Basic oxygen steelmaking

Last updated
Oxygen converter being charged at ThyssenKrupp steel mill in Duisburg (Germany) ThyssenKrupp Duisburg 016.jpg
Oxygen converter being charged at ThyssenKrupp steel mill in Duisburg (Germany)

Basic oxygen steelmaking (BOS, BOP, BOF, or OSM), also known as Linz-Donawitz steelmaking or the oxygen converter process, [1] is a method of primary steelmaking in which carbon-rich molten pig iron is made into steel. Blowing oxygen through molten pig iron lowers the carbon content of the alloy and changes it into low-carbon steel. The process is known as basic because fluxes of burnt lime or dolomite, which are chemical bases , are added to promote the removal of impurities and protect the lining of the converter. [2]

Contents

The process was invented in 1948 by Swiss engineer Robert Durrer and commercialized in 1952–1953 by the Austrian steelmaking company VOEST and ÖAMG. The LD converter, named after the Austrian towns Linz and Donawitz (a district of Leoben) is a refined version of the Bessemer converter where blowing of air is replaced with blowing oxygen. It reduced capital cost of the plants and smelting time, and increased labor productivity. Between 1920 and 2000, labor requirements in the industry decreased by a factor of 1,000, from more than three man-hours per metric ton to just 0.003. [3] The majority of steel manufactured in the world is produced using the basic oxygen furnace. In 2000, it accounted for 60% of global steel output. [3]

Modern furnaces will take a charge of iron of up to 400 tons [4] and convert it into steel in less than 40 minutes, compared to 10–12 hours in an open hearth furnace.

History

The basic oxygen process developed outside of traditional "big steel" environment. It was developed and refined by a single man, Swiss engineer Robert Durrer, and commercialized by two small steel companies in allied-occupied Austria, which had not yet recovered from the destruction of World War II. [5]

In 1856, Henry Bessemer had patented a steelmaking process involving oxygen blowing for decarbonizing molten iron (UK Patent No. 2207). For nearly 100 years commercial quantities of oxygen were not available or were too expensive, and the invention remained unused. During WWII German (Karl Valerian Schwarz), Belgian (John Miles) and Swiss (Durrer and Heinrich Heilbrugge) engineers proposed their versions of oxygen-blown steelmaking, but only Durrer and Heilbrugge brought it to mass-scale production. [5]

In 1943, Durrer, formerly a professor at the Berlin Institute of Technology, returned to Switzerland and accepted a seat on the board of Roll AG, the country's largest steel mill. In 1947 he purchased the first small 2.5-ton experimental converter from the US, and on April 3, 1948 the new converter produced its first steel. [5] The new process could conveniently process large amounts of scrap metal with only a small proportion of primary metal necessary. [6] In the summer of 1948, Roll AG and two Austrian state-owned companies, VÖEST and ÖAMG, agreed to commercialize the Durrer process. [6]

By June 1949, VÖEST developed an adaptation of Durrer's process, known as the LD (Linz-Donawitz) process. [7] [8] In December 1949, VÖEST and ÖAMG committed to building their first 30-ton oxygen converters. [8] They were put into operation in November 1952 (VÖEST in Linz) and May 1953 (ÖAMG, Donawitz) [8] and temporarily became the leading edge of the world's steelmaking, causing a surge in steel-related research. [9] Thirty-four thousand businesspeople and engineers visited the VÖEST converter by 1963. [9] The LD process reduced processing time and capital costs per ton of steel, contributing to the competitive advantage of Austrian steel. [7] VÖEST eventually acquired the rights to market the new technology. [8] Errors by the VÖEST and the ÖAMG management in licensing their technology made control over its adoption in Japan impossible. By the end of the 1950s, the Austrians lost their competitive edge. [7]

In the original LD process, oxygen was blown over the top of the molten iron through the water-cooled nozzle of a vertical lance. In the 1960s, steelmakers introduced bottom-blown converters and developed inert gas blowing for stirring the molten metal and removing phosphorus impurities. [3]

In the Soviet Union, some experimental production of steel using the process was done in 1934, but industrial use was hampered by lack of efficient technology to produce liquid oxygen. In 1939, the Russian physicist Pyotr Kapitsa perfected the design of the centrifugal turboexpander. The process was put to use in 1942–1944. Most turboexpanders in industrial use since then have been based on Kapitsa's design and centrifugal turboexpanders have taken over almost 100% of industrial gas liquefaction, and in particular the production of liquid oxygen for steelmaking. [10]

Big American steelmakers were late adopters of the new technology. The first oxygen converters in the US were launched at the end of 1954 by McLouth Steel in Trenton, Michigan, which accounted for less than 1% of the national steel market. [3] U.S. Steel and Bethlehem Steel introduced the oxygen process in 1964. [3] By 1970, half of the world's and 80% of Japan's steel output was produced in oxygen converters. [3]

