Vacuum arc remelting

Last updated

Vacuum arc remelting (VAR) is a secondary melting process for production of metal ingots with elevated chemical and mechanical homogeneity for highly demanding applications. [1] The VAR process has revolutionized the specialty traditional metallurgical techniques industry, and has made possible tightly-controlled materials used in biomedical, aviation and aerospace.

Contents

Overview

A vacuum arc remelting (VAR) furnace (or Arc Melter) from Edmund Buhler Arc-melting.jpg
A vacuum arc remelting (VAR) furnace (or Arc Melter) from Edmund Buhler

VAR is used most frequently in high value applications. It is an additional processing step to improve the quality of metal. Because it is time consuming and expensive, a majority of commercial alloys do not employ the process. Nickel, titanium, [2] and specialty steels are materials most often processed with this method. The conventional path for production of titanium alloys includes single, double or even triple VAR processing. [3] Use of this technique over traditional methods presents several advantages:

Process description

The alloy to undergo VAR is formed into a cylinder typically by vacuum induction melting (VIM) or ladle refining (airmelt). This cylinder, referred to as an electrode is then put into a large cylindrical enclosed crucible and brought to a metallurgical vacuum (0.001–0.1 mmHg or 0.1–13.3 Pa). At the bottom of the crucible is a small amount of the alloy to be remelted, which the top electrode is brought close to prior to starting the melt. Several kiloamperes of DC current are used to start an arc between the two pieces, thus a continuous melt is derived. The crucible (typically made of copper) is surrounded by a water jacket to cool the melt and control the solidification rate. To prevent arcing between the electrode and the crucible walls, the diameter of the crucible is larger than the electrode. As a result, the electrode must be lowered as the melt consumes it. Control of the current, cooling water, and electrode gap is essential to effective control of the process and production of defect-free material.

Ideally, the melt rate stays constant throughout the process cycle, but monitoring and control of the vacuum arc remelting process is not simple. [4] This is because there is a complex heat transfer occurring involving conduction, radiation, convection within the liquid metal, and advection caused by the Lorentz force. Ensuring the consistency of the melt process in terms of pool geometry, and melt rate is crucial in ensuring the best possible properties of the alloy.

Materials and applications

The VAR process is used on many different materials. Certain applications almost always use a material that has been VAR treated. A list of materials that may be VAR treated include:

Note that pure titanium and most titanium alloys are double or triple VAR processed. Nickel-based super alloys for aerospace applications are usually VAR processed. Zirconium and niobium alloys used in the nuclear industry are routinely VAR processed. Pure platinum, tantalum, and rhodium may be VAR processed.

See also

Related Research Articles

<span class="mw-page-title-main">Niobium</span> Chemical element, symbol Nb and atomic number 41

Niobium is a chemical element; it has symbol Nb and atomic number 41. It is a light grey, crystalline, and ductile transition metal. Pure niobium has a Mohs hardness rating similar to pure titanium, and it has similar ductility to iron. Niobium oxidizes in Earth's atmosphere very slowly, hence its application in jewelry as a hypoallergenic alternative to nickel. Niobium is often found in the minerals pyrochlore and columbite, hence the former name "columbium". Its name comes from Greek mythology: Niobe, daughter of Tantalus, the namesake of tantalum. The name reflects the great similarity between the two elements in their physical and chemical properties, which makes them difficult to distinguish.

A period 5 element is one of the chemical elements in the fifth row of the periodic table of the chemical elements. The periodic table is laid out in rows to illustrate recurring (periodic) trends in the chemical behaviour of the elements as their atomic number increases: a new row is begun when chemical behaviour begins to repeat, meaning that elements with similar behaviour fall into the same vertical columns. The fifth period contains 18 elements, beginning with rubidium and ending with xenon. As a rule, period 5 elements fill their 5s shells first, then their 4d, and 5p shells, in that order; however, there are exceptions, such as rhodium.

<span class="mw-page-title-main">Brazing</span> Metal-joining technique

Brazing is a metal-joining process in which two or more metal items are joined by melting and flowing a filler metal into the joint, with the filler metal having a lower melting point than the adjoining metal.

Refractory metals are a class of metals that are extraordinarily resistant to heat and wear. The expression is mostly used in the context of materials science, metallurgy and engineering. The definition of which elements belong to this group differs. The most common definition includes five elements: two of the fifth period and three of the sixth period. They all share some properties, including a melting point above 2000 °C and high hardness at room temperature. They are chemically inert and have a relatively high density. Their high melting points make powder metallurgy the method of choice for fabricating components from these metals. Some of their applications include tools to work metals at high temperatures, wire filaments, casting molds, and chemical reaction vessels in corrosive environments. Partly due to the high melting point, refractory metals are stable against creep deformation to very high temperatures.

<span class="mw-page-title-main">Electric arc furnace</span> Type of furnace

An electric arc furnace (EAF) is a furnace that heats material by means of an electric arc.

The Kroll process is a pyrometallurgical industrial process used to produce metallic titanium from titanium tetrachloride. The Kroll process replaced the Hunter process for almost all commercial production.

