Polymer degradation

Last updated

Polymer degradation is the reduction in the physical properties of a polymer, such as strength, caused by changes in its chemical composition. Polymers and particularly plastics are subject to degradation at all stages of their product life cycle, including during their initial processing, use, disposal into the environment and recycling. [1] The rate of this degradation varies significantly; biodegradation can take decades, whereas some industrial processes can completely decompose a polymer in hours.

Contents

Technologies have been developed to both inhibit or promote degradation. For instance, polymer stabilizers ensure plastic items are produced with the desired properties, extend their useful lifespans, and facilitate their recycling. Conversely, biodegradable additives accelerate the degradation of plastic waste by improving its biodegradability. Some forms of plastic recycling can involve the complete degradation of a polymer back into monomers or other chemicals.

In general, the effects of heat, light, air and water are the most significant factors in the degradation of plastic polymers. The major chemical changes are oxidation and chain scission, leading to a reduction in the molecular weight and degree of polymerization of the polymer. These changes affect physical properties like strength, malleability, melt flow index, appearance and colour. The changes in properties are often termed "aging".

2015 Global plastic production by polymer type: PP: polypropylene, PE: polyethylene, PVC: Polyvinyl chloride, PS: Polystyrene, PET: Polyethylene terephthalate Plastics market share en.svg
2015 Global plastic production by polymer type:
PP: polypropylene, PE: polyethylene, PVC: Polyvinyl chloride, PS: Polystyrene, PET: Polyethylene terephthalate

Susceptibility

Plastics exist in huge variety, however several types of commodity polymer dominate global production: polyethylene (PE), polypropylene (PP), polyvinyl chloride (PVC), polyethylene terephthalate (PET, PETE), polystyrene (PS), polycarbonate (PC), and poly(methyl methacrylate) (PMMA). The degradation of these materials is of primary importance as they account for most plastic waste.

These plastics are all thermoplastics and are more susceptible to degradation than equivalent thermosets, as those are more thoroughly cross-linked. The majority (PP, PE, PVC, PS and PMMA) are addition polymers with all-carbon backbones that are more resistant to most types of degradation. PET and PC are condensation polymers which contain carbonyl groups more susceptible to hydrolysis and UV-attack.

Degradation during processing

Plastic compounding scheme Compounding-en.png
Plastic compounding scheme
Short video on injection molding (9 min 37 s)

Thermoplastic polymers (be they virgin or recycled) must be heated until molten to be formed into their final shapes, with processing temperatures anywhere between 150-320 °C (300–600 °F) depending on the polymer. [2] Polymers will oxidise under these conditions, but even in the absence of air, these temperatures are sufficient to cause thermal degradation in some materials. The molten polymer also experiences significant shear stress during extrusion and moulding, which is sufficient to snap the polymer chains. Unlike many other forms of degradation, the effects of melt-processing degrades the entire bulk of the polymer, rather than just the surface layers. This degradation introduces chemical weak points into the polymer, particularly in the form of hydroperoxides, which become initiation sites for further degradation during the object's lifetime.

Polymers are often subject to more than one round of melt-processing, which can cumulatively advance degradation. Virgin plastic typically undergoes compounding to introduce additives such as dyes, pigments and stabilisers. Pelletised material prepared in this may also be pre-dried in an oven to remove trace moisture prior to its final melting and moulding into plastic items. Plastic which is recycled by simple re‑melting (mechanical recycling) will usually display more degradation than fresh material and may have poorer properties as a result. [3]

Thermal oxidation

Although oxygen levels inside processing equipment are usually low, it cannot be fully excluded and thermal-oxidation will usually take place more readily than degradation that is exclusively thermal (i.e. without air). [4] Reactions follow the general autoxidation mechanism, leading to the formation of organic peroxides and carbonyls. The addition of antioxidants may inhibit such processes.

Thermal degradation

Heating polymers to a sufficiently high temperature can cause damaging chemical changes, even in the absence of oxygen. This usually starts with chain scission, generating free radicals, which primarily engage in disproportionation and crosslinking. PVC is the most thermally sensitive common polymer, with major degradation occurring from ~250 °C (480 °F) onwards; [5] other polymers degrade at higher temperatures. [6]

Thermo-mechanical degradation

Molten polymers are non-Newtonian fluids with high viscosities, and the interaction between their thermal and mechanical degradation can be complex. At low temperatures, the polymer-melt is more viscous and more prone to mechanical degradation via shear stress. At higher temperatures, the viscosity is reduced, but thermal degradation is increased. Friction at points of high sheer can also cause localised heating, leading to additional thermal degradation.

Mechanical degradation can be reduced by the addition of lubricants, also referred to as processing aids or flow aids. These can reduce friction against the processing machinery but also between polymer chains, resulting in a decrease in melt-viscosity. Common agents are high-molecular-weight waxes (paraffin wax, wax esters, etc.) or metal stearates (i.e.zinc stearate).

In-service degradation

Global plastic waste generation by industrial sector for 2015, measured in tonnes per year Plastic waste generation by industrial sector, OWID.svg
Global plastic waste generation by industrial sector for 2015, measured in tonnes per year

Most plastic items, like packaging materials, are used briefly and only once. These rarely experience polymer degradation during their service-lives. Other items experience only gradual degradation from the natural environment. Some plastic items, however, can experience long service-lives in aggressive environments, particularly those where they are subject to prolonged heat or chemical attack. Polymer degradation can be significant in these cases and, in practice, is often only held back by the use of advanced polymer stabilizers. Degradation arising from the effects of heat, light, air and water is the most common, but other means of degradation exist.

