Organic solar cell

Last updated
Fig. 1. Schematic of plastic solar cells. PET - polyethylene terephthalate, ITO - indium tin oxide, PEDOT:PSS - poly(3,4-ethylenedioxythiophene), active layer (usually a polymer:fullerene blend), Al - aluminium. Solarcells4.gif
Fig. 1. Schematic of plastic solar cells. PET – polyethylene terephthalate, ITO – indium tin oxide, PEDOT:PSS – poly(3,4-ethylenedioxythiophene), active layer (usually a polymer:fullerene blend), Al – aluminium.

An organic solar cell (OSC [1] ) or plastic solar cell is a type of photovoltaic that uses organic electronics, a branch of electronics that deals with conductive organic polymers or small organic molecules, [2] for light absorption and charge transport to produce electricity from sunlight by the photovoltaic effect. Most organic photovoltaic cells are polymer solar cells.

Contents

Fig. 2. Organic Photovoltaic manufactured by the company Solarmer. 4inchcell.jpg
Fig. 2. Organic Photovoltaic manufactured by the company Solarmer.

The molecules used in organic solar cells are solution-processable at high throughput and are cheap, resulting in low production costs to fabricate a large volume. [3] Combined with the flexibility of organic molecules, organic solar cells are potentially cost-effective for photovoltaic applications. [4] Molecular engineering (e.g., changing the length and functional group of polymers) can change the band gap, allowing for electronic tunability. The optical absorption coefficient of organic molecules is high, so a large amount of light can be absorbed with a small amount of materials, usually on the order of hundreds of nanometers. The main disadvantages associated with organic photovoltaic cells are low efficiency, low stability and low strength compared to inorganic photovoltaic cells such as silicon solar cells.

Compared to silicon-based devices, polymer solar cells are lightweight (which is important for small autonomous sensors), potentially disposable and inexpensive to fabricate (sometimes using printed electronics), flexible, customizable on the molecular level and potentially have less adverse environmental impact. Polymer solar cells also have the potential to exhibit transparency, suggesting applications in windows, walls, flexible electronics, etc. An example device is shown in Fig. 1. The disadvantages of polymer solar cells are also serious: they offer about 1/3 of the efficiency of hard materials, and experience substantial photochemical degradation. [5]

Polymer solar cells' stability problems, [6] combined with their promise of low costs [7] and potential for increasing efficiencies [8] have made them a popular field in solar cell research. In 2015, polymer solar cells were achieving efficiencies of more than 10% via a tandem structure. [9] In 2023, a new record-breaking efficiency of 19.3% was achieved by Hong Kong Polytechnic University. [10]

Physics

Fig. 3: Examples of organic photovoltaic materials Examples of organic photovoltaic materials.svg
Fig. 3: Examples of organic photovoltaic materials

A photovoltaic cell is a specialized semiconductor diode that converts light into direct current (DC) electricity. Depending on the band gap of the light-absorbing material, photovoltaic cells can also convert low-energy, infrared (IR) or high-energy, ultraviolet (UV) photons into DC electricity. A common characteristic of both the small molecules and polymers (Fig. 3) used as the light-absorbing material in photovoltaics is that they all have large conjugated systems. A conjugated system is formed where carbon atoms covalently bond with alternating single and double bonds. These hydrocarbons' electrons pz orbitals delocalize and form a delocalized bonding π orbital with a π* antibonding orbital. The delocalized π orbital is the highest occupied molecular orbital (HOMO), and the π* orbital is the lowest unoccupied molecular orbital (LUMO). In organic semiconductor physics, the HOMO takes the role of the valence band while the LUMO serves as the conduction band. The energy separation between the HOMO and LUMO energy levels is considered the band gap of organic electronic materials and is typically in the range of 1–4 eV. [11]

All light with energy greater than the band gap of the material can be absorbed, though there is a trade-off to reducing the band gap as photons absorbed with energies higher than the band gap will thermally give off their excess energy, resulting in lower voltages and power conversion efficiencies. When these materials absorb a photon, an excited state is created and confined to a molecule or a region of a polymer chain. The excited state can be regarded as an exciton, or an electron-hole pair bound together by electrostatic interactions. In photovoltaic cells, excitons are broken up into free electron-hole pairs by effective fields. The effective fields are set up by creating a heterojunction between two dissimilar materials. In organic photovoltaics, effective fields break up excitons by causing the electron to fall from the conduction band of the absorber to the conduction band of the acceptor molecule. It is necessary that the acceptor material has a conduction band edge that is lower than that of the absorber material. [12] [13] [14] [15]

Solarcells2m.gif
Solarcells2m.gif
Solarcells2m.gif
Solarcells1.gif
Solarcells2m.gif
Solarcells2m.gif
Solarcells2m.gif
Solarcells1.gif
Fig. 4: Polymer chain with diffusing polaron surrounded by fullerene molecules

Polymer solar cells usually consist of an electron- or hole-blocking layer on top of an indium tin oxide (ITO) conductive glass followed by electron donor and an electron acceptor (in the case of bulk heterojunction solar cells), a hole or electron blocking layer, and metal electrode on top. The nature and order of the blocking layers – as well as the nature of the metal electrode – depends on whether the cell follows a regular or an inverted device architecture. In an inverted cell, the electric charges exit the device in the opposite direction as in a normal device because the positive and negative electrodes are reversed. Inverted cells can utilize cathodes out of a more suitable material; inverted OPVs enjoy longer lifetimes than regularly structured OPVs, and they usually show higher efficiencies compared with the conventional counterparts. [16]

In bulk heterojunction polymer solar cells, light generates excitons. Subsequent charge separation in the interface between an electron donor and acceptor blend within the device's active layer. These charges then transport to the device's electrodes where the charges flow outside the cell, perform work and then re-enter the device on the opposite side. The cell's efficiency is limited by several factors, especially non-geminate recombination. Hole mobility leads to faster conduction across the active layer. [17] [18]

Organic photovoltaics are made of electron donor and electron acceptor materials rather than semiconductor p-n junctions. The molecules forming the electron donor region of organic PV cells, where exciton electron-hole pairs are generated, are generally conjugated polymers possessing delocalized π electrons that result from carbon p orbital hybridization. These π electrons can be excited by light in or near the visible part of the spectrum from the molecule's highest occupied molecular orbital (HOMO) to the lowest unoccupied molecular orbital (LUMO), denoted by a π -π* transition. The energy bandgap between these orbitals determines which wavelength(s) of light can be absorbed.

Unlike in an inorganic crystalline PV cell material, with its band structure and delocalized electrons, excitons in organic photovoltaics are strongly bound with an energy between 0.1 and 1.4 eV. This strong binding occurs because electronic wave functions in organic molecules are more localized, and electrostatic attraction can thus keep the electron and hole together as an exciton. The electron and hole can be dissociated by providing an interface across which the chemical potential of electrons decreases. The material that absorbs the photon is the donor, and the material acquiring the electron is called the acceptor. In Fig. 3, the polymer chain is the donor and the fullerene is the acceptor. Even after dissociation, the electron and hole may still be joined as a "geminate pair", and an electric field is then required to separate them. The electron and hole must be collected at contacts. If charge carrier mobility is insufficient, the carriers will not reach the contacts, and instead recombine at trap sites or remain in the device as undesirable space charges that oppose the flow of new carriers. The latter problem can occur if electron and hole mobilities are not matched. In that case, space-charge limited photocurrent (SCLP) hampers device performance.

Organic photovoltaics can be fabricated with an active polymer and a fullerene-based electron acceptor. Illumination of this system by visible light leads to electron transfer from the polymer to a fullerene molecule. As a result, the formation of a photoinduced quasiparticle, or polaron (P+), occurs on the polymer chain and the fullerene becomes a radical anion (C
60
). Polarons are highly mobile and can diffuse away.

Junction types

In organic solar cells, junctions are the interfaces between different layers or materials within the device's structure. These interfaces contribute to the separation and collection of charge carriers (electrons and holes) that are generated when sunlight is absorbed. The properties and structures of these junctions affects the efficiency, stability, and overall performance of organic solar cells.

The simplest organic PV device features a planar heterojunction (Fig. 1). A film of organic active material (polymer or small molecule), of electron donor or electron acceptor type is sandwiched between contacts. Excitons created in the active material may diffuse before recombining and separate, hole and electron diffusing to its specific collecting electrode. Because charge carriers have diffusion lengths of just 3–10 nm in typical amorphous organic semiconductors, planar cells must be thin, but the thin cells absorb light less well. Bulk heterojunctions (BHJs) address this shortcoming. In a BHJ, a blend of electron donor and acceptor materials is cast as a mixture, which then phase-separates. Regions of each material in the device are separated by only several nanometers, a distance suited for carrier diffusion. BHJs require sensitive control over materials morphology on the nanoscale. Important variables include materials, solvents and the donor-acceptor weight ratio.

The next logical step beyond BHJs are ordered nanomaterials for solar cells, or ordered heterojunctions (OHJs). OHJs minimize the variability associated with BHJs. OHJs are generally hybrids of ordered inorganic materials and organic active regions. For example, a photovoltaic polymer can be deposited into pores in a ceramic such as TiO2. Since holes still must diffuse the length of the pore through the polymer to a contact, OHJs suffer similar thickness limitations. Mitigating the hole mobility bottleneck is key to further enhancing device performance of OHJ's.

Single layer

Fig. 5: Sketch of a single layer organic photovoltaic cell Fig 2. sketch of single layer organic photovoltaic cell.JPG
Fig. 5: Sketch of a single layer organic photovoltaic cell

Single layer organic photovoltaic cells are the simplest form. These cells are made by sandwiching a layer of organic electronic materials between two metallic conductors, typically a layer of indium tin oxide (ITO) with high work function and a layer of low work function metal such as Aluminum, Magnesium or Calcium. The basic structure of such a cell is illustrated in Fig. 5.

The difference of work function between the two conductors sets up an electric field in the organic layer. When the organic layer absorbs light, electrons will be excited to the LUMO and leave holes in the HOMO, thereby forming excitons. The potential created by the different work functions helps to split the exciton pairs, pulling electrons to the positive electrode (an electrical conductor used to make contact with a non-metallic part of a circuit) and holes to the negative electrode. [12] [13] [14]

Examples

In 1958 the photovoltaic effect or the creation of voltage of a cell based on magnesium phthalocyanine (MgPc)—a macrocyclic compound having an alternating nitrogen atom-carbon atom ring structure—was discovered to have a photovoltage of 200 mV. [19] An Al/MgPc/Ag cell obtained photovoltaic efficiency of 0.01% under illumination at 690 nm. [20]

Conjugated polymers were also used in this type of photovoltaic cell. One device used polyacetylene (Fig. 1) as the organic layer, with Al and graphite, producing an open-circuit voltage of 0.3 V and a charge collection efficiency of 0.3%. [21] An Al/poly(3-nethyl-thiophene)/Pt cell had an external quantum yield of 0.17%, an open-circuit voltage of 0.4 V and a fill factor of 0.3. [22] An ITO/PPV/Al cell showed an open-circuit voltage of 1 V and a power conversion efficiency of 0.1% under white-light illumination. [23]

Issues

Single layer organic solar cells do not work well. They have low quantum efficiencies (<1%) and low power conversion efficiencies (<0.1%). A major problem with them is that the electric field resulting from the difference between the two conductive electrodes is seldom sufficient to split the excitons. Often the electrons recombine with the holes without reaching the electrode.

Bilayer

Fig. 6: Sketch of a multilayer organic photovoltaic cell. Fig 3 sketch of multilayer organic photovoltaic cell.JPG
Fig. 6: Sketch of a multilayer organic photovoltaic cell.

Bilayer cells contain two layers in between the conductive electrodes (Fig. 6). The two layers have different electron affinity and ionization energies, therefore electrostatic forces are generated at the interface between the two layers. Light must create excitons in this small charged region for an efficient charge separation and collecting. The materials are chosen to make the differences large enough that these local electric fields are strong, which splits excitons much more efficiently than single layer photovoltaic cells. The layer with higher electron affinity and ionization potential is the electron acceptor, and the other layer is the electron donor. This structure is also called a planar donor-acceptor heterojunction. [12] [13] [14] [15]

Examples

C60 has high electron affinity, making it a good acceptor. A C60/MEH-PPV double layer cell had a relatively high fill factor of 0.48 and a power conversion efficiency of 0.04% under monochromatic illumination. [24] PPV/C60 cells displayed a monochromatic external quantum efficiency of 9%, a power conversion efficiency of 1% and a fill factor of 0.48. [25]

Perylene derivatives display high electron affinity and chemical stability. A layer of copper phthalocyanine (CuPc) as electron donor and perylene tetracarboxylic derivative as electron acceptor, fabricating a cell with a fill factor as high as 0.65 and a power conversion efficiency of 1% under simulated AM2 illumination. [26] Halls et al. fabricated a cell with a layer of bis(phenethylimido) perylene over a layer of PPV as the electron donor. This cell had peak external quantum efficiency of 6% and power conversion efficiency of 1% under monochromatic illumination, and a fill factor of up to 0.6. [27]

Issues

The diffusion length of excitons in organic electronic materials is typically on the order of 10 nm. In order for most excitons to diffuse to the interface of layers and split into carriers, the layer thickness should be in the same range as the diffusion length. However, a polymer layer typically needs a thickness of at least 100 nm to absorb enough light. At such a large thickness, only a small fraction of the excitons can reach the heterojunction interface.