In the last quarter of the 20th century, use of basic oxygen converters for steel production was gradually, partially replaced by the electric arc furnace using scrap steel and iron. In Japan the share of LD process decreased from 80% in 1970 to 70% in 2000; worldwide share of the basic oxygen process stabilized at 60%. [3]

Process

Principle of a LD (Linz Donawitz) converter Schema LD metallurgie.svg
Principle of a LD (Linz Donawitz) converter
Cross-section of a basic oxygen furnace LDkonverter01.jpg
Cross-section of a basic oxygen furnace
The outside of a basic oxygen steelmaking plant at the Scunthorpe steel works (England) BOS Plant (Scunthorpe Steelworks).jpg
The outside of a basic oxygen steelmaking plant at the Scunthorpe steel works (England)

Basic oxygen steelmaking is a primary steelmaking process for converting molten pig iron into steel by blowing oxygen through a lance over the molten pig iron inside the converter. Exothermic heat is generated by the oxidation reactions during blowing.

The basic oxygen steel-making process is as follows:

  1. Molten pig iron (sometimes referred to as "hot metal") from a blast furnace is poured into a large refractory-lined container called a ladle.
  2. The metal in the ladle is sent directly for basic oxygen steelmaking or to a pretreatment stage where sulfur, silicon, and phosphorus are removed before charging the hot metal into the converter. In external desulfurizing pretreatment, a lance is lowered into the molten iron in the ladle and several hundred kilograms of powdered magnesium are added and the sulfur impurities are reduced to magnesium sulfide in a violent exothermic reaction. The sulfide is then raked off. Similar pretreatments are possible for external desiliconisation and external dephosphorisation using mill scale (iron oxide) and lime as fluxes. The decision to pretreat depends on the quality of the hot metal and the required final quality of the steel.
  3. Filling the furnace with the ingredients is called charging. The BOS process is autogenous, i.e. the required thermal energy is produced during the oxidation process. Maintaining the proper charge balance, the ratio of hot metal from melt to cold scrap is important. The BOS vessel can be tilted up to 360° and is tilted towards the deslagging side for charging scrap and hot metal. The BOS vessel is charged with steel or iron scrap (25–30%), if required. Molten iron from the ladle is added as required for the charge balance. A typical chemistry of hotmetal charged into the BOS vessel is: 4% C, 0.2–0.8% Si, 0.08%–0.18% P, and 0.01–0.04% S, all of which can be oxidised by the supplied oxygen except sulfur (which requires reducing conditions).
  4. The vessel is then set upright and a water-cooled, copper tipped lance with 3–7 nozzles is lowered into it to within a few feet of the surface of the bath and high-purity oxygen at a pressure of 700–1,000 kilopascals (100–150 psi) is introduced at supersonic speed. The lance "blows" 99% pure oxygen over the hot metal, igniting the carbon dissolved in the steel, to form carbon monoxide and carbon dioxide, causing the temperature to rise to about 1700 °C. This melts the scrap, lowers the carbon content of the molten iron and helps remove unwanted chemical elements. It is this use of pure oxygen (instead of air) that improves upon the Bessemer process, as the nitrogen (an undesirable element) and other gases in air do not react with the charge, and decrease the efficiency of the furnace. [11]
  5. Fluxes (burnt lime or dolomite) are fed into the vessel to form slag, to maintain basicity of the slag – the ratio of calcium oxide to silicon oxide – at a level to minimise refractory wear and absorb impurities during the steelmaking process. During "blowing", churning of metal and fluxes in the vessel forms an emulsion that facilitates the refining process. Near the end of the blowing cycle, which takes about 20 minutes, the temperature is measured and samples are taken. A typical chemistry of the blown metal is 0.3–0.9% C, 0.05–0.1% Mn, 0.001–0.003% Si, 0.01–0.03% S and 0.005–0.03% P.
  6. The BOS vessel is tilted towards the slagging side and the steel is poured through a tap hole into a steel ladle with basic refractory lining. This process is called tapping the steel. The steel is further refined in the ladle furnace, by adding alloying materials to impart special properties required by the customer. Sometimes argon or nitrogen is bubbled into the ladle to make the alloys mix correctly.
  7. After the steel is poured off from the BOS vessel, the slag is poured into the slag pots through the BOS vessel mouth and dumped.

Variants

Earlier converters, with a false bottom that can be detached and repaired, are still in use. Modern converters have a fixed bottom with plugs for argon purging. The Energy Optimization Furnace (EOF) is a BOF variant associated with a scrap preheater where the sensible heat in the off-gas is used for preheating scrap, located above the furnace roof.