The in-service degradation of mechanical properties is an important aspect which limits the applications of these materials. Polymer degradation caused by in-service degradation can cause life threatening accidents. In 1996, a baby was fed via a Hickman line and suffered an infection, when new connectors were used by a hospital. The reason behind this infection was the cracking and erosion of the pipes from the inner side due to contact with liquid media. [7]

Chlorine-induced cracking

Chlorine attack on an acetal resin plumbing joint Chlorine attack1.jpg
Chlorine attack on an acetal resin plumbing joint

Drinking water which has been chlorinated to kill microbes may contain trace levels of chlorine. The World Health Organization recommends an upper limit of 5 ppm. [8] Although low, 5 ppm is enough to slowly attack certain types of plastic, particularly when the water is heated, as it is for washing. Polyethylene, [9] [10] polybutylene [11] and acetal resin (polyoxymethylene) [12] pipework and fittings are all susceptible. Attack leads to hardening of pipework, which can leave it brittle and more susceptible to mechanical failure.

Electronics

Plastics are used extensively in the manufacture of electrical items, such as circuit boards and electrical cables. These applications can be harsh, exposing the plastic to a mixture of thermal, chemical and electrochemical attack. Many electric items like transformers, microprocessors or high-voltage cables operate at elevated temperatures for years, or even decades, resulting in low-level but continuous thermal oxidation. This can be exacerbated by direct contact with metals, which can promote the formation of free-radicals, for instance, by the action of Fenton reactions on hydroperoxides. [13] High voltage loads can also damage insulating materials such as dielectrics, which degrade via electrical treeing caused by prolonged electrical field stress. [14] [15]

Galvanic action

Mechanism of galvanic degradation of high temperature polyimide thermoset polymer Galvanic Degradation Mechanism of Polymer.jpg
Mechanism of galvanic degradation of high temperature polyimide thermoset polymer

Polymer degradation by galvanic action was first described in the technical literature in 1990 by Michael C. Faudree, an employee at General Dynamics, Fort Worth Division. [16] [17] The phenomenon has been referred to as the "Faudree Effect", [18] and can possibly be used as a sustainable process to degrade non-recyclable thermoset plastics, and also has had implications for preventing corrosion on aircraft for safety such as changes in design. [19] [20] When carbon-fiber-reinforced polymer is attached to a metal surface, the carbon fiber can act as a cathode if exposed to water or sufficient humidity, resulting in galvanic corrosion. This has been seen in engineering when carbon-fiber polymers have been used to reinforce weakened steel structures. [21] [22] Reactions have also been seen in aluminium [23] and magnesium alloys, [24] polymers affected include bismaleimides (BMI), and polyimides. The mechanism of degradation is believed to involve the electrochemical generation of hydroxide ions, which then cleave the amide bonds. [25]

Degradation in the environment

Most plastics do not biodegrade readily, [26] however, they do still degrade in the environment because of the effects of UV-light, oxygen, water and pollutants. This combination is often generalised as polymer weathering. [27] Chain breaking by weathering causes increasing embrittlement of plastic items, which eventually causes them to break apart. Fragmentation then continues until eventually microplastics are formed. As the particle sizes get smaller, so their combined surface area increases. This facilitates the leaching of additives out of plastic and into the environment. Many controversies associated with plastics actually relate to these additives. [28] [29]

Photo-oxidation

Photo-oxidation is the combined action of UV-light and oxygen and is the most significant factor in the weathering of plastics. [27] Although many polymers do not absorb UV-light, they often contain impurities like hydroperoxide and carbonyl groups introduced during thermal processing, which do. These act as photoinitiators to give complex free radical chain reactions where the mechanisms of autoxidation and photodegradation combine. Photo-oxidation can be held back by light stabilizers such as hindered amine light stabilizers (HALS). [30]

Hydrolysis

Polymers with an all-carbon backbone, such as polyolefins, are usually resistant to hydrolysis. Condensation polymers like polyesters, [31] polyamides, polyurethanes and polycarbonates can be degraded by hydrolysis of their carbonyl groups, to give lower molecular weight molecules. Such reactions are exceedingly slow at ambient temperatures, however, they remain a significant source of degradation for these materials, particularly in the marine environment. [32] Swelling caused by the absorption of minute amounts of water can also cause environmental stress cracking, which accelerates degradation.

Ozonolysis of rubbers

Ozone cracking in natural rubber tubing Ozone cracks in tube1.jpg
Ozone cracking in natural rubber tubing

Polymers, which are not fully saturated, are vulnerable to attack by ozone. This gas exists naturally in the atmosphere but is also formed by nitrogen oxides released in vehicle exhaust pollution. Many common elastomers (rubbers) are affected, with natural rubber, polybutadiene, styrene-butadiene rubber and NBR being most sensitive to degradation. The ozonolysis reaction results in immediate chain scission. Ozone cracks in products under tension are always oriented at right angles to the strain axis, so will form around the circumference in a rubber tube bent over. Such cracks are dangerous when they occur in fuel pipes because the cracks will grow from the outside exposed surfaces into the bore of the pipe, and fuel leakage and fire may follow. The problem of ozone cracking can be prevented by adding antiozonants.

