Uranium glassware glowing under ultraviolet lightUranium glass used as lead-in seals in a vacuum capacitor
Uranium glass is glass which has had uranium, usually in oxide diuranate form, added to a glass mix before melting for colouration. The proportion usually varies from trace levels to about 2% uranium by weight, although some 20th-century pieces were made with up to 25% uranium.[1][2]
First identified in 1789 by German chemist Martin Heinrich Klaproth, uranium was soon being added to decorative glass for its fluorescent effect. James Powell’s Whitefriars Glass company in London, England, was one of the first to market the glowing glass, but other manufacturers soon realised its sales potential and uranium glass was produced across Europe[3] and later In Ohio.[4]
Uranium glass was once made into tableware and household items, but fell out of widespread use when the availability of uranium to most industries was sharply curtailed during the Cold War in the 1940s to 1990s. Most such objects are now considered antiques or retro-era collectibles, although there has been a minor revival in art glassware. Otherwise, modern uranium glass is now mainly limited to small objects like beads or marbles as scientific or decorative novelties.
Appearance
The normal colour of uranium glass ranges from yellow to green depending on the oxidation state and concentration of the metal ions, although this may be altered by the addition of other elements as glass colorants. Uranium glass also fluoresces bright green under ultraviolet light.[5]
Modern uranium glass beads (black background)
Modern uranium glass beads (UV light)
Vaseline glass
The most common color of uranium glass is pale yellowish-green, which in the 1930s led to the nickname "Vaseline glass", based on a perceived resemblance to the appearance of Vaseline-brand petroleum jelly as formulated at that time. Specialized collectors still define Vaseline glass as transparent or semi-transparent uranium glass in this specific color.[6]
Vaseline glass is sometimes used as a synonym for any uranium glass, especially in the United States, but this usage is frowned upon,[7] since Vaseline-brand petroleum jelly was only yellow, not other colors. The term is sometimes applied to other types of glass based on certain aspects of their superficial appearance in normal light, regardless of actual uranium content which requires a blacklight test to verify the characteristic green fluorescence.[8]
In the United Kingdom and Australia, the term Vaseline glass can be used to refer to any type of translucent glass.
Other colors
"Jadite" redirects here. Not to be confused with Jadeite.
Several other common subtypes of uranium glass have their own nicknames:
Custard glass (opaque or semiopaque pale yellow)
Jadite glass (opaque or semi-opaque pale green; initially, the name was trademarked as "Jadite", although this is sometimes over-corrected in modern usage to "jadeite")
Burmese glass (opaque glass that shades from pink to yellow)
Like "Vaseline", the terms "custard" and "jad(e)ite" are often applied on the basis of superficial appearance rather than uranium content. Conversely, "Depression glass" is a general description for any piece of glassware manufactured during the Great Depression regardless of appearance or formula.
Fabrication
Uranium glass is used as one of several intermediate glasses in what is known to scientific glass blowers as a 'graded seal'. This is typically used in glass-to-metal seals such as tungsten and molybdenum or nickel based alloys such as Kovar, as an intermediary glass between the metal sealing glass and lower expansion borosilicate glass.
In 1789, Martin Klaproth discovered uranium. He later experimented with the use of the element as a glass colourant.
Uranium glass became popular in the mid-19th century, with its period of greatest popularity being from the 1880s to the 1920s.
The first major producer of items made of uranium glass is commonly recognized as Austrian Franz Xaver Riedel, who named the yellow (German: Gelb) and yellow-green (German: Gelb-Grün) varieties of the glass "annagelb" and "annagrün", respectively, in honor of his daughter Anna Maria. Riedel was a prolific blower of uranium glass in Unter-Polaun (today Dolni Polubny), Bohemia from 1830 to 1848.[citation needed]
By the 1840s, many other European glassworks began to produce uranium glass items and developed new varieties of uranium glass. The Baccarat glassworks in France created an opaque green uranium glass which they named chrysoprase from its similarity to that green form of chalcedony.