Discrete heterojunction

A three-layer (two acceptor and one donor) fullerene-free stack achieved a conversion efficiency of 8.4%. The implementation produced high open-circuit voltages and absorption in the visible spectra and high short-circuit currents. Quantum efficiency was above 75% between 400 nm and 720 nm wavelengths, with an open-circuit voltage around 1 V. [28]

Bulk heterojunction

Fig. 7: Sketch of a dispersed junction photovoltaic cell Fig 4 sketch of dispersed junction photovoltaic cell.JPG
Fig. 7: Sketch of a dispersed junction photovoltaic cell

Bulk heterojunctions have an absorption layer consisting of a nanoscale blend of donor and acceptor materials. The domain sizes of this blend are on the order of nanometers, allowing for excitons with short lifetimes to reach an interface and dissociate due to the large donor-acceptor interfacial area. [29] However, efficient bulk heterojunctions need to maintain large enough domain sizes to form a percolating network that allows the donor materials to reach the hole transporting electrode (Electrode 1 in Fig. 7) and the acceptor materials to reach the electron transporting electrode (Electrode 2). Without this percolating network, charges might be trapped in a donor or acceptor rich domain and undergo recombination. Bulk heterojunctions have an advantage over layered photoactive structures because they can be made thick enough for effective photon absorption without the difficult processing involved in orienting a layered structure while retaining similar level of performances.

Bulk heterojunctions are most commonly created by forming a solution containing the two components, casting (e.g., drop casting and spin coating) and then allowing the two phases to separate, usually with the assistance of an annealing step. The two components will self-assemble into an interpenetrating network connecting the two electrodes. [30] They are normally composed of a conjugated molecule based donor and fullerene based acceptor. The nanostructural morphology of bulk heterojunctions tends to be difficult to control, but is critical to photovoltaic performance.

After the capture of a photon, electrons move to the acceptor domains, then are carried through the device and collected by one electrode, and holes move in the opposite direction and collected at the other side. If the dispersion of the two materials is too fine, it will result in poor charge transfer through the layer. [13] [14] [19] [31]

Most bulk heterojunction cells use two components, although three-component cells have been explored. The third component, a secondary p-type donor polymer, acts to absorb light in a different region of the solar spectrum. This in theory increases the amount of absorbed light. These ternary cells operate through one of three distinct mechanisms: charge transfer, energy transfer or parallel-linkage.

In charge transfer, both donors contribute directly to the generation of free charge carriers. Holes pass through only one donor domain before collection at the anode. In energy transfer, only one donor contributes to the production of holes. The second donor acts solely to absorb light, transferring extra energy to the first donor material. In parallel linkage, both donors produce excitons independently, which then migrate to their respective donor/acceptor interfaces and dissociate. [32]

Examples

Fullerenes such as C60 and its derivatives are used as electron acceptor materials in bulk heterojunction photovoltaic cells. A cell with the blend of MEH-PPV and a methano-functionalized C60 derivative as the heterojunction, ITO and Ca as the electrodes [33] showed a quantum efficiency of 29% and a power conversion efficiency of 2.9% under monochromatic illumination. Replacing MEH-PPV with P3HT produced a quantum yield of 45% under a 10 V reverse bias. [34] [35] Further advances in modifying the electron acceptor has resulted in a device with a power conversion efficiency of 10.61% with a blend of PC71BM as the electron acceptor and PTB7-Th as the electron donor. [36]

Polymer/polymer blends are also used in dispersed heterojunction photovoltaic cells. A blend of CN-PPV and MEH-PPV with Al and ITO as the electrodes, yielded peak monochromatic power conversion efficiency of 1% and fill factor of 0.38. [37] [38]

Dye sensitized photovoltaic cells can also be considered important examples of this type.

Issues

Fullerenes such as PC71BM are often the electron acceptor materials found in high performing bulk heterojunction solar cells. However, these electron acceptor materials very weakly absorb visible light, decreasing the volume fraction occupied by the strongly absorbing electron donor material. Furthermore, fullerenes have poor electronic tunability, resulting in restrictions placed on the development of conjugated systems with more appealing electronic structures for higher voltages. Recent research has been done on trying to replace these fullerenes with organic molecules that can be electronically tuned and contribute to light absorption. [39]

Graded heterojunction

The electron donor and acceptor are mixed in such a way that the gradient is gradual. This architecture combines the short electron travel distance in the dispersed heterojunction with the advantage of the charge gradient of the bilayer technology. [40] [41]

Examples

A cell with a blend of CuPc and C60 showed a quantum efficiency of 50% and a power conversion efficiency of 2.1% using 100 mW/cm2 simulated AM1.5G solar illumination for a graded heterojunction. [42]

Continuous junction

Similar to the graded heterojunction the continuous junction concept aims at realizing a gradual transition from an electron donor to an electron acceptor. However, the acceptor material is prepared directly from the donor polymer in a post-polymerization modification step. [43]

Production

Since its active layer largely determines device efficiency, this component's morphology received much attention. [44]

If one material is more soluble in the solvent than the other, it will deposit first on top of the substrate, causing a concentration gradient through the film. This has been demonstrated for poly-3-hexyl thiophene (P3HT), phenyl-C61-butyric acid methyl ester (PCBM) devices where the PCBM tends to accumulate towards the device's bottom upon spin coating from ODCB solutions. [45] This effect is seen because the more soluble component tends to migrate towards the "solvent rich" phase during the coating procedure, accumulating the more soluble component towards the film's bottom, where the solvent remains longer. The thickness of the generated film affects the phases segregation because the dynamics of crystallization and precipitation are different for more concentrated solutions or faster evaporation rates (needed to build thicker devices). Crystalline P3HT enrichment closer to the hole-collecting electrode can only be achieved for relatively thin (100 nm) P3HT/PCBM layers. [46]

The gradients in the initial morphology are then mainly generated by the solvent evaporation rate and the differences in solubility between the donor and acceptor inside the blend. This dependence on solubility has been clearly demonstrated using fullerene derivatives and P3HT. [47] When using solvents which evaporate at a slower rate (as chlorobenzene (CB) or dichlorobenzene (DCB)) you can get larger degrees of vertical separation or aggregation while solvents that evaporate quicker produce a much less effective vertical separation. Larger solubility gradients should lead to more effective vertical separation while smaller gradients should lead to more homogeneous films. These two effects were verified on P3HT:PCBM solar cells. [48] [49]

The solvent evaporation speed as well as posterior solvent vapor or thermal annealing procedures were also studied. [50] Blends such as P3HT:PCBM seem to benefit from thermal annealing procedures, while others, such as PTB7:PCBM, seem to show no benefit. [51] In P3HT the benefit seems to come from an increase of crystallinity of the P3HT phase which is generated through an expulsion of PCBM molecules from within these domains. This has been demonstrated through studies of PCBM miscibility in P3HT as well as domain composition changes as a function of annealing times. [52] [53] [54]

The above hypothesis based on miscibility does not fully explain the efficiency of the devices as solely pure amorphous phases of either donor or acceptor materials never exist within bulk heterojunction devices. A 2010 paper [55] suggested that current models that assume pure phases and discrete interfaces might fail given the absence of pure amorphous regions. Since current models assume phase separation at interfaces without any consideration for phase purity, the models might need to be changed.

The thermal annealing procedure varies depending on precisely when it is applied. Since vertical species migration is partly determined by the surface tension between the active layer and either air or another layer, annealing before or after the deposition of additional layers (most often the metal cathode) affects the result. In the case of P3HT:PCBM solar cells vertical migration is improved when cells are annealed after the deposition of the metal cathode.

Donor or acceptor accumulation next to the adjacent layers might be beneficial as these accumulations can lead to hole or electron blocking effects which might benefit device performance. In 2009 the difference in vertical distribution on P3HT:PCBM solar cells was shown to cause problems with electron mobility which ends up with the yielding of very poor device efficiencies. [56] Simple changes to device architecture – spin coating a thin layer of PCBM on top of the P3HT – greatly enhance cell reproducibility, by providing reproducible vertical separation between device components. Since higher contact between the PCBM and the cathode is required for better efficiencies, this largely increases device reproducibility.

According to neutron scattering analysis, P3HT:PCBM blends have been described as "rivers" (P3HT regions) interrupted by "streams" (PCBM regions). [57]

Progress in growth techniques

Mostly organic films for photovoltaic applications are deposited by spin coating and vapor-phase deposition. However each method has certain draw backs, spin coating technique can coat larger surface areas with high speed but the use of solvent for one layer can degrade the already existing polymer layer. Another problem is related with the patterning of the substrate for device as spin-coating results in coating the entire substrate with a single material.

Vacuum thermal evaporation

Fig. 9: Vacuum thermal evaporation (a) and organic phase vapor deposition (b) Fig.6 (a) Vapor thermal Evaporation.JPG
Fig. 9: Vacuum thermal evaporation (a) and organic phase vapor deposition (b)

Another deposition technique is vacuum thermal evaporation (VTE) which involves the heating of an organic material in vacuum. The substrate is placed several centimeters away from the source so that evaporated material may be directly deposited onto the substrate, as shown in Fig. 9(a). This method is useful for depositing many layers of different materials without chemical interaction between different layers. However, there are sometimes problems with film-thickness uniformity and uniform doping over large-area substrates. In addition, the materials that deposit on the wall of the chamber can contaminate later depositions. This "line of sight" technique also can create holes in the film due to shadowing, which causes an increase in the device series-resistance and short circuit. [58]

Organic vapor phase deposition

Organic vapor phase deposition (OVPD), shown in Fig. 9(b), allows better control of the structure and morphology of the film than vacuum thermal evaporation. The process involves evaporation of the organic material over a substrate in the presence of an inert carrier gas. The resulting film morphology can be tuned by changing the gas flow rate and the source temperature. Uniform films can be grown by reducing the carrier gas pressure, which will increase the velocity and mean free path of the gas, and as a result boundary layer thickness decreases. Cells produced by OVPD do not have issues related with contaminations from the flakes coming out of the walls of the chamber, as the walls are warm and do not allow molecules to stick to and produce a film upon them.

Another advantage over VTE is the uniformity in evaporation rate. This occurs because the carrier gas becomes saturated with the vapors of the organic material coming out of the source and then moves towards the cooled substrate, Fig. 9(b). Depending on the growth parameters (temperature of the source, base pressure and flux of the carrier gas) the deposited film can be crystalline or amorphous in nature. Devices fabricated using OVPD show a higher short-circuit current density than that of devices made using VTE. An extra layer of donor-acceptor hetero-junction at the top of the cell may block excitons, whilst allowing conduction of electron; resulting in improved cell efficiency. [58]

Solvent effects

Conditions for spin coating and evaporation affect device efficiency. [59] [60] Solvent and additives influence donor-acceptor morphology. [61] Additives slow down evaporation, leading to more crystalline polymers and thus improved hole conductivities and efficiencies. Typical additives include 1,8-octanedithiol, ortho-dichlorobenzene, 1,8-diiodooctane (DIO), and nitrobenzene. [48] [62] [63] [64] The DIO effect was attributed to the selective solubilization of PCBM components, modifies fundamentally the average hopping distance of electrons, and thus improves electron mobility. [65] Additives can also lead to big increases in efficiency for polymers. [66] For HXS-1/PCBM solar cells, the effect was correlated with charge generation, transport and shelf-stability. [67] Other polymers such as PTTBO also benefit significantly from DIO, achieving PCE values of more than 5% from around 3.7% without the additive.