Biological degradation

The major appeal of biodegradation is that, in theory, the polymer will be completely consumed in the environment without needing complex waste management and that the products of this will be non-toxic. Most common plastics biodegrade very slowly, sometimes to the extent that they are considered non-biodegradable. [26] [33] As polymers are ordinarily too large to be absorbed by microbes, biodegradation initially relies on secreted extracellular enzymes to reduce the polymers to manageable chain-lengths. This requires the polymers bear functional groups the enzymes can 'recognise', such as ester or amide groups. Long-chain polymers with all-carbon backbones like polyolefins, polystyrene and PVC will not degrade by biological action alone [34] and must first be oxidised to create chemical groups which the enzymes can attack. [35] [36]

Oxidation can be caused by melt-processing or weathering in the environment. Oxidation may be intentionally accelerated by the addition of biodegradable additives. These are added to the polymer during compounding to improve the biodegradation of otherwise very resistant plastics. Similarly, biodegradable plastics have been designed which are intrinsically biodegradable, provided they are treated like compost and not just left in a landfill site where degradation is very difficult because of the lack of oxygen and moisture. [37]

Degradation during recycling

Global means of disposal for plastic waste Global plastic waste by disposal, OWID.svg
Global means of disposal for plastic waste

The act of recycling plastic degrades its polymer chains, usually as a result of thermal damage similar to that seen during initial processing. In some cases, this is turned into an advantage by intentionally and completely depolymerising the plastic back into its starting monomers, which can then be used to generate fresh, un-degraded plastic. In theory, this chemical (or feedstock) recycling offers infinite recyclability, but it is also more expensive and can have a higher carbon footprint because of its energy costs. [3] Mechanical recycling, where the plastic is simply remelted and reformed, is more common, although this usually results in a lower-quality product. Alternatively, plastic may simply be burnt as a fuel in a waste-to-energy process. [38] [39]

Remelting

Thermoplastic polymers like polyolefins can be remelted and reformed into new items. This approach is referred to as mechanical recycling and is usually the simplest and most economical form of recovery. [3] Post-consumer plastic will usually already bear a degree of degradation. Another round of melt-processing will exacerbate this, with the result being that mechanically recycled plastic will usually have poorer mechanical properties than virgin plastic. [40] Degradation can be enhanced by high concentrations of hydroperoxides, cross-contamination between different types of plastic and by additives present within the plastic. Technologies developed to enhance the biodegradation of plastic can also conflict with its recycling, with oxo-biodegradable additives, consisting of metallic salts of iron, magnesium, nickel, and cobalt, increasing the rate of thermal degradation. [41] [42] Depending on the polymer in question, an amount of virgin material may be added to maintain the quality of the product. [43]

Thermal depolymerisation & pyrolysis

As polymers approach their ceiling temperature, thermal degradation gives way to complete decomposition. Certain polymers like PTFE, polystyrene and PMMA [44] undergo depolymerization to give their starting monomers, whereas others like polyethylene undergo pyrolysis, with random chain scission giving a mixture of volatile products. Where monomers are obtained, they can be converted back into new plastic (chemical or feedstock recycling), [45] [46] [47] whereas pyrolysis products are used as a type of synthetic fuel (energy recycling). [48] In practice, even very efficient depolymerisation to monomers tends to see some competitive pyrolysis. Thermoset polymers may also be converted in this way, for instance, in tyre recycling.

Chemical depolymerisation

Condensation polymers baring cleavable groups such as esters and amides can also be completely depolymerised by hydrolysis or solvolysis. This can be a purely chemical process but may also be promoted by enzymes. [49] Such technologies are less well developed than those of thermal depolymerisation, but have the potential for lower energy costs. Thus far, polyethylene terephthalate has been the most heavily studied polymer. [50] Alternatively, waste plastic may be converted into other valuable chemicals (not necessarily monomers) by microbial action. [51] [52]

Stabilisers

Hindered amine light stabilizers (HALS) stabilise against weathering by scavenging free radicals that are produced by photo-oxidation of the polymer matrix. UV-absorbers stabilise against weathering by absorbing ultraviolet light and converting it into heat. Antioxidants stabilise the polymer by terminating the chain reaction because of the absorption of UV light from sunlight. The chain reaction initiated by photo-oxidation leads to cessation of crosslinking of the polymers and degradation of the property of polymers. Antioxidants are used to protect from thermal degradation.

Detection

Irspec1.jpg

Degradation can be detected before serious cracks are seen in a product using infrared spectroscopy. [53] In particular, peroxy-species and carbonyl groups formed by photo-oxidation have distinct absorption bands.

See also

Bibliography

Related Research Articles

<span class="mw-page-title-main">Biodegradation</span> Decomposition by living organisms

Biodegradation is the breakdown of organic matter by microorganisms, such as bacteria and fungi. It is generally assumed to be a natural process, which differentiates it from composting. Composting is a human-driven process in which biodegradation occurs under a specific set of circumstances.

<span class="mw-page-title-main">Polypropylene</span> Thermoplastic polymer

Polypropylene (PP), also known as polypropene, is a thermoplastic polymer used in a wide variety of applications. It is produced via chain-growth polymerization from the monomer propylene.

