirror

A dielectric mirror, also known as a Bragg mirror, is a type of mirror composed of multiple thin layers of dielectric material, typically deposited on a substrate of glass or some other optical material. By careful choice of the type and thickness of the dielectric layers, one can design an optical coating with specified reflectivity at different wavelengths of light. Dielectric mirrors are also used to produce ultra-high reflectivity mirrors: values of 99.999% or better over a narrow range of wavelengths can be produced using special techniques. Alternatively, they can be made to reflect a broad spectrum of light, such as the entire visible range or the spectrum of the Ti-sapphire laser. Mirrors of this type are very common in optics experiments, due to improved techniques that allow inexpensive manufacture of high-quality mirrors. Examples of their applications include laser cavity end mirrors, hot and cold mirrors, thin-film beamsplitters, high damage threshold mirrors, and the coatings on modern mirrorshades.

A prism coupler is a prism designed to couple a substantial fraction of the power contained in a beam of light into a thin film to be used as a waveguide without the need for precision polishing of the edge of the film, without the need for sub-micrometer alignment precision of the beam and the edge of the film, and without the need for matching the numerical aperture of the beam to the film. Using a prism coupler, a beam coupled into a thin film can have a diameter hundreds of times the thickness of the film. Invention of the coupler contributed to the initiation of a field of study known as integrated optics.

Chirped mirror

A chirped mirror is a dielectric mirror with chirped spaces—spaces of varying depth designed to reflect varying wavelengths of lights—between the dielectric layers (stack).

X-ray optics is the branch of optics that manipulates X-rays instead of visible light. It deals with focusing and other ways of manipulating the X-ray beams for research techniques such as X-ray crystallography, X-ray fluorescence, small-angle X-ray scattering, X-ray microscopy, X-ray phase-contrast imaging, X-ray astronomy etc.

Interference reflection microscopy

Interference reflection microscopy (IRM) is an optical microscopy technique that utilizes polarized light to form an image of an object on a glass surface. The intensity of the signal is a measure of proximity of the object to the glass surface. This technique can be used to study events at the cell membrane without the use of a (fluorescent) label in contrast to TIRF microscopy.

Thin-film interference

Thin-film interference is a natural phenomenon in which light waves reflected by the upper and lower boundaries of a thin film interfere with one another, either enhancing or reducing the reflected light. When the thickness of the film is an odd multiple of one quarter-wavelength of the light on it, the reflected waves from both surfaces interfere to cancel each other. Since the wave cannot be reflected, it is completely transmitted instead. When the thickness is a multiple of a half-wavelength of the light, the two reflected waves reinforce each other, increasing the reflection and reducing the transmission. Thus when white light, which consists of a range of wavelengths, is incident on the film, certain wavelengths (colors) are intensified while others are attenuated. Thin-film interference explains the multiple colors seen in light reflected from soap bubbles and oil films on water. It is also the mechanism behind the action of antireflection coatings used on glasses and camera lenses.

Picture framing glass usually refers to flat glass or acrylic ("plexi") used for framing artwork and for presenting art objects in a display box.

Liquid optically clear adhesive (LOCA) is liquid-based bonding technology used in touch panels and display devices to bind the cover lens, plastic, or other optical materials to the main sensor unit or each other. These adhesives improve optical characteristics and durability. LOCA glue is often hardened using ultraviolet light.

A rugate filter, also known as a gradient-index filter, is an optical filter based on a dielectric mirror that selectively reflects specific wavelength ranges of light. This effect is achieved by a periodic, continuous change of the refractive index of the dielectric coating. The word "rugate" is derived from corrugated structures found in nature, which also selectively reflect certain wavelength ranges of light, for example the wings of the Morpho butterfly.