Polymer Solar Cells fabricated from chloronaphthalene (CN) as a co-solvent enjoy a higher efficiency than those fabricated from the more conventional pure chlorobenzene solution. This is because the donor-acceptor morphology changes, which reduces the phase separation between donor polymer and fullerene. As a result, this translates into high hole mobilities. Without co-solvents, large domains of fullerene form, decreasing photovoltaic performance of the cell due to polymer aggregation in solution. This morphology originates from the liquid-liquid phase separation during drying; solve evaporation causes the mixture to enter into the spinodal region, in which there are significant thermal fluctuations. Large domains prevent electrons from being collected efficiently (decreasing PCE). [68]

Small differences in polymer structure can also lead to significant changes in crystal packing that inevitably affect device morphology. PCPDTBT differs from PSBTBT caused by the difference in bridging atom between the two polymers (C vs. Si), which implies that better morphologies are achievable with PCPDTBT:PCBM solar cells containing additives as opposed to the Si system which achieves good morphologies without help from additional substances. [69]

Self-assembled cells

Supramolecular chemistry was investigated, using donor and acceptor molecules that assemble upon spin casting and heating. Most supramolecular assemblies employ small molecules. [70] [71] Donor and acceptor domains in a tubular structure appear ideal for organic solar cells. [72]

Diblock polymers containing fullerene yield stable organic solar cells upon thermal annealing. [73] Solar cells with pre-designed morphologies resulted when appropriate supramolecular interactions are introduced. [74]

Progress on BCPs containing polythiophene derivatives yield solar cells that assemble into well defined networks. [75] This system exhibits a PCE of 2.04%. Hydrogen bonding guides the morphology.

Device efficiency based on co-polymer approaches have yet to cross the 2% barrier, whereas bulk-heterojunction devices exhibit efficiencies >7% in single junction configurations. [76]

Fullerene-grafted rod-coil block copolymers have been used to study domain organization. [77]

Supramolecular approaches to organic solar cells provide understanding about the macromolecular forces that drive domain separation.

Transparent polymer cells

Transparent or semi-transparent PSCs allow for the absorption of low- or high-energy photons outside the visible spectrum, thus optimizing its sunlight harnessing capabilities and covering a broader absorption spectra. [78] [79] These types of PSCs are ideal for capturing near-infrared or ultraviolet photons due to its low inherent sensitivity to photons within the visible spectrum. Typical PSCs utilize opaque metal electrodes that limit its transparency, and thus its performance. [78] The absorber layer of PSCs are intrinsically semi-transparent. [80] Thus, one approach to achieving a visibly transparent PSC is to modify the top electrode to make it more transparent. Materials such as ITO, ultra-thin metals, metal grids, graphene, and carbon nanotubes have been used to fabricate semi-transparent top electrodes. [81] [82] Yet, the performance of transparent PSCs have shown to be lacking when compared to their opaque electrode PSC counterparts. [83] When the top electrode is made transparent, the cell's ability to trap the electromagnetic field in the absorber layer decreases, resulting in a low PCE. An extensive amount of research is currently being conducted to improve the PCE of such cells. [81] These types of PSCs have been applied to building-integrated photovoltaics, tandem devices, and portable electronics. [78] [82] [83]

Infrared polymer cells

Infrared cells preferentially absorb light in the infrared range rather than visible wavelengths. A 2010 study developed infrared-transparent PSCs with a CNT film top electrode on the back side and an ITO glass layer on the front side allowing for optical transmittance from both sides of the cell. A ZnO layer was placed on top of the ITO with a P3HT:PCBM layer being added to the ZnO, thus creating an ITO/ZnO/P3HT:PCBM/CNT (bottom to top) cell. It was observed that the top CNT electrode and bottom ITO electrode both exhibited 80% transmittance within a 500 nm to 2.5 um spectra. The cell itself had an optical transmittance of 80% in the 670 nm to 1.2 um range, 60% in the 1.2 um to 2.5 um range. Conversely, a control cell with an Ag top electrode resulted in no transmittance within this spectra. Additionally, the cell had a relatively low transmittance in the visible region due to the high visible absorbance of the P3HT:PCBM layer. Such cells can be applied to tandem devices and the vertical assembly of PSCs. [78]

As of 2012, infrared cells were nearly 70% transparent to visible light. The cells allegedly can be made in high volume at low cost using solution processing. The cells employ silver nanowire/titanium dioxide composite films as the top electrode, replacing conventional opaque metal electrodes. With this combination, 4% power-conversion efficiency was achieved. [84]

In 2014, near-infrared polymer solar cells based on a copolymer of naphthodithiophene diimide and bithiophene (PNDTI-BT-DT) were fabricated in combination with PTB7 as an electron donor. Both PNDTI-BT-DT and PTB7 formed a crystalline structure in the blend films similar to in the pristine films, leading to the efficient charge generation contributed from both polymers. [85]

Much research has been focused on developing a transparent top electrode for PSCs. However, a 2017 study explored optimizing the active layer of semi-transparent PSCs. The researchers proposed a semi-transparent PSC with enhanced efficiency that utilizes both narrow bandgap polymer donor, PTB7-Th, and non-fullerene acceptor, IHIC. The results of this study showed that the proposed PSC exhibited high transmittance and absorption in the infrared spectrum but low absorption in the visible spectrum. This cell showed to be relatively stable and have a maximum PCE of 9.77%, which, as of 2017, is the highest reported PCE value. [86]

Typical Current-Voltage Behavior and Power Conversion Efficiency

Organic photovoltaics, similar to inorganic photovoltaics, are generally characterized through current-voltage analysis. [87] This analysis provides multiple device metrics values that are used to understand device performance. One of the most crucial metrics is the Power Conversion Efficiency (PCE).

Organic Photovoltaic Current Voltage Curve.png

PCE (η) is proportional to the product of the short-circuit current (JSC), the open-circuit voltage (VOC), and the fill factor (FF), all of which can be determined from a current-voltage curve.

Where Pin is the incident solar power.

The short circuit current (Jsc), is the maximum photocurrent generation value. [88] It corresponds to the y-intercept value of standard current-voltage curve in which current is plotted along the y-axis and voltage is plotted along the x-axis.  Within organic solar cells, the short circuit current can be impacted by a variety of material factors. These include the mobility of charge carriers, the optical absorption profile and general energetic driving forces that lead to a more efficient extraction of charge carriers [88]

The open-circuit voltage (Voc) is the voltage when there is no current running through the device. [88] This corresponds to the x-intercept on a current-voltage curve. Within bulk heterojunction organic photovoltaic devices, this value is highly dependent on HOMO and LUMO energy levels and work functions for the active layer materials [88]

Since power is the product of voltage and current, the maximum power point occurs when the product between voltage and current is maximized.

The fill factor, FF, can be thought of as the "squareness" of a current voltage curve. [87] It is the quotient of the maximum power value and the product of the open-circuit voltage and short circuit current. [87] This is shown in the image above as the ratio of the area of the yellow rectangle to the greater blue rectangle. For organic photovoltaics, this fill factor is essentially a measure of how efficiently generated charges are extracted from the device. [88] This can be thought of as a "competition" between charges transporting through the device, and charges that recombine. [88]

A major issue surrounding polymer solar cells is the low Power Conversion Efficiency (PCE) of fabricated cells. In order to be considered commercially viable, PSCs must be able to achieve at least 10–15% efficiency [89] —this is already much lower than inorganic PVs. However, due to the low cost of polymer solar cells, a 10–15% efficiency is commercially viable.

Recent advances in polymer solar cell performance have resulted from compressing the bandgap to enhance short-circuit current while lowering the Highest Occupied Molecular Orbital (HOMO) to increase open-circuit voltage. However, PSCs still suffer from low fill factors (typically below 70%). However, as of 2013, researchers have been able to fabricate PSCs with fill factors of over 75%. Scientists have been able to accomplish via an inverted BHJ and by using nonconventional donor / acceptor combinations. [90]

Commercialization

Number of scientific publications contributing to the subject "polymer solar cell(s)" by year. Search done through ISI, Web of Science. Polymer solar cells publications by year.jpg
Number of scientific publications contributing to the subject "polymer solar cell(s)" by year. Search done through ISI, Web of Science.

Polymer solar cells have yet to commercially compete with silicon solar cells and other thin-film cells. The present efficiency of polymer solar cells lies near 10%, well below silicon cells. Polymer solar cells also suffer from environmental degradation, lacking effective protective coatings.

Further improvements in performance are needed to promote charge carrier diffusion; transport must be enhanced through control of order and morphology; and interface engineering must be applied to the problem of charge transfer across interfaces.

Research is being conducted into using tandem architecture in order to increase efficiency of polymer solar cells. Similar to inorganic tandem architecture, organic tandem architecture is expected to increase efficiency. Compared with a single-junction device using low-bandgap materials, the tandem structure can reduce heat loss during photon-to-electron conversion. [9]

Polymer solar cells are not widely produced commercially. Starting in 2008, Konarka Technologies started production of polymer-fullerene solar cells. [92] The initial modules were 3–5% efficient, and only last for a few years. Konarka has since filed for bankruptcy, as those polymer solar cells were unable to penetrate the PV market.

PSCs also still suffer from low fill factors (typically below 70%). However, as of 2013, researchers have been able to fabricate PSCs with fill factors of over 75%. Scientists have been able to accomplish via an inverted BHJ and by using nonconventional donor / acceptor combinations. [90]

However, efforts are being made to upscale manufacturing of polymer solar cells, in order to decrease costs and also advocate for a practical approach for PSC production. Such efforts include full roll-to-roll solution processing. However, roll-to-roll solution processing is ill-suited for on-grid electricity production due to the short lifetime of polymer solar cells. Therefore, commercial applications for polymer solar cells still include primarily consumer electronics and home appliances. [93]

Modeling organic solar cells

As discussed above, organic semiconductors are highly disordered materials with no long range order. This means that the conduction band and valence band edges are not well defined. Furthermore, this physical and energetic disorder generates trap states in which photogenerated electrons and holes can become trapped and then eventually recombine.

Key to accurately describing organic solar cells in a device model is to include carrier trapping and recombination via trap states. A commonly used approach is to use an effective medium model, where by standard drift diffusion equations are used to describe transport across the device. Then, an exponential tail of trap states is introduced which decays into the band gap from the mobility edges. [94] To describe capture/escape from these trap states the Shockley–Read–Hall (SRH) can be used. The Shockley-Read-Hall mechanism has been shown able to reproduce polymer:fullerene device behavior in both time domain and steady state. [94]

Designing organic solar cells requires optimization of a large number of structural and compositional parameters, such as band gaps and layer thicknesses. Numerical device simulation can provide instrumental insight to identify the optimum stack configuration. This allows reducing the requested time for the development of efficient solar cells.

Current challenges and recent progress

Difficulties associated with organic photovoltaic cells include their low external quantum efficiency (up to 70%) [95] compared to inorganic photovoltaic devices, despite having good internal quantum efficiency; this is due to insufficient absorption with active layers on the order of 100 nanometers. Instabilities against oxidation and reduction, recrystallization and temperature variations can also lead to device degradation and decreased performance over time. This occurs to different extents for devices with different compositions, and is an area into which active research is taking place. [96]

Other important factors include the exciton diffusion length, charge separation and charge collection which are affected by the presence of impurities.

Charge carrier mobility and transport

Especially for bulk heterojunction solar cells, understanding charge carrier transport is vital in improving the efficiencies of organic photovoltaics. Currently, bulk heterojunction devices have imbalanced charge-carrier mobility, with the hole mobility being at least an order of magnitude lower than that of the electron mobility; this results in space charge build-up and a decrease in the fill factor and power conversion efficiency of a device. [97] Due to having low mobility, efficient bulk heterojunction photovoltaics have to be designed with thin active layers to avoid recombination of the charge carriers, which is detrimental to absorption and scalability in processing. Simulations have demonstrated that in order to have a bulk heterojunction solar cell with a fill factor above 0.8 and external quantum efficiency above 90%, there needs to be balanced charge carrier mobility to reduce a space charge effect, as well as an increase in charge carrier mobility and/or a decrease in the bimolecular recombination rate constant. [98]

Effect of film morphology

Fig. 8: Highly folded heterojunction (a); heterojunction with controlled growth (b) Fig 5 (a)- Highly folded Hetero-junction, (b)- Hetero-junction with controlled growth.JPG
Fig. 8: Highly folded heterojunction (a); heterojunction with controlled growth (b)

As described above, dispersed heterojunctions of donor-acceptor organic materials have high quantum efficiencies compared to the planar hetero-junction, because in dispersed heterojunctions it is more likely for an exciton to find an interface within its diffusion length. Film morphology can also have a drastic effect on the quantum efficiency of the device. Rough surfaces and the presence of voids can increase the series resistance and also the chance of short-circuiting. Film morphology and, as a result, quantum efficiency can be improved by annealing of a device after covering it by a ~1000 Å thick metal cathode. Metal film on top of the organic film applies stresses on the organic film, which helps to prevent the morphological relaxation in the organic film. This gives more densely packed films and at the same time allows the formation of phase-separated interpenetrating donor-acceptor interface inside the bulk of organic thin film. [99]

Controlled growth heterojunction

Charge separation occurs at the donor-acceptor interface. Whilst traveling to the electrode, a charge can become trapped and/or recombine in a disordered interpenetrating organic material, resulting in decreased device efficiency. Controlled growth of the heterojunction provides better control over positions of the donor-acceptor materials, resulting in much greater power efficiency (ratio of output power to input power) than that of planar and highly disoriented hetero-junctions (as shown in Fig. 8). Thus, the choice of suitable processing parameters in order to better control the structure and film morphology is highly desirable. [32]

Light trapping

Various type of components are applied to increase light trapping (Light in-coupling) effects in thin organic solar cells. [100] In addition to the flexibility of organic solar cells, by using flexible electrodes [101] [102] and substrates [103] instead of ITO and glass respectively, fully flexible organic solar cells can be produced. By these use of flexible substrates and substrates, easier methods to provide light trapping effects to OPVs are introduced such as polymer electrodes with embedded scattering particles, [104] nano imprinted polymer electrodes, [105] patterned PET substrates [106] [107] and even optical display film commercialized for liquid crystal displays (LCD) as substrates. [108] Much research will be taken for enhancing the performance of OPVs with the merit of easy light trapping structures processing.