Titanium alloys are alloys that contain a mixture of titanium and other chemical elements. Such alloys have very high tensile strength and toughness. They are light in weight, have extraordinary corrosion resistance and the ability to withstand extreme temperatures. However, the high cost of both raw materials and processing limit their use to military applications, aircraft, spacecraft, bicycles, medical devices, jewelry, highly stressed components such as connecting rods on expensive sports cars and some premium sports equipment and consumer electronics.

Ferroalloy refers to various alloys of iron with a high proportion of one or more other elements such as manganese (Mn), aluminium (Al), or silicon (Si). They are used in the production of steels and alloys. The alloys impart distinctive qualities to steel and cast iron or serve important functions during production and are, therefore, closely associated with the iron and steel industry, the leading consumer of ferroalloys. The leading producers of ferroalloys in 2014 were China, South Africa, India, Russia and Kazakhstan, which accounted for 84% of the world production. World production of ferroalloys was estimated as 52.8 million tonnes in 2015.

<span class="mw-page-title-main">Foundry</span> Factory that produces metal castings

A foundry is a factory that produces metal castings. Metals are cast into shapes by melting them into a liquid, pouring the metal into a mold, and removing the mold material after the metal has solidified as it cools. The most common metals processed are aluminum and cast iron. However, other metals, such as bronze, brass, steel, magnesium, and zinc, are also used to produce castings in foundries. In this process, parts of desired shapes and sizes can be formed.

<span class="mw-page-title-main">Electro-slag remelting</span>

Electroslag remelting (ESR), also known as electro-flux remelting, is a process of remelting and refining steel and other alloys for mission-critical applications in aircraft, thermal power stations, nuclear power plants, military technology and others.

Titanium powder metallurgy (P/M) offers the possibility of creating net shape or near net shape parts without the material loss and cost associated with having to machine intricate components from wrought billet. Powders can be produced by the blended elemental technique or by pre-alloying and then consolidated by metal injection moulding, hot isostatic pressing, direct powder rolling or laser engineered net shaping.

Spray forming, also known as spray casting, spray deposition and in-situ compaction, is a method of casting near net shape metal components with homogeneous microstructures via the deposition of semi-solid sprayed droplets onto a shaped substrate. In spray forming an alloy is melted, normally in an induction furnace, then the molten metal is slowly poured through a conical tundish into a small-bore ceramic nozzle. The molten metal exits the furnace as a thin free-falling stream and is broken up into droplets by an annular array of gas jets, and these droplets then proceed downwards, accelerated by the gas jets to impact onto a substrate. The process is arranged such that the droplets strike the substrate whilst in the semi-solid condition, this provides sufficient liquid fraction to 'stick' the solid fraction together. Deposition continues, gradually building up a spray formed billet of metal on the substrate.

Alloy steel is steel that is alloyed with a variety of elements in total amounts between 1.0% and 50% by weight to improve its mechanical properties.

<span class="mw-page-title-main">Nickel titanium</span> High-durability alloy

Nickel titanium, also known as nitinol, is a metal alloy of nickel and titanium, where the two elements are present in roughly equal atomic percentages. Different alloys are named according to the weight percentage of nickel; e.g., nitinol 55 and nitinol 60.

Electron-beam additive manufacturing, or electron-beam melting (EBM) is a type of additive manufacturing, or 3D printing, for metal parts. The raw material is placed under a vacuum and fused together from heating by an electron beam. This technique is distinct from selective laser sintering as the raw material fuses having completely melted.

<span class="mw-page-title-main">Mishra Dhatu Nigam</span> Metallurgy industry

Mishra Dhatu Nigam Limited, is a specialized metals and metal alloys manufacturing facility in India, located in Hyderabad, Telangana. It is a Public Sector Undertaking (PSU), under the administrative control of Department of Defence Production, Ministry of Defence, Government of India. MIDHANI is the only producer of titanium in India.

The coinage metals comprise those metallic chemical elements and alloys which have been used to mint coins. Historically, most coinage metals are from the three nonradioactive members of group 11 of the periodic table: copper, silver and gold. Copper is usually augmented with tin or other metals to form bronze. Gold, silver and bronze or copper were the principal coinage metals of the ancient world, the medieval period and into the late modern period when the diversity of coinage metals increased. While coins are primarily made from metal, some non-metallic materials have also been used.

A niobium alloy is one in which the most common element is niobium.

Gloria Material Technology Corp. is a company headquartered in Liouying industrial zone, Tainan, Taiwan. It is the only specialty alloy professional manufacturer in Taiwan which owns melting, forging, rolling, heat treating and finishing processes. GMTC provides more than 500 steel grades such as superalloy, titanium alloy, ESR & VAR steel, high speed steel, stainless steel, quenched-tempered steel, tool steel, special steel profile and precision parts machining. The main product shapes are focused on round bars and square bars.

References

  1. "Modeling for Casting & Solidification Processing", by Kuang-Oscar Yu,CRC; 1st edition (October 15, 2001), ISBN   0-8247-8881-8
  2. D.Zagrebelnyy, Modeling macrosegregation during vacuum arc remelting of Ti-10V-2Fe-3Al alloy ISBN   978-3-8364-5948-8
  3. Titanium: Past, Present, and Future (1983) ISBN   0-309-07765-6
  4. DA Melgaard, RG Erdmann, JJ Beaman, RL Williamson - 2007

Further reading