Thermal depolymerization (TDP) is the process of converting a polymer into a monomer or a mixture of monomers, by predominantly thermal means. It may be catalyzed or un-catalyzed and is distinct from other forms of depolymerization which may rely on the use of chemicals or biological action. This process is associated with an increase in entropy.

<span class="mw-page-title-main">Plastic recycling</span> Processes which convert waste plastic into new items

Plastic recycling is the processing of plastic waste into other products. Recycling can reduce dependence on landfill, conserve resources and protect the environment from plastic pollution and greenhouse gas emissions. Recycling rates lag behind those of other recoverable materials, such as aluminium, glass and paper. From the start of plastic production through to 2015, the world produced around 6.3 billion tonnes of plastic waste, only 9% of which has been recycled and only ~1% has been recycled more than once. Of the remaining waste, 12% was incinerated and 79% was either sent to landfills or lost to the environment as pollution.

<span class="mw-page-title-main">Polylactic acid</span> Biodegradable polymer

Polylactic acid, also known as poly(lactic acid) or polylactide (PLA), is a thermoplastic polyester with backbone formula (C
3H
4O
2)
n or [–C(CH
3)HC(=O)O–]
n, formally obtained by condensation of lactic acid C(CH
3)(OH)HCOOH with loss of water. It can also be prepared by ring-opening polymerization of lactide [–C(CH
3)HC(=O)O–]
2, the cyclic dimer of the basic repeating unit.

<span class="mw-page-title-main">Bioplastic</span> Plastics derived from renewable biomass sources

Bioplastics are plastic materials produced from renewable biomass sources, such as vegetable fats and oils, corn starch and rice starch, straw, woodchips, sawdust, recycled food waste, etc. Some bioplastics are obtained by processing directly from natural biopolymers including polysaccharides and proteins, while others are chemically synthesized from sugar derivatives and lipids from either plants or animals, or biologically generated by fermentation of sugars or lipids. In contrast, common plastics, such as fossil-fuel plastics are derived from petroleum or natural gas.

<span class="mw-page-title-main">Polyester</span> Category of polymers, in which the monomers are joined together by ester links

Polyester is a category of polymers that contain one or two ester linkages in every repeat unit of their main chain. As a specific material, it most commonly refers to a type called polyethylene terephthalate (PET). Polyesters include naturally occurring chemicals, such as in plants and insects, as well as synthetics such as polybutyrate. Natural polyesters and a few synthetic ones are biodegradable, but most synthetic polyesters are not. Synthetic polyesters are used extensively in clothing.

Polyethylene or polythene film biodegrades naturally, albeit over a long period of time. Methods are available to make it more degradable under certain conditions of sunlight, moisture, oxygen, and composting and enhancement of biodegradation by reducing the hydrophobic polymer and increasing hydrophilic properties.

<span class="mw-page-title-main">Biodegradable plastic</span> Plastics that can be decomposed by the action of living organisms

Biodegradable plastics are plastics that can be decomposed by the action of living organisms, usually microbes, into water, carbon dioxide, and biomass. Biodegradable plastics are commonly produced with renewable raw materials, micro-organisms, petrochemicals, or combinations of all three.

PBAT is a biodegradable random copolymer, specifically a copolyester of adipic acid, 1,4-butanediol and terephthalic acid. PBAT is produced by many different manufacturers and may be known by the brand names ecoflex, Wango,Ecoworld, Eastar Bio, and Origo-Bi. It is also called poly(butylene adipate-co-terephthalate) and sometimes polybutyrate-adipate-terephthalate or even just "polybutyrate". It is generally marketed as a fully biodegradable alternative to low-density polyethylene, having many similar properties including flexibility and resilience, allowing it to be used for many similar uses such as plastic bags and wraps. The structure is a random-block polymer consisting of butanediol–adipic acid and butanediol-terephthalic acid blocks.

Biodegradable polymers are a special class of polymer that breaks down after its intended purpose by bacterial decomposition process to result in natural byproducts such as gases (CO2, N2), water, biomass, and inorganic salts. These polymers are found both naturally and synthetically made, and largely consist of ester, amide, and ether functional groups. Their properties and breakdown mechanism are determined by their exact structure. These polymers are often synthesized by condensation reactions, ring opening polymerization, and metal catalysts. There are vast examples and applications of biodegradable polymers.

Many opportunities exist for the application of synthetic biodegradable polymers in the biomedical area particularly in the fields of tissue engineering and controlled drug delivery. Degradation is important in biomedicine for many reasons. Degradation of the polymeric implant means surgical intervention may not be required in order to remove the implant at the end of its functional life, eliminating the need for a second surgery. In tissue engineering, biodegradable polymers can be designed such to approximate tissues, providing a polymer scaffold that can withstand mechanical stresses, provide a suitable surface for cell attachment and growth, and degrade at a rate that allows the load to be transferred to the new tissue. In the field of controlled drug delivery, biodegradable polymers offer tremendous potential either as a drug delivery system alone or in conjunction to functioning as a medical device.