Use in tandem photovoltaics

Recent research and study has been done in utilizing an organic solar cell as the top cell in a hybrid tandem solar cell stack. Because organic solar cells have a higher band gap than traditional inorganic photovoltaics like silicon or CIGS, they can absorb higher energy photons without losing much of the energy due to thermalization, and thus operate at a higher voltage. The lower energy photons and higher energy photons that are unabsorbed pass through the top organic solar cell and are then absorbed by the bottom inorganic cell. Organic solar cells are also solution processible at low temperatures with a low cost of 10 dollars per square meter, resulting in a printable top cell that improves the overall efficiencies of existing, inorganic solar cell technologies. [109] Much research has been done to enable the formation of such a hybrid tandem solar cell stack, including research in the deposition of semi-transparent electrodes that maintain low contact resistance while having high transparency. [110]

Mechanical behavior

Understanding the mechanical properties of organic semiconductors and in particular, the wide range of failure mechanisms of operating organic solar cell devices are critical in determining the operational stability of organic solar cells for various applications.The mechanical properties of organic solar cells can be attributed to intermolecular and surface forces present in the material. These attributes are not only influenced by the molecular structure but are also quite sensitive to processing conditions, making the study of mechanical properties of polymer thin films such as tensile modulus, ductility and fracture toughness under strain rather difficult. [111] Because of this, it is nontrivial to quantify a "figure of merit" that will predict the mechanical stability of a device and the robustness of a device under strain will depend on many factors.

Most often, the substrate provides support to the device and mechanical failure of the substrate will lead to suboptimal power conversion efficiency of the device. Hence while it is necessary that the substrate provides mechanical support to the organic active layer, care must be taken to ensure that increasing the tensile strength of the substrate does not come at the cost of the film fracturing at low strains. In general, it is desirable that the active layer deforms in tandem with the substrate. This is made possible with a low elastic modulus and high elastic limit. The ductility of a thin film is commonly measured as the strain at which cracks appear on the film. However, the crack onset strain is also dependent on other factors such as the degree of cohesion/adhesion between the film and the substrate. Various studies have related the cohesive or adhesive fracture energy Gc , defined as the work required to break separate polymer interfaces to molecular parameters and processing conditions. [112] [113] Along with the cohesion, the trajectory of crack propagation following formation depends on the mechanical properties of the material the crack propagates through. In polymers like P3HT that exhibit good plasticity, a plastic zone forms at the crack tip upon the application of a tensile strain normal to the plane of the device and expands until it is confined by either crystalline domains in the film or by a rigid substrate, thus dissipating the deformation energy and decreasing the cohesion between the interfaces. [114] The mechanical buckling technique has also proven to be quite successful in determining the elastic moduli of various organic thin films. The method is based on the buckling instability that gives rise to wrinkles in the film under a compressive strain.The wavelength of the wrinkling pattern, can be related to the tensile modulus of the film in terms of the film thickness and elastic modulus of the substrate. [115]

In the design of devices incorporating organic solar cells, Gc and strain at fracture have been identified as two metrics that are important to consider. The bulk heterojunction (BHJ) layer is usually the weakest layer of an organic solar cell, so it is necessary to design the BHJ materials to be mechanically stable, with a target Gc of 5 J m-2 and a target strain at fracture of 20-30%. Polymer-based acceptors have been shown to exhibit superior mechanical properties when compared to small-molecule acceptors and fullerene-based acceptors. Additionally, the mechanical properties of polymer-based acceptors are influenced by Mn, the number-average molecular weight of the polymer molecules. It was determined that mechanical properties increase with increasing Mn, but only once Mn has surpassed Mc, the critical molecular weight at which entanglements cause the rate of viscosity change to increase with increasing Mn. This phenomenon occurs because the rate of chain entanglement and miscibility between the polymer acceptor and donor both increase. The effect of these characteristics is that the plastic deformation of these materials in reaction to mechanical stress was high, meaning that more of the energy was dissipated, while the materials with less mechanical strength fractured more readily. [116]

Recent directions for bulk heterojunction materials research

One major area of current research is the use of non-fullerene acceptors. While fullerene acceptors have been the standard for most organic photovoltaics due to their compatibility within bulk heterojunction cell designs as well as their good transport properties, they do have some fallbacks that are leading researchers to attempt to find alternatives. [117] Some negatives of fullerene acceptors include their instability, that they are somewhat limited in energy-tunability and they have poor optical absorption. [117] Researchers have developed small molecule acceptors that due to their good energy tunability, can exhibit high open-circuit voltages. [117] Combining a polymer donor (D18) with a small molecule acceptor (Y6), scientists have fabricated organic solar cells in the laboratory giving high efficiencies over 18%. [118] However, there are still major challenges with non-fullerene acceptors, including the low charge carrier mobilities of small molecule acceptors, and that the sheer number of possible molecules is overwhelming for the research community. [117]

A challenge facing the development of organic solar cells utilizing non-fullerene acceptors (NFAs) is the selection of a solvent that has a high boiling point and is environmentally friendly, whereas conventional solvents such as chloroform (CF) tend to exhibit low boiling points and toxicity. Such a solvent is required for further scale-up of organic solar cells, but has also been associated with decreases in PCE due to poor solubility of donor and acceptor materials within the solvent. Appending alkyl chains to NFAs has led to increases in solubility but decreases in molecular packing (π-stacking), which leads to no net impact on PCE. The use of guest assistance has been found to benefit both solubility and molecular packing. A guest molecule named BTO with oligo(ethylene glycol) (OEG) side chains used in conjunction with the NFA Y6 as the acceptor, PM6 as the donor, and paraxylene (PX) as the high-melting-point and sustainable solvent led to an increase in PCE from 11% to over 16%, regarded an acceptable level of efficiency. [119] A further modification that has been successful in the development of cleaner organic photovoltaics is the hot-spin coating of substrates by non-halogenated solvents. It was found that the temperature at which hot-spin coating was operated altered the solution to solid phase evolution of the acceptor-donor blends so that higher temperatures resulted in a higher acceptor concentration in the surface of the substrate. This is because higher temperatures facilitated decreased aggregation and precipitation, allowing the substrate to retain a higher acceptor concentration. In an experiment, organic solar cells constructed with ternary blends of PM6 donor and Y6-1O and BO-4Cl acceptors and various non-halogenated solvents including o-xylene and toluene exhibited PCE values of over 18%, which are the most efficient organic photovoltaics constructed with non-halogenated solvents, to date. Further morphological analyses showed that the hot-spun OPVs prepared with non-halogenated solvents exhibited similar morphological characteristics to that of OPVs prepared with halogenated solvents. [120]

Small molecules are also being heavily researched to act as donor materials, potentially replacing polymeric donors. Since small molecules do not vary in molecular weights the way polymers do, they would require less purification steps and are less susceptible to macromolecule defects and kinks that can create trap states leading to recombination. [121] Recent research has shown that high-performing small molecular donor structures tend to have planar 2-D structures and can aggregate or self assemble. [121] Sine performance of these devices is highly depended on active layer morphology, present research is continuing to investigate small molecule possibilities, and optimize device morphology through processes such as annealing for various materials. [121]

See also

Other third-generation solar cells:

Related Research Articles

<span class="mw-page-title-main">Organic electronics</span> Field of materials science

Organic electronics is a field of materials science concerning the design, synthesis, characterization, and application of organic molecules or polymers that show desirable electronic properties such as conductivity. Unlike conventional inorganic conductors and semiconductors, organic electronic materials are constructed from organic (carbon-based) molecules or polymers using synthetic strategies developed in the context of organic chemistry and polymer chemistry.

Organic semiconductors are solids whose building blocks are pi-bonded molecules or polymers made up by carbon and hydrogen atoms and – at times – heteroatoms such as nitrogen, sulfur and oxygen. They exist in the form of molecular crystals or amorphous thin films. In general, they are electrical insulators, but become semiconducting when charges are either injected from appropriate electrodes, upon doping or by photoexcitation.

<span class="mw-page-title-main">Dye-sensitized solar cell</span> Type of thin-film solar cell

A dye-sensitized solar cell is a low-cost solar cell belonging to the group of thin film solar cells. It is based on a semiconductor formed between a photo-sensitized anode and an electrolyte, a photoelectrochemical system. The modern version of a dye solar cell, also known as the Grätzel cell, was originally co-invented in 1988 by Brian O'Regan and Michael Grätzel at UC Berkeley and this work was later developed by the aforementioned scientists at the École Polytechnique Fédérale de Lausanne (EPFL) until the publication of the first high efficiency DSSC in 1991. Michael Grätzel has been awarded the 2010 Millennium Technology Prize for this invention.

<span class="mw-page-title-main">Solar cell</span> Photodiode used to produce power from light on a large scale

A solar cell or photovoltaic cell is an electronic device that converts the energy of light directly into electricity by means of the photovoltaic effect. It is a form of photoelectric cell, a device whose electrical characteristics vary when it is exposed to light. Individual solar cell devices are often the electrical building blocks of photovoltaic modules, known colloquially as "solar panels". The common single-junction silicon solar cell can produce a maximum open-circuit voltage of approximately 0.5 to 0.6 volts.

Hybrid solar cells combine advantages of both organic and inorganic semiconductors. Hybrid photovoltaics have organic materials that consist of conjugated polymers that absorb light as the donor and transport holes. Inorganic materials in hybrid cells are used as the acceptor and electron transporter in the structure. The hybrid photovoltaic devices have a potential for not only low-cost by roll-to-roll processing but also for scalable solar power conversion.

<span class="mw-page-title-main">Quantum dot solar cell</span> Type of solar cell based on quantum dot devices

A quantum dot solar cell (QDSC) is a solar cell design that uses quantum dots as the captivating photovoltaic material. It attempts to replace bulk materials such as silicon, copper indium gallium selenide (CIGS) or cadmium telluride (CdTe). Quantum dots have bandgaps that are adjustable across a wide range of energy levels by changing their size. In bulk materials, the bandgap is fixed by the choice of material(s). This property makes quantum dots attractive for multi-junction solar cells, where a variety of materials are used to improve efficiency by harvesting multiple portions of the solar spectrum.

<span class="mw-page-title-main">Phenyl-C61-butyric acid methyl ester</span> Chemical compound

PCBM is the common abbreviation for the fullerene derivative [6,6]-phenyl-C61-butyric acid methyl ester. It is being investigated in organic solar cells.

<span class="mw-page-title-main">PEDOT-TMA</span> Chemical compound

Poly(3,4-ethylenedioxythiophene)-tetramethacrylate or PEDOT-TMA is a p-type conducting polymer based on 3,4-ethylenedioxylthiophene or the EDOT monomer. It is a modification of the PEDOT structure. Advantages of this polymer relative to PEDOT are that it is dispersible in organic solvents, and it is non-corrosive. PEDOT-TMA was developed under a contract with the National Science Foundation, and it was first announced publicly on April 12, 2004. The trade name for PEDOT-TMA is Oligotron. PEDOT-TMA was featured in an article entitled "Next Stretch for Plastic Electronics" that appeared in Scientific American in 2004. The U.S. Patent office issued a patent protecting PEDOT-TMA on April 22, 2008.