At the end of the 19th century, glassmakers discovered that uranium glass with certain mineral additions could be tempered at high temperatures, inducing varying degrees of micro-crystallization. This produced a range of increasingly opaque glasses from the traditional transparent yellow or yellow-green to an opaque white. During the Depression years, more iron oxide was added to the mixture to match popular preferences for a greener glass.[12] This material, technically a glass-ceramic, acquired the name "vaseline glass" because of its supposedly similar appearance to petroleum jelly. Today[when?], a few manufacturers continue the vaseline glass tradition: Fenton Glass, Mosser Glass, Gibson Glass and Jack Loranger.[13]
U.S. production of uranium glasses ceased in the middle years of World War II because of the government's confiscation of uranium supplies for the Manhattan Project from 1942 to 1958. After the restrictions in the United States were eased several firms resumed production of uranium glass, including Fenton, and Mosser; though uranium was still regulated as a strategic material.[14] Following the Cold War, restrictions on uranium glass were completely lifted. During this time many older pieces entered the free market and new pieces continued to be produced in small quantities into the 2000s.[15]
Uranium glass can register above background radiation on a sufficiently sensitive Geiger counter, although most pieces of uranium glass are considered to be harmless and only negligibly radioactive.[5]
See also
Wikimedia Commons has media related to Uranium glass.
Glass is a non-crystalline solid that is often transparent, brittle and chemically inert. It has widespread practical, technological, and decorative use in, for example, window panes, tableware, and optics.
Fiesta is a line of ceramic glazed dinnerware manufactured and marketed by the Fiesta Tableware Company of Newell, West Virginia since its introduction in 1936, with a hiatus from 1973 to 1985. Fiesta is noted for its Art Deco styling and its range of often bold, solid colors.
Fire-King is an Anchor Hocking brand of glassware similar to Pyrex. It was formerly made of low expansion borosilicate glass and ideal for oven use. Currently it is made of tempered soda-lime-silicate glass in the US and borosilicate in Japan
An opacifier is a substance added to a material in order to make the ensuing system opaque. An example of a chemical opacifier is titanium dioxide (TiO2), which is used as an opacifier in paints, in paper, and in plastics. It has very high refraction index (rutile modification 2.7 and anatase modification 2.55) and optimum refraction is obtained with crystals about 225 nanometers. Impurities in the crystal alter the optical properties. It is also used to opacify ceramic glazes and milk glass; bone ash is also used.
Goldstone is a type of glittering glass made in a low-oxygen reducing atmosphere. The finished product can take a smooth polish and be carved into beads, figurines, or other artifacts suitable for semiprecious stone, and in fact goldstone is often mistaken for or misrepresented as a natural material.
Burmese glass is a type of opaque colored art glass, shading from yellow, blue or green to pink. It is found in either the rare original "shiny" finish or the more common "satin" finish. It is used for table glass and small, ornamental vases and dressing table articles.
Depression glass is glassware made in the period 1929–1939, often clear or colored translucent machine-made glassware that was distributed free, or at low cost, in the United States and Canada around the time of the Great Depression. Depression glass is so called because collectors generally associate mass-produced glassware in pink, yellow, crystal, green, and blue with the Great Depression in America.
Luminous paint is paint that emits visible light through fluorescence, phosphorescence, or radioluminescence.
The La Hague site is a nuclear fuel reprocessing plant at La Hague on the Cotentin Peninsula in northern France, with the Manche storage centre bordering on it. Operated by Orano, formerly AREVA, and prior to that COGEMA, La Hague has nearly half of the world's light water reactor spent nuclear fuel reprocessing capacity. It has been in operation since 1976, and has a capacity of about 1,700 tonnes per year. It extracts plutonium which is then recycled into MOX fuel at the Marcoule site.
Uranium dioxide or uranium(IV) oxide , also known as urania or uranous oxide, is an oxide of uranium, and is a black, radioactive, crystalline powder that naturally occurs in the mineral uraninite. It is used in nuclear fuel rods in nuclear reactors. A mixture of uranium and plutonium dioxides is used as MOX fuel. Prior to 1960, it was used as yellow and black color in ceramic glazes and glass.
Sodium diuranate, also known as the yellow oxide of uranium, is an inorganic chemical compound with the chemical formula Na2U2O7. It is a sodium salt of a diuranate anion. It forms a hexahydrate Na2U2O7·6H2O. Sodium diuranate is commonly referred to by the initials SDU. Along with ammonium diuranate it was a component in early yellowcakes. The ratio of the two compounds is determined by process conditions; however, yellowcake is now largely a mix of uranium oxides.