Polymer stabilizers are chemical additives which may be added to polymeric materials, such as plastics and rubbers, to inhibit or retard their degradation. Common polymer degradation processes include oxidation, UV-damage, thermal degradation, ozonolysis, combinations thereof such as photo-oxidation, as well as reactions with catalyst residues, dyes, or impurities. All of these degrade the polymer at a chemical level, via chain scission, uncontrolled recombination and cross-linking, which adversely affects many key properties such as strength, malleability, appearance and colour.

<span class="mw-page-title-main">Photo-oxidation of polymers</span>

In polymer chemistry photo-oxidation is the degradation of a polymer surface due to the combined action of light and oxygen. It is the most significant factor in the weathering of plastics. Photo-oxidation causes the polymer chains to break, resulting in the material becoming increasingly brittle. This leads to mechanical failure and, at an advanced stage, the formation of microplastics. In textiles the process is called phototendering.

Oxo-degradation, refers to the process by which plastics that contain additives that accelerate its breakdown into smaller fragments, called microplastics, when exposed to heat, light or oxygen. This is in contrast to biodegradable or compostable plastics, which break down at the molecular or polymer level. Oxo-degradable plastics are currently banned in the EU, but still permitted in other jurisdictions such as the UK.

<span class="mw-page-title-main">Biodegradable bag</span> Bag capable of being decomposed

Biodegradable bags are bags that are capable of being decomposed by bacteria or other living organisms.

<span class="mw-page-title-main">Plastic</span> Material of a wide range of synthetic or semi-synthetic organic solids

Plastics are a wide range of synthetic or semi-synthetic materials that use polymers as a main ingredient. Their plasticity makes it possible for plastics to be molded, extruded or pressed into solid objects of various shapes. This adaptability, plus a wide range of other properties, such as being lightweight, durable, flexible, and inexpensive to produce, has led to their widespread use. Plastics typically are made through human industrial systems. Most modern plastics are derived from fossil fuel-based chemicals like natural gas or petroleum; however, recent industrial methods use variants made from renewable materials, such as corn or cotton derivatives.

Biodegradable additives are additives that enhance the biodegradation of polymers by allowing microorganisms to utilize the carbon within the polymer chain as a source of energy. Biodegradable additives attract microorganisms to the polymer through quorum sensing after biofilm creation on the plastic product. Additives are generally in masterbatch formation that use carrier resins such as polyethylene (PE), polypropylene (PP), polystyrene (PS) or polyethylene terephthalate (PET).

<span class="mw-page-title-main">Biodegradable athletic footwear</span>

Biodegradable athletic footwear is athletic footwear that uses biodegradable materials with the ability to compost at the end-of-life phase. Such materials include natural biodegradable polymers, synthetic biodegradable polymers, and biodegradable blends. The use of biodegradable materials is a long-term solution to landfill pollution that can significantly help protect the natural environment by replacing the synthetic, non-biodegradable polymers found in athletic footwear.

<span class="mw-page-title-main">Plastic degradation by marine bacteria</span> Ability of bacteria to break down plastic polymers

Plastic degradation in marine bacteria describes when certain pelagic bacteria break down polymers and use them as a primary source of carbon for energy. Polymers such as polyethylene (PE), polypropylene (PP), and polyethylene terephthalate (PET) are incredibly useful for their durability and relatively low cost of production, however it is their persistence and difficulty to be properly disposed of that is leading to pollution of the environment and disruption of natural processes. It is estimated that each year there are 9-14 million metric tons of plastic that are entering the ocean due to inefficient solutions for their disposal. The biochemical pathways that allow for certain microbes to break down these polymers into less harmful byproducts has been a topic of study to develop a suitable anti-pollutant.