Organic photovoltaic devices (OPVs) are fabricated from thin films of organic semiconductors, such as polymers and small-molecule compounds, and are typically on the order of 100 nm thick. Because polymer based OPVs can be made using a coating process such as spin coating or inkjet printing, they are an attractive option for inexpensively covering large areas as well as flexible plastic surfaces. A promising low cost alternative to conventional solar cells made of crystalline silicon, there is a large amount of research being dedicated throughout industry and academia towards developing OPVs and increasing their power conversion efficiency.

<span class="mw-page-title-main">Transparent conducting film</span> Optically transparent and electrically conductive material

Transparent conducting films (TCFs) are thin films of optically transparent and electrically conductive material. They are an important component in a number of electronic devices including liquid-crystal displays, OLEDs, touchscreens and photovoltaics. While indium tin oxide (ITO) is the most widely used, alternatives include wider-spectrum transparent conductive oxides (TCOs), conductive polymers, metal grids and random metallic networks, carbon nanotubes (CNT), graphene, nanowire meshes and ultra thin metal films.

A photoactive layer is used in solar cells for absorbing light. It can be found in all solar cells, but with different panels the photoactive layer is made of different materials. Inorganic layers are made from inorganic materials such as silicon. The film has a layer arrangement of electrodes and counter electrode with organic layers in between the two. The layer is found underneath the glass, adhesive, and reflection coating, but is the first required part of the cell.

<span class="mw-page-title-main">Polyfluorene</span> Chemical compound

Polyfluorene is a polymer with formula (C13H8)n, consisting of fluorene units linked in a linear chain — specifically, at carbon atoms 2 and 7 in the standard fluorene numbering. It can also be described as a chain of benzene rings linked in para positions with an extra methylene bridge connecting every pair of rings.

<span class="mw-page-title-main">Photoconductive atomic force microscopy</span> Type of atomic force microscopy

Photoconductive atomic force microscopy (PC-AFM) is a variant of atomic force microscopy that measures photoconductivity in addition to surface forces.

<span class="mw-page-title-main">Perovskite solar cell</span> Alternative to silicon-based photovoltaics

A perovskite solar cell (PSC) is a type of solar cell that includes a perovskite-structured compound, most commonly a hybrid organic–inorganic lead or tin halide-based material as the light-harvesting active layer. Perovskite materials, such as methylammonium lead halides and all-inorganic cesium lead halide, are cheap to produce and simple to manufacture.

<span class="mw-page-title-main">Polymer-fullerene bulk heterojunction solar cell</span>

Polymer-fullerene bulk heterojunction solar cells are a type of solar cell researched in academic laboratories. Polymer-fullerene solar cells are a subset of organic solar cells, also known as organic photovoltaic (OPV) cells, which use organic materials as their active component to convert solar radiation into electrical energy. The polymer, which functions as the donor material in these solar cells, and fullerene derivatives, which function as the acceptor material, are essential components. Specifically, fullerene derivatives act as electron acceptors for donor materials like P3HT, creating a polymer-fullerene based photovoltaic cell. The Polymer-fullerene BHJ forms two channels for transferring electrons and holes to the corresponding electrodes, as opposed to the planar architecture when the Acceptor (A) and Donor (D) materials were sequentially stacked on top of each other and could selectively touch the cathode and anode electrodes. Hence, the D and A domains are expected to form a bi-continuous network with Nano-scale morphology for efficient charge transport and collection after exciton dissociation. Therefore, in the BHJ device architecture, a mixture of D and A molecules in the same or different solvents was used to form a bi-continual layer, which serves as the active layer of the device that absorbs light for exciton generation. The bi-continuous three-dimensional interpenetrating network of the BHJ design generates a greater D-A interface, which is necessary for effective exciton dissociation in the BHJ due to short exciton diffusion. When compared to the prior bilayer design, photo-generated excitons may dissociate into free holes and electrons more effectively, resulting in better charge separation for improved performance of the cell.

Diketopyrrolopyrroles (DPPs) are organic dyes and pigments based on the heterocyclic dilactam 2,5-dihydropyrrolo[3,4-c]pyrrole-1,4-dione, widely used in optoelectronics. DPPs were initially used as pigments in the painting industry due to their high resistance to photodegradation. More recently, DPP derivatives have been also investigated as promising fluorescent dyes for bioimaging applications, as well as components of materials for use in organic electronics.

<span class="mw-page-title-main">Contorted aromatics</span> Hydrocarbon compounds composed of rings fused such that the molecule is nonplanar

In organic chemistry, contorted aromatics, or more precisely contorted polycyclic aromatic hydrocarbons, are polycyclic aromatic hydrocarbons (PAHs) in which the fused aromatic molecules deviate from the usual planarity.

Light harvesting materials harvest solar energy that can then be converted into chemical energy through photochemical processes. Synthetic light harvesting materials are inspired by photosynthetic biological systems such as light harvesting complexes and pigments that are present in plants and some photosynthetic bacteria. The dynamic and efficient antenna complexes that are present in photosynthetic organisms has inspired the design of synthetic light harvesting materials that mimic light harvesting machinery in biological systems. Examples of synthetic light harvesting materials are dendrimers, porphyrin arrays and assemblies, organic gels, biosynthetic and synthetic peptides, organic-inorganic hybrid materials, and semiconductor materials. Synthetic and biosynthetic light harvesting materials have applications in photovoltaics, photocatalysis, and photopolymerization.

Non-fullerene acceptors (NFAs) are types of acceptors used in organic solar cells (OSCs). The name Fullerene comes from another type of acceptor-molecule which was used as the main acceptor material for bulk heterojunction Organic solar cells. Non-fullerene acceptors are thus defined as not being a part of this sort of acceptors.

Ellen Moons is a Belgian materials scientist who is a professor at Karlstad University. Her research considers the organisation of molecules and materials in thin films. She is mainly interested in organic and hybrid materials for solution processed photovoltaics.