The lance used for blowing has undergone changes. Slagless lances, with a long tapering copper tip, have been employed to avoid jamming of the lance during blowing. Post-combustion lance tips burn the CO generated during blowing into CO2 and provide additional heat. For slag-free tapping, darts, refractory balls, and slag detectors are employed. Modern converters are fully automated with automatic blowing patterns and sophisticated control systems.[ citation needed ]

See also

Related Research Articles

<span class="mw-page-title-main">Bessemer process</span> Steel production method

The Bessemer process was the first inexpensive industrial process for the mass production of steel from molten pig iron before the development of the open hearth furnace. The key principle is removal of impurities from the iron by oxidation with air being blown through the molten iron. The oxidation also raises the temperature of the iron mass and keeps it molten.

<span class="mw-page-title-main">Pig iron</span> Iron alloy

Pig iron, also known as crude iron, is an intermediate good used by the iron industry in the production of steel, which is developed by smelting iron ore in a blast furnace. Pig iron has a high carbon content, typically 3.8–4.7%, along with silica and other constituents of dross, which makes it brittle and not useful directly as a material except for limited applications.

<span class="mw-page-title-main">Steelmaking</span> Process for producing steel from iron ore and scrap

Steelmaking is the process of producing steel from iron ore and/or scrap. In steelmaking, impurities such as nitrogen, silicon, phosphorus, sulfur and excess carbon are removed from the sourced iron, and alloying elements such as manganese, nickel, chromium, carbon and vanadium are added to produce different grades of steel.

<span class="mw-page-title-main">Slag</span> By-product of smelting ores and used metals

Slag is a by-product of smelting (pyrometallurgical) ores and recycled metals. Slag is mainly a mixture of metal oxides and silicon dioxide. Broadly, it can be classified as ferrous, ferroalloy or non-ferrous/base metals. Within these general categories, slags can be further categorized by their precursor and processing conditions.

<span class="mw-page-title-main">William Kelly (inventor)</span> American businessman

William Kelly, born in Pittsburgh, Pennsylvania, was an American inventor. He is credited with being one of the inventors of modern steel production, through the process of injecting air into molten iron, which he experimented with in the early 1850s. A similar process was discovered independently by Henry Bessemer and patented in 1855. Due to a financial panic in 1857, a company that had already licensed the Bessemer process was able to purchase Kelly's patents, and licensed both under a single scheme using the Bessemer name. Kelly's role in the invention of the process is much less known.

<span class="mw-page-title-main">Steel mill</span> Plant for steelmaking

A steel mill or steelworks is an industrial plant for the manufacture of steel. It may be an integrated steel works carrying out all steps of steelmaking from smelting iron ore to rolled product, but may also be a plant where steel semi-finished casting products are made from molten pig iron or from scrap.

<span class="mw-page-title-main">Open hearth furnace</span> A type of industrial furnace for steelmaking

An open-hearth furnace or open hearth furnace is any of several kinds of industrial furnace in which excess carbon and other impurities are burnt out of pig iron to produce steel. Because steel is difficult to manufacture owing to its high melting point, normal fuels and furnaces were insufficient for mass production of steel, and the open-hearth type of furnace was one of several technologies developed in the nineteenth century to overcome this difficulty. Compared with the Bessemer process, which it displaced, its main advantages were that it did not expose the steel to excessive nitrogen, was easier to control, and permitted the melting and refining of large amounts of scrap iron and steel.

<span class="mw-page-title-main">New Zealand Steel</span>

New Zealand Steel Limited is the owner of the Glenbrook Steel Mill, a steel mill located 40 kilometres south of Auckland, in Glenbrook, New Zealand. The mill was constructed in 1968 and began producing steel products in 1969. Currently, the mill produces 650,000 tonnes of steel a year, which is either used domestically or exported. Over 90% of New Zealand's steel requirements are produced at Glenbrook, while the remaining volume is produced by Pacific Steel, a steel recycling facility in Ōtāhuhu, Auckland. The mill is served by the Mission Bush Branch railway line, which was formerly a branch line to Waiuku. Coal and lime trains arrive daily. Steel products are also transported daily. The mill employs 1,150 full-time staff and 200 semi-permanent contractors.

<span class="mw-page-title-main">Electric arc furnace</span> Type of furnace

An electric arc furnace (EAF) is a furnace that heats material by means of an electric arc.

<span class="mw-page-title-main">Puddling (metallurgy)</span> Step in the manufacture of iron

Puddling is the process of converting pig iron to bar (wrought) iron in a coal fired reverberatory furnace. It was developed in England during the 1780s. The molten pig iron was stirred in a reverberatory furnace, in an oxidizing environment to burn the carbon, resulting in wrought iron. It was one of the most important processes for making the first appreciable volumes of valuable and useful bar iron without the use of charcoal. Eventually, the furnace would be used to make small quantities of specialty steels.