References

  1. ↑ Singh, Baljit; Sharma, Nisha (March 2008). "Mechanistic implications of plastic degradation". Polymer Degradation and Stability. 93 (3): 561–584. doi:10.1016/j.polymdegradstab.2007.11.008.
  2. ↑ Ragaert, Kim; Delva, Laurens; Van Geem, Kevin (November 2017). "Mechanical and chemical recycling of solid plastic waste". Waste Management. 69: 24–58. doi:10.1016/j.wasman.2017.07.044. PMID   28823699.
  3. 1 2 3 Schyns, Zoé O. G.; Shaver, Michael P. (February 2021). "Mechanical Recycling of Packaging Plastics: A Review". Macromolecular Rapid Communications . 42 (3): 2000415. doi: 10.1002/marc.202000415 . PMID   33000883.
  4. ↑ Peterson, Jeffery D.; Vyazovkin, Sergey; Wight, Charles A. (2001). "Kinetics of the Thermal and Thermo-Oxidative Degradation of Polystyrene, Polyethylene and Poly(propylene)". Macromolecular Chemistry and Physics . 202 (6): 775–784. doi:10.1002/1521-3935(20010301)202:6<775::AID-MACP775>3.0.CO;2-G.
  5. ↑ Yu, Jie; Sun, Lushi; Ma, Chuan; Qiao, Yu; Yao, Hong (February 2016). "Thermal degradation of PVC: A review". Waste Management. 48: 300–314. doi:10.1016/j.wasman.2015.11.041. PMID   26687228.
  6. ↑ Matsuzawa, Yoshiaki; Ayabe, Muneo; Nishino, Junya; Kubota, Nobuhiko; Motegi, Mikio (August 2004). "Evaluation of char fuel ratio in municipal pyrolysis waste". Fuel . 83 (11–12): 1675–1687. doi:10.1016/j.fuel.2004.02.006.
  7. ↑ Saharudin, Mohd Shahneel; Atif, Rasheed; Shyha, Islam; Inam, Fawad (2015-12-22). "The degradation of mechanical properties in polymer nano-composites exposed to liquid media – a review". RSC Advances. 6 (2): 1076–1089. doi: 10.1039/C5RA22620A . ISSN   2046-2069. S2CID   98370832.
  8. ↑ Guidelines for drinking-water quality (Fourth incorporating the first addendum ed.). Geneva: World Health Organization. 2017. ISBN   978-92-4-154995-0.
  9. ↑ Hassinen, J (May 2004). "Deterioration of polyethylene pipes exposed to chlorinated water". Polymer Degradation and Stability. 84 (2): 261–267. doi:10.1016/j.polymdegradstab.2003.10.019.
  10. ↑ Duvall, Donald (June 2014). "Oxidation Resistance of Polypropylene Random Copolymer Pipe to Chlorinated Water". Journal of Failure Analysis and Prevention. 14 (3): 336–342. doi:10.1007/s11668-014-9809-3. S2CID   137141131.
  11. ↑ Fujii, Takehiro; Matsui, Yuichi; Hirabayashi, Hideo; Igawa, Kazuhisa; Okada, Saori; Honma, Hidekazu; Nishimura, Hiroyuki; Yamada, Kazushi (September 2019). "Influence of residual chlorine and pressure on degradation of polybutylene pipe". Polymer Degradation and Stability. 167: 1–9. doi:10.1016/j.polymdegradstab.2019.06.012. S2CID   197611740.
  12. ↑ Öner, Mualla; White, Don H. (January 1993). "Investigation of the degradation of commercial polyoxymethylene copolymer in water service applications". Polymer Degradation and Stability. 40 (3): 297–303. doi:10.1016/0141-3910(93)90135-6.
  13. ↑ Osawa, Zenjiro (January 1988). "Role of metals and metal-deactivators in polymer degradation". Polymer Degradation and Stability. 20 (3–4): 203–236. doi:10.1016/0141-3910(88)90070-5.
  14. ↑ Zakrevskii, V. A.; Sudar, N. T.; Zaopo, A.; Dubitsky, Yu. A. (15 February 2003). "Mechanism of electrical degradation and breakdown of insulating polymers". Journal of Applied Physics . 93 (4): 2135–2139. Bibcode:2003JAP....93.2135Z. doi:10.1063/1.1531820.
  15. ↑ Mayoux, C. (October 2000). "Degradation of insulating materials under electrical stress". IEEE Transactions on Dielectrics and Electrical Insulation. 7 (5): 590–601. doi:10.1109/TDEI.2000.879355.
  16. ↑ Faudree, Michael C. (1991). "Relationship of Graphite/Polyimide Composites to Galvanic Processes" (PDF). Society for the Advancement of Material and Process Engineering(SAMPE) Journal. 2: 1288–1301. ISBN   0-938994-56-5.
  17. ↑ C, Faudree M. (1991). "電気化学的過程とグラファイト/ポリイミド複合材料の関係". International Sampe Symposium and Exhibition (Society for the Advancement of Material and Process Engineering). 36 (2): 1288–1301.
  18. ↑ Gnanavel, G.; Thirumarimurugan, M.; Mohana Jeya Valli, V.P (2015). "Current Scenario of Biodegradation of Plastics – Review" (PDF). Australian Journal of Basic and Applied Sciences. 9: 408–417. ISSN   1991-8178.
  19. ↑ Dornheim, Michael (November 26, 1990). "ATF Researchers Address Potential for Bismaleimide Composile Degradation". Aviation Week and Science Technology: 122–123.
  20. ↑ Faudree, Michael C. (1991). "Relationship of Graphite/Polyimide Composites to Galvanic Processes" (PDF). Society for the Advancement of Material and Process Engineering(SAMPE) Journal. 2: 1288–1301. ISBN   0-938994-56-5.