References

  1. Ameri, Tayebeh; Dennler, Gilles; Lungenschmied, Christoph; Brabec, Christoph (2009). "Organic tandem solar cells: A review". Energy & Environmental Science. 2 (4): 348. doi:10.1039/B817952B . Retrieved 2019-05-20.
  2. Pulfrey, L.D. (1978). Photovoltaic Power Generation. New York: Van Nostrand Reinhold Co. ISBN   9780442266400.
  3. Nelson, Jenny (2011-10-01). "Polymer:fullerene bulk heterojunction solar cells". Materials Today. 14 (10): 462–470. doi: 10.1016/S1369-7021(11)70210-3 .
  4. "What can organic solar cells bring to the table?" . Retrieved 26 March 2021.
  5. Luther, Joachim; Nast, Michael; Fisch, M. Norbert; Christoffers, Dirk; Pfisterer, Fritz; Meissner, Dieter; Nitsch, Joachim (2000). "Solar Technology". Ullmann's Encyclopedia of Industrial Chemistry. doi:10.1002/14356007.a24_369. ISBN   3527306730.
  6. Jørgensen, Mikkel; Norrman, Kion; Krebs, Frederik C. (2008). "Stability/degradation of polymer solar cells". Solar Energy Materials and Solar Cells. 92 (7): 686. doi:10.1016/j.solmat.2008.01.005.
  7. Po, Riccardo; Carbonera, Chiara; Bernardi, Andrea; Tinti, Francesca; Camaioni, Nadia (2012). "Polymer- and carbon-based electrodes for polymer solar cells: Toward low-cost, continuous fabrication over large area". Solar Energy Materials and Solar Cells. 100: 97. doi:10.1016/j.solmat.2011.12.022.
  8. Scharber, M. C.; Mühlbacher, D.; Koppe, M.; Denk, P.; Waldauf, C.; Heeger, A. J.; Brabec, C. J. (2006). "Design Rules for Donors in Bulk-Heterojunction Solar Cells—Towards 10 % Energy-Conversion Efficiency" (PDF). Advanced Materials. 18 (6): 789. Bibcode:2006AdM....18..789S. doi:10.1002/adma.200501717. S2CID   13842344.
  9. 1 2 You, Jingbi; Dou, Letian; Yoshimura, Ken; Kato, Takehito; Ohya, Kenichiro; Moriarty, Tom; Emery, Keith; Chen, Chun-Chao (5 February 2013). "A polymer tandem solar cell with 10.6% power conversion efficiency". Nature Communications. 4: 1446. Bibcode:2013NatCo...4.1446Y. doi:10.1038/ncomms2411. PMC   3660643 . PMID   23385590.
  10. "PolyU researchers achieve record 19.31% efficiency with organic solar cells". Hong Kong Polytechnic University. 25 May 2023. Retrieved 7 June 2023.
  11. Rivers P. N. (2007). Leading edge research in solar energy. Nova Science Publishers. ISBN   978-1600213366.
  12. 1 2 3 McGehee D.G.; Topinka M.A. (2006). "Solar cells: Pictures from the blended zone". Nature Materials. 5 (9): 675–676. Bibcode:2006NatMa...5..675M. doi:10.1038/nmat1723. PMID   16946723. S2CID   43074502.
  13. 1 2 3 4 Nelson J. (2002). "Organic photovoltaic films". Current Opinion in Solid State and Materials Science. 6 (1): 87–95. Bibcode:2002COSSM...6...87N. doi:10.1016/S1359-0286(02)00006-2.
  14. 1 2 3 4 Halls J.J.M.; Friend R.H. (2001). Archer M.D.; Hill R.D. (eds.). Clean electricity from photovoltaics. London: Imperial College Press. pp. 377–445. ISBN   978-1860941610.
  15. 1 2 Hoppe, H. & Sariciftci, N. S. (2004). "Organic solar cells: An overview". J. Mater. Res. 19 (7): 1924–1945. Bibcode:2004JMatR..19.1924H. doi:10.1557/JMR.2004.0252. S2CID   22455511.
  16. Zyga, Lisa. "Inverted polymer solar cell efficiency sets world record". Phys.org. Retrieved 18 February 2015.
  17. Pivrikas, A.; Sarıçiftçi, N. S.; Juška, G.; Österbacka, R. (2007). "A review of charge transport and recombination in polymer/fullerene organic solar cells" (PDF). Progress in Photovoltaics: Research and Applications. 15 (8): 677. doi: 10.1002/pip.791 .
  18. Tessler, Nir; Preezant, Yevgeni; Rappaport, Noam; Roichman, Yohai (2009). "Charge Transport in Disordered Organic Materials and Its Relevance to Thin-Film Devices: A Tutorial Review" (PDF). Advanced Materials. 21 (27): 2741. Bibcode:2009AdM....21.2741T. doi:10.1002/adma.200803541. S2CID   25748928.
  19. 1 2 Kearns D.; Calvin M. (1958). "Photovoltaic Effect and Photoconductivity in Laminated Organic Systems". J. Chem. Phys. 29 (4): 950–951. Bibcode:1958JChPh..29..950K. doi:10.1063/1.1744619. S2CID   95918786.
  20. Ghosh A.K.; et al. (1974). "Photovoltaic and rectification properties of Al/Mg phthalocyanine/Ag Schottky-barrier cells". J. Appl. Phys. 45 (1): 230–236. Bibcode:1974JAP....45..230G. doi:10.1063/1.1662965.
  21. Weinberger B.R.; et al. (1982). "Polyacetylene photovoltaic devices". Synth. Met. 4 (3): 187–197. doi:10.1016/0379-6779(82)90012-1.
  22. Glenis S, et al. (1986). "Influence of the doping on the photovoltaic properties of thin films of poly-3-methylthiophene". Thin Solid Films. 139 (3): 221–231. Bibcode:1986TSF...139..221G. doi:10.1016/0040-6090(86)90053-2.
  23. Karg S, et al. (1993). "Electrical and optical characterization of poly(phenylene-vinylene) light emitting diodes". Synthetic Metals. 54 (1–3): 427–433. doi:10.1016/0379-6779(93)91088-J.
  24. Sariciftci, N. S.; Braun, D.; Zhang, C.; Srdanov, V. I.; Heeger, A. J.; Stucky, G.; Wudl, F. (1993). "Semiconducting polymer-buckminsterfullerene heterojunctions: Diodes, photodiodes, and photovoltaic cells". Applied Physics Letters. 62 (6): 585–587. Bibcode:1993ApPhL..62..585S. doi:10.1063/1.108863.
  25. Halls J.J.M.; et al. (1996). "Exciton diffusion and dissociation in a poly(p-phenylenevinylene)/C60 heterojunction photovoltaic cell". Appl. Phys. Lett. 68 (22): 3120–3122. Bibcode:1996ApPhL..68.3120H. doi:10.1063/1.115797.
  26. Tang C.W. (1986). "Two-layer organic photovoltaic cell". Appl. Phys. Lett. 48 (2): 183–185. Bibcode:1986ApPhL..48..183T. doi:10.1063/1.96937.
  27. Halls J.J.M.; et al. (1997). "The photovoltaic effect in a poly(p-phenylenevinylene)/perylene heterojunction". Synth. Met. 85 (1–3): 1307–1308. doi:10.1016/S0379-6779(97)80252-4.
  28. Imec achieves record 8.4% efficiency in fullerene-free organic solar cells. Rdmag.com. Retrieved on 2015-11-12.
  29. Cao, Weiran; Xue, Jiangeng (2014). "Recent progress in organic photovoltaics: device architecture and optical design". Energy & Environmental Science. 7 (7): 2123. doi:10.1039/C4EE00260A.
  30. Heeger, Alan J. (January 2014). "25th Anniversary Article: Bulk Heterojunction Solar Cells: Understanding the Mechanism of Operation". Advanced Materials. 26 (1): 10–28. Bibcode:2014AdM....26...10H. doi:10.1002/adma.201304373. PMID   24311015. S2CID   6693600.
  31. Scharber, M.C.; Sariciftci, N.S. (December 2013). "Efficiency of bulk-heterojunction organic solar cells". Progress in Polymer Science. 38 (12): 1929–1940. doi:10.1016/j.progpolymsci.2013.05.001. PMC   3837184 . PMID   24302787.
  32. 1 2 Yang F, et al. (2005). "Controlled growth of a molecular bulk heterojunction photovoltaic cell". Nature Materials. 4 (1): 37–41. Bibcode:2005NatMa...4...37Y. doi:10.1038/nmat1285. S2CID   137668833.
  33. Yu G, et al. (1995). "Polymer Photovoltaic Cells: Enhanced Efficiencies via a Network of Internal Donor-Acceptor Heterojunctions". Science. 270 (5243): 1789–1791. Bibcode:1995Sci...270.1789Y. CiteSeerX   10.1.1.320.7494 . doi:10.1126/science.270.5243.1789. S2CID   135489167.
  34. Yu G, et al. (1998). "Large-Area, Full-Color Image Sensors Made with Semiconducting Polymers". Advanced Materials. 10 (17): 1431–1434. doi:10.1002/(SICI)1521-4095(199812)10:17<1431::AID-ADMA1431>3.0.CO;2-4.
  35. Kaneko, Masao & Okura, Ichiro (2002). Photocatalysis: Science and Technology. Springer. ISBN   978-3-540-43473-3.
  36. He, Zhicai; Xiao, Biao; Liu, Feng; Wu, Hongbin; Yang, Yali; Xiao, Steven; Wang, Cheng; Russell, Thomas P.; Cao, Yong (2015-03-01). "Single-junction polymer solar cells with high efficiency and photovoltage". Nature Photonics. 9 (3): 174–179. Bibcode:2015NaPho...9..174H. doi:10.1038/nphoton.2015.6. S2CID   119702307.
  37. Halls J.J.M.; et al. (1995). "Efficient photodiodes from interpenetrating polymer networks". Nature. 376 (6540): 498–500. Bibcode:1995Natur.376..498H. doi:10.1038/376498a0. S2CID   4336280.
  38. Seraphin B.O., ed. (1979). Solar energy conversion: solid-state physics aspects. Topics in applied physics. Vol. 31. doi:10.1007/3-540-09224-2. ISBN   978-3-540-35369-0.
  39. Sauvé, Geneviève; Fernando, Roshan (2015-09-09). "Beyond Fullerenes: Designing Alternative Molecular Electron Acceptors for Solution-Processable Bulk Heterojunction Organic Photovoltaics". The Journal of Physical Chemistry Letters. 6 (18): 3770–3780. doi:10.1021/acs.jpclett.5b01471. PMID   26722869.
  40. Pandey, Richa; Holmes, Russell J. (2010). "Organic Photovoltaic Cells Based on Continuously Graded Donor–Acceptor Heterojunctions". IEEE Journal of Selected Topics in Quantum Electronics. 16 (6): 1537–1543. Bibcode:2010IJSTQ..16.1537P. doi:10.1109/jstqe.2010.2049256. S2CID   41396369.
  41. "Organic Photovoltaic Solar Cells using Graded Heterojunction Technology". University of Minnesota.
  42. Holmes, Russel; Pandey, Richa (2010). "Organic Photovoltaic Cells Based on Continuously Graded Donor–Acceptor Heterojunctions". IEEE Journal of Selected Topics in Quantum Electronics. 16 (6): 7. Bibcode:2010IJSTQ..16.1537P. doi:10.1109/JSTQE.2010.2049256. S2CID   41396369.
  43. Glöcklhofer, Florian; Lumpi, Daniel; Kohlstädt, Markus; Yurchenko, Olena; Würfel, Uli; Fröhlich, Johannes (2015). "Towards continuous junction (CJ) organic electronic devices: Fast and clean post-polymerization modification by oxidation using dimethyldioxirane (DMDO)". Reactive and Functional Polymers. 86: 16–26. doi:10.1016/j.reactfunctpolym.2014.10.006. hdl: 10044/1/87961 .
  44. Clarke, Tracey M.; Ballantyne, Amy M.; Nelson, Jenny; Bradley, Donal D. C.; Durrant, James R. (2008). "Free Energy Control of Charge Photogeneration in Polythiophene/Fullerene Solar Cells: The Influence of Thermal Annealing on P3HT/PCBM Blends". Advanced Functional Materials. 18 (24): 4029. doi:10.1002/adfm.200800727. S2CID   96860273.
  45. Xu, Zheng; Chen, Li-Min; Yang, Guanwen; Huang, Chun-Hao; Hou, Jianhui; Wu, Yue; Li, Gang; Hsu, Chain-Shu; Yang, Yang (2009). "Vertical Phase Separation in Poly(3-hexylthiophene): Fullerene Derivative Blends and its Advantage for Inverted Structure Solar Cells" (PDF). Advanced Functional Materials. 19 (8): 1227. doi:10.1002/adfm.200801286. S2CID   9366182.
  46. Van Bavel, Svetlana; Sourty, Erwan; De With, Gijsbertus; Frolic, Kai; Loos, Joachim (2009). "Relation between Photoactive Layer Thickness, 3D Morphology, and Device Performance in P3HT/PCBM Bulk-Heterojunction Solar Cells". Macromolecules. 42 (19): 7396. Bibcode:2009MaMol..42.7396V. doi:10.1021/ma900817t.
  47. Troshin, Pavel A.; Hoppe, Harald; Renz, Joachim; Egginger, Martin; Mayorova, Julia Yu.; Goryachev, Andrey E.; Peregudov, Alexander S.; Lyubovskaya, Rimma N.; Gobsch, Gerhard; Sariciftci, N. Serdar; Razumov, Vladimir F. (2009). "Material Solubility-Photovoltaic Performance Relationship in the Design of Novel Fullerene Derivatives for Bulk Heterojunction Solar Cells" (PDF). Advanced Functional Materials. 19 (5): 779. doi:10.1002/adfm.200801189. S2CID   97354654.
  48. 1 2 Moulé, A.J. & K. Meerholz (2008). "Controlling Morphology in Polymer–Fullerene Mixtures" (PDF). Advanced Materials. 20 (2): 240. Bibcode:2008AdM....20..240M. doi:10.1002/adma.200701519. S2CID   137313225. Archived from the original (PDF) on 2014-09-03. Retrieved 2017-02-26.
  49. Dang, Minh Trung; Wantz, Guillaume; Bejbouji, Habiba; Urien, Mathieu; Dautel, Olivier J.; Vignau, Laurence; Hirsch, Lionel (2011). "Polymeric solar cells based on P3HT:PCBM: Role of the casting solvent". Solar Energy Materials and Solar Cells. 95 (12): 3408. doi:10.1016/j.solmat.2011.07.039.