<span class="mw-page-title-main">Electrometallurgy</span>

Electrometallurgy is a method in metallurgy that uses electrical energy to produce metals by electrolysis. It is usually the last stage in metal production and is therefore preceded by pyrometallurgical or hydrometallurgical operations. The electrolysis can be done on a molten metal oxide which is used for example to produce aluminium from aluminium oxide via the Hall-Hérault process. Electrolysis can be used as a final refining stage in pyrometallurgical metal production (electrorefining) and it is also used for reduction of a metal from an aqueous metal salt solution produced by hydrometallurgy (electrowinning).

<span class="mw-page-title-main">Ladle (metallurgy)</span>

In metallurgy, a ladle is a bucket-shaped container or vessel used to transport and pour out molten metals. Ladles are often used in foundries and range in size from small hand carried vessels that resemble a kitchen ladle and hold 20 kilograms (44 lb) to large steelmill ladles that hold up to 300 tonnes. Many non-ferrous foundries also use ceramic crucibles for transporting and pouring molten metal and will also refer to these as ladles.

Deoxidization is a method used in metallurgy to remove the oxygen content during steel manufacturing. In contrast, antioxidants are used for stabilization, such as in the storage of food. Deoxidation is important in the steelmaking process as oxygen is often detrimental to the quality of steel produced. Deoxidization is mainly achieved by adding a separate chemical species to neutralize the effects of oxygen or by directly removing the oxygen.

<span class="mw-page-title-main">Argon oxygen decarburization</span>

Argon oxygen decarburization (AOD) is a process primarily used in stainless steel making and other high grade alloys with oxidizable elements such as chromium and aluminium. After initial melting the metal is then transferred to an AOD vessel where it will be subjected to three steps of refining; decarburization, reduction, and desulfurization.

<span class="mw-page-title-main">Cupola furnace</span> Small blast furnace for melting scrap iron without reduction reactions

A cupola or cupola furnace is a melting device used in foundries that can be used to melt cast iron, Ni-resist iron and some bronzes. The cupola can be made almost any practical size. The size of a cupola is expressed in diameters and can range from 1.5 to 13 feet. The overall shape is cylindrical and the equipment is arranged vertically, usually supported by four legs. The overall look is similar to a large smokestack.

<span class="mw-page-title-main">Robert Durrer</span> Swiss engineer (1890–1978)

Robert Durrer (1890–1978) was a Swiss engineer who invented the basic oxygen steelmaking process during his career in Nazi Germany. The process was successfully tested by Durrer in 1948. A team led by Dr Theodor Eduard Suess in Austria adapted the process and scaled it to industrial size, after which it was commercialized by VÖEST and ÖAMG.

The HIsarna ironmaking process is a direct reduced iron process for iron making in which iron ore is processed almost directly into liquid iron (pig iron). The process combines two process units, the Cyclone Converter Furnace (CCF) for ore melting and pre-reduction and a Smelting Reduction Vessel (SRV) where the final reduction stage to liquid iron takes place. The process does not require the manufacturing of iron ore agglomerates such as pellets and sinter, nor the production of coke, which are necessary for the blast furnace process. Without these steps, the HIsarna process is more energy-efficient and has a lower carbon footprint than traditional ironmaking processes. In 2018 Tata Steel announced it has demonstrated that more than 50% CO2 emission reduction is possible with HIsarna technology, without the need for carbon capture technology.

A Kaldo converter is a rotary vessel oxygen based metal refining method. Originally applied to the refining of iron into steel, with most installations in the 1960s, the process is (2014) used primarily to refine non ferrous metals, typically copper. In that field, it is often named TBRC, or Top Blown Rotary Converter.

Primetals Technologies Limited, is an engineering and plant construction company headquartered in London, United Kingdom, with numerous locations worldwide. It serves clients in the metals industry, both the ferrous and the nonferrous metals sector. It was established as a joint venture between Siemens VAI Metals Technologies and Mitsubishi-Hitachi Metals Machinery in 2015. As of 2020, Primetals Technologies is a joint venture of Mitsubishi Heavy Industries and partners.

References

  1. Brock and Elzinga, p. 50.
  2. "Basic Oxygen Steelmaking Simulation User Guide version 2.00" (PDF). steeluniversity.org . Archived (PDF) from the original on 2021-04-27. Retrieved 2021-04-27.
  3. 1 2 3 4 5 6 7 Smil, p. 99.
  4. "Hot metal and crude steel production". stahl-online.de. Archived from the original on 2021-01-16.
  5. 1 2 3 Smil, p. 97.
  6. 1 2 Smil, pp. 97–98.
  7. 1 2 3 Tweraser, p. 313.
  8. 1 2 3 4 Smil, p. 98.
  9. 1 2 Brock and Elzinga, p. 39.
  10. Ebbe Almqvist (2002). History of Industrial Gases (First ed.). Springer. p.  165. ISBN   0-306-47277-5.
  11. McGannon, p 486

Bibliography