References

  1. Hemant Kumar Raut; V. Anand Ganesh; A. Sreekumaran Nairb; Seeram Ramakrishna (2011). "Anti-reflective coatings: A critical, in-depth review". Energy & Environmental Science. 4 (10): 3779–3804. doi:10.1039/c1ee01297e.
  2. Duffner, Lee R (27 February 2015). "Anti-reflective Coating - American Academy of Ophthalmology". Anti-reflective Coating - American Academy of Ophthalmology. American Academy of Ophthalmology. Retrieved 22 January 2016.
  3. "Understanding bottom antireflective coatings" (PDF). Archived from the original (PDF) on 25 April 2012. Retrieved 25 June 2012.
  4. Yet, Siew Ing (2004). Investigation of UFO defect on DUV CAR and BARC process. 5375. SPIE. pp. 940–948. Bibcode:2004SPIE.5375..940Y. doi:10.1117/12.535034.
  5. Zhang, Jun-Chao; Xiong, Li-Min; Fang, Ming; He, Hong-Bo (2013). "Wide-angle and broadband graded-refractive-index antireflection coatings" (PDF). Chinese Physics B. 22 (4): 044201. Bibcode:2013ChPhB..22d4201Z. doi:10.1088/1674-1056/22/4/044201 . Retrieved 13 May 2016.
  6. "Opstar AR fluoride coatings and application methods". Archived from the original on 29 January 2011.
  7. Moghal, Jonathan; Kobler, Johannes; Sauer, Jürgen; Best, James; Gardener, Martin; Watt, Andrew A.R.; Wakefield, Gareth (2012). "High-performance, single-layer antireflective optical coatings comprising mesoporous silica nanoparticles". ACS Applied Materials & Interfaces. 4 (2): 854–859. doi:10.1021/am201494m. PMID   22188238.
  8. "Nanostructured Surfaces" (PDF). Fraunhofer Magazine (2): 10. 2005. Archived from the original (PDF) on 10 June 2011. Retrieved 17 June 2009.
  9. Han, Z.W.; Wang, Z.; Feng, X.M.; et al. (14 October 2016). "Antireflective surface inspired from biology: A review". Biosurface and Biotribology. Elsevier. 2 (4): 137–150. doi:10.1016/j.bsbt.2016.11.002 . Retrieved 16 November 2020.
  10. "Novel film inspired by moths" (Press release). Pro-talk. 3 December 2003. Archived from the original on 13 December 2014. Retrieved 17 June 2009.
  11. "Canon Subwavelength Coating (SWC)". www.eos-magazine.com. July–September 2009. Retrieved 24 July 2019.
  12. Boudoire, Florent; Toth, Rita; Heier, Jakob; Braun, Artur; Constable, Edwin C. (2014). "Photonic light trapping in self-organized all-oxide microspheroids impacts photoelectrochemical water splitting". Energy Environ Sci. 7 (8): 2680–2688. doi:10.1039/C4EE00380B.
  13. "Photoelectrochemical Water Splitting Can Be Achieved with Self-Organized, All-Oxide Electrodes". Materials Research Society. 2014. Retrieved 24 July 2014.
  14. "Photonic light trapping in self-organized all-oxide microspheroids impacts photoelectrochemical water splitting". Authors. 2014. Retrieved 1 May 2014.
  15. "HNCP Circular Polarizing Filter". www.visionteksystems.co.uk.
  16. Information Display. Society for Information Display. 2006.
  17. Krepelka, J. (1992). "Maximally flat antireflection coatings" (PDF). Jemná Mechanika a Optika (3–5): 53. Archived from the original (PDF) on 12 January 2011. Retrieved 17 June 2009.
  18. Moreno, I.; Araiza, J.; Avendano-Alejo, M. (2005). "Thin-film spatial filters" (PDF). Optics Letters . 30 (8): 914–916. Bibcode:2005OptL...30..914M. doi:10.1364/OL.30.000914. PMID   15865397. Archived from the original (PDF) on 19 February 2009. Retrieved 26 June 2007.
  19. Hsu, Ching-Mei; Connor, Stephen T.; Tang, Mary X.; Cui, Yi (2008). "Wafer-scale silicon nanopillars and nanocones by Langmuir–Blodgett assembly and etching". Applied Physics Letters. 93 (13): 133109. Bibcode:2008ApPhL..93m3109H. doi:10.1063/1.2988893. ISSN   0003-6951. S2CID   123191151.
  20. A. Deinega; et al. (2011). "Minimizing light reflection from dielectric textured surfaces". JOSA A. 28 (5): 770–7. Bibcode:2011JOSAA..28..770D. doi:10.1364/josaa.28.000770. PMID   21532687.
  21. MacLeod, H A (2001). Thin Film Optical Filters (3rd ed.). CRC. p. 4. ISBN   9780750306881.
  22. British Patent 29561, 31 December 1904
  23. "History of Camera Lenses from Carl Zeiss - 1935 - Alexander Smakula develops anti-reflection coating". Zeiss.com. Retrieved 15 June 2013.
  24. "Lens coating". Zeiss.com. Archived from the original on 1 January 2013. Retrieved 15 June 2013.
  25. Patent DE 685767,"Verfahren zur Erhoehung der Lichtdurchlaessigkeit optischer Teile durch Erniedrigungdes Brechungsexponenten an den Grenzflaechen dieser optischen Teile",published 1935-11-01, assigned to Zeiss Carl FA
  26. "Carl Zeiss – A History of a Most Respected Name in Optics". Southwest Museum of Engineering, Communications and Computation. 2007.

Sources