  50. Nagarjuna, Gavvalapalli; Venkataraman, Dhandapani (2012). "Strategies for controlling the active layer morphologies in OPVs". Journal of Polymer Science Part B: Polymer Physics. 50 (15): 1045–1056. Bibcode:2012JPoSB..50.1045N. doi: 10.1002/polb.23073 .
  51. Matthias A. Ruderer & Peter Müller-Buschbaum (2011). "Morphology of polymer-based bulk heterojunction films for organic photovoltaics". Soft Matter. 7 (12): 5482. Bibcode:2011SMat....7.5482R. doi:10.1039/C0SM01502D.
  52. Treat, Neil D.; Brady, Michael A.; Smith, Gordon; Toney, Michael F.; Kramer, Edward J.; Hawker, Craig J.; Chabinyc, Michael L. (2011). "Interdiffusion of PCBM and P3HT Reveals Miscibility in a Photovoltaically Active Blend". Advanced Energy Materials. 1: 82. doi:10.1002/aenm.201000023. S2CID   153383.; Treat, Neil D.; Brady, Michael A.; Smith, Gordon; Toney, Michael F.; Kramer, Edward J.; Hawker, Craig J.; Chabinyc, Michael L. (2011). "Correction: Interdiffusion of PCBM and P3HT Reveals Miscibility in a Photovoltaically Active Blend (Adv. Energy Mater. 2/2011)". Advanced Energy Materials. 1 (2): 145. doi: 10.1002/aenm.201190008 .
  53. Kozub, Derek R.; Vakhshouri, Kiarash; Orme, Lisa M.; Wang, Cheng; Hexemer, Alexander; Gomez, Enrique D. (2011). "Polymer Crystallization of Partially Miscible Polythiophene/Fullerene Mixtures Controls Morphology". Macromolecules. 44 (14): 5722. Bibcode:2011MaMol..44.5722K. doi:10.1021/ma200855r.
  54. Jo, Jang; Kim, Seok-Soon; Na, Seok-In; Yu, Byung-Kwan; Kim, Dong-Yu (2009). "Time-Dependent Morphology Evolution by Annealing Processes on Polymer:Fullerene Blend Solar Cells". Advanced Functional Materials. 19 (6): 866. doi:10.1002/adfm.200800968. S2CID   94880690.
  55. Collins, Brian A.; Gann, Eliot; Guignard, Lewis; He, Xiaoxi; McNeill, Christopher R.; Ade, Harald (2010). "Molecular Miscibility of Polymer−Fullerene Blends" (PDF). The Journal of Physical Chemistry Letters. 1 (21): 3160. doi:10.1021/jz101276h. Archived from the original (PDF) on February 1, 2022. Supporting information [ permanent dead link ]
  56. Tremolet De Villers, Bertrand; Tassone, Christopher J.; Tolbert, Sarah H.; Schwartz, Benjamin J. (2009). "Improving the Reproducibility of P3HT:PCBM Solar Cells by Controlling the PCBM/Cathode Interface". The Journal of Physical Chemistry C. 113 (44): 18978. CiteSeerX   10.1.1.476.2064 . doi:10.1021/jp9082163.
  57. Yin, W.; Dadmun, M. (2011). "A New Model for the Morphology of P3HT/PCBM Organic Photovoltaics from Small-Angle Neutron Scattering: Rivers and Streams". ACS Nano. 5 (6): 4756–4768. doi:10.1021/nn200744q. PMID   21563761.
  58. 1 2 Forrest S.R. (2004). "The path to ubiquitous and low-cost organic electronic appliances on plastic". Nature. 428 (6986): 911–918. Bibcode:2004Natur.428..911F. doi:10.1038/nature02498. PMID   15118718. S2CID   1099780.
  59. Nilsson, Svante; Bernasik, Andrzej; Budkowski, Andrzej; Moons, Ellen (2007). "Morphology and Phase Segregation of Spin-Casted Films of Polyfluorene/PCBM Blends". Macromolecules. 40 (23): 8291. Bibcode:2007MaMol..40.8291N. doi:10.1021/ma070712a.
  60. Lecover, Rachel; Williams, Nicholas; Markovic, Nina; Reich, Daniel H.; Naiman, Daniel Q.; Katz, Howard E. (2012). "Next-Generation Polymer Solar Cell Materials: Designed Control of Interfacial Variables". ACS Nano. 6 (4): 2865–70. doi:10.1021/nn301140w. PMID   22444948.
  61. Pivrikas, Almantas; Neugebauer, Helmut; Sariciftci, Niyazi Serdar (2011). "Influence of processing additives to nano-morphology and efficiency of bulk-heterojunction solar cells: A comparative review". Solar Energy. 85 (6): 1226. Bibcode:2011SoEn...85.1226P. doi:10.1016/j.solener.2010.10.012.
  62. Yao, Yan; Hou, Jianhui; Xu, Zheng; Li, Gang; Yang, Yang (2008). "Effects of Solvent Mixtures on the Nanoscale Phase Separation in Polymer Solar Cells" (PDF). Advanced Functional Materials. 18 (12): 1783. doi:10.1002/adfm.200701459. S2CID   982890.
  63. Lee, Jae Kwan; Ma, Wan Li; Brabec, Christoph J.; Yuen, Jonathan; Moon, Ji Sun; Kim, Jin Young; Lee, Kwanghee; Bazan, Guillermo C.; Heeger, Alan J. (2008). "Processing Additives for Improved Efficiency from Bulk Heterojunction Solar Cells". Journal of the American Chemical Society. 130 (11): 3619–23. doi:10.1021/ja710079w. PMID   18288842.
  64. Rogers, James T.; Schmidt, Kristin; Toney, Michael F.; Bazan, Guillermo C.; Kramer, Edward J. (2012). "Time-Resolved Structural Evolution of Additive-Processed Bulk Heterojunction Solar Cells". Journal of the American Chemical Society. 134 (6): 2884–7. doi:10.1021/ja2104747. PMID   22276735.
  65. Carr Hoi Yi Ho; Qi Dong; Hang Yin; Winky Wing Ki Leung; Qingdan Yang; Harrison Ka Hin Lee; Sai Wing Tsang; Shu Kong So (2015). "Impact of Solvent Additive on Carrier Transport in Polymer:Fullerene Bulk Heterojunction Photovoltaic Cells". Advanced Materials Interfaces. 2 (12): n/a. doi:10.1002/admi.201500166. S2CID   53487971.
  66. Liang, Yongye; Xu, Zheng; Xia, Jiangbin; Tsai, Szu-Ting; Wu, Yue; Li, Gang; Ray, Claire; Yu, Luping (2010). "For the Bright Future—Bulk Heterojunction Polymer Solar Cells with Power Conversion Efficiency of 7.4%". Advanced Materials. 22 (20): E135–8. Bibcode:2010AdM....22E.135L. doi:10.1002/adma.200903528. PMID   20641094. S2CID   36190616.
  67. Li, Weiwei; Zhou, Yi; Viktor Andersson, B.; Mattias Andersson, L.; Thomann, Yi; Veit, Clemens; Tvingstedt, Kristofer; Qin, Ruiping; Bo, Zhishan; Inganäs, Olle; Würfel, Uli; Zhang, Fengling (2011). "The Effect of additive on performance and shelf-stability of HSX-1/PCBM photovoltaic devices". Organic Electronics. 12 (9): 1544. doi:10.1016/j.orgel.2011.05.028.
  68. van Franekar, Jacobus; Turbiez, Mathieu; Li, Weiwei; Wienk, Martijn; Janssen, René (6 February 2015). "A real-time study of the benefits of co-solvents in polymer solar cell processing" (PDF). Nature Communications. 6: 6229. Bibcode:2015NatCo...6.6229V. doi: 10.1038/ncomms7229 . PMID   25656313.
  69. Beaujuge, P.M. & J.M.J. Fréchet (2011). "Molecular Design and Ordering Effects in π-Functional Materials for Transistor and Solar Cell Applications". Journal of the American Chemical Society. 133 (50): 20009–29. doi:10.1021/ja2073643. PMID   21999757.
  70. Troshin, Pavel A.; Koeppe, Robert; Peregudov, Alexander S.; Peregudova, Svetlana M.; Egginger, Martin; Lyubovskaya, Rimma N.; Sariciftci, N. Serdar (2007). "Supramolecular Association of Pyrrolidinofullerenes Bearing Chelating Pyridyl Groups and Zinc Phthalocyanine for Organic Solar Cells". Chemistry of Materials. 19 (22): 5363. doi:10.1021/cm071243u.
  71. Tevis, Ian D.; Tsai, Wei-Wen; Palmer, Liam C.; Aytun, Taner; Stupp, Samuel I. (2012). "Grooved Nanowires from Self-Assembling Hairpin Molecules for Solar Cells". ACS Nano. 6 (3): 2032–40. doi:10.1021/nn203328n. PMID   22397738.
  72. Dössel, L.F.; Kamm, Valentin; Howard, Ian A.; Laquai, Frédéric; Pisula, Wojciech; Feng, Xinliang; Li, Chen; Takase, Masayoshi; et al. (2012). "Synthesis and Controlled Self-Assembly of Covalently Linked Hexa-peri-hexabenzocoronene/Perylene Diimide Dyads as Models To Study Fundamental Energy and Electron Transfer Processes". Journal of the American Chemical Society. 134 (13): 5876–86. doi:10.1021/ja211504a. PMID   22394147.
  73. Miyanishi, Shoji; Zhang, Yue; Tajima, Keisuke; Hashimoto, Kazuhito (2010). "Fullerene attached all-semiconducting diblock copolymers for stable single-component polymer solar cells". Chemical Communications. 46 (36): 6723–5. doi:10.1039/C0CC01819H. PMID   20717605.
  74. Sary, Nicolas; Richard, Fanny; Brochon, Cyril; Leclerc, Nicolas; Lévêque, Patrick; Audinot, Jean-Nicolas; Berson, Solenn; Heiser, Thomas; et al. (2010). "A New Supramolecular Route for Using Rod-Coil Block Copolymers in Photovoltaic Applications" (PDF). Advanced Materials. 22 (6): 763–8. Bibcode:2010APS..MAR.C1002M. doi:10.1002/adma.200902645. PMID   20217786. S2CID   205234659.
  75. Lin, Ying; Lim, Jung Ah; Wei, Qingshuo; Mannsfeld, Stefan C. B.; Briseno, Alejandro L.; Watkins, James J. (2012). "Cooperative Assembly of Hydrogen-Bonded Diblock Copolythiophene/Fullerene Blends for Photovoltaic Devices with Well-Defined Morphologies and Enhanced Stability". Chemistry of Materials. 24 (3): 622. doi:10.1021/cm203706h.
  76. Topham, Paul D.; Parnell, Andrew J.; Hiorns, Roger C. (2011). "Block copolymer strategies for solar cell technology". Journal of Polymer Science Part B: Polymer Physics. 49 (16): 1131. Bibcode:2011JPoSB..49.1131T. doi:10.1002/polb.22302.
  77. Barrau, Sophie; Heiser, Thomas; Richard, Fanny; Brochon, Cyril; Ngov, Chheng; Van De Wetering, Karin; Hadziioannou, Georges; Anokhin, Denis V.; Ivanov, Dimitri A. (2008). "Self-Assembling of Novel Fullerene-Grafted Donor–Acceptor Rod−Coil Block Copolymers". Macromolecules. 41 (7): 2701. Bibcode:2008MaMol..41.2701B. doi:10.1021/ma7022099.
  78. 1 2 3 4 Xia, Xinyuan; Wang, Shanshan; Jia, Yi; Bian, Zuqiang; Wu, Dehai; Zhang, Luhui; Cao, Anyuan; Huang, Chunhui (2010). "Infrared-transparent polymer solar cells". Journal of Materials Chemistry. 20 (39): 8478. doi:10.1039/c0jm02406f. ISSN   0959-9428.
  79. Wang, Xiangjun; Perzon, Erik; Delgado, Juan Luis; de la Cruz, Pilar; Zhang, Fengling; Langa, Fernando; Andersson, Mats; Inganäs, Olle (2004-11-22). "Infrared photocurrent spectral response from plastic solar cell with low-band-gap polyfluorene and fullerene derivative". Applied Physics Letters. 85 (21): 5081–5083. Bibcode:2004ApPhL..85.5081W. doi: 10.1063/1.1825070 . ISSN   0003-6951.
  80. Betancur, Rafael; Romero-Gomez, Pablo; Martinez-Otero, Alberto; Elias, Xavier; Maymó, Marc; Martorell, Jordi (December 2013). "Transparent polymer solar cells employing a layered light-trapping architecture". Nature Photonics. 7 (12): 995–1000. Bibcode:2013NaPho...7..995B. doi:10.1038/nphoton.2013.276. ISSN   1749-4885. S2CID   16747502.
  81. 1 2 Romero-Gómez, Pablo; Pastorelli, Francesco; Mantilla-Pérez, Paola; Mariano, Marina; Martínez-Otero, Alberto; Elias, Xavier; Betancur, Rafael; Martorell, Jordi (2015-02-16). "Semi-transparent polymer solar cells". Journal of Photonics for Energy. 5 (1): 057212. doi: 10.1117/1.JPE.5.057212 . hdl: 2117/107388 . ISSN   1947-7988.
  82. 1 2 Chen, Chun-Chao; Dou, Letian; Zhu, Rui; Chung, Choong-Heui; Song, Tze-Bin; Zheng, Yue Bing; Hawks, Steve; Li, Gang; Weiss, Paul S.; Yang, Yang (2012-08-28). "Visibly Transparent Polymer Solar Cells Produced by Solution Processing". ACS Nano. 6 (8): 7185–7190. doi:10.1021/nn3029327. ISSN   1936-0851. PMID   22789123.
  83. 1 2 Chen, Kung-Shih; Salinas, José-Francisco; Yip, Hin-Lap; Huo, Lijun; Hou, Jianhui; Jen, Alex K.-Y. (2012). "Semi-transparent polymer solar cells with 6% PCE, 25% average visible transmittance and a color rendering index close to 100 for power generating window applications". Energy & Environmental Science. 5 (11): 9551. doi:10.1039/c2ee22623e. ISSN   1754-5692.
  84. Marcus, Jennifer (July 20, 2012). "Scientists create highly transparent solar cells for windows that generate electricity". Phys.org. Retrieved 2012-07-23.
  85. Zhou, Erjun; Nakano, Masahiro; Izawa, Seiichiro; Cong, Junzi; Osaka, Itaru; Takimiya, Kazuo; Tajima, Keisuke (18 August 2014). "All-Polymer Solar Cell with High Near-Infrared Response Based on a Naphthodithiophene Diimide (NDTI) Copolymer". ACS Macro Lett. 3 (9): 872–875. doi:10.1021/mz5004272. PMID   35596351.
