Bismuth strontium calcium copper oxide

Last updated • 6 min readFrom Wikipedia, The Free Encyclopedia

A piece of cuprate of bismuth and strontium: this piece is a cube with an edge of nearly 1 mm. BI2223-piece3 001.jpg
A piece of cuprate of bismuth and strontium: this piece is a cube with an edge of nearly 1 mm.

Bismuth strontium calcium copper oxide (BSCCO, pronounced bisko), is a type of cuprate superconductor having the generalized chemical formula Bi 2 Sr 2 Ca n−1 Cu n O 2n+4+x, with n = 2 being the most commonly studied compound (though n = 1 and n = 3 have also received significant attention). Discovered as a general class in 1988, [1] BSCCO was the first high-temperature superconductor which did not contain a rare-earth element.

Contents

It is a cuprate superconductor, an important category of high-temperature superconductors sharing a two-dimensional layered (perovskite) structure (see figure at right) with superconductivity taking place in a copper-oxide plane. BSCCO and YBCO are the most studied cuprate superconductors.

Specific types of BSCCO are usually referred to using the sequence of the numbers of the metallic ions. Thus Bi-2201 is the n = 1 compound (Bi 2 Sr 2 Cu O 6+x), Bi-2212 is the n = 2 compound (Bi 2 Sr 2 Ca Cu 2 O 8+x), and Bi-2223 is the n = 3 compound (Bi 2 Sr 2 Ca 2 Cu 3 O 10+x).

The BSCCO family is analogous to a thallium family of high-temperature superconductors referred to as TBCCO and having the general formula Tl 2 Ba 2 Ca n−1 Cu n O 2n+4+x, and a mercury family HBCCO of formula Hg Ba 2 Ca n−1 Cu n O 2n+2+x. There are a number of other variants of these superconducting families. In general, their critical temperature at which they become superconducting rises for the first few members and then falls. Thus Bi-2201 has Tc ≈ 33 K, Bi-2212 has Tc ≈ 96 K, Bi-2223 has Tc ≈ 108 K, and Bi-2234 has Tc ≈ 104 K. This last member is very difficult to synthesize.

Wires and tapes

For practical applications, BSCCO is compressed with silver metal into tape by the powder-in-tube process Bisco2223tape.jpg
For practical applications, BSCCO is compressed with silver metal into tape by the powder-in-tube process

BSCCO was the first HTS material to be used for making practical superconducting wires. All HTS have an extremely short coherence length, of the order of 1.6 nm. This means that the grains in a polycrystalline wire must be in extremely good contact – they must be atomically smooth. Further, because the superconductivity resides substantially only in the copper-oxygen planes, the grains must be crystallographically aligned. BSCCO is therefore a good candidate because its grains can be aligned either by melt processing or by mechanical deformation. The double bismuth-oxide layer is only weakly bonded by van der Waals forces. So like graphite or mica, deformation causes slip on these BiO planes, and grains tend to deform into aligned plates. Further, because BSCCO has n = 1, 2 and 3 members, these naturally tend to accommodate low angle grain boundaries, so that indeed they remain atomically smooth. Thus, first-generation HTS wires (referred to as 1G) have been manufactured for many years now by companies such as American Superconductor Corporation (AMSC) in the USA and Sumitomo in Japan, though AMSC has now abandoned BSCCO wire in favour of 2G wire based on YBCO. [ citation needed ]

Typically, precursor powders are packed into a silver tube, which is then extruded down in diameter. These are then repacked as multiple tubes in a silver tube and again extruded down in diameter, then drawn down further in size and rolled into a flat tape. The last step ensures grain alignment. The tapes are then reacted at high temperature to form dense, crystallographically aligned Bi-2223 multifilamentary conducting tape suitable for winding cables or coils for transformers, magnets, motors and generators. [2] [3] Typical tapes of 4 mm width and 0.2 mm thickness support a current of 200 A at 77 K, giving a critical current density in the Bi-2223 filaments of 5 kA/mm2. This rises markedly with decreasing temperature so that many applications are implemented at 30–35 K, even though Tc is 108 K.

Applications

Electrical power transmission :

Electromagnets and their current leads :

Discovery

BSCCO as a new class of superconductor was discovered around 1988 by Hiroshi Maeda and colleagues [1] at the National Research Institute for Metals in Japan, though at the time they were unable to determine its precise composition and structure. Almost immediately several groups, and most notably Subramanian [5] et al. at Dupont and Cava [6] et al. at AT&T Bell Labs, identified Bi-2212. The n = 3 member proved quite elusive and was not identified until a month or so later by Tallon [7] et al. in a government research lab in New Zealand. There have been only minor improvements to these materials since. A key early development was to replace about 15% of the Bi by Pb, which greatly accelerated the formation and quality of Bi-2223.