  21. ↑ Tavakkolizadeh, Mohammadreza; Saadatmanesh, Hamid (August 2001). "Galvanic Corrosion of Carbon and Steel in Aggressive Environments". Journal of Composites for Construction. 5 (3): 200–210. doi:10.1061/(ASCE)1090-0268(2001)5:3(200).
  22. ↑ Zhao, Xiao-Ling; Zhang, Lei (August 2007). "State-of-the-art review on FRP strengthened steel structures". Engineering Structures. 29 (8): 1808–1823. doi:10.1016/j.engstruct.2006.10.006.
  23. ↑ Liu, Z.; Curioni, M.; Jamshidi, P.; Walker, A.; Prengnell, P.; Thompson, G.E.; Skeldon, P. (September 2014). "Electrochemical characteristics of a carbon fibre composite and the associated galvanic effects with aluminium alloys". Applied Surface Science. 314: 233–240. Bibcode:2014ApSS..314..233L. doi:10.1016/j.apsusc.2014.06.072.
  24. ↑ Pan, Yingcai; Wu, Guoqing; Cheng, Xu; Zhang, Zongke; Li, Maoyuan; Ji, Sudong; Huang, Zheng (September 2015). "Galvanic corrosion behaviour of carbon fibre reinforced polymer/magnesium alloys coupling". Corrosion Science. 98: 672–677. doi:10.1016/j.corsci.2015.06.024.
  25. ↑ Woo, E. M.; Chen, J. S.; Carter, C. S. (1993). "Mechanisms of degradation of polymer composites by galvanic reactions between metals and carbon fiber". Polymer Composites. 14 (5): 395–401. doi:10.1002/pc.750140505.
  26. 1 2 Andrady, Anthony L. (February 1994). "Assessment of Environmental Biodegradation of Synthetic Polymers". Journal of Macromolecular Science, Part C: Polymer Reviews. 34 (1): 25–76. doi:10.1080/15321799408009632.
  27. 1 2 Feldman, D. (1 October 2002). "Polymer Weathering: Photo-Oxidation". Journal of Polymers and the Environment. 10 (4): 163–173. doi:10.1023/A:1021148205366. S2CID   92300829.
  28. ↑ Hahladakis, John N.; Velis, Costas A.; Weber, Roland; Iacovidou, Eleni; Purnell, Phil (February 2018). "An overview of chemical additives present in plastics: Migration, release, fate and environmental impact during their use, disposal and recycling" (PDF). Journal of Hazardous Materials. 344: 179–199. doi: 10.1016/j.jhazmat.2017.10.014 . PMID   29035713.
  29. ↑ Teuten, Emma L.; Saquing, Jovita M.; Knappe, Detlef R. U.; Barlaz, Morton A.; Jonsson, Susanne; Björn, Annika; Rowland, Steven J.; Thompson, Richard C.; Galloway, Tamara S.; Yamashita, Rei; Ochi, Daisuke; Watanuki, Yutaka; Moore, Charles; Viet, Pham Hung; Tana, Touch Seang; Prudente, Maricar; Boonyatumanond, Ruchaya; Zakaria, Mohamad P.; Akkhavong, Kongsap; Ogata, Yuko; Hirai, Hisashi; Iwasa, Satoru; Mizukawa, Kaoruko; Hagino, Yuki; Imamura, Ayako; Saha, Mahua; Takada, Hideshige (27 July 2009). "Transport and release of chemicals from plastics to the environment and to wildlife". Philosophical Transactions of the Royal Society B: Biological Sciences. 364 (1526): 2027–2045. doi:10.1098/rstb.2008.0284. PMC   2873017 . PMID   19528054.
  30. ↑ Wiles, D.M.; Carlsson, D.J. (November 1980). "Photostabilisation mechanisms in polymers: A review". Polymer Degradation and Stability. 3 (1): 61–72. doi:10.1016/0141-3910(80)90008-7. S2CID   96033161.
  31. ↑ Allen, Norman S.; Edge, Michael; Mohammadian, Mehrdad; Jones, Ken (January 1991). "Hydrolytic degradation of poly(ethylene terephthalate): Importance of chain scission versus crystallinity". European Polymer Journal . 27 (12): 1373–1378. doi:10.1016/0014-3057(91)90237-I.
  32. ↑ Gewert, Berit; Plassmann, Merle M.; MacLeod, Matthew (2015). "Pathways for degradation of plastic polymers floating in the marine environment". Environmental Science: Processes & Impacts . 17 (9): 1513–1521. doi: 10.1039/C5EM00207A . PMID   26216708. S2CID   16732335.
  33. ↑ Ahmed, Temoor; Shahid, Muhammad; Azeem, Farrukh; Rasul, Ijaz; Shah, Asad Ali; Noman, Muhammad; Hameed, Amir; Manzoor, Natasha; Manzoor, Irfan; Muhammad, Sher (March 2018). "Biodegradation of plastics: current scenario and future prospects for environmental safety". Environmental Science and Pollution Research. 25 (8): 7287–7298. doi:10.1007/s11356-018-1234-9. PMID   29332271. S2CID   3962436.
  34. ↑ Danso, Dominik; Chow, Jennifer; Streit, Wolfgang R. (19 July 2019). "Plastics: Environmental and Biotechnological Perspectives on Microbial Degradation". Applied and Environmental Microbiology . 85 (19): e01095–19, /aem/85/19/AEM.01095–19.atom. Bibcode:2019ApEnM..85E1095D. doi:10.1128/AEM.01095-19. PMC   6752018 . PMID   31324632.
  35. ↑ Tokiwa, Yutaka; Calabia, Buenaventurada; Ugwu, Charles; Aiba, Seiichi (26 August 2009). "Biodegradability of Plastics". International Journal of Molecular Sciences . 10 (9): 3722–3742. doi: 10.3390/ijms10093722 . PMC   2769161 . PMID   19865515.