  86. Wang, Wei; Yan, Cenqi; Lau, Tsz-Ki; Wang, Jiayu; Liu, Kuan; Fan, Yan; Lu, Xinhui; Zhan, Xiaowei (2017). "Fused Hexacyclic Nonfullerene Acceptor with Strong Near-Infrared Absorption for Semitransparent Organic Solar Cells with 9.77% Efficiency". Advanced Materials. 29 (31): 1701308. Bibcode:2017AdM....2901308W. doi:10.1002/adma.201701308. PMID   28608531. S2CID   205280045.
  87. 1 2 3 Deibel, Carsten; Dyakonov, Vladimir (2010-09-01). "Polymer–fullerene bulk heterojunction solar cells". Reports on Progress in Physics. 73 (9): 096401. arXiv: 1003.0359 . Bibcode:2010RPPh...73i6401D. doi:10.1088/0034-4885/73/9/096401. ISSN   0034-4885. S2CID   118855668.
  88. 1 2 3 4 5 6 Hoppe, Harald; Sariciftci, Niyazi Serdar (July 2004). "Organic solar cells: An overview". Journal of Materials Research. 19 (7): 1924–1945. Bibcode:2004JMatR..19.1924H. doi:10.1557/JMR.2004.0252. ISSN   0884-2914. S2CID   22455511.
  89. Xue, Rongming; Zhang, Jingwen; Li, Yaowen; Li, Yongfang (2018). "Organic Solar Cell Materials toward Commercialization". Small. 14 (41): e1801793. doi:10.1002/smll.201801793. PMID   30106505. S2CID   51975017.
  90. 1 2 Guo, Xugang; Zhou, Nanjia; Lou, Sylvia; Smith, Jeremy; Tice, Daniel; Hennek, Jonathan; Ortiz, Rocío; López Navarrete, Juan; Li, Shuyou; Strzalka, Joseph; Chen, Lin; Chang, Robert; Facchetti, Antonio; Marks, Tobin (11 August 2013). "Polymer solar cells with enhanced fill factors". Nature Photonics. 7 (10): 825. Bibcode:2013NaPho...7..825G. doi:10.1038/nphoton.2013.207. S2CID   15817634.
  91. For a similar graph, see: Hoppe, Harald; Sariciftci, N. Serdar (2008). "Polymer Solar Cells". Photoresponsive Polymers II. pp. 1–86 (4). doi:10.1007/12_2007_121. ISBN   978-3-540-69452-6.
  92. Kevin Bullis. Mass Production of Plastic Solar Cells, Technology Review Magazine, October 17, 2008.
  93. Krebs, Frederik; Tromholt, Thomas; Jørgensen, Mikkel (4 May 2010). "Upscaling of polymer solar cell fabrication using full roll-to-roll processing". Nanoscale. 2 (6): 873–86. Bibcode:2010Nanos...2..873K. doi:10.1039/B9NR00430K. PMID   20648282.
  94. 1 2 MacKenzie, Roderick C. I.; Shuttle, Christopher G.; Chabinyc, Michael L.; Nelson, Jenny (2012). "Extracting Microscopic Device Parameters from Transient Photocurrent Measurements of P3HT:PCBM Solar Cells". Advanced Energy Materials. 2 (6): 662. doi:10.1002/aenm.201100709. S2CID   98547540.
  95. Chiu, S.W.; Lin, L.Y.; Lin, H.W.; Chen, Y.H.; Huang, Z.Y.; Lin, Y.T.; Lin, F.; Liu, Y.H.; Wong, K.T. (2012). "A donor-acceptor-acceptor molecule for vacuum-processed organic solar cells with a power conversion efficiency of 6.4%". Chemical Communications. 48 (13): 1857–9. doi:10.1039/C2CC16390J. PMID   22167175.
  96. Li, Bin; Wang, Liduo; Kang, Bonan; Wang, Peng; Qiu, Yong (2006). "Review of recent progress in solid-state dye-sensitized solar cells". Solar Energy Materials and Solar Cells. 90 (5): 549–573. doi:10.1016/j.solmat.2005.04.039.
  97. Mihailetchi, V. D.; Xie, H. X.; de Boer, B.; Koster, L. J. A.; Blom, P. W. M. (2006-03-20). "Charge Transport and Photocurrent Generation in Poly(3-hexylthiophene): Methanofullerene Bulk-Heterojunction Solar Cells" (PDF). Advanced Functional Materials. 16 (5): 699–708. doi:10.1002/adfm.200500420. hdl: 11370/aa761002-7f50-41e4-b6cb-8c908610accd . S2CID   55436282.
  98. Bartelt, Jonathan A.; Lam, David; Burke, Timothy M.; Sweetnam, Sean M.; McGehee, Michael D. (2015-08-01). "Charge-Carrier Mobility Requirements for Bulk Heterojunction Solar Cells with High Fill Factor and External Quantum Efficiency >90%". Advanced Energy Materials. 5 (15): 1500577. doi:10.1002/aenm.201500577. S2CID   14735539.
  99. Peumans P, et al. (2003). "Efficient bulk heterojunction photovoltaic cells using small-molecular-weight organic thin films". Nature. 425 (6954): 158–162. Bibcode:2003Natur.425..158P. doi:10.1038/nature01949. PMID   12968174. S2CID   4361523.
  100. Park, Yoonseok; Vandewal, Koen; Leo, Karl (2018-07-05). "Optical In-Coupling in Organic Solar Cells". Small Methods. 2 (10): 1800123. doi:10.1002/smtd.201800123. ISSN   2366-9608. S2CID   139574649.
  101. Kim, Yong Hyun; Sachse, Christoph; Machala, Michael L.; May, Christian; Müller-Meskamp, Lars; Leo, Karl (2011-03-22). "Highly Conductive PEDOT:PSS Electrode with Optimized Solvent and Thermal Post-Treatment for ITO-Free Organic Solar Cells". Advanced Functional Materials. 21 (6): 1076–1081. doi:10.1002/adfm.201002290. ISSN   1616-3028. S2CID   136583700.
  102. Park, Yoonseok; Bormann, Ludwig; Müller-Meskamp, Lars; Vandewal, Koen; Leo, Karl (2016-09-01). "Efficient flexible organic photovoltaics using silver nanowires and polymer based transparent electrodes". Organic Electronics. 36: 68–72. doi:10.1016/j.orgel.2016.05.032.
  103. Kaltenbrunner, Martin; White, Matthew S.; Głowacki, Eric D.; Sekitani, Tsuyoshi; Someya, Takao; Sariciftci, Niyazi Serdar; Bauer, Siegfried (2012-04-03). "Ultrathin and lightweight organic solar cells with high flexibility". Nature Communications. 3: 770. Bibcode:2012NatCo...3..770K. doi:10.1038/ncomms1772. ISSN   2041-1723. PMC   3337988 . PMID   22473014.
  104. Park, Yoonseok; Müller-Meskamp, Lars; Vandewal, Koen; Leo, Karl (2016-06-20). "PEDOT:PSS with embedded TiO2 nanoparticles as light trapping electrode for organic photovoltaics". Applied Physics Letters. 108 (25): 253302. Bibcode:2016ApPhL.108y3302P. doi: 10.1063/1.4954902 . ISSN   0003-6951.
  105. Park, Yoonseok; Berger, Jana; Will, Paul-Anton; Soldera, Marcos; Glatz, Bernhard; Müller-Meskamp, Lars; Taretto, Kurt; Fery, Andreas; Lasagni, Andrés Fabián (2016-01-01). Kafafi, Zakya H; Lane, Paul A; Samuel, Ifor D. W (eds.). "Light trapping for flexible organic photovoltaics". Organic Photovoltaics XVII. 9942: 994211–994211–9. Bibcode:2016SPIE.9942E..11P. doi:10.1117/12.2229582. S2CID   138521932.
  106. Park, Yoonseok; Berger, Jana; Tang, Zheng; Müller-Meskamp, Lars; Lasagni, Andrés Fabián; Vandewal, Koen; Leo, Karl (2016-08-29). "Flexible, light trapping substrates for organic photovoltaics". Applied Physics Letters. 109 (9): 093301. Bibcode:2016ApPhL.109i3301P. doi: 10.1063/1.4962206 . ISSN   0003-6951.
  107. Müller-Meskamp, Lars; Kim, Yong Hyun; Roch, Teja; Hofmann, Simone; Scholz, Reinhard; Eckardt, Sebastian; Leo, Karl; Lasagni, Andrés Fabián (2012-02-14). "Efficiency Enhancement of Organic Solar Cells by Fabricating Periodic Surface Textures using Direct Laser Interference Patterning". Advanced Materials. 24 (7): 906–910. Bibcode:2012AdM....24..906M. doi:10.1002/adma.201104331. ISSN   1521-4095. PMID   22403830. S2CID   19890510.
  108. Park, Yoonseok; Nehm, Frederik; Müller-Meskamp, Lars; Vandewal, Koen; Leo, Karl (2016-05-16). "Optical display film as flexible and light trapping substrate for organic photovoltaics". Optics Express. 24 (10): A974-80. Bibcode:2016OExpr..24A.974P. doi: 10.1364/OE.24.00A974 . ISSN   1094-4087. PMID   27409970.
  109. Beiley, Zach M.; McGehee, Michael D. (2012). "Modeling low cost hybrid tandem photovoltaics with the potential for efficiencies exceeding 20%". Energy & Environmental Science. 5 (11): 9173. doi:10.1039/C2EE23073A.
  110. Margulis, George Y.; Christoforo, M. Greyson; Lam, David; Beiley, Zach M.; Bowring, Andrea R.; Bailie, Colin D.; Salleo, Alberto; McGehee, Michael D. (2013-12-01). "Spray Deposition of Silver Nanowire Electrodes for Semitransparent Solid-State Dye-Sensitized Solar Cells". Advanced Energy Materials. 3 (12): 1657–1663. doi:10.1002/aenm.201300660. S2CID   8781905.
  111. Vijay, Venugopalan; Rao, Arun D.; Narayan, K. S. (2011-04-15). "In situ studies of strain dependent transport properties of conducting polymers on elastomeric substrates". Journal of Applied Physics. 109 (8): 084525–084525–6. Bibcode:2011JAP...109h4525V. doi:10.1063/1.3580514. ISSN   0021-8979.
  112. Bruner, Christopher; Miller, Nichole C.; McGehee, Michael D.; Dauskardt, Reinhold H. (2013-01-17). "Molecular Intercalation and Cohesion of Organic Bulk Heterojunction Photovoltaic Devices". Advanced Functional Materials. 23 (22): 2863–2871. doi:10.1002/adfm.201202969. ISSN   1616-301X. S2CID   93941136.
  113. Bruner, Christopher; Dauskardt, Reinhold (2014-01-24). "Role of Molecular Weight on the Mechanical Device Properties of Organic Polymer Solar Cells". Macromolecules. 47 (3): 1117–1121. Bibcode:2014MaMol..47.1117B. doi:10.1021/ma402215j. ISSN   0024-9297.
  114. Brand, Vitali; Bruner, Christopher; Dauskardt, Reinhold H. (April 2012). "Cohesion and device reliability in organic bulk heterojunction photovoltaic cells". Solar Energy Materials and Solar Cells. 99: 182–189. doi:10.1016/j.solmat.2011.11.035. ISSN   0927-0248.
  115. Stafford, Christopher M.; Harrison, Christopher; Beers, Kathryn L.; Karim, Alamgir; Amis, Eric J.; VanLandingham, Mark R.; Kim, Ho-Cheol; Volksen, Willi; Miller, Robert D.; Simonyi, Eva E. (2004-07-11). "A buckling-based metrology for measuring the elastic moduli of polymeric thin films". Nature Materials. 3 (8): 545–550. Bibcode:2004NatMa...3..545S. doi:10.1038/nmat1175. ISSN   1476-1122. PMID   15247909. S2CID   6413911.
  116. Choi, Joonhyeong; Kim, Wansun; Kim, Seonha; Kim, Taek-Soo; Kim, Bumjoon J. (2019). "Influence of Acceptor Type and Polymer Molecular Weight on the Mechanical Properties of Polymer Solar Cells". Chemistry of Materials. 31 (21): 9057–9069. doi:10.1021/acs.chemmater.9b03333. S2CID   208694659.
  117. 1 2 3 4 Yan, He; Facchetti, Antonio; Guo, Xugang; Tan, Huei Shuan; Zhang, Jianquan (September 2018). "Material insights and challenges for non-fullerene organic solar cells based on small molecular acceptors". Nature Energy. 3 (9): 720–731. Bibcode:2018NatEn...3..720Z. doi:10.1038/s41560-018-0181-5. ISSN   2058-7546. S2CID   189046590.
  118. Liu, Qishi; Jiang, Yufan; Jin, Ke; Qin, Jianqiang; Xu, Jingui; Li, Wenting; Xiong, Ji; Liu, Jinfeng; Xiao, Zuo; Sun, Kuan; Yang, Shangfeng; Zhang, Xiaotao; Ding, Liming (2020). "18% Efficiency organic solar cells". Science Bulletin. 65 (4): 272–275. Bibcode:2020SciBu..65..272L. doi:10.1016/j.scib.2020.01.001. PMID   36659090.
  119. Chen, Haiyang; Zhang, Rui; Chen, Xiaobin; Zeng, Guang; Kobera, Libor; Abbrent, Sabina; Zhang, Ben; Chen, Weijie; Xu, Guiying; Oh, Jiyeon; Kang, So-Huei; Chen, ShanShan; Yang, Changduk; Brus, Jiri; Hou, Jianhui; Gao, Feng; Li, Yaowen; Li, Yongfang (November 2021). "A guest-assisted molecular-organization approach for >17% efficiency organic solar cells using environmentally friendly solvents". Nature Energy. 6 (11): 1045–1053. Bibcode:2021NatEn...6.1045C. doi:10.1038/s41560-021-00923-5. S2CID   240450956.
  120. Sun, Rui; Wu, Yao; Yang, Xinrong; Gao, Yuan; Chen, Zeng; Li, Kai; Qiao, Jiawei; Wang, Tao; Guo, Jing; Liu, Chao; Hao, Xiaotao; Zhu, Haiming; Min, Jie (April 2022). "Single-Junction Organic Solar Cells with 19.17% Efficiency Enabled by Introducing One Asymmetric Guest Acceptor". Advanced Materials. 34 (26): e2110147. Bibcode:2022AdM....3410147S. doi:10.1002/adma.202110147. PMID   35438225. S2CID   248242142.
  121. 1 2 3 Collins, Samuel D.; Ran, Niva A.; Heiber, Michael C.; Nguyen, Thuc-Quyen (May 2017). "Small is Powerful: Recent Progress in Solution-Processed Small Molecule Solar Cells". Advanced Energy Materials. 7 (10): 1602242. doi:10.1002/aenm.201602242. S2CID   125931498.

Further reading