The crystal unit cell of BSCCO-2212, comprising two repeat units offset by (1/2,0,0). The other BSCCO family members have very similar structures: 2201 has one less CuO2 in its top and bottom half and no Ca layer, while 2223 has an extra CuO2 and Ca layer in each half. Bi2212 Unit Cell.png
The crystal unit cell of BSCCO-2212, comprising two repeat units offset by (1/2,0,0). The other BSCCO family members have very similar structures: 2201 has one less CuO2 in its top and bottom half and no Ca layer, while 2223 has an extra CuO2 and Ca layer in each half.

Properties

BSCCO needs to be hole-doped by an excess of oxygen atoms (x in the formula) in order to superconduct. As in all high-temperature superconductors (HTS) Tc is sensitive to the exact doping level: the maximal Tc for Bi-2212 (as for most HTS) is achieved with an excess of about 0.16 holes per Cu atom. [8] [9] This is referred to as optimal doping. Samples with lower doping (and hence lower Tc) are generally referred to as underdoped, while those with excess doping (also lower Tc) are overdoped. By changing the oxygen content, Tc can thus be altered at will. By many measures,[ clarification needed ] overdoped HTS are strong superconductors, even if their Tc is less than optimal, but underdoped HTS become extremely weak.[ citation needed ]

The application of external pressure generally raises Tc in underdoped samples to values that well exceed the maximum at ambient pressure. This is not fully understood, though a secondary effect is that pressure increases the doping. Bi-2223 is complicated in that it has three distinct copper-oxygen planes. The two outer copper-oxygen layers are typically close to optimal doping, while the remaining inner layer is markedly underdoped. Thus the application of pressure in Bi-2223 results in Tc rising to a maximum of about 123 K due to optimization of the two outer planes. Following an extended decline, Tc then rises again towards 140 K due to optimization of the inner plane. A key challenge therefore is to determine how to optimize all copper-oxygen layers simultaneously.

BSCCO is a Type-II superconductor. The upper critical field Hc2 in Bi-2212 polycrystalline samples at 4.2 K has been measured as 200 ± 25 T (cf 168 ± 26 T for YBCO polycrystalline samples). [10] In practice, HTS are limited by the irreversibility field H*, above which magnetic vortices melt or decouple. Even though BSCCO has a higher upper critical field than YBCO it has a much lower H* (typically smaller by a factor of 100) [11] thus limiting its use for making high-field magnets. It is for this reason that conductors of YBCO are preferred to BSCCO, though they are much more difficult to fabricate.

See also

Related Research Articles

Unconventional superconductors are materials that display superconductivity which does not conform to either the conventional BCS theory or Nikolay Bogolyubov's theory or its extensions.

<span class="mw-page-title-main">High-temperature superconductivity</span> Superconductive behavior at temperatures much higher than absolute zero

High-temperature superconductors are defined as materials that behave as superconductors at temperatures above 77 K, the boiling point of liquid nitrogen. The adjective "high temperature" is only in respect to previously known superconductors, which function at even colder temperatures close to absolute zero. In absolute terms, these "high temperatures" are still far below ambient, and therefore require cooling. The first high-temperature superconductor was discovered in 1986, by IBM researchers Bednorz and Müller, who were awarded the Nobel Prize in Physics in 1987 "for their important break-through in the discovery of superconductivity in ceramic materials". Most high-Tc materials are type-II superconductors.

A room-temperature superconductor is a material that is capable of exhibiting superconductivity at operating temperatures above 0 °C, that is, temperatures that can be reached and easily maintained in an everyday environment. As of 2020, the material with the highest accepted superconducting temperature is an extremely pressurized carbonaceous sulfur hydride with a critical transition temperature of +15 °C at 267 GPa. On 22 September 2022, the original article reporting superconductivity in the carbonaceous sulfur hydride material was retracted by Nature journal editorial board due to a non standard, user-defined data analysis, calling into question the scientific validity of the claim.

<span class="mw-page-title-main">Magnesium diboride</span> Chemical compound

Magnesium diboride is the inorganic compound with the formula MgB2. It is a dark gray, water-insoluble solid. The compound has attracted attention because it becomes superconducting at 39 K (−234 °C). In terms of its composition, MgB2 differs strikingly from most low-temperature superconductors, which feature mainly transition metals. Its superconducting mechanism is primarily described by BCS theory.