  36. ↑ Krueger, Martin C.; Harms, Hauke; Schlosser, Dietmar (November 2015). "Prospects for microbiological solutions to environmental pollution with plastics". Applied Microbiology and Biotechnology . 99 (21): 8857–8874. doi:10.1007/s00253-015-6879-4. PMID   26318446. S2CID   8797245.
  37. ↑ Shah, Aamer Ali; Hasan, Fariha; Hameed, Abdul; Ahmed, Safia (May 2008). "Biological degradation of plastics: A comprehensive review". Biotechnology Advances . 26 (3): 246–265. doi:10.1016/j.biotechadv.2007.12.005. PMID   18337047.
  38. ↑ Singh, Narinder; Hui, David; Singh, Rupinder; Ahuja, I.P.S.; Feo, Luciano; Fraternali, Fernando (April 2017). "Recycling of plastic solid waste: A state of art review and future applications". Composites Part B: Engineering. 115: 409–422. doi:10.1016/j.compositesb.2016.09.013.
  39. ↑ Hopewell, Jefferson; Dvorak, Robert; Kosior, Edward (27 July 2009). "Plastics recycling: challenges and opportunities". Philosophical Transactions of the Royal Society B: Biological Sciences. 364 (1526): 2115–2126. doi:10.1098/rstb.2008.0311. PMC   2873020 . PMID   19528059.
  40. ↑ Yin, Shi; Tuladhar, Rabin; Shi, Feng; Shanks, Robert A.; Combe, Mark; Collister, Tony (December 2015). "Mechanical reprocessing of polyolefin waste: A review". Polymer Engineering & Science. 55 (12): 2899–2909. doi:10.1002/pen.24182.
  41. ↑ Babetto, Alex S.; Antunes, Marcela C.; Bettini, Sílvia H. P.; Bonse, Baltus C. (February 2020). "A Recycling-Focused Assessment of the Oxidative Thermomechanical Degradation of HDPE Melt Containing Pro-oxidant" . Journal of Polymers and the Environment. 28 (2): 699–712. doi:10.1007/s10924-019-01641-6. S2CID   209432804.
  42. ↑ Aldas, Miguel; Paladines, Andrea; Valle, Vladimir; Pazmiño, Miguel; Quiroz, Francisco (2018). "Effect of the Prodegradant-Additive Plastics Incorporated on the Polyethylene Recycling". International Journal of Polymer Science. 2018: 1–10. doi: 10.1155/2018/2474176 .
  43. ↑ Eriksen, M.K.; Christiansen, J.D.; Daugaard, A.E.; Astrup, T.F. (August 2019). "Closing the loop for PET, PE and PP waste from households: Influence of material properties and product design for plastic recycling" (PDF). Waste Management. 96: 75–85. doi:10.1016/j.wasman.2019.07.005. PMID   31376972. S2CID   199067235.
  44. ↑ Kaminsky, W; Predel, M; Sadiki, A (September 2004). "Feedstock recycling of polymers by pyrolysis in a fluidised bed". Polymer Degradation and Stability. 85 (3): 1045–1050. doi:10.1016/j.polymdegradstab.2003.05.002.
  45. ↑ Kumagai, Shogo; Yoshioka, Toshiaki (1 November 2016). "Feedstock Recycling via Waste Plastic Pyrolysis". Journal of the Japan Petroleum Institute. 59 (6): 243–253. doi: 10.1627/jpi.59.243 .
  46. ↑ Rahimi, AliReza; García, Jeannette M. (June 2017). "Chemical recycling of waste plastics for new materials production". Nature Reviews Chemistry. 1 (6): 0046. doi:10.1038/s41570-017-0046.
  47. ↑ Coates, Geoffrey W.; Getzler, Yutan D. Y. L. (July 2020). "Chemical recycling to monomer for an ideal, circular polymer economy". Nature Reviews Materials . 5 (7): 501–516. Bibcode:2020NatRM...5..501C. doi:10.1038/s41578-020-0190-4. S2CID   215760966.
  48. ↑ Aguado, J.; Serrano, D. P.; Escola, J. M. (5 November 2008). "Fuels from Waste Plastics by Thermal and Catalytic Processes: A Review". Industrial & Engineering Chemistry Research . 47 (21): 7982–7992. doi:10.1021/ie800393w.
  49. ↑ Wei, Ren; Zimmermann, Wolfgang (November 2017). "Microbial enzymes for the recycling of recalcitrant petroleum-based plastics: how far are we?". Microbial Biotechnology . 10 (6): 1308–1322. doi:10.1111/1751-7915.12710. PMC   5658625 . PMID   28371373.
  50. ↑ Geyer, B.; Lorenz, G.; Kandelbauer, A. (2016). "Recycling of poly(ethylene terephthalate) – A review focusing on chemical methods". Express Polymer Letters. 10 (7): 559–586. doi: 10.3144/expresspolymlett.2016.53 .
  51. ↑ Ru, Jiakang; Huo, Yixin; Yang, Yu (21 April 2020). "Microbial Degradation and Valorization of Plastic Wastes". Frontiers in Microbiology . 11: 442. doi: 10.3389/fmicb.2020.00442 . PMC   7186362 . PMID   32373075. S2CID   216028039.
  52. ↑ Wierckx, Nick; Prieto, M. Auxiliadora; Pomposiello, Pablo; Lorenzo, Victor; O'Connor, Kevin; Blank, Lars M. (November 2015). "Plastic waste as a novel substrate for industrial biotechnology". Microbial Biotechnology . 8 (6): 900–903. doi:10.1111/1751-7915.12312. PMC   4621443 . PMID   26482561.
  53. ↑ Celina, Mathew C.; Linde, Erik; Martinez, Estevan (March 2021). "Carbonyl Identification and Quantification Uncertainties for Oxidative Polymer Degradation". Polymer Degradation and Stability. 188: 109550. doi: 10.1016/j.polymdegradstab.2021.109550 . OSTI   1772948. S2CID   233639741.
This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.