Wood's glass is an optical filter glass invented in 1903 by American physicist Robert Williams Wood (1868–1955), which allows ultraviolet and infrared light to pass through, while blocking most visible light.
Sea glass are naturally weathered pieces of glass, which often have the appearance of tumbled stones. Sea glass is physically and chemically weathered glass found on beaches along bodies of salt water. These weathering processes produce natural frosted glass. Sea glass is used for decoration, most commonly in jewellery. "Beach glass" comes from fresh water and is often less frosted in appearance than sea glass. Sea glass takes 20–40 years, and sometimes as much as 100–200 years, to acquire its characteristic texture and shape. It is also colloquially referred to as drift glass from the longshore drift process that forms the smooth edges. In practice, the two terms are used interchangeably.
Opaline glass is a style of antique glassware that was produced in Europe, particularly 19th-century France. It was made by adding particular phosphates or oxides during the mixing process of the glass' processing, giving the material a quality of opalescence.
The A.H. Heisey Company was formed in Newark, Ohio, in 1895 by A.H. Heisey. The factory provided fine quality glass tableware and decorative glass figurines. Both pressed and blown glassware were made in a wide variety of patterns and colors. The company also made glass automobile headlights and Holophane Glassware lighting fixtures. The company was operated by Heisey and his sons until 1957, when the factory closed.
Uranium tiles have been used in the ceramics industry for many centuries, as uranium oxide makes an excellent ceramic glaze, and is reasonably abundant. In addition to its medical usage, radium was used in the 1920s and 1930s for making watch, clock and aircraft dials. Because it takes approximately three metric tons of uranium to extract 1 gram of radium, prodigious quantities of uranium were mined to sustain this new industry. The uranium ore itself was considered a waste product and taking advantage of this newly abundant resource, the tile and pottery industry had a relatively inexpensive and abundant source of glazing material. Vibrant colors of orange, yellow, red, green, blue, black, mauve, etc. were produced, and some 25% of all houses and apartments constructed during that period used bathroom or kitchen tiles that had been glazed with uranium. These can now be detected by a Geiger counter that detects the beta radiation emitted by uranium's decay chain.
Glass coloring and color marking may be obtained in several ways.
by the addition of coloring ions,
by precipitation of nanometer-sized colloids, Ancient Roman enamelled glass, 1st century, Begram Hoard
by colored inclusions
by light scattering
by dichroic coatings, or
by colored coatings
Claude Félix Abel Niépce de Saint-Victor was a French photographic inventor. Claude was an army lieutenant and the cousin of Nicéphore Niépce. He first experimented in 1847 with negatives made with albumen on glass, a method subsequently used by Frederick Langenheim for his and his brother’s lantern slides. At his laboratory near Paris, Saint-Victor worked on the fixation of natural photographic colour as well as the perfection of his cousin's heliographing process for photomechanical printing. His method of photomechanical printing, called heliogravure, was published in 1856 in Traité pratique de gravure héliographique. In the 1850s, he also published frequently in La Lumière.
Adolf Patera, was a Bohemian chemist, mineralogist and metallurgist, best known for the important role he played in the utilisation of uranium in colour production in glass, and associated with silver extraction from the mines at Joachimsthal, then part of the Austro-Hungarian Empire, now known as Jáchymov. Pateraite, supposedly a cobalt molybdate, is named after him.
Jadeite, “Jadite” or “Jade-ite” is a type of jade green opaque milk glass, originally popular in the United States in the early to mid-20th century. A blue milk glass called “Delphite” and "Azur-ite" was also produced for several years.
References
↑ Big Book of Vaseline Glass, by Barrie Skelcher, Pub. Schiffer
↑ Glickman, Jay L. and Fedosky, Terry, Yellow-Green Vaseline A Guide to the Magic Glass, Revised Edition, c. 1998, The Glass Press, Inc., dba Antique Publications. ISBN1570800456 (PB) or 1570800464 (HB)
↑ Boot, Roeland (February 2017). "Uranium Glass: A Glowing Alternative to Conventional Sources of Radioactivity". The Physics Teacher. 55 (2): 76–78. Bibcode:2017PhTea..55...76B. doi:10.1119/1.4974115.
This page is based on this Wikipedia article Text is available under the CC BY-SA 4.0 license; additional terms may apply. Images, videos and audio are available under their respective licenses.