<span class="mw-page-title-main">Yttrium barium copper oxide</span> Chemical compound

Yttrium barium copper oxide (YBCO) is a family of crystalline chemical compounds that display high-temperature superconductivity; it includes the first material ever discovered to become superconducting above the boiling point of liquid nitrogen at about 93 K.

<span class="mw-page-title-main">Type-II superconductor</span> Superconductor characterized by the formation of magnetic vortices in an applied magnetic field

In superconductivity, a type-II superconductor is a superconductor that exhibits an intermediate phase of mixed ordinary and superconducting properties at intermediate temperature and fields above the superconducting phases. It also features the formation of magnetic field vortices with an applied external magnetic field. This occurs above a certain critical field strength Hc1. The vortex density increases with increasing field strength. At a higher critical field Hc2, superconductivity is destroyed. Type-II superconductors do not exhibit a complete Meissner effect.

<span class="mw-page-title-main">Georg Bednorz</span> German physicist

Johannes Georg Bednorz is a German physicist who, together with K. Alex Müller, discovered high-temperature superconductivity in ceramics, for which they shared the 1987 Nobel Prize in Physics.

<span class="mw-page-title-main">K. Alex Müller</span> Swiss physicist and Nobel laureate (1927–2023)

Karl Alexander Müller was a Swiss physicist and Nobel laureate. He received the Nobel Prize in Physics in 1987 with Georg Bednorz for their work in superconductivity in ceramic materials.

Cuprate superconductors are a family of high-temperature superconducting materials made of layers of copper oxides (CuO2) alternating with layers of other metal oxides, which act as charge reservoirs. At ambient pressure, cuprate superconductors are the highest temperature superconductors known. However, the mechanism by which superconductivity occurs is still not understood.

Superconductors can be classified in accordance with several criteria that depend on physical properties, current understanding, and the expense of cooling them or their material.

<span class="mw-page-title-main">Iron-based superconductor</span>

Iron-based superconductors (FeSC) are iron-containing chemical compounds whose superconducting properties were discovered in 2006. In 2008, led by recently discovered iron pnictide compounds, they were in the first stages of experimentation and implementation..

<span class="mw-page-title-main">Thallium barium calcium copper oxide</span> Family of high-temperature superconductors

Thallium barium calcium copper oxide, or TBCCO (pronounced "tibco"), is a family of high-temperature superconductors having the generalized chemical formula TlmBa2Can−1CunO2n+m+2.

<span class="mw-page-title-main">Superconducting wire</span> Wires exhibiting zero resistance

Superconducting wires are electrical wires made of superconductive material. When cooled below their transition temperatures, they have zero electrical resistance. Most commonly, conventional superconductors such as niobium-titanium are used, but high-temperature superconductors such as YBCO are entering the market.

<span class="mw-page-title-main">Lanthanum barium copper oxide</span> High temperature superconductor

Lanthanum barium copper oxide, or LBCO, is an inorganic compound with the formula CuBa0.15La1.85O4. It is a black solid produced by heating an intimate mixture of barium oxide, copper(II) oxide, and lanthanum oxide in the presence of oxygen. The material was discovered in 1986 and was the first high temperature superconductor. Johannes Georg Bednorz and K. Alex Müller shared the 1987 Nobel Prize in physics for the discovery that this material exhibits superconductivity at the then unusually high temperature. This finding led to intense and fruitful efforts to generate other cuprate superconductors.

Superstripes is a generic name for a phase with spatial broken symmetry that favors the onset of superconducting or superfluid quantum order. This scenario emerged in the 1990s when non-homogeneous metallic heterostructures at the atomic limit with a broken spatial symmetry have been found to favor superconductivity. Before a broken spatial symmetry was expected to compete and suppress the superconducting order. The driving mechanism for the amplification of the superconductivity critical temperature in superstripes matter has been proposed to be the shape resonance in the energy gap parameters ∆n that is a type of Fano resonance for coexisting condensates.

<span class="mw-page-title-main">Distrontium ruthenate</span> Chemical compound

Distrontium ruthenate, also known as strontium ruthenate, is an oxide of strontium and ruthenium with the chemical formula Sr2RuO4. It was the first reported perovskite superconductor that did not contain copper. Strontium ruthenate is structurally very similar to the high-temperature cuprate superconductors, and in particular, is almost identical to the lanthanum doped superconductor (La, Sr)2CuO4. However, the transition temperature for the superconducting phase transition is 0.93 K (about 1.5 K for the best sample), which is much lower than the corresponding value for cuprates.

LSAT is the most common name for the inorganic compound lanthanum aluminate - strontium aluminium tantalate, which has the chemical formula (LaAlO3)0.3(Sr2TaAlO6)0.7 or its less common alternative: (La0.18Sr0.82)(Al0.59Ta0.41)O3. LSAT is a hard, optically transparent oxide of the elements lanthanum, aluminum, strontium and tantalum. LSAT has the perovskite crystal structure, and its most common use is as a single crystal substrate for the growth of epitaxial thin films.

<span class="mw-page-title-main">Rare-earth barium copper oxide</span> Chemical compounds known for exhibiting high temperature superconductivity

Rare-earth barium copper oxide is a family of chemical compounds known for exhibiting high temperature superconductivity (HTS). ReBCO superconductors have the potential to sustain stronger magnetic fields than other superconductor materials.

Bernard Raveau, born in 1940, is a French researcher in materials science, professor emeritus at the University of Caen Normandy, member of the French Academy of sciences.

<span class="mw-page-title-main">Lanthanum cuprate</span> Chemical compound

Lanthanum cuprate usually refers to the inorganic compound with the formula CuLa2O4. The name implies that the compound consists of a cuprate (CuOn]2n-) salt of lanthanum (La3+). In fact it is a highly covalent solid. It is prepared by high temperature reaction of lanthanum oxide and copper(II) oxide follow by annealing under oxygen.

References

  1. 1 2 H. Maeda; Y. Tanaka; M. Fukutumi & T. Asano (1988). "A New High-Tc Oxide Superconductor without a Rare Earth Element". Jpn. J. Appl. Phys. 27 (2): L209–L210. Bibcode:1988JaJAP..27L.209M. doi: 10.1143/JJAP.27.L209 .
  2. ↑ C. L. Briant; E. L. Hall; K. W. Lay; I. E. Tkaczyk (1994). "Microstructural evolution of the BSCCO-2223 during powder-in-tube processing". J. Mater. Res. 9 (11): 2789–2808. Bibcode:1994JMatR...9.2789B. doi:10.1557/JMR.1994.2789.
  3. ↑ Timothy P. Beales; Jo Jutson; Luc Le Lay & Michelé Mölgg (1997). "Comparison of the powder-in-tube processing properties of two (Bi2−xPbx)Sr2Ca2Cu3O10+δpowders". J. Mater. Chem. 7 (4): 653–659. doi:10.1039/a606896k.
  4. ↑ HTS materials for LHC current leads
  5. ↑ M. A. Subramanian; et al. (1988). "A new high-temperature superconductor: Bi2Sr3−xCaxCu2O8+y". Science. 239 (4843): 1015–1017. Bibcode:1988Sci...239.1015S. doi:10.1126/science.239.4843.1015. PMID   17815702. S2CID   35551648.
  6. ↑ R. J. Cava; et al. (1988). "Structure and physical properties of single crystals of the 84-K superconductor Bi2.2Sr2Ca0.8Cu2O8+δ". Physical Review B. 38 (1): 893–896. Bibcode:1988PhRvB..38..893S. doi:10.1103/PhysRevB.38.893. PMID   9945287.
  7. ↑ J. L. Tallon; et al. (1988). "High-Tc superconducting phases in the series Bi2.1(Ca,Sr)n+1CunO2n+4+δ". Nature. 333 (6169): 153–156. Bibcode:1988Natur.333..153T. doi:10.1038/333153a0. S2CID   4348096.
  8. ↑ M. R. Presland; et al. (1991). "General trends in oxygen stoichiometry effects in Bi and Tl superconductors". Physica C. 176 (1–3): 95. Bibcode:1991PhyC..176...95P. doi:10.1016/0921-4534(91)90700-9.
  9. ↑ J. L. Tallon; et al. (1995). "Generic Superconducting Phase Behaviour in High-Tc Cuprates: Tc variation with hole concentration in YBa2Cu3O7−δ". Physical Review B. 51 (18): (R)12911–4. Bibcode:1995PhRvB..5112911T. doi:10.1103/PhysRevB.51.12911. PMID   9978087.
  10. ↑ A. I. Golovashkin; et al. (1991). "Low temperature direct measurements of Hc2 in HTSC using megagauss magnetic fields". Physica C: Superconductivity. 185–189: 1859–1860. Bibcode:1991PhyC..185.1859G. doi:10.1016/0921-4534(91)91055-9.
  11. ↑ K. Togano; et al. (1988). "Properties of Pb-doped Bi-Sr-Ca-Cu-O superconductors". Applied Physics Letters. 53 (14): 1329–1331. Bibcode:1988ApPhL..53.1329T. doi:10.1063/1.100452.
This page is based on this Wikipedia article
Text is available under the CC BY-SA 4.0 license; additional terms may apply.
Images, videos and audio are available under their respective licenses.